Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/22—Esters containing halogen
  • C08F220/24—Esters containing halogen containing perhaloalkyl radicals
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/06—Ethers; Acetals; Ketals; Ortho-esters
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/10—Esters; Ether-esters
  • C08K5/101—Esters; Ether-esters of monocarboxylic acids
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D133/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Coating compositions based on derivatives of such polymers
  • C09D133/04—Homopolymers or copolymers of esters
  • C09D133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
  • C09D133/16—Homopolymers or copolymers of esters containing halogen atoms
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
  • C09J133/04—Homopolymers or copolymers of esters
  • C09J133/14—Homopolymers or copolymers of esters of esters containing halogen, nitrogen, sulfur or oxygen atoms in addition to the carboxy oxygen
  • C09J133/16—Homopolymers or copolymers of esters containing halogen atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
  • C08F220/1804—C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31855—Of addition polymer from unsaturated monomers

Definitions

• the present invention relates to compositions containing a photosensitive fluorochemical polymer and uses thereof.
• Fluorochemical acrylates have been used for surface protection.
• fluorochemical polyacrylates have been used as anti-graffiti or easy-clean coating for signs or displays and release coatings for use on release liners used to protect pressure-sensitive adhesive tapes from self-adherence.
• Such coatings typically also included inorganic fillers to improve abrasion resistance of the coatings.
• fluorochemical acrylates that have been used in such applications include those derived from poly-(hexafluoropropylene oxide), poly(difluoromethylene oxide-co-tetrafluoroethylene oxide), and N-methyl perfluorobutanesulfonamidoethyl acrylate.
• fluorochemical acrylates that have been used for surface protection have had poor adhesion to the substrate, have cured incompletely, and have been incompatible with conventional crosslinkers. Others are effective for their intended purpose, but are expensive to manufacture or difficult to use in a coatings manufacturing process.
• the invention provides a fluorochemical composition
• a fluorochemical composition comprising a mixture of: (A) fluorochemical copolymer selected from the formula:
• RF is a fluorinated group having the formula: R f - W-, wherein Rf is a perfluoroalkyl or perfluoropolyether group and W is a divalent linking group;
• PI is a monovalent pendant organic moiety comprising benzophenone, substituted benzophenone, acetophenone, or substituted acetophenone groups;
• R is H, CH 3 , or F;
• Rh is lower alkyl selected from the group consisting of linear or branched alkyl groups having from 1 to about 8 carbon atoms, cycloalkyl-containing alkyl groups having from 4 to about 8 carbon atoms, and cycloalkyl groups having from 3 to about 8 carbon atoms, all optionally containing catenated O or N atoms; m is at least 2; n is at least 1 ; q is zero or greater; and
• the invention provides an article comprising: a polymeric substrate; and a fluorochemical composition on a surface of the substrate wherein the fluorochemical composition comprises fluorochemical having the above formula.
• the invention provides fluorochemical copolymer composition comprising: a fluorochemical selected from the formula:
• RF is a fluorinated group having the formula: R f - W-, wherein R f is a perfluoropolyether group and W is a divalent linking group;
• PI is a monovalent pendant organic moiety comprising benzophenone, substituted benzophenone, acetophenone, or substituted acetophenone groups;
• R is H, CH 3 , or F;
• Rh is lower alkyl selected from the group consisting of linear or branched alkyl groups having from 1 to about 8 carbon atoms, cycloalkyl-containing alkyl groups having from 4 to about 8 carbon atoms, and cycloalkyl groups having from 3 to about 8 carbon atoms; m is at least 2; n is at least 1 ; q is zero or greater.
• the invention provides fluorochemical copolymer composition
• a fluorochemical selected from the formula:
• RF is a fluorinated group having the formula: R f W-, wherein R f is a perfluoroalkyl group and W is a divalent linking group;
• PI is a monovalent pendant organic moiety comprising benzophenone, substituted benzophenone, acetophenone, or substituted acetophenone groups;
• R is H, CH 3 , or F;
• Rh is lower alkyl selected from the group consisting of linear or branched alkyl groups having from 1 to about 8 carbon atoms, cycloalkyl-containing alkyl groups having from 4 to about 8 carbon atoms, and cycloalkyl groups having from 3 to about 8 carbon atoms; m is at least 2; n is at least 1 ; q is zero or greater, wherein n/(n+m+q) is less than 0.1.
• This invention describes a class of fiuorochemical acrylic copolymers bearing pendant groups comprising benzophenone, substituted benzophenone, acetophenone, or substituted acetophenone moieties which can generate free radicals upon irradiation with ultraviolet light sources. These copolymers are useful for generation of bound fiuorochemical coatings on a range of substrates, particularly polymer films.
• the invention also includes a method for use of these materials and generation of coated articles. Specifically, the invention relates to compositions, articles, and methods containing or using fluorochemicals selected from the Formula I:
• RF is a fluorinated group having the formula: Rr W-, wherein R f is a perfluoroalkyl or perfluoropolyether group and W is a divalent linking group;
• PI is a monovalent pendant organic moiety comprising benzophenone, substituted benzophenone, acetophenone, or substituted acetophenone groups;
• R is H, CH 3 , or F;
• Rh is lower alkyl selected from the group consisting of linear or branched alkyl groups having from 1 to about 8 carbon atoms, cycloalkyl-containing alkyl groups having from 4 to about 8 carbon atoms, and cycloalkyl groups having from 3 to about 8 carbon atoms, and all optionally containing catenated O or N atoms; m is at least 2; n is at least 1 ; and q is zero or greater.
• R f is a perfluoroalkyl group and n/(n+m+q) is less than 0.1, 0.075, 0.05, 0.025, 0.01, or any number less than 0.1 and greater than 0.
• the perfluorinated group R f can be linear, branched, cyclic, or combinations thereof. If R f is a perfluoroalkyl group, it contains from 1 to 18 carbon atoms and can optionally contain one catenated O or N atom. IfR f is a perfluoropolyether group, it has at least two catenated oxygen heteroatoms.
• Exemplary perfluoropolyethers include, but are not limited to, those that have perfluorinated repeating units selected from the group of -(CpF 2p )-, -(C p F 2p O)-, -(CF(X))-, -(CF(X)O)-, -(CF(X)C p F 2p O)-, -(C p F 2p CF(X)O)-, -(CF 2 CF(X)O)-, or combinations thereof.
• p is typically an integer of 1 to 10. In some embodiments, p is an integer of 1 to 8, 1 to 6, 1 to 4, or 1 to 3.
• the X group is a perfluoroalkyl group, perfluoroether group, perfluoropolyether, or a perfluoroalkoxy group, all of which can be linear, branched, or cyclic.
• the X group typically has no more than 12 carbon atoms, no more than 10 carbon atoms, or no more than 9 carbon atoms, no more than 4 carbon atoms, no more than 3 carbon atoms, no more than 2 carbon atoms, or no more than 1 carbon atom.
• the X group can have no more than 4, no more than 3, no more than 2, no more than 1, or no oxygen atoms.
• the different repeat units can be distributed randomly along the chain.
• R is desirably monovalent.
• Exemplary perfluoroalkyl groups include CF 3 -, CF 3 CF 2 -, CF 3 CF 2 CF 2 -, (CF 3 ) 2 CF-, CF 3 CF 2 CF 2 -, CF 3 OCF 2 CF 2 -, and (CF 3 ) 2 NCF 2 CF 2 -.
• the inert terminal groups can be (CpF 2p+ i)-, (CpF 2p+ i0)-, (X'C p F 2p O)-, or (X'C p F 2P+ i)- where X' is hydrogen, chlorine, or bromine and p is an integer of 1 to 10.
• monovalent perfluoropolyether R f groups the terminal group is perfluorinated and p is an integer of 1 to 10, 1 to 8, 1 to 6, 1 to 4, or 1 to 3.
• Exemplary monovalent perfluoropolyether R f groups include C 3 F 7 O(CF(CF 3 )CF 2 O) n CF(CF 3 )- , C 3 F 7 O(CF 2 CF 2 CF 2 O) n CF 2 CF 2 -, and CF 3 O(C 2 F 4 O) n CF 2 - wherein n has an average value of 0 to 50, 1 to 50, 3 to 30, 3 to 15, or 3 to 10.
• n has an average value of about 5 to 6.
• perfluoropolyether group-containing compounds according to Formula I can include a mixture of Rf groups.
• the average structure is the structure averaged over the mixture components.
• the values of n in these average structures can vary, as long as the perfluoropolyether group has a number average molecular weight of at least about 400.
• Compounds of Formula I often have a molecular weight (number average) of 400 to 5000, 800 to 4000, or 1000 to 3000.
• Linking group W can be unsubstituted or substituted with an alkyl, aryl, halo, or combinations thereof.
• the W group typically has no more than 30 carbon atoms.
• the W group has no more than 20 carbon atoms, no more than 10 carbon atoms, no more than 6 carbon atoms, no more than 4 carbon atoms, or no more than 1 carbon atom.
• W can be an alkylene, an alkylene substituted with an aryl group, or an alkylene in combination with an arylene.
• W groups include, but are not limited to, difunctional groups: -C(O)NH(C k H 2k )-, -SO 2 NR(C k H 2k )-, -(CjH 2j ) S -CH(R,)-; -CH 2 O(C k H 2k )-,
• Examples of specific linking groups (W) are -C(O)NH(CH 2 ) 2 -, -CH 2 -, -CH 2 O(CH 2 ) 3 -, and -CH 2 OC(0)N(R)(CH 2 ) 2 .
• a UV-absorbing group such as benzophenone or acetophenone or substituted derivatives.
• exemplary of this class are 4-(acryloxy)benzophenone, 4- (acryloxy)acetophenone, 2-(acrylamido)acetophenone, and 4- (acryloxyethoxy)benzophenone, all described by Kellen and Taylor in U.S. Pat. No. 4,847,137 as crosslinkers for acrylic adhesives.
• Lower alkyl acrylates optionally useful in making the polymers of the invention include C 1 to C 8 acrylates and methacrylates, which can further contain catenary O or N atoms.
• Exemplary of such lower alkyl acrylates are butyl acrylate, dimethylaminoethyl methacrylate, and ethoxy ethyl acrylate.
• Such alkyl acrylates may be optionally added in small amounts, for example, 5 weight percent or less, to the predominately fluorochemical composition.
• the polymers of the invention are conveniently made by thermal initiation of radical polymerization of the monomer mixtures in solution, although they could also be made by emulsion or suspension techniques.
• Useful compositions contain predominantly the fluoromonomer (generally 85 to 99% by weight on a total solids basis, 1-5% by weight (total solids) of the photoinitiator monomer, and, if present, up to 10% by weight (total solids) of the alkyl acrylate monomer). Allowed values of ratios relating the subscripts m, n, and q in Formula I are such as to be consistent with the abovementioned weight percents of the various comonomers.
• thermal initiators include "azo” compounds such as VAZO 67 thermal initiator available from DuPont, Wilmington, DE, and "peroxy” compounds such as ammonium persulfate.
• the polymeric product solution can be diluted further with a solvent such as an HFE, usually to 0.2 to 2% concentration by weight, and coated or sprayed onto a substrate which contains aliphatic C-H bonds, such as polyethylene terephthalate, amine-primed polyethylene terephthalate, polycarbonate, trimethylolpropanetriacrylate (TMPTA) and pentaerythritol tetraacrylate (PETA)-based hardcoats such as described by Bilkadi and May et al. in U.S. Pat. No.
• a solvent such as an HFE, usually to 0.2 to 2% concentration by weight
• HFEs Hydrofluoroethers
• HFEs suitable for use as a solvent in preparing and in coating compositions of the invention are generally low polarity chemical compounds minimally containing carbon, fluorine, hydrogen, and catenary (that is, in-chain) oxygen atoms. HFEs can optionally contain additional catenary heteroatoms, such as nitrogen and sulfur.
• HFEs have molecular structures that can be linear, branched, or cyclic, or a combination thereof (such as alkylcycloaliphatic), and are preferably free of ethylenic unsaturation, having a total of about 4 to about 20 carbon atoms. Such HFEs are known and are readily available, either as essentially pure compounds or as mixtures.
• hydrofluoroethers can have a boiling point in the range from about 30 0 C to about 275 0 C, and in other embodiments, from about 50 0 C to about 200 °C, and in other embodiments, from about 50 0 C to about 110 °C. While a wide variety of HFE's are described by Flynn et al. in U.S. Pat. No.
• HFE's generally do not alter the surface appearance of the polymeric substrates being coated with the polymers of this invention.
• the polymer/HFE coated surface is allowed to dry and then is subjected to UV irradiation, such as in a model MC-6RQN photoprocessor commercially available from Fusion UV Systems Inc., Gaithersburg, MD. Irradiation can be done under an inert atmosphere, such as nitrogen, or for some substrates, under air.
• the cured product typically has a small residue of uncured polymer which can be left or removed by solvent rinse or by buffing with a dry fabric.
• the surface has an abrasion-resistant fluorochemical topcoat, evidenced by de- wetting of oil and water and by easy release of adhesive tape with minimal decrease in re-adhesion values.
• Methyl t- butyl ether (MTBE, 200 mL) was added to the reaction mixture and the organic phase was extracted twice with water/HCl (about 5%) to remove unreacted amine and methanol. The MTBE layer was dried with MgSO 4 . The MTBE was removed under reduced pressure to yield a clear, viscous liquid.
• Polymers were made by charging a bottle with the monomers and solvent(s) indicated, in the amounts indicated in Table 1 below, with VAZO 67, purging the bottles with nitrogen for about 35 seconds, and then heating the bottles at 60 0 C in a rotating water bath for about 24 hours.
• the amounts of VAZO 67 used was as follows: Example 1 : 0.6 weight percent; Examples 3-14: 0.3 weight percent.
• the above polymers were coated with a #8 Meyer rod at 6 to 25% concentration on an unprimed PET sheet (commercially available from 3M Company), and were irradiated in a mercury lamp UV photoprocessor.
• the resulting films were either rubbed with paper wipe or rinsed with HFE to remove any unbound polymer.
• Example 4 showed good bonding when coated at 2% and 0.2% concentrations, with less excess material noted at the 0.2% level.
• the polymer solution prepared by dilution of the copolymer from Example 1 was applied to a commercially available matte hardcoated PET film substrate obtained from U.S.A. Kimoto Tech, Cedartown, GA under the trade designation "N4D2A" (S-2).
• the matte film was used without further modification.
• the solution was applied to the hardcoated film using a metered, precision die coating process.
• a flow meter was used to monitor and set the flow rate of the material from a pressurized container. The flow rate was adjusted by changing the air pressure inside the sealed container which forces liquid out through a tube, through a filter, the flow meter and then through the die.
• a syringe pump was used to meter the solution into the die.
• the solution was diluted to a concentration of 2 wt % solids as indicated above and coated onto the hardcoat to achieve a nominal dry thickness of 60 run.
• the material was dried in a conventional air flotation oven and then sent through a UV chamber having less than 50 ppm oxygen.
• the UV chamber was equipped with a 600 watt H-type bulb from Fusion UV systems, Gaithersburg, MD, operating at full power.
• a sample of the coating was rinsed with HFE 7100 to remove unbound coating material, then tested according to the ink beading test and found to give dewetting of the ink into hemispherical droplets.
• the ink test was repeated after subjecting the coating to 250 and 500 wipes in the steel wool test under a 1 kg weight. Unchanged ink beading and no scratching were observed after 250 wipes, and partial ink beading and slight scratching were observed after 500 rubs, demonstrating mechanical durability of the fluorochemical coating. Water static/advancing/receding contact angles were measured on the fresh coating sample after rinsing and found to be 116/121/106 degrees.
• the abrasion resistance of coatings was tested cross- web to the coating direction by use of a mechanical device capable of oscillating steel wool fastened to a stylus (by means of a rubber gasket) across the film's surface.
• the stylus oscillated over a 10 cm wide sweep width at a rate of 3.5 wipes/second wherein a "wipe" is defined as a single travel of 10 cm.
• the stylus had a flat, cylindrical geometry with a diameter of 6 mm.
• the device was equipped with a platform on which weights were placed to increase the force exerted by the stylus normal to the film's surface.
• the steel wool was obtained from Rhodes- American a division of Homax Products, Bellingham, WA under the trade designation "#0000-Super-Fine" and was used as received. A single sample was tested for each example, specifying the weight in grams applied to the stylus and the number of wipes employed during testing.
• Polymers were made by charging a bottle with the monomers and solvent(s) indicated, in the amounts indicated in Table 1 below, with VAZO 67, purging the bottles with nitrogen for about 35 seconds, and then heating the bottles at 60 0 C in a rotating water bath for about 24 hours, except example 20 and 22 were held for about 48 hours.
• the amounts of VAZO 67 used were as follows: Examples 15-18 0.080 g; Examples 19 - 22 0.030 g.
• Examples 15-22 were diluted to 2% by weight solids with HFE and coated using a
• the coatings were rinsed for 1 minute by hand agitation in IPA before being subjected to measurement of water contact angles. Measurements were made using deionized water filtered through a filtration system obtained from Millipore Corporation (Billerica, MA), on a video contact angle analyzer available as product number VCA- 2500XE from AST Products (Billerica, MA). Reported values are the averages of measurements on at least three drops measured on the right and the left sides of the drops, and are shown in Table 4. Drop volumes were 5 ⁇ L for static measurements and 1-3 ⁇ L for advancing and receding.
• the release value is a quantitative measure of the force required to remove a flexible adhesive tape from a substrate coated with the test composition at a specific angle and rate of removal. In the following examples, this force is expressed in g/in.
• release testing was conducted by laminating a 2.54 cm by 20.32 cm strip of the coated substrate (coated side up) to the stage of a slip/peel tester SP 2000, available from I-Mass Instruments, Accord, MA, with double coated tape.
• a 1.91 cm by 15.24 cm strip of a pressure-sensitive adhesive (PSA) coated test tape was rolled down onto the laminate thus formed with a 2 kg rubber roller. The average force required to remove this tape at 180 degrees and a peel rate of 90 in/min (228.6 cm/minute) is reported in Table 5. Three samples were measured for each example.
• Readhesion was also measured by adhering the freshly peeled tape to a clean glass plate and measuring the peel adhesion in normal fashion using an SP-2000 slip/peel tester indicated above, again peeling at 90 in/min (228.6 cm/min) and at a 180° peel angle. Readhesions are reported as a percentage of the average force required to remove the sample from a clean glass plate versus the force required to remove a control tape sample from a clean glass plate that has not been adhered to the release coating. Comparative Example C-I is 3M 610 tape, available from 3M Company. Three samples were measured for each example.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Polymers & Plastics (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Materials Engineering (AREA)
• Wood Science & Technology (AREA)
• Engineering & Computer Science (AREA)
• Life Sciences & Earth Sciences (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Paints Or Removers (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Laminated Bodies (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=36190705

Family Applications (1)

Country Status (10)

Cited By (6)

Families Citing this family (19)

Citations (4)

Family Cites Families (27)

• 2005
  • 2005-12-23 US US11/317,682 patent/US7682771B2/en not_active Expired - Fee Related
  • 2005-12-28 CN CN2005800455491A patent/CN101107280B/zh not_active Expired - Fee Related
  • 2005-12-28 EP EP20050855894 patent/EP1833862B1/en not_active Expired - Lifetime
  • 2005-12-28 AT AT05855894T patent/ATE423150T1/de not_active IP Right Cessation
  • 2005-12-28 RU RU2007123778/04A patent/RU2007123778A/ru unknown
  • 2005-12-28 JP JP2007549635A patent/JP5074207B2/ja not_active Expired - Fee Related
  • 2005-12-28 KR KR1020077017365A patent/KR101290491B1/ko not_active Expired - Fee Related
  • 2005-12-28 WO PCT/US2005/047403 patent/WO2006071981A1/en not_active Ceased
  • 2005-12-28 ES ES05855894T patent/ES2321537T3/es not_active Expired - Lifetime
  • 2005-12-28 DE DE200560012868 patent/DE602005012868D1/de not_active Expired - Lifetime

Patent Citations (4)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events