WO2005037534A2 - 積層体及びその製造方法 - Google Patents

積層体及びその製造方法 Download PDF

Info

Publication number
WO2005037534A2
WO2005037534A2 PCT/JP2004/015867 JP2004015867W WO2005037534A2 WO 2005037534 A2 WO2005037534 A2 WO 2005037534A2 JP 2004015867 W JP2004015867 W JP 2004015867W WO 2005037534 A2 WO2005037534 A2 WO 2005037534A2
Authority
WO
WIPO (PCT)
Prior art keywords
metal compound
layer
polyvalent metal
carboxyl group
group
Prior art date
Application number
PCT/JP2004/015867
Other languages
English (en)
French (fr)
Other versions
WO2005037534A3 (ja
WO2005037534A1 (ja
Inventor
Hideaki Tanaka
Masahiro Yamazaki
Mototaka Kawashima
Original Assignee
Kureha Chemical Ind Co Ltd
Hideaki Tanaka
Masahiro Yamazaki
Mototaka Kawashima
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kureha Chemical Ind Co Ltd, Hideaki Tanaka, Masahiro Yamazaki, Mototaka Kawashima filed Critical Kureha Chemical Ind Co Ltd
Priority to DE200460030466 priority Critical patent/DE602004030466D1/de
Priority to JP2005514888A priority patent/JP4915097B2/ja
Priority to AT04792983T priority patent/ATE490866T1/de
Priority to US10/576,879 priority patent/US7569267B2/en
Priority to EP20040792983 priority patent/EP1676699B1/en
Publication of WO2005037534A2 publication Critical patent/WO2005037534A2/ja
Publication of WO2005037534A1 publication Critical patent/WO2005037534A1/ja
Publication of WO2005037534A3 publication Critical patent/WO2005037534A3/ja

Description

明細書 積層体及びその製造方法 技術分野
本発明は、 高分子基材上に、 ポリ(メタ) アクリル酸に代表されるカルボキ シル基含有重合体を含有する層と多価金属化合物を含有する層とが隣接して 配置された層構成を有する積層体に関し、 さらに詳しくは、 ガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に優れ、 低湿条件下ではもとより、 高湿条件下でのガスバリア性に優れた積層体に関する。 また、 本発明は、 該 積層体の製造方法に関する。
本発明において、 積層体とは、 例えば、 コーティング法、 ラミネーシヨン 法、 蒸着法、 またはこれらの方法の組み合わせにより、 各層が形成された多 層構造体をいう。 また、 本発明において、 フィルムとは、 厚みが 0 . 2 5 m m未満のものだけではなく、 0 . 2 5 mm以上のシートをも意味するものと する。 さらに、 本発明において、 ポリ(メタ) アクリル酸とは、 ポリアクリル 酸またはポリメタクリル酸若しくはこれらの混合物を意味する。 背景技術
ポリビュルアルコールフィルムは、 ガスバリア性に優れているが、 耐湿性 及ぴ耐水性が不十分であり、 ガスパリァ性の湿度依存性も大きく、 吸湿によ つて酸素ガスバリア性が著しく低下し易い。 エチレン一ビュルアルコール共 重合体フィルムは、 ガスバリア性及ぴ耐水性が比較的良好であるものの、 ガ スパリア性の湿度依存性が大きい。 ポリ (メタ) アクリル酸フィルムは、 相 対湿度 0 %のような乾燥条件下では優れたガスバリア性を示すが、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に劣り、 特に高湿条件下においてガスバリア 性が著しく低下する。
従来、 ポリ (メタ) アクリル酸またはその部分中和物とポリビュルアルコ ールまたは糖類との混合物から形成された塗膜を熱処理することにより、 ガ スバリア性、 耐水性、 耐熱水性に優れ、 ガスパリア性の湿度依存性が小さな フィルムを得る方法が提案されている (例えば、 日本国の特許第 2 7 3 6 6 0 0号公報、 特許第 2 8 1 1 5 4 0号公報、 特許第 3 2 0 3 2 8 7号公報、 及び特許第 3 3 4 0 7 8 0号公報)。
これらの方法により得られたガスパリア性フィルムは、 熱処理により、 ポ リ (メタ) アクリル酸またはその部分中和物とポリビュルアルコールまたは 糖類との間にエステル結合が生成し、 高度に架橋 (「エステル架橋」 という) されている。
上記 4件の文献に記載された方法により得られたガスバリア性フィルムの 耐熱水性や耐水蒸気性を更に高めるために、 エステル結合に加えて、 金属ィ オンによるイオン結合を導入する方法が提案されている。
例えば、 ポリ (メタ) アタリル酸とポリビュルアルコールまたは糖類との 混合物からなる塗膜を熱処理してフィルムを作製し、 次いで、 該フィルムを アルカリ金属またはアル力リ土類金属を含む媒体中に浸漬処理して、 ポリ (メタ) アタリ/レ酸と金属との間にイオン結合を導入する方法が提案されて いる (例えば、 特開平 1 0— 2 3 7 1 8 0号公報)。
特開平 1 0— 2 3 7 1 8 0号公報に記載の方法によれば、 耐熱水性及び耐 水蒸気性が向上したガスパリア性フィルムを製造することができる。 しかし、 この方法では、 熱処理したフィルムを、 金属化合物または金属イオンを含有 する水溶液などの媒体中において、 例えば、 9 0〜 1 3 0 °C程度の高温で比 較的長時間にわたって浸漬処理を行う必要がある。
また、 ポリ (メタ) アクリル酸またはその部分中和物とポリビュルアルコ ールまたは糖類との混合物から形成された塗膜の表面に金属化合物層を形成 し、 該塗膜中への金属化合物の移行によりイオン結合を形成させる方法が提 案されている (例えば、 特開 2 0 0 0— 9 3 1号公報)。 該塗膜は、 熱処理し てポリ (メタ) アクリル酸またはその部分中和物とポリビュルアルコールま たは糖類との間にエステル結合が形成されている。
塗膜上に金属ィ匕合物層を形成する前記方法によれば、 金属化合物層からの 金属イオンの移行による固相反応により、 塗膜中にイオン結合が形成されて、 ガスバリア性、 耐熱水' fe、 耐水蒸気性が更に優れたフィルムを製造すること ができる。 この方法により得られたガスパリア性フィルムには、 熱処理によ り生成したエステル結合からなるエステル架橋構造に加えて、 カルボキシル 基と金属イオンとの間のイオン結合によるイオン架橋構造が導入されている。 上記特開 2 0 0 0— 9 3 1号公報に記載の方法において、 金属化合物層と して多価金属化合物と樹脂とを含む混合物層を用いると、 層間接着性に優れ た多層フィルムを得るこ とができるが、 その場合に、 多価金属イオンの移行 効率を十分に高めることが望まれていた。
さらに、 上記方法で【ま、 ポリ (メタ) アクリル酸またはその部分中和物と ポリビュルアルコールまたは糖類との間にエステル結合による架橋構造を形 成することが必要である。 エス.テル結合を形成しない場合には、 エステル架 橋されていないポリビニ^/アルコールまたは糖類の存在により、 多層フィル ムの耐熱水性や耐水蒸気'性が損なわれる。 このエステル結合の形成には、 前 記組成を持つ塗膜を高温条件下で熱処理する必要があることに加えて、 エス テル結合による強い架橋構造を有しているため、 多層フィルムの廃棄処理や 再生処理が困難である。
したがって、 用途分野や廃棄処理、 再生処理などの観点から、 ガスパリア 性に優れた多層フィルムを得るのに、 エステル結合を形成させる場合だけで はなく、 必ずしもエステル結合を形成しなくても適用可能な方法が求められ ていた。 発明の開示
本発明の目的は、 カノレポキシル基含有重合体を多価金属によりィォン架橋 してなるガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に優れ、 低 湿条件下ではもとより、 高湿条件下でのガスバリア性にも優れた重合体層を 含む積層体を提供するこ とにある。
特に本発明の目的は、 高分子基材の少なくとも片面にカルボキシル基含有 重合体層と多価金属化合物含有層とが隣接して配置された層構成を有する積 層体において、 多価金属化合物含有層からの多価金属化合物粒子の移行性に 優れた積層体を提供することにある。
さらに、 本発明の目的は、 カルボキシル基含有重合体層が必ずしも架橋剤 成分 (例えば、 ポリビュルアルコール、 糖類) を含有しなくても、 多価金属 によるイオン架橋のみで、 ガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水 蒸気性に優れた積層体を提供することにある。
本発明の他の目的は、 前記の如き諸特性を有する積層体の製造方法を提供 することにある。
本発明者らは、 前記目的を達成するために鋭意研究した結果、 ポリ (メ タ) ァクリル酸のようなカルボキシル基含有重合体を多価金属でイオン架橋 することにより、 ガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に 優れ、 低湿条件下ではもとより、 高湿条件下でのガスバリア性にも優れたフ イルムが得られることを見出した。
具体的には、 高分子基材の少なくとも片面に、 力ルポキシル基含有重合体 層を形成し、 該カルボキシル基含有重合体層の片面または両面に多価金属化 合物含有層を隣接して配置した積層体を形成する。 その際、 多価金属化合物 粒子、 バインダー樹脂、 及ぴ界面活性剤を含有する混合物を用いて多価金属 化合物含有層を形成すると、 カルボキシル基含有重合体層への多価金属化合 物粒子の移行が効率良く進行し、 酸素ガスバリァ性に優れた積層体を効率的 に得ることができる。
カルボキシル基含有重合体層が架橋剤成分を含有しない場合には、 カルボ キシル基含有重合体層は、 イオン結合のみで架橋されている。 このような力 ルポキシル基含有重合体層は、 通常の使用条件下で、 水、 熱水、 水蒸気など によって溶解したり形状が崩れたりすることはないが、 強酸性または強アル カリ性の水に溶角军するため、 廃棄処理や再生利用が容易である。 もちろん、 力ルポキシル基含有重合体層には、 必要に応じて、 架橋剤成分を含有させて、 エステル結合などによるイオン架橋以外の架橋構造を導入してもよい。 本発 明は、 これらの知見に基づいて完成するに至ったものである。
本発明によれば、 高分子基材の少なくとも片面に、 カルボキシル基含有重 合体層(A)と多価金属化合物含有層(B)とが隣接して配置された層構成を有す る積層体であって、 多価金属化合物含有層(B)が、 多価金属化合物粒子、 バイ ンダ一樹脂、 及び界面活性剤を含有することを特徴とする積層体が提供され る。
また、 本発明によれば、 高分子基材の少なくとも片面に、 (1 ) カルボキシ ル基含有重合体を含有する塗工液を塗布し、 乾燥させてカルボキシル基含有 重合体層(A)を形成させる工程 1と、 (2 ) 工程 1の前または後に、 多価金属 化合物粒子、 バインダー樹脂、 及び界面活性剤を含有する塗工液を塗布し、 乾燥させて多価金属化合物含有層(B)を形成させる工程 2とを含む、 高分子基 材の少なくとも片面に、 カルボキシル基含有重合体層(A)と多価金属化合物含 有層(B)とが隣接して配置された層構成を有する積層体の製造方法が提供され る。 図面の簡単な説明
図 1は、 多層フィルムの層構成について、 その一例を示す断面図である。 図 2は、 多層フィルムの層構成について、 他の一例を示す断面図である。 発明を実施するための最良の形態
1 . 高分子基材:
本発明で使用する高分子基材の材質は、 特に制限されず、 各種ポリマーを 用いることができる。 基材の形態は、 一般に、 フィルムまたはシート (以下、 単に 「フィルム」 という)、 板などの平坦な表面を有するものであるが、 所望 により、 ボトル、 カップ、 トレー、 袋などの容器;その他の立体構造を有す るものであってもよい。
基材としては、 プラスチックフィルムが好ましく用いられる。 プラスチッ クフィルムを構成するプラスチックの種類には、 熱可塑性樹脂及ぴ熱硬化性 樹脂があり、 特に制限されないが、 例えば、 高密度ポリエチレン、 中密度ポ リエチレン、 低密度ポリエチレン、 直鎖状低密度ポリエチレン、 ポリプロピ レン、 ポリ 4ーメチルペンテン、 環状ポリオレフインなどのォレフィン重合 体類及ぴその酸変性物 ;ポリ酢酸ビュル、 エチレン一酢酸ビュル共重合体、 エチレン一酢酸ビ二/レ共重合体ケン化物、 ポリビュルアルコールなどの酢酸 ビュル重合体類及ぴその変性物;ポリエチレンテレフタレート、 ポリブチレ ンテレフタレ一ト、 ポリエチレンナフタレ一トなどのポリエステル類;ポリ ε—力プロラク トン、 ポリヒ ドロキシプチレ一ト、 ポリヒ ドロキシバリレー トなどの脂肪族ポリエステル類;ナイロン 6、 ナイロン 6 6、 ナイロン 1 2、 ナイロン 6 Ζ 6 6共重合体、 ナイロン 6ノ1 2共重合体、 メタキシレンアジ パミ ド ·ナイロン 6共重合体などのポリアミ ド類;ポリエチレンダリコール、 ポリエーテノレスノレホン、 ポリフエ二レンス/レフイ ド、 ポリフエ二レンォキシ ドなどのポリエーテノレ類; ポリ塩化ビエル、 ポリ塩化ビ-リデン、 ポリフッ 化ビュル、 ポリフツイ匕ビニリデンなどのハロゲン化重合体類;ポリメチルァ クリレート、 ポリエヂノレアタリレー ト、 ポリメチルメタタリ レート、 ポリエ チルメタクリレート、 ポリアタリロニトリルなどのアタリル重合体類;ポリ ィミ ド樹脂;その他、 アルキド樹脂、 メラミン樹脂、 アタリル樹脂、 硝化綿、 ウレタン樹脂、 ポリエステル樹脂、 フエノール樹脂、 ァミノ樹脂、 フッ素樹 脂、 エポキシ樹脂などの塗料用バインダー樹脂;セルロース、 澱粉、 プルラ ン、 キチン、 キトサン、 グノレコマンナン、 ァガロース、 ゼラチンなどの天然 高分子化合物; を挙【デることができる。
高分子基材としてほ、 これらプラスチック類からなる未延伸フィルムゃ延 伸フィルムが好まし Vヽが、 所望により、 これらのプラスチック類からなるポ トル、 カップ、 トレー、 袋などの容器を用いることができる。
また、 プラスチックフィルムや容器などの表面上に、 酸化珪素、 酸化アル ミニゥム、 アルミ二ケム、 窒化珪素などの無機化合物;金属化合物; などか らなる薄膜が、 蒸着法、 スパッタリング法、 イオンプレーティング法により 形成されたものを高分子基材として用いることができる。 一般に、 これらの 無機化合物や金属化合物からなる薄膜は、 ガスパリア性の付与を目的に用い られる。
2 . カルボキシル基含有重合体:
本発明で使用するカルボキシル基含有重合体は、 分子内に 2個以上のカル ポキシル基を有する重合体であり、 「ポリカルボン酸重合体」 と呼ばれること がある。 カルボキシル基含有重合体としては、 力ルポキシル基含有不飽和単 量体の単独重合体、 カルボキシル基含有不飽和単量体の共重合体、 カルボキ シル基含有不飽和単量体と他の重合性単量体との共重合体、 及び分子内に力 ルポキシル基を含有する多糖類 (「酸性多糖類」 ともいう) が代表的なもので める。
カルボキシル基には、 遊離の力ルポキシル基のみならず、 酸無水物基 (具 体的には、 ジカルボン酸無水物基) も含まれる。 酸無水物基は、 部分的に開 環してカルボキシノレ基となっていてもよい。 カルボキシル基の一部は、 例え ば、 水酸化ナトリウム、 水酸化リチウム、 水酸化カリウムなどのアルカリ金 属水酸化物、 あるいはアンモニアなどの揮発性の塩基により、 部分的に中和 されていてもよい。 この場合、 中和度は、 2 0 %以下であることが好ましい。 また、 ポリオレフインなどの力ルポキシル基を含有していない重合体に力 ルポキシル基含有不飽和単量体をグラフト重合してなるグラフト重合体も、 カルボキシル基含有重合体として使用することができる。 アルコキシカルボ ニル基 (例えば、 メ トキシカルボ二ル基) のような加水分解性のエステル基 を持つ重合体を加水分解して、 カルボキシル基に変換した重合体をカルボキ シル基含有重合体と して使用することもできる。 - カルボキシル基含有不飽和単量体としては、 Οί , _モノエチレン性不飽 和カルボン酸が好ましい。 したがって、 カルボキシル基含有重合体には、 a , i3—モノエチレン' f生不飽和カルボン酸の単独重合体、 2種以上の α, i3—モ ノエチレン性不飽和カルポン酸の共重合体、 及ぴ0;, 3—モノエチレン性不 飽和カルボン酸と他の重合性単量体との共重合体が含まれる。 他の重合性単 量体としては、 エチレン性不飽和単量体が代表的なものである。
a , jS—モノエチレン性不飽和カルボン酸としては、 例えば、 アクリル酸、 メタクリル酸、 クロ トン酸などの不飽和モノカルボン酸;マレイン酸、 フマ ル酸、 ィタコン酸などの不飽和ジカルボン酸;無水マレイン酸、 無水イタコ ン酸などの不飽和ジカルボン酸無水物; これらの 2種以上の混合物が挙げら れる。 これらの中でも、 アクリル酸、 メタクリル酸、 クロ トン酸、 マレイン 酸、 フマル酸、 及びイダコン酸からなる群より選ばれる少なくとも 1種の α, 一モノエチレン性不飽和カルボン酸が好ましく、 アクリル酸、 メタクリル 酸、 及びマレイン酸からなる群より選ばれる少なくとも 1種の α, 13 _モノ エチレン性不飽和力ルポン酸がより好ましい。
a , 3—モノエチレ 性不飽和カルボン酸と共重合可能な他の重合性単量 体、 特にエチレン性不飽和単量体としては、 例えば、 エチレン ; プロピレン、 1ーブテン、 1一ペンテン、 1一へキセン、 1—ォクテンなどの α—ォレフ イン ;酢酸ビュルなど 飽和カルボン酸ビュルエステル類; ァクリル酸メチ ル、 アクリル酸ェチルなどのアクリル酸アルキルエステル類; メタクリル酸 メチル、 メタクリル酸ェチルなどのメタクリル酸アルキルエステル類;塩化 ビュル、 塩化ビニリデンなどの塩素含有ビュル単量体; フッ化ビニル、 フッ 化ビニリデンなどのフグ素含有ビュル単量体; アクリロニトリル、 メタタリ ロニトリルなどの不飽禾 |3二トリル類; スチレン、 α—メチルスチレンなどの 芳香族ビュル単量体;ィ タコン酸アルキルエステル類;などを挙げることが できる。
これらのエチレン性不飽和単量体は、 それぞれ単独で、 あるいは 2種以上 を組み合わせて使用する ことができる。 また、 カルボキシル基含有重合体が α , β—モノエチレン' |¾不飽和カルボン酸と酢酸ビュルなどの飽和カルポン 酸ビニルエステル類との共重合体である場合は、 該共重合体をケン化して飽 和カルボン酸ビニルエステル単位をビュルアルコール単位に変換した共重合 体も使用することができる。
カルボキシル基含有多糖類としては、 例えば、 アルギン酸、 力ルポキシメ チルセルロース、 ぺクチンなどの分子内に力ルポキシル基を有する酸性多糖 類を挙げることができる。 これらの酸性多糖類は、 それぞれ単独で、 あるい は 2種以上を組み合わせて使用することができる。 また、 酸性多糖類を α, 一モノエチレン性不飽和カルボン酸の (共) 重合体と組み合わせて使用す ることもできる。 ここで、 用語 「(共) 重合体」 は、 単独重合体または共重合 体若しくはこれらの混合物を意味する。
本発明で用いるカルボキシル基含有重合体が、 α, —モノエチレン性不 飽和カルボン酸とその他のエチレン性不飽和単量体との共重合体である場合 には、 得られるフィルムのガスバリア性、 耐熱水性、 耐水蒸気性の観点から、 その共重合組成は、 α, /3—モノエチレン性不飽和カルボン酸単量体組成が 6 0モル%以上であることが好ましく、 8 0モル%以上であることがより好 ましく、 9 0モル °/0以上であることが特に好ましい。
カルボキシル基含有重合体は、 ガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に優れ、 高湿条件下でのガスバリア性にも優れたフィルムが得ら れやすい点で、 α, j3—モノエチレン性不飽和カルボン酸のみの重合によつ て得られる単独重合体または共重合体であることが好ましい。
カルボキシル基含有重合体が a, i3—モノエチレン性不飽和カルボン酸の みからなる (共) 重合体の場合、 その好ましい具体例は、 アクリル酸、 メタ クリル酸、 クロ トン酸、 マレイン酸、 フマル酸、 及ぴィタコン酸からなる群 から選ばれる少なく とも 1種の α, jS—モノエチレン性不飽和カルボン酸の 重合によって得られる単独重合体、 共重合体、 及ぴそれらの 2種以上の混合 物である。 これらの中でも、 アクリル酸、 メタクリル酸、 及ぴマレイン酸か らなる群より選ばれる少なくとも 1種の α, β—モノエチレン性不飽和カル ボン酸の単独重合体及ぴ共重合体がより好ましい。
カルボキシル基含有重合体としては、 ポリアクリル酸、 ポリメタクリル酸、 ポリマレイン酸、 及ぴこれらの 2種以上の混合物が特に好ましい。 酸性多糖 類としては、 ァノレギン酸が好ましい。 これらの中でも、 入手が比較的容易で、 諸物性に優れたフィルムが得られやすい点で、 ポリアクリル酸が特に好まし い。
カルボキシル基含有重合体の分子量は、 特に制限されないが、 フィルム形 成性とフィルム物性の観点から、 数平均分子量が 2, 0 0 0〜1 0, 0 0 0, 0 0 0の範囲であることが好ましく、 5, 0 0 0〜1, 0 0 0, 0 0 0の範 囲であることがよ り好ましく、 1 0, 0 0 0〜 5 0 0, 0 0 0の範囲である ことがさらに好ましい。 数平均分子量は、 ゲルパーミエーシヨンクロマトグ ラフィ (G P C ) により測定することができる。 G P C測定では、 一般に、 標準ポリスチレン換算で重合体の数平均分子量が測定される。 本発明のフィルムを構成する重合体として、 力ルポキシル基含有重合体以 外にも、 フィルムのガスバリア性、 耐熱水性、 耐水蒸気性などの特性を損な わない範囲内において、 他の重合体を混合して用いることができる。 多くの 場合、 カルボキシル基含有重合体のみを使用することが好ましい。
原料として使用する力ルポキシル基含有重合体は、 それを単独で用いて形 成したフィルムについて、 3 0°C及ぴ相対湿度 0%の乾燥条件下で測定した 酸素透過係数が好ましくは 1, O O O c m3 ' ^ m/ (m2 . d a y · MP a) 以下、 より好ましくは 5 0 0 c m3 · μ m/ (m2 · d a y · Μ Ρ a ) 以 下、 特に好ましくは 1 O 0 c m3 · μ m/ (m2 · d a y · MP a) 以下のも のであることが望ましレ、。 原料として使用するカルボキシル基含有重合体の 酸素透過係数が低すぎると、 本発明の積層体におけるカルボキシル基含有重 合体層(A)のガスパリア '["生、 熱水または水蒸気に対する安定性 (耐熱水性、 耐 水蒸気性) が不十分となり易い。
原料として使用するカルボキシル基含有重合体の酸素透過係数は、 以下の 方法により求めることができる。 力ルポキシル基含有重合体を水に溶解して 濃度 1 0重量%の水溶液を調製する。 この水溶液を、 バーコ一ターを用いて、 プラスチックフィルム基材上に塗布し、 乾燥することにより、 乾燥厚さ 1 μ mのカルボキシル基含有重合体層が形成されたコーティングフィルムを作製 する。 得られたコーティングフィルムについて、 3 0°C及び相対湿度 0°/0の 条件下における酸素透過度を測定する。 プラスチックフィルム基材として、 その酸素透過度が比較的大きいプラスチックフィルムを用いる。 得られた力 ルポキシル基含有重合体の乾燥塗膜を有するコーティングフィルムの酸素透 過度が、 基材として用 V、たプラスチックフィルム単独の酸素透過度に対して、 1 0分の 1以下であれ ίま、 その酸素透過度の測定値を実質的にカルボキシル 基含有重合体層単独の酸素透過度と見なすことができる。
上記のようにして得られた測定値は、 厚さ 1 mのカルボキシル基含有重 合体層の酸素透過度でおるため、 その測定値に 1 / mを乗じることにより、 酸素透過係数に変換することができる。 酸素透過度の測定は、 例えば、 モダ ンコントロール (Mo d e r n C o n t r o l )社製の酸素透過試験器オタ ストラン (OXTRAN) 2 20を用いて行うことができる。 酸素透過度 の測定方法は、 AS TM D 3985-81 [J I S K 7126に規 定されている B¾ (等圧法) に相当〕 に従って実施する。 測定値は、 単位 c m3 (S TP) / (m2 · d a y · MP a) で表記することができるが、 ST Pは、 酸素の体積を規定するための標準条件 (0°C、 1気圧) を意味するの で、 STPを割愛して表記することがある。
本発明では、 力ノレボキシル基含有重合体層(A)を形成するのに、 カルポキシ ル基含有重合体のみを用いることができるが、 必要に応じて、 カルボキシル 基含有重合体を架橋することができる架橋剤成分を用いることができる。 架橋剤としては、 例えば、 ポリビニルアルコール、 多糖類、 グリセリンな どのポリアルコーノレ類;ジイソシァネート化合物、 ジエポキシ化合物、 カル ポジイミド化合物等を挙げることができる。 架橋剤は、 カルボキシル基含有 重合体層(A)を塗;!:法により形成する際、 カルボキシル基含有重合体を含有す る塗工液に含有させて用いる。 架橋処理は、 カルボキシル基含有重合体と架 橋剤を含有する塗工液を塗布し、 乾燥させた後、 熱処理することにより行う ことができる。
架橋剤としてポリビニルアルコールや糖類などのポリアルコール類を用い る場合 は、 その種類や使用割合、 熱処理による架橋条件などは、 前述の 6 つの特許文献を参照することができる。 例えば、 カルボキシル基含有重合体 とポリアルコール類との割合は、 通常、 5 : 95〜90 : 10の重量比であ る。 エステル架橋开成のための熱処理条件は、 通常 1 00°C以上、 好ましく は 100〜300°C、 より好ましくは 160〜 230 °Cの温度で、 通常 30 秒間〜 48時間、 好ましくは 1分間〜 24時間、 より好ましくは 5分間〜 1 時間の熱処理時間である。
また、 電子線や紫外線などの活性エネルギー線によって、 カルボキシル基 含有重合体自体を架橋することもできる。 この場合、 カルボキシル基含有重 合体を含有する塗工液を塗布し、 乾燥した塗膜に活性エネルギー線を照射し て、 架橋構造を形成する。 3 . 多価金属化合物粒子: ·
本発明で用いる多価金属化合物粒子は、 金属ィオンの価数が 2以上の多価 金属原子単体及ぴ多価金属化合物の粒子である。 したがって、 本発明で使用 する多価金属化合物には、 多価金属原子単体も含まれる。
多価金属の具体例としては、 ベリリウム、 マグネシウム、 カルシウムなど の周期表 2 A族の金属;チタン、 ジルコニウム、 クロム、 マンガン、 鉄、 コ バルト、 ニッケ 7レ、 銅、 亜鉛などの遷移金属;アルミニウムを挙げることが できるが、 これらに限定されない。
多価金属化合物の具体例としては、 多価金属の酸化物、 水酸化物、 炭酸塩、 有機酸塩、 無機酸塩が挙げられるが、 これらに限定されない。
有機酸塩としては、 例えば、 酢酸塩、 シユウ酸塩、 クェン酸塩、 乳酸塩、 リン酸塩、 亜リン酸塩、 次亜リン酸塩、 ステアリン酸塩、 モノエチレン性不 飽和カルボン酸塩が挙げられるが、 これらに限定されない。 無機酸塩として は、 例えば、 塩 f匕物、 硫酸塩、 硝酸塩を挙げることができるが、 これらに限 定されない。 多価金属のアルキルアルコキシドも多価金属化合物として使用 することができる。 これらの多価金属化合物は、 それぞれ単独で、 あるいは 2種以上を組み合わせて使用することができる。
多価金属化合物の中でも、 塗工液 (コーティング液) の分散安定性と形成 される多層フィ レムのガスバリア性の観点から、 ベリ リウム、 マグネシウム、 カルシウム、 銅、 コバルト、 ニッケル、 亜鉛、 アルミニウム、 及ぴジルコニ ゥムの化合物が好ましく、 ベリリウム、 マグネシウム、 カルシウム、 銅、 亜 鉛、 コバルト、 及ぴニッケルなどの 2価金属の化合物がより好ましい。
好ましい 2価金属化合物としては、 例えば、 酸化亜鉛、 酸化マグネシウム、 酸化銅、 酸化ニッケル、 酸化コバルトなどの酸化物;炭酸カルシウムなどの 炭酸塩;乳酸力/レシゥム、 乳酸亜鉛、 アクリル酸カルシウムなどの有機酸塩 ;マグネシウムメ トキシドなどのアルコキシド;などを挙げることができる 力 これらに限定されない。
多価金属化合物含有層(B)は、 通常、 多価金属化合物粒子、 バインダー樹脂、 及び界面活性剤を含有する塗工液を塗布し、 乾燥することにより形成される。 多価金属化合物は、 粒子の形態で用いられ、 塗工液中ではもとより、 多価金 属化合物含有層中でも粒子形状が維持される。
多価金属化合物粒子の平均粒子径は、 塗工液の分散安定性と多価金属化合 物粒子の移行性の観, から、 好ましくは 1 0 n mから 1 0 μ m ( 1 0, 0 0 O n m)、 より好ましくは 1 2 n mから 1〃 m ( 1 , 0 0 0 n m)、 さらに好 ましくは 1 5 n mから 5 0 0 n m、 特に好ましくは 1 5 n mから 5 0 n mの 範囲であることが望ましい。
多価金属化合物粒子の平均粒子径が大きすぎると、 得られる塗膜の膜厚の 均一性、 表面の平坦' 、 力ルポキシル基含有重合体とのイオン架橋反応性な どが不十分となり易レ、。 多価金属化合物粒子の平均粒子径が小さすぎると、 カルボキシル基含有重合体とのイオン架橋反応が早期に進行するおそれがあ り、 また、 1 0 n m来満の超微粒子をその状態で均一分散させることが困難 である。
多価金属化合物粒子の平均粒子径は、 乾燥した固体の場合には、 走査型電 子顕微鏡または透過型電子顕微鏡を用いて計測と計数を行うことにより測定 することができる。 塗工液中の多価金属化合物粒子の平均粒子径は、 光散乱 法により測定することができる 〔参考文献: 「微粒子工学体系」 第 I卷、 第 3 6 2〜3 6 5頁、 フジテクノシステム (2 0 0 1 )〕。 多価金属化合物粒子は、 —次粒子、 二次粒子、 またはこれらの混合物として存在するが、 多くの場合、 平均粒子径からみて二次粒子として存在するものと推定される。
4 . バインダ一樹脂:
本発明で使用するバインダー樹脂としては、 例えば、 アルキッ ド樹脂、 メ ラミン樹脂、 アタリノレ樹脂、 硝化綿、 ウレタン樹脂、 ポリエステル樹脂、 フ ヱノール樹脂、 ァミノ樹脂、 フッ素樹脂、 エポキシ樹脂などの塗料用として 汎用のバインダー樹脂を挙げることができる。 これらの樹脂は、 多価金属化 合物と反応するカルボ、キシル基を含有しない樹脂である。 これらのバインダ 一樹脂は、 単独で用いてもよいが、 硬化剤を併用することが多い。 5 . 界面活性剤:
本発明では、 多価金属化合物粒子の分散性を高めるため、 界面活性剤を使 用する。 界面活性剤とは、 分子内に親水性基と親油性基の両方を持つ化合物 であり、 ァニ才ン性、 カチオン性、 両性のイオン性界面活性剤や非イオン性 界面活性剤があるが、 本発明では、 いずれの界面活性剤でも使用することが できる。
ァニオン系界面活性剤には、 例えば、 カルボン酸型、 スルホン酸型、 硫酸 エステル型、 リン酸エステル型がある。 カルボン酸型としては、 例えば、 脂 肪族モノカルボン酸塩、 ポリォキシエチレンアルキルエーテルカルボン酸塩、 N—ァシルサ/レコシン酸塩、 N—ァシルグルタミン酸塩がある。 スルホン酸 型としては、 例えば、 ジアルキルスルホコハク酸塩、 アルカンスルホン酸塩、 アルファオレフインスルホン酸塩、 直鎖アルキルベンゼンスルホン酸塩、 ァ レキノレ (分岐鎖) ベンゼンスノレホン酸塩、 ナフタレンスノレホン酸塩一ホノレム アルデヒ ド縮合物、 アルキルナフタレンスルホン酸塩、 N—メチルー N—ァ シルタウリン酸塩が挙げられる。 硫酸エステル型としては、 例えば、 アルキ ル硫酸塩、 ポリオキシエチレンアルキルエーテル硫酸壌、 油脂硫酸エステル 塩が挙げられる。 リン酸エステル型としては、 例えば、 アルキルリン酸塩、 ポリオキシエチレンアルキルエーテルリン酸塩、 ポリオキシエチレンアルキ ルフヱニルエーテルリン酸塩が挙げられる。
カチオン系界面活性剤としては、 例えば、 アルキルアミン塩型、 第 4級ァ ンモニゥム塩型がある。 アルキルアミン塩型としては、 例えば、 モノアルキ ルァミン塩、 ジアルキルアミン塩、 トリアルキルアミン塩が挙げられる。 第 四級アンモニゥム塩型としては、 例えば、 ハロゲン化 (塩化、 臬化またはョ ゥ化) アルキ/レトリメチルアンモニゥム塩、 塩化アルキルベンザルコニゥム が挙げられる。
両性界面活' I"生剤としては、 例えば、 カルボキシベタイン型、 2—アルキル イミダゾリンの誘導体型、 グリシン型、 アミンォキシド型がある。 カルボキ シべタイン型としては、 例えば、 アルキルべタイン、 脂肪酸アミ ドプロピル ベタインが挙げられる。 2—アルキルイミダゾリンの誘導体型としては、 例 えば、 2—アルキル一 N—カルボキシメチノレー N—ヒ ドロキシェチルイミダ ゾリニゥムベタイン 挙げられる。 グリシン型としては、 例えば、 アルキル 若しくはジアルキルジエチレントリアミノ酢酸が挙げられる。 アミノォキシ ド型としては、 例えば、 アルキルアミンォキシドが挙げられる。
非イオン性の界面活 剤としては、 例えば、 エステル型、 エーテル型、 ェ ステルエーテル型、 力ノールアミ ド型がある。 エステル型としては、 例 えば、 グリセリン脂肪酸エステル、 ソルビタン脂肪酸エステル、 しょ糖脂肪 酸エステルが挙げられる。 エーテル型としては、 例えば、 ポリオキシェチレ ンァ /レキノレエーテル、 ポリォキシエチレンアルキルフエニルエーテル、 ポリ ォキシエチレンポリナキシプロピレングリコールが挙げられる。 エステルエ 一テル型としては、 例えば、 脂肪酸ポリエチレングリコール、 脂肪酸ポリオ キシエチレンソルビタンが挙げられる。 アル力ノールアミ ド型としては、 例 えば、 脂肪酸アル力ノールアミ ドが挙げられる。
スチレン一アタリノレ酸共重合体などのポリマー骨格を有する界面活性剤も 使用することができる。
これらの界面活性剤の中でも、 リン酸エステルなどのァニオン系界面活性 剤、 スチレン一アタリノレ酸共重合体などのポリマー骨格を有する界面活性剤 などが好ましい。 6 . 積層体とその製造方法:
本発明の積層体は、 高分子基材の少なくとも片面に、 少なくとも 1層の力 ルポキシル基含有重合体層(A)と少なくとも 1層の多価金属化合物含有層(B) とが隣接して配置された層構成を有する積層体である。 カルボキシル基含有 重合体層(A)と多価金属化合物層(B)は、 高分子基材の片面または両面に形成 するが、 多くの場合、 片面に形成するだけで所望のガスバリア性を持つ積層 体を得ることが可能である。
本発明の積層体の基本的な層構成は、
(i)高分子基材 カルボキシル基含有重合体層(A) /多価金属化合物含有層 (B)、
(ii)高分子基材 /多価金属化合物含有層(B)ノカルポキシル基含有重合体層 (A) /多価金属 fヒ合物含有層(B)、
(iii)高分子基材 カルボキシル基含有重合体層(A) /多価金属化合物含有層
(B) /カルボキシル基含有重合体層(A)
である。
上記の基本的な層構成に加えて、 積層体の片面または両面に、 少なくとも 1つの他の樹脂層を配置してもよい。 その他の樹脂層を配置する方法は、 特 に制限されず、 例えば、 ラミネーシヨン法やコーティング法などを採用する ことができる。 他の樹脂層としては、 基材として用いた樹脂層が挙げられる が、 それらに限定されず、 ヒートシール性、 耐摩耗性、 耐熱性などの所望の 特性を付与することができる各種樹脂層を配置することが可能である。 さら に、 本発明の積層体には、 所望により、 ラミネーシヨン法や蒸着法により金 属箔ゃ酸化珪素などの金属層または無機酸化物層などを 1層以上形成するこ とができる。
高分子基材の厚みは、 特に限定されず、 用途に応じて適宜選定することが できる。 本発明の積層体を多層フィルムの用途に用いる場合には、 高分子基 材の厚みは、 通常 1 μπι〜1ηιπι、 好ましくは 3〜500 μπι、 より好まし くは 5〜100 mの範囲である。 カルボキシル基含有重合体層(A)の厚みは、 特に限定されないが、 フィルム (塗膜) 形成時の成形性や多層フィルムのハ ンドリング性の観点から、 通常 0. 00 1 μ π!〜 1 mm、 好ましくは 0. 0 l〜100 jum、 より好ましくは、 0. 1〜 1 0 μ m、 特に好ましくは 0. 5〜5 μπιの範囲である。 多価金属化合物含有層(Β)の厚みは、 通常 0. 00 1 11!〜 lmm、 好ましくは 0. 0 1〜1 00 μπι、 より好ましくは、 0. 1〜10 j mの範囲である。
本発明の積層体を製造するには、 カルボキシル基含有重合体を含有する塗 ェ液を用いて、 高分子基材上または高分子基材上に形成した多価金属化合物 含有層上に塗布し、 乾燥させて塗膜を形成する。 多価金属化合物含有層を形 成するには、 多価金属化合物、 バインダー樹脂、 及び界面活性剤を含有する 塗工液を用いて、 高分子基材上または高分子基材上に形成した力ルポキシル 基含有重合体層上に塗布し、 乾燥させて塗膜を形成する。 すなわち、 本発明の積層体は、 高分子基材の少なくとも片面に、 (1 ) カル ボキシル基含有重合体を含有する塗工液を塗布し、 乾燥させてカルボキシル 基含有重合体層(A)を形成させる工程 1と、 (2 ) 工程 1の前または後に、 多 価金属化合物粒子、 バインダー樹脂、 及び界面活性剤を含有する塗工液を塗 布し、 乾燥させて多価金属化合物含有層(B)を形成させる工程 2とを含む方法 により製造することができる。 工程 1及び工程 2は、 必要に応じて、 順次多 数回実施することができる。
カルボキシノレ基含有重合体を含有する塗工液は、 力ルポキシル基含有重合 体を均一に溶角军または分散することができる溶媒を用いて調製する。 溶媒と しては、 例え ίま、 水 ; メチルアルコール、 エチルアルコール、 イソプロピル アルコールなどのアルコール類; Ν, Ν—ジメチルスルホキシド、 Ν, Ν— ジメチルホルムアミ ド、 ジメチルァセトアミ ドなどの極性有機溶媒;を挙げ ることができる。
カルボキシ/レ基含有重合体と溶媒を含有する塗工液中のカルボキシル基含 有重合体の濃度は、 特に限定されないが、 塗工液の安定性、 均一性、 塗工作 業性などの観点から、 好ましくは 0 . 1 〜 6 0重量%、 より好ましくは 0 . 5〜 2 5重量ヅ ο、 特に好ましくは 1〜 1 0重量%の範囲であることが望まし レ、。 カルボキシル基含有重合体を含有する塗工液には、 前述の架橋剤を含有 させることができる。
カルボキシ /レ基含有重合体を含有する塗工液には、 ガスバリア性を損なわ ない範囲内で、 必要に応じて、 その他の重合体、 柔軟剤、 安定剤、 アンチブ ロッキング剤、 粘着剤、 モンモリロナイ トに代表される無機層状化合物、 着 色剤、 紫外線吸収剤などの添加剤成分を適宜添加することができる。 その添 加量は、 添加剤の総量として、 カルボキシル基含有重合体の好ましくは 5重 量%以下、 より好ましくは 3重量%以下、 特に好ましくは 1重量%以下であ ることが望ましい。
多価金属化合物を含有する塗工液は、 多価金属化合物粒子、 パインダ一樹 脂、 及び界面活性剤を、 溶媒に溶解または分散させることにより調製するこ とができる。 溶媒は、 これらの成分を均一に溶解または分散することができ るものであればよく、 特に限定されないが、 その具体例としては、 水; メチ ルアルコール、 ェチノレアノレコーノレ、 イソプロピルアルコー 7レ、 n—プロピル アルコーノレ、 n—プチノレァノレコーノレ、 n—ペンチ/レアノレコーノレなどのァノレコ ール類; ァセトン、 メチルェチルケトンなどのケトン類; ジェチルエーテル、 ジォキサン、 テトラヒ ドロフランなどのエーテル類;酢酸ェチル、 酢酸ブチ ルなどのエステル類; ジメチルスルホキシド、 N, N—ジメチルァセトアミ ド、 N, N—ジメチルホルムアミ ド、 N—メチル一 2—ピロリ ドン、 テトラ メチル尿素、 へキサメチルリン酸トリアミ ド、 γ—ブチロラタ トンなどの極 性有機溶媒; トルエン、 へキサン、 ヘプタン、 シクロへキサンなどの炭化水 素類;を挙げることができる。 これらの溶媒は、 それぞれ単独で、 あるいは 2種以上を組み合わせて使用することができる。
多価金属化合物を含有する塗工液には、 必要に応じて、 柔軟剤、 安定剤、 膜形成剤、 アンチブロッキング剤、 粘着剤などの添加剤を適宜 ·適量で添加 することができる。
多価金属化合物粒子とバインダー樹脂との混合比 (質量比) は、 通常 99 : :!〜 1 : 9 9、 好ましくは 85 : 1 5〜20 : 80の範囲である。 バイン ダー樹脂の割合が少なすぎると、 カルボキシル基含有重合体層との層間接着 性が低下傾向を示す。 また、 多価金属化合物粒子に対する界面活性剤の混合 比 (質量比) は、 通常 99. 9 : 0. 1〜 50 : 50の範囲である。
塗工液中での多価金属化合物粒子の含有量は、 通常 0. 0 5〜50重量%、 好ましくは 0. 05〜30重量%、 より好ましくは 0. 1〜30重量%の範 囲である。 塗工液 でのバインダー樹脂の含有量は、 通常 0. 05~50重 量%、 好ましくは 0. 0 5〜30重量%、 より好ましくは 0. 1〜30重量 %の範囲である。
界面活性剤は、 多価金属化合物粒子が安定して分散するに足る量で用いら れるが、 塗工液の全量規準で、 通常 0. 0001〜50重量%、 好ましくは 0. 00 1〜20重量%、 より好ましくは 0. 1〜 10重量%の割合で含有 させることが望ましい。 界面活性剤を添加しないと、 塗工液中での多価金属 化合物粒子の平均粒子径が十分に小さくなるように分散させることが困難に なり、 その結果、 多価金属化合物粒子が均一に分散した塗工液を得ることが 難しく、 基材上または力ルポキシル基含有重合体層上に塗布するとき、 膜厚 が均一な塗膜を形成することが難しくなる。
多価金属化合物を含有する塗工液は、 溶媒以外の成分の合計濃度が好まし くは 0 . 1〜 6 0重量%、 より好ましくは 0 . 5〜5 0重量0 /0、 特に好まし くは 1〜3 0重量%の範囲内にあることが、 作業性良く所望の膜厚の塗膜を 得る上で好ましい。
カルボキシル基含有重合体に対する多価金属化合物粒子の割合は、 カルボ キシル基含有重合体のカルボキシル基の合計 (A t ) に対する多価金属化合 物粒子の合計 (B t ) の化学当量が 0 . 6以上となる割合であることが好ま しい。 この化学当量は、 より好ましくは 0 . 8以上、 特に好ましくは 1 . 0 以上である。 この化学当量の上限は、 通常 1 0 . 0、 好ましくは 5 . 0、 よ り好ましくは 2 . 0である。 カルボキシル基含有重合体のカルボキシル基に 対する多価金属化合物粒子の化学当量が小さすぎると、 カルボキシル基含有 重合体層 (フィルム) のガスバリア性、 耐熱水性、 耐水蒸気性などの諸特性 が低下傾向を示す。
カルボキシル基の合計は、 遊離のカルボキシル基だけではなく、 カルボン 酸多価金属塩となっているカルボキシル基など他の形態となっているものを も含む。 同様に、 多価金属化合物の合計は、 カルボン酸多価金属塩となって いるものも含む。 また、 これらの計算は、 多層構成の全層について行う。
前記化学当量は、 例えば、 以下のようにして求めることができる。 カルボ キシル基含有重合体がポリアクリル酸で多価金属化合物が酸化マグネシウム の場合を例に挙げて説明する。 ポリアクリル酸の質量を 1 0 0 gとした場合、 ポリアタリル酸の単量体単位の分子量は 7 2であり、 単量体 1分子当たり 1 個の力ルポキシル基を有するため、 ポリアクリル酸 1 0 0 g中のカルボキシ ル基の量は、 1 . 3 9モルである。 このとき、 ポリアクリル酸 1 0 0 gに対 する 1 . 0化学当量とは、 1 . 3 9モルを中和する塩基の量である。 ポリア クリル酸 1 0 0 gに対して、 酸化マグネシウムを 0 . 6化学当量混合する場 合、 0 . 8 3 4モルのカルボキシル基を中和するだけの酸化マグネシウムを 加えればよい。 マグネシウムの価数は 2価であり、 酸化マグネシウムの分子 量は 4 0であるため、 ポリアクリル酸 1 0 0 gに対する 0 . 6化学当量の酸 化マグネシウムとは、 1 6 . 6 8 g ( 0 . 4 1 7モル) である。
高分子基材上に、 少なくとも 1層のカルボキシル基含有重合体層(A)と少な くとも 1層の多価金属化合物含有層(B)とが隣接して配置されるように、 各塗 ェ液を塗布し、 乾燥させる。 この場合、 1つの塗工液を塗布し、 乾燥させた 後、 その上に他の塗工液を塗布し、 乾燥させる方法を採用する。 層構成とし ては、 前述の層構成を採用することができるが、 高分子基材層をも含めた好 ましい層構成としては、 例えば、 高分子基材層を 「基材」、 カルボキシル基含 有重合体層を 「AJ、 多価金属化合物含有層を 「B」 として表記すると、 多層 の層構成の具体例としては、 例えば、 図 1に示す 「基材/ A/B」 (基材 1 Z カルボキシル基含有重合体層 2 多価金属化合物含有層 3 )、 図 2に示す 「基 材/ B /A/B」 (基材 2 1 /多価金属化合物含有層 2 2 /カルボキシル基含 有重合体層 2 3ノ多価金属化合物含有層 2 4 )、 あるいは 「基材 ZA/ B / A」 が挙げられる。 もちろん、 これ以上の多層となるように A及ぴ Bを交互 に重ねて配置してもよい。 基材とその上の塗膜との密着性を高めるために、 接着剤層を配置することもできる。
各塗工液の塗工方法としては、 スプレー法、 デイツビング法、 コーターを 用いた塗布法、 印刷機による印刷法など任意である。 コーターや印刷機を用 いて塗布する場合には、 ダイレク トグラビア方式、 リバースグラビア方式、 キスリバースダラビア方式、 オフセットグラビア方式などのグラビアコ一タ 一; リパースローノレコーター、 マイクログラビアコーター、 エアナイフコー ター、 ディ、ソプ: =t一ター— ノ ーコーター- コンマコーター- ダイコータ一な どの各種方式を探用することができる。
塗膜の乾燥方 ¾は、 特に制限されず、 溶媒を蒸発させて固形層を得ること ができる方法でおればよく、 例えば、 雰囲気環境下で自然乾燥させる方法、 所定の温度に設定したオープン中で乾燥させる方法、 その他の任意の乾燥手 段を用いる方法などが挙げられる。 その他の乾燥方法としては、 各種コータ 一に付属するアーチドライヤー、 フローティングドライヤー、 ドラムドライ ヤー、 赤外線ドライヤーなどの乾燥機が代表的なものである。 乾燥条件は、 塗膜やフィルム、 基材などが熱による損傷を蒙らない範囲で任意に設定する ことができる。 乾燥は、 塗膜中の溶媒が実質的に除去されるまで行う。 カル ボキシル基含有重合体層 (A)が架橋剤を含有する場合には、 乾燥による溶媒の 除去に加えて、 エステル結合などの架橋構造を導入するための熱処理を行う。 高分子基材上に各層を形成した後、 力ルポキシル基含有重合体層(A)中へ瞵 接する多価金属化合物含有層(B)から多価金属化合物粒子を移行させて、 カル ボキシル基含有重合体の多価金属塩を形成し、 カルボキシル基含有重合体層 (A)中にカルボキシル基含有重合体の多価金属塩を形成させる。 多価金属化 合物粒子の移行は、 多価金属イオンの形態での移行を含む。
多価金属化合物粒子の移行は、 カルボキシル基含有重合体層(A)と多価金属 化合物含有層(B)とを有する多層フィルムを常温 ·常湿下で長時間放置するこ とによって行うことができるが、 多価金属化合物粒子の移行を加速化させ、 多層フィ /レムの二次成形加工前に所望のガスバリア性 (酸素ガス透過度また は酸素ガス透過係数) の水準を付与するには、 熱処理を行うか、 あるいは所 定の湿度と温度に調製した雰囲気下でエージング (調湿処理) させることが 望ましい。
エージング方法としては、 多層フィルムを、 相対湿度が通常 20%以上、 好ましくほ 40〜: I 00 %、 より好ましくは 60〜: L 00 %、 温度が通常 5 〜 200 °C、 好ましくは 20〜150°C、 より好ましくは 30〜1 30での 雰囲気下に放置する方法が挙げられる。 エージングは、 上記の条件に調整し た気相中または液相中で行う。
エージング時間は、 相対湿度や温度によって適宜調整し、 所望のガスパリ ァ性が得られるまでとするが、 好ましくは 10 以内、 より好ましくは 5日 以内、 さらに好ましくは 2日以内である。 エージング時の圧力は、 0. 00 IMP a (0. 01 a t m) から l O O OMP a (10000 a tm) の範 囲から適宜選択することができる。
本発明の積層体は、 多価金属化合物含有層(B)からの多価金属化合物粒子の 移行性に優れており、 カルボキシル基含有重合体層(A)中の力ルポキシル基含 有重合体が多価金属イオンによってイオン結合 (イオン架橋) され、 それに よって、 ガスパリア性、 耐水性、 耐熱水性、 耐水蒸気性に優れた塗膜.(フィ ルム) を持つ積層体を得ることができる。 バインダー樹脂が存在することに より、 多価金属化合物含有層(B)とカルボキシル基含有重合体層(A)との接着 性が改善される。 界面活性剤が存在することによって、 多価金属化合物粒子 の移行性が促進される。 力ルポキシル基含有重合体層(A)がィオン架橋するこ とにより、 熱水や水蒸気中でも形状が保持される耐熱水性と耐水蒸気性が付 与されることに加えて、 高湿度条件下でも優れたガスパリァ性を示す積層体 を得ることができる。
本発明の積層体は、 温度 30 °Cと相対湿度 0 %、 及び温度 30 と相対湿 度 80%のいずれの条件下においても、 酸素透過度が、 好ましくは 1, 00 0 cm3 (S TP) / (m2 · d a y · MP a) 以下、 より好ましくは 500 cm3 (S TP) / (m2 · d a y · MP a) 以下、 特に好ましくは 100 c m3 (STP) Z (m2 · d a y · MP a) 以下のガスバリア性を有するもの であることが望ましい。
本発明の積層体は、 高分子基材を含む多層フィルムとして用いることが多 レ、。 本発明の積層体には、 必要に応じて、 ラミネーシヨン法やコーティング 法などにより、 他の樹脂層を 1層以上配置することができる。 本発明の積層 体は、 酸素によって変質を受け易い食品、 飲料、 薬品、 医薬品、 電子部品な どの包装材料として好適である。 本発明の積層体は、 ポトル、 カップ、 トレ 一、 チューブ、 袋などの包装容器の材料として好適である。 このような容器 への二次成形加工は、 ヒートシール、 シート成形 (真空成形及び/または圧 空成形) など任意である。 実施例
以下に実施例及ぴ比較例を挙げて、 本発明について、 より具体的に説明す る。 本発明における物性の測定法及ぴ評価法は、 下記のとおりである。
( 1 ) 酸素透過度:
フィルムの酸素透過度は、 酸素透過試験器 (Mo d e r n c o n t r o •1社製 OX T RAN 2/2 0) を用いて、 温度 3 0 °C及び相対湿度 8 0 % の雰囲気下で測定した。 単位は、 c m3Z (m2 · d a y · MP a) である。 調製例 1 (塗工液 I )
ポリアク リル酸水溶液 〔東亞合成 (株) 製、 商品名 「ァロン A— 1 0H」、 濃度 2 5重量%、 数平均分子量 2 0 0, 0 0 0〕 を水とイソプロパノール ( I P A) で希釈して、 ポリアクリル酸 (PAA) の 5重量%溶液 (塗工液 I ) を調製した。 この塗工液 Iの溶媒組成は、 水/ I PA- 50/5 0 (重 量比) であった。 調製例 2 (塗工液 II)
ポリアクリル酸水溶液 〔東亞合成 (株) 製、 商品名 「ァロン A— 1 0H」、 濃度 2 5重量%、 数平均分子量 2 0 0, 0 0 0〕 を I PAで希釈して、 PA Aの 5重量%溶液を調製した。 さらに、 該溶液に含まれる PAAのアクリル 酸単位のモ 7レ数に対して 1 Omo 1 %の割合の水酸化ナトリウムを添加し溶 解して、 アクリル酸単位の 1 Omo 1 %が中和された PA A部分中和物溶液 (塗工液 Π) を調製した。 塗工液 IIの溶媒組成は、 水 Z I PA 90Z10 (重量比) であった。 調製例 3 (塗工液 III)
ポリアクリル酸粉末 〔A 1 d r i c h (株) 製試薬、 数平均分子量 4 5 0, 000〕 を I P Aに加温下に溶解し、 八の5重量%溶液 (塗工液 III) を 調製した。 塗工液 IIIの溶媒組成は、 I P Aが 9 9重量%以上であった。 調製例 4 (塗工液 IV)
調製例 2で調製した塗工液 IIに、 架橋剤としてグリセリンを添加して、 塗 ェ液 IVを調製した。 塗工液 IV中の PAA部分中和物とグリセリンとの比率は- 6 0/40 (重量比) であった。 . 調製例 5 (塗工液 V)
多価金属化合物粒子として、 微粒子炭酸カルシウム 〔白石工業 (株) 製、 白艷華 0、 平均粒子径 4 0 n m〕 を用いた。 樹脂として、 ウレタン樹脂の溶 液 〔大日精化 (株) 製、 商品名 「インキ用メジゥム N Tハイラミック」、 溶媒 =酢酸ェチルダ酢酸プロピル Zメチルェチルケトン/ I P A〕 を用いた。 樹 脂の硬化剤として、 イソシァネート化合物の溶液 〔大日精化 (株) 製、 商品 名 「ラミック Bハードナー」、 溶媒 = トノレェン/メチルェチルケトン Z酢酸ェ チル〕 を用いた。 界面活性剤として、 ソルビタンモノステアレートを用いた。 これらの成分を下記の割合になるように混合し、 最終的に超音波ホモジナイ ザ一を用いて混合して、 塗工液 Vを調製した。
炭酸カルシウム : 1 0 0 0 g
ウレタン樹脂 (固形分) : 5 0 0 g
ソノレビタンモノステアレート : 2 0 0 g
硕化剤 (固形分) : 6 0 g
溶媒: 3 2 0 0 g
溶媒は、 トルエン/メチルェチルケトン /酢酸ェチル / I P Aの混合溶媒 である。 炭酸カルシウム Zウレタン樹脂の重量比は、 6 7 / 3 3であり、 炭 酸カルシウム 界面活性剤の重量比は、 8 4 Z 1 6である。 調製例 6 (塗工液 VI)
多価金属化合物粒子として、 微粒子炭酸カルシウム 〔白石工業 (株) 製、 白艷華 0、 平均粒子径 4 0 n m〕 を用いた。 樹脂として、 ドライラミネート 用接着剤として用いられているポリエステル樹脂の溶液 〔三井武田ケミカル (株) 製、 商品名 「タケラック A— 5 2 5」、 溶媒 =酢酸ェチル〕 を用いた。 樹脂の硬化剤として、 イソシァネート化合物の溶液 〔三井武田ケミカル (株)、 商品名 「タケネート A 5 2」、 溶媒 =酢酸ェチル〕 を用いた。 界面活性剤とし ては、 スチレン一アクリル酸共重合体 〔大日精化 (株) 製〕 を用いた。 これ らの成分を下記の割合になるように混合し、 最終的に超音波ホモジナイザー を用いて混合して、 塗工液 VIを調製した。 炭酸カルシウム : 1 0ひ 0 g
ポリエステル樹脂 (固形分) : 1 0 0 0 g
スチレン一アクリル酸共重合体: l O O O g
硬ィ匕剤 (固形分) : 8 0 g
酢酸ェチル: 6 0 0 0 g
炭酸カルシウム/ポリエステル樹脂の重量比は、 5 0 / 5 0であり、 炭酸 カルシウムノ界面活性剤の重量比は、 5 0ノ 5 0である。 調製例 7 (塗工液 VII)
多価金属化合物粒子として、 微粒子酸化亜鉛 〔シーアィ化成 (株) 製、 商 品名 「超微粒子酸化亜鉛 N a n o t e c」、 平均粒子径 2 0 n m〕 を用いた。 樹脂として、 ポリエステル一ウレタン樹脂の溶液 〔住化パイエルウレタン (株) 製、 ポリエステル一ウレタン水性ディスパージヨン、 商品名 「バイヒ ドロール P R 2 4 0」、 溶媒 =水〕 を用いた。 界面活性剤として、 丸菱油化工 業 (株) 製のリン酸エステル塩型界面活性剤を用いた。 これらの成分を下記 の割合になるように混合し、 最終的に超音波ホモジナイザーを用いて混合し て、 塗工液 VIIを調製した。
酸 f匕亜鉛: 1 0 0 0 g
ポリエステル一ウレタン樹脂 (固形分) : 5 0 0 g
リン酸エステル塩型界面活性剤: 1 0 0 g
水: 3 4 0 0 g
酸匕亜鉛ノポリエステル一ウレタン樹脂の重量比は、 6 7ノ 3 3であり、 酸化亜鉛/界面活性剤の重量は、 9 1 9である。 調製例 8 (塗工液 VIII)
塗: C液 Vにおいて、 界面活性剤のソルビタンモノステアレートを添加しな かつ广ここと以外は、 調整例 5と同様にして、 塗工液 VIIIを調製した。 邇製例 9 (塗工液 IX) 塗工液 VIにおいて、 界面活性剤のスチレン—ァクリル酸共重合体を添加し なかったこと以外は、 調整例 6と同様にして、 塗工液 IXを調製した。 調製例 1 0 (塗工液 X)
塗工液 VIIにおいて、 界面活性剤のリン酸エステル塩型界面活性剤を添加し なかったこと以外は、 調整例 7と同様にして、 塗工液 Xを調製した。 実施例
2軸延伸ポリエステルフィルム 〔P E Tフィルム ;東レ (株) 製、 商品名 「ルミラー P 6 0」、 厚さ 1 2 Ai m〕 上に、 グラビアコーターを用いて塗工液 Iを塗布し、 乾燥させた (乾燥厚み 1 μ πι)。 さらにその上に、 グラビアコー ターを用いて塗工液 Vを塗布し、 乾燥させた (乾燥厚み 1 ιη)。
このようにして得られた多層フィルムを、 温度 3 0 °C及ぴ相対湿度 8 0 % の雰囲気に調整した恒温恒湿槽中に 2 4時間静置して、 金属イオンを P AA フィルム中に移行せしめ、 固相反応で P AAの金属塩を形成させた。 得られ た多層フィルムの酸素透過度を測定した。 結果を表 1に示す。 実施例 2
塗工液 Iに代えて塗工液 IIを用いたこと以外は、 実施例 1と同様にして多 層フィルムを作製し、 酸素透過度を測定した。 各塗膜の乾燥厚みは、 いずれ 1 μ mでめつ 7こ。 実施例 3
塗工液 Iに代えて塗工液 IIIを用いたこと以外は、 実施例 1と同様にして多 層フィルムを作製し、 酸素透過度を測定した。 各塗膜の乾燥厚みは、 いずれ ¾ 1 mであった。 実施例 4
P E Tフィルム 〔東レ (株) 製、 商品名 「ルミラー P 6 0 J、 厚さ 1 2 / m〕 上に、 グラビアコーターを用いて塗工液 IVを塗布し、 乾燥させた (乾燥 厚み 1 m)。 乾燥後のフィルムをオーブン中で 200°C及び 15分間の条件 で熱処理することにより、 PAAとグリセリンとの間で架橋反応を行わせた。 このようにして得られたフィルム上に、 実施例 1同様にグラビアコーターを 用いて混合液 Vを塗布し、 乾燥させた (乾燥厚み 1 μπι)。 得られた多層フィ ルムの酸素透過度を測定した。 結果を表 1に示す。 実施例 5
塗工液 Vに代えて塗工液 VIを用いたこと以外は、 実施例 1と同様にして多 層フィルムを作製し、 酸素透過度を測定した。 各塗膜の乾燥厚みは、 いずれ も 1 mであった。 実施例 6
塗工液 Vに代えて塗工液 VIIを用いたこと以外は、 実施例 1と同様にして多 層フィルムを作製し、 酸素透過度を測定した。 各塗膜の乾燥厚みは、 いずれ ¾ 1 mであった。 実施例 7
PETフィルムに代えて 2軸延伸ナイロン 6フィルム 〔ONyフィルム ; ュニチカ (株) 製、 商品名 「EMBLEM ONBCJ, 厚さ 15 m) を用 いたこと以外は、 実施例 1と同様にして多層フィルムを作製し、 酸素透過度 を評価した。 結果を表 1に示す。 実施例 8
P ETフィルムに代えて 2軸延伸ポリプロピレンフィルム 〔OPPフィル ム ;二村化学 (株) 製、 商品名 「太閤 FOR」、 厚さ 20 μηι〕 を用いたこと 以外は、 実施例 1と同様にして多層フィルムを作製し、 酸素透過度を評価し た。 結果を表 1に示す。 実施例 9
P E Tフィルムに代えて未延伸ポリプロピレンフィルム (C Ρ Ρフィルム ;東レ合成 (株) 製、 商品名 「トレファン NO、 ZK93FMJ、 厚さ 60 μ m〕 を用いたこと以外は、 実施例 1と同様にして多層フィルムを作製し、 酸 素透過度を評価した。 結果を表 1に示す。 実施例 10
P E Tフィルムに代えて未延伸の直鎖低密度ポリエチレンフィルム 〔 L L DPEフィルム;東セロ (株) 製、 商品名 「TUX— TCS」、 厚さ 50 μ m〕 を用いたこと以外は、 実施例 1と同様にして多層フィルムを作製し、 酸 素透過度を評価した。 結果を表 1に示す。 実施例 1 1
PETフィルムに代えて酸化ケィ素蒸着 PETフィルム 〔尾池工業 (株) 製、 商品名 「MOS—TR」、 厚さ 12 μπι〕 を用いたこと以外は、 実施例 1 と同様にして多層フィルムを作製し、 酸素透過度を評価した。 塗工液 Iは、 酸化ケィ素蒸着面に塗布した。 結果を表 1に示す。 実施例 12
塗工液 Iを酸化ケィ素蒸着 Ρ Ε Τフィルムの酸化ケィ素蒸着面とは反対側 の面 (背面) に対して塗布したこと以外は、 実施例 11と同様にして多層フ イルムを作製し、 酸素透過度を評価した。 結果を表 1に示す。 実施例 13
Ρ ΕΤフィルム 〔東レ (株) 製、 商品名 「ルミラー Ρ 60」、 厚さ 1 2 n m] 上に、 グラビアコーターを用いて、 接着剤 〔三井武田ケミカル (株) 製 ドライラミネート用接着剤、 商品名 「タケラック A— 525」、 硬化剤-タケ ネート A— 52〕 を塗布し、 乾燥させた (乾燥厚み 0. 5 μπι)。 その上に、 塗工液 Iを、 グラビアコーターを用いて塗布し、 乾燥させた (乾燥厚み 1 μ m) 0 さらにその上に、 グラビアコーターを用いて塗工液 Vを塗布し、 乾燥さ せた (乾燥厚み 1 // πι)。 得られた多層フィルムの酸素透過度を測定した。 結 果を表 1に示す。 実施例 1 4
Ρ Ε Τフィルム 〔東レ (株) 製、 商品名 「ルミラー Ρ 6 0」、 厚さ 1 2 m〕 上に、 塗布液 Vを塗布し、 乾燥させた (乾燥厚み 0 . 5 m)。 その上に、 塗工液 Iをグラビアコーターを用いて塗布し、 乾燥させた (乾燥厚み 1 i m)。 さらにその上に、 グラビアコーターを用いて塗工液 Vを塗布し、 乾燥させた (乾燥厚み 0 . 5 /x m)。 得られた多層フィルムの酸素透過度を測定した。 結 果を表 1に示す。 比較例 1
塗工液 Vに代えて界面活性剤を含有しない塗工液 VIIIを用いたこと以外は、 実施例 1と同様にして多層フィルムを作製し、 酸素透過度を評価した。 結果 を表 1に示す。 比較例 2
塗工液 Vに代えて界面活性剤を含有しない塗工液 IXを用いたこと以外は、 実施例 1と同様にして多層フィルムを作製し、 酸素透過度を評価した。 結果 を表 1に示す。 比較例 3
塗工液 Vに代えて界面活性剤を含有しない塗工液 Xを用いたこと以外は、 実施例 1と同様にして多層フィルムを作製し、 酸素透過度を評価した。 結果 を表 1に示す。 力ルポキシル基含有
多価金属化合物含有層
重合体層
ま偷例 ¾& フノ レ 冒 ( nm° / Ρ
TWlXr in / mrn^ · udνy·Μ ivirdο、ノ ィ 1用老 厚さ 厚さ
涂丁據 Kjj ονϋΐνπ
(μ m) (μ m)
実施例 1 I 1.0 V 1.0 PET I/V 10
実施例 2 Π 1.0 V 1.0 PET n/v 10
実施例 3 in 1.0 V 1.0 PET in/v 10
実施例 4 IV 1.0 V 1.0 PET IV/ V 10 熱処理 実施例 5 I 1.0 VI 1.0 PET I /VI 10
実施例 6 I 1.0 1.0 PET Ι/ΥΠ 10
実施例 7 I 1.0 V 1.0 ONy I/V 10
実施例 8 I 1.0 V 1.0 OP P I/V 10
実施例 9 I 1.0 V 1.0 CPP I/V 10
実施例 10 1.0 V 1.0 LLDPE I/V 10
実施例 11 1.0 V 1.0 酸化ケィ素 I/V 10 謹ェ 実施例 12 1.0 V 1.0 蒸着 PET I/V 10 蒸着背面塗工 実施例 13 1.0 V 1.0 PET 接着/ iZv 10 接着層有り 実施例 14 1.0 V 1.0 PET V/I/V 10 V/I/V 比較例 1 1.0 m 1.0 PET i/vin 1, 500
界面活性剤 比較例 2 1.0 K 1.0 PET I/K 1, 500
無添加 比較例 3 1.0 X 1.0 PET I/X 1,500
産業上の利用可能性 .
本発明によれば、 カルボキシル基含有重合体を多価金属によりイオン架橋 してなるガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に優れ、 低 湿条件下ではもとより、 高湿条件下でのガスバリア性にも優れた重合体層を 含む積層体及びその製造方法が提供される。
本発明の積層体は、 カルボキシル基含有重合体層に対する多価金属化合物 含有層からの多価金属化合物粒子の移行性に優れている。 本発明の積層体は、 カルボキシル基含有重合体層が必ずしも架橋剤成分を含有しなくても、 多価 金属によるイオン架橋のみで、 ガスバリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気性に優れている。
本発明の積層体は、 ガスパリア性、 耐湿性、 耐水性、 耐熱水性、 耐水蒸気 性に優れ、 低湿条件下ではもとより、 高湿条件下でのガスバリァ性に優れて いる。 本発明の積層体は、 これらの諸特性を生かして、 例えば、 包装材料と して好適である。

Claims

請求の範囲
1 . 高分子基材の少なくとも片面に、 カルボキシル基含有重合体層(A)と多 価金属化合物含有層(B)とが隣接して配置された層構成を有する積層体であつ て、 多価金属化合物含有層(B)が、 多価金属化合物粒子、 バインダー樹脂、 及 ぴ界面活性剤を含有する積層体。
2 . カルボキシル基含有重合体層(A)が、 多価金属化合物含有層(B)から移 行した多価金属イオンによってイオン架橋されている請求項 1記載の積層体。
3 . 高分子基材の少なくとも片面に、 カルボキシル基含有重合体層(A) /多 価金属化合物含有層(B)、 多価金属化合物含有層(B)ノカルポキシル基含有重 合体層(A) /多価金属化合物含有層(B)、 またはカルボキシル基含有重合体層 (A) /多価金属化合物含有層(B) /カルボキシル基含有重合体層(A)がこの順に 配置された層構成を有する多層フィルムが配置された請求項 1記載の積層体。
4 . 高分子基材の少なくとも片面に、 前記層構成の多層フィルムに加えて、 少なくとも 1層の他の樹脂層が更に配置された層構成を有する請求項 1記載 の積層体。
5 . 高分子基材がプラスチックフィルムであって、 積層体全体が多層ブイ ルムである請求項 1記載の積層体。
6 . カルボキシル基含有重合体に対する多価金属化合物粒子の割合が、 力 ルポキシル基含有重合体のカルボキシル基の合計 (A t ) に対する多価金属 化合物粒子の合計 (B t ) の化学当量が 0 . 6以上となる割合である請求項 1記載の積層体。
7 . カルボキシル基含有重合体が、 力ルポキシル基含有不飽和単量体の単 独重合体、 カルボキシル基含有不飽和単量体の共重合体、 力ルポキシル基含 有不飽和単量体と他の重合性単量体との共重合体、 カルボキシル基含有多糖 類、 またはこれらの 2種以上の混合物である請求項 1記載の積層体。
8. カルボキシル基含有不飽和単量体が、 アクリル酸、 メタクリル酸、 ク 口 トン酸、 ィタコン酸、 マレイン酸、 及ぴフマル酸からなる群より選ばれる 少なくとも 1種の α, β一モノエチレン性不飽和カルボン酸である請求項 7 記載の積層体。
9. 多価金属化合物粒子が、 平均粒子径 1 0 nm〜l 0 μπιの粒子である 請求項 1記載の積層体。
10. 多価金属化合物が、 ベリリウム、 マグネシウム、 カルシウム、 銅、 コバルト、 ニッケル、 亜鉛、 アルミニウムまたはジルコニウムの酸化物、 炭 酸塩、 有機酸塩またはアルコキシドである請求項 1記載の積層体。
1 1. 多価金属化合物粒子が、 2価金属化合物粒子である請求項 1記載の
12. 多価金属化合物含有層(Β)が、 多価金属化合物粒子とバインダー樹脂 とを、 重量比で 99 : 1〜1 : 99の割合で含有するものである請求項 1記 載の積層体。
1 3. 多価金属化合物含有層 (Β)が、 多価金属化合物粒子と界面活性剤とを、 質量比で 99. 9 : 0. 1〜 50: 50の割合で含有するものである請求項
1記載の積層体。
14. カルボキシル基含有重合体層(Α)の厚みが 0. 00 1 μ m〜 1 mmで、 多価金属化合物含有層(B)の厚みが 0. 001 // !11〜1111111でぁる請求項1記 載の積層体。
1 5. 高分子基材の少なくとも片面に、 少なくとも 1層のカルボキシル基 含有重合体層(A)と少なくとも 1層の多価金属化合物含有層(B)とを塗工法に より隣接して形成し、 その後、 相対湿度 20%以上、 温度 5°C〜200°Cの 雰囲気下でエージングして、 多価金属化合物含有層(B)から多価金属化合物を 力ルポキシル基含有重合体層(A)中に移行させて、 カルボキシル基含有重合体 のカルボキシル基と多価金属塩を形成させる方法により得 れたものである 請求項 1記載の積層体。
1 6. 高分子基材の少なくとも片面に、 (1) カルボキシル基含有重合体を 含有する塗工液を塗布し、 乾燥させて力ルポキシル基含有重合体層(A)を形成 させる工程 1と、 (2) 工程 1の前または後に、 多価金属化合物粒子、 バイン ダー樹脂、 及び界面活性剤を含有する塗工液を塗布し、 乾燥させて多価金属 化合物含有層(B)を形成させる工程 2とを含む、 高分子基材の少なくとも片面 に、 力ルポキシル基含有重合体層 (A)と多価金属化合物含有層(B)とが隣接し て配置された層構成を有する積層体の製造方法。
1 7. 前記層構成が、 カルボキシル基含有重合体層(A)/多価金属化合物含 有層(B)、 多価金属化合物含有層(B)Zカルボキシル基含有重合体層(A)/多価 金属化合物含有層(B)、 またはカルボキシル基含有重合体層(A)Z多価金属化 合物含有層(B)ノカルボキシル基含有重合体層 (A)がこの順に配置された層構 成である請求項 16記載の製造方法。
1 8. 前記層構成に加えて、 少なくとも 1層の他の樹脂層を更に配置する 請求項 16記載の製造方法。
1 9. 多価金属化合物粒子、 バインダー樹脂、 及び界面活性剤を含有する 塗工液が、 多価金属化合物粒子 0. 0 5〜50重量%、 バインダー樹脂 0. 05〜 50重量%、 及び界面活性剤 0. 0001〜 50重量%を含有するも のである請求項 1 6記載の製造方法。
20. 前記工程 1及び 2を順次必要回数実施することにより、 高分子基材 の少なくとも片面に、 少なくとも 1層のカルボキシル基含有重合体層(A)と少 なくとも 1層の多価金属化合物含有層 (B)とを塗工法により隣接して形成して 積層体を形成し、 さらに、 その後、 相対湿度 20%以上、 温度 5°C~20 O °Cの雰囲気下でエージングして、 多価金属化合物含有層(B)から多価金属化合 物を力ルポキシル基含有重合体層(A)中に移行させて、 カルボキシル基含有重 合体の力ルポキシル基と多価金属塩を形成させる請求項 1 6記載の製造方 ¾。
PCT/JP2004/015867 2003-10-22 2004-10-20 積層体及びその製造方法 WO2005037534A1 (ja)