Classifications

• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
  • C01G49/00—Compounds of iron
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
  • C01G49/00—Compounds of iron
  • C01G49/0018—Mixed oxides or hydroxides
  • C01G49/0036—Mixed oxides or hydroxides containing one alkaline earth metal, magnesium or lead
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
  • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
  • C04B35/26—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on ferrites
  • C04B35/2683—Other ferrites containing alkaline earth metals or lead
• • H—ELECTRICITY
  • H01—ELECTRIC ELEMENTS
  • H01F—MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
  • H01F1/00—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties
  • H01F1/01—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials
  • H01F1/03—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity
  • H01F1/032—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials
  • H01F1/10—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials non-metallic substances, e.g. ferrites, e.g. [(Ba,Sr)O(Fe2O3)6] ferrites with hexagonal structure
  • H01F1/11—Magnets or magnetic bodies characterised by the magnetic materials therefor; Selection of materials for their magnetic properties of inorganic materials characterised by their coercivity of hard-magnetic materials non-metallic substances, e.g. ferrites, e.g. [(Ba,Sr)O(Fe2O3)6] ferrites with hexagonal structure in the form of particles

Definitions

• the invention relates to a method for producing barium or strontium hexaferrite powder for the production of permanent magnets, be i in which the raw material mixture homogenized with the addition of water, the iron oxide and barium or. Contains strontium carbonate as solids, which is reaction fired to hexaferrite.
• the magnetic quality of the finished permanent magnet essentially depends on the microcrystalline nature of the reaction-fired hexaferrite powder, which is essentially due to the preparation of the raw material mixture.
• Such a method has weak points in that, on the one hand, dewatering the raw material mixture causes costs and, on the other hand, the magnetic values for the hexaferrite powder that can be achieved in the known method are limited. Furthermore, the strontium carbonate added as a solid causes a large part of the raw material costs.
• Strontium hexaferrite powder in which with the help of chemical coprecipitation from barium or strontium chlorides and iron chloride with the addition of a precipitating agent hexaferrite powder with good magnetic Properties is obtained.
• a precipitating agent hexaferrite powder with good magnetic Properties is obtained.
• the object of the invention is therefore to improve a method of the type mentioned at the outset in such a way that it becomes more economical on the one hand and on the other hand the magnetic properties of the hexaferrite powder are improved.
• a barium or strontium hydroxide solution is added to the raw material mixture, which at least partially replaces the barium or strontium carbonate.
• the invention is characterized in that the largest possible proportion of the carbonate added to the raw material mixture as a solid is replaced by a barium or strontium hydroxide solution in which the barium or strontiura oxide ions are present in a solvent.
• the raw materials are now mixed on an ionic basis in the mixing process. Due to the better miscibility of the raw material, the water content of the raw material mixture can be reduced.
• the barium or strontium oxide ions accumulate much more uniformly on the iron oxide particles, so that during the subsequent reaction firing the raw material is converted more completely into hexaferrite. This increases the economics of the process.
• An improvement in the magnetic characteristics of the hexaferrite powder results from the fact that, as a result of the improved mixing, the reaction-sintered hexaferrite has a very narrow grain band with extremely low-defect crystals.
• the barium or strontium oxide solution can be supplied much more easily when the raw materials are weighed in on a batch weigher than the carbonate supplied as a solid, which over
• Screw conveyors must be fed.
• the hydroxide is taken from a preliminary stage of the barium or strontium carbonate production process!
• the barium or strontium oxide solution is mixed with water containing carbon dioxide, whereby the carbonate precipitates, which is further processed as a solid.
• the process step of precipitation can be omitted.
• a further advantageous embodiment of the method is obtained when the press wastewater obtained during the wet pressing of the reaction-fired hexaferrite powder to the permanent magnet, which also contains barium or strontium oxide ions in solution, is used for the raw material batch. Since the processing of the hexaferrite powder for wet pressing usually uses an excess of barium or strontium oxide, the excess barium or strontium oxide is in the emerging press water. This is important because the barium or Strontiumoxidanteii is an important factor in raw material costs.
• the invention is explained in more detail below with the aid of a drawing representing an exemplary embodiment.
• the drawing shows the procedure in the manufacture of permanent magnets made of strontium hexaferrite.
• the components of the raw material mixture are weighed in one after the other.
• a certain proportion of water 2c is also added to the raw material mixture in order to achieve good miscibility.
• the individual components of the raw material batch are dimensioned in such a way that the stoichiometric relationship between strontium oxide (SrO) and iron oxide (Fe 2 O 3 ), responsible for the magnetic properties, of about 5.3 to 5.5 is fulfilled.
• a fine-grained and water-dispersed calcium silicate is added to the raw material mixture as small component 2e in a proportion of 0.5 to 0.8%, which acts as a glass binder in the ferrite formation process.
• the solid components iron oxide 2a and strontium carbonate 2b are fed to the feed weigher 1 via discharge screws, while the liquid components water 2c, strontium hydroxide 2d and the small component calcium silicate dispersion 2e are fed via pipelines.
• the raw material mixture is fed to a mixer 3, which is advantageously designed as an attritor or a stirring mixer.
• the raw material mixture homogenized in the attritor is then brought to the desired fineness in a continuous ball mill.
• the raw material mixture then passes through a centrifuge 4, in which excess water is centrifuged off, so that the concentrated raw material mixture is used for the highest possible throughput of the furnace designed as a continuous furnace 6 has the consistency required for the reaction fire.
• the water content in this stage of the process is only about 22-26%.
• the raw material mixture is conveyed from the centrifuge into the continuous furnace with the aid of a thick matter pump 5.
• a two-piston thick-matter pump is advantageously used, the hydraulically actuated pistons of which operate in tandem.
• reaction-fired hexaferrite in the form of granules, which are further processed into permanent magnets in subsequent production steps.
• the pasty magnetic material is compacted by means of a wet press 8 to form a green compact, which after drying is further processed in the subsequent finished sintering process in a sintering furnace 9 to the finished permanent magnet.
• the press water obtained in the wet press 8 has strontium oxide ions in dissolved form, since in the
• the press wastewater is drawn off from the discharge channels of the press tool using a water jet pump. Since the strontium oxide concentration in the press wastewater is relatively low, the discharged press water is passed through a concentrator 10 which the strontium oxide concentration is increased, for example, by repeatedly passing the waste water stream. The water with the concentrated strontium oxide is then pumped back through a pipe into the batch container 2d of the strontium oxide solution. A pipe 11, from which strontium hydroxide is fed, which is obtained as a preliminary product in the production of strontium carbonate, also opens into this batch container 2d!
• the strontium oxide solution obtained in the production of strontium carbonate can also be used directly can be obtained from the manufacturer of the strontium carbonate without having to carry out the intermediate step, which consists of the addition of water containing carbon dioxide to the strontium oxide ions.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Ceramic Engineering (AREA)
• Inorganic Chemistry (AREA)
• Manufacturing & Machinery (AREA)
• General Life Sciences & Earth Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Power Engineering (AREA)
• Materials Engineering (AREA)
• Structural Engineering (AREA)
• Geology (AREA)
• Compounds Of Iron (AREA)
• Hard Magnetic Materials (AREA)
• Manufacturing Cores, Coils, And Magnets (AREA)
• Enzymes And Modification Thereof (AREA)
• Peptides Or Proteins (AREA)
• Medicines Containing Antibodies Or Antigens For Use As Internal Diagnostic Agents (AREA)
• Preparation Of Compounds By Using Micro-Organisms (AREA)

Priority Applications (2)

Applications Claiming Priority (2)

Publications (1)

Family

ID=6346782

Family Applications (1)

Country Status (5)

Families Citing this family (2)

Citations (2)

Family Cites Families (2)

• 1988
  • 1988-02-06 DE DE3803596A patent/DE3803596C1/de not_active Expired
  • 1988-12-22 JP JP1500299A patent/JPH02503135A/ja active Pending
  • 1988-12-22 KR KR1019890701838A patent/KR960010785B1/ko not_active Expired - Fee Related
  • 1988-12-22 DE DE8989900575T patent/DE3875115D1/de not_active Expired - Lifetime
  • 1988-12-22 EP EP89900575A patent/EP0360842B1/de not_active Expired - Lifetime
  • 1988-12-22 WO PCT/DE1988/000774 patent/WO1989007088A1/de not_active Ceased

Patent Citations (2)

Non-Patent Citations (2)

Also Published As

Similar Documents

Legal Events