WO2005100638A1 - エッチング方法及びエッチング液 - Google Patents
エッチング方法及びエッチング液 Download PDFInfo
- Publication number
- WO2005100638A1 WO2005100638A1 PCT/JP2005/006871 JP2005006871W WO2005100638A1 WO 2005100638 A1 WO2005100638 A1 WO 2005100638A1 JP 2005006871 W JP2005006871 W JP 2005006871W WO 2005100638 A1 WO2005100638 A1 WO 2005100638A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- etching
- weight
- base film
- nitric acid
- Prior art date
Abstract
基板上に形成されたクロム、ニッケル、或いはクロム及び／又はニッケルを含む合金よりなる下地膜と、この下地膜の全面又は一部を被覆するように形成された貴金属又は貴金属合金よりなる上層膜との積層膜の、少なくとも下地膜をエッチングするに当たり、電触作用に起因するサイドエッチングを防止して所望のエッチングを行う。
基板上に形成されたクロム、ニッケル、或いはクロム及び／又はニッケルを含む合金よりなる下地膜と、この下地膜の全面又は一部を被覆するように形成された貴金属又は貴金属合金よりなる上層膜との積層膜の、少なくとも下地膜をエッチングするためのエッチング液であって、硝酸濃度３５重量％以上の水溶液からなるエッチング液と、このエッチング液を用いたエッチング方法。
Description
明 細 書
エッチング方法及びエッチング液
技術分野
[0001] 本発明は、エッチング方法及びエッチング液に係り、特に、基板上に形成されたク ロム、ニッケル、或いはクロム及び Z又はニッケルを含む合金よりなる下地膜と、この 下地膜の全面又は一部を被覆するように形成された貴金属又は貴金属合金よりなる 上層膜との積層膜の、少なくとも下地膜をエッチングするエッチング方法と、このため のエッチング液に関する。 背景技術
[0002] 半導体関連における Siウェハ基板や III/V族基板をベースにしたデバイス、液晶 関連でのガラス基板をベースとしたデバイス、ポリイミド材等の有機膜基板をベースと したデバイス、更にはシリカ及びアルミナ等をベースとしたセラミックス基板を用いた デバイスなど、各種のデバイス分野においては、以下の理由から、基板上に形成され た異種金属からなる積層膜を、電蝕によるサイドエッチングを防止しながらエッチング を行って配線又はバンプ等を形成する技術が要求されている。
[0003] 即ち、金属自体が固有に持つイオン化のし易さの指標であるイオンィ匕傾向順番表 示として、 K > Ca >Al >Ti > Cr>Ni >Mo > (H) >Cu>Ag >Pd >Pt >Au等の 順にイオン化し易いことが従来より知られている。ここで、水素（H)を挟んでイオンィ匕 傾向の大きい方 (左側）が卑金属、小さい方 (右側）が貴金属であり、電気抵抗が低く 電気の通り易い金属としてはアルミニウムを除いて一般的には貴金属が挙げられる。 しかし、貴金属は一般にシリコンやガラス基板とは密着性が悪い。従って、密着性が 良い金属よりなる下地膜を基板上に成膜し、この下地膜上に貴金属膜を形成するこ とが行われている。この下地膜に用いられる金属としては、シリコンやガラス基板に対 して密着性に優れた、モリブデン、ニッケル、クロム、チタンが知られており、このうち、 特にクロムやニッケルは取り扱い性に優れることから、広く採用されている。
[0004] しかし、クロムやニッケノレのような卑金属下地膜上に貴金属膜を形成した積層膜を エッチングしょうとすると、イオン化傾向の異なる金属が接触しているため電蝕作用が
起こり、卑金属下地膜のエッチング速度は、卑金属膜の単層膜をエッチングする場 合に比べて加速されてしまう。このため下地膜は非常に速くエッチングされ、急速な サイドエッチングを引き起こし、ひいては微細な配線やバンプ等パターンを精度良く 形成できなくなってしまう。つまり寸法安定性が悪化してしまう。
[0005] 金属同士が接触しない場合には急速なサイドエッチング現象は起こらないことから
、次のように推定される。貴金属膜と卑金属膜とが接触する積層膜では、局部電池が 生じ、卑金属がイオンィ匕し易くなつてエッチング液中に溶出するとともに、生じる電子 が貴金属側に移動するため、エッチング液中に溶出しない貴金属が触媒作用を生じ 、エッチング性に大きく影響が出るものと考えられる。
[0006] このような電蝕作用に起因する積層膜のエッチングにおけるサイドエッチングは、以 下のような問題を引き起こすため、良好なデバイスを形成し得ない。
(1) 積層膜を同時エッチングして積層膜よりなるバンプや配線等を形成する場合、 下地膜と上層膜とでエッチング速度が大きく異なり、下地膜のエッチング速度が上層 膜のエッチング速度よりも速いと、下地膜のアンダーカット（下地膜の方が上層膜より もエッチングの進行が速ぐ上層膜が庇状に突出した状態となる）が生じる。アンダー カットが生じた場合には、例えば、その後の絶縁膜による被覆が不十分となり、絶縁 耐圧不良を生じる恐れがある。逆に、上層膜のエッチング速度が下地膜のエッチング 速度よりも速いと、上層膜のサイドエッチングで下地膜の露出面積が大きくなり、導電 不良につながる。
(2) 下地膜上に上層膜力 なるバンプを形成し、バンプ間に表出した下地膜のみを 選択的にエッチングして積層膜よりなるバンプを形成する場合、下地膜のサイドエツ チングが進行し易いと、上記と同様にアンダーカットが形成される。
[0007] 従って、積層膜のエッチングに際しては、サイドエッチングを防止して所望のエッチ ングを行うことが必要となるが、上述の如ぐ特に、卑金属膜と貴金属膜との積層膜に あっては、電蝕作用によるエッチング速度の加速のために、サイドエッチングが起こり 易い。
[0008] 従来、電蝕作用に起因したエッチング速度の加速を防止するために、エッチング液 の添加剤について種々検討がなされている力 適当なエッチング液やエッチング方
法は提供されてレ、なレ、のが現状である。
発明の開示
発明が解決しょうとする課題
[0009] 従って、本発明は、基板上に形成されたクロム、ニッケル、或いはクロム及び/又は ニッケノレを含む合金よりなる下地膜と、この下地膜の全面又は一部を被覆するように 形成された貴金属又は貴金属合金よりなる上層膜との積層膜の、少なくとも下地膜を エッチングするに当たり、電触作用に起因するサイドエッチングを防止して所望のェ ツチングを行うためのエッチング液と、このエッチング液を用いたエッチング方法を提 供することを目的とする。
課題を解決するための手段
[0010] 本発明のエッチング方法は、基板上に形成されたクロム、ニッケノレ、或いはクロム及 び/又はニッケルを含む合金よりなる下地膜と、この下地膜の全面又は一部を被覆 するように形成された貴金属又は貴金属合金よりなる上層膜との積層膜のうち、少な くとも前記下地膜を、硝酸濃度 35重量％以上の水溶液からなるエッチング液を用い てエッチングする。本発明においては、酸化剤等の他の添加物を含む場合、硝酸濃 度はそれら全てを含めた水溶液に対しての濃度を言う。
[0011] 好ましくはエッチング液の硝酸濃度が 35〜70重量％であり。またさらに酸化剤を含 むことが好ましい。
[0012] 本発明のエッチング方法は、例えば上層膜が金、パラジウム、白金或いはこれらの 金属の 1以上を含む合金からなる膜である積層膜の下地膜を選択的にエッチングす る場合、エッチング液の酸化剤濃度を 0. 5〜： 12重量％とするのが好ましい。また、上 層膜が銅、銀或いはこれらの金属の 1以上を含む合金からなる膜であり、積層膜の下 地膜と上層膜とを同時エッチングする場合、酸化剤濃度を 0. 5〜6重量％とするのが 好ましい。
[0013] 本発明のエッチング液は、基板上に形成されたクロム、ニッケノレ、或いはクロム及び /又はニッケルを含む合金よりなる下地膜と、この下地膜の全面又は一部を被覆す るように形成された貴金属又は貴金属合金よりなる上層膜との積層膜のうち、少なくと も前記下地膜をエッチングするためのエッチング液であって、硝酸濃度 35重量％以
上の水溶液からなる。
[0014] なお本願にぉレ、て、貴金属とは金、銀、銅、ルテニウム、ロジウム、パラジウム、ォス ミゥム、イリジウム、及び白金を指し、卑金属とはこれら以外の金属を指す。
[0015] 本発明者らは鋭意検討の結果、酸化性酸はその濃度が高くなると酸化電位が高く なり、それに伴ってエッチング速度が速くなるのが一般的であるが、硝酸については 、硝酸濃度が 35重量％以上になると、酸化電位は高くなるにも拘わらずエッチング 速度は逆に遅くなる特異な性質があることを確認した。
[0016] さらに、クロム、ニッケル等からなる下地膜と貴金属からなる上層膜との積層膜を、 酸化剤を含む硝酸水溶液をエッチング液としてエッチングすると、硝酸濃度 35重量 %以上の領域では、エッチング速度はやや遅くなるものの電蝕作用が抑制され非常 に良好なエッチングが行われること、し力 通常使用される 35重量％以下の低硝酸 濃度の領域では、濃度上昇とともにエッチング速度は速くなるが電蝕作用の抑制は 見られないこと、を見いだし本発明に至った。
[0017] なお従来より、図 1に示す如ぐスズ (Sn)のエッチングにおける硝酸濃度とエツチン グ速度（重量ロス％)との関係から、エッチング液の硝酸濃度 35重量％が特異点とな り、硝酸濃度 35重量％まではエッチング速度が硝酸濃度に比例して上昇し、硝酸濃 度 35重量％以上ではエッチング速度が下降することが知られている（日本金属学会 誌 B14No4 (1950) p55 - 58 (C. A. 1952 7504)。また図 2に示す如く、石肖酸 濃度と酸化電位との関係において、硝酸濃度 35重量％付近までは酸化電位は対数 増加するが、 35重量％で酸化電位の上昇が頭打ちになることも知られている。特開 平 01— 086524号公幸 (USP5007984号）には、クロム月莫のノヽ。ターニング方法とし て、硝酸濃度 12. 6重量％ (2モル Zリットル)以上のエッチング液を用いることが提案 されている。し力、しいずれの文献にも、積層膜における電蝕作用によるサイドエツチン グの抑制を示唆する記述は全くなレ、。
[0018] このように硝酸濃度 35重量％を境に性質が変化する理由は明らかではないが、本 発明者らは以下のように推定する。
[0019] 通常、硝酸は水存在下で解離しており、水の量が増え硝酸が減るとともにエツチン グ速度は下がる。し力 硝酸がある程度高濃度になり相対的に水の量が少なくなると
、逆にイオン解離しにくくなつてしまうと考えられる。即ちこの領域では酸解離が律速 となりエッチング速度を制限するため、硝酸濃度を高めるほど (水が少なくなるほど） エッチング速度が下がるものと思われる。
[0020] そして硝酸にぉレ、ては、他の酸では見られなレ、硝酸特有の性質として、硝酸濃度 3 5重量％、水が 65重量％という、水の量がかなり多い領域でこの酸解離律速になるも のと推定される。
[0021] 他の酸であっても、酸濃度が非常に高く水の量がかなり少ない領域では同様の性 質を示す場合があり、例えば酢酸は 80重量％以上でこのような性質を示すようである 。しかし酸濃度が高いと、酸化剤等の添加剤が溶解できなくなってしまい実用が困難 になるため、硝酸が、比較的酸濃度が低い領域でこのような性質を示すことは非常に 重要である。
[0022] 硝酸は、高濃度領域ではイオン解離しにくくなる一方、硝酸同士が会合するなどし て有機物としての性質が強まると考えられる。このことは例えば、硝酸濃度 35重量％ 以上のエッチング液は樹脂等の有機物表面への濡れ性が向上し、樹脂がエッチング されやすくなる事実からも推測できる。
発明の効果
[0023] 本発明のエッチング方法及びエッチング液によれば、基板上に形成されたクロム、 ニッケノレ、或いはクロム及び/又はニッケルを含む合金よりなる下地膜と、この下地 膜の全面又は一部を被覆するように形成された貴金属又は貴金属合金よりなる上層 膜との積層膜のうち、少なくとも前記下地膜をエッチングするに当たり、電触作用に起 因するサイドエッチングを抑制して所望のエッチングを行うことができる。ひいては微 細パターンを精度良く形成でき、寸法安定性にも優れた被エッチング物を得ることが できる。
図面の簡単な説明
[0024] [図 1]スズ (Sn)のエッチングにおける硝酸濃度とエッチング速度（重量ロス％)との関 係を示すグラフである。
[図 2]硝酸濃度と酸化電位との関係を示すグラフである。
発明を実施するための最良の形態
[0025] 以下に本発明のエッチング液及びエッチング方法の実施の形態を詳細に説明する
[0026] 本発明において、積層膜が形成される基材の材質としては特に制限はなぐシリコ ン、ガラス、セラミック、ポリイミド等の樹脂等、基材に必要とされる強度などの性質を 備えたものであれば各種無機物及び有機物を用いうる。
[0027] このような基板上に形成される積層膜の下地膜は、クロム、ニッケノレ、或いはクロム 及び/又はニッケルを含む合金よりなる。例えばクロムとニッケルを含む合金としては ニクロムがある。下地膜がクロム及び Z又はニッケルと、それ以外の金属との合金より なる場合、合金中のクロム及び/又はニッケル含有量は 80重量％以上であることが 好ましレ、。特に好ましくは下地膜は、クロム単体又はニッケル単体、或いはクロム含有 量 20〜60重量％程度のクロム—ニッケル合金からなる。
[0028] このような下地膜上に形成される上層膜は、貴金属又は貴金属合金よりなる。本発 明において貴金属とは金、銀、銅、ルテニウム、ロジウム、パラジウム、オスミウム、イリ ジゥム、及び白金を指し、卑金属とはこれら以外の金属を指す。貴金属合金とは前記 貴金属群より選ばれる 1種または 2種以上を含む合金であり、貴金属と卑金属との合 金であってもよい。上層膜が貴金属と卑金属との合金である場合、上層膜中の貴金 属含有量は 80重量％以上であることが好ましい。特に好ましくは上層膜は、金、銀、 銅、パラジウム及び白金からなる群より選ばれる 1種または 2種以上を含む合金であ る。これらと卑金属との合金であってもよい。
[0029] 下地膜や上層膜の膜厚には特に制限はなぐ使用目的に応じて適宜決定すれば よレ、。一般には下地膜は 10nm〜200nm程度の厚さとする。上層膜は一般に 100η m〜10 x m程度の厚さとする力 好ましくは、形成すべきパターンが配線である場合 には上層膜の厚さは 100nm〜400nm程度、形成すべきパターンがバンプである場 合には上層膜の厚さは 1 μ m〜10 μ m程度とする。
[0030] 下地膜や上層膜は、本発明の効果を著しく損なわない限り、必要に応じてそれぞ れ複数層力もなつてもよい。また下地膜や上層膜の他にも、本発明の効果を著しく損 なわない限り、必要に応じて他の層を設けてもよい。
[0031] このような積層膜をエッチングするための本発明のエッチング液は、硝酸濃度が 35
重量％以上の水溶液からなる。本発明においては、酸化剤等の他の添加物を含む 場合、硝酸濃度はそれら全てを含めた水溶液に対しての濃度を言う。硝酸濃度が 35 重量％未満では電触抑制効果を得ることができず、サイドエッチングを十分に防止し 得ない。より好ましくは 37重量％以上とする。
[0032] エッチング液中の硝酸濃度は 35重量％以上であればよいが、硝酸濃度の上限は 通常 70重量％以下である。硝酸は水と最低共沸物を作るため、通常、蒸留精製法 では 70重量％を超える水溶液の調製は困難である。一般に、硝酸濃度 70重量％を 超えるものは発煙硝酸と称し、 NOxを多量に含む特殊なものであり、 NOxガスが常 温で発生し周辺機器の腐食が問題となることからエッチングには不適当である。
[0033] 硝酸濃度が高くなると、エッチング速度が遅くなる傾向があるため、エッチング速度 をできるだけ高めたい場合には、硝酸濃度を低めにするのが好ましい。また、硝酸濃 度が高いほど他の物質が溶解しに《なるため、酸化剤等の添加剤を加える場合に は硝酸濃度を低めにするのが好ましい。これらの観点から硝酸濃度の上限は 65重量 %以下とするのが好ましぐより好ましくは 60重量％以下とし、さらに好ましくは 57重 量％以下とする。
[0034] ただし、エッチング速度が多少落ちても電蝕抑制を重視する場合には、硝酸濃度を 高めにするのが好ましい。
[0035] 本発明のエッチング液は、エッチング効果を高めるため更に酸化剤を含むことが好 ましレ、。通常、酸化剤としてはエッチングすべき膜を構成する金属より酸化電位の高 レ、ものを用いる。本発明においては少なくとも下地膜を構成する金属より酸化電位の 高いものを用いるのが好ましい。酸化電位は pHにより多少変化する力 おおむね、 クロム下地膜では、酸化電位力 以上の酸化剤を、ニッケル下地膜では、酸化電位 が 0. 6V以上の酸化剤を用いるのが好ましい。
[0036] 下地膜がクロムよりなる場合には、 6価クロムイオン (重クロム酸イオン）の酸化電位 が高いので、酸化電位が IV以上の酸化剤を用いるのが好ましい。酸化剤の種類は 特に限定されないが、例えば、セリウム 4価イオンを含む化合物や過硫酸アンモニゥ ムが好適に用いられる。より好ましくはセリウム 4価イオンを含む化合物であり、化合物 の安定性、水への溶解性の点から特に好ましくは硝酸セリウムアンモニゥム (4価）（
硝酸セリウムアンモン (4価）とも称する。）である。硝酸セリウムアンモニゥム（4価）の 場合、酸化剤が還元されて生じる生成物も水溶性であることも好ましい理由である。 なお、過酸化水素や過マンガン酸塩は、酸性領域では 6価クロムイオンより酸化電位 が低レ、ので、クロム下地膜の酸化剤としては好ましくなレ、。
[0037] 下地膜がニッケルよりなる場合には、酸化電位が 0. 6V以上の酸化剤を用いるのが 好ましレ、。酸化剤の種類は特に限定されないが、例えば、セリウム 4価イオンを含む 化合物、過硫酸アンモニゥム、過マンガン酸塩等が好適に用いられる。より好ましくは セリウム 4価イオンを含む化合物であり、化合物の安定性、水への溶解性、還元生成 物の水への溶解性の点から特に好ましくは硝酸セリウムアンモニゥム（4価）である。
[0038] 下地膜がニクロムよりなる場合は、クロムを含むのでクロムの場合と同様に酸化剤が 選択使用できる。
[0039] なお硝酸は酸化剤としても酸としても作用する力 酸化剤共存下では酸としての作 用が強くなる。
[0040] 酸化剤の濃度は、酸化剤の飽和溶解度を上限として、本発明の効果が得られる範 囲であれば特に限定されないが、本発明においては硝酸濃度が高くなると硝酸セリ ゥムアンモニゥム (4価）の溶解度は小さくなるため、硝酸濃度と硝酸セリウムアンモニ ゥム濃度のバランスを考えて決めるのが好ましレ、。なお酸化剤の溶解度は酸化剤の 種類やエッチング液の濃度等により多少変動する。
[0041] 酸化剤の濃度は、酸化剤添加効果を十分発揮させるため、好ましくは 0. 5重量％ 以上とする。硝酸濃度 35重量％、液温約 20°Cにおける酸化剤の飽和溶解度は 12 重量％であるため、約 20°Cでの酸化剤の濃度は、通常、 12重量％以下とする。より 好ましくは 10重量％以下とする。従って、液温約 20°Cでは硝酸セリウムアンモニゥム (4価）濃度として好ましくは 0. 5重量％〜： 12重量％であり、より好ましくは 5〜： 10重 量％である。なお通常、液温を上げるほど飽和溶解度が高くなる傾向にあるので、好 ましい酸化剤濃度はより高めになる。ただし通常 20重量％以下である。また本発明 においては、エッチング対象とする膜の種類により酸化剤濃度を調整することが望ま しい。
[0042] 以下に、エッチング対象とする膜の種類と酸化剤濃度について説明する。
[1] クロムやニッケノレよりなる下地膜と、この下地膜を部分的に覆う、金、パラジウム 又は白金 (或いはこれらを主成分とする合金)よりなる上層膜との積層膜に対して、上 層膜間に表出する下地膜のみをエッチングする場合。
[0043] 本発明のエッチング液によれば、金、パラジウム又は白金（或いはこれらを主成分と する合金)よりなる上層膜を実質的に溶解しないので、上層膜の保護を考える必要が ない。すなわち本エッチング方法及びエッチング液によれば、下地膜のみを選択的 にエッチングできるので、上層膜を保護するための保護膜が不要となる利点がある。 例えば後述の実施例 1に示すような、下地膜の金属を陰極としてメツキを施すことによ りバンプのような形で上層膜を形成した場合に、この上層膜そのものをメタルマスクと して用いることができるので、上層膜をレジスト膜などで保護する必要がなレ、。従って 、電蝕抑制によるサイドエッチング防止効果に加えて、積層構造の製造工程を簡略 化できる利点があり、 目的とするデバイスの積層構造を簡易かつ安価に形成できる。
[0044] ただし上層膜に更にパターンを形成するなどの目的でレジスト膜を形成することを 排除するものではない。
[0045] 本エッチング方法の場合、上層膜の保護は考慮せず、下地膜のエッチング性能の みを考えればよい。従ってサイドエッチングを防止しつつ下地膜のエッチング速度を 過度に低下させないために、酸化剤濃度をやや高めとし、硝酸濃度を高すぎない程 度とするのが望ましい。好ましくは酸化剤の濃度を 0. 5〜： 12重量％とし、より好ましく は酸化剤の濃度を 0. 5〜： 10重量％とする。硝酸濃度は通常 35〜65重量％、好まし くは 35〜60重量％とし、より好ましくは 35〜57重量％とする。
[2] クロムやニッケノレよりなる下地膜上に銅又は銀 (或いはこれらを主成分とする合 金)よりなる上層膜が形成された積層膜に対して、 2層を同時にエッチングする場合。
[0046] 銅や銀は、貴金属ながら酸化剤入り高濃度硝酸水溶液に溶解する傾向があるため 、上層膜上にパターンィ匕レジスト膜などの保護膜を形成して、 2層同時にエッチング を行う。
[0047] このとき、酸化剤濃度を高めると、下地膜のエッチング速度はあまり変化しないが、 銅や銀のエッチング速度は速くなる傾向があるため、酸化剤濃度を変えることで両層 のエッチング速度比を制御することができる。そこで、電蝕抑制によるサイドエツチン
グ防止効果が得られるような硝酸濃度としつつ、酸化剤濃度を最適化して、両層のェ ツチング速度が同程度となるように制御するのが好ましい。本方法によれば、電蝕抑 制によるサイドエッチングを防止しつつ、 2層を同時にエッチングできる利点があり、 積層構造の製造工程を簡略化できる利点があり、 目的とするデバイスの積層構造を 簡易かつ安価に形成できる。
[0048] 本エッチング方法において、好ましくは酸化剤の濃度を 0. 5重量％以上とし、より 好ましくは 2重量％以上とし、更に好ましくは 3重量％以上とする。但し好ましくは酸化 剤の濃度を 6重量％以下とし、より好ましくは 5重量％以下とする。硝酸濃度は通常 3 5〜65重量％、好ましくは 35〜60重量％とし、より好ましくは 35〜57重量％とする。
[0049] 但し、両層のエッチング速度に差があるエッチング液であっても目的により使用が 可能である。例えば、酸化剤を多く添加し、上層膜のエッチング速度を高めたエッチ ング液を用いて上層膜を短時間でエッチング処理する。このとき下地膜のエッチング は不十分に終わるため、その後、実質的に下地膜のみをエッチングできる別の液、 例えば酸化剤を含まない濃塩酸等によりエッチングを行う。これにより下地膜と上層 膜の両方に同じパターンを形成できる。
[0050] この場合は 2度エッチングを行うことになる力 電蝕抑制によるサイドエッチング防止 効果があるので、良好なエッチング端面が得られ、微細パターンを精度良く形成でき る利点がある。
[0051] 本エッチング方法の場合は、好ましくは酸化剤の濃度を 0. 5重量％以上とし、より 好ましくは 2重量％以上とし、更に好ましくは 3重量％以上とする。但し好ましくは酸化 剤の濃度を 12重量％以下とし、より好ましくは 10重量％以下とする。硝酸濃度は通 常 35〜65重量％、好ましくは 35〜60重量％とし、より好ましくは 35〜57重量％とす る。
[0052] 本発明のエッチング液には、本発明の効果を著しく損なわない限り、必要に応じて 酸化剤以外の添加剤を任意の量添加してもよい。
[0053] 本発明においてエッチングを行う温度は特に限定されず、 目的とするエッチング速 度やエッチング性能が得られるよう決定すればよいが、通常、常温（20°C)から 50°C までの範囲で実施される。
[0054] 以下に、実施例及び比較例を挙げて本発明をより具体的に説明するが、本発明は その要旨を超えない限り、以下の実施例に限定されるものではない。
実施例 1
[0055] 6B (6インチ）シリコンウェハ基板の表面にスパッタ装置を用いてクロム金属膜を 20 Onm厚みで全面に成膜した。このクロム金属膜上にポジレジストを塗布後、フォトリソ グラフィ一により柱状のレジストパターンを形成し、その隙間部分のクロム金属膜が露 出している部分で、そのクロム金属膜を陰極にして、金メッキ浴中にてクロム金属膜 上に金メッキを施した。その後、柱状のレジストパターン部分を除去し、シリコンウェハ 基板上にクロム金属膜が全面に形成され、その上に、高さ 2 /i m (2, OOOnm)の金バ ンプが各所に立ち、バンプの周りにはクロム下地膜が露出しているような積層膜バン プ付き基板を作成し、テストピースとした。
[0056] 硝酸濃度 42重量％、及び硝酸セリウムアンモニゥム (4価)濃度 9重量％のエツチン グ液を作成し、これを 200mlビーカーに 120ml容量で仕込んだ。硝酸濃度は硝酸セ リウムアンモニゥムを含めた水溶液に対する濃度である。温度は室温（23°C)とし、ス ターラーにて撹拌をしながら、上記テストピースを部分的に浸漬させ、クロム金属膜の 部分が無くなるまでの時間を測定してエッチング速度を調べた。金バンプ周辺に表 出したクロム金属膜がなくなる点をジャストエッチングとして止め、その後基板をリンス 水で十分に洗浄した後に乾燥させた。
[0057] 次いで、クロム下地膜の電蝕によるサイドエッチングを確認すベぐこのエッチング 処理品の SEM (電子顕微鏡)及びレーザー顕微鏡写真から、金バンプの幅、長さ等 の寸法等を確認した後に、該エッチング処理品を金エッチング液（ヨウ素濃度 3重量 %、ヨウ化カリウム濃度 12重量％水溶液）で処理することにより、上層に存在する金 バンプ部分を完全に除去した。この金エッチング液は、予め別テストにて、クロム金属 単独膜を処理した場合には重量変化も外観上も全くエッチングされないことを確認し てある。従って、このエッチング処理品をこの金エッチング液で処理した場合、エッチ ングされなレ、下地膜であるクロム金属膜部分がそのまま形状を残す。金エッチング液 で処理後、リンス水洗、乾燥した後に、 SEM及びレーザー顕微鏡写真を撮ってクロ ム下地膜部分の寸法を測定して、金バンプ形状部分の測定寸法と比較して、サイド
エッチング量 (金バンプの端面より内側へエッチングされたクロム下地膜端面のサイド エッチング幅）を計算で求めた。この結果を表 1に示す。
[比較例 1]
[0058] クロムエッチング液の硝酸濃度を 13重量％、硝酸セリウムアンモニゥム（4価)濃度 を 9重量％としたこと以外は実施例 1と同様にしてエッチング速度とサイドエッチング 量を調べ、結果を表 1に示した。
[0059] [表 1]
[0060] 表 1より、硝酸濃度が 35重量％以上の本発明のエッチング液であれば、金バンプ 下層のクロム下地膜のサイドエッチングを防止した上で、金バンプ間から表出したク ロム金属膜を選択的にエッチング除去することができることが分力^)。
[0061] これに対して、硝酸濃度の低い比較例 1では、エッチング速度は速レ、が、クロム下 地膜のサイドエッチング量も多ぐクロム下地膜のアンダーカット部分が問題となる。 特に、オーバーエッチング (終点よりもエッチング時間を長めにすること）にする程影 響が大きぐサイドエッチングが顕著に現れる。
実施例 2
[0062] 6B (6インチ）シリコンウェハ材の表面にスパッタ装置を用いてクロム金属膜を 50nm 厚みで全面的に成膜した。このクロム金属膜の上にスパッタ装置を用いて銅金属膜 を 200nm厚みで全面的に積層成膜した。この銅金属膜の上にポジ型レジストを塗布 してパターン化し、レジストが除去された部分に銅金属膜が露出しているような積層 膜付き基板を作成し、テストピースとした。
[0063] 硝酸濃度 42重量％、及び硝酸セリウムアンモニゥム (4価)濃度 4重量％のエツチン グ液を作成し、このエッチング液を用いて実施例 1と同様にしてテストピースを浸漬さ せてエッチング処理を行レ、、上層の銅金属膜のエッチング速度とクロム下地膜のエツ
チング速度とを調べると共に、クロム下地膜のサイドエッチング量 (銅金属膜の端面よ り内側にエッチングされたクロム下地膜のエッチング幅）を調べ、結果を表 2に示した [比較例 2]
[0064] エッチング液の硝酸濃度を 13重量％、硝酸セリウムアンモニゥム (4価)濃度を 4重 量％にしたこと以外は実施例 2と同様にしてエッチング速度とサイドエッチング量を調 ベ、結果を表 2に示した。
[0065] [表 2]
[0066] ※クロム下地膜よりも上層の銅金属膜のサイドエッチングが進行する。
表 2より、硝酸濃度が 35重量％以上の本発明のエッチング液であれば、酸化剤で ある硝酸セリウムアンモニゥム濃度を調整することにより上層の銅金属膜とクロム下地 膜とのエッチング速度を同等とすることができ、サイドエッチングを防止して積層膜の 同時エッチングを行えることが分かる。
[0067] これに対して、硝酸濃度の低い比較例 2では、上層の銅金属膜のエッチング速度 力 Sクロム金属膜のエッチング速度に比べて速すぎ、上層の銅金属膜がクロム下地膜 よりもずつと速くエッチングされてしまった。このように比較例 2のエッチング液では両 金属膜を同等のエッチング速度にコントロールできず、実用不可能である。
[0068] 本発明を詳細にまた特定の実施態様を参照して説明した力 S、本発明の精神と範囲 を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明ら かである。
[0069] 本出願は、 2004年 4月 14日出願の日本特許出願（特願 2004-119195)に基づくもの であり、その内容はここに参照として取り込まれる。
産業上の利用可能性
本発明によれば、基板上に形成されたクロム、ニッケル、或いはクロム及び/又は ニッケノレを含む合金よりなる下地膜と、この下地膜の全面又は一部を被覆するように 形成された貴金属又は貴金属合金よりなる上層膜との積層膜をエッチングして、所 望の形状の配線又はバンプ等を形成する技術として、工業的に有用である。本発明 は、半導体関連における Siウェハ基板や III/V族基板をベースにしたデバイス、液 晶関連でのガラス基板をベースとしたデバイス、ポリイミド材等の有機膜を形成した基 板をベースとしたデバイス、更にはシリカ及びアルミナ等をベースとしたセラミックス基 板を用いたデバイスなど、各種のデバイス分野に適用できる。
Claims
[1] 基板上に形成されたクロム、ニッケル、或いはクロム及び/又はニッケルを含む合 金よりなる下地膜と、この下地膜の全面又は一部を被覆するように形成された貴金属 又は貴金属合金よりなる上層膜との積層膜のうち、少なくとも前記下地膜を、硝酸濃 度 35重量％以上の水溶液からなるエッチング液を用いてエッチングすることを特徴と するエッチング方法。
[2] 請求項 1において、前記硝酸濃度が 35〜70重量％であることを特徴とするエッチ ング方法。
[3] 請求項 1において、前記エッチング液がさらに酸化剤を含むことを特徴とするエッチ ング方法。
[4] 請求項 3において、前記エッチング液の酸化剤の濃度が 0. 5〜： 12重量％であり、 前記上層膜が金、パラジウム、白金或いはこれらの金属の 1以上を含む合金からなる 膜であり、前記積層膜のうちの下地膜を選択的にエッチングすることを特徴とするェ ツチング方法。
[5] 請求項 3において、前記エッチング液の酸化剤の濃度が 0. 5〜6重量％であり、前 記上層膜が銅、銀或いはこれらの金属の 1以上を含む合金からなる膜であり、前記積 層膜の下地膜と上層膜とをエッチングすることを特徴とするエッチング方法。
[6] 基板上に形成されたクロム、ニッケル、或いはクロム及び/又はニッケルを含む合 金よりなる下地膜と、この下地膜の全面又は一部を被覆するように形成された貴金属 又は貴金属合金よりなる上層膜との積層膜のうち、少なくとも前記下地膜をエツチン グするためのエッチング液であって、硝酸濃度 35重量％以上の水溶液からなること を特徴とするエッチング液。
[7] 請求項 6において、前記硝酸濃度が 35〜70重量％であることを特徴とするエッチ ング液。
[8] 請求項 6において、前記エッチング液がさらに酸化剤を含むことを特徴とするエッチ ング液。
[9] 請求項 8において、前記上層膜が金、パラジウム、白金或いはこれらの金属の 1以 上を含む合金からなる膜であって、前記エッチング液が前記積層膜のうちの下地膜
を選択的にエッチングするためのエッチング液であり、前記酸化剤の濃度が 0. 5〜1 2重量％であることを特徴とするエッチング液。
請求項 8において、前記上層膜が銅、銀或いはこれらの金属の 1以上を含む合金 からなる膜であって、前記エッチング液が前記積層膜の下地膜と上層膜の両方をェ ツチングするためのエッチング液であり、前記酸化剤の濃度が 0. 5〜6重量％である ことを特徴とするエッチング液。