WO2018047389A1 - Matériau textile à cristaux liquides et produit textile - Google Patents

Matériau textile à cristaux liquides et produit textile Download PDF

Info

Publication number
WO2018047389A1
WO2018047389A1 PCT/JP2017/013246 JP2017013246W WO2018047389A1 WO 2018047389 A1 WO2018047389 A1 WO 2018047389A1 JP 2017013246 W JP2017013246 W JP 2017013246W WO 2018047389 A1 WO2018047389 A1 WO 2018047389A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystalline
fiber material
polyurethane
phase
crystalline polyurethane
Prior art date
Application number
PCT/JP2017/013246
Other languages
English (en)
Japanese (ja)
Inventor
井関　清治
裕希 日▲高▼
Original Assignee
東洋ゴム工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋ゴム工業株式会社 filed Critical 東洋ゴム工業株式会社
Priority to JP2018538011A priority Critical patent/JP6660474B2/ja
Publication of WO2018047389A1 publication Critical patent/WO2018047389A1/fr

Abstract

La présente invention concerne un matériau textile à cristaux liquides possédant une sensibilité thermique à une température proche de la normale, tout en possédant une résistance (durabilité) donnée ou supérieure, en se focalisant sur un phénomène selon lequel lorsqu'un polyuréthane à cristaux liquides effectue une transition de phase entre une phase cristalline et une phase isotrope en raison d'un changement de température, son taux d'allongement change. Un matériau textile à cristaux liquides (11) comprend un polyuréthane à cristaux liquides qui s'étire de manière réversible entre une phase cristalline et une phase isotrope en fonction d'un changement de température, le taux d'allongement dans la direction de la fibre étant fixé entre 102 et 200 %, un état du polyuréthane à cristaux liquides le plus rétracté étant utilisé comme point de référence (100 %), et le facteur de retrait dans la direction de la fibre étant fixé entre 98,04 et 50 %, un état du polyuréthane à cristaux liquides le plus expansé étant utilisé comme point de référence (100 %).
PCT/JP2017/013246 2016-09-09 2017-03-30 Matériau textile à cristaux liquides et produit textile WO2018047389A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018538011A JP6660474B2 (ja) 2016-09-09 2017-03-30 液晶性繊維材料、及び繊維製品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016176504 2016-09-09
JP2016-176504 2016-09-09

Publications (1)

Publication Number Publication Date
WO2018047389A1 true WO2018047389A1 (fr) 2018-03-15

Family

ID=61562231

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/013246 WO2018047389A1 (fr) 2016-09-09 2017-03-30 Matériau textile à cristaux liquides et produit textile

Country Status (2)

Country Link
JP (1) JP6660474B2 (fr)
WO (1) WO2018047389A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0211108U (fr) * 1988-07-01 1990-01-24
JPH07258369A (ja) * 1994-03-18 1995-10-09 Nitta Ind Corp 高分子液晶ポリウレタン
WO2008026509A1 (fr) * 2006-08-29 2008-03-06 National Institute Of Advanced Industrial Science And Technology Composition d'élastomère thermoplastique présentant une structure hiérarchique et son procédé de fabrication
WO2017002682A1 (fr) * 2015-07-01 2017-01-05 東洋ゴム工業株式会社 Fibre unique comprenant un élastomère thermosensible à cristaux liquides, fil de filaments et produit fibreux

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20180053350A (ko) * 2015-12-24 2018-05-21 도요 고무 고교 가부시키가이샤 열응답성 재료, 및 열응답성 재료를 이용한 열제어 장치 및 섬유

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0211108U (fr) * 1988-07-01 1990-01-24
JPH07258369A (ja) * 1994-03-18 1995-10-09 Nitta Ind Corp 高分子液晶ポリウレタン
WO2008026509A1 (fr) * 2006-08-29 2008-03-06 National Institute Of Advanced Industrial Science And Technology Composition d'élastomère thermoplastique présentant une structure hiérarchique et son procédé de fabrication
WO2017002682A1 (fr) * 2015-07-01 2017-01-05 東洋ゴム工業株式会社 Fibre unique comprenant un élastomère thermosensible à cristaux liquides, fil de filaments et produit fibreux

Also Published As

Publication number Publication date
JP6660474B2 (ja) 2020-03-11
JPWO2018047389A1 (ja) 2019-06-24

Similar Documents

Publication Publication Date Title
JP6616600B2 (ja) 熱応答性液晶エラストマーを含む単繊維、フィラメント糸、繊維製品
JP6568305B2 (ja) 液晶性エラストマー前駆体、及び液晶性エラストマー
US5811506A (en) Extrudable thermoplastic elastomeric urea-extended polyurethane
JP2502132B2 (ja) 形状記憶ポリウレタンエラストマ―成形体
JP6152056B2 (ja) エラストマー樹脂、その繊維および布、ならびにそれらの使用
JP2006505672A5 (fr)
JPH01131227A (ja) 吹込フィルム用法のための軟質熱可塑性ポリウレタン
AU2016376548B2 (en) Thermoresponsive material, and heat control device and fiber using thermoresponsive material
JP2017014393A (ja) 液晶性ウレタン化合物、熱応答性液晶ポリウレタンエラストマー及びその製造方法
TWI645971B (zh) 用於經強化之結合的彈性纖維
WO2018047389A1 (fr) Matériau textile à cristaux liquides et produit textile
JP7008480B2 (ja) 熱応答性布帛
JP2019090138A (ja) 熱応答性布帛
JP2019090137A (ja) 熱応答性布帛
JP6937228B2 (ja) 熱応答性布帛
JP6757135B2 (ja) 熱応答性材料、並びに、熱応答性材料を用いた熱制御装置及び繊維
JP6237113B2 (ja) ポリウレタンエラストマー、及び弾性繊維
JP6622082B2 (ja) 熱応答性材料、並びに、熱応答性材料を用いた熱制御装置及び繊維
JP3658733B2 (ja) 耐久性ポリウレタン繊維およびその製造方法
WO2017149640A1 (fr) Composé cristallin liquide, matériau sensible à la chaleur et procédé pour sa production
EP1846470A1 (fr) Matiere polymere a resistance a la traction hautement reactive a deux stimuli externes
JP2019112605A (ja) 液晶性ポリマー、及び液晶性ポリマーの製造方法
JP6150226B2 (ja) ポリウレタン弾性繊維、その製造方法、および弾性布帛
EP1273606A1 (fr) Polyurethanne et fibre elastique en polyurethanne
JP2019112606A (ja) シリコーン含有液晶性ポリマー、及びシリコーン含有液晶性ポリマーの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17848336

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018538011

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17848336

Country of ref document: EP

Kind code of ref document: A1