WO2003026794A1 - Feuille adsorbante et filtre de purification d'air - Google Patents
Feuille adsorbante et filtre de purification d'air Download PDFInfo
- Publication number
- WO2003026794A1 WO2003026794A1 PCT/JP2002/008896 JP0208896W WO03026794A1 WO 2003026794 A1 WO2003026794 A1 WO 2003026794A1 JP 0208896 W JP0208896 W JP 0208896W WO 03026794 A1 WO03026794 A1 WO 03026794A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sheet
- powder resin
- thermoplastic powder
- adsorbent
- air
- Prior art date
Description
Claims