WO2014126102A1 - Procédé de production pour film d'alignement de cristaux liquides, film d'alignement de cristaux liquides, élément d'affichage à cristaux liquides et agent d'alignement de cristaux liquides - Google Patents

Procédé de production pour film d'alignement de cristaux liquides, film d'alignement de cristaux liquides, élément d'affichage à cristaux liquides et agent d'alignement de cristaux liquides Download PDF

Info

Publication number
WO2014126102A1
WO2014126102A1 PCT/JP2014/053188 JP2014053188W WO2014126102A1 WO 2014126102 A1 WO2014126102 A1 WO 2014126102A1 JP 2014053188 W JP2014053188 W JP 2014053188W WO 2014126102 A1 WO2014126102 A1 WO 2014126102A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
carbon atoms
alignment film
crystal alignment
group
Prior art date
Application number
PCT/JP2014/053188
Other languages
English (en)
Japanese (ja)
Inventor
幸司 巴
奈穂 菊池
雅章 片山
徳俊 三木
Original Assignee
日産化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日産化学工業株式会社 filed Critical 日産化学工業株式会社
Priority to JP2015500256A priority Critical patent/JP6361887B6/ja
Priority to KR1020157024894A priority patent/KR102172134B1/ko
Priority to CN201480020966.XA priority patent/CN105122128B/zh
Publication of WO2014126102A1 publication Critical patent/WO2014126102A1/fr

Abstract

Selon l'invention, un agent d'alignement de cristaux liquides est appliqué sur un substrat et par la suite cuit pour obtenir un film d'alignement de cristaux liquides ayant un taux d'imidation de 50-70 %. L'agent d'alignement de cristaux liquides comprend : un précurseur de polyimide ayant des motifs répétés représentés par la formule [1] ; et au moins un polymère choisi parmi les polyimides qui ont des motifs répétés représentés par la formule [1] et qui ont un taux d'imidation inférieur à 50 % (dans la formule [1] : A1 représente un groupe organique divalent ; A2 représente un groupe organique divalent ; et C1 et C2 représentent chacun un atome d'hydrogène ou un groupe alkyle en C1-3 et peuvent être identiques l'un à l'autre ou différents l'un de l'autre).
PCT/JP2014/053188 2013-02-13 2014-02-12 Procédé de production pour film d'alignement de cristaux liquides, film d'alignement de cristaux liquides, élément d'affichage à cristaux liquides et agent d'alignement de cristaux liquides WO2014126102A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2015500256A JP6361887B6 (ja) 2013-02-13 2014-02-12 液晶配向膜の製造方法、液晶配向膜、液晶表示素子
KR1020157024894A KR102172134B1 (ko) 2013-02-13 2014-02-12 액정 배향막의 제조 방법, 액정 배향막, 액정 표시 소자 및 액정 배향제
CN201480020966.XA CN105122128B (zh) 2013-02-13 2014-02-12 液晶取向膜的制造方法、液晶取向膜、液晶表示元件和液晶取向剂

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013-026054 2013-02-13
JP2013026054 2013-02-13

Publications (1)

Publication Number Publication Date
WO2014126102A1 true WO2014126102A1 (fr) 2014-08-21

Family

ID=51354101

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/053188 WO2014126102A1 (fr) 2013-02-13 2014-02-12 Procédé de production pour film d'alignement de cristaux liquides, film d'alignement de cristaux liquides, élément d'affichage à cristaux liquides et agent d'alignement de cristaux liquides

Country Status (5)

Country Link
JP (1) JP6361887B6 (fr)
KR (1) KR102172134B1 (fr)
CN (1) CN105122128B (fr)
TW (1) TWI628202B (fr)
WO (1) WO2014126102A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021199974A1 (fr) * 2020-03-30 2021-10-07 日産化学株式会社 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
CN113635632A (zh) * 2018-07-25 2021-11-12 日东电工株式会社 光学薄膜及其制造方法、偏光板、以及图像显示装置

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20180101453A (ko) * 2016-01-07 2018-09-12 닛산 가가쿠 가부시키가이샤 액정 배향제, 액정 배향막 및 그것을 사용한 액정 표시 소자

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08208835A (ja) * 1995-01-31 1996-08-13 Japan Synthetic Rubber Co Ltd ポリイミド系共重合体の製造方法、薄膜形成剤、並びに液晶配向膜およびその製造方法
JPH08220542A (ja) * 1994-03-30 1996-08-30 Toray Ind Inc 液晶配向膜および液晶表示素子

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0840161B1 (fr) * 1996-05-16 2005-04-06 JSR Corporation Agent d'alignement de cristaux liquides
KR101775182B1 (ko) 2010-04-22 2017-09-05 닛산 가가쿠 고교 가부시키 가이샤 액정 배향 처리제, 액정 배향막 및 액정 표시 소자
CN103119509B (zh) * 2010-07-26 2015-08-19 日产化学工业株式会社 液晶取向处理剂、液晶取向膜及液晶显示元件
JP5879693B2 (ja) 2011-02-22 2016-03-08 Jsr株式会社 液晶配向剤、液晶配向膜及び液晶表示素子

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08220542A (ja) * 1994-03-30 1996-08-30 Toray Ind Inc 液晶配向膜および液晶表示素子
JPH08208835A (ja) * 1995-01-31 1996-08-13 Japan Synthetic Rubber Co Ltd ポリイミド系共重合体の製造方法、薄膜形成剤、並びに液晶配向膜およびその製造方法

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113635632A (zh) * 2018-07-25 2021-11-12 日东电工株式会社 光学薄膜及其制造方法、偏光板、以及图像显示装置
CN113635632B (zh) * 2018-07-25 2023-06-06 日东电工株式会社 光学薄膜及其制造方法、偏光板、以及图像显示装置
WO2021199974A1 (fr) * 2020-03-30 2021-10-07 日産化学株式会社 Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides

Also Published As

Publication number Publication date
CN105122128A (zh) 2015-12-02
KR102172134B1 (ko) 2020-10-30
KR20150119199A (ko) 2015-10-23
JP6361887B6 (ja) 2018-08-15
TW201446839A (zh) 2014-12-16
CN105122128B (zh) 2017-11-28
TWI628202B (zh) 2018-07-01
JP6361887B2 (ja) 2018-07-25
JPWO2014126102A1 (ja) 2017-02-02

Similar Documents

Publication Publication Date Title
JP6504377B2 (ja) 重合体
KR101951501B1 (ko) 액정 배향 처리제, 액정 배향막 및 액정 표시 소자
JP2020056034A (ja) 組成物、液晶配向処理剤、液晶配向膜及び液晶表示素子
WO2011132751A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides
JP5930239B2 (ja) 組成物、液晶配向処理剤、液晶配向膜および液晶表示素子
WO2014157235A1 (fr) Élément d'affichage à cristaux liquides, film d'alignement de cristaux liquides, et agent de traitement d'alignement à cristaux liquides
JP6331028B2 (ja) 液晶配向処理剤、液晶配向膜および液晶表示素子
JP5900337B2 (ja) 液晶配向処理剤、液晶配向膜及び液晶表示素子
JP6079627B2 (ja) 組成物、液晶配向処理剤、液晶配向膜及び液晶表示素子
JP6052171B2 (ja) 組成物、液晶配向処理剤、液晶配向膜及び液晶表示素子
WO2014092126A1 (fr) Composition, agent de traitement d'alignement de cristaux liquides, film d'alignement de cristaux liquides et élément d'affichage à cristaux liquides
KR20140120353A (ko) 액정 배향 처리제, 액정 배향막 및 액정 표시 소자
JP5930238B2 (ja) 組成物、液晶配向処理剤、液晶配向膜および液晶表示素子
JP6361887B2 (ja) 液晶配向膜の製造方法、液晶配向膜、液晶表示素子
WO2012121257A1 (fr) Composition, agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides, et élément d'affichage à cristaux liquides
WO2014133043A1 (fr) Agent d'alignement de cristaux liquides, film d'alignement de cristaux liquides et dispositif d'affichage à cristaux liquides

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14751141

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015500256

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20157024894

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 14751141

Country of ref document: EP

Kind code of ref document: A1