WO2010119770A1 - プラスチックフィルム挿入合わせガラスの製造方法 - Google Patents

プラスチックフィルム挿入合わせガラスの製造方法 Download PDF

Info

Publication number
WO2010119770A1
WO2010119770A1 PCT/JP2010/055832 JP2010055832W WO2010119770A1 WO 2010119770 A1 WO2010119770 A1 WO 2010119770A1 JP 2010055832 W JP2010055832 W JP 2010055832W WO 2010119770 A1 WO2010119770 A1 WO 2010119770A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
plastic film
resin intermediate
glass
laminated
Prior art date
Application number
PCT/JP2010/055832
Other languages
English (en)
French (fr)
Inventor
健介 泉谷
敦 高松
浩道 坂本
功 中村
Original Assignee
セントラル硝子株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by セントラル硝子株式会社 filed Critical セントラル硝子株式会社
Publication of WO2010119770A1 publication Critical patent/WO2010119770A1/ja

Abstract

室外側ガラス板、樹脂中間膜、プラスチックフィルム、樹脂中間膜、室内側ガラス板の順に積層してなるプラスチックフィルム挿入合わせガラスにおいて、ガラス板の周辺部に不透明な着色膜が形成され、該ガラス板の透視面積より大きく、ガラス板より小さい面積に裁断されたプラスチックフィルムを２枚の樹脂中間膜に挟み込み、プラスチックフィルムの周辺部で、中間膜をプラスチックフィルムあるいはもう一枚の樹脂中間膜と熱融着されてなる積層中間膜を作製することを特徴とする。

Description

プラスチックフィルム挿入合わせガラスの製造方法
 ガラス板、樹脂中間膜、透明なプラスチックフィルム、樹脂中間膜、ガラス板をこの順に積層して作製される合わせガラスの製造方法に関し、特に、自動車の窓に用いられる合わせガラスの製造方法に関する。
 プラスチックフィルム、特にポリエチレンテレフタレートフィルムを挟持した２枚の樹脂中間膜を用いて、２枚のガラス板を積層したものが、熱線反射機能を持たせた合わせガラスとして、知られている。
 通常、合わせガラスは、オートクレーブを用いて、高温高圧処理され、ガラス板とポリエステルフィルムが、樹脂中間膜により熱融着される。
 例えば、特許文献１では、薄膜がポリエステルフィルムに形成されてなる熱線反射プラスチックフィルムを、２枚の樹脂中間膜で挟持した可撓性積層体を、２枚のガラス板の間に挟んで積層される、合わせガラスが開示されている。
 また、特許文献２には、赤外線反射膜が形成されているＰＥＴフィルムあるいはＰＥＮフィルムを、１９９～２０４℃あるいは２２７～２４３℃で加熱し、曲面に前記ＰＥＴフィルムあるいはＰＥＮフィルムを用いるときに、熱収縮によってシワが生じないようにすることが開示されている。
 さらに、特許文献３において、３０～７０μｍの厚さで、延伸方向で０．３～０．６％の熱収縮率を有する二軸延伸された熱可塑性支持体フィルムを用いたプラスチックフィルム挿入合わせガラスの製造方法が開示されている。
 赤外線反膜が形成されたプラスチックフィルムに関しては、特許文献４にはＡｇ等の金属でなる赤外線反射膜がプラスチックに形成されたものが、特許文献５には、屈折率の異なる誘電体を積層してなる赤外線反射膜がプラスチックフィルムに形成してなるものが、また特許文献６には、屈折率の異なる樹脂膜をプラスチックフィルムに積層してなるものが開示されている。
特開昭５６－３２３５２号公報 特表２００４－５０３４０２号公報 特許３６６９７０９号公報 特開２００７－２９１５２９号公報 特開２００７－１４８３３０号公報 特開２００６－２０５７２９号公報
 プラスチックフィルムを樹脂中間膜の間に挟持し、これを２枚のガラス板の間に挟持した合わせガラスを作製するとき、曲面形状に曲げられているガラス板の場合、プラスチックフィルムにシワが生じ、外観欠陥となる。
 本発明は、曲面形状に曲げられているガラス板を用いてプラスチックフィルム挿入合わせガラスを作製する場合、プラスチックフィルムにシワの生じない製造方法の提供を課題とする。
本発明に係るプラスチックフィルム挿入合わせガラスの製造方法は、曲げ加工によって湾曲した形状の２枚のガラス板と、２枚の樹脂中間膜と、赤外線反射膜が形成されてなるプラスチックフィルムとが、ガラス板、樹脂中間膜、プラスチックフィルム、樹脂中間膜、ガラス板の順に積層されてなるプラスチックフィルム挿入合わせガラスの製造方法において、少なくとも１枚のガラス板の周辺部に不透明な着色膜を形成し、次の工程１～３で積層中間膜を作製し、該積層中間膜を２枚のガラス板の間に挿入して、加熱・加圧処理を行うことを特徴とするプラスチックフィルム挿入合わせガラスの製造方法である。
工程１：プラスチックフィルムと１枚の樹脂中間膜とを加熱圧着した加熱圧着膜を作製する工程。
 工程２：加熱圧着膜のプラスチックフィルムを、プラスチックフィルムのエッジがガラス板の不透明な着色膜に全周で重なる形状で、かつガラス板の面積よりも小さい面積に裁断し、プラスチックフィルムの不要部を樹脂中間膜から剥がし取る工程。
 工程３：樹脂中間膜に加熱圧着されたプラスチックフィルム側にもう1枚の樹脂中間膜を重ね、重なり合う樹脂中間膜と樹脂中間膜とを、あるいは樹脂中間膜とプラスチックフィルムとを、プラスチックフィルムの辺に平行な線状に熱融着する工程。
 また、本発明に係るプラスチックフィルム挿入合わせガラスの製造方法は、前記プラスチックフィルム挿入合わせガラスの製造方法において、加熱圧着膜を加熱ロールを用いて作製することを特徴とするプラスチックフィルム挿入合わせガラスの製造方法である。
 また、本発明に係るプラスチックフィルム挿入合わせガラスの製造方法は、前記プラスチックフィルム挿入合わせガラスの製造方法において、熱融着に線状の加熱体を有する加熱装置を用いるか、あるいはレーザー光を照射して熱融着することを特徴とするプラスチックフィルム挿入合わせガラスの製造方法である。
 ２枚の樹脂中間膜でプラスチックフィルムを挟持した積層膜により、同形状に湾曲した２枚のガラス板を用いて作製されるプラスチック挿入合わせガラスに関し、プラスチックフィルムにシワが生じない、外観が良好なプラスチックフィルム挿入合わせガラスの製造方法を提供する。
 特に、自動車や車両の窓に用いられているガラスのように、場所によって、また同じ場所でも方向によって、曲率半径が異なるような、湾曲したガラスを用いて合わせガラスを作製する場合に、プラスチックフィルムにシワを生じないプラスチックフィルム挿入合わせガラスの作製を可能とする。
本発明に係るプラスチックフィルム挿入合わせガラスの概略平面図を示す。 図１の線ａ－ａ´に沿った断面図を示す。 図１のプラスチックフィルム挿入合わせガラスの端部概略断面図を示す。 プラスチックフィルムと樹脂中間膜との加熱圧着膜を作製する方法を示す概略断面図である。 樹脂中間膜にプラスチックフィルムが加熱圧着された加熱圧着膜を示す断面図である。 樹脂中間膜にプラスチックフィルムが加熱圧着された加熱圧着膜を示す断面図である。 加熱圧着膜のプラスチックフィルムが裁断されているところを示す平面図である。 加熱圧着膜のプラスチックフィルムが裁断されているところを示す断面図である。 加熱圧着膜のプラスチックフィルムが所定形状（ガラス板の面積よりも小さい面積で、かつプラスチックフィルムのエッジがガラス板の不透明な着色膜に全周で重なる形状）に裁断されているところを示す平面図である。 加熱圧着膜のプラスチックフィルムが所定形状（ガラス板の面積よりも小さい面積で、かつプラスチックフィルムのエッジがガラス板の不透明な着色膜に全周で重なる形状）に裁断されているところを示す断面図である。 樹脂中間膜と樹脂中間膜とを熱融着して得られる積層中間膜の平面図である。 樹脂中間膜と樹脂中間膜とを熱融着して得られる積層中間膜の断面図である。 樹脂中間膜とプラスチックフィルムとを熱融着して得られる積層中間膜の平面図である。 樹脂中間膜とプラスチックフィルムとを熱融着して得られる積層中間膜の断面図である。 プラスチックフィルムを挟みこんだ樹脂中間膜を、ヒータの加熱部と押さえ部とで挟み、部分的に熱融着する、熱融着装置を示す概略断面図である。 プラスチックフィルムを挟みこんだ樹脂中間膜を、２台のヒータの加熱部で挟み、部分的に熱融着する、熱融着装置を示す概略断面図である。 プラスチックフィルムを挟みこんだ樹脂中間膜を、レーザー光で熱融着する、熱融着装置を示す概略断面図である。 ロールを用いる脱気方法を示す概略断面図である。 チューブを用いる脱気方法を示す概略平面図である。 チューブを用いる脱気方法を示す概略断面図（図１２のｇ－ｇ´の断面）である。 真空バッグを用いる脱気方法を示す概略平面図である。 真空バッグを用いる脱気方法を示す概略断面図（図１４のｈ－ｈ´の断面）である。
 本発明に係るプラスチックフィルム挿入合わせガラスの製造方法は、図１、図２に示すような、湾曲したプラスチックフィルム挿入合わせガラス１を製造するものである。
 プラスチックフィルム挿入合わせガラス１は、プラスチックフィルム１４を両側から樹脂中間膜１１、１２で挟み込んだ構成の積層中間膜２８を用い、曲げ加工された２枚のガラス板１０、１３を接着してなる、合わせガラスである。
 曲げ加工された２枚のガラス板１０、１３の形状としては、球面、楕円球面、あるいは、自動車の前面ガラスなどのような曲率半径が場所によって異なるガラス板がある。
 湾曲したガラス板の曲率半径は、０．９ｍ～３ｍであることが望ましい。
 曲率半径が０．９ｍより小さいと、合わせ加工において、プラスチックフィルム１４のシワが生じやすいので、曲率半径は０．９ｍ以上であることが望ましい。
 また、曲率半径が大きくなると、平面に近い形状となり、プラスチックフィルム１４のシワが生じないという本発明の効果がほとんどなく、湾曲したガラスの曲率半径が３ｍ以下で、本発明の効果が現れる。
 室外側ガラス板１０には、ガラス板の周辺部に不透明な着色膜１５が形成されたものを用いることが望ましい。
 室外側ガラス板１０に不透明な着色膜１５が形成されたものを用いるのは、プラスチックフィルムのエッジ４に太陽光が当たると、プラスチックフィルムのエッジ４で光が散乱し、プラスチックフィルムのエッジ４が目立つだけでなく、運転に支障をきたす恐れがあるので、車外側に位置する車外側ガラス板１０の合わせ面に着色膜１５を設けて、プラスチックフィルムのエッジ４に太陽光が当たらないようにすることができるためである。
 また、挿入されるプラスチックフィル１４の形状は、プラスチックフィルム１４のエッジ４が室外側ガラス板１０の不透明な着色膜１５に全周で重なる形状で、かつ室外側ガラス板１０あるいは室内側ガラス板１３の面積よりも小さい面積に裁断されたものを用いることが好ましい。
 プラスチックフィルム１４のエッジ４が室外側ガラス板１０の不透明な着色膜１５に全周で重なる形状として、プラスチックフィルムの不要透視部５と相似形とすることが、着色膜１５を形成するためのＣＡＤデータを利用できるので、望ましい。
 図３はプラスチック挿入合わせガラスの端部の概略断面を示すもので、寸法ｄ２（ガラスエッジ２から着色膜エッジ３までの寸法）よりも、寸法ｄ１（ガラスエッジ２からプラスチックフィルムエッジ４までの寸法）を小さくし、プラスチックフィルムのエッジ４で太陽光が散乱するのを防ぐため、ｄ３＝ｄ２－ｄ１は５ｍｍ以上とすることが好ましい。
 樹脂中間膜１１、１２には、ポリビニルブチラール（ＰＶＢ）やエチレンビニルアセテート（ＥＶＡ）などのホットメルトタイプの接着剤が、好適に用いられる。
 室内側に用いられる樹脂中間膜１２に、Ａｇ、Ａｌ、Ｔｉなどの金属微粒子、金属窒化物、金属酸化物の微粒子、また、ＩＴＯ、ＡＴＯ、ＡＺＯ、ＧＺＯ、ＩＺＯなどの導電性透明酸化物微粒子を混入させると、プラスチック挿入合わせガラスの断熱性が向上し好ましい。
 プラスチックフィルム１４には、延伸法で作製されているものが好適であり、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリカーボネート、ポリメチルメタクリレート、ポリエーテルスルフォン、ナイロン、ポリアリレート、シクロオレフィンポリマーなどでなるプラスチックフィルムの中から選ばれたフィルムに、赤外線反射膜（図示せず）が形成されたものが用いられる。
 プラスチックフィルム１４の厚さは、３０μｍよりも薄いとフィルムが変形しやすくなり、シワが発生しやすい。また、フィルムの取り扱いが難しく、かつ赤外線反射膜を成膜した場合には赤外線反射膜の応力によりカールしやすい。一方、フィルムの厚さが２００μｍより厚いと合わせ加工時に脱気不良による外観欠陥が出るため、厚さは３０μｍ～２００μｍであることが望ましい。
 特に２軸延伸法で製膜される結晶性のポリエチレンテレフタレートフィルム（ＰＥＴフィルム）は、耐熱性にも優れていて広範囲の温度環境に使用することができ、また、透明性が高く、大量に生産されているために品質も安定しており、好適である。
 また、中間膜の間に挿入されるプラスチックフィルムによっては、中間膜と密着性が悪かったり、赤外線反射膜を成膜すると白濁が生じたりすることがあり、ハードコート膜を界面に形成することで、これらの不具合を解決できる。
 赤外線反射膜に導電性薄膜を用いる場合、導電性薄膜として、Ａｇ、Ａｕ、Ｃｕ、Ａｌ、Ｐｄ、Ｐｔ、Ｓｎ、Ｉｎ、Ｚｎ、Ｔｉ、Ｃｄ、Ｆｅ、Ｃｏ、Ｃｒ、Ｎｉなどの金属または合金等でなる金属膜または合金膜、あるいはアンチモンドープ酸化錫、錫ドープ酸化インジウム等でなる導電性金属酸化物が好適に用いられる。
 また、プラスチックフィルムに積層する赤外線反射膜として、屈折率の異なる誘電体の多層膜、あるいは屈折率の異なる樹脂の多層膜を用いると、放送や通信で用いられる電磁波を透過するので好ましい。
 屈折率の異なる誘電体の多層膜、あるいは屈折率の異なる樹脂の多層膜とは、屈折率ｎ１の積層膜と屈折率ｎ２（ｎ２≠ｎ１）の積層膜とを交互に繰り返して積層されてなる多層膜である。
 赤外線反射膜に、高屈折率の酸化物膜と低屈折率の酸化物膜とを交互に積層してなる多層膜を用いる場合、ＴｉＯ2、Ｎｂ2Ｏ5、Ｔａ2Ｏ5、ＳｉＯ2、Ａｌ2Ｏ3、ＺｒＯ2、ＭｇＦ2から選ばれる１種以上の誘電体でなる膜が好適に用いられる。
 特に、屈折率の低い膜にＳｉＯ2を用い、屈折率の高い膜に、ＴｉＯ2、Ｎｂ2Ｏ5、Ｔａ2Ｏ5から選ばれる１種以上の誘電体を用いる場合は、４層から１１層の多層膜で、近赤外線を反射する好適な赤外線反射膜が形成できるので、好ましい。
 さらに、断熱性能を効果的に行うために、誘電体膜でなる赤外線反射膜は、次の（１）および（２）の条件を満たすように、誘電体膜が４層以上、１１層以下で積層してなり、波長９００ｎｍから１４００ｎｍの波長領域で５０％を越える反射の極大値を有することが望ましい。
（１）誘電体膜をプラスチックフィルム側から順に数え、偶数番目層の屈折率の最大値をｎemax、最小値をｎeminとし、奇数番目層の屈折率の最大値をｎomax、最小値をｎominとしたとき、ｎemax＜ｎominあるいはｎomax＜ｎemin。
（２）ｉ番目の層の屈折率をｎiと厚さをｄiとしたとき、波長λが９００～１４００ｎｍの範囲の赤外線に対して、２２５ｎｍ≦ｎi・ｄi≦３５０ｎｍ。
 屈折率の異なる２種類のポリマー薄膜を交互に積層してなる多層膜を熱線反射膜に用いる場合、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリカーボネート、ポリメチルメタクリレート、ポリエーテルスルフォン、ナイロン、ポリアリレート、シクロオレフィンポリマー等を用いることが好ましく、２種類のポリマー層が交互に積層された多層膜の総数は、５０～２００層であることが好適である。
 導電性薄膜や誘電体膜は、ＰＶＤ法、スパッタリング法などにより成膜することが好ましく、また、ポリマー薄膜は、ロールコート法、フローコート法やディッピング法などで成膜することが好ましい。
 図１、図２に示されるプラスチックフィルム挿入合わせガラス１は、次の工程１～工程５によって製造される。工程１～工程３によって、プラスチックフィルムが２枚の樹脂中間膜の間に挟み込まれた構成の積層中間膜が作製される。
　工程１：プラスチックフィルムと樹脂中間膜とを加熱圧着した加熱圧着膜を作製する工程。
　工程２：加熱圧着膜のプラスチックフィルムを、プラスチックフィルムのエッジがガラス板の不透明な着色膜に全周で重なる形状で、かつガラス板の面積よりも小さい面積に裁断し、プラスチックフィルムの不要部を樹脂中間膜から剥がし取る工程。
　工程３：樹脂中間膜に加熱圧着されたプラスチックフィルム側に樹脂中間膜を重ね、プラスチックフィルムの辺に近い位置で、重なり合う樹脂中間膜と樹脂中間膜とを、あるいは樹脂中間膜とプラスチックフィルムとを、プラスチックフィルムの辺に平行な線状に熱融着する工程。
　工程４：工程３で得られる積層中間膜を２枚の湾曲したガラス板の間に入れて積層体となし、該２枚のガラス板の間を脱気する工程。
　工程５：脱気した後の積層体を加圧加温して接着する工程。
 工程１から工程５までは次のようにして実施される。
　工程１は、例えば、図４に示すように樹脂中間膜（１１または１２）とプラスチックフィルム１４を重ねて、加圧ロール２１と加熱ロール２０との間を通して、図５А、図５Ｂに示すような加熱圧着膜を作製することができる。このとき、プラスチックフィルム１４側に加熱ロールを配置することが好ましい。
 加熱ロール２０には、ヒータを内蔵する金属表面のロールが好適に用いられる。
　加熱ロール２０の表面の温度は５０℃～１１０℃であることが好ましく、プラスチックフィルム２２の表面温度は４０℃～６０℃の範囲にあることが好ましい。
　プラスチックフィルム２２の樹脂中間膜側の表面温度が４０℃より低いと、熱融着が不充分となる。また、６０℃より高いと、プラスチックフィルムと樹脂中間膜とが強く接着されて、工程２でプラスチックフィルムの不要部２６を樹脂中間膜２３から剥がすことができないという不具合や、樹脂中間膜２３が押し圧ロール４１に接着するなどの不具合が生じてしまう。
押し圧ロール４１は、樹脂中間膜２３とプラスチックフィルム２２との間の脱気を行うもので、表面がシリコンゴム、ウレタンゴムなどのゴム製の樹脂で覆われたロールを用いるのが好ましい。また、押し圧ロールの表面には、樹脂中間膜に融着しないような材料を用いることが望ましい。
　また、押し圧ロール４１の圧力は０．１ＭＰａ～０．３ＭＰａ、樹脂中間膜２３やプラスチックフィルム２２の搬送速度は０．５ｍ／ｍｉｎ～４ｍ／ｍｉｎの範囲にあることが望ましい。
　押し圧ロール４１の圧力が０．１ＭＰａより小さい場合、あるいは、０．３ＭＰａより大きい場合、共にプラスチックフィルムと樹脂中間膜との間の脱気が不十分となってしまう。
 樹脂中間膜やプラスチックフィルムの搬送速度は０．５ｍ／ｍｉｎ～４ｍ／ｍｉｎの範囲にあることが望ましい。送り速度が０．５ｍ／ｍｉｎより遅いと生産性が劣り、４ｍ／ｍｉｎより早いと、接着強度や脱気が不十分となる。
 工程１によって図５に示すようなプラスチックフィルム１４と樹脂中間膜２３とが一体となる加熱圧着膜２４が作製される。
 工程２で、図５に示される加熱圧着膜２４のプラスチックフィルム２２を、図６А、図６Ｂに示すような所定形状プラスチックフィルム２５に裁断し、不要部２６を除去する。
 プラスチックフィルム２２の裁断は、カッターナイフを用いて、プラスチックフィルム２２側から樹脂中間膜２３に届く切れ目を入れる。カッターナイフの移動を数値制御で行うＮＣカッターを用いることが好ましい。
 不要部２６を樹脂中間膜２３から剥がして除去して、図７Ａ，図７Ｂに示すプラスチックフィルム付き樹脂中間膜２７が得られる。
 所定形状プラスチックフィルム２５は、図１に示されるプラスチックフィルム挿入合わせガラス１の透視部５と相似形であることが望ましい。
 所定形状プラスチックフィルム２５を透視部５と相似形にするため、曲げ加工されているガラス板１０に加熱圧着膜２４を重ねてプラスチックフィルム２２の裁断を行って、所定形状プラスチックフィルム２５が得られる。
 しかし、室内側ガラス板１３は曲率が場所によって異なる複雑な面形状をしていることが多く、曲面上で裁断することは困難となることが多いので、室内側ガラス板１３が曲げ加工される前の、平板形状での透視部の形に合わせて、加熱圧着膜２４が平面の状態で、プラスチックフィルム２２を裁断することが望ましい。
 工程３では、図８Ａ，図８Ｂに示すように、プラスチックフィルム付き樹脂中間膜２７のプラスチックフィルム２５側にもう一枚の樹脂中間膜２３´を重ね、所定形状プラスチックフィルム２５の辺中央付近で、樹脂中間膜２３と２３´とを、線状の熱融着部２９が形成されるように加熱融着して、積層中間膜２８が作製される。
 あるいは、図９Ａ，図９Ｂに示すように、プラスチックフィルム付き樹脂中間膜２７のプラスチックフィルム２５側にもう一枚の樹脂中間膜２３´を重ね、所定形状プラスチックフィルム２５の辺中央付近で、樹脂中間膜２３´と所定形状プラスチックフィルム２５とを、線状の熱融着部２９´が形成されるように加熱融着して、積層中間膜２８´を作製してもよい。
 線状の熱融着部２９、２９´は、シワの発生しやすい、所定形状プラスチックフィルム２５の辺中央付近に形成されることが好ましい。
 積層中間膜２８、２８´の作製は、プラスチックフィルムが曲げ加工されたガラス板に重ねられるとき、プラスチックフィルムの辺近傍に生じるシワの発生を防止できるという効果を有する。
 このシワの発生防止を効果的にするためには、線状の熱融着部２９、２９´の長さを５ｍｍ以上とすることが好ましい。また、樹脂中間膜２３、２３´の間の脱気不良が起こらないようにするため、線状の熱融着部２９、２９´の長さを３００ｍｍ以下とすることが好ましい。
 なお、熱融着部２９、２９´は、所定形状プラスチックフィルム２５の、全ての辺の中央付近に形成することが好ましいが、曲げ加工されたガラス板の曲率が３ｍより大きく、プラスチックフィルムにシワの発生する危険性がない辺の場合は、形成しなくてもよい。熱融着部２９は、図１０Ａに示すように、電気ヒータ３０を用い、電気ヒータの加熱体３１を樹脂中間膜２３´に押し当て、形成することができる。
 図１０Ｂに示すように、電気ヒータ３０を２台用いて、樹脂中間膜の両側から加熱体３１を押し当てて、加熱してもよい。また、図１０Ｃに示すように、レーザー光３３を樹脂中間膜２３と２３´とが接触する面に凸レンズ３４等で集光させて、熱融着部２９を形成してもよい。レーザー光で加熱する場合は、樹脂中間膜２３´のエンボス加工されている表面で光が散乱しないように、ガラス板のような透明板３５で樹脂中間膜の表面を圧迫し、レーザー光が樹脂中間膜の表面で散乱しないようにすることが望ましい。
樹脂中間膜２３´と所定形状プラスチックフィルム２５とが加熱融着されている熱融着部２９´も、熱融着部２９と同様にして形成することができる。
 工程４では、工程１～工程３で作製された積層中間膜２８を用い、室外側ガラス板１０、積層中間膜２８、室内側ガラス板１３と重ねて積層体４０とし、室外側ガラス板１０と室内側ガラス板１３との間の脱気を行う。
脱気は、特に限定するものではないが、図１１に示すような押し圧ロール４１によって、積層体４０の両面から押し圧して脱気する方法、図１２、図１３に示すような、ゴム系の樹脂でできたチューブ４２を積層体４０の周辺に装着し、排気ノズル４３から空気を排気して脱気する方法、図１４、図１５に示すような、真空バッグ４４の中に積層体４０を入れて、排気ノズル４５から空気を排気して行うことができる。空気の排気には、真空ポンプ（図示せず）が好ましく使用できる。
　工程５は、工程４の脱気している状態の積層体４０を、オートクレーブ装置によって加熱加圧処理する。加熱加圧処理の温度範囲は９０～１５０℃の加熱、加圧は１ＭＰａ以下とし、３０分程度行うことが好ましい。
　なお、工程１から工程３において、樹脂中間膜にロール状の連続したものを用い、樹脂中間膜が連続している状態の積層中間膜を作製してもよい。この場合は、工程４の前に、樹脂中間膜が連続した状態から、図８Ａ，図８Ｂに示すような形に切り離して、積層中間膜をガラス板と重ねればよい。
　以下、図面を参照しながら本発明を、実施例および比較例を挙げて、詳細に説明する。なお、本発明は、以下に示す実施例に限定されるものではない。
　図１、図２に示す、室外側ガラス板１０、樹脂中間膜１１、赤外線反射膜が形成されたプラスチックフィルム１４、樹脂中間膜１２、室内側ガラス板１３が積層されてなるプラスチックフィルム挿入合わせガラス１を作製した。
 ガラス板には、サイズが１１００ｍｍ×１８００ｍｍ、厚さが２ｍｍのフロートガラスを曲げ加工したものを、また樹脂中間膜１１、１２には、厚さが０．３８ｍｍのＰＶＢ膜を用いた。
 プラスチックフィルム１４には、厚さが１００μｍのＰＥＴフィルムを用い、該プラスチックフィルムの片面に、ハードコート膜（図示せず）を塗布し、さらにその上に赤外線反射膜（図示せず）を形成した。
 また、ハードコート膜および赤外線反射膜を形成した面と反対側のＰＥＴフィルム面に、シランカップリング剤の膜（図示せず）を成膜した。
ハードコート膜としては、厚さ５μｍのアクリル系ハードコート膜をロールコート法で成膜した。
 赤外線反射膜には誘電体多層膜によるものを用い、ＴｉＯ2膜（厚さ１０５ｎｍ）、ＳｉＯ2膜（厚さ１７５ｎｍ）、ＴｉＯ2膜（厚さ１０５ｎｍ）、ＳｉＯ2膜（厚さ１７５ｎｍ）、ＴｉＯ2膜（厚さ１０５ｎｍ）、ＳｉＯ2膜（厚さ１７５ｎｍ）、ＴｉＯ2膜（厚さ１０５ｎｍ）、ＳｉＯ2膜（厚さ１７５ｎｍ）、ＴｉＯ2膜（厚さ１０５ｎｍ）をハードコート膜上に順次スパッタリングで成膜した。
 樹脂中間膜１１には、厚さが０．３８ｍｍのＰＶＢフィルムを用いた。
 湾曲したガラス板には、自動車の前面窓に合わせガラスとして用いられる、室外側ガラス板と室内側ガラス板を用いた。
 さらに、室外側に用いるガラス板１０には、凹面側にセラミックペーストをスクリーン印刷して焼成し、着色膜を形成した。
 着色膜の幅（図３のｄ２）は、最小となる所では３０ｍｍ、最大となる所では２００ｍｍとした。湾曲したガラス板の曲率半径は、０．９ｍ～１ｍの間にあり、周辺部が０．９ｍの値であり、中央部が１ｍの値であった。
 工程１～工程５を次のようにして実施し、図１、図２に示すプラスチック挿入合わせガラスを作製した。
 〈工程１〉
 ＰＥＴフィルムにハードコート膜、赤外線反射膜およびシランカップリング剤の塗膜が形成されたプラスチックフィルム２２と樹脂中間膜２３とを重ねて、図４に示すように、ステンレス鋼表面の加熱ロール２０とシリコンゴムで作製された押し圧ロール４１の間を通し、図５А、図５Ｂに示す加熱圧着膜を作製した。
 押し圧ロール４１の圧力は０．２ＭＰａ、加熱ロールの温度は９０℃とし、プラスチックフィルム２２が加熱ロール２０と接するようにした。また、樹脂中間膜２３、プラスチックフィルム２２の搬送速度は、３ｍ／ｍｉｎとした。
 〈工程２〉
 ＮＣカッターを用いて、プラスチックフィルム２２を図６Ａ，図６Ｂに示すような所定形状プラスチックフィルム２５に裁断し、不要部２６を剥がして、図７Ａ，図７Ｂに示すプラスチックフィルム付き樹脂中間膜２７を作製した。
 プラスチックフィルム２５の形状は、図１の透視部５と相似形で、図３に示すｄ３を１０ｍｍとした。
〈工程３〉
工程２で作製したプラスチックフィルム付き樹脂中間膜２７のプラスチックフィルム側に樹脂中間膜２３´を重ね、プラスチックフィルムのエッジ付近で、２枚の樹脂中間膜２３、２３´を加熱融着し、図８Ａ，図８Ｂのように、プラスチックフィルムの辺の中央部付近に、熱融着部２９を形成して、積層中間膜２８とした。
 加熱融着は、図８Ａに示す装置を用いて行った。加熱体３１の樹脂中間膜２３に押し当てる面積を１０ｍｍ×２００ｍｍとし、加熱体の温度を４５℃に加熱し、１平方ｃｍ当たり１Ｎの力で２０秒間、樹脂中間膜２３´に押し当てて行い、図８Ａ，図８Ｂに示す熱融着部２９を形成した。
 〈工程４〉
 工程３で作製した積層中間膜２８を湾曲した室外側ガラス１０に重ね、さらに湾曲した室内側ガラス１３をその上に重ね、湾曲したガラス板の縁からはみ出た樹脂中間膜をカッターナイフで切り取り、積層体４０を形成した。
 積層体４０の形成において、図３に示すｄ３が１０ｍｍとなるように、積層中間膜２８を湾曲した室外側ガラス１０に重ねた。
 また、プラスチックフィルムに形成されている赤外線反射膜は、図２の室外側樹脂中間膜１１に接するように配置した。積層体４０の脱気を、図１２、１３に示すチューブ４２を用い。排気ノズル４３に、図示しない真空ポンプをつないで行った。チューブ４２には、ゴム系樹脂で作製されたものを用いた。
 〈工程５〉
 図１２、１３に示す積層体４０を、チューブ４２を用いて脱気している図１２、１３の状態のまま、オートクレーブに入れ、１５分間、加圧（０．２ＭＰａ）・加熱（９５℃）処理した後、積層体４０をオートクレーブから取出した。
 積層体４０からチューブ４２を取外し、チューブ４２を取り外した積層体４０を再度オートクレーブに入れ、３０分間、加圧（１ＭＰａ）・加熱（１４０℃）処理し、図１に示すプラスチック挿入合わせガラス１を作製した。
 作製したプラスチックフィルム挿入合わせガラス１は、プラスチックフィルム１４にシワがなく、外観不良の無いものであった。さらに、ＪＩＳＲ３２１１－１９９８に規定されている可視光線透過率も７０％有し、自動車のフロントガラスとして好適に使用できるものであった。
 実施例２
 図１、２のプラスチックフィルム１４に、ＰＥＴフィルムに酸化亜鉛と銀の薄膜をスパッタリング法で積層してなる赤外線反射膜を形成したものを用いた他は、全て実施例１と同様にして、プラスチックフィルム挿入合わせガラス１を作製した。
 本実施例で作製したプラスチックフィルム挿入合わせガラス１は、プラスチックフィルム１４にシワがなく、外観不良の無いものであった。
さらに、ＪＩＳＲ３２１１－１９９８に規定されている可視光線透過率も７０％有し、自動車のフロントガラスとして好適に使用できるものであった。
 比較例１
 実施例１の工程３において、熱融着部２９を形成しないで積層中間膜２８とした他は、全て実施例１と同様にして、プラスチックフィルム挿入合わせガラスを作製した。
 作製したプラスチックフィルム挿入合わせガラスには、プラスチックフィルム１４の周辺部でシワが観察され、外観不良のため実用には適さないものであった。
１　プラスチックフィルム挿入合わせガラス
２　プラスチックフィルム挿入合わせガラスのエッジ
３　着色膜のエッジ
４　プラスチックフィルムのエッジ
５　プラスチックフィルム挿入合わせガラス透視部
１０　室外側ガラス板
１１、１２　樹脂中間膜
１３　室内側ガラス
１４　プラスチックフィルム
１５　着色膜
２０　加熱ロール
２１　加圧ロール
２２　プラスチックフィルム
２３　樹脂中間膜
２４　加熱圧着膜
２５　所定形状プラスチックフィルム
２６　不要部
２７　プラスチックフィルム付き樹脂中間膜
２８、２８´　積層中間膜
２９、２９´　熱融着部
３０　ヒータ
３１　加熱体
３２　押さえ部
３３　レーザー光
３４　凹凸レンズ
３５　透明板
４０　積層体
４１　押し圧ロール
４２　チューブ
４３、４５　排気ノズル
４４　真空バッグ

Claims (3)

  1.  曲げ加工によって湾曲した形状の２枚のガラス板と、２枚の樹脂中間膜と、赤外線反射膜が形成されてなるプラスチックフィルムとが、ガラス板、樹脂中間膜、プラスチックフィルム、樹脂中間膜、ガラス板の順に積層されてなるプラスチックフィルム挿入合わせガラスの製造方法において、少なくとも１枚のガラス板の周辺部に不透明な着色膜を形成し、次の工程１～３で積層中間膜を作製し、該積層中間膜を２枚のガラス板の間に挿入して、加熱・加圧処理を行うことを特徴とするプラスチックフィルム挿入合わせガラスの製造方法。
    工程１：プラスチックフィルムと樹脂中間膜とを加熱圧着した加熱圧着膜を作製する工程。
    工程２：加熱圧着膜のプラスチックフィルムを、プラスチックフィルムのエッジがガラス板の不透明な着色膜に全周で重なる形状で、かつガラス板の面積よりも小さい面積に裁断し、プラスチックフィルムの不要部を樹脂中間膜から剥がし取る工程。
    工程３：樹脂中間膜に加熱圧着されたプラスチックフィルム側に樹脂中間膜を重ね、プラスチックフィルムの辺に近い位置で、重なり合う樹脂中間膜と樹脂中間膜とを、あるいは樹脂中間膜とプラスチックフィルムとを、プラスチックフィルムの辺に平行な線状に熱融着する工程。
  2.  前記加熱圧着膜を加熱ロールを用いて作製することを特徴とする請求項１に記載のプラスチックフィルム挿入合わせガラスの製造方法。
  3.  熱融着に線状の加熱体を有する加熱装置を用いるか、あるいはレーザー光を照射して熱融着することを特徴とする請求項１または２に記載のプラスチックフィルム挿入合わせガラスの製造方法。
PCT/JP2010/055832 2009-04-16 2010-03-31 プラスチックフィルム挿入合わせガラスの製造方法 WO2010119770A1 (ja)