WO2015161732A1 - Procédé de préparation de poudre composite de cristaux de carbure de tungstène nanométriques revêtus de cobalt, et de carbure métallique à grains ultra-fins - Google Patents

Procédé de préparation de poudre composite de cristaux de carbure de tungstène nanométriques revêtus de cobalt, et de carbure métallique à grains ultra-fins Download PDF

Info

Publication number
WO2015161732A1
WO2015161732A1 PCT/CN2015/075305 CN2015075305W WO2015161732A1 WO 2015161732 A1 WO2015161732 A1 WO 2015161732A1 CN 2015075305 W CN2015075305 W CN 2015075305W WO 2015161732 A1 WO2015161732 A1 WO 2015161732A1
Authority
WO
WIPO (PCT)
Prior art keywords
cobalt
composite powder
tungsten
coated
powder
Prior art date
Application number
PCT/CN2015/075305
Other languages
English (en)
Chinese (zh)
Inventor
谭兴龙
邓军旺
王艳艳
李礼
Original Assignee
湖南顶立科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 湖南顶立科技有限公司 filed Critical 湖南顶立科技有限公司
Publication of WO2015161732A1 publication Critical patent/WO2015161732A1/fr

Abstract

L'invention concerne un procédé de préparation de poudre composite de cristaux de carbure de tungstène (CW) nanométriques revêtus de cobalt, consistant : (1) à mélanger des matières premières avec de l'eau pour obtenir une solution saline composite tungstène-cobalt, les matières premières comprenant les composants suivants (en pourcentage en poids), de 40 à 60% d'oxyde de tungstène violet, de 30 à 52% de sel de cobalt hydrosoluble, de 4 à 10% d'une source de carbone, de 1 à 4% de PEG et de 0,05 à 3% d'agent dispersant ; (2) à sécher la solution saline composite tungstène-cobalt obtenue à l'étape (1) afin d'obtenir une poudre précurseur revêtue de cobalt ; (3) à réduire et à carboniser la poudre précurseur revêtue de cobalt obtenue à l'étape (2), dans une atmosphère réductrice, afin d'obtenir la poudre composite de cristaux de CW nanométriques revêtue de cobalt. La poudre composite obtenue par la mise en oeuvre de ce procédé présente des performances stables, une composition homogène et une fine taille de grains de CW, et les composants de la poudre peuvent être facilement régulés.
PCT/CN2015/075305 2014-04-25 2015-03-27 Procédé de préparation de poudre composite de cristaux de carbure de tungstène nanométriques revêtus de cobalt, et de carbure métallique à grains ultra-fins WO2015161732A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201410171633.9A CN103909274B (zh) 2014-04-25 2014-04-25 一种制备钴包覆纳米wc晶体复合粉末及超细晶硬质合金的方法
CN201410171633.9 2014-04-25

Publications (1)

Publication Number Publication Date
WO2015161732A1 true WO2015161732A1 (fr) 2015-10-29

Family

ID=51035449

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2015/075305 WO2015161732A1 (fr) 2014-04-25 2015-03-27 Procédé de préparation de poudre composite de cristaux de carbure de tungstène nanométriques revêtus de cobalt, et de carbure métallique à grains ultra-fins

Country Status (2)

Country Link
CN (1) CN103909274B (fr)
WO (1) WO2015161732A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018051106A1 (fr) * 2016-09-14 2018-03-22 Metalysis Limited Procédé de production d'un matériau composite
WO2018051105A1 (fr) * 2016-09-14 2018-03-22 Metalysis Limited Procédé de production d'une poudre
CN111069618A (zh) * 2020-01-02 2020-04-28 崇义章源钨业股份有限公司 WC-Co复合粉末及其制备方法和应用
CN113184853A (zh) * 2021-05-26 2021-07-30 崇义章源钨业股份有限公司 超细碳化钨粉及其制备方法与应用
CN114360884A (zh) * 2021-12-31 2022-04-15 华南理工大学 一种适用于高频电感元件的高磁感低损耗梯度纳米晶磁粉芯及其制备方法与应用
CN114752799A (zh) * 2022-04-26 2022-07-15 江西理工大学 CNTs增强WC-Co硬质合金材料及其制备方法
CN116287829A (zh) * 2023-03-24 2023-06-23 承德天大钒业有限责任公司 一种铝钼碳合金及其制备方法

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103909274B (zh) * 2014-04-25 2016-06-15 湖南顶立科技有限公司 一种制备钴包覆纳米wc晶体复合粉末及超细晶硬质合金的方法
CN106424702B (zh) * 2016-09-12 2018-06-29 黑龙江北方工具有限公司 一种钨合金成形剂及其制备方法和应用
CN108941530A (zh) * 2017-05-27 2018-12-07 东莞华晶粉末冶金有限公司 硬质合金基喂料及其制备方法、硬质合金基坯体及其制备方法
CN108031856B (zh) * 2017-12-26 2021-02-12 江西理工大学 高钴纳米/超细WC-Co复合粉末的制备方法
CN108274005B (zh) * 2018-02-08 2019-09-13 合肥工业大学 一种以纳米WC-Co复合粉末制备低钴、超细晶硬质合金棒材的方法
CN111069619B (zh) * 2019-12-12 2023-04-07 湖南博云东方粉末冶金有限公司 一种特粗晶硬质合金混合料的制备方法
CN113857474A (zh) * 2021-09-01 2021-12-31 河海大学 一种添加Ce元素的WC表面包覆Co粉末制备方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998024576A1 (fr) * 1996-12-05 1998-06-11 The University Of Connecticut Metaux nanostructures, alliages metalliques, carbures metalliques et carbures d'alliages metalliques et synthese chimique des elements susmentionnes
WO2009001929A1 (fr) * 2007-06-27 2008-12-31 Kyocera Corporation Carbure cémenté, outil de coupe et dispositif de coupe
CN101811195A (zh) * 2010-04-22 2010-08-25 福建金鑫钨业股份有限公司 纳米WC-Co复合粉制备方法
CN102198514A (zh) * 2011-05-12 2011-09-28 中南大学 一种超细晶碳化钨/钴系复合粉的制备方法
CN102310199A (zh) * 2011-10-10 2012-01-11 西南大学 一种原位还原碳化制备WC-Co纳米复合粉的方法
CN103056381A (zh) * 2013-01-04 2013-04-24 安徽融达复合粉体科技有限公司 一种纳米碳化钨/钴复合粉末的制备方法
CN103909274A (zh) * 2014-04-25 2014-07-09 湖南顶立科技有限公司 一种制备钴包覆纳米wc晶体复合粉末及超细晶硬质合金的方法

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59185702A (ja) * 1983-04-06 1984-10-22 Mitsubishi Metal Corp 超硬合金製造用複合原料粉末およびその製造法
JPH10259433A (ja) * 1996-10-16 1998-09-29 Mitsubishi Materials Corp 高強度を有する微粒炭化タングステン基超硬合金の製造方法
JP3303187B2 (ja) * 1996-12-26 2002-07-15 三菱マテリアル株式会社 高強度を有する炭化タングステン基超硬合金の製造方法
CN1293215C (zh) * 2004-03-26 2007-01-03 武汉理工大学 碳化钨－钴纳米复合粉末的直接还原碳化制备方法
CN1990888A (zh) * 2005-12-27 2007-07-04 中南大学 具有纤维状wc晶体的钨钴硬质合金的制造方法
CN102758112A (zh) * 2012-08-10 2012-10-31 王永富 一种微纳米WC-Co硬质合金、其制备方法及应用
CN103056382B (zh) * 2013-01-04 2015-11-11 湖南顶立科技有限公司 一种纳米结构碳化钨/钴复合粉末的制备方法
CN103056376B (zh) * 2013-01-04 2015-04-08 湖南顶立科技有限公司 一种制备球形纳米结构碳化钨/钴复合粉末的方法
CN103056377B (zh) * 2013-01-04 2015-07-01 湖南顶立科技有限公司 一种纳米碳化钨/钴复合粉末的制备方法
CN103627942A (zh) * 2013-03-20 2014-03-12 厦门钨业股份有限公司 一种高性能WC-Co纳米晶硬质合金的制备方法
CN103447526A (zh) * 2013-09-11 2013-12-18 中南大学 一种纳米WC-Co复合粉末的制备方法
CN103710604B (zh) * 2013-12-27 2015-11-18 株洲硬质合金集团有限公司 一种硬质合金、制备方法及其应用

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998024576A1 (fr) * 1996-12-05 1998-06-11 The University Of Connecticut Metaux nanostructures, alliages metalliques, carbures metalliques et carbures d'alliages metalliques et synthese chimique des elements susmentionnes
WO2009001929A1 (fr) * 2007-06-27 2008-12-31 Kyocera Corporation Carbure cémenté, outil de coupe et dispositif de coupe
CN101811195A (zh) * 2010-04-22 2010-08-25 福建金鑫钨业股份有限公司 纳米WC-Co复合粉制备方法
CN102198514A (zh) * 2011-05-12 2011-09-28 中南大学 一种超细晶碳化钨/钴系复合粉的制备方法
CN102310199A (zh) * 2011-10-10 2012-01-11 西南大学 一种原位还原碳化制备WC-Co纳米复合粉的方法
CN103056381A (zh) * 2013-01-04 2013-04-24 安徽融达复合粉体科技有限公司 一种纳米碳化钨/钴复合粉末的制备方法
CN103909274A (zh) * 2014-04-25 2014-07-09 湖南顶立科技有限公司 一种制备钴包覆纳米wc晶体复合粉末及超细晶硬质合金的方法

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018051106A1 (fr) * 2016-09-14 2018-03-22 Metalysis Limited Procédé de production d'un matériau composite
WO2018051105A1 (fr) * 2016-09-14 2018-03-22 Metalysis Limited Procédé de production d'une poudre
CN111069618A (zh) * 2020-01-02 2020-04-28 崇义章源钨业股份有限公司 WC-Co复合粉末及其制备方法和应用
CN111069618B (zh) * 2020-01-02 2022-10-25 崇义章源钨业股份有限公司 WC-Co复合粉末及其制备方法和应用
CN113184853A (zh) * 2021-05-26 2021-07-30 崇义章源钨业股份有限公司 超细碳化钨粉及其制备方法与应用
CN114360884A (zh) * 2021-12-31 2022-04-15 华南理工大学 一种适用于高频电感元件的高磁感低损耗梯度纳米晶磁粉芯及其制备方法与应用
CN114752799A (zh) * 2022-04-26 2022-07-15 江西理工大学 CNTs增强WC-Co硬质合金材料及其制备方法
CN116287829A (zh) * 2023-03-24 2023-06-23 承德天大钒业有限责任公司 一种铝钼碳合金及其制备方法

Also Published As

Publication number Publication date
CN103909274A (zh) 2014-07-09
CN103909274B (zh) 2016-06-15

Similar Documents

Publication Publication Date Title
WO2015161732A1 (fr) Procédé de préparation de poudre composite de cristaux de carbure de tungstène nanométriques revêtus de cobalt, et de carbure métallique à grains ultra-fins
CN107475548B (zh) 一种纳米增韧超细晶WC-Co硬质合金的制备方法
CN100507038C (zh) 碳化钨—抑制剂复合粉末及其超细硬质合金的制备方法
CN109943739B (zh) 一种等离子体球磨制备超细晶WC-Co硬质合金的方法
CN103924111B (zh) 一种硬质合金纳米粒径粉末与高性能烧结块体材料的制备方法
WO2006106873A1 (fr) Poudre de carbure de titane et poudre composite carbure de titane - ceramique et leur methode de fabrication, et piece frittee en poudre de carbure de titane et piece frittee en poudre composite carbure de titane - ceramique et leur methode de fabrication
CN1293215C (zh) 碳化钨－钴纳米复合粉末的直接还原碳化制备方法
He et al. Synthesis of WC composite powder with nano-cobalt coatings and its application in WC-4Co cemented carbide
WO2014098370A1 (fr) Procédé pour la fabrication de carbure cémenté incluant un nanotube de carbone, carbure cémenté fabriqué de cette façon, et outil de coupe de carbure cémenté incluant le carbure cémenté
Wang et al. Microstructure and preparation of an ultra-fine-grained W-Al2O3 composite via hydrothermal synthesis and spark plasma sintering
Wu et al. Preparation technology of ultra-fine tungsten carbide powders: an overview
Xiong et al. Ultrafine hardmetals prepared by WC–10 wt.% Co composite powder
Wu et al. Synthesis of tungsten carbide nanopowders by direct carbonization of tungsten oxide and carbon: Effects of tungsten oxide source on phase structure and morphology evolution
CN102251130B (zh) 一种超细晶粒硬质合金的制备方法
KR101694528B1 (ko) 탄질화티타늄-텅스텐 소결체 제조방법 및 이에 따라 제조된 탄질화티타늄-텅스텐 소결체
CN109665848B (zh) 一种超高温SiC-HfB2复合陶瓷及其制备方法和应用
Wu et al. Ultrafine/nano WC-Co cemented carbide: Overview of preparation and key technologies
CN107199346B (zh) 一种纳米w/wc复合粉末的工业化制备方法
KR100536062B1 (ko) 나노구조형 ＴａＣ- 천이금속계 복합분말 제조방법
CN108975339B (zh) 一种过渡金属碳化物粉末和过渡金属碳化物-氮化物复合粉末的制备工艺
Yi et al. Preparation of WC-Co powder by direct reduction and carbonization
JP2008031016A (ja) 炭化タンタル粉末および炭化タンタル−ニオブ複合粉末とそれらの製造方法
CN112846170B (zh) 一种(Ti,W)C固溶体粉末及其制备方法
CN113716565B (zh) 超细碳化钨粉及其制备方法和硬质合金
CN114394834A (zh) 一种碳化硼基纳米复合粉体的制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15782437

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15782437

Country of ref document: EP

Kind code of ref document: A1