Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F120/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride, ester, amide, imide or nitrile thereof
  • C08F120/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F120/10—Esters
  • C08F120/12—Esters of monohydric alcohols or phenols
  • C08F120/14—Methyl esters, e.g. methyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F130/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing phosphorus, selenium, tellurium or a metal
  • C08F130/04—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing phosphorus, selenium, tellurium or a metal containing a metal
  • C08F130/08—Homopolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing phosphorus, selenium, tellurium or a metal containing a metal containing silicon
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/26—Esters containing oxygen in addition to the carboxy oxygen
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F230/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing phosphorus, selenium, tellurium or a metal
  • C08F230/04—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing phosphorus, selenium, tellurium or a metal containing a metal
  • C08F230/08—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and containing phosphorus, selenium, tellurium or a metal containing a metal containing silicon
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F299/00—Macromolecular compounds obtained by interreacting polymers involving only carbon-to-carbon unsaturated bond reactions, in the absence of non-macromolecular monomers
  • C08F299/02—Macromolecular compounds obtained by interreacting polymers involving only carbon-to-carbon unsaturated bond reactions, in the absence of non-macromolecular monomers from unsaturated polycondensates
  • C08F299/08—Macromolecular compounds obtained by interreacting polymers involving only carbon-to-carbon unsaturated bond reactions, in the absence of non-macromolecular monomers from unsaturated polycondensates from polysiloxanes
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/04—Azo-compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
  • C08F8/42—Introducing metal atoms or metal-containing groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/08—Processes
  • C08G18/16—Catalysts
  • C08G18/22—Catalysts containing metal compounds
  • C08G18/24—Catalysts containing metal compounds of tin
  • C08G18/244—Catalysts containing metal compounds of tin tin salts of carboxylic acids
  • C08G18/246—Catalysts containing metal compounds of tin tin salts of carboxylic acids containing also tin-carbon bonds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/71—Monoisocyanates or monoisothiocyanates
  • C08G18/718—Monoisocyanates or monoisothiocyanates containing silicon
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/80—Masked polyisocyanates
  • C08G18/8061—Masked polyisocyanates masked with compounds having only one group containing active hydrogen
  • C08G18/8093—Compounds containing active methylene groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/81—Unsaturated isocyanates or isothiocyanates
  • C08G18/8108—Unsaturated isocyanates or isothiocyanates having only one isocyanate or isothiocyanate group
  • C08G18/8116—Unsaturated isocyanates or isothiocyanates having only one isocyanate or isothiocyanate group esters of acrylic or alkylacrylic acid having only one isocyanate or isothiocyanate group
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/83—Chemically modified polymers
  • C08G18/837—Chemically modified polymers by silicon containing compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G77/00—Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
  • C08G77/42—Block-or graft-polymers containing polysiloxane sequences
  • C08G77/442—Block-or graft-polymers containing polysiloxane sequences containing vinyl polymer sequences
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G81/00—Macromolecular compounds obtained by interreacting polymers in the absence of monomers, e.g. block polymers
  • C08G81/02—Macromolecular compounds obtained by interreacting polymers in the absence of monomers, e.g. block polymers at least one of the polymers being obtained by reactions involving only carbon-to-carbon unsaturated bonds
  • C08G81/024—Block or graft polymers containing sequences of polymers of C08C or C08F and of polymers of C08G

Definitions

• the invention relates to novel polyacrylate-polysilane block copolymers.
• the invention also relates to methods of preparation of the polyacrylate-polysilane block copolymers. Description of the Related Art:
• Acrylate-based polymers are widely used for applications in adhesives, sealants and in coatings since they are relatively low-cost.
• One particular advantage of acrylate-based polymers is its compatibility with other polymers such as olefin- based polymers or copolymers like polypropylene.
• Silane-based polymers are relatively more expensive. They are non-compatible with many of the polymers. However, they have excellent thermo-oxidative stability, low surface energy and find applications as additives in coatings and plastics.
• Copolymers of polyacrylate and Si-based monomers are known.
• US-20151 19536 A1 and US-2013012653 A1 describe silicone-acrylic copolymers prepared by reacting a mixture of a silicone polymer and mixtures of acrylic monomers with a radical initiator and a scrambling catalyst.
• US-20151 19526 A1 discloses an acrylic modified polyorganosiloxane obtained by emulsion and graft polymerisation of a mixture comprising polyorganosiloxane, a methacrylate monomer and a copolymerisable monomer having a carboxyl, amide, hydroxyl or vinyl functional group.
• JPH-02258815 A describes a copolymer obtained by copolymerising triorganosilyl (meth)acrylate with a triorganosiloxysilylalkylene group-containing (meth)acrylate.
• Block copolymers are a special class of copolymers that are made of blocks of different polymerized monomeric units.
• the block copolymers can combine the properties of the individual polymer types within themselves and are therefore very interesting for many applications. Therefore, it is desirable to provide a block copolymer that advantageously combines properties of both acrylate as well as silane polymers.
• the present invention provides a polyacrylate-polysilane block copolymer of the general formula (I)
• n and n independent of one another are integers ranging from 2 to
• p is an integer ranging from 0 to 5;
• R 1 represents hydrogen, straight-chain or branched alkyl group having 1 to 4 carbon atoms
• R 2 represents hydrogen, straight-chain or branched alkyl group having 1 to 18 carbon atoms
• R 3 represents hydrogen, hydroxyl group, straight-chain or
• L is a single bond or bivalent group -NH-, -C(O)NH-,
• R 4 , R 5 and R 6 independent of one another, represent hydrogen, straight-chain or branched alkyl group having 1 to 8 carbon atoms or a polydimethylsiloxane residue;
• R 7 represents hydrogen or methyl group.
• n represents the degree of polymerization of the polyacrylate block (A) of the polyacrylate-polysilane block copolymer of formula (I). In a preferred embodiment, n is in a range of from 10 to 3000, more preferably from 50 to 2500, most preferably from 100 to 1000.
• m represents the degree of polymerization of the polysilane block (B) of the polyacrylate-polysilane block copolymer of formula (I).
• m is in a range of 10 to 3000, more preferably from 50 to 2500, most preferably from 100 to 1000.
• Preferred R 1 groups include hydrogen, methyl, ethyl, propyl, isopropyl, butyl, iso-butyl, more preferred are hydrogen, methyl and ethyl.
• R 2 groups include hydrogen, methyl, ethyl, propyl, isopropyl, butyl, iso-butyl, more preferred are hydrogen, methyl and ethyl.
• R 1 is hydrogen and R 2 is hydrogen.
• R 1 is methyl and R 2 is hydrogen.
• p is an integer ranging from 0 to 3, more preferably p is 0 or 1 , most preferred p is 0.
• q is an integer ranging from 1 to 3, more preferably q is 1 or 2, most preferably q is 1 .
• p is 1 and q is 1 .
• m is in a range of 100 to 2200
• n is in a range of 100 to 2200
• p is in a range of 0 to 3
• q is in a range of 1 to 3.
• R 3 represents hydrogen, straight-chain or branched alkyl group having 1 to 4 carbon atoms, or a C6-Cio-aryl group, e.g phenyl or naphthyl. Most preferred, R 3 is hydrogen.
• L represents a -CH2- group.
• R 4 , R 5 and R 6 are hydrogen, straight-chain or branched alkyl group having 1 to 6 carbon atoms or a polydimethylsiloxane residue.
• R 7 is methyl group.
• At least one of the groups R 4 , R 5 and R 6 represent a polydimethylsiloxane residue.
• Polydimethylsiloxane has the formula (II)
• x ranges from 6.5 to 4054 such that a number average molecular weight in a range of about 500 g/mole to about 300,000 g/mole results.
• the number average molecular weight of PDMS is from 500 g/mole to 20,000 g/mole.
• the weight ratio of PDMS to the total weight of polyacrylate-polysilane block copolymer of formula (I) is in a range of 1 :2.8 to 1 :24023.
• Another aspect of the present invention is a method to prepare a polyacrylate- polysilane block copolymer of formula (I) comprising polymerizing an acrylate polymer of formula "block (A)” and a silane polymer of formula "block (B)” in the presence of an initiator and at a reaction temperature of at most 120 °C.
• the number average molecular weight of polyacrylate block A is preferably in a range of 400 g/mole to 3.04 million g/mole, more preferably of 10,000 to
• the number average molecular weight of polysilane block B is preferably in a range of 490 g/mole to 7,204 million g/mole, more preferably of 24,500 to
• the weight ratio of the polyacrylate block A to the polysilane block B in preparing the polyacrylate-polysilane block copolymer of formula (I) is in a range of 1 :1 .8 x 10 7 to 6204:1 .
• the polyacrylate-polysilane block copolymer has a number average molecular weight in a range of about 890 g/mole to about 7,207 million g/mole.
• the polyacrylate block (A) is formed by polymerizing an acrylate monomer in a first reaction mixture.
• the polymerization can be carried out by a solution, bulk, suspension or emulsion polymerization process.
• Suitable acrylate monomers include for example, Ci to Cis straight chain or branched a Iky I esters of methacrylic acid, including methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, octyl methacrylate, lauryl methacrylate, stearyl methacrylate; acrylate esters, such as Ci to Cis straight chain or branched alkyl esters of acrylic acid, including methyl acrylate, ethyl acrylate, n-butyl acrylate and 2-ethylhexyl acrylate.
• the first reaction mixture may optionally contain a solvent such as water, acetone, methanol, isopropanol, tetrahydrofuran (THF), chloroform, acetone,
• a solvent such as water, acetone, methanol, isopropanol, tetrahydrofuran (THF), chloroform, acetone,
• the polymerization of the acrylate monomer may be in the presence of an initiator.
• the initiator is preferably selected based on such parameters as its solubility in one or more of the other components (e.g., monomer, solvent); half-life at the desired polymerization temperature (preferably a half-life within the range of from about 30 minutes to about 10 hours), and stability.
• initiators include azo compounds such as 2,2'-azobis (isobutyronitrile), 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis [2-methyl-N-(1 ,1 -bis(hydroxymethyl)-2-(hydroxyethyl)]- propionamide, and 2,2'-azobis [2-methyl-N-(2-hydroxyethyl)]-propionamide;
• azo compounds such as 2,2'-azobis (isobutyronitrile), 4,4'-azobis(4-cyanovaleric acid), 2,2'-azobis [2-methyl-N-(1 ,1 -bis(hydroxymethyl)-2-(hydroxyethyl)]- propionamide, and 2,2'-azobis [2-methyl-N-(2-hydroxyethyl)]-propionamide;
• peroxides such as t-butyl hydroperoxide, benzoyl peroxide; sodium, potassium, or ammonium persulphate or combinations thereof.
• Redox initiator systems may also be used, such as for example persulphate or peroxide in combination with a reducing agent such as sodium metabisulphite, sodium bisulfite, sodium
• the concentration of initiator used during the polymerization process is preferably chosen to obtain the desired degree of polymerization.
• the concentration of initiator used during the polymerization process is preferably chosen to obtain the desired degree of polymerization.
• the concentration of initiator used during the polymerization process is preferably chosen to obtain the desired degree of polymerization.
• the concentration of initiator used during the polymerization process is preferably chosen to obtain the desired degree of polymerization.
• the concentration of initiator used during the polymerization process is preferably chosen to obtain the desired degree of polymerization.
• the concentration of initiator used during the polymerization process is preferably chosen to obtain the desired degree of polymerization.
• the concentration of the initiator is from 0.2 weight percent to 3 weight percent, and more preferably from 0.5 weight percent to 1 .5 weight percent, based on the weight of the monomer.
• the first reaction mixture may additionally include catalysts, such as for example a transition metal chelate complex.
• the transition metal chelate complex is a cobalt (II) or (III) chelate complex such as, for example, dioxime complexes of cobalt (II), cobalt (II) porphyrin complexes, or cobalt (II) chelates of vicinal iminohydroxyimino compounds, dihydroxyimino compounds, diazadihydroxy- iminodialkyldecadienes, or diazadihydroxyiminodialkylundecadienes, or
• Said first reaction mixture is expediently heated to a temperature of 20 to 150 °C, preferably to 50 °C to 80 °C.
• the reaction may be continued for a time period of 1 to 5 hours.
• the solids level at the completion of the polymerization is typically from 5 weight percent to 70 weight percent, and more preferably from 30 weight percent to 60 weight percent, based on the total weight of the aqueous emulsion or suspension.
• a silane monomer is polymerized to form the polysilane block (B) of the block copolymer of formula (I).
• silane monomers examples include (3-Acryloxypropyl)tris(trimethylsiloxy)-silane; reaction product of 2-hydroxyethyl acrylate with 3-isocyanatopropyltriethoxysilane; reaction product of
• 3-aminopropyltrimethoxysilane with glycidyl methacrylate reaction product of 3-aminopropyltriethoxysilane with glycidyl methacrylate , reaction product of acrylic acid with (3-aminopropyl)trimethoxysilane; reaction product of acrylic acid with (3-aminopropyl)triethoxysilane; reaction product of methacryloyloxyethyl isocyanate with (3-aminopropyl)trimethoxysilane; or reaction product of
• first reaction mixture and “second reaction mixture” is not be construed as having any restriction on the sequence of reaction process as they may be interchangeable.
• second reaction mixture may be reacted prior to first reaction mixture.
• Said second reaction mixture optionally contains a solvent, such as water, acetone, methanol, isopropanol, THF, chloroform, dimethylformamide,
• a solvent such as water, acetone, methanol, isopropanol, THF, chloroform, dimethylformamide,
• polymerization of the silane monomer may be in the presence of an initiator.
• Suitable initiators are those described previously with respect to the first reaction mixture.
• the concentration of initiator in the second reaction mixture is from 0.2 weight percent to 3 weight percent, and more preferably from 0.5 weight percent to 1 .5 weight percent, based on the total weight of the silane monomer.
• the second reaction mixture may additionally include catalysts as mentioned previously with respect to first reaction mixture.
• the second reaction mixture is heated to a temperature in a range of about 40 °C to 75 °C, more preferably to 50 to 65 °C.
• the reaction may be continued for a time period ranging from 1 to 4 hours.
• the polymerization reaction to form the polyacrylate-polysilane block copolymer of general formula (I) can be carried out by a solution, bulk, suspension or emulsion polymerization process.
• the polymerization process can be a continuous process, a batch or a semi-batch process.
• the acrylate polymer block A and the silane polymer block B are expediently polymerized in the presence of an initiator and at a reaction temperature of 40 to 120 °C, preferably of 50 to 80 °C. In one
• the polymerization is performed by solution polymerization. In another embodiment, the polymerization is performed by bulk polymerization. The reaction may be continued for a time period of up to 5 hours, preferably of 1 to 5 hours.
• the polysilane block (B) of the block copolymer of formula (I) is grafted with at least one polydimethylsiloxane (PDMS) group.
• PDMS polydimethylsiloxane
• PDMS monomer such as hydroxyl-terminated PDMS is reacted with polysilane block B in the presence of a graft polymerization catalyst to form PDMS grafted polysilane block B.
• grafting of PDMS is carried out after the polymerization reaction between polyacrylate block A and polysilane block B to form the polyacrylate-polysilane block copolymer of general formula (I).
• the graft polymerization may be performed in the presence of a solvent.
• solvents include water, acetone, methanol, isopropanol, tetrahydrofuran (THF), chloroform, acetone, dimethylformamide, dimethylsulfoxide,
• the graft polymerization reaction may be initiated by means of an initiator.
• Suitable initiators include those described previously with respect to first reaction mixture.
• Examples of graft polymerization catalysts are those selected from the group comprising of organic bases, carboxylic acids and organometallic compounds including organic titanates and complexes or carboxylates of lead, cobalt, iron, nickel, zinc and tin.
• catalysts examples include dibutyltin dilaurate (DBTL), dibutyltin dioctoate, dibutyltin diacetate, stannuous octoate, stannous oleate, lead octoate, zinc 2-ethylhexoate, cobalt naphthenate, cobalt octoate, iron
• 2-ethylhexoate bis(acetylacetonyl)di-isopropyl titanate, di-isopropoxy titanium di(ethylacetoacetate), tetrabutyl titanate, tetranonyl titanate, ethylene glycol titanate, tetrabutyl zirconate, ethylamine, hexylamine, dibutylamine, piperidine, ethylene diamine, octadecylamine acetate, p-toluene sulphonic acid and acetic acid.
• the preferred catalysts are organic tin compounds, e.g. dibutyltin dilaurate and dibutyltin diacetate.
• the catalyst is preferably added in an amount of from about 0.01 to about 1 percent by weight, more preferably about 0.05 to about 0.5 percent by weight, and most preferably about 0.1 to 0.2 percent by weight of the component polymers.
• the graft polymerization reaction mixture is heated to a temperature in a range of about 40 °C to 75 °C, more preferably to 50 to 65 °C.
• the reaction may be continued for a time period ranging from 1 to 5 hours, preferably from 1 to 3 hours.
• the polyacrylate-polysilane block copolymers may enhance surface appearance with respect to less scratching of a polymer due to the low surface energy of the polysilane block and at the same time have good compatibilty with other polymers due to the polyacrylate block.
• the inventive block copolymer may enhance the scratch-resistance of a polymer, such as polyolefin, when blended therewith.
• a glass transition temperature (Tg) of a polymer is the
• Tg temperatures below Tg to a fluid or rubbery state at temperatures above Tg.
• the Tg of a polymer is typically measured by differential scanning calorimetry (DSC) using the mid-point in the heat flow versus temperature transition as the Tg value.
• DSC differential scanning calorimetry
• one Tg can be measured, or calculated, for the phase formed by the polyacrylate block, and another Tg for the phase formed by the polysilane block.
• An "average Tg", or “overall Tg” may be calculated for such systems as a weighted average of the amount of polymer in each phase of a given Tg.
• the molecular weight of synthetic polymers are almost always a mixture of chains varying in molecular weight, i.e., there is a "molecular weight distribution" as referred by polydispersity. Given that there is a distribution of molecular weights, the most complete characterization of the molecular weight of a given sample is the determination of the entire molecular weight distribution. This characterization is obtained by separating the members of the distribution and then quantitating the amount of each that is present. As used herein, the terms “number average molecular weight (M n )" and “weight average molecular weight (M w )" are
• a three-necked round bottom (RB) flask was attached with a condenser and a Schlenk line for purging with nitrogen.
• the RB flask was placed over a stirrer and a hot plate with heat on block. Nitrogen gas was flushed through preheated and dried RB flask to remove any moisture content prior to polymerization.
• MMA methyl methacrylate
• ml_ tetrahydrofuran
• reaction mixture containing silane polymer of Example 1 a was taken under inert atmosphere and added to the flask of Example 1 b.
• the reaction was continued for further 1 hour and then about 10 g of polydimethylsiloxane (PDMS Mn 500 g/mole) was added to the RB flask along with 0.2 g of dibutyltin dilaurate (DBTDL).
• PDMS Mn 500 g/mole polydimethylsiloxane
• DBTDL dibutyltin dilaurate
• the reaction was continued for further 2 hours and precipitated out in excess methanol.
• the resulting product was then filtered and dried in vacuum oven at 40°C for 24 hours to remove traces of methanol from the product.
• the block copolymer product thus obtained was then weighed to get a yield of 89 % and used for further characterisation.
• the block copolymer formation is confirmed by NMR from the appearance of peak at ⁇ 0.3-0.0 corresponding to [Si-Chb].
• the molecular weight analysis of block copolymer was performed in chloroform solvent using GPC with polystyrene standards and is listed in Table 1
• the block copolymer has a weight average molecular weight (M w ) of 240,000, a number average molecular weight (M n ) of 105,000 and a polydispersity of 2.3 as shown in Table 1 .
• Tg of the polymer was recorded using DSC (Perkin Elmer DSC 6000) at a heating rate of 10 °C/min.
• the block copolymer exhibits two Tg (the first Tg corresponding to PDMS appear at around 50 °C to 70 °C and the second Tg corresponding to acrylate appear between 140 °C and 150 °C.
• the TGA (Thermogravimetric Analysis) of the block copolymer was measured using Perkin Elmer TGA 4000 to know the degradation temperature. A sample of the block copolymer was heated under nitrogen atmosphere and the heating was continued to a temperature of up to 700 °C at the rate of 20 °C per minute. The TGA of the block copolymer shows onset of degradation at a temperature of 250 °C which indicates the suitability of these block polymers in conventional polymer processing methods.
• Example 2a The product from Example 2a is added under inert condition to the RB flask of Example 2b and the reaction is continued for one more hour. About 7.5 g of PDMS (Mn 500 g/mole) along with 0.18g of DBTDL is added to the reaction mixture and the reaction is continued for two more hours. At the end of the reaction, the block copolymer product is precipitated in excess of methanol and dried.
• the product can be characterized by NMR, DSC and TGA.
• Acrylic acid 7.2 g was taken in a RB Flask containing 100 ml of toluene attached to Dean stark apparatus. 1 -octanol (13 g) was added to it along with 0.2 g of para toluene sulphonic acid (PTSA). The reaction mixture was refluxed. The completion of reaction was marked by the disappearance of the hydroxyl peak of 1 -octanol between 3200-3400 cm -1 by IR spectroscopy. The reaction was stopped after 4 hours following the disappearance of hydroxyl peak. The reaction product was dissolved in dichloromethane and washed with water. It was dried over anydrous sodium sulphate and concentrated using rotavapor.
• PTSA para toluene sulphonic acid
• Example 3b To the product of Example 3b was added 2.7 g of product of Example 3a under nitrogen atmosphere. The reaction was continued for 1 hour. About 2.7 g of PDMS (Mn 500 g/mole) along with 0.05 g of DBTDL was added to the reaction mixture with continued heating for 2 hours. The reaction mixture was cooled down and precipitated in excess methanol, filtered, dried and used for further

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• General Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Graft Or Block Polymers (AREA)
• Other Resins Obtained By Reactions Not Involving Carbon-To-Carbon Unsaturated Bonds (AREA)
• Silicon Polymers (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Macromonomer-Based Addition Polymer (AREA)

Priority Applications (12)

Applications Claiming Priority (2)

Publications (1)

Family

ID=56555224

Family Applications (1)

Country Status (14)

Families Citing this family (4)

Citations (7)

Family Cites Families (14)

• 2016
  • 2016-07-27 EP EP16181390.2A patent/EP3275909A1/en not_active Withdrawn
• 2017
  • 2017-06-21 TW TW106120788A patent/TWI803464B/zh active
  • 2017-07-17 JP JP2019503522A patent/JP7068269B2/ja active Active
  • 2017-07-17 SG SG11201811317UA patent/SG11201811317UA/en unknown
  • 2017-07-17 EP EP17740019.9A patent/EP3491035B1/en active Active
  • 2017-07-17 CN CN201780046182.8A patent/CN109563211B/zh active Active
  • 2017-07-17 US US16/320,594 patent/US10968321B2/en active Active
  • 2017-07-17 BR BR112019000358-4A patent/BR112019000358B1/pt active IP Right Grant
  • 2017-07-17 PL PL17740019T patent/PL3491035T3/pl unknown
  • 2017-07-17 KR KR1020197005613A patent/KR102385976B1/ko active Active
  • 2017-07-17 MX MX2019001091A patent/MX2019001091A/es unknown
  • 2017-07-17 ES ES17740019T patent/ES2910984T3/es active Active
  • 2017-07-17 RU RU2019105172A patent/RU2019105172A/ru unknown
  • 2017-07-17 WO PCT/EP2017/068048 patent/WO2018019642A1/en not_active Ceased
  • 2017-07-17 CA CA3030061A patent/CA3030061C/en active Active

Patent Citations (8)

Also Published As

Similar Documents

Legal Events