WO2011125952A1 - Mousse de polyuréthane flexible pour moulage par presse à chaud, procédé pour la produire, article moulé par presse à chaud, et procédé pour le produire - Google Patents

Mousse de polyuréthane flexible pour moulage par presse à chaud, procédé pour la produire, article moulé par presse à chaud, et procédé pour le produire Download PDF

Info

Publication number
WO2011125952A1
WO2011125952A1 PCT/JP2011/058458 JP2011058458W WO2011125952A1 WO 2011125952 A1 WO2011125952 A1 WO 2011125952A1 JP 2011058458 W JP2011058458 W JP 2011058458W WO 2011125952 A1 WO2011125952 A1 WO 2011125952A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyol
polyurethane foam
hot press
mass
flexible polyurethane
Prior art date
Application number
PCT/JP2011/058458
Other languages
English (en)
Japanese (ja)
Inventor
孝之 佐々木
賀来　大輔
Original Assignee
旭硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 旭硝子株式会社 filed Critical 旭硝子株式会社
Publication of WO2011125952A1 publication Critical patent/WO2011125952A1/fr

Abstract

L'invention concerne une mousse de polyuréthane flexible sur laquelle un moulage par presse à chaud peut être efficacement mis en œuvre et qui a une fermeté suffisante et une excellente aptitude au traitement pendant la découpe. La mousse de polyuréthane flexible pour moulage par presse à chaud est produite en faisant réagir un mélange de polyols (X) et un composé isocyanate en présence d'un catalyseur d'uréthanation, d'un agent de moussage, et d'un stabilisant de mousse. Le mélange de polyols (X) comprend : un polyoxyalkylène polyol (A) dans lequel le nombre moyen de groupes hydroxyle est de 2 à 3, l'indice d'hydroxyle est de 5 à 90 mg de KOH/g et la teneur en groupes oxyéthylène est de 0 à 30 % en masse; un polyoxyalkylène polyol (B) dans lequel le nombre moyen de groupes hydroxyle est de 2 à 3 et l'indice d'hydroxyle est de 100 à 250 mg de KOH/g; et un polyoxyalkylène mono-ol (D) dans lequel l'indice d'hydroxyle est de 10 à 200 mg de KOH/g. La quantité de composé polyisocyanate utilisé est de 90 ou plus sur l'indice d'isocyanate.
PCT/JP2011/058458 2010-04-02 2011-04-01 Mousse de polyuréthane flexible pour moulage par presse à chaud, procédé pour la produire, article moulé par presse à chaud, et procédé pour le produire WO2011125952A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010086124A JP2013127011A (ja) 2010-04-02 2010-04-02 熱プレス成形用軟質ポリウレタンフォームおよびその製造方法、ならびに熱プレス成形品およびその製造方法
JP2010-086124 2010-04-02

Publications (1)

Publication Number Publication Date
WO2011125952A1 true WO2011125952A1 (fr) 2011-10-13

Family

ID=44762890

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/058458 WO2011125952A1 (fr) 2010-04-02 2011-04-01 Mousse de polyuréthane flexible pour moulage par presse à chaud, procédé pour la produire, article moulé par presse à chaud, et procédé pour le produire

Country Status (3)

Country Link
JP (1) JP2013127011A (fr)
TW (1) TW201202287A (fr)
WO (1) WO2011125952A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018190051A1 (fr) * 2017-04-12 2018-10-18 豊和繊維工業株式会社 Matériau de revêtement utilisé dans un plafond moulé pour véhicules
WO2019110726A1 (fr) 2017-12-08 2019-06-13 Shell Internationale Research Maatschappij B.V. Antioxydant pour mousse de polyuréthane de faible densité
JP2020019390A (ja) * 2018-08-01 2020-02-06 住友ゴム工業株式会社 制音体付き空気入りタイヤ，及びその製造方法
CN113480705A (zh) * 2021-08-23 2021-10-08 安徽美世嘉新材料有限公司 一种超低温内衣模压成型绵及其制备方法
CN115304744A (zh) * 2022-09-16 2022-11-08 中山成长鞋材有限公司 一种低温热压内衣泡棉及其制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20130122560A (ko) * 2012-04-30 2013-11-07 (주)아모레퍼시픽 화장용 퍼프
US9498927B2 (en) * 2013-03-15 2016-11-22 Nike, Inc. Decorative foam and method

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002293867A (ja) * 2001-03-28 2002-10-09 Mitsui Chemicals Inc 軟質ポリウレタンフォーム及びその製造方法
JP2004300352A (ja) * 2003-03-31 2004-10-28 Sanyo Chem Ind Ltd 低反発ポリウレタンフォームの製造方法
WO2006115169A1 (fr) * 2005-04-21 2006-11-02 Asahi Glass Company, Limited Mousse tendre de polyurethane de faible resilience et son procede de production
WO2008050841A1 (fr) * 2006-10-25 2008-05-02 Asahi Glass Company, Limited Procédé de production d'une mousse de polyuréthane souple
WO2009041535A1 (fr) * 2007-09-28 2009-04-02 Asahi Glass Company, Limited Procédé de fabrication d'une mousse flexible de polyuréthane, procédé de fabrication d'un article moulé par pressage à chaud et article moulé par pressage à chaud

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002293867A (ja) * 2001-03-28 2002-10-09 Mitsui Chemicals Inc 軟質ポリウレタンフォーム及びその製造方法
JP2004300352A (ja) * 2003-03-31 2004-10-28 Sanyo Chem Ind Ltd 低反発ポリウレタンフォームの製造方法
WO2006115169A1 (fr) * 2005-04-21 2006-11-02 Asahi Glass Company, Limited Mousse tendre de polyurethane de faible resilience et son procede de production
WO2008050841A1 (fr) * 2006-10-25 2008-05-02 Asahi Glass Company, Limited Procédé de production d'une mousse de polyuréthane souple
WO2009041535A1 (fr) * 2007-09-28 2009-04-02 Asahi Glass Company, Limited Procédé de fabrication d'une mousse flexible de polyuréthane, procédé de fabrication d'un article moulé par pressage à chaud et article moulé par pressage à chaud

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018190051A1 (fr) * 2017-04-12 2018-10-18 豊和繊維工業株式会社 Matériau de revêtement utilisé dans un plafond moulé pour véhicules
WO2019110726A1 (fr) 2017-12-08 2019-06-13 Shell Internationale Research Maatschappij B.V. Antioxydant pour mousse de polyuréthane de faible densité
JP2020019390A (ja) * 2018-08-01 2020-02-06 住友ゴム工業株式会社 制音体付き空気入りタイヤ，及びその製造方法
WO2020027115A1 (fr) * 2018-08-01 2020-02-06 住友ゴム工業株式会社 Pneu avec amortisseur acoustique, et procédé de fabrication dudit pneu
EP3822091A4 (fr) * 2018-08-01 2022-04-06 Sumitomo Rubber Industries, Ltd. Pneu avec amortisseur acoustique, et procédé de fabrication dudit pneu
JP7089433B2 (ja) 2018-08-01 2022-06-22 住友ゴム工業株式会社 制音体付き空気入りタイヤ，及びその製造方法
CN113480705A (zh) * 2021-08-23 2021-10-08 安徽美世嘉新材料有限公司 一种超低温内衣模压成型绵及其制备方法
CN115304744A (zh) * 2022-09-16 2022-11-08 中山成长鞋材有限公司 一种低温热压内衣泡棉及其制备方法
CN115304744B (zh) * 2022-09-16 2024-05-31 中山成长鞋材有限公司 一种低温热压内衣泡棉及其制备方法

Also Published As

Publication number Publication date
TW201202287A (en) 2012-01-16
JP2013127011A (ja) 2013-06-27

Similar Documents

Publication Publication Date Title
JP5266756B2 (ja) 低反発性軟質ポリウレタンフォームおよびその製造方法
JP3909598B2 (ja) 低反発軟質ポリウレタンフォームの製造方法
JP5228914B2 (ja) 軟質ポリウレタンフォームの製造方法
JP5720571B2 (ja) 軟質ポリウレタンフォームの製造方法
EP2565215B1 (fr) Polyoxyalkylène-polyol, polyol dans lequel un polymère est dispersé, mousse de polyuréthane flexible, et procédés pour la production de ceux-ci
JP4910702B2 (ja) 軟質ポリウレタンフォームの製造方法
JP5229229B2 (ja) 軟質ポリウレタンフォームおよび熱プレス成形品の製造方法
EP1316571B1 (fr) Mousse de polyuréthane flexible et procédé pour sa préparation
WO2011125952A1 (fr) Mousse de polyuréthane flexible pour moulage par presse à chaud, procédé pour la produire, article moulé par presse à chaud, et procédé pour le produire
WO2001079323A1 (fr) Procede de production de mousse de polyurethane flexible
WO2011125951A1 (fr) Mousse de polyuréthane flexible et procédé pour la produire
JP4058954B2 (ja) 軟質ポリウレタンフォーム
JPWO2013021871A1 (ja) 軟質ポリウレタンフォームの製造方法
JP4412116B2 (ja) 低反発性軟質ポリウレタンフォームおよびその製造方法
JP4529300B2 (ja) 軟質ポリウレタンフォームの製造方法
JPWO2012115113A1 (ja) 低反発性軟質ポリウレタンフォームおよびその製造方法
JP2008031241A (ja) 軟質ポリウレタンフォームの製造方法
JPWO2003059980A1 (ja) 軟質ポリウレタンフォームの製造方法
JP4182733B2 (ja) 軟質ポリウレタンフォームおよびその製造方法
JP5151461B2 (ja) 軟質ポリウレタンフォームの製造方法およびその用途
JP2003231747A (ja) ポリオールとその製造方法および軟質ポリウレタンフォームの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11765852

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11765852

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP