WO2011051385A2 - Zeitmodifiziert feuchtigkeitsaushärtende formulierungen - Google Patents
Zeitmodifiziert feuchtigkeitsaushärtende formulierungen Download PDFInfo
- Publication number
- WO2011051385A2 WO2011051385A2 PCT/EP2010/066349 EP2010066349W WO2011051385A2 WO 2011051385 A2 WO2011051385 A2 WO 2011051385A2 EP 2010066349 W EP2010066349 W EP 2010066349W WO 2011051385 A2 WO2011051385 A2 WO 2011051385A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- curable composition
- component
- compound
- weight
- groups
- Prior art date
Abstract
Description
Claims