Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/02—Elements
  • C08K3/04—Carbon
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
  • C08K5/0041—Optical brightening agents, organic pigments

Definitions

• the present invention relates to non-streaking black color formulations for polycarbonate-siloxane resins and blends containing polycarbonate-siloxane resins.
• the present invention further relates to resins containing the non-streaking black color formulations.
• Polycarbonate-siloxane copolymers and blends contain two immiscible phases.
• the median siloxane domain size is greater than 100 nanometers, the matrix appears translucent or even opaque depending on part thickness, which creates several colorability problems.
• size corresponds to the largest dimension of the domain.
• Domain sizes are characterized using microscopic techniques such as Scanning Electron Microscopy, Transmission Electron Microscopy. Typically, median size is determined from the distribution of the domain sizes measured according to the SEM or TEM techniques. Since the siloxane domains in these copolymers and blends are of a non-negligible size compared to the wavelengths of visible light, and with the refractive index of these domains being significantly different from the polycarbonate phase, a significant amount of light scattering occurs.
• jet-black colored resins are usually obtained by addition of carbon black.
• Commercial jet-black color formulations in polycarbonate and polycarbonate blends typically contain between 0.2 and 0.5% of carbon black.
• such formulations cannot be incorporated into polycarbonate- siloxane copolymers and blends having a median siloxane domain size greater than 100 nanometers because streaks (also referred to as knit-lines or flow-lines) appear in the finished article made from the colored resin.
• jet-black polycarbonate formulations contain between 0.2 and 0.5% carbon black, such as commercially available jet-black polycarbonate compositions like GE Plastics (USA) LEXAN 141R-701. Black pigments used for coloring plastics are listed for example in "Coloring Plastics", ed. Thomas G. Webber, Wiley Interscience, NY (1979), p.38-39. Knit-lines, or "streaks" appear of a darker color as a result of the different siloxane domain size distribution in the streak. The average siloxane domain size being usually smaller in the knit-line region, less light will be scattered there thus providing more color depth. As a result, the streaks will appear darker.
• the present invention relates to a resin composition
• a resin composition comprising:
• a polycarbonate-siloxane copolymer resin comprising polycarbonate units and polyorganosiloxane units wherein the median siloxane domain size is greater than 100 nanometers;
• a colorant combination of at least one organic colorant and at least one inorganic colorant wherein the combination of the organic and inorganic colorant results in a black molded part with an L* value of less than about 29 and C* value less than about 1.5 (specular component included) or L* value of less than 8 and C* value of less than about 3 (specular component excluded).
• the present invention relates to a method of reducing the visibility of knit lines in a composition comprising a polycarbonate-polysiloxane copolymer, the method comprising incorporating a colorant combination comprising at least one organic colorant and at least one colored inorganic colorant, such that the combination results in a black molded part with an L* value of less than about 29 and C* value of less than about 1.5 and C* value of less than about 1.5 (specular component included) or L* value of less than 8 and C* value of less than about 3 (specular component excluded).
• specular component corresponds to specular reflection as defined in ASTM E284.
• a color is defined by 3 attributes: lightness, chroma and hue. In jet black articles, hue is not very relevant because lightness and chroma are very low. A jet black color is about the lowest chroma and lowest lightness color that can be made. A black color has a much broader definition, i.e. can tolerate higher L* and C* values. A jet black color is a subset of black colors that corresponds to the lowest lightness and chroma.
• the present invention relates to jet-black formulations with L* less than about 29 and C* less than about 1.5.
• C* corresponds to a measure of chroma defined by ASTM E284 as the attribute of color used to indicate the degree of departure of the color from a gray of the same lightness.
• Colorant combinations according to the present invention contain at least one organic colorant resulting in a dark color and at least one colored inorganic pigment resulting in a dark color.
• the colored inorganic pigment will disperse throughout the resin matrix giving a dark color, but not dark enough to be considered a jet-black. Beyond a certain total colored inorganic pigment loading the knit lines will disappear.
• the colored inorganic pigment is present in at least 0.5 weight %, based on the weight of the resin; preferably at least about 0.75 weight % based on the weight of the resin; and more preferably at least about 1 weight %, based on the weight of the resin.
• the organic colorant present in the colorant combination further improves the color appearance and provides the final jet-black color.
• the jet-black appearance can be obtained in the color formulations of this invention with a minimum of 0.3% carbon black and/or combination of organic matter resulting in a black color in addition to the colored inorganic pigments.
• Suitable organic colorants include but are not limited to: carbon black (e.g. pigment black 7), organic dyes and pigments such as azo dyes, methine dyes, coumarins, pyrazolones, quinophtalones, quinacridones, perinones, anthraquinones, phtalocyanines, perylene derivatives, anthracene derivatives, indigoid and thioindigoid derivatives, imidazole derivatives, naphtalimide derivatives, xanthenes, thioxanthenes, azine dyes, rhodamines, and all their derivatives.
• carbon black e.g. pigment black 7
• organic dyes and pigments such as azo dyes, methine dyes, coumarins, pyrazolones, quinophtalones, quinacridones, perinones, anthraquinones, phtalocyanines, perylene derivatives, anthrac
• Suitable colored inorganic pigments include but are not limited to: metal oxides, mixed metal oxides, titanates, aluminates, carbonates, iron oxides, chromium oxides, ultramarines and metal sulfides (including rare-earth sulfides).
• colored organic pigments include pigments with low lightness and low chroma such as Pigment Black 28 or Pigment Black 30. Such pigments are for instance available from Shepherd Color Company (Cleveland, OH - USA) under the references "Black 1", “Black 376", “Black 462", and "Black 41 1".
• the total amount of inorganic pigments is greater than or equal to about 0.5% and the total amount of organic colorants is greater than or equal to about 0.3%), based on the weight of the resin.
• the total loading of colored inorganic pigments is greater than or equal to about 0.75%) and the total loading of organic colorant greater than or equal to about 0.5%, based on the weight of the resin.
• the total loading of colored inorganic pigments is greater than or equal to about 1% and the total loading of organic colorant greater than or equal to about 0.8%, based on the weight of the resin.
• the colorant combination comprises carbon black and at least one inorganic colorant.
• the colorant combination comprises carbon black, an additional organic colorant and at least one inorganic colorant.
• the colorant combination comprises carbon black, at least two organic colorants that produce black, and at least one inorganic colorant.
• Example of organic colorants that produce a black color include but are not limited to mixtures of Solvent Green 3 and Solvent Red 135 or Solvent Green 3, Solvent Violet 13, and Pigment Blue 15:4 as referenced in the Color Index
• the colorant combination comprises a minimum of about 0.2 to about 0.3 weight % of carbon black, based on the weight of the resin. In another embodiment, the colorant combination comprises a total of two organic colorants at a minimum of about 0.5 weight %, based on the weight of the resin.
• the color formulations disclosed in this invention are usually compounded with the polycarbonate-siloxane copolymer or blend.
• polycarbonate includes polymers having structural units of the formula (I):
• R 1 is an aromatic organic radical and, more preferably, a radical of the formula (II):
• each of A and A is a monocyclic divalent aryl radical and Y is a bridging radical having zero, one, or two atoms which separate A from A .
• one atom separates A from A .
• radicals of this type are -O-, -S-, -S(O)-, -S(0 2 )-, -C(O)-, methylene, cyclohexyl- methylene, 2-[2,2,l]-bicycloheptylidene, ethylidene, isopropylidene, neopentylidene, cyclohexylidene, cyclopentadecylidene, cyclododecylidene, adamantylidene, and the
• the bridging radical Y 1 can be a hydrocarbon group or a saturated hydrocarbon group such as methylene, cyclohexylidene or isopropylidene.
• Polycarbonates can be produced by the reaction of dihydroxy compounds in which only one atom separates A 1 and A 2 .
• dihydroxy compound includes, for example, bisphenol compounds having general formula (III) as follows:
• R a and R b each independently represent hydrogen, a halogen atom, or a monovalent hydrocarbon group; p and q are each independently integers from 0 to 4; and X a represents one of the groups of formula (IV):
• R c and R d each independently represent a hydrogen atom or a monovalent linear or cyclic hydrocarbon group, and R e is a divalent hydrocarbon group.
• dihydroxy compounds include dihydric phenols and the dihydroxy-substituted aromatic hydrocarbons such as those disclosed by name or formula (generic or specific) in U.S. Patent No. 4,217,438,.
• a nonexclusive list of specific examples of the types of bisphenol compounds that may be represented by formula (III) includes the following: l ,l -bis(4-hydroxyphenyl) methane; 1 , 1 -bis(4-hydroxyphenyl) ethane; 2,2-bis(4-hydroxyphenyl) propane (hereinafter "bisphenol A” or "BPA”); 2,2-bis(4-hydroxyphenyl) butane; 2,2-bis(4- hydroxyphenyl) octane; l ,l -bis(4-hydroxyphenyl) propane; l ,l-bis(4-hydroxyphenyl) n-butane; bis(4-hydroxyphenyl) phenylmethane; 2,2-bis(4-hydroxy-l-methylphenyl) propane; l ,l-bis(4-hydroxy-t-butylphenyl) propane; bis(hydroxyaryl) alkanes such as 2,2-bis(4-hydroxy-3-bromophenyl) propane
• polycarbonates resulting from the polymerization of two or more different dihydric phenols or a copolymer of a dihydric phenol with a glycol or with a hydroxy- or acid-terminated polyester or with a dibasic acid or with a hydroxy acid or with an aliphatic diacid in the event a carbonate copolymer rather than a homopolymer is desired for use.
• useful aliphatic diacids have about 2 to about 40 carbons.
• a preferred aliphatic diacid is dodecandioic acid.
• Siloxane-polycarbonate block copolymers have been recognized for their low temperature ductility and flame retardancy and may also be utilized as the matrix for incorporating the phosphorescent pigments.
• These block copolymers can be made by introducing phosgene under interfacial reaction conditions into a mixture of a dihydric phenol, such as BPA, and a hydroxyaryl-terminated polydiorganosiloxane. The polymerization of the reactants can be facilitated by use of a tertiary amine catalyst.
• hydroxyaryl-terminated polydiorganosiloxanes that may be used include phenol-siloxanes of the formula (V)
• each R may be the same or different and is selected from the group of radicals consisting of hydrogen, halogen, C(i -8 ) alkoxy, C(i -8) alkyl and C( 6- ⁇ 3 ) aryl
• R 1 is a C( 2-8 ) divalent aliphatic radical
• R 2 is selected from the same or different Co- ⁇ * monovalent organic radicals
• n is an integer greater than or equal to 1 , preferably greater than or equal to about 10, more preferably greater than or equal to about 25 and most preferably greater than or equal to about 40. It is also preferred to have n be an integer less then or equal to 1000, preferably less than or equal to 100, more preferably less than or equal to about 75 and most preferably less than or equal to about 60.
• n is less than or equal to 50.
• Particularly preferred hydroxyaryl- terminated polydiorganosiloxanes are those where R 2 is methyl and R is hydrogen or methoxy and located in the ortho position to the phenolic substituent and where R 1 is propyl and located ortho or para to the phenolic substituent.
• radicals included within R in the above formula (V) are hydrogen, halogen radicals, such as bromo, and chloro; alkyl radicals such as methyl, ethyl, and propyl; alkoxy radicals such as methoxy, ethoxy, and propoxy; aryl radicals such as phenyl, chlorophenyl, and tolyl.
• Radicals included within R 1 are, for example, dimethylene, trimethylene and tetramethylene.
• Radicals included within R 2 are, for example, C ( M 3) alkyl radicals, haloalkyl radicals such as trifluoropropyl and cyanoalkyl radicals; aryl radicals such as phenyl, chlorophenyl and tolyl.
• R is preferably methyl, or a mixture of methyl and trifluoropropyl, or a mixture of methyl and phenyl.
• the siloxane-polycarbonate block copolymers have a weight-average molecular weight (Mw, measured, for example, by Gel Permeation Chromatography, ultra- centrifugation, or light scattering) of greater than or equal to about 10,000, preferably greater than or equal to about 20,000. Also preferred is a weight average molecular weight of less than or equal to about 200,000, preferably less than or equal to about 100,000. It is generally desirable to have the polyorganosiloxane units contribute about 0.5 to about 80 wt%> of the total weight of the siloxane-polycarbonate copolymer.
• the chain length of the siloxane blocks corresponds to about 10 to about 100 chemically bound organosiloxane units. They can be prepared such as described in for example US-A-5,530,083, incorporated herein by reference in its entirety.
• compositions of the invention may comprise further additives like anti-oxidants, mold release agents, flame retarding agents, or any combination of colorants to achieve the desired aesthetic look under day light and UV stabilizers (e.g. less than about 3 wt.% of the total composition) as is known in the art.
• particulate inorganic fillers may be added up to about 15 wt. %, preferably no more than 10 wt. %> in order to impart desired processing and physical characteristics to the molding composition.
• Such fillers include but are not limited to glass fibers, glass microspheres, wollastonite, ground quartz and the like of a particulate inorganic filler.
• Such characteristics include thermal stability, increased density, stiffness, lower creep, and texture.
• the largest dimension of the particles may vary, and can be less than or equal to about 50 micrometers, with less than or equal to about 15 micrometers preferred, and less than or equal to about 10 micrometers more preferred. Also preferred is minimum dimension of greater than or equal to about 0.1 micrometers, with greater than or equal to about 1 micrometer more preferred, and greater than or equal to about 2 micrometers especially desired.
• Resin made from the color compositions disclosed in this invention can be produced according to all known processes for the manufacture of compositions comprising thermoplastic resins.
• the compositions are preferably prepared by melt mixing the required component followed by extrusion and pelletization of the extrudate. Note that it is also possible - but not preferred - to use the color compositions of this invention in a masterbatch form to color polycarbonate-siloxane copolymers or blends directly at the molding machine provided that the molding machine allows sufficient mixing of the total resin composition.
• the polycarbonate-siloxane block copolymer may be blended with other polymers, for example a polycarbonate homopolymer, to form a resin.
• Blends may be prepared according to mixing techniques well known in the art. In general, the different components of the blend are dry mixed mechanically (blenders/high speed mixers), fed to an extruder where the different resins are melted, and the different phases of the blend will get dispersed. Colorants can be added to the extruder along with the resin components as a dry mixture, added separately as a dry mixture, or added separately downstream. Colorants can also be added during the molding process in the form of a master batch/concentrate.
• the resin formulations from the compositions of the invention are, for instance, suitable for making objects that can be used in applications such as business equipment, computers and peripherals, consumer electronics, telecom (cell phones, personal data assistants, wireless devices, enclosures), in the automotive industry (knobs, dashboards and interior/exterior trim), medical devices, and protective helmets.
• Batches (A) through (C) represent state-of-the-art formulations for a jet-black color as used in many polycarbonate and polycarbonate blends currently available on the market. As seen in Table 1 , formulations (A) through (C) contain respectively 0.2, 0.35 and 0.5 wt. % of carbon black (here Pigment Black 7 from Monarch). Formulation (D) is similar to (C) but also contains 0.8 wt. %> titanium dioxide (Dupont GE01) to avoid the streaks as disclosed in the prior art by Maruvada and co-workers. Batch (E) has been prepared using a color formulation as described in this invention.
• batch (E) represents a typical formulation of this invention with a total of about 0.63%> of organic colorants (0.5%> pigment black 7 and 0.13% of pigment blue 15:4) and 0.85%> of colored inorganic pigments (0.25%> of pigment red 265 and 0.60%> of pigment green 50). All color measurements were performed using a MacBeth ColorEye 7000A integrating sphere spectrophotometer using D65 illuminant, 10 Degree observer. Color data are reported using the CIE1976 LCh color space. When molded objects have a textured surface, color measurements made with specular component excluded are the preferred method.
• Color formulations (A) to (F) were compounded with the polycarbonate-siloxane copolymer matrix using a Prism twin-screw extruder and then pelletized. Pellets were then injection-molded in a special tool that has the characteristics of enhancing the visibility of appearance defects due to the presence of cuts, ribs, thickness/texture variations and other intricate geometries in the part. Flat non-textured color chips were also molded at a thickness of 2.54 mm for color analysis. All color measurements were performed using a MacBeth ColorEye 7000A integrating sphere spectrophotometer using D65 illuminant, 10 Degree observer for both Specular Component Included and Specular Component Excluded modes. Color data are reported using the CIE1976 LCh color space.
• Formulations (E) and (F) exhibited a jet black color as evidenced by an L* value of less than about 29 and C* value of less than about 1.5 and C* value of less than about 1.5 (specular component included) or L* value of less than 8 and C* value of less than about 3 (specular component excluded).
• Formulation (A) had slightly milky, grayish black appearance instead of the jet-black appearance.
• Formulation (B) shows some slight improvements over (A) but cannot be considered a jet black.
• Formulation (D) had a grayish black appearance instead of jet-black due to the presence of titanium dioxide in the color formulation but did not exhibit significant streaking.
• Formulation (C) is visually very close to a jet black color which is also evidenced by the color data.
• Formulations (A) to (C) showed visible streaks (knit-lines/flow-lines) that appeared darker than the overall color. No visible streaks, knit-lines or flow-lines were visible in formulation (E) thus illustrating the advantages of the formulations disclosed in the present invention.
• formulation (E) had a true jet-black color as illustrated by an L* value of 28.46 and C* value of 1.3 (specular component included) or L* value of 6.13 and C* value of 2.12 (specular component excluded)
• Batches (F) in Table 1 illustrates another example of a color formulation of this invention with improved jet-black color and absence of knit-lines, streaks or flow- lines.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Silicon Polymers (AREA)
• Polyesters Or Polycarbonates (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (2)

Family

ID=32324481

Family Applications (1)

Country Status (8)

Cited By (1)

Families Citing this family (29)

Citations (3)

Family Cites Families (3)

• 2002
  • 2002-11-21 US US10/301,139 patent/US6822041B2/en not_active Expired - Lifetime
• 2003
  • 2003-10-23 JP JP2004555341A patent/JP2006507393A/ja active Pending
  • 2003-10-23 CN CNB2003801039225A patent/CN100341931C/zh not_active Expired - Fee Related
  • 2003-10-23 AU AU2003284925A patent/AU2003284925A1/en not_active Abandoned
  • 2003-10-23 AT AT03779245T patent/ATE462758T1/de not_active IP Right Cessation
  • 2003-10-23 DE DE60331954T patent/DE60331954D1/de not_active Expired - Lifetime
  • 2003-10-23 EP EP03779245A patent/EP1578861B1/en not_active Expired - Lifetime
  • 2003-10-23 WO PCT/US2003/033827 patent/WO2004048460A1/en not_active Ceased

Patent Citations (3)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events