WO2007043822A9 - Compositions adhesives acryliques sensibles a la pression - Google Patents
Compositions adhesives acryliques sensibles a la pression Download PDFInfo
- Publication number
- WO2007043822A9 WO2007043822A9 PCT/KR2006/004118 KR2006004118W WO2007043822A9 WO 2007043822 A9 WO2007043822 A9 WO 2007043822A9 KR 2006004118 W KR2006004118 W KR 2006004118W WO 2007043822 A9 WO2007043822 A9 WO 2007043822A9
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- meth
- acrylate
- acrylic
- adhesive composition
- group
- Prior art date
Abstract
La présente invention concerne des compositions adhésives acryliques, et plus précisément des compositions adhésives acryliques présentant des propriétés antistatiques améliorées sans que la durabilité, la transparence et la résistance au pelage ne soient affectées, lesdites compositions étant composées d'un copolymère acrylique, d'un composé hydrophile complexe et d'un composé hydrophobe complexe, de manière à inhiber de manière suffisante le développement d'électricité statique, quelque soit l'état de la surface (hydrophobe ou hydrophile) d'une plaque polarisante.
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2006800461270A CN101326254B (zh) | 2005-10-14 | 2006-10-13 | 丙烯酸压敏粘合剂组合物 |
EP06799197A EP1943321B1 (fr) | 2005-10-14 | 2006-10-13 | Compositions adhesives acryliques sensibles a la pression |
JP2008535457A JP5334581B2 (ja) | 2005-10-14 | 2006-10-13 | アクリル系粘着剤組成物 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020050097159A KR100830814B1 (ko) | 2005-10-14 | 2005-10-14 | 아크릴계 점착제 조성물 |
KR10-2005-0097159 | 2005-10-14 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2007043822A1 WO2007043822A1 (fr) | 2007-04-19 |
WO2007043822A9 true WO2007043822A9 (fr) | 2010-05-27 |
Family
ID=37943014
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2006/004118 WO2007043822A1 (fr) | 2005-10-14 | 2006-10-13 | Compositions adhesives acryliques sensibles a la pression |
Country Status (7)
Country | Link |
---|---|
US (1) | US7655285B2 (fr) |
EP (1) | EP1943321B1 (fr) |
JP (1) | JP5334581B2 (fr) |
KR (1) | KR100830814B1 (fr) |
CN (1) | CN101326254B (fr) |
TW (1) | TWI324628B (fr) |
WO (1) | WO2007043822A1 (fr) |
Families Citing this family (36)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5259940B2 (ja) * | 2005-09-05 | 2013-08-07 | 日東電工株式会社 | 粘着剤組成物、粘着シートおよび表面保護フィルム |
KR100830814B1 (ko) * | 2005-10-14 | 2008-05-20 | 주식회사 엘지화학 | 아크릴계 점착제 조성물 |
KR100904153B1 (ko) * | 2007-04-30 | 2009-06-25 | 도레이새한 주식회사 | 디스플레이 광학소재용 보호필름 |
WO2009002110A2 (fr) * | 2007-06-27 | 2008-12-31 | Kwang Suck Suh | Composition adhésive autocollante à caractéristiques de pelage améliorées et films de protection utilisant une telle composition |
JP5452850B2 (ja) * | 2007-07-13 | 2014-03-26 | チェイル インダストリーズ インコーポレイテッド | 光学部材用の表面保護シート |
JP5769353B2 (ja) * | 2007-07-13 | 2015-08-26 | チェイル インダストリーズ インコーポレイテッド | 粘着剤組成物及び光学部材 |
JP5483808B2 (ja) * | 2007-08-14 | 2014-05-07 | チェイル インダストリーズ インコーポレイテッド | 粘着剤組成物及び光学部材 |
KR101023842B1 (ko) * | 2008-01-11 | 2011-03-22 | 주식회사 엘지화학 | 점착제 조성물, 상기를 포함하는 편광판 및 액정표시장치 |
KR101082450B1 (ko) * | 2008-01-14 | 2011-11-11 | 주식회사 엘지화학 | 아크릴계 점착제 조성물 |
JP5641634B2 (ja) * | 2008-03-13 | 2014-12-17 | 日東電工株式会社 | 粘着剤組成物、粘着剤層、粘着部材および画像表示装置、並びに画像表示装置からの光学フィルムの剥離方法および表示パネルの取り出し方法 |
KR101576101B1 (ko) | 2008-04-15 | 2015-12-09 | 동우 화인켐 주식회사 | 대전방지성 점착제 조성물, 이를 이용한 편광판 및 표면보호필름 |
DE102008023758A1 (de) | 2008-05-09 | 2009-11-12 | Tesa Se | Haftklebebänder zur Verklebung von Druckplatten |
WO2010002197A2 (fr) * | 2008-07-01 | 2010-01-07 | (주)Lg화학 | Composition acrylique pour éléments optiques, film protecteur pour éléments optiques, plaque polarisante et afficheur à cristaux liquides |
KR101084033B1 (ko) * | 2008-07-16 | 2011-11-16 | 도레이첨단소재 주식회사 | 아크릴계 점착제 조성물 및 그를 이용한 표면보호필름 |
KR101509442B1 (ko) * | 2008-08-06 | 2015-04-06 | 동우 화인켐 주식회사 | 대전방지성 및 빛샘방지성 점착제 조성물 및 이를 이용한편광판 |
JP5580069B2 (ja) * | 2009-02-26 | 2014-08-27 | 日東電工株式会社 | 表面保護フィルム用粘着剤組成物とその利用 |
KR101206591B1 (ko) | 2009-08-25 | 2012-11-29 | (주)엘지하우시스 | 수성 점착제 조성물, 그 제조방법 및 점착 필름 |
JP2011168751A (ja) | 2010-02-22 | 2011-09-01 | Nitto Denko Corp | 表面保護フィルム |
WO2011115224A1 (fr) * | 2010-03-18 | 2011-09-22 | 積水化学工業株式会社 | Composition d'adhésif autocollant pour éléments optiques et ruban adhésif autocollant pour éléments optiques |
KR101552741B1 (ko) * | 2010-04-05 | 2015-09-11 | (주)엘지하우시스 | 터치 패널용 점착제 조성물, 점착필름 및 터치 패널 |
KR20130106281A (ko) * | 2010-06-08 | 2013-09-27 | 헨켈 코포레이션 | 이중 경화 접착제 |
JP5588361B2 (ja) * | 2011-01-06 | 2014-09-10 | 日東電工株式会社 | 表面保護シート |
CN102226067A (zh) * | 2011-05-16 | 2011-10-26 | 永一胶粘(中山)有限公司 | 一种丙烯酸酯溶剂型压敏胶粘剂及其制品 |
JP5426715B2 (ja) * | 2011-09-30 | 2014-02-26 | 日東電工株式会社 | 粘着剤、粘着剤層、および粘着シート |
CN103814095B (zh) | 2011-11-08 | 2016-08-17 | Lg化学株式会社 | 用于具有抗静电性的保护膜的压敏粘合剂组合物及其制备方法 |
JP5882774B2 (ja) * | 2012-02-13 | 2016-03-09 | 藤森工業株式会社 | 粘着剤組成物、粘着フィルム及び表面保護フィルム |
KR101940543B1 (ko) | 2014-12-24 | 2019-01-21 | 주식회사 엘지화학 | 아크릴계 점착 시트, 의료용 점착 테이프 및 제조방법 |
CN104531033B (zh) * | 2015-01-20 | 2016-08-24 | 广州市聚科聚氨酯有限公司 | 一种耐高温的水性聚氨酯胶粘剂的制备方法 |
KR101969342B1 (ko) * | 2015-07-10 | 2019-04-16 | 주식회사 엘지화학 | 가교성 조성물 |
JP6038268B2 (ja) * | 2015-12-11 | 2016-12-07 | 日東電工株式会社 | 粘着剤組成物、粘着剤層、粘着剤層付偏光板および画像形成装置 |
CN105694087A (zh) * | 2016-02-05 | 2016-06-22 | 浙江美登特种薄膜有限公司 | 一种抗静电电容笔的制备方法 |
KR102159513B1 (ko) * | 2017-12-15 | 2020-09-25 | 주식회사 엘지화학 | 가교성 조성물 |
KR102236532B1 (ko) | 2018-04-25 | 2021-04-06 | 주식회사 엘지화학 | 가교성 조성물 |
KR102294139B1 (ko) * | 2018-04-25 | 2021-08-26 | 산진 옵토일렉트로닉스 (쑤저우) 컴퍼니 리미티드 | 가교성 조성물 |
KR102329983B1 (ko) | 2018-10-31 | 2021-11-22 | 주식회사 엘지화학 | 점착제 조성물, 표면 보호 필름 및 유기 발광 전자 장치의 제조 방법 |
KR102671572B1 (ko) * | 2022-06-29 | 2024-06-04 | 주식회사 켐코 | 저탄소 배출 공정을 이용하여 제조되는 친환경 점착제 수지, 이를 포함하는 점착제 조성물 및 이를 이용하여 형성된 점착제층 |
Family Cites Families (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3658744A (en) * | 1969-10-17 | 1972-04-25 | Uniroyal Inc | Antistatic carpet composition containing alkali metal carboxylate and polyhydric alcohol |
US4542095A (en) * | 1984-07-25 | 1985-09-17 | Eastman Kodak Company | Antistatic compositions comprising polymerized alkylene oxide and alkali metal salts and elements thereof |
US4759983A (en) * | 1986-05-30 | 1988-07-26 | Union Oil Company Of California | Pressure sensitive adhesives and adhesive articles |
JP3457308B2 (ja) * | 1991-11-15 | 2003-10-14 | ミネソタ マイニング アンド マニュファクチャリング カンパニー | 二相複合導性感圧接着剤の施された生物医療電極 |
JP3190743B2 (ja) | 1992-10-14 | 2001-07-23 | 日東電工株式会社 | 粘着テープまたはシート |
US5508107A (en) * | 1993-07-28 | 1996-04-16 | Minnesota Mining And Manufacturing Company | Pressure-sensitive adhesive tapes for electronics applications |
US5378405A (en) | 1993-07-28 | 1995-01-03 | Minnesota Mining And Manufacturing Company | Conductive microparticles and pressure-sensitive adhesive tapes made therefrom |
EP0745655A3 (fr) * | 1995-06-02 | 1998-04-29 | National Starch and Chemical Investment Holding Corporation | Adhésif stratifié antistatique |
JP4096209B2 (ja) * | 1996-02-02 | 2008-06-04 | 綜研化学株式会社 | 粘着剤組成物およびそれを塗布してなる表面保護フィルム |
KR0165527B1 (ko) * | 1996-07-09 | 1999-01-15 | 박상욱 | 아크릴계 에멀젼 점착체 조성물 |
US5885708A (en) * | 1997-02-14 | 1999-03-23 | Minnesota Mining And Manufacturing Company | Antistatic latex adhesives |
JP2000129235A (ja) * | 1998-10-27 | 2000-05-09 | Minnesota Mining & Mfg Co <3M> | 帯電防止性粘着剤組成物 |
JP4336427B2 (ja) * | 1999-10-01 | 2009-09-30 | 帝人株式会社 | 表面保護フィルムおよびそれからなる積層体 |
US6592988B1 (en) * | 1999-12-29 | 2003-07-15 | 3M Innovative Properties Company | Water-and oil-repellent, antistatic composition |
JP4247956B2 (ja) | 2001-07-04 | 2009-04-02 | 古河電気工業株式会社 | 帯電防止ダイシングテープ |
US20030114560A1 (en) * | 2001-08-02 | 2003-06-19 | Jie Yang | Optically clear and antistatic pressure sensitive adhesives |
US20030181557A1 (en) * | 2002-03-01 | 2003-09-25 | Jsr Corporation | Aqueous emulsion dispersion of thermoplastic elastomer and process for preparing the same |
JP2004287199A (ja) | 2003-03-24 | 2004-10-14 | Sun A Kaken Co Ltd | 表面保護フィルム |
JP5422091B2 (ja) | 2003-12-26 | 2014-02-19 | 東洋インキScホールディングス株式会社 | 帯電防止アクリル粘着剤 |
JP4474937B2 (ja) * | 2004-02-20 | 2010-06-09 | 東洋インキ製造株式会社 | 水性接着剤組成物、製造方法および積層体 |
JP4837257B2 (ja) * | 2004-02-26 | 2011-12-14 | 日東電工株式会社 | 帯電防止性粘着型光学フィルムおよび画像表示装置 |
JP4657756B2 (ja) * | 2004-02-27 | 2011-03-23 | 三洋化成工業株式会社 | 帯電防止性粘着シート |
JP2006001240A (ja) * | 2004-06-21 | 2006-01-05 | Seiko Epson Corp | 液体収容体 |
JP4799900B2 (ja) * | 2004-10-28 | 2011-10-26 | 日東電工株式会社 | 粘着剤組成物、粘着シート類および表面保護フィルム |
JP2007070420A (ja) * | 2005-09-06 | 2007-03-22 | Japan Carlit Co Ltd:The | 導電性付与剤及び導電性材料 |
KR100830814B1 (ko) * | 2005-10-14 | 2008-05-20 | 주식회사 엘지화학 | 아크릴계 점착제 조성물 |
-
2005
- 2005-10-14 KR KR1020050097159A patent/KR100830814B1/ko active IP Right Grant
-
2006
- 2006-10-13 CN CN2006800461270A patent/CN101326254B/zh active Active
- 2006-10-13 TW TW095137686A patent/TWI324628B/zh active
- 2006-10-13 JP JP2008535457A patent/JP5334581B2/ja active Active
- 2006-10-13 EP EP06799197A patent/EP1943321B1/fr active Active
- 2006-10-13 WO PCT/KR2006/004118 patent/WO2007043822A1/fr active Application Filing
- 2006-10-16 US US11/581,079 patent/US7655285B2/en active Active
Also Published As
Publication number | Publication date |
---|---|
KR20070041238A (ko) | 2007-04-18 |
EP1943321A1 (fr) | 2008-07-16 |
WO2007043822A1 (fr) | 2007-04-19 |
EP1943321B1 (fr) | 2012-05-16 |
TW200714684A (en) | 2007-04-16 |
CN101326254A (zh) | 2008-12-17 |
TWI324628B (en) | 2010-05-11 |
US7655285B2 (en) | 2010-02-02 |
US20070087133A1 (en) | 2007-04-19 |
JP2009511705A (ja) | 2009-03-19 |
JP5334581B2 (ja) | 2013-11-06 |
CN101326254B (zh) | 2010-09-08 |
KR100830814B1 (ko) | 2008-05-20 |
EP1943321A4 (fr) | 2010-05-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7655285B2 (en) | Acrylic pressure sensitive adhesive compositions | |
EP2231807B1 (fr) | Composition d'adhésif sensible à la pression, film protecteur, polariseur et dispositif d'affichage à cristaux liquides la comprenant | |
EP2796523B1 (fr) | Composition adhésive | |
US8513363B2 (en) | Adhesive composition | |
EP2891693B1 (fr) | Composition d'adhésif sensible à la pression | |
US20130040137A1 (en) | Water-dispersible acrylic pressure-sensitive adhesive composition and pressure-sensitive adhesive sheet | |
US9315691B2 (en) | Adhesive composition | |
EP2889351B1 (fr) | Composition adhésive | |
WO2007021152A1 (fr) | Composition d'adhésif acrylique sensible à la pression | |
JP2008506833A (ja) | 帯電防止性能に優れたアクリル系粘着剤組成物 | |
EP1969078A1 (fr) | Compositions d'adhesif acrylique autocollant | |
US9551812B2 (en) | Adhesive composition, adhesive layer, optical member, and adhesive sheet | |
US20120315476A1 (en) | Adhesive composition and surface protection film using the same | |
EP3147337A1 (fr) | Composition adhésive | |
KR100980187B1 (ko) | 편광판 | |
US9163167B2 (en) | Adhesive composition and optical member using the same | |
WO2008093946A1 (fr) | Plaque polarisante munie d'une couche adhésive autocollante présentant une propriété de fuite de lumière améliorée | |
KR102045736B1 (ko) | 점착제 조성물 및 점착 필름 | |
KR102159487B1 (ko) | 점착제 조성물 | |
KR20100058429A (ko) | 아크릴계 점착제 조성물 | |
KR20090110812A (ko) | 아크릴계 점착제 조성물 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 200680046127.0 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
ENP | Entry into the national phase |
Ref document number: 2008535457 Country of ref document: JP Kind code of ref document: A |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006799197 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |