WO1995018185A1 - Verfahren zur herstellung eines umweltfreundlichen werkstoffs, der bei dem verfahren erhaltene werkstoff und seine verwendung - Google Patents
Verfahren zur herstellung eines umweltfreundlichen werkstoffs, der bei dem verfahren erhaltene werkstoff und seine verwendung Download PDFInfo
- Publication number
- WO1995018185A1 WO1995018185A1 PCT/DE1994/001537 DE9401537W WO9518185A1 WO 1995018185 A1 WO1995018185 A1 WO 1995018185A1 DE 9401537 W DE9401537 W DE 9401537W WO 9518185 A1 WO9518185 A1 WO 9518185A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- castor oil
- catalyst
- filler
- weight
- mixed
- Prior art date
Abstract
Description
Claims