WO1997043119A1 - Feuille metallique recouverte d'une resine extremement transparente et presentant une bonne adhesion - Google Patents

Feuille metallique recouverte d'une resine extremement transparente et presentant une bonne adhesion Download PDF

Info

Publication number
WO1997043119A1
WO1997043119A1 PCT/JP1997/001623 JP9701623W WO9743119A1 WO 1997043119 A1 WO1997043119 A1 WO 1997043119A1 JP 9701623 W JP9701623 W JP 9701623W WO 9743119 A1 WO9743119 A1 WO 9743119A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin
layer
metal plate
coated metal
film
Prior art date
Application number
PCT/JP1997/001623
Other languages
English (en)
Japanese (ja)
Inventor
Takayuki Kaneko
Takashi Minamigi
Tetsuo Nakamoto
Original Assignee
Toyo Kohan Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toyo Kohan Co., Ltd. filed Critical Toyo Kohan Co., Ltd.
Priority to AU27885/97A priority Critical patent/AU2788597A/en
Priority to JP09540740A priority patent/JP3090956B2/ja
Publication of WO1997043119A1 publication Critical patent/WO1997043119A1/fr

Abstract

On décrit une feuille métallique à revêtement extrêmement transparent, dans laquelle une couche de résine molle lisse les irrégularités superficielles d'une feuille métallique et de couches imprimées et présente d'excellentes propriétés d'adhésion et de transparence. Cette feuille métallique recouverte d'une résine comprend donc un substrat, composé d'une feuille métallique (S) dont la rugosité superficielle est représentée par une hauteur moyenne de ligne médiane (Ra) supérieure à 0 m mais ne dépassant pas 10 m, et dont au moins un côté a été stratifié à partir du substrat, à l'aide successivement et dans cet ordre, d'une couche de peinture colorante (D), d'une couche de résine molle (C), d'une couche d'adhésif (B) et d'un film de résine transparente (A).
PCT/JP1997/001623 1996-05-14 1997-05-14 Feuille metallique recouverte d'une resine extremement transparente et presentant une bonne adhesion WO1997043119A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU27885/97A AU2788597A (en) 1996-05-14 1997-05-14 Metallic sheet covered with highly clear resin and having work adhesiveness
JP09540740A JP3090956B2 (ja) 1996-05-14 1997-05-14 加工密着性に優れた高鮮映性樹脂被覆金属板

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP8/142378 1996-05-14
JP14237896 1996-05-14

Publications (1)

Publication Number Publication Date
WO1997043119A1 true WO1997043119A1 (fr) 1997-11-20

Family

ID=15313989

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP1997/001623 WO1997043119A1 (fr) 1996-05-14 1997-05-14 Feuille metallique recouverte d'une resine extremement transparente et presentant une bonne adhesion

Country Status (8)

Country Link
JP (1) JP3090956B2 (fr)
KR (1) KR100366984B1 (fr)
CN (1) CN1103283C (fr)
AU (1) AU2788597A (fr)
ID (1) ID17403A (fr)
MY (1) MY121257A (fr)
TW (1) TW434145B (fr)
WO (1) WO1997043119A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005011977A1 (fr) * 2003-07-30 2005-02-10 Dainippon Ink And Chemicals, Inc. Feuille stratifiee servant a former un article
JP2010201856A (ja) * 2009-03-05 2010-09-16 Hokkai Can Co Ltd 缶体材料被覆用印刷ポリエステルフィルム、その製造方法及びそれを用いる缶体
CN103553437A (zh) * 2013-10-26 2014-02-05 桂林理工大学 一种高阻燃石英石板材的制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101058352B1 (ko) 2009-09-08 2011-08-22 정영철 자외선 미러 코팅용 도료 조성물
US8409678B2 (en) 2010-04-06 2013-04-02 Pao Yi Technology Co., Ltd. Thin metal casing with plastic part and manufacturing method thereof

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0255126A (ja) * 1988-08-22 1990-02-23 Toyo Kohan Co Ltd 高鮮映性を有する樹脂被覆金属板の製造方法
JPH04238026A (ja) * 1991-01-22 1992-08-26 Dainippon Printing Co Ltd 高鮮映積層金属板およびそれに使用する化粧シート

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
MY136271A (en) * 1994-12-29 2008-09-30 Toyo Kohan Co Ltd A resin-coated metal sheet with higher vivid reflectivity having the excellent workable adhesion strength

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0255126A (ja) * 1988-08-22 1990-02-23 Toyo Kohan Co Ltd 高鮮映性を有する樹脂被覆金属板の製造方法
JPH04238026A (ja) * 1991-01-22 1992-08-26 Dainippon Printing Co Ltd 高鮮映積層金属板およびそれに使用する化粧シート

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005011977A1 (fr) * 2003-07-30 2005-02-10 Dainippon Ink And Chemicals, Inc. Feuille stratifiee servant a former un article
US7553548B2 (en) 2003-07-30 2009-06-30 Dainippon Ink & Chemicals, Inc. Laminated sheet for molding
JP2010201856A (ja) * 2009-03-05 2010-09-16 Hokkai Can Co Ltd 缶体材料被覆用印刷ポリエステルフィルム、その製造方法及びそれを用いる缶体
CN103553437A (zh) * 2013-10-26 2014-02-05 桂林理工大学 一种高阻燃石英石板材的制备方法

Also Published As

Publication number Publication date
ID17403A (id) 1997-12-24
MY121257A (en) 2006-01-28
KR20000010887A (ko) 2000-02-25
JP3090956B2 (ja) 2000-09-25
CN1222881A (zh) 1999-07-14
AU2788597A (en) 1997-12-05
TW434145B (en) 2001-05-16
CN1103283C (zh) 2003-03-19
KR100366984B1 (ko) 2003-09-19

Similar Documents

Publication Publication Date Title
JPH04500638A (ja) 改良したフッ素ポリマー―金属ラミネート
CN106827743A (zh) 具有金属高光层的表面覆膜结构
JP3691068B2 (ja) 加工密着性に優れた高鮮映性樹脂被覆金属板
KR20010093139A (ko) 화장판 적층용 수지 필름 및 그 수지 필름을 적층한 화장판
WO2007013232A1 (fr) Plaque ayant deja un revetement et procede servant a produire celle-ci
JP2010089399A (ja) 加飾樹脂成形品及びその製造方法
CN112659709A (zh) 具有表面触感和透明电镀效果的ins膜及其制备方法
WO1997043119A1 (fr) Feuille metallique recouverte d'une resine extremement transparente et presentant une bonne adhesion
KR20080014269A (ko) 알루미늄 포일형 고광택시트
CN212046306U (zh) 具有表面触感和透明电镀效果的ins膜
JP5016577B2 (ja) 化粧金属板の製造方法
JPH0623909A (ja) 高鮮映積層金属板およびその製造法
JP2018062114A (ja) 樹脂成形体用表皮材、合成樹脂成形体、及び合成樹脂成形体の製造方法
JP4853852B2 (ja) 転写箔
CN211165664U (zh) 一种拉丝彩涂板
JP2007030384A (ja) 干渉模様を抑えたクリア塗装ステンレス鋼板
WO2001000411A1 (fr) Film de resine d'impression destine a la stratification de feuille stratifiee decorative de grande nettete presentant une excellente usinabilite et feuille stratifiee decorative de grande nettete stratifiee avec ces films de resine
CN1195623C (zh) 高性能金属材料及其制备方法
JP2006315248A (ja) 化粧フィルムおよび化粧板
JPH0255126A (ja) 高鮮映性を有する樹脂被覆金属板の製造方法
JP4280658B2 (ja) 塗膜密着性に優れたクリア塗装ステンレス鋼板
JP7294560B1 (ja) 化粧材
JP2009018591A (ja) 化粧鋼板の製造方法
JP6821466B2 (ja) 積層シートおよび積層板
JP2000280403A (ja) 高光輝性印刷ｐｅｔフィルムラミネート鋼板

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 97194566.7

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE HU IL IS JP KE KG KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG US UZ VN YU AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1019980709034

Country of ref document: KR

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA

WWP Wipo information: published in national office

Ref document number: 1019980709034

Country of ref document: KR

WWG Wipo information: grant in national office

Ref document number: 1019980709034

Country of ref document: KR