WO2014109223A1 - Composition polymérisable, produit polymérisé, feuille adhésive pour des applications optiques, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image - Google Patents

Composition polymérisable, produit polymérisé, feuille adhésive pour des applications optiques, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image Download PDF

Info

Publication number
WO2014109223A1
WO2014109223A1 PCT/JP2013/084476 JP2013084476W WO2014109223A1 WO 2014109223 A1 WO2014109223 A1 WO 2014109223A1 JP 2013084476 W JP2013084476 W JP 2013084476W WO 2014109223 A1 WO2014109223 A1 WO 2014109223A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
polymerizable composition
image display
present
polymer
Prior art date
Application number
PCT/JP2013/084476
Other languages
English (en)
Japanese (ja)
Inventor
一彦 大賀
律子 東
眸 上野
Original Assignee
昭和電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 昭和電工株式会社 filed Critical 昭和電工株式会社
Priority to JP2014556372A priority Critical patent/JPWO2014109223A1/ja
Publication of WO2014109223A1 publication Critical patent/WO2014109223A1/fr

Abstract

L'invention concerne une composition polymérisable pour former une couche de produit polymérisé qui est à interposer entre une partie d'affichage d'image et une partie de protection éettant la lumière d'un dispositif d'affichage d'image, ladite composition polymérisable étant utilisée pour la production d'un produit polymérisé qui est faible en retrait de volume pendant la polymérisation et est moins sensible à la coloration par la chaleur, tout en ayant une constante diélectrique élevée et une adhérence élevée à une matière telle que du verre qui est utilisée pour la partie de protection émettant la lumière. Une composition polymérisable de la présente invention contient (composant 1) un composé polymère contenant un groupe (méth)acryloyle ayant une masse moléculaire moyenne en nombre dans la plage de 1 000-10 000 et (composant 2) un initiateur de photopolymérisation. La constante diélectrique d'un produit polymérisé qui est obtenu par polymérisation de la composition est 5,0 ou plus telle que mesurée à 23°C à une fréquence de 1 MHz sous une application de tension de 100 mV.
PCT/JP2013/084476 2013-01-10 2013-12-24 Composition polymérisable, produit polymérisé, feuille adhésive pour des applications optiques, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image WO2014109223A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2014556372A JPWO2014109223A1 (ja) 2013-01-10 2013-12-24 重合性組成物、重合物、光学用粘着シート、画像表示装置およびその製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013-002737 2013-01-10
JP2013002737 2013-01-10

Publications (1)

Publication Number Publication Date
WO2014109223A1 true WO2014109223A1 (fr) 2014-07-17

Family

ID=51166880

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/084476 WO2014109223A1 (fr) 2013-01-10 2013-12-24 Composition polymérisable, produit polymérisé, feuille adhésive pour des applications optiques, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image

Country Status (3)

Country Link
JP (1) JPWO2014109223A1 (fr)
TW (1) TW201441326A (fr)
WO (1) WO2014109223A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015111584A1 (fr) * 2014-01-22 2015-07-30 旭硝子株式会社 Composition de résine durcissable et corps stratifié et dispositif d'affichage d'images utilisant la composition de résine durcissable
WO2016080084A1 (fr) * 2014-11-20 2016-05-26 協立化学産業株式会社 Composition de résine photodurcissable
JP2016196607A (ja) * 2015-04-06 2016-11-24 協立化学産業株式会社 光硬化型接着組成物
WO2018025700A1 (fr) * 2016-08-01 2018-02-08 デクセリアルズ株式会社 Composition de résine photodurcissable, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image
JP2018504476A (ja) * 2014-12-23 2018-02-15 エルジー・ケム・リミテッド 光学用粘接着組成物、これを多段硬化させる方法、及び画像表示装置
WO2018062524A1 (fr) * 2016-09-30 2018-04-05 日立化成株式会社 Film adhésif et composition durcissable
US20190031603A1 (en) * 2016-03-31 2019-01-31 Lg Chem, Ltd. Compound
JP2020148983A (ja) * 2019-03-15 2020-09-17 日本化薬株式会社 ディスプレイ用封止剤
JP2020148982A (ja) * 2019-03-15 2020-09-17 日本化薬株式会社 ディスプレイ用封止剤
JP2020172573A (ja) * 2019-04-09 2020-10-22 協立化学産業株式会社 光硬化型接着剤組成物
JP2021500445A (ja) * 2018-02-02 2021-01-07 エルジー・ケム・リミテッド フォルダブルディスプレイ用粘着剤組成物、それを用いた粘着フィルム、およびそれを含むフォルダブルディスプレイ
JP2021505853A (ja) * 2017-12-19 2021-02-18 ゲナ・ソシエテ・アノニム・モントレ・ヴァルジン 時計ガラス
JP2023011929A (ja) * 2019-04-09 2023-01-24 協立化学産業株式会社 光硬化型接着剤組成物

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008169319A (ja) * 2007-01-12 2008-07-24 Dic Corp 接着剤用硬化型樹脂組成物
JP2011094108A (ja) * 2009-09-30 2011-05-12 Daicel-Cytec Co Ltd 金属蒸着向けアンダーコート用樹脂組成物
JP2012214640A (ja) * 2011-03-31 2012-11-08 Sanyo Chem Ind Ltd 光学部品成型用紫外線硬化性樹脂組成物
JP2013003952A (ja) * 2011-06-20 2013-01-07 Nitto Denko Corp 静電容量タッチパネル

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008169319A (ja) * 2007-01-12 2008-07-24 Dic Corp 接着剤用硬化型樹脂組成物
JP2011094108A (ja) * 2009-09-30 2011-05-12 Daicel-Cytec Co Ltd 金属蒸着向けアンダーコート用樹脂組成物
JP2012214640A (ja) * 2011-03-31 2012-11-08 Sanyo Chem Ind Ltd 光学部品成型用紫外線硬化性樹脂組成物
JP2013003952A (ja) * 2011-06-20 2013-01-07 Nitto Denko Corp 静電容量タッチパネル

Cited By (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2015111584A1 (ja) * 2014-01-22 2017-03-23 旭硝子株式会社 硬化性樹脂組成物、ならびに、硬化性樹脂組成物を用いた積層体および画像表示装置
WO2015111584A1 (fr) * 2014-01-22 2015-07-30 旭硝子株式会社 Composition de résine durcissable et corps stratifié et dispositif d'affichage d'images utilisant la composition de résine durcissable
WO2016080084A1 (fr) * 2014-11-20 2016-05-26 協立化学産業株式会社 Composition de résine photodurcissable
JP2016098304A (ja) * 2014-11-20 2016-05-30 協立化学産業株式会社 光硬化性樹脂組成物
US10435598B2 (en) 2014-12-23 2019-10-08 Lg Chem, Ltd. Adhesive bonding composition for optical use, method for multistage curing thereof, and image display device
JP2018504476A (ja) * 2014-12-23 2018-02-15 エルジー・ケム・リミテッド 光学用粘接着組成物、これを多段硬化させる方法、及び画像表示装置
JP2016196607A (ja) * 2015-04-06 2016-11-24 協立化学産業株式会社 光硬化型接着組成物
US20190031603A1 (en) * 2016-03-31 2019-01-31 Lg Chem, Ltd. Compound
US10927073B2 (en) * 2016-03-31 2021-02-23 Lg Chem, Ltd. Compound for a curable composition
WO2018025700A1 (fr) * 2016-08-01 2018-02-08 デクセリアルズ株式会社 Composition de résine photodurcissable, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image
WO2018062524A1 (fr) * 2016-09-30 2018-04-05 日立化成株式会社 Film adhésif et composition durcissable
JP2019206601A (ja) * 2016-09-30 2019-12-05 日立化成株式会社 粘着フィルム及び硬化性組成物
JP2022123083A (ja) * 2017-12-19 2022-08-23 ゲナ・ソシエテ・アノニム・モントレ・ヴァルジン 時計ガラス
JP7368353B2 (ja) 2017-12-19 2023-10-24 ゲナ・ソシエテ・アノニム・モントレ・ヴァルジン 時計ガラス
JP2021505853A (ja) * 2017-12-19 2021-02-18 ゲナ・ソシエテ・アノニム・モントレ・ヴァルジン 時計ガラス
US11708512B2 (en) 2018-02-02 2023-07-25 Lg Chem, Ltd. Adhesive composition for foldable display, adhesive film using same, and foldable display comprising same
JP7136529B2 (ja) 2018-02-02 2022-09-13 エルジー・ケム・リミテッド フォルダブルディスプレイ用粘着剤組成物、それを用いた粘着フィルム、およびそれを含むフォルダブルディスプレイ
JP2021500445A (ja) * 2018-02-02 2021-01-07 エルジー・ケム・リミテッド フォルダブルディスプレイ用粘着剤組成物、それを用いた粘着フィルム、およびそれを含むフォルダブルディスプレイ
JP7164469B2 (ja) 2019-03-15 2022-11-01 日本化薬株式会社 液晶滴下工法用液晶シール剤
JP7149041B2 (ja) 2019-03-15 2022-10-06 日本化薬株式会社 ディスプレイ用封止剤
CN111690367A (zh) * 2019-03-15 2020-09-22 日本化药株式会社 显示器用密封剂及液晶显示器
JP2020148982A (ja) * 2019-03-15 2020-09-17 日本化薬株式会社 ディスプレイ用封止剤
TWI819200B (zh) * 2019-03-15 2023-10-21 日商日本化藥股份有限公司 顯示器用密封劑及液晶顯示器
JP2020148983A (ja) * 2019-03-15 2020-09-17 日本化薬株式会社 ディスプレイ用封止剤
JP2020172573A (ja) * 2019-04-09 2020-10-22 協立化学産業株式会社 光硬化型接着剤組成物
JP7181601B2 (ja) 2019-04-09 2022-12-01 協立化学産業株式会社 光硬化型接着剤組成物
JP2023011929A (ja) * 2019-04-09 2023-01-24 協立化学産業株式会社 光硬化型接着剤組成物
JP7233786B2 (ja) 2019-04-09 2023-03-07 協立化学産業株式会社 光硬化型接着剤組成物

Also Published As

Publication number Publication date
JPWO2014109223A1 (ja) 2017-01-19
TW201441326A (zh) 2014-11-01

Similar Documents

Publication Publication Date Title
WO2014109223A1 (fr) Composition polymérisable, produit polymérisé, feuille adhésive pour des applications optiques, dispositif d'affichage d'image et procédé de fabrication de dispositif d'affichage d'image
JP6124916B2 (ja) 重合性組成物、重合物、光学用粘着シート、画像表示装置およびその製造方法
JP6104244B2 (ja) 重合性組成物、重合物、光学用粘着シート、画像表示装置およびその製造方法
JP6069298B2 (ja) 重合性組成物、重合物、粘着シート、及び画像表示装置の製造方法
JP6072000B2 (ja) 重合性組成物、重合物、画像表示装置およびその製造方法
JP2015214594A (ja) 重合性組成物、重合物、光学用粘着シート、画像表示装置およびその製造方法
WO2014192502A1 (fr) Composition polymérisable, polymère, feuille adhésive optique, dispositif d'affichage d'image et son procédé de production
JP6226652B2 (ja) 画像表示装置の製造方法
JP6198597B2 (ja) 画像表示装置の製造方法およびその製造方法により製造された画像表示装置
JP6108918B2 (ja) 画像表示装置の製造方法
JPWO2020066866A1 (ja) 表面保護シート用粘着剤組成物及び表面保護シート
JP2015215373A (ja) 画像表示装置の製造方法および画像表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13871172

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2014556372

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13871172

Country of ref document: EP

Kind code of ref document: A1