WO2008047629A1 - Procédé de protection d'une base - Google Patents

Procédé de protection d'une base Download PDF

Info

Publication number
WO2008047629A1
WO2008047629A1 PCT/JP2007/069668 JP2007069668W WO2008047629A1 WO 2008047629 A1 WO2008047629 A1 WO 2008047629A1 JP 2007069668 W JP2007069668 W JP 2007069668W WO 2008047629 A1 WO2008047629 A1 WO 2008047629A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
substrate
substrate surface
positively charged
repellent
Prior art date
Application number
PCT/JP2007/069668
Other languages
English (en)
Japanese (ja)
Inventor
Shiro Ogata
Original Assignee
Sustainable Titania Technology Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sustainable Titania Technology Inc. filed Critical Sustainable Titania Technology Inc.
Priority to JP2008539752A priority Critical patent/JPWO2008047629A1/ja
Publication of WO2008047629A1 publication Critical patent/WO2008047629A1/fr

Abstract

L'invention porte sur un nouveau procédé de prévention ou de réduction de l'adhésion d'un contaminant à une base, tout en empêchant ou en réduisant une dégradation de couleur ou un changement de couleur de la base au cours du temps. Ce procédé est caractérisé par le fait qu'un agent hydrophobe ou un agent empêchant l'absorption d'eau et une ou plusieurs substances positivement chargées choisies dans le groupe constitué par (1) des cations, (2) des corps conducteurs ou diélectriques positivement chargés et (3) des corps composites d'un corps conducteur et d'un corps diélectrique ou semi-conducteur, sont disposés sur la surface de la base ou dans la couche de surface de la base.
PCT/JP2007/069668 2006-10-13 2007-10-09 Procédé de protection d'une base WO2008047629A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2008539752A JPWO2008047629A1 (ja) 2006-10-13 2007-10-09 基体の保護方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2006280318 2006-10-13
JP2006-280318 2006-10-13

Publications (1)

Publication Number Publication Date
WO2008047629A1 true WO2008047629A1 (fr) 2008-04-24

Family

ID=39313868

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2007/069668 WO2008047629A1 (fr) 2006-10-13 2007-10-09 Procédé de protection d'une base

Country Status (3)

Country Link
JP (1) JPWO2008047629A1 (fr)
TW (1) TW200909569A (fr)
WO (1) WO2008047629A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012245724A (ja) * 2011-05-30 2012-12-13 Toppan Printing Co Ltd 撥水機能を有したカード及びその製造方法
JP2014172933A (ja) * 2013-03-06 2014-09-22 Mitsubishi Electric Corp 撥水性膜の形成方法および撥水性膜が形成された物品
JP2021080325A (ja) * 2019-11-15 2021-05-27 株式会社リンレイ 床用洗浄剤

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003342526A (ja) * 2002-05-30 2003-12-03 Japan Hydrotect Coatings Kk 自己浄化性水性塗料組成物、及び自己浄化性部材
JP2005319601A (ja) * 2004-05-06 2005-11-17 Sustainable Titania Technology Inc 撥水性基体の親水化防汚方法及びその人工物における使用
WO2005108056A1 (fr) * 2004-05-06 2005-11-17 Sustainable Titania Technology Inc. Méthode de protection de base
JP2006005004A (ja) * 2004-06-15 2006-01-05 Sustainable Titania Technology Inc 電子デバイス又はその製造手段の表面処理方法
JP2006321993A (ja) * 2005-04-22 2006-11-30 Sustainable Titania Technology Inc 金属元素でドープされたチタン酸化物を含む基材表面処理用溶液又は分散液、前記液を用いる基材表面処理方法、及び前記方法を用いて得られる表面処理材料

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2003342526A (ja) * 2002-05-30 2003-12-03 Japan Hydrotect Coatings Kk 自己浄化性水性塗料組成物、及び自己浄化性部材
JP2005319601A (ja) * 2004-05-06 2005-11-17 Sustainable Titania Technology Inc 撥水性基体の親水化防汚方法及びその人工物における使用
WO2005108056A1 (fr) * 2004-05-06 2005-11-17 Sustainable Titania Technology Inc. Méthode de protection de base
JP2006005004A (ja) * 2004-06-15 2006-01-05 Sustainable Titania Technology Inc 電子デバイス又はその製造手段の表面処理方法
JP2006321993A (ja) * 2005-04-22 2006-11-30 Sustainable Titania Technology Inc 金属元素でドープされたチタン酸化物を含む基材表面処理用溶液又は分散液、前記液を用いる基材表面処理方法、及び前記方法を用いて得られる表面処理材料

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012245724A (ja) * 2011-05-30 2012-12-13 Toppan Printing Co Ltd 撥水機能を有したカード及びその製造方法
JP2014172933A (ja) * 2013-03-06 2014-09-22 Mitsubishi Electric Corp 撥水性膜の形成方法および撥水性膜が形成された物品
JP2021080325A (ja) * 2019-11-15 2021-05-27 株式会社リンレイ 床用洗浄剤

Also Published As

Publication number Publication date
TW200909569A (en) 2009-03-01
JPWO2008047629A1 (ja) 2010-02-25

Similar Documents

Publication Publication Date Title
JP4398869B2 (ja) チタニア−金属複合体及びその製造方法、並びにその複合体分散液を用いた造膜方法
JP4926176B2 (ja) 基体の保護方法
KR100849150B1 (ko) 기체의 보호 방법
MXPA06013795A (es) Recubrimientos en multicapas y metodos relacionados.
JP4995738B2 (ja) 基体の保護方法
WO2006115209A1 (fr) Solution ou dispersion destinee au traitement d’une surface de base renfermant un oxyde de titane dope avec un element metallique, procede destine au traitement d’une surface de base avec un liquide, et materiau obtenu a la suite de ce procede et dont la surface a ete traitee
JP5624458B2 (ja) 基体の保護方法
JP2006321993A (ja) 金属元素でドープされたチタン酸化物を含む基材表面処理用溶液又は分散液、前記液を用いる基材表面処理方法、及び前記方法を用いて得られる表面処理材料
JPWO2007091479A1 (ja) 基体の保護方法
WO2008047629A1 (fr) Procédé de protection d'une base
JP5936132B2 (ja) 基体表面の保護方法
JP4508717B2 (ja) 撥水性基体の親水化防汚方法及びその人工物における使用
JPWO2005090067A1 (ja) 積層体およびその製造方法
JP6124276B2 (ja) 基体表面の親水性維持方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07829406

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2008539752

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07829406

Country of ref document: EP

Kind code of ref document: A1