WO2006054716A1 - Mousse en resine de propylene extrudee - Google Patents

Mousse en resine de propylene extrudee Download PDF

Info

Publication number
WO2006054716A1
WO2006054716A1 PCT/JP2005/021283 JP2005021283W WO2006054716A1 WO 2006054716 A1 WO2006054716 A1 WO 2006054716A1 JP 2005021283 W JP2005021283 W JP 2005021283W WO 2006054716 A1 WO2006054716 A1 WO 2006054716A1
Authority
WO
WIPO (PCT)
Prior art keywords
propylene
extruded foam
based resin
polymer
extruded
Prior art date
Application number
PCT/JP2005/021283
Other languages
English (en)
Japanese (ja)
Inventor
Minoru Sugawara
Yasuhiko Otsuki
Motoki Yamada
Ryoichi Tsunori
Original Assignee
Prime Polymer Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Prime Polymer Co., Ltd. filed Critical Prime Polymer Co., Ltd.
Priority to JP2006545177A priority Critical patent/JPWO2006054716A1/ja
Publication of WO2006054716A1 publication Critical patent/WO2006054716A1/fr

Abstract

L’invention concerne une résine de propylène extrudée pouvant avoir un diamètre cellulaire moyen réduit tout en conservant un rapport d’expansion accru et présentant ainsi une excellente performance d’isolation thermique et une performance satisfaisante d’amortissement des vibrations. La mousse en résine de propylène extrudée est obtenue par extrusion-moussage d’une résine de propylène. La résine de propylène constituant la mousse extrudée comprend un polymère oléfinique dont le facteur de dissipation (tanδ) déterminé à une température de 298 K et à une fréquence de 10 Hz varie de 0,04 à 100. La mousse présente un taux d’expansion de 10 ou plus et un diamètre cellulaire moyen inférieur à 400 µm. En raison de sa constitution, la mousse en résine de propylène extrudée combine une excellente performance d’isolation thermique et une excellente performance d’amortissement des vibrations.
PCT/JP2005/021283 2004-11-19 2005-11-18 Mousse en resine de propylene extrudee WO2006054716A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2006545177A JPWO2006054716A1 (ja) 2004-11-19 2005-11-18 プロピレン系樹脂押出発泡体

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2004-336681 2004-11-19
JP2004336681 2004-11-19

Publications (1)

Publication Number Publication Date
WO2006054716A1 true WO2006054716A1 (fr) 2006-05-26

Family

ID=36407252

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2005/021283 WO2006054716A1 (fr) 2004-11-19 2005-11-18 Mousse en resine de propylene extrudee

Country Status (2)

Country Link
JP (1) JPWO2006054716A1 (fr)
WO (1) WO2006054716A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008302678A (ja) * 2007-06-11 2008-12-18 Asahi Fiber Glass Co Ltd 熱可塑性樹脂発泡体およびその製造方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07292147A (ja) * 1994-04-28 1995-11-07 Sekisui Chem Co Ltd ポリオレフィン系樹脂発泡体の製造方法
JPH0925354A (ja) * 1995-07-07 1997-01-28 Asahi Chem Ind Co Ltd ポリプロピレン系樹脂押出発泡細条集束体及びその製造方法
JP2001001384A (ja) * 1999-04-23 2001-01-09 Kanegafuchi Chem Ind Co Ltd ポリプロピレン系樹脂押出発泡細条集束体の製造方法
JP2002105256A (ja) * 2000-09-28 2002-04-10 Grand Polymer Co Ltd ポリプロピレン樹脂組成物およびそれから得られる発泡体
JP2003094504A (ja) * 2001-09-25 2003-04-03 Sumitomo Chem Co Ltd 多層発泡シートの製造方法
JP2004217755A (ja) * 2003-01-14 2004-08-05 Mitsui Chemicals Inc 発泡体

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH115860A (ja) * 1997-06-19 1999-01-12 Jsp Corp 無架橋ポリプロピレン系樹脂発泡シート

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07292147A (ja) * 1994-04-28 1995-11-07 Sekisui Chem Co Ltd ポリオレフィン系樹脂発泡体の製造方法
JPH0925354A (ja) * 1995-07-07 1997-01-28 Asahi Chem Ind Co Ltd ポリプロピレン系樹脂押出発泡細条集束体及びその製造方法
JP2001001384A (ja) * 1999-04-23 2001-01-09 Kanegafuchi Chem Ind Co Ltd ポリプロピレン系樹脂押出発泡細条集束体の製造方法
JP2002105256A (ja) * 2000-09-28 2002-04-10 Grand Polymer Co Ltd ポリプロピレン樹脂組成物およびそれから得られる発泡体
JP2003094504A (ja) * 2001-09-25 2003-04-03 Sumitomo Chem Co Ltd 多層発泡シートの製造方法
JP2004217755A (ja) * 2003-01-14 2004-08-05 Mitsui Chemicals Inc 発泡体

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008302678A (ja) * 2007-06-11 2008-12-18 Asahi Fiber Glass Co Ltd 熱可塑性樹脂発泡体およびその製造方法

Also Published As

Publication number Publication date
JPWO2006054716A1 (ja) 2008-06-05

Similar Documents

Publication Publication Date Title
WO2006054715A1 (fr) Mousse de resine de propylene extrudee et son procede de production
JP5280680B2 (ja) プロピレン系樹脂押出発泡複合体
EP1899415B1 (fr) Polymeres de propylene presentant une large distribution de masses moleculaires
KR102112981B1 (ko) 용융 강도 안정성이 증가한 장쇄 분지형 폴리프로필렌 조성물
JP4999462B2 (ja) プロピレン系樹脂押出発泡体
KR20190079656A (ko) 폴리올레핀 필름 조성물의 제조 방법 및 그로부터 제조된 필름
JP5202942B2 (ja) プロピレン系樹脂押出発泡体の製造方法
KR20190077520A (ko) 발포 용도의 폴리프로필렌 조성물
JP2018503731A (ja) 半結晶性ポリオレフィンおよびスルホニルアジドを含む組成物、結果的に得られるフォーム、およびそれを製造する方法
JP2007119760A (ja) プロピレン系重合体及び発泡成形体
JP5123659B2 (ja) プロピレン系樹脂押出発泡体及びプロピレン系樹脂押出発泡体の製造方法
WO2006054716A1 (fr) Mousse en resine de propylene extrudee
JP2008143147A (ja) プロピレン系樹脂押出発泡体およびその製造方法
JP5527153B2 (ja) 発泡用ポリフェニレンスルフィド系樹脂組成物および発泡成形体
KR20080023304A (ko) 넓은 분자량 분포를 갖는 프로필렌 중합체
JP2009299056A (ja) ポリプロピレン系射出発泡体、および、その製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KN KP KR KZ LC LK LR LS LT LU LV LY MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU LV MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2006545177

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 05806880

Country of ref document: EP

Kind code of ref document: A1