WO2008035429A1 - Courroie sans fin pourvue d'un guide empêchant tout serpentement - Google Patents

Courroie sans fin pourvue d'un guide empêchant tout serpentement Download PDF

Info

Publication number
WO2008035429A1
WO2008035429A1 PCT/JP2006/318778 JP2006318778W WO2008035429A1 WO 2008035429 A1 WO2008035429 A1 WO 2008035429A1 JP 2006318778 W JP2006318778 W JP 2006318778W WO 2008035429 A1 WO2008035429 A1 WO 2008035429A1
Authority
WO
WIPO (PCT)
Prior art keywords
endless belt
prevention guide
guide member
belt
meandering prevention
Prior art date
Application number
PCT/JP2006/318778
Other languages
English (en)
French (fr)
Inventor
Tokio Fujita
Toshihiko Tomita
Original Assignee
Nitto Denko Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corporation filed Critical Nitto Denko Corporation
Priority to CNA2006800555795A priority Critical patent/CN101506740A/zh
Priority to PCT/JP2006/318778 priority patent/WO2008035429A1/ja
Priority to US12/377,363 priority patent/US20100221042A1/en
Priority to EP06798217A priority patent/EP2065764A4/en
Publication of WO2008035429A1 publication Critical patent/WO2008035429A1/ja

Description

明 細 書
蛇行防止ガイド付エンドレスベルト
技術分野
[0001] 本発明は、蛇行防止ガイド付エンドレスベルトに関し、プリンター、複写機、ビデオ プリンタ一等の電子写真記録装置などに有用である。 背景技術
[0002] 従来より、電子写真記録装置等の中間転写装置、転写装置、搬送装置等には、ェ ンドレスベルトが使用されている。当該エンドレスベルトは、例えば、図 1に示すように 、複写機の中間転写装置の中間転写ベルト 6として用いられ、下記のプロセスにて 中間転写が行なわれる。即ち、感光ドラム 1は、チヤジャー 3により帯電され、露光器 2 により露光され、現像器 5によりトナーによるトナー像が形成される。トナー像は静電 転写機 10により、中間転写ベルト 6に転写され、転写されたトナー像は一組の押圧口 一ラー 9、 12により記録紙 11に再び転写される。中間転写ベルト 6は、その内面に接 するローラー 7、 8、 9により支持されている。
[0003] 力かる中間転写ベルトにおいては、高精度にて駆動しなければ、エンドレスベルト が蛇行しやすぐベルトが蛇行すると、転写に際して露光位置や転写位置がずれる。 その結果、画像ムラや画像ズレが発生したり、エンドレスベルトが蛇行により破壊する t 、う問題が生じることがあった。
[0004] このようなベルトの蛇行を防止するために、エンドレスベルトに蛇行防止ガイド部材 を設置する技術が知られている (例えば、特許文献 1および 2を参照)。この蛇行防止 ガイド部材のエンドレスベルトへの取り付けは、シームレス状に取り付けることが困難 であることから、ベルト内周長に相当する長さの蛇行防止ガイド部材が、粘着層を介 して取り付けられている（例えば、特許文献 3を参照)。
特許文献 1 :特開 2000— 310291号公報
特許文献 2 :特開 2002— 87568号公報
特許文献 3：特開 2004— 53629号公報
発明の開示 発明が解決しょうとする課題
[0005] し力しながら、蛇行防止ガイド部材の発揮する効果は、その蛇行防止ガイド部材と エンドレスベルトとの間の接着力に相関があり、これまでは、粘着層を介して取り付け られる蛇行防止ガイド部材は、粘着層単体での接着力では、蛇行防止効果が不十 分であり、ガイド部材の剥がれやベルトの割れを生じることがあった。そこで、本発明 の目的は、蛇行防止ガイド部材のエンドレスベルトからの剥がれを防止し、高精度に 駆動する耐久寿命の長いエンドレスベルトを提供することにある。
課題を解決するための手段
[0006] 本発明者らは、上記目的を達成すベぐ鋭意研究したところ、次の条件を兼ね備え た場合に満足する特性を有するエンドレスベルトを得ることを見出し、本発明を完成 するに至った。
[0007] すなわち、本発明の蛇行防止ガイド付エンドレスベルトは、榭脂製のエンドレスベル ト、粘着層、粘着層を介してエンドレスベルトに貼設された蛇行防止ガイド部材、及び 、粘着層の両面に設けられたプライマー層を有する蛇行防止ガイド付エンドレスベル トである。
[0008] 本発明のベルトは、粘着層の両面にプライマー層を設けることにより、エンドレスべ ルトと蛇行防止ガイド部材との間の接着力を大幅に向上させ、エンドレスベルトからの 蛇行防止ガイド部材の剥がれ及びエンドレスベルト本体の破壊を防止できる。
[0009] また、前記蛇行防止ガイド付エンドレスベルトにお 、て、前記エンドレスベルトと前 記蛇行防止ガイド部材との剥離接着強さが 4〜： LOONZlOmmであることが好ましい 尚、本発明における前記剥離接着強さとは、 JIS K 6854- 1 (90° ピール試験） に準じて測定した値であり、その測定方法は、実施例に記載されている。かかるベル トによれば、ベルト本体力 蛇行防止ガイド部材の剥がれおよびベルトの破壊をより 確実に防止できる。
発明の効果
[0010] 本発明のエンドレスベルトによれば、エンドレスベルトと蛇行防止ガイド部材との間 の接着力が従来に比べ向上しているため、蛇行防止ガイドの端部からの剥がれ及び ベルト破壊を防止でき、これにより耐久寿命の長 、エンドレスベルトを得ることができ る。
図面の簡単な説明
[0011] [図 1]電子写真式複写機の中間転写装置におけるエンドレスベルトの使用状態を説 明するための概略構成図である。
[図 2]本発明の蛇行防止ガイド付エンドレスベルトを例示する一部断面を示した斜視 図である。
[図 3]蛇行防止ガイドとエンドレスベルトの接着部を示す要部断面図である。
符号の説明
[0012] 1 感光ドラム
6 中間転写ベルト（エンドレスベルト）
7, 8, 9 ローラ
11 記録紙
21 エンドレスベルト
22 蛇行防止ガイド (部材）
23 粘着層
24 プライマー層
発明を実施するための最良の形態
[0013] 以下、本発明の実施の形態について、図面を参照しながら説明する。図 2および図 3に示すように、本発明のエンドレスベルトは、榭脂製のエンドレスベルト 21に、蛇行 防止ガイド部材 22が粘着層 23およびプライマー層 24を介して貼設されているもので ある。
[0014] プライマー層を除く部分、即ち、榭脂製のエンドレスベルト、蛇行防止ガイド部材及 び粘着層の材質、形状、大きさ、機能等は、特に限定されず、従来公知のものがい ずれも使用可能である。例えば、榭脂製のエンドレスベルトとしては、電子写真式複 写機、レーザープリンタ一等における感光装置、中間転写装置、転写分離装置、搬 送装置、帯電装置、現像装置等に使用されるエンドレスベルトが挙げられ、これらの 用途、機能に応じた、材質、形状、大きさ等が適宜設定される。一例を挙げると、電 子写真記録装置等における中間転写ベルト及び転写搬送ベルトの場合、導電性フ イラ一を含有するポリイミド系榭脂からなる半導電性ベルト等が使用される。
[0015] その他の用途を含めて、榭脂製エンドレスベルトの材質としては、ポリイミド系榭脂、 ポリエステル系榭脂、ポリウレタン系榭脂、ポリアミド系榭脂、フッ素系榭脂等が挙げ られる。なお、榭脂製エンドレスベルトは繋ぎ目があってもなくてもよい。また、ベルト 本体の厚みは、特に限定されないが、通常、 0. 05mm〜0. 5mm程度が好ましい。
[0016] 蛇行防止ガイド部材としては、適当な硬度を有する弾性体等が使用でき、具体的に は、ポリウレタン、ネオプレンゴム、ウレタンゴム、ポリエステルエラストマ一、クロロプレ ンゴム、二トリルゴム、ブチルゴム、シリコーンゴムなどを挙げることができる。これらの 中でも、粘着層への接着性、電気絶縁性、耐湿性、耐溶剤性、耐オゾン性、耐摩耗 性等を考慮すると、ウレタンゴム、クロロプレンゴム、シリコーンゴムが好ましぐ特にゥ レタンゴムが好ましい。また、蛇行防止ガイド部材の硬度としては、 JIS硬度 30° 〜9 5° の範囲が好ましぐより好ましくは 50° 〜80° である。
[0017] 蛇行防止ガイド部材の厚みは、蛇行防止効果や耐久性等の観点から、 0. 05mm 〜3. Omm程度が好ましぐより好ましくは 0. 5mn！〜 2mmである。なお、蛇行防止ガ イド部材の幅や長さは、エンドレスベルトの形状や大きさに応じて適宜設定され、特 に限定されない。
[0018] 粘着層に使用される粘着剤としては、例えば、アクリル系、シリコーン系、天然ゴム 系、合成ゴム系、ウレタン系の粘着剤などを挙げることができる力 常温で圧力のみを 加えることにより所望の接着強度を得られる点で、感圧性のアクリル系粘着剤が好ま しい。また、前記粘着剤には、 1種または 2種以上の添加剤を必要に応じて添加して ちょい。
[0019] 粘着層は、前記粘着剤をプライマー層に直接塗布等して形成してもよ ヽが、取扱 ヽ 易さの点から、予めセパレータに前記粘着剤を塗布等した両面粘着テープを使用す ることが好ましぐアクリル系粘着剤を有する両面粘着テープがさらに好ましい。両面 粘着テープとしては、不織布、布、ブラスティックフィルム、発泡体等の中芯基材の両 面に前記粘着剤を塗布または含浸させた両面粘着テープゃ不織布等の中芯基材を 用いずに前記粘着剤単独で構成される両面粘着テープ (以下、「基材レス両面粘着 テープ」ということがある）などをあげることができる。なかでも、接着力を高めるために は、基材レス両面粘着テープを使用することが好まし 、。
[0020] また、粘着層の厚みは、通常 5〜500 /z mとすること力好ましく、更に好ましくは 20 〜200 μ mである。すなわち粘着層の厚みが 5 μ m未満の場合は、ガイド及びベルト の接着力が不足する。また、 500 mを超えるとガイドの蛇行によるせん断力により粘 着層から蛇行防止ガイドがずれ、精度の高いベルト制御が困難となる。粘着層の幅 や長さは、蛇行防止ガイド部材の形状や大きさに応じて適宜設定され、特に限定さ れない。
[0021] 本発明の蛇行防止ガイド付エンドレスベルトは、前記粘着層の両面にプライマー層 を有する。すなわち、蛇行防止ガイド部材およびエンドレスベルトは、プライマー層を 介して粘着層にそれぞれ接着される。例えば、図 3に示すように、蛇行防止ガイド部 材 22はプライマー層 24を介して粘着層 23に、エンドレスベルト 21はプライマー層 24 を介して粘着層 23に、それぞれ接着される。
プライマー層に使用されるプライマーとしては、エンドレスベルトまたは蛇行防止ガ イド部材と粘着層との間の接着力が充分発揮できるものであれば、特に限定されるも のではないが、ポリイソシァネート系プライマーやポリウレタン系プライマーが好ましく 、ポリウレタン系プライマーがさらに好ましい。本発明のエンドレスベルトは、粘着層の エンドレスベルト側及び蛇行防止ガイド部材側にプライマー層を設けることにより、粘 着層を介してエンドレスベルトに貼設される蛇行防止ガイド部材が、ローラー部等で のベルトの変形に対し、エンドレスベルトと蛇行防止ガイド部材との間の接着効果に より、蛇行防止ガイド部材のベルト本体からの剥がれ及びベルト本体の破壊を防ぐこ とがでさる。
[0022] プライマー層の厚みとしては、通常 0. 01-10 μ mとすることが好ましぐ更に好ま しくは 0. 1〜1 μ mである。すなわちプライマー層の厚みが 0. 01 μ m未満の場合は 、プライマーの効果がなくなる。また、 10 mを超えると作業上扱い難くなる。プライ マー層の幅や長さは、蛇行防止ガイド部材ゃ粘着層の形状、大きさに応じて適宜設 定され、特に限定されない。
[0023] 本発明のベルトにおいて、エンドレスベルトと蛇行防止ガイド部材との剥離接着強さ は、大きいほど好ましいと言える力 実用的には 4〜： LOONZlOmmが好ましぐより 好ましくは 6〜50NZlOmmである。
[0024] 蛇行防止ガイドの貼設位置は、特に限定されな!、が、蛇行防止効果、耐久性、補 強効果の点から、エンドレスベルトの両端部に通常設けることが好ましい。例えば、図 2および図 3に示すように、エンドレスベルト 21の内周面の両端部全周に亘つて蛇行 防止ガイド部材 22が、プライマー層 24および粘着層 23を介して貼設することができ る。また、エンドレスベルト 21の外周面にプライマー層 24および粘着層 23を形成して 、蛇行防止ガイド部材 22を貼設してもよい。
[0025] また、ベルト本体の裂けによるベルト破壊を防止するため、エンドレスベルトの内周 面または外周面に強度の向上を目的として粘着テープ状の帯状部材 (以下、「補強 テープ」 、うことがある）を設けてもよ!、。またプライマー層は前記帯状部材上に形 成されてもよい。
[0026] 蛇行防止ガイド部材をエンドレスベルトに貼設する方法は、特に制限されな!、が、 好適な方法としては、例えば、以下の方法をあげることができる。
[0027] まず、蛇行防止ガイド部材 22にプライマーを塗布、乾燥等して、蛇行防止ガイド部 材 22にプライマー層 24を形成する。ついで、プライマー層 24上に粘着層 23を形成 する。粘着層 23の形成方法は、粘着剤をプライマー層 24に直接塗布する方法、ある いは両面粘着テープを用いて接着させる方法などがあげられるが、取扱い易さの点 力も両面粘着テープを用いる方法が好ましい。つぎに、エンドレスベルト 21にプライ マーを塗布等してプライマー層 24を形成し、蛇行防止ガイド部材 22上に形成された 粘着層 23とエンドレスベルト 21上に形成されたプライマー層 24とを接着することによ つて、本発明の蛇行防止ガイド付エンドレスベルトを得ることができる。
[0028] なお、各々の層同士の貼り合わせは、気泡を入れずに貼り合わせることが重要で、 通常ハンドローラ、ゴムローラ、プレス等での貼り合わせ、減圧下または加圧下での 貼り合わせ等の方法を用いることができる。
実施例
[0029] 以下、具体的実施例により本発明をさらに説明する力 本発明はこれらの実施例に 限定されるものではない。 [0030] なお、実施例及び比較例における使用材料は下記の通りである。
1.蛇行防止ガイド部材
(1)ウレタンゴム（タイガースポリマー製タイプレン TR100— 50)
2.エンドレスべノレト
(1)ポリイミド製エンドレスベルト
3.補強テープ
(1)ポリエステル粘着テープ（日東電工社製 NO. 31Bテープ）
4.粘着剤
(1)アクリル系粘着剤 (日東電工製 LA— 150両面テープ (基材レス両面粘着テープ) )
(2)アクリル系粘着剤（日東電工製 NO. 500両面テープ (不織布基材の両面粘着テ 一プ)）
5.プライマー
(1)ポリウレタン系プライマー（コ-シ社製シールフプライマー # 7)
(2)イソシァネート系プライマー（3M社製 N— 200)
(3)イソシァネート系プライマー（バイエル社製デスモジュール RE)
[0031] 実施例及び比較例の評価方法は次の通りである。
1.耐久性試験
両端部に蛇行防止ガイド部材を貼設した、幅 300mm、外径 300mmのエンドレス ベルトをロール径 φ 30mm、ロール速度 lOOmmZ分、ベルト張力 5kgZ300mmの 条件で 100時間連続駆動させ、蛇行防止ガイド部材の剥がれ、ベルトの破壊につい て評価した。変化がないものを A、蛇行防止ガイド部材の剥がれ、ベルトの破壊が発 生したものを Bとした。
2.剥離接着強さ試験
蛇行防止ガイド部材となるウレタンゴムに、粘着層または粘着層およびプライマー 層を介して、 10mm幅に切断したエンドレスベルト基材を 2kg荷重のゴムローラの条 件で貼りあわせ、 JIS K 6854- 1 (90° ピール試験）の剥離接着強さ試験方法に 準じ、引張測定機にて、剥離速度 300mmZ分、 90° ピール測定により接着強さを 測定した。引張測定機は島津製作所製オートグラフ AG500Eを使用した。
[0032] <実施例 1 >
蛇行防止ガイド部材となる厚さ 1. Ommのウレタンゴム（タイガースポリマー製タイプ レン TR100— 50)にゴム用プライマーとしてコ-シ社製シールプライマー # 7を塗布 し、乾燥した後、両面テープ LA— 150を貼りあわせ、スリツターを用い幅 5mm、長さ 942mmに切断し、プライマー層および粘着層を有する蛇行防止ガイド部材を得た。 次 ヽで、厚さ 80 μ m、外径 φ 300mm,幅 300mmのポジイミド製べノレ卜の内面にネ甫 強テープとして幅 10mmのポリエステルテープを貼り付け、さらにポリエステルテープ の上にコ-シ社製シールプライマー # 7を施し、ベルト両端部に沿わせてそれぞれ蛇 行防止ガイド部材を接着した。得られたベルトを用いて耐久性試験にて評価した結 果、ガイド部材の剥がれもベルトの破壊も起きなカゝつた。このときのエンドレスベルト基 材と蛇行防止ガイド部材との剥離接着強さは、 10. 5NZl0mmであった。
[0033] <実施例 2>
ポリイミド製ベルトの内面に補強テープとして貼り付けたポリエステルテープの上に 3M社製 N— 200プライマーを施した以外は、実施例 1と同様の方法でベルトを作製 した。得られたベルトを用いて耐久性試験にて評価した結果、蛇行防止ガイド部材の 剥がれもベルトの破壊も起きなカゝつた。このときのエンドレスベルト基材と蛇行防止ガ イド部材との剥離接着強さは、 9. 1N/I0mmであった。
[0034] <実施例 3 >
使用する両面テープを日東電工社製 NO. 500両面テープに変更する以外は、実 施例 1と同様の方法でベルトを作製した。得られたベルトを用 ヽて耐久性試験にて評 価した結果、蛇行防止ガイド部材の剥がれもベルトの破壊も起きな力つた。このときの エンドレスベルト基材と蛇行防止ガイド部材との剥離接着強さは、 4. 9NZlOmmで めつに。
[0035] <比較例 1 >
蛇行防止ガイド部材となる厚さ 1. Ommのウレタンゴム (タイ力ガースポリマー製タイ プレン TR100— 50)にプライマーを施さず、基材レス両面テープ LA— 150を直接 貝占りあわせ、スリツターを用い幅 5mm、長さ 942mmに切断し、蛇行防止ガイド部材を 得た。次いで、厚さ 80 μ m、外径 φ 300mm,幅 300mmのポリイミド製ベルトの内面 に補強テープとして幅 10mmのポリエステルテープを貼り付け、また、プライマーは 施さず、ベルト両端部に沿わせてそれぞれ前記のようにして得た蛇行防止ガイドを接 着した。得られたベルトを用いて耐久性試験にて評価した結果、 12時間後に蛇行防 止ガイド部材の剥がれが発生した。このときのエンドレスベルト基材と蛇行防止ガイド 部材との剥離接着強さは、 2. 5NZl0mmであった。
[0036] <比較例 2>
蛇行防止ガイド部材となる厚さ 1. Ommのウレタンゴム (タイガースポリマー製タイプ レン TR100— 50)にゴム用プライマーとして 3M社製 N— 200プライマーを施した以 外は、比較例 1と同様の方法でベルトを作製した。得られたベルトを用いて耐久性試 験にて評価した結果、 35時間後に蛇行防止ガイド部材の剥がれが発生した。このと きのエンドレスベルト基材と蛇行防止ガイド部材との剥離接着強さは、 3. 8N/10m mであった。
[0037] <比較例 3 >
ポリイミド製ベルトの内面に補強テープとして貼り付けたポリエステルテープの上に バイエル社製デスモジュール REプライマーを施した以外は、比較例 1と同様の方法 でベルトを作製した。得られたベルトを用いて耐久性試験にて評価した結果、 20時 間後に蛇行防止ガイド部材の剥がれが発生した。このときのエンドレスベルト基材と 蛇行防止ガイド部材との剥離接着強さは、 3. 5NZl0mmであった。
[0038] <比較例 4 >
蛇行防止ガイド部材となる厚さ 1. Ommのウレタンゴム (タイガースポリマー製タイプ レン TR100— 50)にゴム用プライマーとしてバイエル社製デスモジュール REプライ マーを施した以外は、比較例 1と同様の方法でベルトを作製した。得られたベルトを 用いて耐久性試験にて評価した結果、 26時間後に蛇行防止ガイド部材の剥がれが 発生した。このときのエンドレスベルト基材と蛇行防止ガイド部材の剥離接着強さは、 3. 7NZ 10mmであった。
[0039] [表 1] 剥離接着強さ
耐久性試験
( N/ 1 0 m m) 実施例 1 1 0 . 5 A
実施例 2 9 . 1 A
実施例 3 4 . 9 A
比較例 1 2 . 5 B
比較例 2 3 . 8 B
比較例 3 3 . 5 B
比較例 4 3 . 7 B
剥離接着強さ
(NZlOmm)耐久性試験実施例 110. 5A実施例 29. 1A実施例 34. 9A比較例 12 . 5B比較例 23. 8B比較例 33. 5B比較例 43. 7B
[0040] 表 1の結果が示すように、エンドレスベルト側および蛇行防止ガイド側の両方 (粘着 層の両面）にプライマー層を有する実施例 1〜3のベルトでは、 100時間の連続耐久 試験によっても蛇行防止ガイド部材の剥がれ、ベルトの破壊を生じな力つた。一方、 エンドレスベルト側および蛇行防止ガイド側の両方または一方にプライマー層を設け ていない比較例 1〜4のベルトでは、それぞれ、 12時間後、 35時間後、 20時間後、 2 6時間後に蛇行防止ガイド部材の剥がれを生じた。
[0041] 本発明を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲 を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明ら かである。
本出願は、 2005年 3月 25日出願の日本特許出願 (特願 2005— 088051)に基づ くものであり、その内容はここに参照として取り込まれる。
産業上の利用可能性
[0042] 本発明の蛇行防止ガイド付エンドレスベルトは、プリンター、複写機、ビデオプリンタ 一等の電子写真記録装置などに好適に使用できる。

Claims

請求の範囲
榭脂製のエンドレスベルト、
粘着層、
前記榭脂層を介して前記エンドレスベルトに貼設された蛇行防止ガイド部材、及び 前記粘着層の両面に設けられたプライマー層を有する蛇行防止ガイド付エンドレス ベノレト。
前記エンドレスベルトと前記蛇行防止ガイド部材との剥離接着強さが 4〜： LOONZ1 Ommである請求項 1記載の蛇行防止ガイド付エンドレスベルト。
PCT/JP2006/318778 2006-09-21 2006-09-21 Courroie sans fin pourvue d'un guide empêchant tout serpentement WO2008035429A1 (fr)