WO2018230629A1 - ラップフィルム巻回体、並びに、ラップフィルム収容体及びその製造方法 - Google Patents

ラップフィルム巻回体、並びに、ラップフィルム収容体及びその製造方法 Download PDF

Info

Publication number
WO2018230629A1
WO2018230629A1 PCT/JP2018/022693 JP2018022693W WO2018230629A1 WO 2018230629 A1 WO2018230629 A1 WO 2018230629A1 JP 2018022693 W JP2018022693 W JP 2018022693W WO 2018230629 A1 WO2018230629 A1 WO 2018230629A1
Authority
WO
WIPO (PCT)
Prior art keywords
wrap film
resin
core
less
film
Prior art date
Application number
PCT/JP2018/022693
Other languages
English (en)
French (fr)
Inventor
裕幸 宮田
Original Assignee
日立化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日立化成株式会社 filed Critical 日立化成株式会社
Priority to JP2019525510A priority Critical patent/JPWO2018230629A1/ja
Priority to CN201880038747.2A priority patent/CN110740947B/zh
Publication of WO2018230629A1 publication Critical patent/WO2018230629A1/ja

Abstract

本発明の一態様は、巻芯と、巻芯に巻回されたラップフィルムと、を備え、巻芯は、６００Ｎ以下の扁平耐圧強度及び１０００Ｎ以下の軸圧縮強度を有する、ラップフィルム巻回体である。

Description

ラップフィルム巻回体、並びに、ラップフィルム収容体及びその製造方法
　本発明は、ラップフィルム巻回体、並びに、ラップフィルム収容体及びその製造方法に関する。
　従来、ラップフィルムは、家庭用として、あるいは、ホテル、レストラン等において業務用として、食品保存時、調理時等に幅広く使用されている（例えば特許文献１）。ラップフィルムは、通常、巻芯に巻回されたラップフィルム巻回体の形態で使用され、ラップフィルムを使い切った後、巻芯は廃棄される。
国際公開第２０１５／１２５３８４号
　本発明は、省スペースでかつ簡便に廃棄することできるラップフィルム巻回体を提供することを目的とする。
　本発明者は、従来のラップフィルム巻回体において、ラップフィルムを使い切った後に巻芯を廃棄することが必ずしも容易ではないという新規な課題が存在することを見出した。そして、本発明者らは、当該課題を解決するために、巻芯を折って廃棄することが可能なラップフィルム巻回体を用いることを見出した。すなわち、本発明の一態様は、巻芯と、巻芯に巻回されたラップフィルムと、を備え、巻芯は、６００Ｎ以下の扁平耐圧強度及び１０００Ｎ以下の軸圧縮強度を有する、ラップフィルム巻回体である。このラップフィルム巻回体の巻芯は折って破棄することが可能であるため、ラップフィルム巻回体を省スペースで（折った状態で）かつ簡便に廃棄することできる。
　ラップフィルムは、樹脂フィルムであってよい。樹脂フィルムは、ポリ塩化ビニリデン系樹脂、ポリ塩化ビニル系樹脂及びポリオレフィン系樹脂からなる群より選ばれる少なくとも一種の樹脂を含んでいてよい。
　ラップフィルムは、食品包装用、医薬包装用、臭気遮断用及び湿気遮断用からなる群より選ばれる少なくとも一種の用途で用いられてよい。
　本発明は、他の一態様において、上記のラップフィルム巻回体と、ラップフィルム巻回体が収容された箱体と、を備えるラップフィルム収容体である。
　本発明は、他の一態様において、６００Ｎ以下の扁平耐圧強度及び１０００Ｎ以下の軸圧縮強度を有する巻芯にラップフィルムを巻回し、ラップフィルム巻回体を得る工程と、ラップフィルム巻回体を箱体に収容してラップフィルム収容体を得る工程と、を備える、ラップフィルム収容体の製造方法である。
　本発明は、他の一態様において、上記のラップフィルム収容体に収容されたラップフィルムを用いて、屋外で被包装体を包装する方法である。
　本発明によれば、省スペースでかつ簡便に廃棄することできるラップフィルム巻回体を提供することができる。
一実施形態に係るラップフィルム巻回体の模式図である。
　図１は、一実施形態に係るラップフィルム巻回体の模式図である。図１に示すように、ラップフィルム巻回体１は、略円筒状の巻芯２と、巻芯２に巻回されたラップフィルム３とを備えている。
　略円筒状の巻芯２は、例えば、８～２０ｍｍの外径（長手方向と直交する断面の直径）、及び、１００～２４０ｍｍの長さ（長手方向の長さ）を有していてよい。巻芯２の外径が小さいほど後述する巻芯２の扁平耐圧強度が小さくなり、巻芯２の長さが小さいほど後述する巻芯２の軸圧縮強度が小さくなる傾向がある。巻芯２の材質は、例えば、紙管原紙、ライナー紙、硫酸紙、上質紙、ボール紙等の紙であってよい。
　巻芯２は、６００Ｎ以下の扁平耐圧強度を有しており、折って廃棄することが更に容易になる観点から、好ましくは５００Ｎ以下、より好ましくは４５０Ｎ以下、更に好ましくは３５０Ｎ以下の扁平耐圧強度を有している。巻芯２の扁平耐圧強度は、例えば３００Ｎ以上であってよい。巻芯２の扁平耐圧強度は、例えば株式会社島津製作所製オートグラフ（ＡＧ－１０ＮＸＰｌｕｓ）に巻芯２を取り付け、巻芯２の軸方向に対して垂直に圧縮し、巻芯２が断面形状を保てなくなった（例えば、巻芯２が円筒状である場合、断面形状が円形でなくなった）時点の圧縮強度として測定される。
　巻芯２は、１０００Ｎ以下の軸圧縮強度を有しており、折って廃棄することが更に容易になる観点から、好ましくは９００Ｎ以下、より好ましくは８００Ｎ以下、更に好ましくは７００Ｎ以下の軸圧縮強度を有している。巻芯２の軸圧縮強度は、例えば６００Ｎ以上であってよい。巻芯２の軸圧縮強度は、例えば株式会社島津製作所製オートグラフ（ＡＧ－１０ＮＸＰｌｕｓ）に巻芯２を取り付け、巻芯２の軸方向に圧縮し、巻芯２が断面形状を保てなくなった（例えば、巻芯２が円筒状である場合、断面形状が円形でなくなった）時点の圧縮強度として測定される。
　ラップフィルム３は、例えば、樹脂フィルム、木材パルプ、ラグパルプ、リンターパルプ等の繊維フィルム、アルミニウム箔等の金属フィルムなどであってよく、好ましくは樹脂フィルムである。樹脂フィルムは、例えば熱可塑性樹脂のフィルムであってよい。このようなラップフィルム３は、食品包装用、医薬包装用、臭気遮断用、湿気遮断用等として好適である。
　熱可塑性樹脂は、ポリ塩化ビニル等のポリ塩化ビニル系樹脂；ポリ塩化ビニリデン等のポリ塩化ビニリデン系樹脂；ポリエチレン、ポリプロピレン、エチレン－酢酸ビニル共重合体ケン化物等のポリオレフィン系樹脂；ブタジエン－スチレン共重合体、アクリロニトリル－スチレン共重合体、ポリスチレン、スチレン－ブタジエン－スチレン共重合体、スチレン－イソプレン－スチレン共重合体、スチレン－アクリル酸共重合体等のポリスチレン系樹脂；ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリブチレンテレフタレート等のポリエステル系樹脂；６－ナイロン、６，６－ナイロン、１２－ナイロン等のポリアミド系樹脂；などであってよい。
　ラップフィルム巻回体１は、携帯用として好適に用いられる。この場合、ラップフィルム３には高度な臭気遮断特性が要求される。すなわち、ラップフィルム３が屋外で使用される場合、例えば台所で使用される場合に比べて臭気の拡散をより抑制する必要があること、被包装体を他の荷物と共に携帯するため、被包装体から他の荷物への臭い移り及び外部からの被包装体への臭い移りが生じやすいこと等から、ラップフィルム３の臭気遮断特性が重要となる。特に、携帯用のラップフィルム巻回体１におけるラップフィルム３では、ラップフィルムを台所等で使用する場合には考慮する必要のなかった臭い、すなわち、被包装体と共に携帯されることが想定される、化粧品、ヘルスケア用品（例えばハンドクリーム）、たばこ、使用済みオムツ等の物品の臭いを遮断できることが望ましい。このような携帯用のラップフィルム巻回体１におけるラップフィルム３に求められる特有の臭気遮断特性に優れる観点から、熱可塑性樹脂は、好ましくは、ポリ塩化ビニル系樹脂、ポリ塩化ビニリデン系樹脂又はポリオレフィン系樹脂であり、より好ましくはポリ塩化ビニル系樹脂又はポリ塩化ビニリデン系樹脂であり、更に好ましくはポリ塩化ビニリデン系樹脂である。
　ポリ塩化ビニル系樹脂は、機械特性に優れる観点から、塩化ビニル単独重合体（ポリ塩化ビニル）であってよく、他の特性を付与する目的から、塩化ビニルとこれに共重合可能なその他のモノマーとの共重合体であってもよい。共重合体は、グラフト共重合体、ブロック共重合体又はランダム共重合体であってよい。その他のモノマーの例としては、エチレン、プロピレン、ポリブテン等のオレフィン；酢酸ビニル、ラウリン酸ビニル等の飽和酸のビニルエステル；アクリル酸メチルエステル、メタクリル酸メチルエステル等の不飽和酸のアルキルエステル；ラウリルビニルエーテル等のアルキルビニルエーテル；マレイン酸、アクリロニトリル、スチレン、メチルスチレン、フッ化ビニリデン；などが挙げられる。ポリ塩化ビニル系樹脂が共重合体である場合、共重合体における塩化ビニル単位の含有量は、モノマー単位全量基準で、１０質量％以上であってよく、機械特性に優れる観点から、好ましくは３０質量％以上、より好ましくは５０質量％以上である。共重合体における塩化ビニル単位の含有量の上限は、特に限定されず、例えば、モノマー単位全量基準で９９質量％以下であってよい。
　ポリ塩化ビニル系樹脂の平均重合度は、フィルムの成形性、耐熱性及び流動性に優れる観点から、好ましくは、７００以上であり、１３００以下である。本明細書における平均重合度は、ＪＩＳ　Ｋ６７２０－２に準じて測定された平均重合度を意味する。
　ポリ塩化ビニリデン系樹脂は、塩化ビニリデン単独重合体（ポリ塩化ビニリデン）であってよく、例えば、塩化ビニリデンと、塩化ビニリデンと共重合可能なその他のモノマーとをモノマー単位として含む共重合体であってもよい。その他のモノマーは、塩化ビニル、アクリル酸と炭素数１～８のアルコールとのアクリル酸エステル、メタクリル酸と炭素数１～８のアルコールとのメタクリル酸エステル、脂肪族カルボン酸のビニルエステル、不飽和脂肪族カルボン酸、オレフィン、ビニルエーテル等であってよい。なお、塩化ビニリデンと塩化ビニルとの共重合体は、ポリ塩化ビニリデン系樹脂に属するものとする。
　ポリ塩化ビニリデン系樹脂における塩化ビニリデン単位の含有量は、フィルムの成形性及び耐熱性の観点から、モノマー単位全量基準で、例えば、６０質量％以上、７０質量％以上、又は８０質量％以上であってよい。ポリ塩化ビニリデン系樹脂における塩化ビニリデン単位の含有量の上限は、特に限定されず、例えば、モノマー単位全量基準で９９質量％以下であってよい。塩化ビニリデン単位の含有量は、核磁気共鳴（ＮＭＲ）装置により測定することができる。
　ポリ塩化ビニリデン系樹脂の重量平均分子量は、例えば、４００００以上、６００００以上、又は８００００以上であってよく、１８００００以下、１６００００以下、又は１４００００以下であってよい。ポリ塩化ビニリデン系樹脂の重量平均分子量は、ＧＰＣ法により、分子量既知のポリスチレンを標準物質として測定することができる。
　ポリ塩化ビニリデン系樹脂の重量平均分子量測定に用いるＧＰＣ法の条件は、以下のとおりである。測定装置としてウォーターズ社製ゲルクロマトグラフＡｌｌｉａｎｃｅＧＰＣ２０００型を使用する。ポリ塩化ビニリデン系樹脂を０．５質量％となるようにテトラヒドロフランに溶解させたものを、試料として用いる。
　カラム：東ソー株式会社製ＴＳＫｇｅｌ　ＧＭＨＨＲ－Ｈ（Ｓ）ＨＴ　３０ｃｍ×２、ＴＳＫｇｅｌ　ＧＭＨ６－ＨＴＬ　３０ｃｍ×２
　移動相：テトラヒドロフラン
　検出器：示差屈折計
　流速：１．０ｍＬ／分
　カラム温度：２０℃
　注入量：５００μＬ
　ポリオレフィン系樹脂は、例えば、エチレン又はプロピレンをモノマー単位として含んでおり、エチレン又はプロピレンの単独重合体（ポリエチレン又はポリプロピレン）であってもよく、エチレン又はプロピレンとこれに共重合可能なその他のモノマーとの共重合体であってもよい。共重合体は、グラフト共重合体、ブロック共重合体又はランダム共重合体であってよい。
　熱可塑性樹脂がポリオレフィン系樹脂である場合、例えば、ラップフィルム３は、中間層とその両側に設けられた表面層とからなる３層フィルムであってよい。この場合、中間層に含まれるポリオレフィン系樹脂は、例えばプロピレンをモノマー単位として含むポリプロピレン系樹脂であってよく、具体的には、例えば、プロピレン単独重合体（ポリプロピレン）、プロピレン－エチレンランダム共重合体、プロピレン－エチレン－α－オレフィンランダム共重合体、プロピレン－エチレン－ブテンランダム共重合体、プロピレンと非晶性ポリオレフィンとの混合物、プロピレンと非晶性ゴムとの共重合ポリマーアロイ等であってよい。
　プロピレン－エチレンランダム共重合体におけるエチレン単位の含有量は、全モノマー単位全量基準で、好ましくは、１質量％以上であり、２０質量％以下である。プロピレン－エチレン－α－オレフィンランダム共重合体におけるエチレン単位の含有量及びα－オレフィン単位の含有量は、全モノマー単位全量基準で、好ましくは、それぞれ、１質量％以上であり、１０質量％以下である。プロピレン－エチレン－ブテン三元ランダム共重合体におけるエチレン単位及びブテン単位の含有量の合計は、全モノマー単位全量基準で、好ましくは、１質量％以上であり、２０質量％以下である。
　中間層に含まれるポリプロピレン系樹脂のＭＦＲ（Melt Mass-Flow Rate）は、好ましくは、０．１ｇ／１０分以上又は０．５ｇ／１０分以上であり、１０ｇ／１０分以下、７ｇ／１０分以下、又は５ｇ／１０分以下である。本明細書におけるポリプロピレン系樹脂のＭＦＲは、ＪＩＳ　Ｋ６９２１－２に準じて２３０℃において測定された値を意味する。
　３層フィルムの表面層に含まれるポリオレフィン系樹脂は、例えばエチレンをモノマー単位として含むポリエチレン系樹脂であってよく、具体的には、例えば、高密度ポリエチレン、分岐構造を有する低密度ポリエチレン、直鎖状低密度ポリエチレン、超低密度ポリエチレン等であってよい。ポリエチレン系樹脂は、透明性に優れる点で、好ましくは、低密度ポリエチレン、直鎖状低密度ポリエチレン又は超低密度ポリエチレンであり、カット性及び密着性に優れる点で、より好ましくは直鎖状低密度ポリエチレンである。
　ポリエチレン系樹脂のＭＦＲは、好ましくは、０．１ｇ／１０分以上又は０．５ｇ／１０分以上であり、１０ｇ／１０分以下、７ｇ／１０分以下、又は５ｇ／１０分以下である。本明細書におけるポリエチレン系樹脂のＭＦＲは、ＪＩＳ　Ｋ６９２２－２に準じて１９０℃において測定された値を意味する。
　ポリエチレン系樹脂が直鎖状低密度ポリエチレンを含む場合、直鎖状低密度ポリエチレンの密度は、好ましくは、０．９００ｇ／ｃｍ３以上又は０．９０５ｇ／ｃｍ３以上であり、０．９２５ｇ／ｃｍ３以下、０．９２０ｇ／ｃｍ３以下、又は０．９１５ｇ／ｃｍ３以下である。この場合、製膜性及びラップフィルム３の表面平滑性を向上させるために、ポリエチレン系樹脂は、直鎖状低密度ポリエチレンに加えて、密度が０．９１０～０．９５０ｇ／ｃｍ３の分岐構造を有する低密度ポリエチレンを更に含んでいてもよい。この場合の分岐構造を有する低密度ポリエチレンの含有量は、好ましくは、直鎖状低密度ポリエチレン１００質量部に対して、５質量部以上であり、２５質量部以下である。
　熱可塑性樹脂の含有量は、生産性に優れる観点から、ラップフィルム３（樹脂フィルム）全量基準で、７０質量％以上又は７５質量％以上であってよく、８５質量％以下又は８０質量％以下であってよい。
　ラップフィルム３（樹脂フィルム）は、熱可塑性樹脂に加えて、その他の成分を更に含有していてもよい。その他の成分としては、防曇剤、熱安定剤、光安定剤、滑剤、充填剤、プレートアウト防止剤、抗酸化剤、離型剤、粘度低下剤、界面活性剤、着色剤、蛍光剤、表面処理剤、架橋剤、加工助剤、粘着剤、帯電防止剤、紫外線吸収剤、アンチブロッキング剤等が挙げられる。
　熱可塑性樹脂がポリ塩化ビニル系樹脂又はポリ塩化ビニリデン系樹脂である場合、ラップフィルム３（樹脂フィルム）は、その他の成分として可塑剤を更に含有していてよい。可塑剤としては、エポキシ化アマニ油、エポキシ化大豆油、エポキシ化脂肪酸アルキルエステル等のエポキシ化油、炭素数６～１０個の直鎖又は分岐アルキル基を有するアジピン酸エステル、アセチルクエン酸トリブチル、アセチル化トリエチル等のヒドロキシ多価カルボン酸エステル、セバシン酸ジノルマルブチル等の脂肪酸族二塩基酸エステル、ペンタエリスリトールエステル、ジエチレングリコールベンゾエート等のグリコールエステル、トリフェニルホスフェート、トリクレジルホスフェート等のリン酸エステル、グリセリンジアセトモノラウレート、塩素化パラフィン、ポリエステル系可塑剤などが挙げられる。これらの可塑剤は、１種単独又は２種以上を組み合わせて用いられる。可塑剤の含有量は、被包装体の種類、包装形態、包装方法等の用途に応じて、ポリ塩化ビニル系樹脂又はポリ塩化ビニリデン系樹脂１００質量部に対して、例えば２０～５０質量部の範囲で適宜調整される。
　ラップフィルム３は、キナクリドンレッド等の赤色着色剤、銅フタロシアニン（銅フタロシアニンブルー）、ヘキサシアノ鉄（ＩＩ）酸鉄（ＩＩＩ）等の青色着色剤、ｏ－ニトロアニリンとアセトアセトアニリドとの混合物、４－クロロ－２－ニトロアニリンとアセトアセトアニリドとの混合物等の黄色着色剤、α－ニトロソ－β－ナフトール鉄錯体等の緑色着色剤、キナクリドンバイオレット等の紫色着色剤、酸化チタン、酸化亜鉛等の白色着色剤を更に含有していてもよい。ラップフィルム３が上記の着色剤を含有することで、ラップフィルム３に色がつき、携帯時に例えば荷物の中で包装物を見分けることが容易になる。特に、赤色着色剤、黄色着色剤、青色着色剤、緑色着色剤及び紫色着色剤の少なくとも一種と、白色着色剤とを併用することで、それぞれの色調を際立たせることができる点で効果的である。
　ラップフィルム３が樹脂フィルムである場合、ラップフィルム３は、一層からなっていてもよく、複数の層からなっていてもよい。ラップフィルム３が複数の層からなる場合、ラップフィルム３は、例えば第１の表面層と中間層と第２の表面層とをこの順に備えていてよい。ラップフィルム３は、例えば、各層間の接着性を向上させるために、酸変性ポリオレフィン樹脂等を含有する接着層を更に備えていてもよく、フィルムの耐熱性を向上させるために、ポリアミド系樹脂を含有する耐熱層を更に備えていてもよい。熱可塑性樹脂がポリ塩化ビニル系樹脂である場合、ラップフィルム３は、好ましくは、熱可塑性樹脂（ポリ塩化ビニル系樹脂）及びその他の成分を含有する層の一層からなっている。
　ラップフィルム３の厚みは、好ましくは５０μｍ以下、より好ましくは２０μｍ以下、更に好ましくは１５μｍ以下である。ラップフィルム３の厚みがこの範囲である場合、臭気遮断特性を更に向上させられると共に、ラップフィルム巻回体１の体積に対し、巻芯２に巻回できるラップフィルム３の量（巻回方向Ｘの長さ）を増加させることが可能となる。ラップフィルム３が樹脂フィルムである場合、上記と同様の観点から、好ましくは１２μｍ以下、より好ましくは１０μｍ以下である。ラップフィルム３の厚みは、例えば０．０１μｍ以上であってよい。
　ラップフィルム巻回体１は、箱体（図示せず）に収容されていてもよい。すなわち、一実施形態に係るラップフィルム収容体は、ラップフィルム巻回体１と、ラップフィルム巻回体１が収容された箱体とを備えている。当該箱体は、ラップフィルムを切断するための刃部を備えていてもよい。
　ラップフィルム収容体は、例えば、箱体を用意する工程と、上述したラップフィルム３を巻芯２に巻回する工程と、箱体に巻芯２及びラップフィルム３を収容してラップフィルム収容体を得る工程と、を備える製造方法により製造される。
　ラップフィルム巻回体１（又はラップフィルム巻回体１が箱体に収容されたラップフィルム収容体）のカーボンフットプリント（ＣＦＰ、Carbon Footprint of Products）は、例えば２００ｇ以下であってよい。カーボンフットプリントは、１つの製品について、生産から廃棄に至るまでに放出される温室効果ガス排出量の総和を示す指標値であり、原材料及び部品の調達段階（例えば、原材料の製造及び精製段階での温室効果ガス排出量）と、製造段階（容器、包装等の製造時の温室効果ガス排出量も含む）と、流通段階（冷蔵輸送等を利用した場合は、冷蔵のために要した温室効果ガス排出量も含む）と、消費・使用・維持管理段階（冷蔵保存を利用した場合は、冷蔵のために要した温室効果ガス排出量も含む）と、廃棄・リサイクル段階（容器、包装等の廃棄時の温室効果ガス排出量も含む）とにおける温室効果ガスの排出量の総和をＣＯ２量に換算した値として定義される。「カーボンフットプリント」の一般的な算出ルールとして、ＩＳＯ／ＴＳ１４０６７が発行されている。
　以上説明したラップフィルム巻回体１は携帯用に適しており、屋外で好適に用いられる。すなわち、本発明の一実施形態は、ラップフィルム巻回体１に収容されたラップフィルム３を用いて、屋外で被包装体を包装する方法である。そして、このラップフィルム巻回体１においては、巻芯２を折ることが容易であるため、ラップフィルム巻回体１を屋外で用いた場合であっても巻芯２の廃棄が簡便となる。
　以下、実施例に基づいて本発明を更に具体的に説明するが、本発明は実施例に限定されるものではない。
　白上質紙１枚、紙管原紙２枚及びライナー紙１枚の４枚の紙で構成され、厚みが１ｍｍであり、かつ表１，２に示される外径（長手方向と直交する断面の直径）及び長さ（長手方向の長さ）を有する各巻芯について、扁平耐圧強度及び軸圧縮強度を以下の手順で測定した。結果を表１，２に示す。
（扁平耐圧強度）
　各巻芯を温度２３℃、相対湿度５０％の環境下で２４時間調湿した後、株式会社島津製作所製オートグラフ（ＡＧ－１０ＮＸＰｌｕｓ）を用いて、試験速度１０ｍｍ／分の条件で扁平耐圧強度を測定した。サンプル数は各々５点とし、５点の扁平耐圧強度の平均値を求めた。
（軸圧縮強度）
　各巻芯を温度２３℃、相対湿度５０％の環境下で２４時間調湿した後、株式会社島津製作所製オートグラフ（ＡＧ－１０ＮＸＰｌｕｓ）を用いて、試験速度１０ｍｍ／分の条件下で軸圧縮強度を測定した。サンプル数は各々５点とし、５点の軸圧縮強度の平均値を求めた。
（片側引張折れ強度）
　各巻芯を温度２３℃、相対湿度５０％の環境下で２４時間調湿した後、株式会社島津製作所製オートグラフ（ＡＧ－１０ＮＸＰｌｕｓ）を用いて、サンプルの一端側を固定した状態で、他端側を試験速度３００ｍｍ／分の条件で上方に引っ張った際の片側引張折れ強度を測定した。サンプル数は各々５点とし、５点の片側引張折れ強度の平均値を求めた。
（巻芯の折りやすさの官能評価）
　巻芯を手で折り曲げた際の巻芯の折りやすさを、以下の基準に従って評価した。なお、評価がＡ又はＢであれば、巻芯の折りやすさに優れているといえる。本評価では１０人のパネラーを用い、各パネラーが以下の基準に従って評価し、評価の最頻値を算出した。
Ａ：巻芯が容易に折れる。
Ｂ：巻芯を折るのに多少の力がいるが折れる。
Ｃ：巻芯が折れにくい。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　続いて、下記の各ラップフィルムａ１～ａ４（ａ１～ａ３は厚み１０μｍ、ａ４は厚み１１μｍ）を用意した。
ポリ塩化ビニリデンフィルムａ１：塩化ビニリデンと塩化ビニルとの共重合体（塩化ビニリデン／塩化ビニル（質量比）＝９０／１０、重量平均分子量：８００００）を主成分とする組成物からなるフィルム
ポリ塩化ビニルフィルムａ２：ポリ塩化ビニル系樹脂（大洋塩ビ株式会社製、「ＴＨ－１０００」、平均重合度：１０００）を主成分とする組成物からなるフィルム
ポリオレフィンフィルムａ３：下記に示すＡ層－Ｂ層－Ｃ層をこの順に備える、３層の積層フィルム
　Ａ層：エチレン－酢酸ビニル共重合体（酢酸ビニル成分＝１５％、密度＝０．９４０ｇ／ｃｍ３、ＭＦＲ＝２．０ｇ／１０分）を主成分とする組成物からなる層
　Ｂ層：エチレン－１－オクテン共重合体（密度＝０．９２６ｇ／ｃｍ３、ＭＦＲ＝２．０ｇ／１０分）と高圧法低密度ポリエチレン（密度＝０．９２１ｇ／ｃｍ３、ＭＦＲ＝０．４ｇ／１０分）とを７：３の割合（質量比）で混合した混合物を主成分とする組成物からなる層
　Ｃ層：エチレン－酢酸ビニル共重合体（酢酸ビニル成分＝１５％、密度＝０．９４０ｇ／ｃｍ３、ＭＦＲ＝２．０ｇ／１０分）を主成分とする組成物からなる層
アルミフィルムａ４：０．０１質量％以下の銅と、０．０１質量％のシリコンと、１質量％のマンガンと、０．８質量％の鉄とを含み、残部がアルミニウムと不可避不純物とを含むアルミニウム合金からなるフィルム
　これらのラップフィルムについて、被包装体をラップフィルムで包装して持ち運ぶ際に、被包装体から他の荷物への臭い移り及び外部からの被包装体への臭い移りの程度を検証するため、携帯する物品として下記ｂ１～ｂ６を用いた。
クッキーｂ１：ＢＵＴＴＥＲ　ＣＯＯＫＩＥＳ（株式会社ブルボン）
チョコレートｂ２：毎日カカオ７０％（株式会社不二家）
使用済みオムツｂ３：パンパースさらさらパンツ（プロクター・アンド・ギャンブル・ジャパン株式会社）
ファンデーションｂ４：ソフィーナ　プリマヴィスタ（花王株式会社）
たばこｂ５：Ｍａｒｌｂｏｒｏ　ｌｉｇｈｔｓ（フィリップモリスジャパン合同会社）
ハンドクリームｂ６：アトリックスビューティーチャージハンドクリーム（ニベア花王株式会社）
（臭気遮蔽特性評価）
　物品ｂ１～ｂ６を、１８ｃｍ×１８ｃｍの大きさに切断したラップフィルムａ１～ａ４でそれぞれ包み、一辺１０ｃｍの立方体である箱に入れて２時間保管した後に、嗜好型試験の１つである採点法により臭気の有無を評価した。使用済みオムツｂ３については、５ｃｍ角に切断したものを使用した。本評価では、１０人のパネラーを用い、各パネラーが臭気遮蔽特性を以下の基準に従って５段階で数値化し、１０人のパネラーの平均値を評価値として算出した。結果を表１に示す。なお、評価値が４以上であれば、臭気遮蔽特性に優れているといえる。
５：臭いが感じられない。
４：どちらかといえば臭いが感じられない。
３：どちらともいえない。
２：どちらかといえば臭いが感じられる。
１：臭いが感じられる。
Figure JPOXMLDOC01-appb-T000003
　表３より、本実施形態に係るラップフィルムは、通常持ち運びの機会の多いクッキー、チョコレート等の臭いを遮断できる。加えて、ラップフィルムがポリ塩化ビニル系樹脂又はポリ塩化ビニリデン系樹脂のフィルム（フィルムａ１，ａ２）である場合、特にラップフィルムがポリ塩化ビニリデン系樹脂のフィルム（フィルムａ１）である場合、ラップフィルムを台所等で使用する場合には考慮する必要のなかった臭いである、使用済みオムツ（ｂ３）、化粧品（ｂ４）、たばこ（ｂ５）、及びヘルスケア用品（ｂ６）の臭いを好適に遮断できることが分かる。
　１…ラップフィルム巻回体、２…巻芯、３…ラップフィルム。

Claims (7)

  1. 　巻芯と、前記巻芯に巻回されたラップフィルムと、を備え、
    　前記巻芯は、６００Ｎ以下の扁平耐圧強度及び１０００Ｎ以下の軸圧縮強度を有する、ラップフィルム巻回体。
  2. 　前記ラップフィルムが樹脂フィルムである、請求項１に記載のラップフィルム巻回体。
  3. 　前記樹脂フィルムが、ポリ塩化ビニリデン系樹脂、ポリ塩化ビニル系樹脂及びポリオレフィン系樹脂からなる群より選ばれる少なくとも一種の樹脂を含む、請求項２に記載のラップフィルム巻回体。
  4. 　前記ラップフィルムが、食品包装用、医薬包装用、臭気遮断用及び湿気遮断用からなる群より選ばれる少なくとも一種の用途で用いられる、請求項１～３のいずれか一項に記載のラップフィルム巻回体。
  5. 　請求項１～４のいずれか一項に記載のラップフィルム巻回体と、
    　前記ラップフィルム巻回体が収容された箱体と、
    を備える、ラップフィルム収容体。
  6. 　６００Ｎ以下の扁平耐圧強度及び１０００Ｎ以下の軸圧縮強度を有する巻芯にラップフィルムを巻回し、ラップフィルム巻回体を得る工程と、
    　前記ラップフィルム巻回体を箱体に収容してラップフィルム収容体を得る工程と、
    を備える、ラップフィルム収容体の製造方法。
  7. 　請求項５に記載のラップフィルム収容体に収容された前記ラップフィルムを用いて、屋外で被包装体を包装する、方法。
PCT/JP2018/022693 2017-06-14 2018-06-14 ラップフィルム巻回体、並びに、ラップフィルム収容体及びその製造方法 WO2018230629A1 (ja)