WO1997026381A1 - Gewinnung von roheisen, ferro- und/oder buntmetall-legierungen zusammen mit synthetischer hochofenschlacke aus müllverbrennungsrückständen und stahlwerksschlacke - Google Patents
Gewinnung von roheisen, ferro- und/oder buntmetall-legierungen zusammen mit synthetischer hochofenschlacke aus müllverbrennungsrückständen und stahlwerksschlacke Download PDFInfo
- Publication number
- WO1997026381A1 WO1997026381A1 PCT/AT1997/000006 AT9700006W WO9726381A1 WO 1997026381 A1 WO1997026381 A1 WO 1997026381A1 AT 9700006 W AT9700006 W AT 9700006W WO 9726381 A1 WO9726381 A1 WO 9726381A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- slag
- alloys
- blast furnace
- waste incineration
- reduction
- Prior art date
Abstract
Description
Claims