  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/10—Homopolymers or copolymers of propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/06—Polyethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/16—Ethene-propene or ethene-propene-diene copolymers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/03—Polymer mixtures characterised by other features containing three or more polymers in a blend
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/08—Copolymers of ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/04—Homopolymers or copolymers of ethene
  • C08L23/08—Copolymers of ethene
  • C08L23/0807—Copolymers of ethene with unsaturated hydrocarbons only containing four or more carbon atoms
  • C08L23/0815—Copolymers of ethene with unsaturated hydrocarbons only containing four or more carbon atoms with aliphatic 1-olefins containing one carbon-to-carbon double bond

Definitions

• the present invention is directed to a polypropylene composition having improved scratch resistance properties.
• the present invention is characterized in that the polypropylene composition comprises: (i) 30 -97 wt.% of a polypropylene (PP);
• polypropylene composition has an excellent combination of properties such as for example impact resistance, elongation at break, modulus and dimensional stability.
• composition according to the present invention can be injection moulded at a high injection rate while the moulded part thus obtained does not exhibit (or at least exhibits them to a strongly reduced extent) surface defects in the form of a stripe or a pattern.
• the polypropylene in the composition according to the invention may be a homopolymer as well as a copolymer, particularly all kinds of reactor copolymers, for instance block copolymers (blends of a homopolymer and a rubber, for instance an EPR rubber) may be used.
• polypropylene are commercially available and they can be readily prepared by methods well known and extensively described in the art using for instance conventional Ziegler-Natta catalysts as well as single site catalysts, for instance metallocene catalysts. Of course, also mixtures of different types of polypropylene can be used.
• the MFI of the polypropylene may range between wide limits, for instance between a lower limit of 0.1 g/10min and an upper limit of 100 g/10min.
• the lower limit is 10 g/10min and more preferably the lower limit is 20 g/10min.
• the polypropylene homopolymer has an isotactic structure, which means that the isotacticity is high, for instance higher than 95% and preferably higher than 98%.
• the propylene is a copolymer of propylene and of an olefin other than polypropylene.
• the olefin other than propylene may be for instance an ⁇ -olefin, in particular 1-alkene having for instance 2 or 4-20 C-atoms or cyclic olefins, optionally containing more than one ring, having a double bond in the ring structure.
• suitable olefins include ethylene, butene, hexene, styrene, cyclopentene and/or norbornadiene.
• the ⁇ -olefin is a 1-alkene having 2 or 4-8 C-atoms.
• the ⁇ -olefin is ethylene.
• the composition comprises 60- 80wt% polypropylene.
• the polypropylene may contain rubber.
• the polypropylene composition may comprise in an amount of, for instance, 0-30 wt.% of a rubber, preferably 5-20 wt.%, with a comonomer content of, for instance 10 -70 wt.%, preferably 30 -65 wt.%.
• the rubber is an ethylene propylene rubber (EPR rubber).
• EPR rubber ethylene propylene rubber
• the EPR rubber has an ethylene content of, for instance 20 -70% and more preferably of 50 -65 wt.%.
• the polypropylene may also contain a modified polypropylene.
• suitable modified polypropylenes are polypropylenes grafted with for instance an unsaturated organic compound, for instance a carboxylic acid, an anhydride, an ester, or salts thereof or maleic, fumaric, (meth)acrylic, itaconic or cinnamic acid or anhydride, ester or salt thereof.
• maleic anhydride is used.
• the amount of modified polypropylene may vary within wide limits. For economical reasons the amount normally will be rather low, for instance lower than 10 wt.%, preferably 0-3 wt.% modified polypropylene calculated with respect to the total amount of polypropylene.
• composition according to the invention contains 2-20 wt.% long- chain branched low density polyethylene (LDPE).
• LDPE long- chain branched low density polyethylene
• the composition contains 5-15 wt.% long- chain branched low density polyethylene.
• Long-chain branching describes the configuration of the polymer molecule possessing side chains with a degree of polymerization of the same order as that of the main chain.
• the density of the polyethylene ranges between 910 kg/m 3 and 935 kg/m 3 and the melt index ranges between 0.10 dg/minute and 100 dg/minute preferably between 8 to 80 g/10min (the MFI is measured in accordance with ISO 1133 using a 2.16 kg weight and at a temperature of 19O 0 C).
• the density of the polyethylene ranges between 915 kg/m 3 and 935 kg/m 3
• the melt index of the polyethylene ranges between 50 and 70 g/10min.
• composition according to the invention comprises 1-20 wt.% of a copolymer of ethylene and a C 3 -C 20 ⁇ -olefin.
• the copolymer of ethylene and a C 3 -C 20 ⁇ -olefin has a density between 840 and 890 kg/m 3 '
• the MFI of the copolymer of ethylene and a C 3 -C 20 ⁇ -olefin is between 0.1 and 100 g/10min (measured in accordance with ISO 1133 using a 2.16 kg weight and at a temperature of 190 0 C).
• the density of the copolymer of ethylene and a C 3 -C 20 ⁇ - olefin is between 860 and 880 kg/m 3 .
• the MFI of the copolymer of ethylene and a C 3 -C 20 ⁇ -olefin is between 0.1 and 10 g/10min. - A -
• composition according to the invention may comprise a mixture of copolymers of ethylene and a C 3 -C 2O ⁇ -olefin.
• the polypropylene composition according to the invention comprises 1-18 wt.% of the copolymer of ethylene and a C 3 -C 20 ⁇ -olefin.
• the polypropylene composition comprises 5-15 wt.% of the copolymer of ethylene and a C 3 -C 20 ⁇ -olefin.
• Suitable fillers include for example talc, glass beads, glass fibers, clay, mica, wollastonite, calcium carbonate, silica, carbon black and/or titanium oxide. According to a preferred embodiment of the invention the filler is talc, glass fiber or carbon black.
• the amount of filler in the polypropylene composition according to the invention is between 0,5 and 60 wt.%. Fillers amounts above 40 wt.% will normally be present in mixtures of a homopolymer of polypropylene and filler or in concentrates (i.e. compositions that normally will be mixed with other compositions before being further processed, for instance moulded).
• compositions used for further processing into articles preferably contain for instance more than 1 wt.% filler, particularly more than 2 wt.% filler, most preferably more than 5 wt.% filler and less than 45 wt.% filler, particularly less than 30 wt.% filler, most preferably less than 20 wt.% filler.
• the composition according to the invention comprises in addition to said components a slip agent.
• the amount of slip agent to be used may range between wide limits, for instance between 0 and 3 wt.%.
• the amount of slip agent ranges between 0.1 and 1 wt.%, calculated with respect to the polypropylene composition.
• Suitable slip agents include for example fatty acid amides and/or polysiloxanes.
• Suitable fatty acid amides are for instance saturated and unsaturated amides or saturated and unsaturated alkylenebisamides.
• suitable amides include palmitamide, stearyl araffleamide, stearamideoethylstearamide, stearamidoethylpalmitamide, erucamide, oleamide, erucamidoethylerucamide, stearamidoethylerucamide and/or oleoamidoethylerucamide.
• the slip agent is a fatty acid amide.
• composition according to the invention may optionally contain additives, for instance nucleating agents and clarifiers, stabilizers, release agents, fillers, plasticizers, anti-oxidants, colorants, ignition resistant additives, lubricants, mold releases, flow enhancers and/or antistatics.
• additives for instance nucleating agents and clarifiers, stabilizers, release agents, fillers, plasticizers, anti-oxidants, colorants, ignition resistant additives, lubricants, mold releases, flow enhancers and/or antistatics.
• additives are well known in the art and the skilled person will select the type and amount of additives such that they do not detrimentally influence the aimed properties of the composition.
• the amount of additives may vary between wide limits, for instance from 0 up to 20 wt.%, particularly between 1 and 10 wt.%, calculated with respect to the polypropylene composition.
• the propylene copolymer composition according to the invention is suitable to be used for instance in blow molding, injection molding or extrusion of moldings, films, sheets or pipes to be applied in a wide range of articles such as for instance, exterior and interior automotive parts, especially esthetic (non painted visible) parts, such as for example bumper beams, bumper fascia, instrument panels and pillars, thin wall packaging, caps and closures, pails and containers, crates and boxes, cans and bottles, appliance housings, houseware, toys, multi-media packaging, electrical applications, for example electrical equipment housing, lawn and garden furniture and construction sheet.
• esthetic (non painted visible) parts such as for example bumper beams, bumper fascia, instrument panels and pillars, thin wall packaging, caps and closures, pails and containers, crates and boxes, cans and bottles, appliance housings, houseware, toys, multi-media packaging, electrical applications, for example electrical equipment housing, lawn and garden furniture and construction sheet.
• the propylene copolymer composition according to the invention is very suitable to be applied in visible interior automotive parts such as for example instrument panels and pillars.
• compositions according to the invention may be performed according to any suitable mixing procedure.
• suitable mixing procedure such as for example dry blending the individual components, optionally followed by melt mixing, and subsequently extrusion or directly injection moulding.
• a composition was obtained by compounding the ingredients according to Table 1 at 210 0 C in a co-rotating twin-screw extruder. The composition was then injection moulded into plates of 65 x 65 x 3.2 mm according to ISO 37-2. The appropriate samples were machined out of the plates. The test results are given in Table 1. The amounts used are given in wt.% calculated with respect of the total composition.
• Example I was repeated except that LDPE was replaced by HDPE.
• the test result shows that the specific combination of the branched low density polyethylene and the copolymer of ethylene and a C 3 -C 2O ⁇ -olefin in the polypropylene composition enhances the scratch resistance.
• the scratch resistance was measured according to the VW PV 3952 scratch method with a load of 1ON using VW texture K59. (VW means Volkswagen)
• the colour of the scratch was measured relative to the unscratched surface.
• the colour was measured according to ISO 7724 (1984).
• the resulting value dl_ is a measure for the scratch resistance because a low dl_ value corresponds to a high scratch resistance.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=34928748

Family Applications (1)

Country Status (9)

Cited By (4)

Families Citing this family (13)

Citations (3)

Family Cites Families (7)

• 2005
  • 2005-11-30 JP JP2007545886A patent/JP4842277B2/ja not_active Expired - Fee Related
  • 2005-11-30 EP EP05814250A patent/EP1824929B1/en not_active Expired - Lifetime
  • 2005-11-30 ES ES05814250T patent/ES2322281T3/es not_active Expired - Lifetime
  • 2005-11-30 AT AT05814250T patent/ATE426637T1/de not_active IP Right Cessation
  • 2005-11-30 DE DE602005013569T patent/DE602005013569D1/de not_active Expired - Lifetime
  • 2005-11-30 WO PCT/EP2005/012947 patent/WO2006063698A1/en not_active Ceased
  • 2005-11-30 US US11/793,115 patent/US7888423B2/en not_active Expired - Fee Related
  • 2005-11-30 CN CN2005800432540A patent/CN101080460B/zh not_active Expired - Fee Related
  • 2005-11-30 KR KR1020077015440A patent/KR101224331B1/ko not_active Expired - Fee Related

Patent Citations (3)

Also Published As

Similar Documents

Legal Events