WO2007015343A1 - 粘着シート - Google Patents
粘着シート Download PDFInfo
- Publication number
- WO2007015343A1 WO2007015343A1 PCT/JP2006/313110 JP2006313110W WO2007015343A1 WO 2007015343 A1 WO2007015343 A1 WO 2007015343A1 JP 2006313110 W JP2006313110 W JP 2006313110W WO 2007015343 A1 WO2007015343 A1 WO 2007015343A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- adhesive sheet
- hole
- pressure
- sensitive adhesive
- base material
- Prior art date
Abstract
Description
Claims