WO2007120561A2 - An absorbent member comprising a modified water absorbent resin - Google Patents

An absorbent member comprising a modified water absorbent resin Download PDF

Info

Publication number
WO2007120561A2
WO2007120561A2 PCT/US2007/008475 US2007008475W WO2007120561A2 WO 2007120561 A2 WO2007120561 A2 WO 2007120561A2 US 2007008475 W US2007008475 W US 2007008475W WO 2007120561 A2 WO2007120561 A2 WO 2007120561A2
Authority
WO
WIPO (PCT)
Prior art keywords
absorbent resin
water absorbent
water
weight
mixing
Prior art date
Application number
PCT/US2007/008475
Other languages
English (en)
French (fr)
Other versions
WO2007120561A3 (en
Inventor
Makoto Matsumoto
Yoshiro Mitsukami
Taku Iwamura
Original Assignee
The Procter & Gamble Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2006108083A external-priority patent/JP2007277466A/ja
Priority claimed from JP2006157582A external-priority patent/JP2007326912A/ja
Application filed by The Procter & Gamble Company filed Critical The Procter & Gamble Company
Priority to JP2009504294A priority Critical patent/JP4928602B2/ja
Priority to CA002649299A priority patent/CA2649299A1/en
Priority to EP07754914A priority patent/EP2004732A2/en
Priority to MX2008013041A priority patent/MX2008013041A/es
Publication of WO2007120561A2 publication Critical patent/WO2007120561A2/en
Publication of WO2007120561A3 publication Critical patent/WO2007120561A3/en

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08JWORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J3/00Processes of treating or compounding macromolecular substances
    • C08J3/28Treatment by wave energy or particle radiation
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61LMETHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
    • A61L15/00Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
    • A61L15/16Bandages, dressings or absorbent pads for physiological fluids such as urine or blood, e.g. sanitary towels, tampons
    • A61L15/42Use of materials characterised by their function or physical properties
    • A61L15/60Liquid-swellable gel-forming materials, e.g. super-absorbents
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08JWORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2300/00Characterised by the use of unspecified polymers
    • C08J2300/14Water soluble or water swellable polymers, e.g. aqueous gels
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08JWORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2333/00Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Derivatives of such polymers
    • C08J2333/02Homopolymers or copolymers of acids; Metal or ammonium salts thereof
    • YGENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10TTECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00Stock material or miscellaneous articles
    • Y10T428/31504Composite [nonstructural laminate]
    • Y10T428/31855Of addition polymer from unsaturated monomers

Definitions

  • the absorbent member for use in absorbent articles, especially diapers and training pants.
  • the absorbent member comprises a water absorbent resin made by a method comprising the step of irradiating a water absorbent resin with active energy rays.
  • a water absorbent resin has been hitherto used as a component for hygienic materials such as sanitary cotton, disposable diaper, and absorbents for other kinds of body fluid.
  • the water absorbent resin hydrolyzate of starch-acrylonitrile graft polymer, neutralized starch-acrylic acid graft polymer, saponified vinyl acetate-acrylic ester copolymer, hydrolyzate of acrylonitrile copolymer or acrylamide copolymer, and cross-linked product thereof, and partially neutralized cross-linked acrylic acid may be cited.
  • These water absorbent resins have an internal cross-linked structure and are in-soluble in water.
  • the characteristics of such a water absorbent resin include for example high absorption capacity, high absorption speed, high gel strength, and fully satisfactory suction power necessary for sucking water from a medium.
  • the water absorbing properties are affected by cross-link density, and an increase in the cross-link density typically leads to an increase in the gel strength but a decrease in the amount of water absorbed.
  • increased absorption capacity typically leads to reduced absorption speed, reduced gel strength, and reduced suction power, for example.
  • the water absorbent resin having improved absorption capacity therefore, would possibly induce inhomogeneous absorption of water and lead to aggregation of absorbent particles when the water absorbent resin particles contact with water, and also induce dramatic decrease in absorption speed because the water is not diffused throughout the entire volumes of water absorbent resin particles.
  • a method which comprises heating an aqueous composition of a polymer having a partial alkali metal salt of polyacrylic acid as a main component and having a low cross-link density in the presence of a water-soluble peroxide radical initiating agent thereby introducing a cross-link therein by radical cross-linking has been proposed (U.S. Patent No. 4,910,250). It is difficult to distribute uniformly internal cross-links in the polymer and uneasy to adjust the cross-link density.
  • a polymer which contains water-soluble polyacrylic acid gel having low cross-link density is obtained and then the polymer is heated together with a persulfate added thereto as a polymerization initiator.
  • U.S. Patent No. 4,910,250 states that excellent water absorbing properties can be attained and a water absorbent resin having no stickiness can be obtained because the adjustment of the amount of the initiator to be added can allow precise control of cross-link density and uniform presence of cross-link in the polymer.
  • a reaction system has also been known, which comprises adding a hydrophilic polymer component and a photo-polymerization initiator, further adding a cross-linking agent thereto, and irradiating them with ultraviolet rays to form an internal cross-link (WO 2004/031253).
  • a method which comprises treating a surface of a water absorbent resin to increase cross-link density of the surface of water absorbent resin has also been known (U.S. Patent Nos. 4,666,983 and 5,422,405, for example).
  • Such water absorbent resins as cited in the preceding publications comprise a reactive functional group on their surfaces.
  • a surface cross-linking agent capable of reacting with the functional groups in order to introduce cross-links between the functional groups cross-link density on the surface of water absorbent resin can be increased and a water absorbent resin having excellent water absorbing properties even under pressure can be obtained.
  • the present invention refers to an absorbent member for use in absorbent articles, the absorbent member comprising modified water absorbent resin.
  • the water absorbent resin is made by a method comprising:
  • a mixing step comprising mixing water absorbent resin, water, and a water-soluble or a heat-degreadable radical polymerization initiator without addition of an ethylenically unsaturated monomer, to obtain a water absorbent resin composition
  • the surface water content of said water absorbent resin in said water absorbent resin composition at least at any point of time in the irradiating step (ii) is controlled to a level of not lower than 3.0% by weight based on 100% by weight of the water absorbent resin.
  • the amount of water mixed in step (i) exceeds 20 parts by weight and is not more than 100 parts by weight based on 100 parts by weight of the water absorbent resin.
  • the present invention further refers to a method of making such absorbent members and modifications of making the absorbent members of claims 1 to 3 as set out in the following description and in the dependent claims.
  • Fig. 1 is a schematic diagram of a measuring device to be used in determining the saline flow conductivity (SFC).
  • the object of surface cross-linking a water absorbent resin is achieved by a method for producing a water absorbent resin having an improved balance between absorption capacity and absorption speed.
  • this object requires a cross-linking agent having at least two functional groups capable of reacting with the functional group present on the surface of the water absorbent resin.
  • the cross-linking agent polyhydric alcohols, polyvalent glycidyl ethers, haloepoxy compounds, polyvalent aldehydes, polyvalent amines, and polyvalent metal salts may be cited. Since the cross-linking agent has low reactivity, the relevant reaction is required to be carried out at an elevated temperature and occasionally to be retained in a heated state for a long time. The reaction, therefore, requires relatively high amounts of energy and time.
  • This invention aims at providing a method for an efficient production of a water absorbent resin having good absorbency against pressure, absorption speed, gel strength, and permeability of liquid.
  • a method for the production of a modified water absorbent resin comprises (i) a mixing step comprising mixing a water absorbent resin, water, and a water-soluble radical polymerization initiator without addition of an ethylenically unsaturated monomer, to obtain a water absorbent resin composition, and (ii) an irradiating step comprising irradiating said water absorbent resin composition obtained in the mixing step with active energy rays, wherein the surface water content of said water absorbent resin in said water absorbent resin composition at least at any point of time during the irradiating step £ii) is controlled to a level of not lower than 3.0% by weight based on 100% by weight of the water absorbent resin.
  • the amount of water mixed in step (i) exceeds 20 parts by weight and is not more than 100 parts by weight based on 100 parts by weight of the water absorbent resin.
  • a uniform cross-linking structure can be introduced on a surface of water absorbent particles.
  • the obtained water absorbent resin has good absorption capacity, good absorption speed, good gel strength, and good suction power.
  • the method of this invention for the production of a modified water absorbent resin achieves surface cross-linking by irradiation with active energy rays, the water absorbent resin can be modified in a shorter period as compared with the conventional method.
  • the water absorbent resin which can be used in this invention is a water-swellable, water-insoluble, cross-linked polymer which can form a hydrogel.
  • the term "ability to swell in water” as used in this invention refers to the free swelling capacity of a given sample in an aqueous 0.9% by weight sodium chloride solution (physiological saline), i.e. the ability of the sample to absorb the physiological saline essentially not lower than 2 g/g and preferably in the range of from 5 to 100 g/g and more preferably in the range of from 10 to 60 g/g.
  • insoluble in water means that an uncross-linked water-soluble component (a water-soluble polymer; hereinafter also called as “an elutable and soluble portion”) in the water absorbent resin, which is preferably in the range of from 0 to 50% by weight, more preferably not more than 25% by weight, still more preferably not more than 15% by weight, and particularly preferably not more than 10% by weight.
  • a value of centrifuge retention capacity a value measured by the method specified in the working example cited below is adopted.
  • an elutable and soluble portion a value measured by a method described below is adopted.
  • a covered plastic container (with a diameter of 6 cm and a height of 9 cm) having a volume of 250 ml, 184.3 g of physiological saline is placed, 1.00 g of water absorbent resin is added.
  • An elutable and soluble portion in a resin is extracted by stirring the mixture for 16 hours with a magnetic stirrer having a diameter of 8 mm and a length of 25 mm at a rotation speed of 500 rpm.
  • This extract is filtrated with one sheet of a filter paper (0.26 mm in thickness and 5 ⁇ m in retained particle diameter; made by Advantec Toyo K.K. and sold under the product name of "JIS P 3801 No. 2"). Then, 50.0 g of the resultant filtrate is taken to make a solution for measuring.
  • an elutable and soluble portion in the water absorbent resin can be calculated on the basis of an average molecular weight of the monomers and the titration amounts obtained by the above described operation in accordance to the equation described below.
  • an average molecular weight of a monomer is calculated, by using a neutralization ratio obtained by titration according to the equation described below.
  • modification refers to all physical or chemical actions performed on a given water absorbent resin , including surface cross-linking, formation of pores therein, and imparting hydrophilic or hydrophobic property thereto, for example.
  • the water absorbent resin which can be used in this invention is not particularly restricted but is only required to be capable of being obtained by polymerizing a monomer component essentially containing an ethylenically unsaturated monomer by means of any of the known methods.
  • the ethylenically unsaturated monomer is not particularly restricted but is preferred to be a monomer having an unsaturated double bond at the terminal thereof.
  • Typical examples thereof are, anionic monomers such as (meth)acrylic acid, 2-(meth)acryloyl ethane sulfonic acid, 2-(meth)acryloyl propane sulfonic acid, 2-(meth)acrylamide-2-methyl propane sulfonic acid, vinyl sulfonic acid, and styrene sulfonic acid, and salts thereof; nonionic hydrophilic group-containing monomers such as (meth)acrylamide, N— substituted (meth)acrylamide, 2-hydroxyethyl (meth)acrylate, and 2-hydroxypropyl (meth)acrylate; and amino group-containing unsaturated monomers such as N,N-dimethylaminoethyl (meth)acrylate, N,N-diethylaminoethyl (meth)acrylate, N
  • monomers may be used either singly or in the form of a mixture of two or more members.
  • (meth)acrylic acid, 2-(meth)acryloyl ethane sulfonic acid, 2-(meth)acrylamide-2-methylpropane sulfonic acid, and salts thereof N,N-dimethylaminoethyl(meth)acrylate and quaternized N,N-dimethylaminoethyl (meth)acrylate, and (meth)acrylamide prove preferable, and acrylic acid and/or the salt thereof are particularly preferable.
  • the monovalent salt of acrylic acid selected among alkali metal salt, ammonium salt, and amine salt of acrylic acid may be preferably used. More preferably, alkali metal salts of acrylic acid may be used, and acrylic acid salts selected among sodium salt, lithium salt, and potassium salt thereof may be particularly preferably used.
  • a monomer component other than the monomers cited above may be used in such an amount as to impair effects of this invention.
  • hydrophobic monomers such as aromatic ethylenically unsaturated monomers having from 8 to 30 carbon atoms, aliphatic ethylenically unsaturated monomers having from 2 to 20 carbon atoms, alicyclic ethylenically unsaturated monomers having from 5 to 15 carbon atoms, and alkyl esters of (meth)acrylic acid containing alkyl groups having from 4 to 50 carbon atoms may be cited.
  • the proportion of such a hydrophobic monomer is generally in the range of from 0 to 20 parts by weight, based on 100 parts by weight of the ethylenically unsaturated monomer. If the proportion of the hydrophobic monomer exceeds 20 parts by weight, water absorbing properties of the produced water absorbent resin would be degraded.
  • the water absorbent resin which can be used in this invention is insolubilized by the formation of an internal cross-link.
  • This internal cross-link may be of self-cross-linking type using no cross-linking agent, or alternatively can be formed by using an internal cross-linking agent having not less than two polymerizable unsaturated groups and/or not less than two reactive functional groups in one molecular unit.
  • the internal cross-linking agent is not particularly restricted.
  • These internal cross-linking agents may be used singly or in the form of a mixture of two or more members.
  • the amount of the internal cross-linking agent to be used is preferably in the range of from 0.0001 to 1 mol%, more preferably from 0.001 to 0.5 mol%, and still more preferably from 0.005 to 0.2 mol%, based on the total amount of monomer components used in the production of a water absorbent resin. If this amount is less than 0.0001 mol%, the internal cross-linking agent may not be introduced satisfactorily into the resin. Conversely, if the amount exceeds 1 mol%, gel strength of the water absorbent resin may be too heigh and the absorption capacity may consequently be too low.
  • the internal cross-linking agent can be added to the reaction system prior to, during, or after the polymerization of monomers, or after the neutralization of the produced polymer.
  • Suitable polymerization initiators include for example water-soluble radical polymerization initiators such as persulfates such as potassium persulfate, ammonium persulfate, and sodium persulfate; potassium peracetate, sodium peracetate, potassium percarbonate, sodium pcrcarbonate, and t-butyl hydroperoxide; hydrogen peroxide; azo compounds such as 2,2'-azobis(2-amidinopropane)-dihydrochloride, and photopolymerization initiators such as 2-hydroxy-2-methyl-l-phenyl-propan-l-one.
  • the water-soluble radical polymerization initiators may be combined with a reducing agent such as a sulfite, L-ascorbic acid, or a ferric salt, to be used as a redox type initiator.
  • the concentration of the monomer in the aqueous monomer solution is not particularly restricted but is preferably within the range of from 15 to 90% by weight, and more preferably from 35 to 80% by weight. If this concentration is less than 15% by weight, a lot of heat and time would be required for drying because the resultant hydrogel has an unduly large content of water.
  • a method for the polymerization is not particularly restricted but may be selected among well-known methods such as solution polymerization, reversed-phase suspension polymerization, precipitation polymerization, and bulk polymerization.
  • the aqueous solution polymerization which comprises dissolving a monomer in an aqueous solution and polymerizing it in the aqueous solution, and the reversed phase suspension polymerization may be particularly advantageous due to the ease of control of polymerization reaction and the performance of a produced water absorbent resin.
  • the polymerization initiator In initiating the polymerization, the polymerization initiator is used to start the polymerization. Besides the polymerization initiator, active energy rays such as ultraviolet rays, electron radiation, and ⁇ rays may be used either singly or in combination with a polymerization initiator.
  • active energy rays such as ultraviolet rays, electron radiation, and ⁇ rays may be used either singly or in combination with a polymerization initiator.
  • the temperature in initiating the polymerization depends on the kind of polymerization initiator used, it is preferably in the range of from 15 to 13O 0 C, and more preferably from 20 to 120 0 C. If the temperature in initiating the polymerization deviates from the range mentioned above, this may result increased amounts of residual monomer in the produced water absorbent resin. Also, self cross-linking may proceed excessively, consequently degrading water absorbing properties of the produced water absorbent resin.
  • the "reversed phase suspension polymerization” is a method of polymerization in which an aqueous monomer solution is suspended in a hydrophobic organic solvent. It is disclosed in U.S. Patent Nos. 4,093,776, 4,367,323, 4,446,261, 4,683,274, and 5,244,735, for example.
  • the "aqueous solution polymerization” is a method for polymerizing an aqueous monomer solution without using a dispersing solvent. It is disclosed in U.S. Patent Nos. 4,625,001 , 4,873,299, 4,286,082, 4,973,632, 4,985,518, 5, 124,416, 5,250,640, 5,264,495, 5,145,906, and 5,380,808, and European Patent Nos. 0 81 1 636, 0 955 086, and 0 922 717, for example.
  • the monomers and the initiators which are cited by way of illustration in these methods of polymerization can be applied to this invention.
  • the aqueous solution polymerization may be performed by polymerizing partially neutralized acrylic acid or by polymerizing an acid group-containing monomer such as acrylic acid and the like and subsequently neutralizing the resultant polymer with such an alkali compound as sodium hydroxide or sodium carbonate.
  • the water absorbent resin to be used in this invention preferably has an acid group and a specific neutralization ratio (mol% of the neutralized acids group in the whole of acid groups).
  • the neutralization ratio of the produced water absorbent resin (mol% of the neutralized acids group in the whole of acid groups) is in the range of from 25 to 100 mol%, and preferably from 50 to 90 mol%, more preferably of from 50 to 75 mol%, and most preferably from 60 to 70 mol%.
  • the preferable embodiment of this invention is to provide a method for the production of a modified water absorbent resin, which comprises (i) mixing a water absorbent resin, water, and persulfate as a radical polymerization initiator without addition of an ethylenically unsaturated monomer and (ii) irradiating the resultant mixture with active energy rays, wherein the water absorbent resin contains an acid group and has a neutralization ratio (mol% of the neutralized acids group in the whole of acid groups) in the range of 50 to 75 mol%. After the completion of the polymerization, a hydrogel-like cross-linked polymer is obtained.
  • the polymer is preferably dried so as to give a water content (% by weight) [100 - (Solid content) (% by weight)] which will be specifically described herein below.
  • a water absorbent resin composition is obtained by mixing a water absorbent resin, a water-soluble radical polymerization initiator and/or a heat-degradable radical polymerization initiator (in the present specification, referred collectively to as "radical polymerization initiator"), and water, which will be described specifically herein below. Then, the resultant composition is irradiated with active energy rays to modify the water absorbent resin. This modification results from the action of active radicals generated from the polymerization initiator on the main chain of the polymer.
  • This modification does not need to be limited to water absorbent resin which is obtained by polymerizing a water-soluble ethylenically unsaturated monomer as described above but may be effected on such a water absorbent resin as cross-linked polyvinyl alcohol, cross-linked polyethylene oxide, cross-linked polyaspartic acid, and cross-linked carboxymethyl cellulose, for example.
  • the water absorbent resin which can be used in this invention is preferably a powdery water absorbent resin which is obtained by polymerizing a monomer having acrylic acid (salt) particularly as its main component.
  • the hydrogel-like polymer which is obtained by polymerization is preferably dried and subsequently pulverized to a water absorbent resin.
  • the drying may be effected by using a drier such as a hot air drier at a temperature in the range of from 100 to 220 0 C, and more preferably from 120 to 200 0 C.
  • the powdering machines having at least one of the powdering mechanisms such as cutting, shearing, striking, and rubbing can be adopted particularly favorably.
  • the powdering machines which have cutting and shearing as main mechanisms can be used particularly advantageously.
  • a roll mill (roll rotary type) powdering machine may be cited as a preferred example.
  • the water absorbent resin which can be used in this invention is preferably in a powdery form. More preferably, it is a powdery water absorbent resin which contains particles of a diameter in the range of from 150 to 850 ⁇ m (as defined by sieve classification) in a proportion in the range of from 90 to 100 % by weight, and particularly preferably from 95 to 100% by weight.
  • the modified water absorbent resin having a particle diameter exceeding 850 ⁇ m is used in disposable diapers, for example, it may rupture the top sheet of a diaper.
  • the fine particles may scatter and clog the texture while in use and would degrade water absorbing properties of the modified water absorbent resin.
  • the weight average particle diameter of the water absorbent resin may be in the range of from 10 to 1,000 ⁇ m, and preferably from 200 to 600 ⁇ m. If the weight average particle diameter is less than 10 ⁇ m, this may possibly result in drawbacks regarding safety and health. Conversely, if it exceeds 1,000 ⁇ m, the water absorbent resin may not be well-suited for use in disposable diapers, for example.
  • a value of the particle diameter a value measured by a measuring method of a particle size distribution specified in the working example cited below is adopted.
  • the water absorbent resin to be used in this invention is preferably obtained by producing a water absorbent resin precursor having a low neutralization ratio, and mixing the water absorbent resin precursor with a base.
  • a multifunctional surface-treatment agent has been conventionally used for the surface-treatment (surface cross-linking).
  • the multifunctional surface-treatment agent serves to react with a carboxyl group (-COOH) in a water absorbent resin but do not react with the salt thereof (for example, -COONa).
  • uniform cross-linking can be attained by preparing an ethylenically unsaturated monomer mixture (for example, a mixture of acrylic acid with sodium acrylate) in which -COOHACOONa ratio has been adjusted within a suitable range in advance, polymerizing the resultant mixture to produce a water absorbent resin having the -COOH and -COONa groups uniformly distributed therein, and subjecting the resultant water absorbent resin to surface cross-linking with a multifunctional surface-treatment agent.
  • an ethylenically unsaturated monomer mixture for example, a mixture of acrylic acid with sodium acrylate
  • -COOHACOONa ratio has been adjusted within a suitable range in advance
  • a water absorbent resin is obtained by polymerizing a monomer mixture including an acid type ethylenically unsaturated monomer like acrylic acid as a main component, and then neutralizing the resultant polymer with an alkali compound such as sodium hydroxide and sodium carbonate, the resultant water absorbent resin has a small elutable portion and high gel strength.
  • the absorbent resin when subjected to surface cross-linking with a multifunctional surface-treatment agent, the absorbent resin likely has degraded water absorbency, because the -COOH and -COONa groups are not uniformly distributed in the water absorbent resin.
  • the water absorbent resin to be produced by the latter method is not desirably subjected to such a conventional surface cross-linking with a multifunctional surface-treatment agent.
  • a water-soluble radical polymerization initiator or a heat-degradable radical polymerization initiator induces cross-linking by extracting a hydrogen in a main chain to form a radical and using the radical for coupling, but not by reacting with -COOH, the cross-linking reaction is not affected by whether or not -COOH groups are uniformly distributed in the water absorbent resin.
  • a water absorbent resin is obtained by polymerizing a monomer or a monomer mixture including as a main component an acid type ethylenically unsaturated monomer like acrylic acid to obtain a water absorbent resin precursor having a low neutralization ratio.
  • This water absorbent resin precursor is then neutralized with an alkali compound such as sodium hydroxide and sodium carbonate, and the resultant modified water absorbent yields high gel strength and good water absorbency.
  • a water absorbent resin precursor having a low neutralization ratio is obtained by polymerizing a monomer or a monomer mixture including as a main component an acid type ethylenically unsaturated monomer, and then adding a base to the water absorbent resin precursor, the base may be added either in a solid form or in a liquid form.
  • the base is added in a liquid form, particularly in an aqueous solution form.
  • adding a base to a water absorbent resin precursor and producing a water absorbent resin composition can done simultaneously.
  • the base which can be used in this embodiment is not particularly limited so long as it permits the neutralization of the water absorbent resin precursor ⁇ J having a low neutralization ratio to a desired neutralization ratio.
  • Well-known inorganic and organic salt and acid can be used, such as sodium hydroxide, potassium hydroxide, lithium hydroxide, ammonium hydroxide, sodium carbonate, potassium carbonate, ammonium carbonate, sodium bicarbonate, potassium bicarbonate, ammonium bicarbonate, sodium phosphate, potassium phosphate, ammonium phosphate, sodium borate, potassium borate, ammonium pentaborate, sodium acetate, potassium acetate, ammonium acetate, sodium lactate, potassium lactate, ammonium lactate, sodium propionate, potassium propionate, ammonium propionate.
  • Suitable monomers are an acid type ethylenically unsaturated monomer such as acrylic acid, hydroxide of monovalent cation such as sodium hydroxide, potassium hydroxide, lithium hydroxide, and ammonium hydroxide; and carbonate of monovalent cation such as sodium carbonate, potassium carbonate, ammonium carbonate, sodium bicarbonate, potassium bicarbonate, and ammonium bicarbonate or mixtures thereof.
  • Suitable monomers should have good physical properties, and permit efficient adjustment of neutralization ratio to a desired level.
  • the amount of base added is not particularly limited and can be suitably selected so that the water absorbent resin used in the mixing step (i) has a desired neutralization ratio adjusted within the preferable range as mentioned above.
  • water absorbent resin precursor having a low neutralization ratio is referred to as a water absorbent resin precursor having a low neutralization ratio (mol% of the neutralized acids group in the whole of acid groups) or having no neutralized acid groups (i.e., the neutralization ratio is zero), and typically referred to as a water absorbent resin precursor having a neutralization ratio (mol% of the neutralized acids group in the whole of acid groups) of from 0 to 50 mol%, more preferably from 0 to 20 mol%.
  • Such a water absorbent resin precursor having a low neutralization ratio can be obtained by the same method as mentioned above by using a monomer mixture including as a main component an acid group-containing monomer like acrylic acid wherein a neutralization ratio is preferably adjusted within the above range.
  • the water content of the water absorbent resin prior to the modification to be used in the method for production of a modified water absorbent resin contemplated by this invention has no particular restriction so long as the water absorbent resin has fluidity.
  • the water absorbent resin after being dried at 180 0 C for three hours has a water content falling in the preferable range of from 0 to 50% by weight, from 0 to 40% by weight, from 0 to 30% by weight, from 0 to 20% by weight, from 0 to 10% by weight, and more preferably from 0 to 5% by weight in this order.
  • the water absorbent resin to be used in this invention is not limited to the product of the method as described above but may be any product obtained by some other method. While the water absorbent resin which is obtained by the method described above is a water absorbent resin having undergone no surface cross-linking, for use in the method for producing a modified water absorbent resin of this invention, the water absorbent resin which has undergone surface cross-linking in advance with a polyhydric alcohol, a polyvalent epoxy compound, an alkylene carbonate, or an oxazolidone compound can be adopted.
  • a water absorbent resin composition is obtained by mixing water and a radical polymerization initiator (a water-soluble radical polymerization initiator and/or a heat-degradable radical polymerization initiator) with the water absorbent resin, without addition of an ethylenically unsaturated monomer.
  • a radical polymerization initiator a water-soluble radical polymerization initiator and/or a heat-degradable radical polymerization initiator
  • the surface cross-linking of a water absorbent resin has been generally effected by using a surface cross-linking agent.
  • the incorporation of the surface cross-linking agent results in strong, chemical binding between the functional groups present on the surface of resin and the surface cross-linking agent, thereby introducing a stable surface cross-link structure into the resin surface. Then, by properly selecting a chain length of the surface cross-linking agent, the distance between cross-links can be adjusted easily. By adjusting an amount of the surface cross-linking agent to be incorporated, the cross-link density can be controlled.
  • This invention permits the modification of a water absorbent resin, specifically the introduction of a cross-link structure to the surface of the water absorbent resin, by merely using a radical polymerization initiator without requiring the incorporation of the surface cross-linking agent. Further, by additionally adding water to obtain a water absorbent composition and irradiating the water absorbent resin composition with active energy rays, a cross-linked structure can be effectively introduced to the surface of the water absorbent resin particles and at the same time, the produced modified water absorbent resin has improved water absorption properties.
  • the addition of water in a relatively large amount to the water absorbent resin in the step (i) permits the efficient introduction of a cross-linking structure on a surface of the water absorbent resin in the step (ii) described in detail below, and thus also results in shortened irradiation time required for improving absorbency against pressure (AAP) and the saline flow conductivity (SFC) of the modified water absorbent resin to a desired level.
  • AAP absorbency against pressure
  • SFC saline flow conductivity
  • This invention uses the expression "without addition of an ethylenically unsaturated monomer” with the object of preventing a radical polymerization initiator from reacting with an ethylenically unsaturated monomer to avoid the consumption of the radical polymerization initiator that is activated by the irradiation with active energy rays prior to the action on the surface of the water absorbent resin in the step (ii).
  • water is mixed with a water absorbent resin.
  • mixing of a water absorbent resin and water may be conducted by adding water alone, or by adding water in a form of an aqueous solution containing another component.
  • an aqueous solution containing a radical polymerization initiator, an aqueous solution containing a mixing aid, and the like may be included.
  • the amount of water mixed with a water absorbent resin preferably exceeds 20_parts by weight and is not more than 100 parts by weight, based on 100 parts by weight of the water absorbent resin (as reduced to as 100 parts by weight of a solid content).
  • the addition of water in a relatively large amount to the water absorbent resin in the step (i) permits the efficient introduction of a cross-linking structure on a surface of the water absorbent resin in the step (ii) described in detail below, and thus a shortened irradiation time.
  • the preferable amount of water mixed with the water absorbent resin exceeds 20 parts by weight and is not more than 70 parts by weight, or exceeds 20 parts by weight and is not more than 50 parts by weight, or exceeds 20 parts by weight and is not more than 40 parts by weight, or exceeds 20 parts by weight and is not more than 30 parts by weight, in this order, based on 100 parts by weight of a water absorbent resin (referred to 100 parts by weight of a solid content). If the amount of water exceeds 100 parts by weight, a large amount of energy may be necessary during a drying step after irradiation with active energy rays. In addition, the water absorbent resin may possibly be decomposed.
  • a water-soluble radical polymerization initiator and/or a heat-degradable radical polymerization initiator are mixed as a radical polymerization initiator with the water absorbent resin composition.
  • a water-soluble radical polymerization initiator and/or a heat-degradable radical polymerization initiator are sometimes called collectively as radical polymerization initiator.
  • a water-soluble radical polymerization initiator when “a water-soluble radical polymerization initiator" is mixed with a water absorbent resin, the initiator can be easily dispersed uniformly on the surface of the water absorbent resin which excels in hydrophilic property and water absorbing property.
  • a water absorbent resin excelling in water absorbing properties can be produced.
  • the water-soluble radical polymerization initiator to be used in this invention has solubility in water (25°C) of not less than 1% by weight, preferably not less than 5% by weight, and more preferably not less than 10% by weight.
  • Typical examples are, persulfates ' such as ammonium persulfate, sodium persulfate, and potassium persulfate; hydrogen peroxide; and water-soluble azo compounds such as 2,2'-azobis-2-amidinopropane dihydrochloride and
  • heat-degradable radical polymerization initiator to be used in this invention is a compound which generates a radical by heating.
  • a heat-degradable radical polymerization initiator having 10 hour half-life decomposition temperature in the range of 0 to 120 0 C, more preferably 20 to 100 0 C, may be preferably used in this invention.
  • a heat-degradable radical polymerization initiator having 10 hour half-life decomposition temperature in the range of 40 to 80 0 C can be particularly preferably used in this invention. If the lower limit of 10 hour half-life decomposition temperature is less than 0 0 C (lower limit), the heat-degradable radical polymerization initiator would be too unstable during storage. Conversely, if the upper limit thereof exceeds 120 0 C (upper limit), the chemical stability of the heat-degradable radical polymerization initiator may be too high.
  • a heat-degradable radical polymerization initiator when “a heat-degradable radical polymerization initiator" is mixed with a water absorbent resin, the surface modification can be carried out at a low temperature for a short period of time, and the resultant modified water absorbent resin can manifest high gel strength and good water-absorbing properties.
  • the heat-degradable radical polymerization initiator to be used in this invention may be either oil-soluble or water-soluble.
  • the decomposition rate of an oil-soluble heat-degradable radical polymerization initiator is less sensitive to a pH value and ion strength as compared to that of a water-soluble heat-degradable radical polymerization initiator.
  • a water-soluble heat-degradable radical polymerization initiator may be more preferably used in respect of its permeability to a water absorbent resin because the water absorbent resin is hydrophilic.
  • the heat-degradable radical polymerization initiator is relatively inexpensive and the process and devices for the production thereof can be simplified because the strict light- shielding is not always required, as compared to a compound which has been commercially available as a photo-degradable radical polymerization initiator.
  • heat-degradable radical polymerization initiator are persulfates such as sodium persulfate, ammonium persulfate, and potassium persulfate; percarbonates such as sodium percarbonate; peracetates such as peracetic acid, and sodium peracetate; hydrogen peroxide; and azo compounds such as 2,2'-azobis(2-amidinopropane) dihydrochloride, 2,2'-azobis[2-(2-imidazolin-2-yl) propane] dihydrochloride, and 2,2'-azobis(2-methylpropionitrile.
  • persulfates such as sodium persulfate, ammonium persulfate, and potassium persulfate
  • percarbonates such as sodium percarbonate
  • peracetates such as peracetic acid, and sodium peracetate
  • hydrogen peroxide and azo compounds
  • 2,2'-azobis(2-amidinopropane) dihydrochloride 2,2'-azobis[2-(2-imidazolin-2
  • persulfates including sodium persulfate, ammonium persulfate, and potassium persulfate, and azo compounds including 2,2'-azobis(2-amidinopropane) dihydrochloride, 2 5 2'-azobis[2-(2-imidazolin-2-yl) propane] dihydrochloride, and 2,2'-azobis(2-methylpropionitrile) which have 10 hour half-life decomposition temperature in the range of 40 to 80 0 C can be used preferably.
  • persulfates may be preferably used in respect of excellent absorbency of physiological saline against pressure, saline flow conductivity, and free swelling capacity.
  • the amount of the radical polymerization initiator is preferably in the range of from 0.01 to 20 parts by weight, more preferably from 0.1 to 15 parts by weight, and particularly preferably from 1 to 10 parts by weight, based on 100 parts by weight of the water absorbent resin. If the amount of the radical polymerization initiator to be mixed is less than 0.01 parts by weight, the water absorbent resin may not be sufficiently modified even upon exposure to the active energy rays. Conversely, if the amount of the radical polymerization initiator to be mixed exceeds 20 parts by weight, water absorbing properties of the modified water absorbent resin may possibly be degraded.
  • the term "oil-soluble photopolymerization initiator” as used herein means a compound having water-solubility of less than 1% by weight.
  • an initiator other than the radical polymerization initiator can be additionally used.
  • the other polymerization initiators which can be additionally used are photopolymerization initiators such as oil-soluble benzoin derivatives, benzyl derivatives, and acetophenone derivatives, and oil-soluble organic peroxides such as oil-soluble ketone peroxide, peroxyketal, hydroperoxide, dialkyl peroxide, peroxy esters, and peroxycarbonate.
  • photopolymerization initiators may be commercially available products such as, for example, products from Ciba Specialty Chemicals sold under the trademark designations of Irgacure 184 (hydroxycyclohexyl-phenyl ketone) and Irgacure 2959 (l-[4-(2-hydroxyethoxy)-phenyl]-2-hydroxy-2-methyl-l-propan-l-on).
  • the amount of the other initiator to be used is in the range of from 0 to 20 parts by weight, preferably from 0 to 15 parts by weight, and particularly preferably from 0 to 10 parts by weight, based on 100 parts by weight of the water absorbent resin.
  • This rate corresponds to a smaller amount than the radical polymerization initiator such as, for example, not more than 1/2, further not more than 1/10, and particularly not more than 1/50 of the weight ratio of the water-soluble radical polymerization initiator.
  • the amount of the radical polymerization initiator is referred to a total amount thereof.
  • the mixing of the radical polymerization initiator and the water absorbent resin mentioned above may be accomplished by mixing the radical polymerization initiator with the unmodified water absorbent resin, it is preferably performed by dissolving the initiator in an aqueous solution and then mixing the resultant aqueous solution with the water absorbent resin. Since the water absorbent resin is capable of absorbing water, the radical polymerization initiator can be uniformly dispersed on the surface of the water absorbent resin and uniformly mixed with the water absorbent resin by mixing the radical polymerization initiator in an aqueous solution form.
  • the aqueous solution may contain, besides water, some other solvent in an amount which does not impair solubility of the radical polymerization initiator.
  • a radical polymerization initiator when added in a form of an aqueous solution, the amount of water in an aqueous solution used is not limited.
  • a form of mixing water into a water absorbent resin is not limited to a case where mixing is conducted in a form of an aqueous solution containing a radical polymerization initiator. After mixing a radical polymerization initiator and a water absorbent resin, water or an aqueous solution may be mixed therewith. Therefore, a hydrogel-like cross-linked product is obtained by polymerizing a monomer component, drying to give a water content of 0 to ,50% by weight, and then directly mixing with a radical polymerization initiator, to obtain a water absorbent resin composition.
  • a mixing aid may be added to the water absorbent resin composition.
  • the time of adding a mixing aid is not particularly critical, the mixing aid is preferably added at the same time as or prior to the mixing step (i).
  • the mixing aid is not particularly limited, as long as it is a water-soluble or water-dispersible compound except an ethylenically unsaturated monomer or a radical polymerization initiator, and it can repress the agglomeration of the water absorbent resin with water and improve the mixing of the aqueous solution with the water absorbent resin.
  • the mixing aid is preferably a water-soluble or water-dispersible compound.
  • surfactants, water-soluble polymers, hydrophilic organic solvents, water-soluble inorganic compounds, inorganic acids, inorganic acid salts, organic acids, and organic acid salts can be typically used.
  • water-soluble compound is referred to as a compound having solubility in 100 g of water at room temperature of not less than 1 g, preferably not less than 1O g. Since the addition of the mixing aid can repress the agglomeration of the water absorbent resin with water and induce the uniform mixing of the aqueous solution with the water absorbent resin, the active energy rays, in the subsequent step, can be radiated equally and evenly to the water absorbent resin and thus the uniform surface cross-linking of the entire water absorbent resin can be attained.
  • the form of the mixing aid is not particularly limited, and it may be used in a powdery form, or may be dissolved, dispersed, or suspended in a solution. Preferably, it is used in the form of an aqueous solution.
  • the order of the addition of the mixing aid is also not particularly limited. Any method such as a method which comprises adding a mixing aid to a water absorbent resin, and then adding and mixing water and a radical polymerization initiator (in some cases, an aqueous solution containing them) to the mixture, and a method which comprises dissolving a mixing aid in an aqueous solution, and simultaneously mixing the resultant solution with a water absorbent resin can be used.
  • surfactant to be used herein at least one kind of surfactant which is selected from the group consisting of nonionic surfactants and anionic surfactants having an HLB of not less than 7 may be adopted.
  • Typical examples of such surfactants are sorbitan aliphatic esters, polyoxyethylene sorbitan aliphatic esters, polyglycerin aliphatic esters, polyoxyethylene alkyl ethers, polyoxyethylene alkylphenol ethers, polyoxyethylene acyl esters, sucrose aliphaatic esters, higher alcohol sulfuric esters, alkyl naphthalene sulfonates, alkylpolyoxyethylene sulfate, and dialkyl sulfosuccinates.
  • polyoxyethylene alkyl ethers can be preferably used.
  • the number average molecular weight of the polyoxyethylene alkyl ether is preferably in the range of 200 to 100,000, more preferably 500 to 10,000. If the number average molecular weight is too large, the solubility in water may decrease and thus the mixing with the water absorbent resin may become inefficient because the concentration of the surfactant in the solution can not be increased. Also, the viscosity of the solution may be increased. Conversely, if the number average molecular weight is too small, the surfactant may become less effective as a mixing aid.
  • Typical examples of the water-soluble polymer are polyvinyl alcohol, polyethylne oxide, polyethylene glycol, polypropylene glycol, polyacrylamide, polyacrylic acid, sodium polyacrylate, polyethylene imine, methyl cellulose, carboxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, dextrin, sodium alginate, and starch.
  • polyethylene glycol can be preferably used.
  • the number average molecular weight of the polyethylene glycol, like polyoxyethylene alkyl ether, is preferably in the range of 200 to 100,000, more preferably 500 to 10,000.
  • hydrophilic organic solvent examples include alcohols such as methyl alcohol, ethyl alcohol, propyl alcohol, isopropyl alcohol, butyl alcohol, isobutyl alcohol, and t-butyl alcohol; ketones such as acetone and methylethyl ketone; ethers such as dioxane, alkoxy( ⁇ oly)ethylene glycol, and tetrahydrofuran; amides such as e-caprolactam and N,N-dimethyl formamide; sulfxides such as dimethyl sulfoxide; and polyhydric alcohols such as ethylene glycol, diethylene glycol, propylene glycol, methylene glycol, tetraethylene glycol, 1,3-propane diol, dipropylene glycol, 2,2,4-trimethyl-l,3-pentane diol, glycerin, 2-butene-l,4-diol, 1,3-butane diol, 1,4
  • Typical examples of the water-soluble inorganic compound are alkali metal salts such as sodium chloride, sodium hydrogen sulfate, and sodium sulfate, ammonium salts such as ammonium chloride, ammonium hydrogen sulfate, and ammonium sulfate, alkali metal hydroxides such as sodium hydroxide and potassium, hydroxide, polyvalent metal salts such as aluminium chloride, polyaluminium chloride, aluminium sulfate, potassium alum, calcium chloride, alkoxy titanium, zirconium ammonium carbonate, zirconium acetate, and non-reducible alkali metal salt pH buffer agents such as hydrogencarbonate, dihydrogen phosphate, and monohydrogen phosphate.
  • alkali metal salts such as sodium chloride, sodium hydrogen sulfate, and sodium sulfate
  • ammonium salts such as ammonium chloride, ammonium hydrogen sulfate, and ammonium sulfate
  • typical examples of the inorganic acid (salt) are hydrochloric acid, sulfuric acid, phosphoric acid, carbonic acid, and boric acid, and the salts thereof, for example, alkali metal salts thereof, and alkali earth metal salts thereof may be cited.
  • the organic acid (salt) acetic acid, propionic acid, lactic acid, citric acid, succinic acid, malic acid, and tartaric acid, and the salts thereof, for example, alkali metal salts thereof, and alkali earth metal salts thereof.
  • At least one water-soluble or water-dispersible compound selected from the group consisting of polyoxyethylene alkyl ethers, polyethylene glycol, water-soluble polyvalent metals, sodium chloride, ammonium hydrogen sulfate, ammonium sulfate, sulfuric acid, and hydrochloric acid may be preferably used as the mixing aid.
  • mixing aids can be used singly or in the mixed form of two or more members.
  • the amount of the mixing aid to be added is not particularly limited as long as it can repress the aggregation of the water absorbent resin with water, and improves the mixing of the aqueous solution with the water absorbent resin, as mentioned above.
  • the mixing aid is preferably added in an amount in the range of from 0.01 to 40 parts by weight, more preferably from 0.1 to 5 parts by weight, to 100 parts by weight of the water absorbent resin.
  • the conditions for mixing a water absorbent resin, water, and a radical polymerization initiator, and optionally a mixing aid are not critical.
  • the mixing temperature in the step (i) is preferably in the range of from 0 to 150 0 C, or from 10 to 120 0 C, or from 20 to 100 0 C, or from 30 to 90 0 C, or from 40 to 70 0 C, in this order. If the mixing temperature exceeds 150 0 C, the water absorbent resin may be degraded by heat, and the surface water content of the water absorbent resin in the step (ii) may be too low due to evaporation of water and the like.
  • a mixing/irradiation system may be preferably closed so as to repress excessive leakage of steam and to increase a surface water content of a water absorbent resin in the step (ii) to a level of not less than 3.0% by weight.
  • the temperatures of water absorbent resin and water prior to the step (i) are not also particularly limited.
  • the temperature of water absorbent resin prior to the step (i) is preferably in the range of from 0 to 150 0 C, or from 10 to 120 0 C, or from 20 to 100 0 C, or from 50 to 100 0 C, in this order. If the temperature of water absorbent resin prior to the step (i) exceeds 150 0 C, the water absorbent resin may be degraded by heat. Conversely, if the mixing temperature is less than 0 0 C, water may be condensed, thereby inhibiting a stable operation.
  • the temperature of water prior to the step (i) is preferably in the range of from 5 to 80 0 C, more preferably from 10 to 60 0 C, particularly preferably from 20 to 50 0 C.
  • the temperature of water prior to the step (i) exceeds 80 0 C, excessive amounts of water may evaporate prior to the mixing step (i) and thus a sufficient amount of water can not be mixed with a water absorbent resin resulting in a surface water content of the water absorbent resin which is too low. Conversely, if it is less than 5 0 C, water may be condensed, thereby inhibiting stable operation.
  • the mixing time in the step (i) is not also particularly limited as long as the above components can be mixed uniformly. Typically, the mixing time is preferably in the range of from 0.1 second to 60 minutes, more preferably from 1 second to 30 minutes, further more preferably from 2 seconds to 20 minutes, most preferably from 5 seconds to 10 minutes.
  • mixing time is less than the lower limit, water absorbent resin, water, and a radical polymerization initiator, and optionally a mixing aid may not be mixed uniformly. Conversely, if the mixing time exceeds the upper limit and becomes unduly long, an excess amount of water would penetrate into an inner part of the water absorbent resin, thereby unduly decreasing the water content on the surface.
  • Suitable devices for mixing a water absorbent resin, water, and a radical polymerization initiator are, for example, V-shape mixer, ribbon type mixer, screw type mixer, rotary circular plate type mixer, air-current type mixer, batch kneader, continuous kneader, paddle type mixer, or space type mixer.
  • a water absorbent resin in production of a water absorbent resin, the rate of polymerization can be increased upon exposure to active energy rays.
  • active energy rays such as ultraviolet rays, electron radiation, or ⁇ rays
  • a water-insoluble absorbent resin having internal cross-links can be prepared.
  • the formation of surface cross-links can be achieved by using a surface cross-linking agent and promoting the relevant reaction by application of heat.
  • compounds such as polyhydric alcohols, polyvalent glycidyl ethers, haloepoxy compounds, and polyvalent aldehydes which contain a plurality of functional groups in one molecular unit may be used.
  • these functional groups can react with carboxyl groups present on the surface of the water absorbent resin to give rise to a cross-linked structure on the surface of the water absorbent resin.
  • a cross-linked structure can be formed on a surface of a water absorbent resin by combining a radical polymerization initiator and exposure with active energy rays without requiring the presence of a surface cross-linking agent and a polymerizable monomer.
  • AAP absorbency against pressure
  • SFC saline flow conductivity
  • a surface water content of a water absorbent resin in the water absorbent resin composition is controlled to be above a predetermined value when irradiated with active energy rays.
  • a surface water content of the water absorbent resin in the water absorbent resin composition is controlled to be not lower than 3.0% by weight.
  • the surface water content may be controlled to a level of not lower than 3.0% by weight at any point of time in the irradiating step, and it is not necessary to control to a level of not lower than 3.0% by weight throughout the course from the beginning to the end of the irradiating step.
  • the modification for example, introduction of a cross-linking structure
  • the surface water content may be controlled to a level of not lower than 3.0% by weight at least at any point of time in the irradiating step. It is preferably controlled to a level of not lower than 3.5% by weight, and more preferably not lower than 4.0% by weight.
  • the upper limit of the surface water content is not particularly critical, and it may be appropriately selected in accordance with purposes.
  • the surface water content is typically not higher than 60.0% by weight, preferably not higher than 50.0% by weight, more preferably not higher than 40.0% by weight, and further preferably not higher than 30.0% by weight. When the surface water content is too high, water absorbent resin particles may adhere or agglomerate, and irradiation with active energy rays may not be effectively carried out.
  • the surface water content at the beginning of the irradiating step is controlled so as to be within the above-described range.
  • the surface water content may be varied. Namely, the surface water content may be increased or decreased as compared to the initial water content.
  • the surface water content should be within the above-described range.
  • the surface water content is controlled to be within the above-described range, in preferably not lower than 30%, more preferably not lower than 60%, further preferably not lower than 90%, and particularly preferably 100% (that is, the whole period), of the whole period of the irradiating step.
  • the term "surface water content” is referred to a weight percentage of a water amount existing in the vicinity of a surface of a particle based on a weight of a water absorbent resin particle. It is essentially different from a concept of a water amount or the water content in the whole particle.
  • the surface water content is measured by the method specified in the working example cited below. The measuring method is briefly explained, as follows. Water is extracted by adding a hydrophilic organic solvent to the water absorbent resin composition obtained in the step (i), a water amount in the extract is quantitatively determined by Karl Fischer method, and thus a value of the surface water content can be calculated.
  • the method of controlling a surface water content of a water absorbent resin is not especially limited.
  • a sufficient amount of water can be added into a water absorbent resin composition obtained in the step (i), or permeation of water into an inner part of a water absorbent resin particle can be promoted; or water evaporation into the atmosphere can be suppressed in the mixing step (i) and in the irradiating step (ii). Since an extent of permeation of water into an inner part of a water absorbent resin particle is influenced by time and temperature, it is preferable to control the temperature in a system during the mixing step (i).
  • a closed system to control the mixing time and the temperature in the system.
  • a closed system can be obtained by covering an opening part for irradiation with a material capable of transmitting active energy rays, such as quartz glass. Promoting permeation of water to an inner part of a water absorbent resin can be achieved by extending the mixing step (i); or by putting the water absorbent resin composition in a closed system: or by heat treating the water absorbent resin composition at a temperature of not higher than a boiling point of water.
  • promoting diffusion of water from a surface can be achieved by subjecting an air stream to a water absorbent resin composition; or by putting the water absorbent resin composition in an open system: or by heat treating the water absorbent resin composition at a temperature of not lower than a boiling point of water.
  • the water absorbent resin composition may be dried to a certain range, or a predetermined amount of water may be added to a water absorbent resin composition, depending on the monitored value.
  • penetration and diffusion of water from a surface to an inner part of the water absorbent resin may appropriately be controlled, or evaporation of water from a surface of a water absorbent resin may appropriately be controlled.
  • the irradiation with active energy rays may be conducted while water absorbent resin, water and radical polymerization initiator are mixed, or the irradiation may be conducted after mixing at least two of these.
  • ultraviolet rays As typical examples of active energy rays, ultraviolet rays, electron radiation, and ⁇ rays may be cited. These active energy rays may be used either singly or in the form of a combination of two or more members. Among these active energy rays, ultraviolet rays and electron radiation prove advantageous. In consideration of influence of active energy rays on human body, ultraviolet rays are more preferable and ultraviolet rays having a wavelength not exceeding 300 nm and particularly preferably in the range of 180 - 290 nm are particularly preferable.
  • intensity of irradiation is preferably in the range of 3 - 1 ,000 mW/cm 2
  • dose of irradiation is preferably in the range of 100 - 10,000 mJ/cm 2 .
  • Typical examples of the device for irradiation with ultraviolet rays are high-pressure mercury-vapor lamp, low-pressure mercury-vapor lamp, metal halide lamps, xenon lamp, and halogen lamps.
  • ultraviolet rays preferably ultraviolet rays of a wavelength of not more than 300 nm, are used, the use of additional different radiation types or different wavelengths is not particularly restricted.
  • voltage of acceleration is preferably in the range of 50 - 800 kV and absorbed dose is preferably in the range of 0.1 - 100 Mrad.
  • the duration of irradiating with active energy rays is preferably not less than 0.1 minute and less than 60 minutes, more preferably not less than 0.2 minute and less than 30 minutes, and more preferably not less than 1 minute and less than 15 minutes.
  • conventional surface cross-linking using a conventional surface cross-linking agent typically requires more time.
  • no application of heat is required for surface cross-linking by irradiation with active energy rays.
  • the irradiation of active energy rays possibly results in generation of radiant heat.
  • a water absorbent resin can be treated at a temperature preferably less than 150 0 C, more preferably less than 120 0 C, still more preferably in the range of room temperature to 100 0 C, and particularly preferably in the range of 50 - 100 0 C.
  • this invention allows a treating temperature below the typical temperature of conventional surface cross-linking.
  • the water absorbent resin is preferably stirred or otherwise agitated to ensure uniform irradiation with the active energy rays.
  • stirring devices are shaking mixer, shaking feeder, ribbon type mixer, conical ribbon type mixer, screw type mixing extruder, air current type mixer, batch kneader, continuous kneader, paddle type mixer, high-speed fluidifying mixer, and buoyant fluidifying mixer.
  • irradiation may originate from the surrounding of an apparatus, while the water absorbent resin composition is in an apparatus having a form of a box or a cylinder.
  • a pressure of gas such as air or the like may be utilized, as is used in flowing a powder with air.
  • air it is preferable to humidify the air to prevent the water absorbent resin composition from drying.
  • uniform surface treatment can be conducted in a short period.
  • the material of which the above-described apparatus is made is not particularly critical, as long as it does not obstruct irradiation with active energy rays onto the water absorbent resin composition.
  • quartz glass would be a suitable material.
  • the water absorbent resin may optionally be subjected to heat treatment at a temperature in the range of 50 - 25O 0 C for drying.
  • a water absorbent resin may be further surface cross-linked by using a conventional surface cross-linking agent such as polyhydric alcohols, polyvalent epoxy compounds, and alkylene carbonates.
  • a water absorbent resin may be added with an agent for enhancing liquid-permeability before, after or during irradiation with active energy rays.
  • an agent for enhancing liquid-permeability is minerals such as talc, kaolin, fuller's earth, bentonite, activated clay, barite, natural asphaltum, strontium ore, ilmenite, and pearlite; aluminum compounds such as aluminum sulfates 14 - 18 hydrates (or anhydrides), potassium aluminum sulfates 12 hydrate, sodium aluminum sulfate 12 hydrate, aluminum chloride, aluminum polychloride, and aluminum oxide, and aqueous solutions thereof; other polyvalent metal salts; hydrophilic amorphous silica (such as, for example, a product by dry method made by Tokuyama K.K.
  • oxide composites such as silicon oxide-aluminum oxide-magnesium oxide composite (such as, for example, a product made by ENGELHARD Corp. and sold under the trademark designation of "Attagel #50"), silicon oxide-aluminum oxide composite, and silicon oxide-magnesium oxide composite.
  • the amount of such a liquid-permeability enhancing agent would preferably be in the range of from 0 to 20 parts by weight, more preferably from 0.01 to 10 parts by weight, and particularly preferably from 0.1 to 5 parts by weight with 100 parts by weight of a water absorbent resin which has been modified.
  • the liquid-permeability enhancing agent can be added in the form of an aqueous solution if it is water-soluble or in the form of powder or slurry when it is water-insoluble.
  • the liquid-permeability enhancing agent may also be added in a mixed form with a radical polymerization initiator.
  • Other additives such as antibacterial agent, deodorant, and chelating agent may aditionally be used in an amount in the range as mentioned above for the liquid-permeability enhancing agent.
  • the produced water absorbent resin has improved absorbency against pressure. It has been hitherto known that the formation of surface cross-linking results in slightly lowering the free swelling capacity while increasing the ability to retain absorbed liquid even under pressed state, namely absorbency against pressure (AAP).
  • AAP absorbency against pressure
  • the absorbency against pressure of 4.83 kPa of the water absorbent resin can be improved by not less than 1 g/g comparing with the absorption against pressure of the resin prior to the modification. It is believed that an increase in AAP indicates that surface cross-linking has taken place.
  • the increase in the absorbency against pressure after the modification is preferably not less than 8 g/g, more preferably not less than 12 g/g, still more preferably not less than 15 g/g, and particularly preferably not less than 20 g/g, most preferably not less than 22 g/g.
  • the modified water absorbent resin of this invention may exhibit absorbency against pressure of 4.83 kPa in the range of 8 - 40 g/g.
  • the centrifuge retention capacity (CRC) of the modified water absorbent resin is preferably not more than 50 g/g, more preferably not more than 40 g/g, still more preferably not more than 35 g/g. Although the lower limit thereof is not particularly limited, it is preferably not less than 10 g/g, more preferably not less than 20 g/g, still more preferably not less than 25 g/g. If the centrifuge retention capacity (CRC) exceeds 50 g/g, gel strength might be decreased, decreasing absorbency against pressure. On the hand, if the centrifuge retention capacity (CRC) is less than 10 g/g, sufficient water absorption capacity may not be obtained.
  • the modified water absorbent resin which is obtained by this invention has a saline flow conductivity(SFC) preferably .of not less than 10 (x 10 "7 > cm ⁇ s-g '1 ), more preferably not less than 30 (x 10 "7 *cm 3 "s- g " '), and still more preferably not less than 50 (x 10 "7 -cm 3 -s-g " '), particularly preferably not less than 70 (x 10 "7 'cm 3 *s t g "1 ), most preferably not less than 100 (x 10 '7 -cm 3 *s-g '1 ).
  • SFC saline flow conductivity
  • the modified water absorbent resin which is obtained by this invention has low residual monomer content. It is believed that this is due to a reaction between the remaining monomers in the water absorbent resin with the initiator radicals formed by irradiation on a radical polymerization initiator with active energy rays. Since the water absorbent resin is used in hygienic materials such as disposable diaper, the residual monomer content is preferably as small as possible in terms of odor and safety. While a residual monomer content of water absorbent resin as a base polymer is generally in the range of 200 to 500 ppm, the residual monomer content of the water absorbent resin surface-treated by this invention is typically not more than 200 ppm (the lower limit is 0 ppm). The residual monomer content of the modified water absorbent resin is preferably not more than 200 ppm, more preferably not more than 150 ppm, particularly not more than 100 ppm (the lower limit is 0 ppm).
  • the modified water absorbent resin which is obtained by this invention has a smaller solid content as compared with a modified water absorbent resin obtained by conventional surface cross-linking. This is because according to the method of this invention, the reaction does not require an elevated temperature and thus the water contained in the aqueous solution which is added to a water absorbent resin does not evaporate or only to a small degree Due to the large water content of the water absorbent resin, there is only a small amount of fine powder having a particle size of not more than 150 ⁇ m. Such particles are not desirable in terms of health. Also, the generation of static electricity on particle surface which causes blocking during the pneumatic conveying can be prevented, and the degradation of physical properties by physical damage during the pneumatic conveying can be ⁇ epressed.
  • the solid content of the modified water absorbent resin is preferably not more than 95%, more preferably not more than 93%, particularly not more than 91%. Although the lower limit is not critical, a solid content of not more than 70% may lead to decreased absorbency per weight of the water absorbent resin.
  • the properties of the surface-treated water absorbent resin which is obtained by this invention can be further adjusted by treatment conditions such as by selecting a suitable unmodified water absorbent resin and agglomeration and molding processes of a water absorbent resin after surface cross-linking.
  • the modified water absorbent resin is in a powdery form.
  • This powder has a weight average particle diameter (specified by classification with sieves) in the range of from 10 to 1 ,000 ⁇ m, and preferably from 200 to 600 ⁇ m.
  • the content of particles having diameters of from 150 to 850 ⁇ m is preferably in the range of from 90 to 100 % by weight, and more preferably from 95 to 100 % by weight, based on the weight of the water absorbent resin.
  • the method of this invention effects an agglomerating a fine powder generated in the production of a water absorbent resin during the course of surface cross-linking of the water absorbent resin. Accordingly, even if the water absorbent resin prior to the modification happens to contain a fine powder, the method for producing a modified water absorbent resin of this invention permits the agglomeration of the contained fine powder, which can lead to an decreased amount of fine powder in the resultant modified water absorbent resin. Thus, the particle size distribution of the produced modified water absorbent resin is shifted toward a larger particle size as compared with the water absorbent resin prior to the modification.
  • the degree of the shift may vary and depends, for example, on the amount of a radical polymerization initiator mixed with the water absorbent resin, on the water content, on the conditions of irradiation with active energy rays, and on the flowing process during the irradiation.
  • the modified water absorbent resin which is obtained by the method of this invention has surface cross-links formed uniformly and with a high cross-link density throughout the entire surface of the water absorbent resin. Thereby good characteristics, such as absorption capacity, absorption speed, gel strength, and suction power which a water absorbent resin can be obtained.
  • speed and extent of the surface cross-linking have been found to depend on the ratio of neutralization, when an acrylic acid type water absorbent resin is subjected to surface cross-linking by using such a surface cross-linking agent as polyhydric alcohol, polyvalent epoxy compound, or alkylene carbonate. Specifically, the surface cross-linking proceeds fast when the ratio of neutralization is low, while surface cross-linking proceeds with difficulties when the ratio of neutralization is high.
  • surface cross-linking of the water absorbent resin can be done independently from the ratio of neutralization of a water absorbent resin and independently from uniformity of post-neutralization. It is believed that since surface cross-linking depends on the action of a radical polymerization initiator on a main chain of the water absorbent resin, surface cross-linking can proceed regardless of whether a carboxyl group is present in the form of an acid or a salt.
  • the surface treatment of the water absorbent resin can be carried out fully satisfactorily even at reaction temperatures near room temperature, and the surface-treated water absorbent resin consequently obtained has good characteristics, such as absorption capacity, absorption speed, gel strength, and suction power which the water absorbent resin. Accordingly, the water absorbent resin which is obtained by this invention is optimally suitable for use in absorbent members, such as disposable diapers, training pants, sanitary napkins and other sanitary materials for absorbing body fluid.
  • absorbent members such as disposable diapers, training pants, sanitary napkins and other sanitary materials for absorbing body fluid.
  • absorbent articles refers to devices that absorb and contain liquid, and more specifically, refers to devices that are placed against or in proximity to the body of the wearer to absorb and contain the various exudates discharged from the body.
  • Absorbent articles include but are not limited to diapers, adult incontinent briefs, diaper holders and liners, sanitary napkins and the like.
  • Preferred absorbent articles of the present invention are diapers and training pants.
  • “diaper” and “training pants” refers to an absorbent article generally worn by infants and incontinent persons about the lower torso.
  • Absorbent articles especially suitable for the present invention typically comprise an outer covering including a liquid pervious topsheet, a liquid impervious backsheet and an absorbent core generally disposed between the topsheet and the backsheet.
  • the absorbent core may comprise any absorbent material that is generally compressible, conformable, non-irritating to the wearer's skin, and capable of absorbing and retaining liquids such as urine and other certain body exudates.
  • the absorbent core may comprise a wide variety of liquid-absorbent materials commonly used in disposable diapers and other absorbent articles such as comminuted wood pulp, which is generally referred to as air felt.
  • Particle size distribution weight average particle diameter ( ⁇ 50) and logarithmic standard deviation ( ⁇ )
  • a water absorbent resin or particulate absorbent of 10 g is passed through JIS standard sieves having mesh sizes of 850 ⁇ m, 710 ⁇ m, 600 ⁇ m, 500 ⁇ m, 425 ⁇ m, 300 ⁇ m, 212 ⁇ m, 150 ⁇ ra, 106 ⁇ m, and 45 ⁇ m (THE HDA TESTING SIEVE, made by Iida Seisakusho K.K., 8 cm in diameter), at room temperature (20 to 25 0 C) and at humidity of 50 RH%, and then classified by using a sieve shaker (IIDA SIEVE SHAKER, TYPE: ES-65type, SER.No.0501, made by Iida Seisakusho K.K.) for 5 minutes.
  • the particle diameters with R being 84.1% by weight and 15.9% by weight are referred to as Xl and X2, respectively.
  • the logarithmic standard deviation ( ⁇ ) is represented by the following formula. Specifically, it means that the smaller the value ⁇ is, the narrower the particle size distribution is.
  • a water absorbent resin as a base polymer 500 g are added to 5 liters of Loedige mixer (made by Loedige Co.,Ltd., Type: M5R), and a treating solution obtained prior to mixing 5.0 g of ammonium persulfate, 2.5 g of a monomethyl ether of a polyethylene glycol (a number average molecular weight of about 2,000) and 40 g of water, are sprayed thereto under stirring at 300 rpm. After being mixed by stirring for 3 min at room temperature, the stirring is terminated. The resultant mixture of 1 g is added to a screw tube, and 4 g of methanol anhydride is added.
  • the mixture is shaken for 30 seconds with a mini-shaker MS 1 made by IKA K.K., and thereafter it is absorbed with a syringe, then is filtrated with a filter (made by Zeal Science Co., Ltd.; Water type 25 A (a pore diameter of 0.45 ⁇ m)).
  • a filter made by Zeal Science Co., Ltd.; Water type 25 A (a pore diameter of 0.45 ⁇ m)
  • the amount of water contained in a filtrate is measured by a method below with a Karl Fischer moisture meter (made by Kyoto Electronics Manufacturing Co.,Ltd.; Type: MKS-IS). Measurement of amount of water with a Karl Fischer moisture meter
  • Polarization is conducted by making slight constant electric current between two platinum electrodes immersed in a solution, and an end point of titration is determined by a Dead Stop method wherein a potential change caused by excessive iodine at an end point is detected.
  • a sample is put in a flask for titration, titrated with a Karl Fischer reagent, and an amount of water in the sample is determined as a product of a titration amount of a Karl Fischer reagent and a titer.
  • W is an amount of water (mg) in a sample
  • K is a titration amount of a Karl Fischer r,eagent (mL).
  • F is a titer of a Karl Fischer reagent (mg/mL).
  • a solvent for measurement a mixed product of 50 mL of an acetic acid (special grade), 50 mL of Buffer solution (HYDRNAL-Buffer), and 900 mL of methanol anhydride
  • a Karl Fischer reagent by pushing a "START" key, to make an inner part of a flask for titration in an anhydrous state.
  • a sample is put into a flask for titration, titration is conducted with a Karl Fischer reagent by pushing a "START" key.
  • a weight of the sample (a) [mg] and an amount of Karl Fischer titration (b) [mL] are recorded. Measuring was conducted by three times in all, and an average value is calculated.
  • the total (d) [wt %] water concentration contained in methanol anhydride is measured.
  • the water concentration derived from water contained in the water absorbent resin before addition of the treating agent is subtracted from the water concentration (c) in methanol anhydride which is used in extraction of water from the mixture containing the water absorbent resin mixture as calculated in the above described equation (1).
  • concentration (g) [mg] which is extracted from the water absorbent resin mixture is calculated by using the concentration (e) and an amount of methanol anhydride (f) [mg] to be used in extraction of water from the water absorbent resin mixture, in accordance with the following equation (3).
  • the amount of water (h) [mg] derived from the treating solution, which is contained in a water absorbent resin mixture (a) can be calculated by using the following equation (4), based on the weight (i) [mg] of the treating solution added per 1,000 mg of the water absorbent resin and the weight of water (j) [mg] contained in the treating solution.
  • the ratio of water (g) extracted from the water absorbent resin to water (h) derived from the treating solution, which is contained in a water absorbent resin mixture (a), is calculated from the following equation (5), which is made as an extraction ratio (k) [wt %].
  • CRC indicates absorbency in an aqueous 0.90 wt.% sodium chloride solution (hereinafter also called simply as "physiological saline”) without load for 30 min.
  • a water absorbent resin 0.200 g is uniformly put in a pouch (85 mm x 60 mm) made of an non-woven fabric (made by Nangoku Pulp Kogyo K.K., Product Name; Heatlon Paper, Model GSP-22), and heat-sealed. Then, the pouch is immersed at room temperature in large excess (about 500 mL) of physiological saline. After 30 min, the pouch is pulled out, and water is removed with a centrifuge (made by Kokusan Co.,Ltd., Type: H-122) by centrifugal force (250G) as described in "Edana ABSORBENCY II 441.1-99" for 3 min.
  • a centrifuge made by Kokusan Co.,Ltd., Type: H-122
  • the weight of the pouch is measured, which is referred to as Wl (g). Further, the same is done without using the water absorbent resin, to measure the weight, which is referred to as WO (g). From these values, Wl and WO, the CRC (g/g) is calculated according to the equation below.
  • 400-mesh wire gauze of stainless steel (38 ⁇ m in mesh size) is welded to a bottom of a plastic supporting cylinder having an inner diameter of 60 mm.
  • 0.900 g of a given water absorbent resin is uniformly scattered on the wire gauze.
  • a piston and a load, each of which is adjusted to exert a load of 4.83 kPa uniformly on the water absorbent resin has an outer diameter slightly smaller than 60 mm but produces no gap relative to the inner wall surface of the supporting cylinder, and does not have its unobstructed vertical motion prevented, were mounted thereon sequentially in the order mentioned, and the whole weight W a (g) of the resultant measuring device is determined.
  • a glass filter 90 mm in diameter (pore diameter: 100 to 120 ⁇ m: made by Sogo Rikagaku Glass Manufactory K.K.) is placed inside a petri dish 150 mm in diameter.
  • An aqueous 0.9 wt.% sodium chloride solution (physiological saline) (20 - 25°C) is added to the petri dish so as to give the same level as the upper surface of the glass filter.
  • One filter paper 90 mm in diameter (0.26 mm in thickness and 5 ⁇ m in retained particle diameter; made by Advantec Toyo K.K. and sold under the product name of "JIS P 3801, No. 2" is mounted on the surface of physiological saline so as to have the surface thereof thoroughly wetted and the excess solution is removed.
  • the resultant measuring device is wholly mounted on the wetted filter paper and the water absorbent resin is allowed to absorb the solution under load for a prescribed time of one hour.
  • the whole measuring device is lifted after the one hour's standing, and the weight thereof W b (g) is determined. This determination of the weight must be performed as quickly as possible without exposing the device to any vibration.
  • the absorbency against pressure (AAP) (g/g) is calculated in accordance with the following formula using W 3 and W b .
  • SFC is a value which indicates the degree of liquid permeability exhibited by water absorbent resin particles in a swollen state. A larger SFC value indicates higher liquid permeability.
  • the SFC is determined in accordance with the test for the saline flow conductivity (SFC) described in JP-T-9 (1997)-509591 with necessary modification. Specifically, by the use of a device illustrated in Fig. 1, SFC is determined.
  • a tank 31 has a glass tube 32 inserted therein and the lower end of the glass tube 32 is disposed so that an aqueous 0.69 wt. % sodium chloride solution 33 can be maintained to a height of 5 cm from the bottom of the swelled gel 44 held in a cell 41.
  • the aqueous 0.69 wt. % sodium chloride solution in the tank 31 is supplied to the cell 41 via an L-letter tube 34 fitted with a cock.
  • the cell 41 has an inside diameter of 6 cm.
  • a wire gauze (opening of sieve: 38 ⁇ m) 42 of stainless steel of No. 400 is disposed on the bottom surface in the lower part of the cell.
  • a piston 46 is provided in the lower part thereof with holes 47 sufficient for passing a liquid, and fitted in the bottom part thereof with a glass filter 45 having good permeability so as to prevent the water absorbent resin or the swelled gel thereof from entering the hole 47.
  • the cell 41 is laid on a stand for mounting the cell. The surface of the stand contacting the cell is placed on a wire gauze 43 of stainless steel incapable of obstructing the passage of liquid.
  • Artificial urine is prepared by mixing 0.25 g of calcium chloride dihydrate, 2.0 g of potassium chloride, 0.50 g of magnesium chloride hexahydrate, 2.0 g of sodium sulfate, 0.85 g of ammonium dihydrogen phosphate, 0.15 g of diammonium hydrogen phosphate, and 994.25 g of purified water together.
  • Water absorbent resin (0.900 g) is uniformly placed in a container 40 and left swelling with an artificial urine under a pressure of 0.3 psi (2.07 kPa) for 60 minutes, and a height of a gel layer of gel 44 is recorded. Subsequently, under a pressure of 0.3 psi (2.07 kPa), an aqueous 0.69 wt. % sodium chloride solution 33 from a tank 31 is passed under a stated hydrostatic pressure through the swelled gel layer. By means of a computer and a balance, the amounts of liquid passing through the gel layer at intervals of 20 seconds are recorded as a function of time over 10 minutes.
  • a flow speed Fs (t) through the swelled gel 44 (mainly between adjacent particles) is determined in unit of [g/s] by dividing an increased weight (g) by an increased time (second).
  • the time in which the constant hydrostatic pressure and the stable flow speed are attained is denoted as Ts.
  • the data obtained for 10 minutes and Ts are exclusively used for the calculation of flow speed.
  • Fs (t) stands for a flow speed expressed in units of [g/s]
  • LO stands for a height of a gel layer expressed in units of cm
  • p stands for a density of an aqueous 0.69 wt. % sodium chloride solution (1.003 g/cm 3 ),
  • A stands for an upper side area of a gel layer in a cell 41 (28.27 cm 2 ),
  • ⁇ P stands for a hydrostatic pressure exerted on a gel layer (4920 dynes/cm ),
  • a unit of SFC is (10 "7 - cm 3 - s- g '1 ).
  • the pulverized hydrogel-like cross-linked polymers are scattered on a wire mesh of 50 mesh (opening of sieve : 300 ⁇ m), and are dried in hot air at 175°C for 50 minutes.
  • a wire mesh of 50 mesh opening of sieve : 300 ⁇ m
  • the resultant powdery agglomerates are pulverized with a roll mill, and are further classified with a JIS standard sieve having an opening of sieve of 710 ⁇ m.
  • particles which passed through a sieve having an opening of sieve of 710 ⁇ m in the above-described operation are classified with a JIS standard sieve having a opening of sieve of 150 ⁇ m, to remove particles which pass through a sieve having a opening of sieve of 150 ⁇ m.
  • water absorbent resin (A) is obtained.
  • the pulverized hydrogel-like cross-linked polymers are scattered on a wire mesh of 50 mesh (opening of sieve : 300 ⁇ m), and are dried in hot air at 175°C for 50 minutes.
  • a wire mesh of 50 mesh opening of sieve : 300 ⁇ m
  • the resultant powdery agglomerates are pulverized with a roll mill, and are further classified with a JIS standard sieve having an opening of sieve of 710 ⁇ m.
  • particles which passed through a sieve having an opening of sieve of 710 ⁇ m in the above-described operation are classified with a JIS standard sieve having a opening of sieve of 150 ⁇ m, to remove particles which pass through a sieve having a opening of sieve of 150 ⁇ m.
  • water absorbent resin (B) is obtained.
  • the particle distribution of the resultant water absorbent resin (B) is shown in Table 1 below, and various properties thereof are shown in Table 2 below.
  • Table 1 "not less than 850 ⁇ m” is referred to as the ratio (% by weight) of the water absorbent resin which remain on the sieve having a mesh size of 850 ⁇ m following the classification process.
  • “not more than 45 ⁇ m” is referred to as the ratio (% by weight) of the water absorbent resin which pass through a sieve having a mesh size of 45 ⁇ m following the classification process.
  • x to y is referred to as the ratio (% by weight) of the water absorbent resin which passes through a sieve having a mesh size of x ⁇ m and also remains on a sieve having a mesh size of y ⁇ m following the classification process.
  • a radiation device able to emit ultraviolet rays (made by Ushio Denki K.K., UV-152/IMNSC3-AA06) furnished with a metal halide lamp of 1 kW (made by the same company, UVL-1500M2-N1) is set at a distance of 8 cm between a center of the lamp and a quartz plate. Then, the water absorbent resin composition (1) is irradiated with ultraviolet rays at room temperature for 15 minutes, to obtain the modified water absorbent resin (1).
  • modified water absorbent resin (1) is tested for various properties, and the results are shown in Table 2 below.
  • Table 2 "CRC after correction with total water content” and “AAP after correction with total water content” are calculated by the following formulas.
  • CRC before correction with total water content is referred to as a centrifuge retention capacity (CRC) of water absorbent resin prior to determination of total water content by the formula (5)
  • AAP before correction with total water content is referred to as an absorbency against pressure (AAP) of water absorbent resin prior to determination of total water content by the formula (5).
  • Example 2 The same procedure as described Example 1 is repeated except that the water amount in the treating solution is changed to 160 g, to obtain water absorbent resin composition (2) having a surface water content of 12.5 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition (2) is irradiated with ultraviolet rays for 15 minutes, to obtain modified water absorbent resin (2).
  • modified water absorbent resin (2) is tested for various properties, and the results are shown in Table 2 below.
  • Example 2 The same procedure as described Example 1 is repeated except that the water amount in the treating solution is changed to 200 g, to obtain a water absorbent resin composition (3) having a surface water content of 15.5 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition (3) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin (3). The thus obtained modified water absorbent resin (3) is tested for various properties, and the results are shown in Table 2 below.
  • a water absorbent resin composition (4) having a surface water content of 12.5 % by weight is obtained by repeating the same procedure as described Example 2. Further, by the same procedure as described Example 1 , the water absorbent resin composition (4) is irradiated with ultraviolet rays for 1 minute, to obtain the modified water absorbent resin (4).
  • Example 2 The same procedure as described Example 1 is repeated except that the water absorbent resin (B) is used as a base polymer instead, to obtain a water absorbent resin composition (5) having a surface water content of 6.5 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition (5) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin (5).
  • Example 2 The same procedure as described Example 2 is repeated except that the water absorbent resin (B) is used as a base polymer instead, to obtain a water absorbent resin composition (6) having a surface water content of 6.7 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition (6) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin (6).
  • Example 3 The same procedure as described Example 3 is repeated except that the water absorbent resin (B) is used as a base polymer instead, to obtain the water absorbent resin composition (7) having a surface water content of 9.6 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition (7) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin (7).
  • Example 1 The same procedure as described Example 1 is repeated except that the water amount in the treating solution is changed to 20 g, to obtain a water absorbent resin composition for comparison (1) having a surface water content of 1.9 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition for comparison (1) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin for comparison (1).
  • Example 2 The same procedure as described Example 1 is repeated except that the water amount in the treating solution is changed to 40 g, to obtain the water absorbent resin composition for comparison (2) having a surface water content of 4.5 % by weight. Further, by the same procedure as described Example 1 , the water absorbent resin composition for comparison (2) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin for comparison (2).
  • Example 2 The same procedure as described Example 1 is repeated except that the water amount in the treating solution is changed to 80 g, to obtain the water absorbent resin composition for comparison (3) having a surface water content of 7.9 % by weight. Further, by the same procedure as described Example 1 , the water absorbent resin composition for comparison (3) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin for comparison (3). The thus obtained modified water absorbent resin for comparison (3) is tested for various properties, and the results are shown in Table 2 below.
  • a water absorbent resin composition for comparison (4) having a surface water content of 4.5 % by weight is obtained by repeating the same procedure as described Control 2. Further, by the same procedure as described Example 4, the water absorbent resin composition for comparison (4) is irradiated with ultraviolet rays for 1 minute, to obtain the modified water absorbent resin for comparison (4).
  • the same procedure as described Control 1 is repeated except that the water absorbent resin (B) is used as a base polymer instead, to obtain the water absorbent resin composition for comparison (5) having a surface water content of 1.1 % by weight. Further, by the same procedure as described Example 1, the water absorbent resin composition for comparison (5) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin for comparison (5).
  • the same procedure as described Control 3 is repeated except that the water absorbent resin (B) is used as a base polymer instead, to obtain the water absorbent resin composition for comparison (6) having a surface water content of 5.2 % by weight. Further, by the same procedure as described Example 1 , the water absorbent resin composition for comparison (6) is irradiated with ultraviolet rays for 15 minutes, to obtain the modified water absorbent resin for comparison (6).
  • WAR Water absorbent resin
  • WAR for com. Water absorbent resin for comparison
  • PEG-OMe Polyethylene glycol monomethyl ether (a number average molecular weight of about 2,000)
  • Example 4 by irradiating water absorbent resin with active energy rays while controlling the surface water content of the water absorbent resin to a level of not less than a prescribed value by adding relatively large amount of water thereto, the modification of surface of water absorbent resin particles can be efficiently carried out even in a short time and a water absorbent resin having excellent water absorbent properties can be produced.
PCT/US2007/008475 2006-04-10 2007-04-04 An absorbent member comprising a modified water absorbent resin WO2007120561A2 (en)

Priority Applications (4)

Application Number Priority Date Filing Date Title
JP2009504294A JP4928602B2 (ja) 2006-04-10 2007-04-04 改質された吸収性樹脂を備える吸収性部材
CA002649299A CA2649299A1 (en) 2006-04-10 2007-04-04 An absorbent member comprising a modified water absorbent resin
EP07754914A EP2004732A2 (en) 2006-04-10 2007-04-04 An absorbent member comprising a modified water absorbent resin
MX2008013041A MX2008013041A (es) 2006-04-10 2007-04-04 Un miembro absorbente que comprende una resina absorbente de agua modificada.

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2006-108083 2006-04-10
JP2006108083A JP2007277466A (ja) 2006-04-10 2006-04-10 改質された吸水性樹脂の製法
JP2006-157582 2006-06-06
JP2006157582A JP2007326912A (ja) 2006-06-06 2006-06-06 改質された吸水性樹脂の製法

Publications (2)

Publication Number Publication Date
WO2007120561A2 true WO2007120561A2 (en) 2007-10-25
WO2007120561A3 WO2007120561A3 (en) 2008-01-03

Family

ID=38515743

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/008475 WO2007120561A2 (en) 2006-04-10 2007-04-04 An absorbent member comprising a modified water absorbent resin

Country Status (6)

Country Link
US (2) US7745507B2 (US07875362-20110125-C00021.png)
EP (1) EP2004732A2 (US07875362-20110125-C00021.png)
JP (1) JP4928602B2 (US07875362-20110125-C00021.png)
CA (1) CA2649299A1 (US07875362-20110125-C00021.png)
MX (1) MX2008013041A (US07875362-20110125-C00021.png)
WO (1) WO2007120561A2 (US07875362-20110125-C00021.png)

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4564284B2 (ja) * 2003-06-03 2010-10-20 株式会社日本触媒 吸水材の製造方法
US8080705B2 (en) 2004-07-28 2011-12-20 The Procter & Gamble Company Superabsorbent polymers comprising direct covalent bonds between polymer chain segments and method of making them
EP1669394A1 (en) 2004-12-10 2006-06-14 The Procter & Gamble Company Superabsorbent polymer particles with improved surface cross-linking and hydrophilicity and method of making them
WO2007120561A2 (en) 2006-04-10 2007-10-25 The Procter & Gamble Company An absorbent member comprising a modified water absorbent resin
EP2121049B1 (en) 2007-02-22 2016-03-30 The Procter and Gamble Company Method of surface treating particulate material using electromagnetic radiation
US8912298B2 (en) * 2008-03-31 2014-12-16 Nippon Shokubai Co., Ltd. Method for producing particulate water absorbing agent containing water absorbent resin as main component
US8562862B2 (en) * 2008-09-12 2013-10-22 Basf Se Water absorbing material
EP2163266A1 (en) 2008-09-12 2010-03-17 The Procter & Gamble Absorbent article comprising water-absorbing material
US20110319849A1 (en) * 2011-07-01 2011-12-29 Dimitris Ioannis Collias Absorbent article comprising a synthetic polymer derived from a renewable resource and methods of producing said article
DE102011086522A1 (de) 2011-11-17 2013-05-23 Evonik Degussa Gmbh Superabsorbierende Polymere für hochgefüllte oder faserfreie Hygieneartikel
DE102013003755A1 (de) * 2013-03-06 2014-09-11 Carl Freudenberg Kg Belüftungseinsatz
KR102468196B1 (ko) * 2018-11-26 2022-11-17 주식회사 엘지화학 고흡수성 수지 및 그 제조 방법
CN113544162A (zh) * 2019-03-08 2021-10-22 住友精化株式会社 吸收体、吸收性物品及渗透速度的调节方法
WO2021080575A1 (en) * 2019-10-23 2021-04-29 Kimberly-Clark Worldwide, Inc. Superabsorbent material absorbent capacity increase with use of selected salts
CN110975818B (zh) * 2019-12-04 2023-02-24 中国非金属矿工业有限公司 一种膨润土复合高吸水垫料及其制备方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4666983A (en) 1982-04-19 1987-05-19 Nippon Shokubai Kagaku Kogyo Co., Ltd. Absorbent article
US4783510A (en) 1986-06-04 1988-11-08 Taiyo Fishery Co., Ltd. Process for improving a water absorbent polyacrylic acid polymer and an improved polymer produced by said process
US4910250A (en) 1985-06-22 1990-03-20 Hayashikane Shipbuilding & Engineering Co., Ltd. Aqueous composition, method of producing a water absorbent polymer
US5422405A (en) 1992-12-16 1995-06-06 Nippon Shokubai Co., Ltd. Method for production of absorbent resin
JP2004099789A (ja) 2002-09-11 2004-04-02 L'oreal Sa 合成高分子ゲルの製造方法
WO2004031253A1 (en) 2002-10-02 2004-04-15 Coloplast A/S A hydrogel

Family Cites Families (155)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL290654A (US07875362-20110125-C00021.png) 1962-03-27 1900-01-01
US3429852A (en) * 1967-03-30 1969-02-25 Nat Starch Chem Corp Ethylenically unsaturated derivatives of benzophenone and crosslinkable polymers thereof
US3661875A (en) * 1970-01-27 1972-05-09 Du Pont 1-(1-alkenyl)bicyclo(1.1.0)butanes and their polymers
US3622848A (en) 1970-03-19 1971-11-23 Du Pont Capacitor with photocrosslinked dielectric
US3959569A (en) * 1970-07-27 1976-05-25 The Dow Chemical Company Preparation of water-absorbent articles
US4304895A (en) 1973-06-20 1981-12-08 Wesley-Jessen, Inc. Ultraviolet absorbing corneal contact lenses
US3860003B2 (en) * 1973-11-21 1990-06-19 Contractable side portions for disposable diaper
US3935099A (en) * 1974-04-03 1976-01-27 The United States Of America As Represented By The Secretary Of Agriculture Method of reducing water content of emulsions, suspensions, and dispersions with highly absorbent starch-containing polymeric compositions
JPS51125468A (en) * 1975-03-27 1976-11-01 Sanyo Chem Ind Ltd Method of preparing resins of high water absorbency
JPS5265597A (en) 1975-11-27 1977-05-31 Sumitomo Chem Co Ltd Preparation of high polimeric materials with improved water absorption
JPS5346389A (en) * 1976-10-07 1978-04-25 Kao Corp Preparation of self-crosslinking polymer of acrylic alkali metal salt
US4043887A (en) * 1977-01-17 1977-08-23 Eastman Kodak Company Benzophenone initiators for the photopolymerization of unsaturated compounds
US4062817A (en) 1977-04-04 1977-12-13 The B.F. Goodrich Company Water absorbent polymers comprising unsaturated carboxylic acid, acrylic ester containing alkyl group 10-30 carbon atoms, and another acrylic ester containing alkyl group 2-8 carbon atoms
US4286082A (en) * 1979-04-06 1981-08-25 Nippon Shokubai Kagaku Kogyo & Co., Ltd. Absorbent resin composition and process for producing same
US4325001A (en) * 1980-03-07 1982-04-13 The United States Of America As Represented By The Administrator Of The National Aeronautics And Space Administration Inorganic spark chamber frame and method of making the same
JPH0367712B2 (US07875362-20110125-C00021.png) 1980-05-12 1991-10-23 Johnson & Johnson Prod Inc
JPS6056724B2 (ja) * 1980-10-22 1985-12-11 株式会社クラレ 吸水性樹脂の製造方法
GB2088392B (en) * 1980-12-03 1984-05-02 Sumitomo Chemical Co Production of hydrogels
JPS57158209A (en) * 1981-03-25 1982-09-30 Kao Corp Production of bead-form highly water-absorbing polymer
US4985518A (en) * 1981-10-26 1991-01-15 American Colloid Company Process for preparing water-absorbing resins
US4610678A (en) * 1983-06-24 1986-09-09 Weisman Paul T High-density absorbent structures
US4514345A (en) * 1983-08-23 1985-04-30 The Procter & Gamble Company Method of making a foraminous member
US4734478A (en) * 1984-07-02 1988-03-29 Nippon Shokubai Kagaku Kogyo Co., Ltd. Water absorbing agent
US4625001A (en) 1984-09-25 1986-11-25 Nippon Shokubai Kagaku Kogyo Co., Ltd. Method for continuous production of cross-linked polymer
JPS6187702A (ja) * 1984-10-05 1986-05-06 Seitetsu Kagaku Co Ltd 吸水性樹脂の製造方法
US4748076A (en) * 1985-02-16 1988-05-31 Hayashikane Shipbuilding & Engineering Co., Ltd. Water absorbent fibrous product and a method of producing the same
JPS61275355A (ja) * 1985-05-29 1986-12-05 Kao Corp 吸収性物品
US4654039A (en) * 1985-06-18 1987-03-31 The Proctor & Gamble Company Hydrogel-forming polymer compositions for use in absorbent structures
US4690996A (en) * 1985-08-28 1987-09-01 National Starch And Chemical Corporation Inverse emulsions
DE3650265T2 (de) * 1985-09-13 1995-07-27 American Cyanamid Co Makrolide Antibiotika und Verfahren zu deren Herstellung.
DE3534645A1 (de) * 1985-09-28 1987-04-02 Merck Patent Gmbh Copolymerisierbare fotoinitiatoren
DE3537276A1 (de) * 1985-10-19 1987-04-23 Basf Ag Verfahren zur kontinuierlichen herstellung von vernetzten feinteiligen gelfoermigen polymerisaten
DE3609545A1 (de) 1986-03-21 1987-09-24 Basf Ag Verfahren zur diskontinuierlichen herstellung von vernetzten, feinteiligen polymerisaten
US4847137A (en) * 1986-05-19 1989-07-11 Minnesota Mining And Manufacturing Company Pressure-sensitive adhesive crosslinked by copolymerizable aromatic ketone monomers
US4737559A (en) 1986-05-19 1988-04-12 Minnesota Mining And Manufacturing Co. Pressure-sensitive adhesive crosslinked by copolymerizable aromatic ketone monomers
JPH078883B2 (ja) * 1986-06-04 1995-02-01 大洋漁業株式会社 改質吸水性樹脂の製造方法
JPH0647626B2 (ja) * 1986-07-01 1994-06-22 三菱油化株式会社 吸水性複合材料の製造法
US4834735A (en) * 1986-07-18 1989-05-30 The Proctor & Gamble Company High density absorbent members having lower density and lower basis weight acquisition zones
JPS6343930A (ja) * 1986-08-11 1988-02-25 Mitsubishi Petrochem Co Ltd 高吸水性ポリマ−の製造法
GB8703606D0 (en) 1987-02-17 1987-03-25 Ward Blenkinsop & Co Ltd Benzophenone derivatives
JPS63260907A (ja) * 1987-04-17 1988-10-27 Mitsubishi Petrochem Co Ltd 高吸水性ポリマ−の製造法
US4940464A (en) * 1987-12-16 1990-07-10 Kimberly-Clark Corporation Disposable incontinence garment or training pant
CA1333439C (en) * 1988-05-23 1994-12-06 Akito Yano Method for production of hydrophilic polymer
US5264533A (en) * 1988-06-16 1993-11-23 Basf Aktiengesellschaft Benzophenone derivatives and their preparation
US5244735A (en) * 1988-06-28 1993-09-14 Nippon Shokubai Kagaku Kabushiki Kaisha Water-absorbent resin and production process
KR930007272B1 (ko) 1988-06-28 1993-08-04 닙본 쇼쿠바이 가브시기 가이샤 흡수성 수지 및 그 제법
US4950692A (en) * 1988-12-19 1990-08-21 Nalco Chemical Company Method for reconstituting superabsorbent polymer fines
DE3844445A1 (de) * 1988-12-31 1990-07-19 Basf Ag Uv-vernetzbare massen auf basis von (meth)-acrylesterpolymerisaten
US5248805A (en) * 1988-12-31 1993-09-28 Basf Aktiengesellschaft Radiation-senstive, ethylenically unsaturated, copolymerizable compounds and their preparation
DE3844444A1 (de) 1988-12-31 1990-08-09 Basf Ag Strahlungsempfindliche, ethylenisch ungesaettigte, copolymerisierbare verbindungen und verfahren zu deren herstellung
US5145906A (en) * 1989-09-28 1992-09-08 Hoechst Celanese Corporation Super-absorbent polymer having improved absorbency properties
US5137537A (en) * 1989-11-07 1992-08-11 The Procter & Gamble Cellulose Company Absorbent structure containing individualized, polycarboxylic acid crosslinked wood pulp cellulose fibers
US5164459A (en) 1990-04-02 1992-11-17 Nippon Shokubai Kagaku Kogyo Co., Ltd. Method for treating the surface of an absorbent resin
DE69124749T2 (de) 1990-04-27 1997-06-12 Nippon Catalytic Chem Ind Verfahren zur Herstellung von salzbeständigem Harz
US5241009A (en) 1990-05-07 1993-08-31 Kimberly-Clark Corporation Polymeric composition containing carboxy nueutralized with lithium or potassium
ES2070369T3 (es) * 1990-07-17 1995-06-01 Sanyo Chemical Ind Ltd Procedimiento para la fabricacion de resinas absorbentes de agua.
DE4037079A1 (de) * 1990-11-22 1992-05-27 Basf Ag Ungesaettigte phenonderivate und ihre verwendung als haftklebstoffe
US5478879A (en) 1991-01-22 1995-12-26 Nippon Shokubai Co., Ltd. Method for production of absorbent resin
TW241279B (US07875362-20110125-C00021.png) * 1991-02-01 1995-02-21 Catalyst co ltd
US5151092A (en) * 1991-06-13 1992-09-29 The Procter & Gamble Company Absorbent article with dynamic elastic waist feature having a predisposed resilient flexural hinge
US5250640A (en) 1991-04-10 1993-10-05 Nippon Shokubai Co., Ltd. Method for production of particulate hydrogel polymer and absorbent resin
GB9107952D0 (en) 1991-04-15 1991-05-29 Dow Rheinmuenster Surface crosslinked and surfactant coated absorbent resin particles and method of preparation
US5075344A (en) 1991-05-20 1991-12-24 The Dow Chemical Company Process for producing a superabsorbent polymer
US5244934A (en) * 1991-06-07 1993-09-14 Takai Rubber Industries, Ltd. Irradiation or thermal treatment of water-impregnated cross-linked poly-acrylic acid metal salt resin particles
WO1993001622A1 (en) * 1991-07-09 1993-01-21 Scimat Limited Polymeric sheet
US5387207A (en) * 1991-08-12 1995-02-07 The Procter & Gamble Company Thin-unit-wet absorbent foam materials for aqueous body fluids and process for making same
US5147345A (en) * 1991-08-12 1992-09-15 The Procter & Gamble Company High efficiency absorbent articles for incontinence management
US5260345A (en) 1991-08-12 1993-11-09 The Procter & Gamble Company Absorbent foam materials for aqueous body fluids and absorbent articles containing such materials
EP0625998B1 (en) 1992-02-10 1996-06-05 Minnesota Mining And Manufacturing Company Radiation crosslinked elastomers
US5342338A (en) * 1993-06-11 1994-08-30 The Procter & Gamble Company Disposable absorbent article for low-viscosity fecal material
US5397316A (en) * 1993-06-25 1995-03-14 The Procter & Gamble Company Slitted absorbent members for aqueous body fluids formed of expandable absorbent materials
JPH07142627A (ja) * 1993-11-18 1995-06-02 Fujitsu Ltd 半導体装置及びその製造方法
SG72621A1 (en) 1993-11-19 2000-05-23 Procter & Gamble Absorbent article with multi-directional extensible side panels
EP0937444B1 (en) * 1993-12-28 2002-11-06 Kao Corporation Crosslinked cellulose fibers, absorbent papers and absorbent members using the same, topsheets using the same, and absorbent articles using the same
US5610208A (en) * 1994-02-17 1997-03-11 Nippon Shokubai Co., Ltd. Water-absorbent agent, method for production thereof, and water-absorbent composition
US5554145A (en) * 1994-02-28 1996-09-10 The Procter & Gamble Company Absorbent article with multiple zone structural elastic-like film web extensible waist feature
US5599335A (en) 1994-03-29 1997-02-04 The Procter & Gamble Company Absorbent members for body fluids having good wet integrity and relatively high concentrations of hydrogel-forming absorbent polymer
WO1995027739A1 (en) * 1994-04-11 1995-10-19 Hoechst Celanese Corporation Superabsorbent polymers and products therefrom
US5883158A (en) * 1994-08-12 1999-03-16 Kao Corporation Process for producing improved super absorbent polymer
DE69430242T2 (de) 1994-09-09 2002-10-24 Procter & Gamble Methode zur Herstellung einer absorbierenden Struktur
US5650222A (en) * 1995-01-10 1997-07-22 The Procter & Gamble Company Absorbent foam materials for aqueous fluids made from high internal phase emulsions having very high water-to-oil ratios
US5569234A (en) 1995-04-03 1996-10-29 The Procter & Gamble Company Disposable pull-on pant
DE19521431A1 (de) * 1995-06-16 1996-12-19 Stockhausen Chem Fab Gmbh Druckfähige Quellpaste und ihre Verwendung zur Kabelisolierung und zur Herstellung von Vliesen
DE19526856A1 (de) * 1995-07-22 1997-01-23 Basf Ag Strahlungshärtbare Massen mit kovalent gebundenen Photoinitiatoren
FR2744456A1 (fr) 1996-02-07 1997-08-08 Atochem Elf Sa Polymeres superabsorbants a structure coeur-coquille et leur procede d'obtention
DE19619680A1 (de) 1996-05-15 1997-11-20 Buna Sow Leuna Olefinverb Gmbh Verfahren zur Herstellung von superabsorbierenden Polymeren auf Stärkebasis
EP0844270B1 (en) 1996-11-20 2004-11-17 Sanyo Chemical Industries, Ltd. Water absorbing agent and method of producing the same
US6228930B1 (en) * 1997-06-18 2001-05-08 Nippon Shokubai Co., Ltd. Water-absorbent resin granule-containing composition and production process for water-absorbent resin granule
US6342298B1 (en) * 1997-11-19 2002-01-29 Basf Aktiengesellschaft Multicomponent superabsorbent fibers
US6222091B1 (en) * 1997-11-19 2001-04-24 Basf Aktiengesellschaft Multicomponent superabsorbent gel particles
DE19809540A1 (de) * 1998-03-05 1999-09-09 Basf Ag Wasserabsorbierende, schaumförmige, vernetzte Polymerisate, Verfahren zu ihrer Herstellung und ihre Verwendung
US6007833A (en) 1998-03-19 1999-12-28 Surmodics, Inc. Crosslinkable macromers bearing initiator groups
US6562879B1 (en) * 1999-02-15 2003-05-13 Nippon Shokubai Co., Ltd. Water-absorbent resin powder and its production process and use
EP1169379B1 (en) * 1999-03-12 2004-09-22 Basf Aktiengesellschaft Color-stable superabsorbent polymer composition
WO2000055418A1 (fr) * 1999-03-16 2000-09-21 Mitsubishi Chemical Corporation Composite d'absorption d'eau et son procede de production en continu
US6565981B1 (en) * 1999-03-30 2003-05-20 Stockhausen Gmbh & Co. Kg Polymers that are cross-linkable to form superabsorbent polymers
US6342652B1 (en) * 1999-09-01 2002-01-29 Nippon Shokubai Co., Ltd. Water-swellable crosslinked polymer, its composition, and their production processes and uses
US6803107B2 (en) 1999-09-07 2004-10-12 Basf Aktiengesellschaft Surface-treated superabsorbent polymer particles
US6391451B1 (en) 1999-09-07 2002-05-21 Basf Aktiengesellschaft Surface-treated superabsorbent polymer particles
US6579958B2 (en) * 1999-12-07 2003-06-17 The Dow Chemical Company Superabsorbent polymers having a slow rate of absorption
US6417425B1 (en) * 2000-02-01 2002-07-09 Basf Corporation Absorbent article and process for preparing an absorbent article
WO2001089591A2 (en) 2000-05-25 2001-11-29 Basf Aktiengesellschaft Surface-treated superabsorbent polymer particles
US6927268B2 (en) 2000-06-21 2005-08-09 Nippon Shokubai Co., Ltd. Production process for water-absorbent resin
US6906159B2 (en) 2000-08-03 2005-06-14 Nippon Shokubai Co., Ltd. Water-absorbent resin, hydropolymer, process for producing them, and uses of them
US6809158B2 (en) 2000-10-20 2004-10-26 Nippon Shokubai Co., Ltd. Water-absorbing agent and process for producing the same
CN1262604C (zh) * 2001-01-26 2006-07-05 株式会社日本触媒 吸水剂及其制法以及吸水制品
ATE440875T1 (de) * 2001-06-08 2009-09-15 Basf Se Wasserlísliche strahlungsaktivierbare polymerharze
DE60135834D1 (de) * 2001-06-08 2008-10-30 Procter & Gamble Cellulosfasern enthaltend strahlungsaktivierbare Harzverbindungen
JP2003073919A (ja) 2001-08-30 2003-03-12 Toagosei Co Ltd 繊維状吸水性樹脂の製造方法
US6617372B2 (en) * 2001-10-23 2003-09-09 Isp Investments Inc. Process of making polymeric hydrogel products
ATE471166T1 (de) 2001-11-21 2010-07-15 Basf Se Vernetzte polyaminbeschichtung auf superabsorbierenden hydrogelen
JP2003156961A (ja) 2001-11-22 2003-05-30 Fuji Xerox Co Ltd 定着用回転体、加圧用回転体、転写用回転体、帯電用回転体、転写同時定着用回転体
AU2002349359A1 (en) * 2001-12-20 2003-07-09 Basf Aktiengesellschaft Absorbent article
DE10221202A1 (de) 2002-05-13 2003-07-10 Basf Ag Verfahren zur Herstellung von wässrigen für die Herstellung von Acrylsäurepolymeren geeigneten Acrylsäure-Lösung II
WO2003104300A1 (de) * 2002-06-01 2003-12-18 Basf Aktiengesellschaft (meth)acrylester von polyalkoxyliertem trimethylolpropan
MXPA04011457A (es) * 2002-06-11 2005-02-14 Basf Ag Esteres (met)acrilicos de trimetilolpropano polialcoxilado.
US20030233082A1 (en) 2002-06-13 2003-12-18 The Procter & Gamble Company Highly flexible and low deformation fastening device
US20040143030A1 (en) * 2002-09-11 2004-07-22 Fumiyoshi Ikkai Method of producing synthetic polymer gel and said gel
US7183336B2 (en) * 2002-10-02 2007-02-27 Super Absorbent Company Irradiated absorbent materials
US6939492B2 (en) * 2002-12-26 2005-09-06 Kimberly-Clark Worldwide, Inc. Method for making fibrous web materials
CN100346843C (zh) * 2003-02-10 2007-11-07 株式会社日本触媒 吸水剂
EP1911425B1 (en) * 2003-02-12 2014-01-15 The Procter and Gamble Company Absorbent core for an absorbent article
TW200500046A (en) * 2003-03-26 2005-01-01 Basf Ag Color-stable superabsorbent polymer composition
BRPI0409007A (pt) 2003-04-03 2006-03-28 Basf Ag mistura de éster, processos para preparar a mesma e para preparar um hidrogel reticulado, polìmero, hidrogel reticulado, uso de um polìmero, composição de matéria, e, usos de uma mistura da reação e de uma mistura de éster
DE10358372A1 (de) 2003-04-03 2004-10-14 Basf Ag Gemische von Verbindungen mit mindestens zwei Doppelbindungen und deren Verwendung
US7405321B2 (en) * 2003-06-06 2008-07-29 Basf Aktiengesellschaft (Meth)acrylic ester of alkenylene glycols and the use thereof
EP1506788A1 (en) 2003-08-06 2005-02-16 The Procter & Gamble Company Superabsorbent polymers having radiation activatable surface cross-linkers and method of making them
CN100471524C (zh) 2003-08-06 2009-03-25 宝洁公司 制备包含已涂敷的水可溶胀聚合物的水可溶胀材料的方法
EP1504772A1 (en) * 2003-08-06 2005-02-09 The Procter & Gamble Company Superabsorbent polymers having radiation activable surface cross-linkers and method of making them
EP1504771A1 (en) 2003-08-06 2005-02-09 The Procter & Gamble Company Superabsorbent polymers having radiation activatable surface cross-linkers and method of making them
EP1510229B1 (en) * 2003-08-27 2010-07-14 Nippon Shokubai Co., Ltd. Process for production of surface-treated particulate water-absorbent resin
EP1516884B2 (en) 2003-09-19 2023-02-22 Nippon Shokubai Co., Ltd. Water-absorbent resin having treated surface and process for producing the same
MXPA06004345A (es) 2003-11-07 2006-06-27 Nippon Catalytic Chem Ind Composicion de resina absorbente de agua en particulas y su proceso de produccion.
US20050142965A1 (en) * 2003-12-29 2005-06-30 Kimberly-Clark Worldwide, Inc. Surface charge manipulation for improved fluid intake rates of absorbent composites
US9125965B2 (en) * 2004-02-24 2015-09-08 The Procter & Gamble Company Superabsorbent polymers comprising direct covalent bonds between polymer chain segments and methods of making them
RU2337750C2 (ru) 2004-03-31 2008-11-10 Ниппон Сокубаи Ко., Лтд. Агент, поглощающий водную жидкость, и способ его получения
US7794441B2 (en) 2004-04-14 2010-09-14 The Procter & Gamble Company Dual cuff for a unitary disposable absorbent article being spaced away from backsheet
EP1624002B1 (en) 2004-08-07 2019-04-03 The Procter & Gamble Company Superabsorbent polymer particles comprising functionalizers and method of making them
US20060128827A1 (en) * 2004-12-10 2006-06-15 The Procter & Gamble Company Absorbent members comprising modified water absorbent resin for use in diapers
JP2007056071A (ja) * 2005-08-22 2007-03-08 Procter & Gamble Co 改質された吸水性樹脂の製法
JP5084513B2 (ja) * 2004-12-10 2012-11-28 株式会社日本触媒 改質された吸水性樹脂の製造方法
DE602005011491D1 (de) 2004-12-10 2009-01-15 Nippon Catalytic Chem Ind Verfahren zur oberflächenbehandlung von wasserabsorbierendem harz
JP2006169267A (ja) * 2004-12-10 2006-06-29 Procter & Gamble Co 改質された吸水性樹脂の製法
TW200635969A (en) * 2005-04-06 2006-10-16 Nippon Catalytic Chem Ind Particulate water absorbing agent, water-absorbent core and absorbing article
WO2007024927A2 (en) * 2005-08-23 2007-03-01 The Procter & Gamble Company Absorbent articles comprising surface cross-linked superabsorbent polymer particles made by a method using ultraviolet radiation
WO2007024926A1 (en) * 2005-08-23 2007-03-01 The Procter & Gamble Company Absorbent articles comprising surface cross-linked superabsorbent polymer particles made by a method using vacuum ultraviolet radiation
EP1757646A1 (en) 2005-08-23 2007-02-28 The Procter and Gamble Company Method of surface cross-linking superabsorbent polymer particles using ultraviolet radiation
EP1757641A1 (en) * 2005-08-23 2007-02-28 The Procter and Gamble Company Method of surface cross-linking highly neutralized superabsorbent polymer particles using Bronsted acids
JP2007077366A (ja) * 2005-09-16 2007-03-29 Procter & Gamble Co 吸水剤の製法
JP2007099845A (ja) * 2005-09-30 2007-04-19 Procter & Gamble Co 水性液吸収剤およびその製法
JP2007277466A (ja) * 2006-04-10 2007-10-25 Procter & Gamble Co 改質された吸水性樹脂の製法
WO2007120561A2 (en) 2006-04-10 2007-10-25 The Procter & Gamble Company An absorbent member comprising a modified water absorbent resin
WO2007119730A1 (en) * 2006-04-10 2007-10-25 Nippon Shokubai Co., Ltd. Method for production of modified water absorbent resin
JP2007321007A (ja) * 2006-05-30 2007-12-13 Nippon Shokubai Co Ltd 改質された吸水性樹脂の製造方法
JP2007321008A (ja) * 2006-05-30 2007-12-13 Procter & Gamble Co 改質された吸水性樹脂の製法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4666983A (en) 1982-04-19 1987-05-19 Nippon Shokubai Kagaku Kogyo Co., Ltd. Absorbent article
US4910250A (en) 1985-06-22 1990-03-20 Hayashikane Shipbuilding & Engineering Co., Ltd. Aqueous composition, method of producing a water absorbent polymer
US4783510A (en) 1986-06-04 1988-11-08 Taiyo Fishery Co., Ltd. Process for improving a water absorbent polyacrylic acid polymer and an improved polymer produced by said process
US5422405A (en) 1992-12-16 1995-06-06 Nippon Shokubai Co., Ltd. Method for production of absorbent resin
JP2004099789A (ja) 2002-09-11 2004-04-02 L'oreal Sa 合成高分子ゲルの製造方法
WO2004031253A1 (en) 2002-10-02 2004-04-15 Coloplast A/S A hydrogel

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
J. PHOTOCHEM. PHOTOBIOL., A., vol. 44, 1988, pages 243
J. PHYS. CHEM., vol. 79, 1975, pages 2693

Also Published As

Publication number Publication date
CA2649299A1 (en) 2007-10-25
MX2008013041A (es) 2008-10-17
JP4928602B2 (ja) 2012-05-09
US7745507B2 (en) 2010-06-29
US20100298794A1 (en) 2010-11-25
EP2004732A2 (en) 2008-12-24
US20070238806A1 (en) 2007-10-11
WO2007120561A3 (en) 2008-01-03
JP2009532567A (ja) 2009-09-10
US7875362B2 (en) 2011-01-25

Similar Documents

Publication Publication Date Title
US7745507B2 (en) Absorbent member comprising a modified water absorbent resin
JP5022226B2 (ja) 吸水性樹脂の表面処理方法
JP5084513B2 (ja) 改質された吸水性樹脂の製造方法
US20060128827A1 (en) Absorbent members comprising modified water absorbent resin for use in diapers
EP1924295B1 (en) An absorbent member comprising a water absorbing agent
JP2010094656A (ja) 微粒子が固着してなる吸水剤
JP2008018328A (ja) 粒子状吸水剤およびその製造方法
JP2007277466A (ja) 改質された吸水性樹脂の製法
JP2007327008A (ja) 抗菌性吸水性樹脂の製造方法
JP5329023B2 (ja) 吸水性樹脂の表面処理方法
WO2007119730A1 (en) Method for production of modified water absorbent resin
JP2007056071A (ja) 改質された吸水性樹脂の製法
JP2006169267A (ja) 改質された吸水性樹脂の製法
WO2009048157A1 (en) Surface treatment method for water-absorbent resin
JP2007326912A (ja) 改質された吸水性樹脂の製法
BRPI0410042B1 (pt) Processo para produqao de uma resina hidrofila, resina hidrofila obtida pelo dito processo e artigo absorvente para absorqao de produtos de excreqao e sangue compreendendo a dita resina

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07754914

Country of ref document: EP

Kind code of ref document: A2

WWE Wipo information: entry into national phase

Ref document number: 2009504294

Country of ref document: JP

Ref document number: 2007754914

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 200780012519.X

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: MX/a/2008/013041

Country of ref document: MX

WWE Wipo information: entry into national phase

Ref document number: 2649299

Country of ref document: CA

NENP Non-entry into the national phase

Ref country code: DE