WO2000024806A1 - Reinigung von polycarbonat enthaltenden lösungen - Google Patents
Reinigung von polycarbonat enthaltenden lösungen Download PDFInfo
- Publication number
- WO2000024806A1 WO2000024806A1 PCT/EP1999/007653 EP9907653W WO0024806A1 WO 2000024806 A1 WO2000024806 A1 WO 2000024806A1 EP 9907653 W EP9907653 W EP 9907653W WO 0024806 A1 WO0024806 A1 WO 0024806A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polycarbonate
- washing
- washing liquid
- liquid
- phase
- Prior art date
Abstract
Description
Claims