Classifications

• • G—PHYSICS
  • G02—OPTICS
  • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
  • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
  • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
  • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
  • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
  • G02F1/1333—Constructional arrangements; Manufacturing methods
  • G02F1/133308—Support structures for LCD panels, e.g. frames or bezels
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C15/00—Surface treatment of glass, not in the form of fibres or filaments, by etching
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
  • C03C17/28—Surface treatment of glass, not in the form of fibres or filaments, by coating with organic material
  • C03C17/32—Surface treatment of glass, not in the form of fibres or filaments, by coating with organic material with synthetic or natural resins
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C27/00—Joining pieces of glass to pieces of other inorganic material; Joining glass to glass other than by fusing
  • C03C27/06—Joining glass to glass by processes other than fusing
  • C03C27/10—Joining glass to glass by processes other than fusing with the aid of adhesive specially adapted for that purpose
• • G—PHYSICS
  • G02—OPTICS
  • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
  • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
  • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
  • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
  • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
  • G02F1/1333—Constructional arrangements; Manufacturing methods
• • G—PHYSICS
  • G02—OPTICS
  • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
  • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
  • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
  • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
  • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
  • G02F1/1333—Constructional arrangements; Manufacturing methods
  • G02F1/133302—Rigid substrates, e.g. inorganic substrates
• • G—PHYSICS
  • G02—OPTICS
  • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
  • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
  • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
  • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
  • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
  • G02F1/1333—Constructional arrangements; Manufacturing methods
  • G02F1/133308—Support structures for LCD panels, e.g. frames or bezels
  • G02F1/133325—Assembling processes
• • G—PHYSICS
  • G02—OPTICS
  • G02F—OPTICAL DEVICES OR ARRANGEMENTS FOR THE CONTROL OF LIGHT BY MODIFICATION OF THE OPTICAL PROPERTIES OF THE MEDIA OF THE ELEMENTS INVOLVED THEREIN; NON-LINEAR OPTICS; FREQUENCY-CHANGING OF LIGHT; OPTICAL LOGIC ELEMENTS; OPTICAL ANALOGUE/DIGITAL CONVERTERS
  • G02F1/00—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics
  • G02F1/01—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour 
  • G02F1/13—Devices or arrangements for the control of the intensity, colour, phase, polarisation or direction of light arriving from an independent light source, e.g. switching, gating or modulating; Non-linear optics for the control of the intensity, phase, polarisation or colour  based on liquid crystals, e.g. single liquid crystal display cells
  • G02F1/133—Constructional arrangements; Operation of liquid crystal cells; Circuit arrangements
  • G02F1/1333—Constructional arrangements; Manufacturing methods
  • G02F1/133308—Support structures for LCD panels, e.g. frames or bezels
  • G02F1/133331—Cover glasses
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2218/00—Methods for coating glass
  • C03C2218/10—Deposition methods
  • C03C2218/11—Deposition methods from solutions or suspensions
  • C03C2218/118—Deposition methods from solutions or suspensions by roller-coating
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2218/00—Methods for coating glass
  • C03C2218/30—Aspects of methods for coating glass not covered above
  • C03C2218/34—Masking

Definitions

• the present invention relates generally to methods of strengthening a glass substrate, and more particularly to methods of strengthening an edge of a display panel.
• a set of processes are disclosed that, when bundled together, provide strength and damage resistance to liquid crystal displays (LCD) or organic light emitting diode (OLED) displays edges and/or surfaces.
• LCD liquid crystal displays
• OLED organic light emitting diode
• These processes include surface and edge strengthening through chemical etching, grinding and polishing to control the location of impact should and impact occur and to minimize chipping and damage, and coating of edges to minimize edge damage that can weaken the glass.
• Such coatings may be temporary and designed to protect surface electronics during the above processes, and to protect the glass during and/or after these processes so as to preserve the strength that has been attained.
• a method of strengthening the edge of a glass substrate comprising masking a display panel, the display panel comprising a first glass substrate and a second glass substrate spaced apart from the first glass substrate and sealed to the first glass substrate with a sealing material, the first glass substrate comprising a terminal portion extending beyond the second glass substrate and electrically conducting terminal members disposed on the terminal portion, the masking comprising depositing a terminal masking material over the electrically conducting terminal members on the terminal portion and exposing edge surfaces of the display panel to an acid solution for a time and at a temperature effective to remove no more than about 20 micrometers of glass from the edge surfaces.
• the acid solution may comprise HF in a molar concentration in a range from about 1.5 M to about 6 M and may further comprises HCl in a molar concentration in a range from about 1 M to about 6 M.
• the acid solution may comprise HF in a molar concentration in a range from about 1.5 M to about 6 M and further comprise HNO 3 in a molar concentration in a range from about 1 M to about 6 M.
• the acid solution may comprise HF in a molar concentration in a range from about 1.5 M to about 6 M and further comprise H 2 SO 4 in a molar concentration in a range from about 1 M to about 6 M.
• the acid solution can comprise HF in a molar concentration in a range from about 3.5 to about 4.5 and HCl in a molar concentration in a range from about 3.5 M to about 4.5 M.
• the acid solution can be at a temperature in a range from about 19°C to about 24°C.
• the display panel comprises as-cut edge surfaces, or the edge surfaces may be processed after cutting, such as by being ground or polished.
• the terminal masking material preferably fills a gap between the first and second glass substrates adjacent the terminal portion after the depositing.
• the terminal masking material can be deposited as a plurality of discrete line segments by a suitable deposition apparatus, such as a dispensing robot.
• the outwardly facing major surfaces of the display panel comprise additional layers of material on the glass substrates, such as ITO or polarization layers, a surface masking film can be deposited on the outwardly facing major surfaces.
• the surface masking film is preferably recessed from edges of the exposed major surfaces a predetermined distance, for example in a range from about 0.1 mm to about 0.5 mm.
• Masking of the display panel may further comprise depositing an edge masking material in a gap between the first glass substrate and the second glass substrate along nonterminal portion sides of the display panel, for example by contacting the edge surfaces of the display panel with a porous and resilient applicator pad to which an edge masking material has been applied.
• the porous, resilient applicator pad can comprise a roller.
• Depositing the edge masking material can comprise inserting an edge surface of the first glass substrate and an edge surface of the second glass substrate opposite the edge surface of the first glass substrate in an elongate channel containing the edge masking material such that the edge surface of the first glass substrate and the edge surface of the second glass substrate contact the edge masking material, and the edge masking material wicks into the gap between the first glass substrate and the second glass substrate.
• FIG. 1 is a graph showing the loss of strength of a glass substrate in going from an as-formed glass substrate to its incorporation into a display device;
• FIG. 2 is a perspective view of an example display panel
• FIG. 3 is an side cross sectional view of the display panel of FIG. 2;
• FIG. 4 is a top view of how a mother display panel may be cut into a plurality of individual display panels;
• FIG. 5 is a process flow chart of a method of strengthening a surface and/or edge of a glass substrate comprising a display panel;
• FIG. 6 is a side cross sectional view of an example display panel according to an embodiment of the present disclosure wherein a masking material has been applied to a terminal portion of the display panel;
• FIG. 7 is a top view of a portion of the display panel of FIG. 6 illustrating the deposition pattern for the masking material
• FIGS. 8A - 8D illustrate a sequence of steps for the deposition of a masking material along non-terminal portion edges of the display panel
• FIG. 9 is a side cross sectional view of the display panel of FIGS. 8A - 8D showing the edge masking material positioned within a capillary gap of the display panel;
• FIGS. 10A - 10B show orthogonal schematic views of a pin stripping apparatus for applying an edge mask material into the edge gap of a display panel
• FIGS. 1 1 A - 1 IE illustrate a sequence of steps for another method of depositing a masking material within the capillary gap of non-terminal portion edges of a display panel
• FIG. 12A - 12B illustrate steps for depositing protective film to edge surfaces of a display panel
• FIG. 13 illustrates another method for depositing protective film to edge surfaces of a display panel
• FIG. 14 is a top view illustrating another method for simultaneously depositing a protective film to edge surfaces of a display panel.
• a display panel may be a liquid crystal display panel that incorporates at least a color filter substrate and a TFT array substrate, both comprised of glass and joined by a sealing material disposed between the two substrates.
• a display panel may be a liquid crystal display panel that incorporates at least a color filter substrate and a TFT array substrate, both comprised of glass and joined by a sealing material disposed between the two substrates.
• the methods described herein may be employed with other display panels, such as plasma display panels, phosphor display panels or more broadly, any glass package comprising two glass substrates joined together by a sealing material.
• cover glass typically placed in front of the display panel.
• the cover glass provides protection from mechanical damage to the display panel itself.
• the cover glass contacts the display panel.
• the cover glass is bonded to the display panel.
• the display panel becomes the strength member of the overall device and stress applied to the cover substrate can be conveyed directly to the display panel.
• some device designs arrange the display in an edge-to-edge configuration to eliminate the bezel usually found on such devices.
• edge-to-edge what is meant is that the display panel extends from one side of the device to the other side of the device, thereby exposing edges of the display panel to contact-induced damage during in- service use rather than the panel edges being protected by the case and/or bezel of the device.
• Newly- formed glass is exceptionally strong.
• a brittle material such as glass, for example a glass substrate used in the manufacture of a display panel
• this initial pristine strength can be degraded by flaws produced on a surface of the glass.
• a brittle material does not experience large-scale plastic flow when a stress is applied, and can be severely weakened by sharp flaws in a surface thereof.
• tensile stress applied close to the tip of a flaw is substantially greater than the average stress over the entire geometry of the flaw.
• An applied tensile stress can break atomic bonds at the flaw tip and produce a crack. The applied tensile stress may cause the crack to propagate across the brittle material, forming new surfaces perpendicular to the maximum value of the applied tensile stress.
• FIG. 1 illustrates a plot of cumulative failure probability as a function of flaw strength, more commonly referred to as a Weibull plot.
• Three sets of data are illustrated, represented by lines A, B and C. Each data set is generally angled from bottom left toward top right, each comprising a positive slope.
• Each data set represents the failure probability of a plurality of glass samples under an applied tensile stress. In reference to FIG. 1 , for a brittle material under a relatively small amount of stress, the probability of material failure is very low.
• the failing flaw To cause material failure at a low tensile stress, for example 100 megaPascal (MPa), the failing flaw must be relatively large, and the probability that such a large flaw exists is low. As the applied tensile stress becomes larger, smaller, stronger flaws begin to cause failure of the material. Eventually, at very high applied tensile stress, for example in the 1000 to 2000 megaPascal regime in reference to the glass samples of FIG. 1, even very small flaws lead to failure and the resultant cumulative probability of failure is high. It should be noted that in this regard, glass strength is determined by the "weakest" flaw. Accordingly, one desires that the flaws of the population are very small flaws, i.e. are very strong flaws.
• the data sets represented by lines B and C represent substrates of as-drawn display- type glass, whereas the data set represented by line A represents display glass removed from manufactured display devices.
• the degradation in glass strength from the as-drawn condition to the device condition is clearly evident by the shift in the data to the left (line A).
• Device manufacturers are concerned with increasing the edge and surface strength of display panels by reducing the population of low strength flaws thereon, and more particularly, by modifying the geometry of flaws, such as by modifying the flaw tip geometry to eliminate sharp flaw tips.
• glass strengths in excess of 900 megaPascals may be required for shaped (e.g. curved) display panels for use in hand held electronic devices.
• a relevant strength distribution on the product of interest and the flaw population of interest e.g. surface or edge can be obtained by first observing the lowest measured strength value from the relevant strength distribution to estimate the largest flaw.
• relevant what is meant is that the strength distribution is an appropriate representation of the flaw population of interest. In particular, one wants to obtain an estimate of the largest flaw that should be etched.
• the lowest strength is a reasonable fraction of the lowest measured strength. For example, if the lowest measured strength is 100 MPa from the relevant strength distribution, one might choose the lowest strength (largest flaw) to be 50% to 70% of that value.
• the largest flaw then, is created artificially through the use of well-established diamond indentation methods where sharp cracks are created. Strength testing is used to match the strength of the indent to the desired strength of the estimated largest flaw. An appropriate etchant recipe and etch time is then developed though an iterative process. [0041] A 4-point bend test (ASTM C158) can be used to evaluate glass strength by simulating stress generated from localized surface contact events. The 4-point bend is a good test for flaws imparted during manufacturing and handling.
• the desired Depth of Removal (DoR) of the glass material should be estimated to be approximately equal to the depth of the largest flaw as estimated from the lowest strength using the following equation
• the glass sample may be etched to the estimated DoR. This will require knowledge of the etch rate for a given chemistry and etchant temperature.
• the strength after etching can be measured and compared to the original strength distribution of the artificial flaws. If the strength of all the artificial flaws increases by about one order of magnitude, the etch process may be deemed acceptable for the intended flaw population. If the flaw population has not shifted sufficiently the etchant chemistry and etch time can be modified until the desired effect on the artificial strength distribution is achieved.
• edges of a display panel surfaces of the display panel and/or cover glass are strengthened through chemical etching. Edges of the display panel may be similarly strengthened. The edges may be as-cut, or ground and polished to control the location of impact should such impact occur, and to minimize damage (e.g. chipping) at the edge. The edge surfaces of the display panel can then be coated after etching to minimize the introduction of post-processing damage that can weaken the glass. Certain coatings can be used as temporary coatings configured to protect surface electronics during the above processes and then removed.
• Embodiments of the present disclosure can provide improved reliability in situations where pre-existing edge flaws experience Hertzian contact stresses during blunt impact. During such an occurrence, pre-existing edge flaws can experience stress due to local flexure.
• Embodiments described herein can provide a significant strength increase that can affect the entire edge and which strength increase is not dependent on the glass shape and can therefore work for shaped glass.
• Methods disclosed herein can also preserve precise device dimensions. Since these methods remove minimal substrate material, the involved etching processes can be performed such that they do not alter the overall substrate dimensions after precision cutting or shaping. To wit, the length, width and thickness of the display (glass substrates) may not be significantly altered.
• U.S. Patent Publication No. 201301091 16 filed on July 3, 2012 describes a method by which the surfaces of large mother display panels can be strengthened by chemical etching.
• the display mother panels are glass envelopes formed by sealing together several sheets of glass, the sealed assembly representing a plurality of yet-to-be individual display panels.
• the mother panel may later be cut into individual display panels destined to be incorporated into separate display devices.
• Surface etching of the mother panel does not address flaws that may be formed along newly-formed edges of the subsequent discrete display panels that are later cut from the mother panel.
• To obtain strengthened and protected edges of a glass substrate, and in particular one or more glass substrates comprising an assembled individual display panel one may begin with a display panel that has been separated into individual device-size panels.
• the edges therefore, are those that will be installed in the final device, and may be weak due to flaws created during the separation process, for example the common score and break process or even by an edge finishing process such as grinding.
• FIGS. 2 and 3 illustrate respectively a perspective view and a side view of an example display panel 10 comprising at least a first glass substrate 12 and a second glass substrate 14 spaced apart from first glass substrate 12 and joined thereto with a sealing material 16.
• Sealing material 16 is generally positioned near a periphery of both first and second glass substrates inward of the perimeter edges of the glass substrates and bonds first glass substrate 12 to second glass substrate 14 via their respective major surfaces.
• Sealing material 16 is typically in the shape of a closed loop that, in combination with the first and second substrates, encapsulates a space 18 interior thereto.
• the display panel may or may not include a liquid crystal material within interior space 18 encapsulated between the glass substrates and the seal.
• First glass substrate 12 includes an outwardly facing first major surface 20 and an inwardly facing second major surface 22.
• First major surface 20 of first glass substrate 12 may be planar as shown and is generally parallel with second major surface 22.
• Outwardly facing first major surface 24 of second glass substrate 14 may be planar as shown and is generally parallel with an inwardly facing second major surface 26 of second glass substrate 14 that is opposite first major surface 24.
• Second major surface 22 of first glass substrate 12 may include an electrically functional layer 28 deposited thereon, which may include one or more layers of silicon, metal and/or metal oxides.
• electrically functional layer 28 may comprise at least a portion of one or more thin film transistors (TFTs).
• Either one or both of first major surfaces 20 and 24 may include one or more additional layers of material 30, such as a metal oxide layer, for example a layer of indium tin oxide (ITO).
• ITO indium tin oxide
• Each glass substrate 12, 14 further comprises a respective peripheral edge surface 32, 34 formed during a separation (e.g. cutting) process from a mother display panel 36, as shown in FIG. 4.
• FIG. 4 illustrates an example where four individual display panels 10 may be cut from mother panel 36 along cut lines 38.
• display panel 10 is assumed to be a rectangle such that the peripheral edge surface 32 of first glass substrate 12 and peripheral edge surface 34 of second glass substrate 14 each comprise four sections.
• Other display panel shapes, with more or fewer edge surface sections may be used.
• the edge surface sections of edge surface 32 are represented by reference numerals 32a, 32b, 32c and 32d.
• edge surface sections of edge surface 34 are represented by reference numerals 34a, 34b, 34c and 34d. As shown, and to simplify discussion, respective edge surface sections are aligned generally such that edge sections 32a and 34a are on the same side of display panel 10, and so on for the remaining respective edge surface sections.
• the individual edge surfaces may be substantially planar and perpendicular to the adjoining major surfaces of the respective glass substrate. In other embodiments the edge surfaces may be further processed after cutting, such as by grinding and/or polishing, and may be shaped. For example, the edge surfaces may comprise a curved or beveled portion.
• first glass substrate 12 may comprise a terminal portion 40 terminating at edge surface 32d that extends outward beyond second glass substrate 14.
• Terminal portion 40 forms an electrical connection area where components of the display device external to the display panel 10 can make electrical connection to the interior space 18.
• terminal portion 40 may include a plurality of electrical terminal elements 42 positioned thereon that extend from terminal portion 40 into interior space 18 through or beneath sealing material 16.
• the plurality of electrical terminal elements 42 may be electrically connected with the one or more thin film transistors that may reside within interior space 18.
• a display panel may comprise more than one terminal portion 40.
• a flow diagram shown in FIG. 5 illustrates an example process 100 for obtaining and/or maintaining strengthened edges of a glass substrate, and more particularly a display panel comprising multiple glass substrates, such as an LCD display panel.
• the panel Prior to performing the etching process, the panel may be cleaned in a cleaning solution.
• a cleaning solution For example, a 1% aqueous bath of SemiClean KG may be used at a temperature of approximately 50°C, for example in a range from about 40°C to about 60°C.
• the panel to be etched is dipped into the cleaning solution bath for a time in a range from about 4 minutes to about 6 minutes, for example about 5 minutes.
• the panel can be rinsed, for example by dipping the panel in warm deionized water for a time sufficient to remove the cleaning solution.
• the rinse step can be performed multiple times if needed, and in different rinse baths.
• the panel can be removed and spray rinsed with deionized water. A gentle flow of nitrogen and/ or air can be used to eliminate dripping water, and the panel can be allowed to air dry.
• a first optional step 102 if one or both of the exposed major surfaces 20, 24 of display panel 10 have an additional layer of material, such as a deposited ITO layer, the additional layer of material may need to be protected during one or more subsequent etching processes.
• an acid resistant film hereinafter referred to as surface mask 44
• surface mask 44 can be applied to one or both of the display panel outwardly facing major surfaces, or to the additional layer of material 30 (e.g. ITO) as best seen in FIG. 6.
• surface mask 44 may be a polymer film, for example a polyester film, and surface mask 44 may further comprise a pressure sensitive adhesive and optionally a release liner.
• a suitable surface mask comprises Nitto Denko Lensguard 7568 adhesive tape.
• a substrate-to-substrate laminator may be used in the application process.
• a suitable substrate laminator is a Suntec MPF65S-TS.
• Numerically controlled guides may be used to determine the placement of the surface mask on the glass.
• Surface mask 44 may be precut to the appropriate size if needed, and sized so that edges of the surface mask are inset a predetermined distance from the edges of the glass substrate to which the surface mask is applied, such as being inset a distance ⁇ from about 0.05 millimeters (mm) to about 0.5 millimeters, for example, from about 0.1 millimeters to about 0.3 millimeters.
• the one or more surface masks 44 may be removed.
• the one or more terminal portions 40, and particularly the electrical terminal elements 42 may also be masked for a subsequent etching process.
• an acid resistant polymer hereinafter referred to as terminal mask 46
• terminal mask 46 an acid resistant polymer
• each edge section 32d and 34d should have less than about 50% of their edge surfaces covered by terminal mask 46, such as less than 25% or less than 10%.
• the terminal mask protects all of the electrical terminal elements, does not extend over edge surfaces of first glass substrate 12, and does not extend over edge surfaces of second glass substrate 14, although it is understood that some degree of edge surface covering may be difficult to avoid.
• Terminal mask 46 may be deposited on terminal portion 40 as a liquid, which liquid wicks into edge gap 48 between the substrates via capillary action.
• Edge gap 48 may be as little as 5 micrometers ( ⁇ ) in thickness, for example in a range from about 5 micrometers to about 15 micrometers.
• terminal portion 40 Prior to application of terminal mask 46, terminal portion 40 may be cleaned of organic contaminants with a suitable solvent to achieve appropriate wetting characteristics, for example by rinsing or wiping with acetone.
• Terminal mask 46 may be applied, for example, via a needle dispense process, but other deposition processes or equipment may be used, such as but not limited to a piezo jet nozzle, a pneumatic jet nozzle, an aerosol jet nozzle or an inkjet print head. Dispensing of the terminal mask material may be performed by applying the mask material along a plurality of pre-determined discrete line segments. The dispense tool path pattern, volume and speed should be specified based on position over the terminal portion.
• FIG. 7 illustrates a portion of a display panel comprising two terminal portions 40, and a pattern comprising a plurality of discrete line segments 50 along which a terminal mask material is deposited onto the terminal portions.
• Such dispense patterns can be determined and programed into the dispensing robot.
• the mask application pattern should be controlled such that adjacent lines of liquid are able to spread and coalesce into a continuous protective film (terminal mask 46) without flowing over edge surface 32d, and should also flow into edge gap 48 without flowing onto edge surface 34d.
• terminal mask 46 can be deposited to be at least 0.05 millimeters from edge surface 32d.
• the terminal mask material should have a viscosity when deposited that is suitable for filling edge gap 48 via capillary action.
• a photoresist material from the MicropositTM SC 1800 Series is a suitable material for producing terminal mask 46.
• the MicropositTM SC 1800 Series of positive photoresists are acid-etch resistant photoresists, available in various viscosities appropriate for masking. For example, SC- 1827 (with a viscosity of 81 centipoise) is compatible with a needle dispense process. Microposit 1800 Series photoresists are shipped in one (1) liter bottles; they arrive pre- filtered and require no special preparation prior to loading in a syringe on a dispenser. However, other photoresist materials may also be suitable. A syringe barrel can be mounted on a dispensing robot and filled to 50% - 80% capacity with resist material. On a laboratory scale, an As mtek Dispensemate 555 robot was employed.
• the syringe barrel can have a volume capacity in a range from about 10 cubic centimeters to about 30 cubic centimeters.
• the syringe barrel should be formed from a UV blocking material (e.g. transparent orange or opaque black). Other equipment could be used for industrial scale operation.
• the display panel can be placed on a substrate of cleanroom paper, and the display panel positioned on a hotplate at approximately 60°C for about 5 minutes, with the cleanroom paper contacting the hotplate. Then, the display and cleanroom paper can be placed in an oven for drying.
• one exemplary drying process can be performed as follows: The oven temperature is raised to 35°C and the display panel inserted into the oven and held at 35°C for 30 minutes, then the temperature is set to 50°C. After an additional 30 minutes the temperature is set to 65°C. After an additional 30 minutes the temperature is set to 75°C.
• the display panel can be allowed to cool and is removed from the oven.
• mask materials comprising solvents, particularly UV-curable materials which also comprise volatile solvents
• such materials should not be UV-cured. It has been found that during the drying process, even very long drying processes, all of the solvent may not be removed. The heat generated during the UV curing may then cause the volatile solvent to form bubbles, craters or other defects in the mask material that could allow the etching acid to reach the terminal elements. It should be understood that the foregoing process is based on a laboratory scale and an industrial-scale process can be implemented that includes the major components of the foregoing process, including the different heating and drying steps.
• Skinning over, bubbles or craters can form in the terminal mask material during the drying process if the terminal mask material is dried too quickly, if the concentration gradient is too large, or if the diffusivity of the solvent is too low. Bubbles or craters can also form when the boiling liquid trapped inside escapes quickly. Bubbles and craters can occur near edge surface 34d, where the terminal mask material is thickest and the edge gap traps residual solvents. Thick coatings and long diffusion paths are particularly susceptible to skinning over and bubble formation. If encountered, this defect may be mitigated by using an alternate terminal mask material, such as a 100% UV curable material containing no solvents, by forming a thinner coating, or by using a drying cycle employing longer drying times.
• an alternate terminal mask material such as a 100% UV curable material containing no solvents
• a solvent- free UV-curable mask material has the advantage of eliminating the drying step and reducing the cure time to only 2 - 3 minutes.
• Suitable alternative materials can include Sun Chemicals XVI 000 UV Etch Resist, General Chemical Coscoat 4300/4560 or the like.
• De-wetting in particular can occur at the edge gap. It is believed that surface energy in this region is different due, for example, to residual surface material remaining from an upstream cleaning operation or other process operation. Different materials on the terminal portion can have different surface energies, resulting in different contact angles and wetting. De-wetting can also occur in the continuous flat areas on bare glass or on display panels where the terminal mask material selectively thins out, leaving an area of low coverage. Wide deposition lines 50 are more prone to these non-uniformities. De-wetting defects can further be found along interface lines between two different materials, such as between the electrical connection elements and bare glass. Accordingly, additional surface cleaning processes, such as using an atmospheric plasma, can be used prior to deposition of terminal mask 46.
• a film to provide mechanical protection during transportation and storage prior to the etching process such as a polyethelyene film or other polymer material, can be applied to the display panel outward facing surfaces and removed prior to step 108.
• black matrix material 52 comprising color filter 54 located on second glass substrate 14.
• Black matrix material 52 is deposited on the second glass substrate to block light within inter-pixel areas of the second glass substrate color filter 54 and/or to prevent ambient light from reaching the thin film transistors.
• the black matrix material can improve contrast ratio in high ambient lighting conditions.
• the black matrix material may comprise, for example, chromium.
• a chromium oxide adhesion layer may be deposited between a chromium metal layer and second glass substrate 14.
• black matrix material 52 may be a polymer material.
• the etchant used in the etching process can affect exposed black matrix material 52 within edge gap 48 between the first and second glass substrates, and in some instances form a multi-color (rainbow) effect.
• this detrimental effect would go un-noticed, since the edge gap would be hidden behind the surrounding bezel.
• the display panel is a so-called edge-to-edge display panel, where the display panel extends from one edge of the display device to another edge of the display device, and the display panel edge surfaces are exposed, such a color effect would be visually undesirable.
• the edge gap between the sealing material and the edge surface portions of the first and second glass substrate 12, 14 is filled with an edge mask prior to the etching, while at the same time substantially preventing the edge mask from coating the edge surfaces 32a through 32c and 34a through 34c such that the etching is effective to modify any flaws on the edge surfaces.
• the edge gap filling process can comprise the following steps: introducing an acid resistant ink (hereinafter edge mask material) into edge gap 48, removing any excess edge mask material from the display panel edge surfaces to insure the edge surfaces are exposed for acid etching, then curing the edge mask material to make it sufficiently robust to survive the acid etching process.
• edge mask material should have a viscosity such that the edge mask material can flow into edge gap 48 along each edge of the display panel to which it is applied.
• an edge mask material e.g. a UV curable carbon black ink such as Swiss Q
• a dipping process can be used wherein the edge surfaces of the display panel are dipped into a suitable edge mask material, a dispensing pen similar to a felt- tip marker, a needle dispensing positive displacement piston or a focused spray into the edge gap.
• a channel member 56 may be used for filling edge gap 48 of the non-terminal portion edge portions of display panel 10, i.e. the gap between edge surface pairs 32a - 34a, 32b - 34b and 32c - 34c.
• FIGS. 8A through 8D includes a cross sectional view of channel member 56 comprising a channel 58 formed between two side walls 60 that serves as a reservoir for edge mask material 62.
• Display panel 10 is illustrated having processed edge surfaces 32 and 34 such that the edge surfaces are curved.
• a width W of channel 58 is sufficiently wide, and the reservoir of edge mask material is sufficiently high, that only the tips of the curved edge surfaces are able to immerse in the edge mask material, as best seen in FIG. 8B.
• the specific width W and the height of edge mask material 62 in channel 58 will depend on the specific thickness of the individual display panel. It is necessary only that edge mask material 62 contact both "tips" of the edge surfaces 32, 34 when lowered into the edge mask material, as shown in FIG. 8B and as indicated by arrow 64.
• the edge surface tips represent the outermost portion of the edge surface, that is to say the extreme perimeter of the substrate assembly.
• edge mask material 62 When the edge mask material 62 contacts both tips of the edge surfaces 32a and 34a, capillary action can cause the edge mask material to wick into the edge gap 48, shown in FIG. 8C. Once the wicking occurs, display panel 10 may be withdrawn from the edge mask material as shown in FIG. 8D and indicated by arrow 66. Excess edge mask material may be wiped from the edge surfaces (e.g. edge surfaces 32a, 34a) with a solvent-soaked cleanroom wipe or by rinsing with a solvent if desired, leaving the edge mask material only within edge gap 48, or with only a very little edge mask material covering the edge surfaces, as shown in FIG. 9.
• edge surfaces e.g. edge surfaces 32a, 34a
• a rinsing process may be used to minimize any damage or the introduction of any contaminants from using the cleanroom wipes to mechanically wipe the edge surfaces. This process may be repeated along other sides of the panel. [0068] The foregoing process may be repeated for the remaining edge surfaces on each non- terminal portion side of the display panel (e.g. edge surfaces 32b - 34b, 32c - 32c).
• edge mask material may be cured after application by a method compatible with the particular material, thereby forming edge mask 68.
• curing may comprise UV curing in a UV curing chamber (e.g. a ProCureTM 350 UV Chamber by 3D systems) that exposes the entire display panel to UV light and insures all of the display panel edge masks 68 are cured and sealed.
• a UV curing chamber e.g. a ProCureTM 350 UV Chamber by 3D systems
• a pin striping apparatus 69 shown in the orthogonal schematic views of FIGS. 1 OA and 10B is provided with the edge mask material.
• the pin striping apparatus shown in FIGS. 10A and 10B comprises an applicator wheel 70 in fluid communication with the edge mask material 62, contained for example in a reservoir 72, via a passage 74.
• the edge mask material can be supplied, for example, to a channel 76 about a perimeter of applicator wheel 70.
• the applicator wheel 70 containing the edge mask material is run along edge gap 48 of the display panel to allow the edge mask material to wick into the edge gap and fill the edge gap with edge mask material. Once the gap is filled, excess edge mask material is gently removed to expose the glass edge surfaces of the panel.
• the edge gap can be permanently filled or temporarily filled, with the only requirement being that the ink survive the acid etching process.
• allowing the edge mask to permanently become part of the display panel eliminates a post-acid etch removal process step that might otherwise impart damage to the now etched glass edge.
• edge mask dramatically minimizes the "color hue” effect within the edge gap
• excess edge mask material on the edge surfaces can seal the surface mask edge to the glass surface which creates little to no acid leakage under the surface mask film compared to panels with no edge mask.
• edge mask material 62 may be cured after application by a method compatible with the particular material, thereby forming edge mask
• curing may comprise UV curing in a UV curing chamber (e.g. a ProCureTM
• edges of the display panel are acid etched by exposing the display panel to an acid solution for a time and at a temperature effective to remove no more than about 20 micrometers of glass per immersed edge.
• the display panel may be gently washed prior to the etching process with a suitable detergent, for example by using a 1% to about 4% aqueous solution of Semi-Clean KG at a temperature in a range from about 65°C to about 90°C, for example from about 65°C to about 75°C, then immediately rinsed with warm (e.g. 50°C - 55°C) deionized water.
• the detergent solution concentration may be kept to equal to or less than a 1 % solution.
• the display panel can then be dried, for example by air drying.
• HF-H 2 SO 4 , HF-HC1 or HF-HNO3 acid solution may be used for etching.
• Exposure of the display panel edges can be performed by immersing the entire display panel into the acid solution so that all edge surface sections of each glass substrate of the display panel are immersed, or by selectively immersing only selected edge surfaces, for example by mounting the display panel in a suitable holder and dipping the edge surfaces singularly into the acid solution.
• a suitable acid solution may comprise HF and HCl in molar concentrations in a range from about 1.5 M (mol/L) to about 6 M and greater than 1 M (for example in a range from about 1 M to about 6 M, respectively (1.5M ⁇ HF ⁇ 6 M, 1M ⁇ HCL ⁇ 6 M), at a temperature in a range from about 19°C to about 24°C, for example in a concentration range from about 3.5 M to about 4.5 M HF (3.5M ⁇ HF ⁇ 4.5 M) and HCl in a range from about 3.5 M to about 4.5 M (3.5M ⁇ HCl ⁇ 4.5 M), or HF in a range from about 3.8 M to about 4.3 M (3.8 M ⁇ HF ⁇ 4.3 M ) and HCl in a range from about 3.8 M to about 4.3 M (3.8 M ⁇ HCl ⁇ 4.3 M).
• a molar concentration of 4 M HF and 4 M HCl has been found to be a reasonable balance between duration of etch and etch rate, having an etch rate of approximately 1.8 micrometers/min.
• the etch rate should be at least 1 micrometer/minute. This is of particular interest owing to the placement of the terminal members and their possible exposure to the acid solution.
• the display panel edge surfaces may be exposed for a time sufficient to remove no more than about 20 micrometers of glass from any particular exposed edge surface, for example in a range from greater than zero micrometers to equal to or less than 20 micrometers, in a range from about 1 micrometer to about 20 micrometers, in a range from about 5 micrometers to about 20 micrometers, or in a range from about 10 micrometers to about 20 micrometers.
• the display panel edge surfaces may be exposed for a time sufficient to remove about 18 to about 20 micrometer of glass, or in a range from about 14 micrometers to about 18 micrometers, or in a range from about 10 micrometers to about 16 micrometers.
• a solution comprising HF in a concentration equal to or greater than 1.5 M but equal to or less than 6 M (1.5M ⁇ HF ⁇ 6 M) and HNO 3 in a concentration greater than or equal to 1 M but equal to or less than 6 M (1.5M ⁇ HN0 3 ⁇ 6 M) may be used at the same temperature range, but with a difference in the quality of the glass edges after etching.
• small portions of the terminal mask may be removed by the HF - HNO3 acid solution.
• a small thin line of residual etching by-products was found around the edge of the surface mask.
• this residue layer was found to be greater when etched with an HF - HNO 3 acid solution when compared with the residue associated with an HF - HC1 etching treatment. Without wishing to be bound by theory, this is believed to indicate that the HF - HC1 solution better dissolves the sludge generated near the edge during etching when compared to HF - HNO 3 acid solution.
• a solution comprising HF in a concentration equal to or greater than 1.5 M but equal to or less than about 6 M (1.5M ⁇ HF ⁇ 6 M), and H 2 SO 4 in a concentration equal to or greater than 1 M but equal to or less than 6 M (1.5M ⁇ H 2 S0 4 ⁇ 6 M ) may be used.
• surface mask 44 can be removed.
• the display panel may be soaked in warm (50°C to about 55°C) tap water or warm deionized (DI) water for a time in a range from about 4 minutes to about 10 minutes, or until the surface mask is released from the panel.
• DI warm deionized
• wet-release methods can sometimes cause surface mask 44 to be released by water seeping under the mask from one of the side edges. This seeping of water beneath the surface mask can result in large surface marking of the glass after removal of the mask.
• an alternative dry film peeling process can be used.
• the display panel can be securely held, such as by placing the display panel on a vacuum chuck. While the panel is held in place by the vacuum chuck, surface mask 44 is peeled away from the display panel surface, for example by using a small adhesive tape attached to a perimeter edge portion of the surface mask and pulling up and back on the adhesive tape.
• the display panel should be completely dry before the dry peeling is performed. Any water near the edge of the surface mask may be dragged across the display panel surface during the peeling and mark the surface of the glass or any ITO layer thereon.
• terminal mask 46 (and edge masks 68, if present), is removed, for example by immersing terminal portion 40 (and/or edge surface sections), including the terminal mask, in a suitable solvent, such as acetone for example, and then the terminal portion may be rinsed using deionized water to remove the solvent.
• a suitable solvent such as acetone for example
• a gentle rub near the edge of the terminal portion using a suitable solvent, for example a methanol-soaked cleanroom cloth may be performed prior to the deionized water rinse to remove any remaining acid residue. In some embodiments it may be unnecessary to remove edge mask 68 from non-terminal portions of edge gap 48.
• edge surfaces 32, 34 may be protected by applying an edge surface coating 78 using whatever edge coating material best meets the need for the particular application, typically a polymer coating material.
• a polymer coating material typically a silica- filled coating such as Masterbond may be used.
• the edge surface coating thickness may be in a range from about 50 micrometers to about 75 micrometers.
• the edge surface coating material may be supplied first to an applicator pad.
• the applicator pad is preferably porous and resilient, for example a foam applicator pad.
• the application of an edge surface coating using an applicator pad is not particularly dependent on edge surface profiles or glass shape, and thus an applicator pad will work for different edge surface profiles and glass shapes.
• foam easily conforms and does not allow the display to slip during the coating application.
• the edge surfaces 32, 34 of display panel 10 are coated by placing one corner of display panel 10 onto applicator pad 80, including the edge coating material, and then lowering the opposite corner down onto the applicator pad until the entire side of the display panel is touching the coating material- laden applicator pad.
• the display panel is removed by lifting the first corner of the display panel out of the coating material slowly until the first corner is no longer in contact with the coating material- laden applicator pad 80.
• the display panel may then be removed from the applicator pad, leaving an edge coating 70 deposited on the display panel edge surfaces for that side. This process can be repeated for each side of the displaypanel.
• a new section of applicator pad 80, with edge coating material, may be used for each subsequent use/edge coating if desired.
• Coverage of edge surface coating 78 over edge surfaces 32, 34 e.g. 32a - 34a, 32b - 34b, 32c - 34c or 32d - 34d
• the edge surface coating material may be cured by a method appropriate to the material. For example, if the edge coating material is a UV curable material, the edge coating material may be placed on or into, as the case may be, a UV cure machine. The display panel surface should be protected during the UV-cure process.
• Applicator pad 80 may have patterns cut from the pad to allow regions of the edge surfaces that are not to be coated to not receive the coating material, for example, where the electrical terminal elements 42 are attached to terminal portion 40.
• the process in respect of FIGS. 1 1 A through 1 IE can then be used, but modified such that any notches or cut-outs 82 are appropriately aligned with regions of the display panels edge surfaces that are not to receive edge surface coating material as illustrated in FIGS. 12A and 12B. Accordingly, such a "stepped" applicator pad can be used to coat recessed edge surface 34d of the second glass substrate.
• applicator pad 80 can be positioned on a roll 84 for on-line edge surface coating application in a manufacturing setting as an alternative method as shown in FIG. 13. Several rolls can be used to coat multiple edge surface portions on multiple sides of the display panel simultaneously. Alternatively, multiple applicator pads 80 may be pressed against respective edge sections of the display panel simultaneously, for example four applicator pads 80 pressed against each of four sides of the display panel as depicted in FIG. 14.
• a polymer film such as a polyethylene film, e.g. Visqueen, may be applied to protect the display panel against mechanical surface damage. This film i9s preferably removed prior to installation of the display panel into a display device.
• the final display panel is protected and ready to ship or be installed into a device.

Landscapes

• Physics & Mathematics (AREA)
• Chemical & Material Sciences (AREA)
• Nonlinear Science (AREA)
• Engineering & Computer Science (AREA)
• Crystallography & Structural Chemistry (AREA)
• Mathematical Physics (AREA)
• General Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• Materials Engineering (AREA)
• Life Sciences & Earth Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• General Chemical & Material Sciences (AREA)
• Geochemistry & Mineralogy (AREA)
• Organic Chemistry (AREA)
• Ceramic Engineering (AREA)
• Inorganic Chemistry (AREA)
• Devices For Indicating Variable Information By Combining Individual Elements (AREA)
• Surface Treatment Of Glass (AREA)

Priority Applications (3)

Applications Claiming Priority (6)

Publications (1)

Family

ID=52432959

Family Applications (1)

Country Status (6)

Families Citing this family (16)

Citations (7)

Family Cites Families (44)

• 2015
  • 2015-01-07 US US14/591,456 patent/US9488857B2/en not_active Expired - Fee Related
  • 2015-01-09 CN CN201580013160.2A patent/CN106536439B/zh not_active Expired - Fee Related
  • 2015-01-09 WO PCT/US2015/010779 patent/WO2015106076A1/en not_active Ceased
  • 2015-01-09 JP JP2016546036A patent/JP2017503745A/ja active Pending
  • 2015-01-09 KR KR1020167021811A patent/KR20160106725A/ko not_active Withdrawn
  • 2015-01-12 TW TW104100975A patent/TWI624442B/zh not_active IP Right Cessation

Patent Citations (7)

Also Published As

Similar Documents

Legal Events