WO2007114811A1 - Polymères fonctionnalisés à base de polypropylène - Google Patents

Polymères fonctionnalisés à base de polypropylène Download PDF

Info

Publication number
WO2007114811A1
WO2007114811A1 PCT/US2006/012061 US2006012061W WO2007114811A1 WO 2007114811 A1 WO2007114811 A1 WO 2007114811A1 US 2006012061 W US2006012061 W US 2006012061W WO 2007114811 A1 WO2007114811 A1 WO 2007114811A1
Authority
WO
WIPO (PCT)
Prior art keywords
propylene
backbone
polymer
before grafting
based polymer
Prior art date
Application number
PCT/US2006/012061
Other languages
English (en)
Inventor
Jean-Roch Schauder
Abdelhadi Sahnoune
Sudhin Datta
Original Assignee
Exxonmobil Chemical Patents Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Exxonmobil Chemical Patents Inc. filed Critical Exxonmobil Chemical Patents Inc.
Priority to CN2006800540709A priority Critical patent/CN101415739B/zh
Priority to JP2009502740A priority patent/JP5279138B2/ja
Priority to CA2647562A priority patent/CA2647562C/fr
Priority to PCT/US2006/012061 priority patent/WO2007114811A1/fr
Priority to EP06740269A priority patent/EP2004714A1/fr
Publication of WO2007114811A1 publication Critical patent/WO2007114811A1/fr

Abstract

La présente invention concerne un procédé de préparation d'un polymère fonctionnalisé à base de propylène et un polymère fonctionnalisé comportant un squelette de polymère à base de propylène. Le squelette de polymère à base de propylène peut en outre contenir une ou plusieurs alpha oléfines.
PCT/US2006/012061 2006-03-30 2006-03-30 Polymères fonctionnalisés à base de polypropylène WO2007114811A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
CN2006800540709A CN101415739B (zh) 2006-03-30 2006-03-30 官能化聚丙烯基聚合物
JP2009502740A JP5279138B2 (ja) 2006-03-30 2006-03-30 官能化ポリプロピレンベースポリマー
CA2647562A CA2647562C (fr) 2006-03-30 2006-03-30 Polymeres fonctionnalises a base de polypropylene
PCT/US2006/012061 WO2007114811A1 (fr) 2006-03-30 2006-03-30 Polymères fonctionnalisés à base de polypropylène
EP06740269A EP2004714A1 (fr) 2006-03-30 2006-03-30 Polymères fonctionnalisés à base de polypropylène

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2006/012061 WO2007114811A1 (fr) 2006-03-30 2006-03-30 Polymères fonctionnalisés à base de polypropylène

Publications (1)

Publication Number Publication Date
WO2007114811A1 true WO2007114811A1 (fr) 2007-10-11

Family

ID=36764202

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2006/012061 WO2007114811A1 (fr) 2006-03-30 2006-03-30 Polymères fonctionnalisés à base de polypropylène

Country Status (5)

Country Link
EP (1) EP2004714A1 (fr)
JP (1) JP5279138B2 (fr)
CN (1) CN101415739B (fr)
CA (1) CA2647562C (fr)
WO (1) WO2007114811A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120100383A1 (en) * 2009-06-19 2012-04-26 Kwangjin Song Metallized Polypropylene Film and a Process of Making the Same
CN105440217A (zh) * 2015-12-29 2016-03-30 佳易容相容剂江苏有限公司 马来酸酐接枝聚丙烯组合物及其制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6624831B2 (ja) * 2015-07-24 2019-12-25 三井化学株式会社 オレフィン系樹脂、該樹脂の製造方法、ペレット、熱可塑性エラストマーおよび架橋ゴム
CN106905491B (zh) * 2017-01-26 2019-10-15 厦门内加湖新材料科技有限公司 聚丙烯基酸改性接枝物以及含有该接枝物的粘合剂

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5059658A (en) * 1989-04-07 1991-10-22 Tonen Sekiyagaku Kabushiki Kaisha Method of producing modified polypropylene
US20050075441A1 (en) * 2001-11-01 2005-04-07 Mitsubishi Chemical Corporation Modified propylene polymer, composition containing the same and use thereof

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06122739A (ja) * 1992-10-13 1994-05-06 Kanegafuchi Chem Ind Co Ltd 変性ポリオレフィンとその製造方法
JP4439686B2 (ja) * 2000-06-09 2010-03-24 三井化学株式会社 シンジオタクティックプロピレン系共重合体及び該共重合体を含む熱可塑性樹脂組成物
JP4509340B2 (ja) * 2000-09-20 2010-07-21 三井化学株式会社 熱可塑性樹脂組成物およびその成形体
DE60142573D1 (de) * 2000-10-30 2010-08-26 Exxon Mobil Chem Patents Inc En-ethylen-copolymere

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5059658A (en) * 1989-04-07 1991-10-22 Tonen Sekiyagaku Kabushiki Kaisha Method of producing modified polypropylene
US20050075441A1 (en) * 2001-11-01 2005-04-07 Mitsubishi Chemical Corporation Modified propylene polymer, composition containing the same and use thereof

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP2004714A1 *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120100383A1 (en) * 2009-06-19 2012-04-26 Kwangjin Song Metallized Polypropylene Film and a Process of Making the Same
CN105440217A (zh) * 2015-12-29 2016-03-30 佳易容相容剂江苏有限公司 马来酸酐接枝聚丙烯组合物及其制备方法
CN105440217B (zh) * 2015-12-29 2019-03-26 佳易容相容剂江苏有限公司 马来酸酐接枝聚丙烯组合物及其制备方法

Also Published As

Publication number Publication date
EP2004714A1 (fr) 2008-12-24
CA2647562C (fr) 2011-07-05
CN101415739A (zh) 2009-04-22
CN101415739B (zh) 2011-08-24
JP5279138B2 (ja) 2013-09-04
JP2009532518A (ja) 2009-09-10
CA2647562A1 (fr) 2007-10-11

Similar Documents

Publication Publication Date Title
US7282541B2 (en) Functionalized polypropylene-based polymers
EP1330479B1 (fr) Polymeres greffes modifies sur la base de nouveaux copolymeres ethylene-propylene
JP4966463B2 (ja) プロピレン−ベース−接着剤組成物
KR101501400B1 (ko) 관능화된 올레핀 혼성중합체, 조성물 및 이로부터 제조된 제품, 및 이의 제조 방법
EP1969022B1 (fr) Interpolymères d'éthylène a bas poids moléculaire, procédé pour les préparer et utilisations
US5723545A (en) Blends of a semi-crystalline polymer and elastic α-olefin/cyclic olefin copolymers
US6716928B2 (en) Grafted propylene copolymers and adhesive blends
US20120065333A1 (en) Crosslinkable high melt strength polypropylene resins
EP1966301A1 (fr) Composition de polypropylene comprenant une composante copolymere de propylene
CA2647562C (fr) Polymeres fonctionnalises a base de polypropylene
JP5237961B2 (ja) 低い硬度及び低い光沢を有するポリオレフィン組成物
EP1963426B1 (fr) Formules adhésives thermoplastiques vulcanisées
JP2003327642A (ja) プロピレン−エチレンブロック共重合体
EP0785969B1 (fr) Melanges de polypropylene et de copolymeres elastiques d'alpha-olefines et d'olefines cycliques
JP5237960B2 (ja) 低硬度及び低光沢性のポリオレフィン組成物
TWI415889B (zh) 具有低硬度與低光澤之聚烯烴組成物
TWI433884B (zh) 具有低硬度與低光澤之聚烯烴組成物
JPH06172460A (ja) 反応性ポリプロピレンの製造方法
JPH06172422A (ja) 反応性ポリプロピレン
JPH0848825A (ja) オレフィン系共重合体組成物
JPH05310858A (ja) 変性ポリオレフィンの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 06740269

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2647562

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 200680054070.9

Country of ref document: CN

WWE Wipo information: entry into national phase

Ref document number: 2009502740

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2006740269

Country of ref document: EP