WO2012164206A1 - Couche barriere aux alcalins - Google Patents

Couche barriere aux alcalins Download PDF

Info

Publication number
WO2012164206A1
WO2012164206A1 PCT/FR2012/051166 FR2012051166W WO2012164206A1 WO 2012164206 A1 WO2012164206 A1 WO 2012164206A1 FR 2012051166 W FR2012051166 W FR 2012051166W WO 2012164206 A1 WO2012164206 A1 WO 2012164206A1
Authority
WO
WIPO (PCT)
Prior art keywords
barrier layer
glazing according
glazing
layer
atomic ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/FR2012/051166
Other languages
English (en)
French (fr)
Inventor
Frédéric CLABAU
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Glass France SAS
Compagnie de Saint Gobain SA
Original Assignee
Saint Gobain Glass France SAS
Compagnie de Saint Gobain SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Saint Gobain Glass France SAS, Compagnie de Saint Gobain SA filed Critical Saint Gobain Glass France SAS
Priority to PL12731054T priority Critical patent/PL2714609T3/pl
Priority to KR1020137031462A priority patent/KR101968777B1/ko
Priority to CN201280026810.3A priority patent/CN103619774A/zh
Priority to JP2014513231A priority patent/JP2014516909A/ja
Priority to EA201391770A priority patent/EA024228B1/ru
Priority to US14/119,564 priority patent/US8828564B2/en
Priority to EP12731054.8A priority patent/EP2714609B1/fr
Priority to BR112013029198-2A priority patent/BR112013029198B1/pt
Publication of WO2012164206A1 publication Critical patent/WO2012164206A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/3411—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions with at least two coatings of inorganic materials
    • C03C17/3429—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions with at least two coatings of inorganic materials at least one of the coatings being a non-oxide coating
    • C03C17/3435—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions with at least two coatings of inorganic materials at least one of the coatings being a non-oxide coating comprising a nitride, oxynitride, boronitride or carbonitride
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/3411—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions with at least two coatings of inorganic materials
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C17/00—Surface treatment of glass, not in the form of fibres or filaments, by coating
    • C03C17/34—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions
    • C03C17/3411—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions with at least two coatings of inorganic materials
    • C03C17/3417—Surface treatment of glass, not in the form of fibres or filaments, by coating with at least two coatings having different compositions with at least two coatings of inorganic materials all coatings being oxide coatings
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/20—Materials for coating a single layer on glass
    • C03C2217/21—Oxides
    • C03C2217/213—SiO2
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/20—Materials for coating a single layer on glass
    • C03C2217/21—Oxides
    • C03C2217/214—Al2O3
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/20—Materials for coating a single layer on glass
    • C03C2217/21—Oxides
    • C03C2217/228—Other specific oxides
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/20—Materials for coating a single layer on glass
    • C03C2217/21—Oxides
    • C03C2217/23—Mixtures
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2217/00—Coatings on glass
    • C03C2217/20—Materials for coating a single layer on glass
    • C03C2217/28—Other inorganic materials
    • C03C2217/281—Nitrides

Definitions

  • the invention relates to a glazing unit incorporating a glass substrate comprising, on at least a portion of its surface, a stack of layers including a barrier layer for the migration of the alkaline ions contained in said substrate, of the sodium Na + , potassium K +, etc. type. .
  • Said layer is contiguous or placed in close proximity to the glass substrate and protects an upper layer.
  • Such a glazing thus comprises in particular one or more functional layers of the antisolar type, low emissive (low-e), antireflection, photocatalytic (self-cleaning glazing) or hydrophobic, that is to say a layer or a succession of layers which confers ( nt) to the glazing in question a particular property. It also finds its application in devices used for the recovery of solar light energy and comprising for example a layer of the type TCO (transparent conductive oxide), particularly in the field of photovoltaic cells or solar collectors.
  • TCO transparent conductive oxide
  • layers of silicon oxide, silicon nitride or silicon oxynitride are among the most used because they are effective and inexpensive to implement.
  • the object of the present invention is to provide such a glazing, provided with a barrier layer having such properties.
  • the present invention relates to a glazing incorporating a glass substrate comprising on at least a portion of its surface a stack of layers including a barrier layer to the migration of ions contained in said substrate, in particular alkaline Na + or K type + , said barrier layer being interposed in said stack between the surface of said substrate and at least one upper layer conferring on said glazing a sunscreen, low emission, antireflection, photocatalytic, hydrophobic or other, said barrier layer consisting mainly of a silicon oxide or a silicon oxynitride, said glazing being characterized in that said oxide or silicon oxynitride further comprises one or more elements selected from the group consisting of Al, Ga or B and in that the atomic ratio Si / X is strictly less than 92/8, X being the sum of the atomic contributions of said elements Al, Ga and B.
  • the Si / X atomic ratio is less than 92/8 and greater than 70/30, preferably greater than 80/20,
  • the Si / X atomic ratio is less than 90/10, preferably less than 88/12,
  • the element X is aluminum
  • the element X is Gallium
  • the element X is the boron
  • the barrier layer comprises at least two elements chosen from boron, gallium and aluminum,
  • the barrier layer is a silicon oxide
  • the barrier layer is a silicon oxynitride
  • the barrier layer is a silicon oxynitride in which the atomic ratio N / O is greater than 10/90, preferably greater than 20/80.
  • the invention also relates to a glazing further provided with a second layer identical to the first barrier layer as previously described, but disposed above said functional layer.
  • its Si / X atomic ratio of said second layer is less than 90/10, preferably less than 88/12,
  • Si / X atomic ratio is less than 90/10, preferably greater than 88/12,
  • the element X is aluminum
  • the element X is Gallium
  • the element X is the boron
  • the second layer comprises at least two elements chosen from boron, gallium and aluminum,
  • the second layer is a silicon oxide
  • the second layer is a silicon oxynitride, for example in which the atomic ratio N / O is greater than 10/90, preferably greater than 20/80.
  • barrier layers consisting of a silicon oxide, of which at least a part of the silicon atoms are substituted by Al or B, have been deposited on soda-lime glass substrates with a thickness of 2 mm, sold under the reference PL .ANILUX® by the applicant company.
  • the barrier layers are obtained in magnetic field assisted magnetron sputtering (magnetron) chambers.
  • Two targets one of Si0 2 and the other of Al 2 0 3 or B 2 0 3 are used as cathodes and co-sprayed by an argon gas plasma in the chamber. Before the deposits, a vacuum is made in the enclosure until reaching a residual value of 0.5 millipascals (mPa), according to techniques well known in the art.
  • mPa millipascals
  • SiAlO denotes a barrier layer of an oxide of silicon and aluminum
  • SiBO denotes a barrier layer of a silicon oxide and boron
  • SiXO denotes a barrier layer of a silicon oxide and an element X, X being aluminum or boron.
  • the Si / X ratio varies over the length of the substrate because of the variation between each point of the surface of this substrate and each of the two targets (one in Si0 2 and the other in Al 2 0 3 or B 2 0 3 ) .
  • the deposition time is adjusted to collect a layer thickness of about 100 nanometers.
  • this first barrier layer is deposited according to conventional techniques in a magnetic field assisted sputtering chamber (magnetron) a functional layer of transparent conductive oxide (TCO) of the type AZO, consisting of ZnO doped with aluminum (2). percent aluminum oxide weight).
  • TCO transparent conductive oxide
  • the thickness of this functional layer is about 200 nm. Table 2 below summarizes the different examples made:
  • the substrates thus coated with the stacks constituted by the barrier layer and the TCO layer are then subjected to a heat treatment consisting of heating at 600 ° C. for 1 hour, in order to calibrate the performances of the various barrier layers synthesized.
  • the AZO layer disposed at the surface of the stack is much better protected alkaline in the case where the barrier layer of silicon oxide comprises a large amount of aluminum or boron according to the invention.
  • the invention in particular aluminum or boron atomic contents of more than 8%, 9% or even 10%, based on the sum of the silicon atoms present in said barrier layers.
  • the concentration of Sodium in the functional layer AZO can be divided by a factor of 10 by virtue of the fact that of a protective layer according to the invention. Additional identical tests, but carried out with barrier layers consisting of silicon oxynitride (with a N / O atomic ratio close to 1) doped in the same manner, gave substantially identical results.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Surface Treatment Of Glass (AREA)
  • Laminated Bodies (AREA)
PCT/FR2012/051166 2011-05-30 2012-05-24 Couche barriere aux alcalins Ceased WO2012164206A1 (fr)

Priority Applications (8)

Application Number Priority Date Filing Date Title
PL12731054T PL2714609T3 (pl) 2011-05-30 2012-05-24 Warstwa zaporowa przed metalami alkalicznymi
KR1020137031462A KR101968777B1 (ko) 2011-05-30 2012-05-24 알칼리 차단층
CN201280026810.3A CN103619774A (zh) 2011-05-30 2012-05-24 碱金属阻挡层
JP2014513231A JP2014516909A (ja) 2011-05-30 2012-05-24 アルカリバリア層
EA201391770A EA024228B1 (ru) 2011-05-30 2012-05-24 Остекление
US14/119,564 US8828564B2 (en) 2011-05-30 2012-05-24 Alkali-barrier layer
EP12731054.8A EP2714609B1 (fr) 2011-05-30 2012-05-24 Couche barriere aux alcalins
BR112013029198-2A BR112013029198B1 (pt) 2011-05-30 2012-05-24 Vidraça que incorpora um substrato de vidro

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
FR1154698 2011-05-30
FR1154698A FR2975989B1 (fr) 2011-05-30 2011-05-30 Couche barriere aux alcalins

Publications (1)

Publication Number Publication Date
WO2012164206A1 true WO2012164206A1 (fr) 2012-12-06

Family

ID=46420370

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/FR2012/051166 Ceased WO2012164206A1 (fr) 2011-05-30 2012-05-24 Couche barriere aux alcalins

Country Status (10)

Country Link
US (1) US8828564B2 (cg-RX-API-DMAC7.html)
EP (1) EP2714609B1 (cg-RX-API-DMAC7.html)
JP (1) JP2014516909A (cg-RX-API-DMAC7.html)
KR (1) KR101968777B1 (cg-RX-API-DMAC7.html)
CN (1) CN103619774A (cg-RX-API-DMAC7.html)
BR (1) BR112013029198B1 (cg-RX-API-DMAC7.html)
EA (1) EA024228B1 (cg-RX-API-DMAC7.html)
FR (1) FR2975989B1 (cg-RX-API-DMAC7.html)
PL (1) PL2714609T3 (cg-RX-API-DMAC7.html)
WO (1) WO2012164206A1 (cg-RX-API-DMAC7.html)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3018802A1 (fr) * 2014-03-19 2015-09-25 Saint Gobain Substrat verrier a couche electroconductrice et tendance diminuee a la delamination
FR3018801A1 (fr) * 2014-03-19 2015-09-25 Saint Gobain Substrat verrier a couche electroconductrice et rugosite diminuee

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7439769B2 (ja) * 2018-12-26 2024-02-28 Ａｇｃ株式会社 撥水撥油層付き基材、およびその製造方法
GB201910988D0 (en) * 2019-08-01 2019-09-18 Pilkington Group Ltd Touchenable coated substrate

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020172775A1 (en) * 2000-10-24 2002-11-21 Harry Buhay Method of making coated articles and coated articles made thereby
US20030165693A1 (en) * 2002-03-01 2003-09-04 Klaus Hartig Thin film coating having transparent base layer
US20080241523A1 (en) * 2004-02-24 2008-10-02 Saint-Gobain Glass France Substrate, Such As A Glass Substrate, With A Hydrophobic Surface And Improved Durability Of Hydrophobic Properties
US20090084438A1 (en) 2006-11-02 2009-04-02 Guardian Industries Corp., Front electrode for use in photovoltaic device and method of making same
US20100326817A1 (en) * 2007-09-14 2010-12-30 Cardinal Cg Company Low-maintenance coatings, and methods for producing low-maintenance coatings
US20110203578A1 (en) * 2010-02-19 2011-08-25 Ppg Industries Ohio, Inc. Solar reflecting mirror and method of making same
WO2011101444A1 (de) * 2010-02-18 2011-08-25 Von Ardenne Anlagentechnik Gmbh Wärmebehandelbares infrarotstrahlung reflektierendes schichtsystem und verfahren zu dessen herstellung

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS57100940A (en) * 1980-12-10 1982-06-23 Asahi Glass Co Ltd Substrate coated with silicon oxide having high durability
JP2696877B2 (ja) * 1988-02-12 1998-01-14 日本板硝子株式会社 可視光透過性を有する熱線反射板
JPH02217337A (ja) * 1989-02-16 1990-08-30 Nippon Sheet Glass Co Ltd 膜付きガラス基板の製造方法
FR2728559B1 (fr) * 1994-12-23 1997-01-31 Saint Gobain Vitrage Substrats en verre revetus d'un empilement de couches minces a proprietes de reflexion dans l'infrarouge et/ou dans le domaine du rayonnement solaire
FR2759362B1 (fr) * 1997-02-10 1999-03-12 Saint Gobain Vitrage Substrat transparent muni d'au moins une couche mince a base de nitrure ou d'oxynitrure de silicium et son procede d'obtention
US6495251B1 (en) * 1997-06-20 2002-12-17 Ppg Industries Ohio, Inc. Silicon oxynitride protective coatings
US6398925B1 (en) * 1998-12-18 2002-06-04 Ppg Industries Ohio, Inc. Methods and apparatus for producing silver based low emissivity coatings without the use of metal primer layers and articles produced thereby
ES2258477T3 (es) * 1999-10-14 2006-09-01 Glaverbel Vidrio.
US20020136905A1 (en) * 1999-11-24 2002-09-26 Medwick Paul A. Low shading coefficient and low emissivity coatings and coated articles
JP4382943B2 (ja) * 2000-01-13 2009-12-16 日本板硝子株式会社 真空容器型ディスプレイ用基板の製造方法
US7267879B2 (en) * 2001-02-28 2007-09-11 Guardian Industries Corp. Coated article with silicon oxynitride adjacent glass
US20030228476A1 (en) * 2001-10-22 2003-12-11 Harry Buhay Methods of changing the visible light transmittance of coated articles and coated articles made thereby
AU2003210976A1 (en) * 2002-02-11 2003-09-04 Ppg Industries Ohio, Inc. Solar control coating
FR2861386B1 (fr) * 2003-10-23 2006-02-17 Saint Gobain Substrat, notamment substrat verrier, portant une couche a propriete photocatalytique revetue d'une couche mince protectrice.
DE10356357B4 (de) * 2003-11-28 2010-05-06 Von Ardenne Anlagentechnik Gmbh Wärmebehandelbares Sonnen- und Wärmeschutzschichtsystem und Verfahren zu dessen Herstellung
US7153578B2 (en) * 2004-12-06 2006-12-26 Guardian Industries Corp Coated article with low-E coating including zirconium silicon oxynitride and methods of making same
US8815420B2 (en) * 2010-09-17 2014-08-26 Guardian Industries Corp. Coated article having zinc oxide seed layer with reduced stress under functional layer and method of making the same
US8808882B2 (en) * 2010-09-17 2014-08-19 Guardian Industries Corp. Coated article having boron doped zinc oxide based seed layer with enhanced durability under functional layer and method of making the same
US8530011B2 (en) * 2010-12-13 2013-09-10 Southwall Technologies Inc. Insulating glass unit with crack-resistant low-emissivity suspended film
US8728636B2 (en) * 2010-12-13 2014-05-20 Southwall Technologies Inc. Insulating glass unit with crack-resistant low-emissivity suspended film

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020172775A1 (en) * 2000-10-24 2002-11-21 Harry Buhay Method of making coated articles and coated articles made thereby
US20030165693A1 (en) * 2002-03-01 2003-09-04 Klaus Hartig Thin film coating having transparent base layer
US20080241523A1 (en) * 2004-02-24 2008-10-02 Saint-Gobain Glass France Substrate, Such As A Glass Substrate, With A Hydrophobic Surface And Improved Durability Of Hydrophobic Properties
US20090084438A1 (en) 2006-11-02 2009-04-02 Guardian Industries Corp., Front electrode for use in photovoltaic device and method of making same
US20100326817A1 (en) * 2007-09-14 2010-12-30 Cardinal Cg Company Low-maintenance coatings, and methods for producing low-maintenance coatings
WO2011101444A1 (de) * 2010-02-18 2011-08-25 Von Ardenne Anlagentechnik Gmbh Wärmebehandelbares infrarotstrahlung reflektierendes schichtsystem und verfahren zu dessen herstellung
US20110203578A1 (en) * 2010-02-19 2011-08-25 Ppg Industries Ohio, Inc. Solar reflecting mirror and method of making same

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR3018802A1 (fr) * 2014-03-19 2015-09-25 Saint Gobain Substrat verrier a couche electroconductrice et tendance diminuee a la delamination
FR3018801A1 (fr) * 2014-03-19 2015-09-25 Saint Gobain Substrat verrier a couche electroconductrice et rugosite diminuee

Also Published As

Publication number Publication date
KR20140026539A (ko) 2014-03-05
US20140199552A1 (en) 2014-07-17
EP2714609B1 (fr) 2018-01-10
US8828564B2 (en) 2014-09-09
EA201391770A1 (ru) 2014-03-31
EA024228B1 (ru) 2016-08-31
FR2975989B1 (fr) 2014-04-25
KR101968777B1 (ko) 2019-04-12
CN103619774A (zh) 2014-03-05
BR112013029198B1 (pt) 2020-09-15
PL2714609T3 (pl) 2018-06-29
FR2975989A1 (fr) 2012-12-07
BR112013029198A2 (pt) 2017-04-18
JP2014516909A (ja) 2014-07-17
EP2714609A1 (fr) 2014-04-09

Similar Documents

Publication Publication Date Title
FR2919430A1 (fr) Substrat de face avant de cellule photovoltaique et utilisation d'un substrat pour une face avant de cellule photovoltaique.
CA2806251C (fr) Vitrage a proprietes antisolaires
EP1120383A2 (fr) Substrats revetus d'un empilement de couches minces, a proprietes de reflexion dans l'infrarouge et/ou sur le rayonnement solaire
EP1663895A1 (fr) Substrat transparent revetu d un empilement de couches mince s a proprietes de reflexion dans l infrarouge et/ou dans le domaine du rayonnement solaire
WO2010063973A1 (fr) Substrat de face avant de panneau photovoltaïque, panneau photovoltaïque et utilisation d'un substrat pour une face avant de panneau photovoltaïque
EP2714609B1 (fr) Couche barriere aux alcalins
FR2981646A1 (fr) Vitrage de controle solaire comprenant une couche d'un alliage nicu
WO2019002737A1 (fr) Vitrage a proprietes antisolaires comprenant une couche d'oxynitrure de titane
EP3917895A1 (fr) Substrat muni d'un empilement a proprietes thermiques et a couche absorbante
EP4110739A1 (fr) Vitrage de controle solaire comprenant une couche de nitrure de titane
BE1019826A3 (fr) Substrat verrier transparent conducteur pour cellule photovoltaique.
EP3055265A1 (fr) Vitrage de contrôle thermique
FR3068031B1 (fr) Vitrage a proprietes antisolaires comprenant une couche d'oxynitrure de titane
WO2010001014A2 (fr) Cellule photovoltaïque et substrat de cellule photovoltaïque
EP2130070A1 (fr) Miroir a reflexion elevee
WO2021063921A1 (fr) Vitrage comprenant un empilement antisolaire et un revêtement protecteur comprenant de l'yttrium
EP3419946B1 (fr) Vitrage de contrôle solaire comprenant une couche d'un alliage nicucr
WO2014006322A1 (fr) Vitrage isolant
FR3131742A1 (fr) Vitrage contrôle solaire
CA2910317A1 (fr) Vitrage de controle solaire comprenant une couche d'un alliage de zinc et de cuivre
FR3131741A1 (fr) Vitrage contrôle solaire

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12731054

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2012731054

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 20137031462

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2014513231

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 201391770

Country of ref document: EA

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112013029198

Country of ref document: BR

WWE Wipo information: entry into national phase

Ref document number: 14119564

Country of ref document: US

ENP Entry into the national phase

Ref document number: 112013029198

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20131112