WO2017122916A1 - Liant sans ciment et son application - Google Patents

Liant sans ciment et son application Download PDF

Info

Publication number
WO2017122916A1
WO2017122916A1 PCT/KR2016/012775 KR2016012775W WO2017122916A1 WO 2017122916 A1 WO2017122916 A1 WO 2017122916A1 KR 2016012775 W KR2016012775 W KR 2016012775W WO 2017122916 A1 WO2017122916 A1 WO 2017122916A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
cement
binder
concrete
parts
Prior art date
Application number
PCT/KR2016/012775
Other languages
English (en)
Korean (ko)
Inventor
오재은
전동호
Original Assignee
울산과학기술원
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 울산과학기술원 filed Critical 울산과학기술원
Priority to CN201680078357.9A priority Critical patent/CN108473373A/zh
Priority to RU2018129097A priority patent/RU2705646C1/ru
Publication of WO2017122916A1 publication Critical patent/WO2017122916A1/fr

Abstract

La présente invention concerne un liant sans ciment et une application associée. Plus précisément, la présente invention concerne un liant sans ciment respectueux de l'environnement comprenant des cendres volantes, de l'oxyde de calcium et du chlorure de calcium dans une formulation particulière. Le liant sans ciment peut être utilisé et appliqué comme mortier et béton présentant un faible coût, une haute résistance, un poids léger et des performances d'adsorption des métaux lourds et d'absorption sonore, et peut ainsi avoir des effets économiques importants.
PCT/KR2016/012775 2016-01-11 2016-11-08 Liant sans ciment et son application WO2017122916A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201680078357.9A CN108473373A (zh) 2016-01-11 2016-11-08 无水泥粘合剂及其应用
RU2018129097A RU2705646C1 (ru) 2016-01-11 2016-11-08 Бесцементное вяжущее вещество и его применение

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020160003160A KR101773961B1 (ko) 2016-01-11 2016-01-11 무시멘트 결합재 및 이의 응용
KR10-2016-0003160 2016-01-11

Publications (1)

Publication Number Publication Date
WO2017122916A1 true WO2017122916A1 (fr) 2017-07-20

Family

ID=59311720

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2016/012775 WO2017122916A1 (fr) 2016-01-11 2016-11-08 Liant sans ciment et son application

Country Status (4)

Country Link
KR (1) KR101773961B1 (fr)
CN (1) CN108473373A (fr)
RU (1) RU2705646C1 (fr)
WO (1) WO2017122916A1 (fr)

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101982087B1 (ko) * 2017-07-25 2019-06-03 주식회사 하우이씨엠 바텀애쉬를 이용한 층간소음 방지보드 제조 방법 및 이에 의해 제조된 층간소음 방지보드
WO2019112079A1 (fr) * 2017-12-05 2019-06-13 한양대학교 에리카산학협력단 Structure de liant activé par un alcali comprenant une résine échangeuse d'ions, et son procédé de fabrication
KR102100404B1 (ko) * 2018-06-27 2020-04-13 울산과학기술원 백색 경화체 및 이를 제조하기 위한 조성물
KR102041733B1 (ko) * 2018-12-05 2019-11-08 한국석회석신소재연구재단 순환유동층연소 비산재를 이용한 칼슘계 배연탈황 흡수제 및 이의 제조방법
US11414353B2 (en) 2019-04-23 2022-08-16 King Fahd University Of Petroleum And Minerals Room temperature cured green concrete derived from natural pozzolan and nanosilica
CN111704433A (zh) * 2020-07-02 2020-09-25 中国海洋石油集团有限公司 一种复合固化剂及应用
KR102265152B1 (ko) 2020-11-05 2021-06-15 주식회사 위드엠텍 건설용 친환경 결합재 조성물
CN113860784A (zh) * 2021-11-02 2021-12-31 惠州市惠政新材料科技有限公司 粉料掺合剂及含有粉料掺合剂的混凝土

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20090070404A (ko) * 2007-12-27 2009-07-01 전남대학교산학협력단 환원슬래그를 이용한 혼합시멘트 제조
KR20140008060A (ko) * 2012-07-10 2014-01-21 한일시멘트 (주) 고로슬래그와 플라이애쉬 기반 무시멘트 조성물 및 이를 이용한 건조 모르타르 제조방법
KR101366003B1 (ko) * 2013-04-26 2014-02-25 한일에코산업 주식회사 무시멘트 결합재를 사용한 콘크리트 블록
KR20150129350A (ko) * 2014-05-12 2015-11-20 주식회사에스피엠 친환경 무시멘트 결합재 조성물
KR20160001348A (ko) * 2014-06-27 2016-01-06 현대제철 주식회사 무시멘트 결합재 및 이의 제조방법

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1081140A (zh) * 1993-09-09 1994-01-26 武汉工业大学 高性能无水泥粉煤灰双免砖
RU2101251C1 (ru) * 1995-08-15 1998-01-10 Акционерное общество открытого типа Сибирская научно-производственная инвестиционная фирма строительных материалов Бетонная смесь
US20060070406A1 (en) * 2004-09-28 2006-04-06 Orgyr Technologies Ltd. Use of coal ash for the safe disposal of mineral waste
CN1654402A (zh) * 2005-02-25 2005-08-17 黄振利 蒸煮粉煤灰膏及其制备方法
NL1031142C2 (nl) * 2006-02-14 2007-08-16 Mega Tech Holding Bv Bindmiddelsamenstelling, constructiesamenstelling omvattende deze bindmiddelsamenstelling evenals werkwijze voor de bereiding van de constructiesamenstelling en toepassing hiervan.
RU2379262C1 (ru) * 2008-07-24 2010-01-20 Государственное образовательное учреждение высшего профессионального образования "Тверской государственный технический университет" Состав для получения неавтоклавного газобетона и способ его приготовления
CN101829668B (zh) * 2010-05-28 2012-06-20 济南市琦泉热电有限责任公司 利用循环流化床锅炉灰渣生产高强度复合灰的工艺
KR101296591B1 (ko) * 2012-04-20 2013-08-14 오스템임플란트 주식회사 치과용 임플란트 표면의 ｈａ 코팅층 후처리 장치
KR101296159B1 (ko) * 2013-03-13 2013-08-28 국보환경(주) 폐아스콘과 무시멘트 결합재를 사용한 기층용 상온 재생아스팔트 조성물 및 포장방법

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20090070404A (ko) * 2007-12-27 2009-07-01 전남대학교산학협력단 환원슬래그를 이용한 혼합시멘트 제조
KR20140008060A (ko) * 2012-07-10 2014-01-21 한일시멘트 (주) 고로슬래그와 플라이애쉬 기반 무시멘트 조성물 및 이를 이용한 건조 모르타르 제조방법
KR101366003B1 (ko) * 2013-04-26 2014-02-25 한일에코산업 주식회사 무시멘트 결합재를 사용한 콘크리트 블록
KR20150129350A (ko) * 2014-05-12 2015-11-20 주식회사에스피엠 친환경 무시멘트 결합재 조성물
KR20160001348A (ko) * 2014-06-27 2016-01-06 현대제철 주식회사 무시멘트 결합재 및 이의 제조방법

Also Published As

Publication number Publication date
KR101773961B1 (ko) 2017-09-04
KR20170083818A (ko) 2017-07-19
CN108473373A (zh) 2018-08-31
RU2705646C1 (ru) 2019-11-11

Similar Documents

Publication Publication Date Title
WO2017122916A1 (fr) Liant sans ciment et son application
Muraleedharan et al. Factors affecting the mechanical properties and microstructure of geopolymers from red mud and granite waste powder: A review
US6482258B2 (en) Fly ash composition for use in concrete mix
WO2016072622A2 (fr) Adjuvant accélérateur sans ciment et composition sans ciment le comprenant
Okoye Geopolymer binder: A veritable alternative to Portland cement
WO2011087304A2 (fr) Matériau de liaison activé par des alcalis sans ciment et comprenant un activateur alcalin complexe, et mortier ou béton utilisant ce matériau
US6251178B1 (en) Fly ash composition
US10807911B2 (en) Concrete composition and production method therefor
Benabed et al. Experimental study on the reuse of cathode ray tubes funnel glass as fine aggregate for developing an ecological self-compacting mortar incorporating metakaolin
US8206503B2 (en) Method and composition for making a concrete product from sludge
KR101779565B1 (ko) 레미콘용 친환경 시멘트 콘크리트 조성물
CN108821692A (zh) 一种电弧炉钢渣制备的砂基透水砖及其制备方法
KR101859704B1 (ko) 염화칼슘이 첨가된 고로슬래그 기반의 무시멘트 결합재
KR101390132B1 (ko) 1종 조강형 시멘트를 사용한 고강도 콘크리트 조성물 및 콘크리트
WO2017131330A1 (fr) Agent solidifiant comprenant des coquilles d'huîtres traitées à l'acide sulfurique, et procédé de constitution utilisant ledit agent
US6997984B2 (en) Cement admixture
WO2017023050A1 (fr) Procédé de fabrication d'un composite de phosphate de magnésie à l'aide de poudre de laitier de ferronickel et composite de phosphate de magnésie fabriqué par un tel procédé à l'aide de poudre de laitier de ferronickel
WO2018155806A1 (fr) Composition de revêtement intérieur de mine
WO2010101412A2 (fr) Procédé de production d'agrégats artificiels légers à base de boues de laminage à chaud ou à froid
US20190308909A1 (en) Sintered ceramics
Sivaprasad et al. Effect of silica fume on steel slag concrete
KR100566948B1 (ko) 폐콘크리트의 재생 방법
JP5506367B2 (ja) 水硬性組成物
SU1502524A1 (ru) Бетонна смесь
JP4567504B2 (ja) 焼成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16885227

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16885227

Country of ref document: EP

Kind code of ref document: A1