WO2004065504A1 - Composition de poudre pulverulente, procede de formation de film de revetement et produit revetu - Google Patents

Composition de poudre pulverulente, procede de formation de film de revetement et produit revetu Download PDF

Info

Publication number
WO2004065504A1
WO2004065504A1 PCT/JP2004/000146 JP2004000146W WO2004065504A1 WO 2004065504 A1 WO2004065504 A1 WO 2004065504A1 JP 2004000146 W JP2004000146 W JP 2004000146W WO 2004065504 A1 WO2004065504 A1 WO 2004065504A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder coating
fluororesin
coating film
monomer
group
Prior art date
Application number
PCT/JP2004/000146
Other languages
English (en)
Japanese (ja)
Inventor
Masaji Komori
Shigehito Sagisaka
Hiroshi Torii
Original Assignee
Daikin Industries, Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Daikin Industries, Ltd. filed Critical Daikin Industries, Ltd.
Priority to JP2005508027A priority Critical patent/JPWO2004065504A1/ja
Publication of WO2004065504A1 publication Critical patent/WO2004065504A1/fr

Abstract

L'invention concerne une composition de revêtement pulvérulente permettant de produire un film de revêtement présentant des propriétés satisfaisantes d'adhésion à un substrat et de régularité de surface, sans qu'il soit nécessaire d'utiliser une amorce ou de poncer la surface du substrat. Ladite composition de revêtement pulvérulente comporte une fluororésine et se caractérise en ce qu'elle possède un point de fusion de 150 à 250 °C et un pic de fusion possédant une largeur à mi valeur d'au moins 30 °C.
PCT/JP2004/000146 2003-01-10 2004-01-13 Composition de poudre pulverulente, procede de formation de film de revetement et produit revetu WO2004065504A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2005508027A JPWO2004065504A1 (ja) 2003-01-10 2004-01-13 粉体塗料、塗膜形成方法及び積層体

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2003-004933 2003-01-10
JP2003004933 2003-01-10

Publications (1)

Publication Number Publication Date
WO2004065504A1 true WO2004065504A1 (fr) 2004-08-05

Family

ID=32767194

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2004/000146 WO2004065504A1 (fr) 2003-01-10 2004-01-13 Composition de poudre pulverulente, procede de formation de film de revetement et produit revetu

Country Status (2)

Country Link
JP (1) JPWO2004065504A1 (fr)
WO (1) WO2004065504A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006113836A1 (fr) * 2005-04-19 2006-10-26 Dupont-Mitsui Fluorochemicals Company, Ltd. Film de revetement a base de fluororesine
JP2008303316A (ja) * 2007-06-08 2008-12-18 Asahi Glass Co Ltd 塗料組成物
JP2009502568A (ja) * 2005-07-28 2009-01-29 三井・デュポンフロロケミカル株式会社 フルオロポリマーフィルムによる積層物およびフィルム形成用フルオロポリマー
JP2019181337A (ja) * 2018-04-04 2019-10-24 Ａｇｃ株式会社 積層体の製造方法
WO2020004197A1 (fr) * 2018-06-26 2020-01-02 日本フッソ工業株式会社 Composition de revêtement en poudre pouvant être cuite contenant une résine fluorée et composition de revêtement liquide et revêtement et corps revêtu comprenant cette composition de revêtement en poudre pouvant être cuite ou cette composition de revêtement liquide
CN114566655A (zh) * 2020-11-27 2022-05-31 国家能源投资集团有限责任公司 碳纳米管/碳纤维纸复合电极材料及其制备方法和全钒液流电池
EP4032430A4 (fr) * 2019-09-20 2023-11-01 Daikin Industries, Ltd. Copolymère contenant du fluor

Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS50103553A (fr) * 1974-01-22 1975-08-15
JPS63227324A (ja) * 1987-03-16 1988-09-21 Daikin Ind Ltd 包みパツキン用外被の製法
JPH01258771A (ja) * 1988-02-24 1989-10-16 Hoechst Ag 熱可塑性弗素樹脂より成る粉末被覆物の製造方法
JPH04131167A (ja) * 1989-12-19 1992-05-01 Hoechst Ag 弗素化された熱可塑性樹脂を用いた粉末被覆法
WO1997021776A1 (fr) * 1995-12-08 1997-06-19 Daikin Industries, Ltd. Materiau fluore pour composition de revetement et procede d'enrobage au moyen de cette composition
WO1997040089A1 (fr) * 1996-04-24 1997-10-30 Daikin Industries, Ltd. Fluoropolymere en poudre et procede de preparation
WO1998046426A1 (fr) * 1997-04-15 1998-10-22 Daikin Industries, Ltd. Materiau composite anti-corrosion
WO2000058414A1 (fr) * 1999-03-29 2000-10-05 Daikin Industries, Ltd. Composition de revetement de resine fluoree en poudre
WO2001025354A1 (fr) * 1999-10-04 2001-04-12 Daikin Industries, Ltd. Procede antirouille dans lequel une composition de revetement pulverulent a base de fluororesine thermodurcissable est utilisee
JP2003002979A (ja) * 2001-06-18 2003-01-08 Daikin Ind Ltd フッ素系重合体粉末製造方法
JP2003003111A (ja) * 2001-06-18 2003-01-08 Daikin Ind Ltd 粉体塗料

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS50103553A (fr) * 1974-01-22 1975-08-15
JPS63227324A (ja) * 1987-03-16 1988-09-21 Daikin Ind Ltd 包みパツキン用外被の製法
JPH01258771A (ja) * 1988-02-24 1989-10-16 Hoechst Ag 熱可塑性弗素樹脂より成る粉末被覆物の製造方法
JPH04131167A (ja) * 1989-12-19 1992-05-01 Hoechst Ag 弗素化された熱可塑性樹脂を用いた粉末被覆法
WO1997021776A1 (fr) * 1995-12-08 1997-06-19 Daikin Industries, Ltd. Materiau fluore pour composition de revetement et procede d'enrobage au moyen de cette composition
WO1997040089A1 (fr) * 1996-04-24 1997-10-30 Daikin Industries, Ltd. Fluoropolymere en poudre et procede de preparation
WO1998046426A1 (fr) * 1997-04-15 1998-10-22 Daikin Industries, Ltd. Materiau composite anti-corrosion
WO2000058414A1 (fr) * 1999-03-29 2000-10-05 Daikin Industries, Ltd. Composition de revetement de resine fluoree en poudre
WO2001025354A1 (fr) * 1999-10-04 2001-04-12 Daikin Industries, Ltd. Procede antirouille dans lequel une composition de revetement pulverulent a base de fluororesine thermodurcissable est utilisee
JP2003002979A (ja) * 2001-06-18 2003-01-08 Daikin Ind Ltd フッ素系重合体粉末製造方法
JP2003003111A (ja) * 2001-06-18 2003-01-08 Daikin Ind Ltd 粉体塗料

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006113836A1 (fr) * 2005-04-19 2006-10-26 Dupont-Mitsui Fluorochemicals Company, Ltd. Film de revetement a base de fluororesine
JP2009502568A (ja) * 2005-07-28 2009-01-29 三井・デュポンフロロケミカル株式会社 フルオロポリマーフィルムによる積層物およびフィルム形成用フルオロポリマー
JP2008303316A (ja) * 2007-06-08 2008-12-18 Asahi Glass Co Ltd 塗料組成物
JP2019181337A (ja) * 2018-04-04 2019-10-24 Ａｇｃ株式会社 積層体の製造方法
JP7059764B2 (ja) 2018-04-04 2022-04-26 Ａｇｃ株式会社 積層体の製造方法
WO2020004197A1 (fr) * 2018-06-26 2020-01-02 日本フッソ工業株式会社 Composition de revêtement en poudre pouvant être cuite contenant une résine fluorée et composition de revêtement liquide et revêtement et corps revêtu comprenant cette composition de revêtement en poudre pouvant être cuite ou cette composition de revêtement liquide
JPWO2020004197A1 (ja) * 2018-06-26 2020-07-02 日本フッソ工業株式会社 フッ素樹脂を含む焼付け用の粉体塗料組成物および液状塗料組成物、この焼付け用の粉体塗料組成物または液状塗料組成物を含む被膜ならびに被膜体
CN112262184A (zh) * 2018-06-26 2021-01-22 日本扶桑工业株式会社 含有氟树脂的烘烤用粉末涂料组成物和液状涂料组成物、含有该烘烤用粉末涂料组成物或液状涂料组成物的薄膜以及薄膜体
US20210206990A1 (en) * 2018-06-26 2021-07-08 Nippon Fusso Co., Ltd Fluororesin-containing bakeable powder coating composition and liquid coating composition, and coating and coated body comprising this bakeable powder coating composition or liquid coating composition
EP4032430A4 (fr) * 2019-09-20 2023-11-01 Daikin Industries, Ltd. Copolymère contenant du fluor
CN114566655A (zh) * 2020-11-27 2022-05-31 国家能源投资集团有限责任公司 碳纳米管/碳纤维纸复合电极材料及其制备方法和全钒液流电池

Also Published As

Publication number Publication date
JPWO2004065504A1 (ja) 2006-05-18

Similar Documents

Publication Publication Date Title
JP3263845B2 (ja) 含フッ素塗料用材料を用いた被覆方法
JP4952505B2 (ja) プライマー組成物
US6403213B1 (en) Highly filled undercoat for non-stick finish
EP0056280B2 (fr) Objets durables revêtus de polymères fluorés
JP6432521B2 (ja) 液体プライマー組成物及びそれを用いた積層体
JP2002514181A (ja) リンを含有するフルオロモノマーおよびそれらのポリマー
JP6149739B2 (ja) プライマー組成物及びそれを用いた積層体
JP7136105B2 (ja) 含フッ素共重合体組成物
JP6819717B2 (ja) 被覆組成物及び被覆物品
WO2003106556A1 (fr) Composition de dispersion aqueuse de resine fluoree et composition de revetement a base d'eau fluoree
JP2006206637A (ja) エチレン／テトラフルオロエチレン系共重合体粉体及びそれを塗装してなる物品
JP6519481B2 (ja) 粉体プライマー組成物及びそれを用いた積層体
WO2004065504A1 (fr) Composition de poudre pulverulente, procede de formation de film de revetement et produit revetu
JP4254536B2 (ja) 含フッ素塗料組成物、塗膜及び塗装物
KR20010006032A (ko) 내약품성 복합재
JP5756262B2 (ja) 塗料組成物、該塗料組成物を用いた被膜製造方法および被膜体
JP3975690B2 (ja) 含フッ素塗料用材料およびそれを用いた被覆方法
JP2022046456A (ja) 塗料組成物及び塗装品
JPH10272744A (ja) 耐候性複合材
JPH10329282A (ja) 意匠性を維持した複合材
JPH10329280A (ja) バインダー層を介さない複合材
KR20240026237A (ko) 피복용 조성물 및 피복 물품
WO2021261450A1 (fr) Peinture et procédé de production de peinture, article peint et procédé de production d'article peint
ITMI950088A1 (it) Procedimento per ancorare un perfluoropolimero ad un substrato

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2005508027

Country of ref document: JP

122 Ep: pct application non-entry in european phase