WO2015098632A1 - Particule composite pour électrode d'élément électrochimique - Google Patents

Particule composite pour électrode d'élément électrochimique Download PDF

Info

Publication number
WO2015098632A1
WO2015098632A1 PCT/JP2014/083339 JP2014083339W WO2015098632A1 WO 2015098632 A1 WO2015098632 A1 WO 2015098632A1 JP 2014083339 W JP2014083339 W JP 2014083339W WO 2015098632 A1 WO2015098632 A1 WO 2015098632A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
negative electrode
active material
electrode active
composite particles
Prior art date
Application number
PCT/JP2014/083339
Other languages
English (en)
Japanese (ja)
Inventor
梓 増田
Original Assignee
日本ゼオン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本ゼオン株式会社 filed Critical 日本ゼオン株式会社
Priority to CN201480066528.7A priority Critical patent/CN105794025B/zh
Priority to KR1020167012496A priority patent/KR102330766B1/ko
Priority to JP2015554771A priority patent/JP6485359B2/ja
Publication of WO2015098632A1 publication Critical patent/WO2015098632A1/fr

Abstract

Particule composite pour électrodes d'éléments électrochimiques, comprenant une matière active d'électrode négative (A), une résine liante particulaire (B), un polymère soluble dans l'eau (C) et des fibres polymères de polysaccharide non solubles dans l'eau (D). Le polymère soluble dans l'eau (C) et les fibres polymères de polysaccharide non solubles dans l'eau (D) sont comprises en une proportion telle que (C)/(D) = 0,2-18.
PCT/JP2014/083339 2013-12-26 2014-12-17 Particule composite pour électrode d'élément électrochimique WO2015098632A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
CN201480066528.7A CN105794025B (zh) 2013-12-26 2014-12-17 电化学元件电极用复合粒子
KR1020167012496A KR102330766B1 (ko) 2013-12-26 2014-12-17 전기 화학 소자 전극용 복합 입자
JP2015554771A JP6485359B2 (ja) 2013-12-26 2014-12-17 電気化学素子電極用複合粒子

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013-268554 2013-12-26
JP2013268554 2013-12-26

Publications (1)

Publication Number Publication Date
WO2015098632A1 true WO2015098632A1 (fr) 2015-07-02

Family

ID=53478496

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/083339 WO2015098632A1 (fr) 2013-12-26 2014-12-17 Particule composite pour électrode d'élément électrochimique

Country Status (4)

Country Link
JP (1) JP6485359B2 (fr)
KR (1) KR102330766B1 (fr)
CN (1) CN105794025B (fr)
WO (1) WO2015098632A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015178241A1 (fr) * 2014-05-20 2015-11-26 日本ゼオン株式会社 Particules composites pour électrode de dispositif électrochimique, et procédé de fabrication de celles-ci
JPWO2017104145A1 (ja) * 2015-12-16 2018-09-06 国立大学法人 東京大学 リチウムイオン二次電池
JP2019131778A (ja) * 2017-07-20 2019-08-08 東ソー株式会社 導電性高分子水溶液、及び導電性高分子膜
CN110679014A (zh) * 2017-09-28 2020-01-10 株式会社Lg化学 预测电极浆料的工艺性和选择电极粘合剂的方法

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN108126637B (zh) * 2018-01-11 2023-10-13 辽宁石油化工大学 一种碳化硅微通道烷基化反应器及其使用方法

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08190912A (ja) * 1995-01-12 1996-07-23 Fuji Photo Film Co Ltd 非水二次電池の負極用合剤の製造方法
JPH08195201A (ja) * 1995-01-17 1996-07-30 Fuji Photo Film Co Ltd 非水二次電池の負極用合剤の製造方法
JP2005116855A (ja) * 2003-10-09 2005-04-28 Nippon Zeon Co Ltd 電気二重層キャパシタ用電極の製造方法
JP2005222933A (ja) * 2004-01-05 2005-08-18 Showa Denko Kk リチウム電池用負極材及びリチウム電池
JP2007224263A (ja) * 2006-01-25 2007-09-06 Dainichiseika Color & Chem Mfg Co Ltd ヒドロキシアルキル化キトサン溶液
JP2009146581A (ja) * 2007-12-11 2009-07-02 Osaka Gas Chem Kk リチウムイオン二次電池用シート状負極及びその製造方法
JP2010135338A (ja) * 2005-02-10 2010-06-17 Showa Denko Kk 二次電池用集電体、二次電池用正極、二次電池用負極、二次電池及びそれらの製造方法
JP2012094331A (ja) * 2010-10-26 2012-05-17 Asahi Glass Co Ltd 蓄電素子用電極の製造方法、蓄電素子用電極および蓄電素子
JP2012164632A (ja) * 2011-01-20 2012-08-30 Mitsubishi Materials Corp リチウムイオン二次電池の負極用組成物及びこれを用いたリチウムイオン二次電池の負極
JP2013175322A (ja) * 2012-02-24 2013-09-05 Asahi Glass Co Ltd 蓄電素子用電極の製造方法および蓄電素子

Family Cites Families (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI390789B (zh) * 2005-02-10 2013-03-21 Showa Denko Kk A battery current collector, a battery positive electrode, a battery negative electrode, a battery, and a manufacturing method
JP5045761B2 (ja) 2007-10-03 2012-10-10 日本ゼオン株式会社 電気二重層キャパシタ用電極およびその製造方法
WO2009147989A1 (fr) * 2008-06-02 2009-12-10 大日精化工業株式会社 Liquide de revêtement, liquide de revêtement pour la fabrication d'une électrode plane, agent de sous-couche et leur utilisation
JP2009295666A (ja) 2008-06-03 2009-12-17 Nippon Zeon Co Ltd 電気化学素子用電極および電気化学素子
CN102089907A (zh) * 2008-07-17 2011-06-08 旭硝子株式会社 非水电解质电池用负极复合材料
WO2010117134A2 (fr) 2009-02-17 2010-10-14 주식회사 아모그린텍 Composition pour produire une électrode positive pour un dispositif de stockage d'énergie électrique, électrode positive pour un dispositif de stockage d'énergie électrique produite au moyen de la composition, et dispositif de stockage d'énergie électrique comprenant l'électrode
CN102576854B (zh) * 2009-08-27 2015-03-11 大日精化工业株式会社 电极板用水系涂装液、蓄电装置用电极板、蓄电装置用电极板的制造方法及蓄电装置
JP5594548B2 (ja) * 2010-08-25 2014-09-24 トヨタ自動車株式会社 電池用電極の製造方法
WO2012096189A1 (fr) * 2011-01-14 2012-07-19 昭和電工株式会社 Collecteur de courant
CN103907226A (zh) * 2011-09-14 2014-07-02 日本瑞翁株式会社 电化学元件用电极
US10020513B2 (en) 2011-09-20 2018-07-10 Nissan Chemical Industries, Ltd. Slurry composition for forming lithium secondary battery electrode containing cellulose fiber as binder, and lithium secondary battery electrode

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08190912A (ja) * 1995-01-12 1996-07-23 Fuji Photo Film Co Ltd 非水二次電池の負極用合剤の製造方法
JPH08195201A (ja) * 1995-01-17 1996-07-30 Fuji Photo Film Co Ltd 非水二次電池の負極用合剤の製造方法
JP2005116855A (ja) * 2003-10-09 2005-04-28 Nippon Zeon Co Ltd 電気二重層キャパシタ用電極の製造方法
JP2005222933A (ja) * 2004-01-05 2005-08-18 Showa Denko Kk リチウム電池用負極材及びリチウム電池
JP2010135338A (ja) * 2005-02-10 2010-06-17 Showa Denko Kk 二次電池用集電体、二次電池用正極、二次電池用負極、二次電池及びそれらの製造方法
JP2007224263A (ja) * 2006-01-25 2007-09-06 Dainichiseika Color & Chem Mfg Co Ltd ヒドロキシアルキル化キトサン溶液
JP2009146581A (ja) * 2007-12-11 2009-07-02 Osaka Gas Chem Kk リチウムイオン二次電池用シート状負極及びその製造方法
JP2012094331A (ja) * 2010-10-26 2012-05-17 Asahi Glass Co Ltd 蓄電素子用電極の製造方法、蓄電素子用電極および蓄電素子
JP2012164632A (ja) * 2011-01-20 2012-08-30 Mitsubishi Materials Corp リチウムイオン二次電池の負極用組成物及びこれを用いたリチウムイオン二次電池の負極
JP2013175322A (ja) * 2012-02-24 2013-09-05 Asahi Glass Co Ltd 蓄電素子用電極の製造方法および蓄電素子

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015178241A1 (fr) * 2014-05-20 2015-11-26 日本ゼオン株式会社 Particules composites pour électrode de dispositif électrochimique, et procédé de fabrication de celles-ci
JPWO2017104145A1 (ja) * 2015-12-16 2018-09-06 国立大学法人 東京大学 リチウムイオン二次電池
JP2019131778A (ja) * 2017-07-20 2019-08-08 東ソー株式会社 導電性高分子水溶液、及び導電性高分子膜
CN110679014A (zh) * 2017-09-28 2020-01-10 株式会社Lg化学 预测电极浆料的工艺性和选择电极粘合剂的方法
EP3648200A4 (fr) * 2017-09-28 2020-06-03 LG Chem, Ltd. Procédé pour prédire l'aptitude au traitement d'une suspension d'électrode et sélectionner un liant d'électrode
CN110679014B (zh) * 2017-09-28 2023-04-04 株式会社Lg新能源 预测电极浆料的工艺性和选择电极粘合剂的方法
US11735735B2 (en) 2017-09-28 2023-08-22 Lg Energy Solution, Ltd. Method for predicting processability of electrode slurry and selecting electrode binder

Also Published As

Publication number Publication date
CN105794025A (zh) 2016-07-20
KR20160102159A (ko) 2016-08-29
KR102330766B1 (ko) 2021-11-23
JPWO2015098632A1 (ja) 2017-03-23
JP6485359B2 (ja) 2019-03-20
CN105794025B (zh) 2020-01-21

Similar Documents

Publication Publication Date Title
JP6217741B2 (ja) 電気化学素子電極用複合粒子、電気化学素子電極用複合粒子の製造方法、電気化学素子電極および電気化学素子
JP6954424B2 (ja) 電気化学素子電極用複合粒子、電気化学素子電極及び電気化学素子
JP6344384B2 (ja) 電気化学素子電極用複合粒子、電気化学素子電極用複合粒子の製造方法、電気化学素子電極および電気化学素子
KR102319301B1 (ko) 전기 화학 소자 전극용 복합 입자 및 전기 화학 소자 전극용 복합 입자의 제조 방법
JP6380526B2 (ja) 電気化学素子電極用複合粒子
WO2014192652A1 (fr) Liant destiné à être utilisé dans des électrodes de dispositif électrochimique, composite particulaire destiné à être utilisé dans des électrodes de dispositif électrochimique, électrode de dispositif électrochimique, dispositif électrochimique, et procédé de fabrication d'électrode pour dispositif électrochimique
JP6485359B2 (ja) 電気化学素子電極用複合粒子
JP6451934B2 (ja) 電気化学素子電極用複合粒子
JP6344143B2 (ja) 電気化学素子電極用複合粒子の製造方法、電気化学素子電極の製造方法及び電気化学素子の製造方法
JP2013077558A (ja) 電気化学素子用電極
JP2016024985A (ja) 電気化学素子電極用複合粒子、電気化学素子電極、電気化学素子、電気化学素子電極用複合粒子の製造方法及び電気化学素子電極の製造方法
JP2016024984A (ja) 電気化学素子電極用複合粒子、電気化学素子電極、電気化学素子、電気化学素子電極用複合粒子の製造方法及び電気化学素子電極の製造方法
JP6398461B2 (ja) 電気化学素子電極用複合粒子の製造方法
JP2016029630A (ja) 電気化学素子電極用複合粒子、電気化学素子電極、電気化学素子、電気化学素子電極用複合粒子の製造方法及び電気化学素子電極の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14875405

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015554771

Country of ref document: JP

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 20167012496

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14875405

Country of ref document: EP

Kind code of ref document: A1