WO2015163463A1 - 眼鏡レンズ - Google Patents
眼鏡レンズ Download PDFInfo
- Publication number
- WO2015163463A1 WO2015163463A1 PCT/JP2015/062596 JP2015062596W WO2015163463A1 WO 2015163463 A1 WO2015163463 A1 WO 2015163463A1 JP 2015062596 W JP2015062596 W JP 2015062596W WO 2015163463 A1 WO2015163463 A1 WO 2015163463A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- spectacle lens
- layer
- group
- hard coat
- lens
- Prior art date
Abstract
Description
特許文献3では、有機系の反射防止層を備え、耐光性の高いプラスチックレンズの製造方法を提供することを目的として、プラスチックレンズ基材の上に直に、又はプライマー層を挟んで、金属酸化物微粒子と有機ケイ素化合物とを、それらの重量比が0.6~1.2の範囲で含む、第1の組成物を塗布することによりハードコート層を形成する工程と、上記ハードコート層の表面に、有機ケイ素化合物を含む第2の組成物を塗布することにより反射防止層を形成する工程とを有するプラスチックレンズの製造方法が開示されている。
本発明は、優れた耐候性を有する、眼鏡レンズを提供することを課題とする。
[1]レンズ基材と、プライマー層と、ハードコート層とを有する眼鏡レンズであって、
ハードコート層の膜厚が10μm以上100μm以下であり、
プライマー層の膜厚が0.4μm以上2.0μm以下である、眼鏡レンズ。
[2]前記プライマー層の膜厚が、0.4μm以上1.2μm以下である、[1]に記載の眼鏡レンズ。
[3]前記プライマー層が、樹脂を含有する、[1]又は[2]に記載の眼鏡レンズ。
[4]前記プライマー層が、ポリウレタン樹脂を含有する、[3]に記載の眼鏡レンズ。
[5]前記プライマー層が、金属原子を含まない、[1]~[4]のいずれかに記載の眼鏡レンズ。
[6]前記ハードコート層が、無機酸化物粒子、ケイ素化合物を含む硬化性組成物を硬化して得られるものである、[1]~[5]のいずれかに記載の眼鏡レンズ。
本発明の眼鏡レンズは、ハードコート層の膜厚が10μm以上100μm以下であり、プライマー層の膜厚が0.4μm以上2.0μm以下である。
上記の構成を有することで、優れた耐候性を有する眼鏡レンズを得ることができる。
本発明者らは、プライマー層の膜厚を所定の範囲内とするとで、耐衝撃性を高めることができ、更に、優れた耐候性を兼ね備えた眼鏡レンズが得られることを見出した。すなわち、上記構成を有することで、優れた耐引掻傷性を有し、かつ、優れた耐衝撃性、並びに、優れた、耐温水クラック性及び耐QUV性等の耐候性を有する、眼鏡レンズを得ることができる。
プライマー層の膜厚は、上述の膜厚を有する優れた耐引掻傷性を示すハードコート層を有する眼鏡レンズにおいて優れた耐候性を得るため、2.0μm以下である。また当該範囲において耐引掻傷性を向上させることができるという効果も奏する。当該膜厚は、優れた耐候性及び耐引掻傷性の観点から、好ましくは1.2μm以下であり、優れた耐候性、耐引掻傷性及び干渉縞抑制の観点から、好ましくは0.9μm以下である。
以下、本発明の眼鏡レンズの構成について詳細に説明する。
レンズ基材は、眼鏡レンズのレンズ基材に使用される材料としては、例えば、ポリウレタン系材料(例えばポリウレタン、ポリウレタンウレア、ポリチオウレタン)、ポリカーボネート、ジエチレングリコールビスアリルカーボネート等のプラスチック、無機ガラス、等が挙げられる。レンズ基材の厚さ及び直径は、特に限定されるものではない。通常、厚さは1~30mm程度、直径は50~100mm程度である。本発明の眼鏡レンズが視力矯正用の眼鏡レンズの場合、レンズ基材としては、屈折率neが1.5~1.8程度のものを使用することが通常である。レンズ基材としては、通常無色のものが使用されるが、透明性を損なわない範囲で着色したものを使用することもできる。また、その上に硬化被膜が形成される基材の表面形状は特に限定されず、平面、凸面、凹面等の任意の形状であることができる。
本発明の眼鏡レンズにおいて、レンズ基材には、少なくともプライマー層、及びハードコート層を含む機能層が設けられる。ほかの機能層としては、干渉縞抑制層、偏光層、フォトクロミック層等を挙げることができる。また、当該ハードコート層の上に、更に必要に応じて、反射防止層、撥水膜、紫外線吸収膜、赤外線吸収膜、フォトクロミック膜、帯電防止膜等の機能層を設けることもできる。これらほかの機能層については、眼鏡レンズに関する公知技術を適用することができる。
また本発明の眼鏡レンズは、基材側から、干渉縞抑制層、プライマー層、ハードコート層の順に積層されていることが好ましく、基材側から、干渉縞抑制層、プライマー層、ハードコート層、反射防止層の順に積層されていることがより好ましい。
ハードコート層は、例えば、無機酸化物粒子(以下「成分(A)」ともいう)と、ケイ素化合物(以下「成分(B)」ともいう)とを含む硬化性組成物を硬化して得られる。硬化性組成物は、好ましくは成分(A)と、成分(B)と、多官能エポキシ化合物(以下「成分(C)」ともいう)とを含む。
加水分解性基としては、アルコキシ基、アリールオキシ基、ヒドロキシ基が挙げられ、好ましくはアルコキシ基である。
ケイ素化合物とは、好ましくは下記一般式(I)で表される有機ケイ素化合物又はその加水分解物である。
(R1)a(R3)bSi(OR2)4 - (a+b) ・・・(I)
R2で表されるアルキル基は、例えば直鎖又は分岐の炭素数1~4のアルキル基であって、具体例としては、メチル基、エチル基、プロピル基、ブチル基等が挙げられ、好ましくはメチル基又はエチル基である。
R2で表されるアシル基は、例えば、炭素数1~4のアシル基であって、具体例としては、アセチル基、プロピオニル基、オレイル基、ベンゾイル基等が挙げられる。
R2で表されるアリール基は、例えば炭素数6~10のアリール基であって、具体例としては、フェニル基、キシリル基、トリル基等が挙げられる。
R3で表されるアルキル基は、例えば直鎖又は分岐の炭素数1~6のアルキル基であって、具体例としては、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、ヘキシル基等が挙げられる。
R3で表されるアリール基としては、例えば炭素数6~10のアリール基であって、具体例としては、フェニル基、キシリル基、トリル基等が挙げられる。
成分(B)の含有量は、硬化性組成物の固形分中、好ましくは5質量%以上、より好ましくは10質量%以上、更に好ましくは15質量%以上であり、好ましくは80質量%以下、好ましくは70質量%以下、更に好ましくは60質量%以下である。
成分(C)の含有量は、硬化性組成物の固形分中、好ましくは0質量%以上、より好ましくは10質量%以上、更に好ましくは15質量%以上であり、好ましくは50質量%以下、より好ましくは40質量%以下、更に好ましくは30質量%以下である。
フィラー/マトリックス比(以下単に「F/M比」ともいう)は、好ましくは0.5以上、より好ましくは0.6以上、更に好ましくは0.7以上であり、また、好ましくは2.0以下、より好ましくは1.8以下、更に好ましくは1.5以下である。
なおF/M比とは、成分(B)と成分(C)の合計質量に対する、成分(A)の質量比[成分(A)/(成分(B)+成分(C))]を意味する。
プライマー層は、例えば、樹脂を含有する。プライマー層は、例えば、樹脂と水系溶媒を含有する水系樹脂組成物から形成される水系樹脂層である。
水系樹脂組成物に含まれる水系溶媒は、例えば、水、水と極性溶媒等との混合溶媒であり、好ましくは水である。水系樹脂組成物中の固形分濃度は、液安定性及び成膜性の観点から、好ましくは1~60質量%であり、より好ましくは5~40質量%である。
水系樹脂組成物は、樹脂のほかに、必要に応じて、酸化防止剤、分散剤、可塑剤等の添加剤を含むことも可能である。しかし、耐候性の観点から、金属原子を含有しないことが好ましい。当該金属原子としては、周期律表第3族から第13属までの元素が挙げられる。
また、市販されている水系樹脂組成物を、水、アルコール、プロピレングリコールモノメチルエーテル(PGM)等の溶媒で希釈して使用してもよい。
塗布方法としては、ディップ法、スピンコート法等の公知の塗布法を用いることができる。塗布条件は、所望の膜厚のプライマー層を形成できるように適宜設定すればよい。塗布前には、被塗布面である偏光膜表面に対し、酸、アルカリ、各種有機溶媒等による化学的処理、プラズマ、紫外線、オゾン等による物理的処理、各種洗剤を用いる洗剤処理を行うこともできる。このような前処理を行うことにより、密着性を向上させることができる。
水系樹脂組成物の塗工後、該組成物を乾燥させることによりプライマー層として水系樹脂層を形成することができる。上記乾燥は、例えば室温~100℃の雰囲気中に5分~24時間、プライマー層を形成した部材を配置することにより行うことができる。
干渉縞抑制層は、干渉縞を抑制するため、波長λが450~650nmの光における光学膜厚が、好ましくは0.2λ~0.3λである。
干渉縞抑制層は、例えば、無機酸化物粒子及び樹脂を少なくとも含有する分散液を塗工して得られる。
分散液は水系溶媒を含んでいてもよい。水系溶媒は、例えば、水、水と極性溶媒等との混合溶媒であり、好ましくは水である。水系樹脂組成物中の固形分濃度は、液安定性及び製膜性の観点から、好ましくは1~60質量%であり、より好ましくは5~40質量%である。水系樹脂組成物は、樹脂成分のほかに、必要に応じて、酸化防止剤、分散剤、可塑剤等の添加剤を含むことも可能である。また、市販されている水系樹脂組成物を、水、アルコール、プロピレングリコールモノメチルエーテル(PGM)等の溶媒で希釈して使用してもよい。
ハードコート層上に反射防止層を設けてもよい。反射防止層は、例えば、低屈折率層及び高屈折率層が交互に配置された構成を有する。反射防止層が有する層は、好ましくは4~10層、より好ましくは5~8層である。
低屈折率層の屈折率は、波長500~550nmで、好ましくは1.35~1.80、より好ましくは1.45~1.50である。低屈折率層は、無機酸化物からなり、好ましくはSiO2からなる。
高屈折率層の屈折率は、波長500~550nmで、好ましくは1.90~2.60であり、より好ましくは2.00~2.40である。
高屈折率層は、例えば、無機酸化物からなる。高屈折率層に用いられる無機酸化物としては、好ましくは、ZrO2、Ta2O5、Y2O3、TiO2、Nb2O5及びAl2O3の中から選ばれる少なくとも一種類の無機酸化物であり、より好ましくはZrO2又はTa2O5である。
ハードコート層が形成されたレンズ基材を用いて、光干渉法による非接触式膜厚測定器((株)システムロード製非接触式膜厚計測器FF8)により測定した。
レンズ中心部厚さが1.0mm(CTと記載する)で、レンズ度数パワ-が0.00D(ディオプター)のレンズで作製して、アメリカ食品医薬品局(FDA:Food and Drug Administration)で定められているドロップボールテストに準じた試験(127cmの高さから、重さ7gの鉄球を落下させた。)を行い、以下の基準で評価した。
A ドロップボールテスト前とレンズの外観が変わらない
B ドロップボールテスト後、レンズの表面に傷が生じた
C ドロップボールテスト後、レンズの表面にヒビ又は割れが生じた
眼鏡レンズの表面にカッターナイフで縦横に交差するように1cmの切り傷を入れ、60℃の温水に浸漬させ2時間ごとにクラックの発生を確認した。クラックの発生を確認した時間を記録した。
眼鏡レンズの表面にカッターナイフで縦横に交差するように1cmの切り傷を入れ、眼鏡レンズをQ-Lab社製QUV紫外線蛍光管式促進耐候試験機において、(1)0.77W紫外線照射を4時間行った後、(2)高湿度環境(湿度90%)下に4時間置いた。(1)(2)を一つのサイクルとして、100時間まで繰り返し、以下の基準で評価した。
5 全くなし
4 先端に1mm以下のクラック
3 先端に5mm以下のクラック
2 全体にクラック
1 全体が白くなる程度
連続荷重式表面測定機(新東科学(株)製Type22)を用いて、先端曲率半径が50μmのダイヤモンド針を装着して、眼鏡レンズとダイヤモンド針の当接荷重を1g/secで徐々に高めながら、10mm/secの速度で直線相対運度させて傷を形成した。蛍光灯下で目視において傷として認識され始める位置から、その荷重を求め「傷発生荷重」とし、当該傷を顕微鏡で確認して、眼鏡レンズの表面被膜が切削され始める位置から、その荷重を求め「膜剥離荷重」とした。
なお、表面被膜が切削されることで、形成される傷の色が白色を示す状態を示す。このように表面膜が切削されると肉眼でも目立つ傷となる。
製造時にクラックが発生した場合はF、製造時にクラックが発生しなかった場合にはPとして評価した。
眼鏡レンズ表面に1.5mm間隔で100目クロスカットし、このクロスカットしたところに粘着テープ(セロテープ(登録商標)、ニチバン(株)製)を強く貼り付けた後、粘着テープを急速に剥がした後の硬化膜の剥離の有無を調べた。
全く剥がれないものは100/100として、全て剥がれたものは0/100として評価した。
干渉縞は外観の目視結果とし、暗室で三波長蛍光灯のもとで、又は通常の室内で白色蛍光灯の下で、以下の基準で評価した。
5 暗室でも全く見えない
4 暗室において、レンズ全面でわずかに見える
3 暗室において、レンズ全面で見える
2 暗室において、レンズ全面で明らかに見える
1 通常の室内において、レンズ全面で明らかに見える
機械的強度試験(JIS静圧試験)JIS T 7331:2006に準拠して試験を行った。結果を以下の基準で評価した。
A 無傷
B ヒビ
C 貫通割れ
プラスチックレンズ基材(HOYA(株)製、眼鏡用プラスチックレンズ、商品名EYNOA、屈折率1.67)を洗浄した。
(プライマー層)
表1に示す成分を含有する混合物を20℃で24時間撹拌しプライマー液PR1を得た。
得られたプライマー液をディップ法にてプラスチックレンズ基材に塗布し、100℃で20分間乾燥固化することにより、レンズ基材両面にプライマー層を形成した。
(ハードコート層)
有機ケイ素化合物γ-グリシドキシプロピルトリメトキシシラン(信越化学工業(株)製KBM-403)8質量部にメタノールを溶媒として30質量部添加した。
これを10分間撹拌した後にpH調整剤として1mol/Lの硝酸を1.0質量部添加し、更に10分間撹拌した。こうして得られた溶液にシリカ粒子(シリカゾル、商品名PGM-ST、日産化学工業(株)製)10質量部(固形分基準)を添加し24時間室温で撹拌した。
24時間撹拌後、多官能エポキシ化合物(トリメチロールプロパンオイルグリシジルエーテル、2~3官能、商品名EX-321、ナガセケムテックス(株)製)6質量部と、硬化剤としてアルミニウムアセチルアセトナート1質量部とレベリング剤(東レ・ダウコーニング(株)製FZ-77)0.1質量部を添加し、更に48時間室温撹拌してハードコート液を調製した。
プライマー層を成膜したレンズ基材に、上記ハードコート液を、形成される硬化被膜の膜厚が20~40μmとなるようにスプレー法により塗布した。
その後、75℃20分の予備硬化、次いで110℃2時間の本硬化を行い両面にハードコート層を有する眼鏡レンズを作製した。
以上の工程により、レンズ基材の両面にそれぞれプライマー層を介してハードコート層を有する眼鏡レンズを得た。
(AR層)
次に、ハードコート層の上に、真空蒸着法にて、表に記載した層を交互に積層した反射防止層(AR層)を形成し、プラスチックレンズを得た。得られたプラスチックレンズについて評価し、それらの結果を以下の表に示す。
Claims (6)
- レンズ基材と、プライマー層と、ハードコート層とを有する眼鏡レンズであって、
ハードコート層の膜厚が10μm以上100μm以下であり、
プライマー層の膜厚が0.4μm以上2.0μm以下である、眼鏡レンズ。 - 前記プライマー層の膜厚が、0.4μm以上1.2μm以下である、請求項1に記載の眼鏡レンズ。
- 前記プライマー層が、樹脂を含有する、請求項1又は2に記載の眼鏡レンズ。
- 前記樹脂が、ポリウレタン樹脂を含有する、請求項3に記載の眼鏡レンズ。
- 前記プライマー層が、金属原子を含まない、請求項1~4のいずれかに記載の眼鏡レンズ。
- 前記ハードコート層が、無機酸化物粒子、ケイ素化合物を含む硬化性組成物を硬化して得られるものである、請求項1~5のいずれかに記載の眼鏡レンズ。