WO2005023468A1 - 貴金属コロイド、貴金属微粒子、組成物および貴金属微粒子の製造方法 - Google Patents
貴金属コロイド、貴金属微粒子、組成物および貴金属微粒子の製造方法 Download PDFInfo
- Publication number
- WO2005023468A1 WO2005023468A1 PCT/JP2004/009063 JP2004009063W WO2005023468A1 WO 2005023468 A1 WO2005023468 A1 WO 2005023468A1 JP 2004009063 W JP2004009063 W JP 2004009063W WO 2005023468 A1 WO2005023468 A1 WO 2005023468A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- noble metal
- colloid
- fine particles
- precious metal
- gold
- Prior art date
Abstract
Description
Claims