WO2004104257A1 - Radiant tube in cracking furnaces - Google Patents
Radiant tube in cracking furnaces Download PDFInfo
- Publication number
- WO2004104257A1 WO2004104257A1 PCT/SE2004/000757 SE2004000757W WO2004104257A1 WO 2004104257 A1 WO2004104257 A1 WO 2004104257A1 SE 2004000757 W SE2004000757 W SE 2004000757W WO 2004104257 A1 WO2004104257 A1 WO 2004104257A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tube
- radiant tube
- weight
- yttrium
- tantalum
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G9/00—Thermal non-catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
- C10G9/14—Thermal non-catalytic cracking, in the absence of hydrogen, of hydrocarbon oils in pipes or coils with or without auxiliary means, e.g. digesters, soaking drums, expansion means
- C10G9/18—Apparatus
- C10G9/20—Tube furnaces
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
Definitions
- the present disclosure relates to a radiant tube formed of a material that meets requirements such as creep strength, ductility and service life in cracking furnaces, preferably furnaces for ethylene cracking.
- H 2 C H 2 C, which constitutes a raw material for the plastics industry.
- the cracking takes place by hydrocarbons being led through a radiant tube, which has been heated by means of surrounding burner to sufficiently high temperature, for instance, about 1,100 °C, for ethylene being formed in the tube.
- the tube usually is made from a FeCrAl material.
- a dense aluminum oxide Al O is formed on the outside and inside of the tube. This oxide prevents Fe contacting the gas flowing in the tube when Fe acts as a catalyst for coke formation in the tube. If coke is formed in the tube, the same is deposited on the inside of the tube, the flow of gas in the tube becoming smaller and the heat transfer to the interior of the tube becoming lower. Coke may also entirely clog the tube.
- a FeCrAl material where it is stated that the creep strength is increased by the fact that the material is alloyed with cobalt, nickel, silicon, manganese, zirconium and titanium as well as a small quantity of yttrium and hafnium, and then the material is heat-treated at minimum 1050 °C until very elongate granules are formed having a length of at least 5 mm and a ratio of length to cross-section of at least 10 to 1. Radiant tubes are manufactured from this material.
- the present disclosure relates to a radiant tube in a cracking furnace, where hydrocarbons are cracked into ethylene in a tube through which hydrocarbons flow, which tube is heated from the outside to a temperature where cracking of hydrocarbons occurs, and is characterized in that the tube is made from a FeCrAl material containing, in addition to Fe, 10 to 25% by weight of Cr, 1 to 10% by weight of Al and 1.5 to 5% by weight of Mo.
- the material comprises up to a total of 2.2 wt.%, preferably up to 2.0 wt.% and more preferably up to 1.0 wt.%, of one or more alloying materials selected from the group consisting of tantalum, hafnium, zirconium, yttrium, mtrogen, carbon and oxygen.
- a radiant tube is found in a cracking furnace, where hydrocarbons are cracked into ethylene in a tube through which hydrocarbons flow.
- the tube is heated from the outside to a temperature where cracking occurs.
- the temperature of the tube, at the inlet end of the gas is 900 °C and at the outlet end 1,125 °C.
- the tube is made from a FeCrAl material containing, in addition to Fe, 10 to 25% by weight of Cr, 1 to 10% by weight of Al and 1.5 to 5% by weight of Mo.
- the material contains smaller fractions of one or more of the alloying materials, tantalum, hafnium, zirconium, yttrium, nitrogen, carbon and oxygen.
- the material comprises up to a total of 2.2 wt.%), preferably up to 2.0 wt.% and more preferably up to 1.0 wt.%, of one or more alloying materials selected from the group consisting of tantalum, hafi ium, zirconium, yttrium, nitrogen, carbon and oxygen.
- the material contains 2 to 3.5% by weight of molybdenum.
- the tube is made from a material having a creep strength high enough that the time to brealc of the tube at a temperature of 1,100 °C and a load of 2.2 MPa exceeds 100,000 hours. This corresponds to substantially a twice as high a creep strength in comparison with tubes made from the material disclosed in the Swedish Patent No. 467 414.
- a cracker tube may typically be 10 to 17 meters long.
- Such a tube consists of two or more tubes welded together in the longitudinal direction. According to a preferred embodiment, the tube is formed in one piece having a length exceeding 10 meters.
- Additional exemplary embodiments of the tube may be varied in respect of the material composition, above all regarding alloying materials having a low percentage in the material.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Physics & Mathematics (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Thermal Sciences (AREA)
- Production Of Liquid Hydrocarbon Mixture For Refining Petroleum (AREA)
- Combustion Of Fluid Fuel (AREA)
- Gas Burners (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP04733228A EP1627093A1 (en) | 2003-05-20 | 2004-05-14 | Radiant tube in cracking furnaces |
JP2006532193A JP2007506866A (ja) | 2003-05-20 | 2004-05-14 | 分解炉用ラジアントチューブ |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
SE0301500A SE0301500L (sv) | 2003-05-20 | 2003-05-20 | Strålningsrör i krackerugn |
SE0301500-5 | 2003-05-20 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2004104257A1 true WO2004104257A1 (en) | 2004-12-02 |
Family
ID=20291377
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/SE2004/000757 WO2004104257A1 (en) | 2003-05-20 | 2004-05-14 | Radiant tube in cracking furnaces |
Country Status (6)
Country | Link |
---|---|
US (1) | US20050019202A1 (zh) |
EP (1) | EP1627093A1 (zh) |
JP (1) | JP2007506866A (zh) |
CN (1) | CN100365151C (zh) |
SE (1) | SE0301500L (zh) |
WO (1) | WO2004104257A1 (zh) |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2006068606A1 (en) * | 2004-12-21 | 2006-06-29 | Sandvik Intellectual Property Ab | Method of joining components, fitting and tube joint where at least one of the components comprises or is made of material difficult to weld |
WO2007064288A1 (en) * | 2005-12-02 | 2007-06-07 | Sandvik Intellectual Property Ab | A tube and use of said tube |
EP2031080A1 (de) * | 2007-08-30 | 2009-03-04 | ALSTOM Technology Ltd | Hochtemperaturlegierung |
WO2009045136A1 (en) * | 2007-10-05 | 2009-04-09 | Sandvik Intellectual Property Ab | The use and method of producing a dispersion strengthened steel as material in a roller for a roller hearth furnace |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ITMI20040040A1 (it) * | 2004-01-15 | 2004-04-15 | Maurizio Spoto | Elemento scambiatore a scambio termico incrementato |
CN102230132B (zh) * | 2011-07-04 | 2012-11-21 | 大连理工大学 | 一种Fe-Cr-Mo-Al-Cu耐蚀高温合金 |
CN210287474U (zh) * | 2019-06-01 | 2020-04-10 | 上海颐柏科技股份有限公司 | 一种基于辐射管的甲醇和丙烷裂解装置 |
CN117144264B (zh) * | 2023-10-31 | 2024-02-02 | 上海核工程研究设计院股份有限公司 | 轻水反应堆燃料组件用铁素体耐热合金、制造方法与应用 |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1018563A1 (en) * | 1997-08-20 | 2000-07-12 | Jgc Corporation | Heating furnace tube, method of using the same, and method of manufacturing the same |
SE513989C2 (sv) * | 2000-01-01 | 2000-12-11 | Sandvik Ab | Förfarande för tillverkning av ett FeCrAl-material och ett sådant marerial |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AT131135B (de) * | 1930-08-27 | 1933-01-10 | Ver Stahlwerke Ag | Krackvorrichtung. |
US4498928A (en) * | 1984-02-06 | 1985-02-12 | The United States Of America As Represented By The Secretary Of Interior | Ductile duplex iron-based alloy containing aluminum |
SE469754B (sv) * | 1990-05-14 | 1993-09-06 | Kanthal Ab | Ugn foer krackning av kolvaeten |
JPH04354850A (ja) * | 1991-05-29 | 1992-12-09 | Nisshin Steel Co Ltd | 耐高温酸化性に優れた高Al含有フェライト系ステンレス鋼 |
JPH0941096A (ja) * | 1995-08-04 | 1997-02-10 | Mitsubishi Heavy Ind Ltd | タービン用翼材料 |
SE508595C2 (sv) * | 1997-08-12 | 1998-10-19 | Sandvik Ab | Användning av en ferritisk Fe-Cr-Al-legering vid framställning av kompoundrör, samt kompoundrör och användning av röret |
JP4281881B2 (ja) * | 1997-08-20 | 2009-06-17 | 日揮株式会社 | 加熱炉管および加熱炉管の製造方法 |
JPH11209850A (ja) * | 1998-01-23 | 1999-08-03 | Jgc Corp | 加熱炉管および加熱炉管の使用方法 |
-
2003
- 2003-05-20 SE SE0301500A patent/SE0301500L/xx not_active IP Right Cessation
-
2004
- 2004-05-14 JP JP2006532193A patent/JP2007506866A/ja active Pending
- 2004-05-14 EP EP04733228A patent/EP1627093A1/en not_active Withdrawn
- 2004-05-14 WO PCT/SE2004/000757 patent/WO2004104257A1/en active Application Filing
- 2004-05-14 CN CNB2004800137969A patent/CN100365151C/zh not_active Expired - Fee Related
- 2004-05-17 US US10/846,593 patent/US20050019202A1/en not_active Abandoned
Patent Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP1018563A1 (en) * | 1997-08-20 | 2000-07-12 | Jgc Corporation | Heating furnace tube, method of using the same, and method of manufacturing the same |
SE513989C2 (sv) * | 2000-01-01 | 2000-12-11 | Sandvik Ab | Förfarande för tillverkning av ett FeCrAl-material och ett sådant marerial |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2006068606A1 (en) * | 2004-12-21 | 2006-06-29 | Sandvik Intellectual Property Ab | Method of joining components, fitting and tube joint where at least one of the components comprises or is made of material difficult to weld |
WO2007064288A1 (en) * | 2005-12-02 | 2007-06-07 | Sandvik Intellectual Property Ab | A tube and use of said tube |
EP1957693A1 (en) * | 2005-12-02 | 2008-08-20 | Sandvik Intellectual Property AB | A tube and use of said tube |
JP2009520172A (ja) * | 2005-12-02 | 2009-05-21 | サンドビック インテレクチュアル プロパティー アクティエボラーグ | 金属管および該金属管の使用 |
EP1957693A4 (en) * | 2005-12-02 | 2011-08-03 | Sandvik Intellectual Property | TUBE AND USE OF SAID TUBE |
US8206658B2 (en) | 2005-12-02 | 2012-06-26 | Sandvik Intellectual Property Ab | Tube and use of said tube |
EP2031080A1 (de) * | 2007-08-30 | 2009-03-04 | ALSTOM Technology Ltd | Hochtemperaturlegierung |
WO2009045136A1 (en) * | 2007-10-05 | 2009-04-09 | Sandvik Intellectual Property Ab | The use and method of producing a dispersion strengthened steel as material in a roller for a roller hearth furnace |
US8597438B2 (en) | 2007-10-05 | 2013-12-03 | Sandvik Intellectual Property Ab | Use and method of producing a dispersion strengthened steel as material in a roller for a roller hearth furnace |
Also Published As
Publication number | Publication date |
---|---|
JP2007506866A (ja) | 2007-03-22 |
CN100365151C (zh) | 2008-01-30 |
EP1627093A1 (en) | 2006-02-22 |
SE524010C2 (sv) | 2004-06-15 |
CN1802447A (zh) | 2006-07-12 |
SE0301500D0 (sv) | 2003-05-20 |
US20050019202A1 (en) | 2005-01-27 |
SE0301500L (sv) | 2004-06-15 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2312581C (en) | Heat resistant nickel base alloy | |
US20050019202A1 (en) | Radiant tube in cracking furnaces | |
JP5118057B2 (ja) | 金属管 | |
JP7059198B2 (ja) | フェライト合金 | |
WO2018088069A1 (ja) | 肉盛溶接用合金、溶接用粉末及び反応管 | |
EP1744854A1 (en) | Method for joining dispersion-strengthened alloy | |
AU774202B2 (en) | Resistance-heating element | |
WO2009045136A1 (en) | The use and method of producing a dispersion strengthened steel as material in a roller for a roller hearth furnace | |
JPH04358037A (ja) | ニッケル基耐熱合金 | |
JP2006517255A (ja) | 高温合金 | |
CN110938781B (zh) | 一种低成本高铝耐热钢及其制备方法 | |
JPH06207235A (ja) | 加工性に優れるニッケル基耐熱合金 | |
JPH0533091A (ja) | ニツケル基耐熱合金 | |
CN112725011B (zh) | 裂解炉用传热管及其制备方法和应用 | |
JPH051344A (ja) | 耐コーキング性に優れたエチレン分解炉管用耐熱鋼 | |
JPH0533090A (ja) | ニツケル基耐熱合金 | |
JPH05239577A (ja) | 加工性に優れるニッケル基耐熱合金 | |
JP6335247B2 (ja) | 内面突起付反応管 | |
JPH05195138A (ja) | すぐれた耐浸炭性と高温低応力条件下における高いクリープ破断強度を備える耐熱合金 | |
JPH05239576A (ja) | 加工性に優れるニッケル基耐熱合金 | |
CN113227328A (zh) | 用于热裂化反应器的耐侵蚀合金 | |
JPH0649602A (ja) | 高耐食耐摩耗鋳鋼 | |
JPH06207236A (ja) | 加工性に優れるニッケル基耐熱合金 | |
JPH02115351A (ja) | 耐浸炭性にすぐれる耐熱鋼 | |
JPS6362850A (ja) | 硼素を多量に含有する高強度、高延性耐熱鋳鋼 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG UZ VC VN YU ZA ZM ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2004733228 Country of ref document: EP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2006532193 Country of ref document: JP |
|
WWE | Wipo information: entry into national phase |
Ref document number: 20048137969 Country of ref document: CN |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2545/KOLNP/2005 Country of ref document: IN |
|
WWP | Wipo information: published in national office |
Ref document number: 2004733228 Country of ref document: EP |