US20260035153A1 - Frangible film and packaging material - Google Patents

Frangible film and packaging material

Info

Publication number
US20260035153A1
US20260035153A1 US18/997,320 US202318997320A US2026035153A1 US 20260035153 A1 US20260035153 A1 US 20260035153A1 US 202318997320 A US202318997320 A US 202318997320A US 2026035153 A1 US2026035153 A1 US 2026035153A1
Authority
US
United States
Prior art keywords
layer
resin
frangible film
base material
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
US18/997,320
Other languages
English (en)
Inventor
Kento Shouji
Yasushi Watanabe
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DIC Corp
Original Assignee
DIC Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DIC Corp filed Critical DIC Corp
Publication of US20260035153A1 publication Critical patent/US20260035153A1/en
Pending legal-status Critical Current

Links

Images

Classifications

    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61J—CONTAINERS SPECIALLY ADAPTED FOR MEDICAL OR PHARMACEUTICAL PURPOSES; DEVICES OR METHODS SPECIALLY ADAPTED FOR BRINGING PHARMACEUTICAL PRODUCTS INTO PARTICULAR PHYSICAL OR ADMINISTERING FORMS; DEVICES FOR ADMINISTERING FOOD OR MEDICINES ORALLY; BABY COMFORTERS; DEVICES FOR RECEIVING SPITTLE
    • A61J1/00—Containers specially adapted for medical or pharmaceutical purposes
    • A61J1/03—Containers specially adapted for medical or pharmaceutical purposes for pills or tablets
    • A61J1/035—Blister-type containers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B65—CONVEYING; PACKING; STORING; HANDLING THIN OR FILAMENTARY MATERIAL
    • B65D—CONTAINERS FOR STORAGE OR TRANSPORT OF ARTICLES OR MATERIALS, e.g. BAGS, BARRELS, BOTTLES, BOXES, CANS, CARTONS, CRATES, DRUMS, JARS, TANKS, HOPPERS, FORWARDING CONTAINERS; ACCESSORIES, CLOSURES, OR FITTINGS THEREFOR; PACKAGING ELEMENTS; PACKAGES
    • B65D75/00—Packages comprising articles or materials partially or wholly enclosed in strips, sheets, blanks, tubes or webs of flexible sheet material, e.g. in folded wrappers
    • B65D75/28—Articles or materials wholly enclosed in composite wrappers, i.e. wrappers formed by associating or interconnecting two or more sheets or blanks
    • B65D75/30—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding
    • B65D75/32—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents
    • B65D75/325—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents one sheet being recessed, and the other being a flat not- rigid sheet, e.g. puncturable or peelable foil
    • B65D75/327—Articles or materials enclosed between two opposed sheets or blanks having their margins united, e.g. by pressure-sensitive adhesive, crimping, heat-sealing, or welding one or both sheets or blanks being recessed to accommodate contents one sheet being recessed, and the other being a flat not- rigid sheet, e.g. puncturable or peelable foil and forming several compartments
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/32—Layered products comprising a layer of synthetic resin comprising polyolefins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/32—Layered products comprising a layer of synthetic resin comprising polyolefins
    • B32B27/325—Layered products comprising a layer of synthetic resin comprising polyolefins comprising polycycloolefins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/30—Properties of the layers or laminate having particular thermal properties
    • B32B2307/31—Heat sealable
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/50—Properties of the layers or laminate having particular mechanical properties
    • B32B2307/582—Tearability
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/724—Permeability to gases, adsorption
    • B32B2307/7242—Non-permeable
    • B32B2307/7244—Oxygen barrier
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/724—Permeability to gases, adsorption
    • B32B2307/7242—Non-permeable
    • B32B2307/7246—Water vapor barrier
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2439/00—Containers; Receptacles
    • B32B2439/70—Food packaging
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2439/00—Containers; Receptacles
    • B32B2439/80—Medical packaging

Definitions

  • the present invention relates to a frangible film and a package.
  • PTP packaging is generally composed of a blister container in which a sheet formed of a resin system is provided with a recessed part for accommodating an item to be packaged, and an aluminum film serving as a lid material for covering the recessed part from the back of the blister container after a capsule or the like is accommodated in this recessed part.
  • a lid material that has a resin composition unified with that of the blister container (mono-materialized) and can be separated and recycled, is desirable.
  • a laminated film for PTP cover As a laminated film for PTP cover that can be used in place of the cover film for PTPs, where aluminum foil has been used so far, a laminated film for PTP cover has been reported, which has a heat-sealable resin (A) layer, a cyclic olefin-based resin (B) layer, and a heat-sealable heat-resistant resin (C) layer, and in which these layers are laminated in the order of layer (A)/layer (B)/layer (C), and the piercing strength measured using a metal needle with a tip diameter of 1 mm is less than 5 N (see, for example, PTL 1).
  • A heat-sealable resin
  • B cyclic olefin-based resin
  • C heat-sealable heat-resistant resin
  • the present invention aims to solve various problems in the related art and to achieve the following object. That is, it is an object to provide a frangible film that has excellent frangibility and is mono-materialized.
  • the present invention is based on the above-described findings of the present inventors, and the means for solving the above-described object is as follows. That is,
  • the various problems in the related art can be solved, the above-described object can be achieved, and a frangible film that has excellent frangibility and is mono-materialized can be provided.
  • FIG. 1 is a schematic cross-sectional view illustrating an example of a frangible film of the present invention.
  • FIG. 2 is a schematic cross-sectional view illustrating another example of the frangible film of the present invention.
  • FIG. 3 is a schematic cross-sectional view illustrating an example of a package of the present invention.
  • the package of the present invention has a container (bottom material) with a recessed part, and a lid material, and the lid material is the frangible film of the present invention that will be described below.
  • the lid material can be thermally adhered (heat-sealed) to an opening part of the container.
  • the package is preferably used for food and beverage packaging or for medical purposes.
  • the package is preferably a PTP (Press Through Package), and specifically, a packaging form having a container (bottom material) with a plurality of independent recessed parts, and a lid material, in which objects to be accommodated (also referred to as contents) are accommodated in the recessed parts, subsequently the lid material is placed thereon, air is removed or purged with an inert gas or the like, and the contact portion between the container and the lid material is heat-sealed, may be mentioned.
  • PTP Pressure Through Package
  • the package is preferably a package having a container such as a paper pack or a plastic cup, and a lid material as a straw piercing opening
  • a packaging form obtained by producing a package in which the contact portion between the container and the lid material is heat-sealed, and then an object to be accommodated such as a beverage is accommodated in the container portion and tightly sealed
  • a packaging form obtained by accommodating an object to be accommodated such as a beverage in the container, subsequently placing a lid material thereon, removing air or purging air with an inert gas or the like, and heat-sealing the contact portion between the container and the lid material.
  • the shape of the recessed part in the package, and the seal width or area between the lid material and the container vary depending on the shape and form of the object to be accommodated that is packaged, and cannot be univocally specified; however, the shape of the recessed part and the seal width or area are not particularly limited and can be appropriately selected in accordance with the intended application form.
  • the package is used for food and beverage packaging or for medical purposes.
  • any pharmaceutical product to which the PTP (Press Through Package) packaging form is applied can be appropriately selected according to the purpose without particular limitation, and examples thereof include tablets and capsules.
  • the food and beverage can be appropriately selected according to the purpose without particular limitation, and examples thereof include food products in a tablet form, such as supplements, chocolates, Ramune candies, and gummies; and beverages accommodated in packages such as paper packs and plastic cups with a lid material as a straw piercing opening.
  • a frangible film of the present invention is a frangible film having a base material layer containing a cyclic olefin resin on a surface thereof, and the thickness of the base material layer with respect to the total thickness of the frangible film is 40% or more.
  • the frangible film can be suitably used as a lid material of the above-described package.
  • frrangibleness means that the film is torn and cut off when force is applied thereto, and it may be easy thrust-out or easy piercing.
  • easy thrust-out means that when force is applied to the film from the outside of the container (bottom material) through an accommodated object (for example, a tablet), the film breaks, and the accommodated object can be thrust out.
  • the “ease of thrust-out” can be evaluated by measuring the thrust strength at the time of thrusting out a fixed film using a jig having a flat plate-shaped tip part (for example, a circular shape with a diameter of 13 mm).
  • the thrust strength of the frangible film when thrusting out using a jig having a circular and flat plate-shaped tip part with a diameter of 13 mm is preferably 35 N or less, more preferably 25 N or less, and even more preferably 20 N or less. When the thrust strength is 35 N or less, the frangible film has satisfactory ease of thrust-out.
  • the thrust strength can be determined by fixing a film as a measurement target, such as a frangible film, between two sheets of stainless steel having a hole (diameter: 55 mm) at the center, thrusting a jig having a flat plate-shaped tip of 13 mm into the film stretched across the hole, and measuring the thrust strength (compression strength) applied when the film breaks.
  • a film as a measurement target such as a frangible film
  • the term “easy piercing” means that when a tip part is pressed against a film and force is applied thereto, the film breaks while the tip part can penetrate the film, and the tip part may be, for example, a diagonally cut tip part of a drinking straw.
  • the “ease of piercing” can be evaluated by thrusting out a fixed film using, for example, a jig having a metal needle with a tip diameter of 1 mm.
  • the frangible film has a base material layer on the surface, and the base material layer may be a combined form composed of a surface resin layer on the surface side and an inorganic substance-containing layer containing an inorganic substance, may be a surface resin layer alone, or may be an inorganic substance-containing layer alone.
  • the frangible film further has a heat seal layer on the opposite side of the surface.
  • the frangible film may further have another layer such as a barrier layer or a print layer, on the surface side of the base material layer.
  • An embodiment of the frangible film is a frangible film having at least a base material layer and a heat seal layer, which are laminated in the order of base material layer/heat seal layer.
  • frangible film is a frangible film which has at least a surface resin layer (A), an inorganic substance-containing layer (B), and a heat seal layer (C), and in which the surface resin layer (A), the inorganic substance-containing layer (B), and the heat seal layer (C) are laminated in the order of (A)/(B)/(C).
  • the base material layer or the surface resin layer (A) is on the outer side of the package, and the heat seal layer (C) is on the inner side of the package and forms a heat seal surface with the container (bottom material).
  • the container of the package can be heat-sealed by the heat seal layer (C) of the frangible film.
  • the frangible film can be suitably used as a frangible film for the package of the present invention.
  • the frangible film is a co-extruded frangible film having at least a surface resin layer (A), an inorganic substance-containing layer (B), and a heat seal layer (C). Furthermore, it is preferable that the frangible film is a frangible film having another layer ( ⁇ ) such as a barrier layer or a print layer on the surface resin layer (A) side, which are laminated in the order of ( ⁇ )/(A)/(B)/(C).
  • ⁇ such as a barrier layer or a print layer on the surface resin layer (A) side
  • the base material layer contains a cyclic olefin resin as a main resin component.
  • the resin component may contain an olefin resin that does not have a cyclic structure, as necessary; however, it is preferable that the resin component is composed of a cyclic olefin resin.
  • the base material layer may be a combined form composed of a surface resin layer and an inorganic substance-containing layer, may be a surface resin layer alone, or may be an inorganic substance-containing layer alone.
  • the base material layer may be a surface layer on which printing can be provided.
  • the surface resin layer (A) contains a cyclic olefin resin as a main resin component, and may contain an olefin resin that does not have a cyclic structure, as necessary; however, it is preferable that the surface resin layer (A) is formed from a cyclic olefin resin.
  • the surface resin layer (A) may be a surface layer on which printing can be provided.
  • the cyclic olefin resin can be appropriately selected according to the purpose without particular limitation, and examples thereof include a norbornene-based polymer, a vinyl alicyclic hydrocarbon polymer, and a cyclic conjugated diene polymer.
  • Examples of the norbornene-based polymer include a ring-opened polymer of a norbornene-based monomer (hereinafter, referred to as “COP”), a norbornene-based copolymer obtained by copolymerizing a norbornene-based monomer and an olefin such as ethylene (hereinafter, referred to as “COC”), and hydrogenation products of COP and COC.
  • COP norbornene-based monomer
  • COC olefin such as ethylene
  • norbornene-based polymers are preferred, and hydrogenation products of COP and COC are more preferred.
  • the weight average molecular weight of the cyclic olefin resin can be appropriately selected according to the purpose without particular limitation; however, the weight average molecular weight is preferably 5,000 to 500,000, and more preferably 7,000 to 300,000.
  • the norbornene-based monomer used as the norbornene-based polymer and a raw material is an alicyclic monomer having a norbornene ring.
  • norbornene-based monomer examples include norbornene, tetracyclododecene, ethylidene norbornene, vinyl norbornene, ethylide tetracyclododecene, dicyclopentadiene, dimethanotetrahydrofluorene, phenyl norbornene, methoxycarbonyl norbornene, and methoxycarbonyl tetracyclododecene. These may be used singly, or two or more kinds thereof may be used in combination.
  • the norbornene-based copolymer is a product obtained by copolymerizing the norbornene-based monomer and an olefin that can be copolymerized with the norbornene-based monomer.
  • olefins having 2 to 20 carbon atoms such as ethylene, propylene, and 1-butene
  • cycloolefins such as cyclobutene, cyclopentene, and cyclohexene
  • non-conjugated dienes such as 1,4-hexadiene.
  • the cyclic olefin resin may be a commercially available product or a synthetic product.
  • Examples of the commercially available product include, as the ring-opened polymer of a norbornene-based monomer (COP), “ZEONOR” manufactured by ZEON CORPORATION; and as the norbornene-based copolymer (COC), “APEL” manufactured by Mitsui Chemicals, Inc., and “TOPAS” manufactured by Polyplastics Co., Ltd.
  • COP norbornene-based monomer
  • ZONOR manufactured by ZEON CORPORATION
  • COC norbornene-based copolymer
  • APEL manufactured by Mitsui Chemicals, Inc.
  • TOPAS manufactured by Polyplastics Co., Ltd.
  • the melt volume rate (MVR) of the cyclic olefin resin can be appropriately selected according to the purpose without particular limitation; however, in the case of measurement conditions of a temperature of 230° C. and a load of 2.16 kg, the melt volume rate is preferably 1.0 cm 3 /10 min to 50.0 cm 3 /10 min, more preferably 1.0 cm 3 /10 min to 20.0 cm 3 /10 min, even more preferably 2.0 cm 3 /10 min to 18.0 cm 3 /10 min, and particularly preferably 2.0 cm 3 /10 min to 15.0 cm 3 /10 min. Furthermore, when measured under the measurement conditions of a temperature of 260° C.
  • the melt volume rate is preferably 1.0 cm 3 /10 min to 50.0 cm 3 /10 min, more preferably 1.0 cm 3 /10 min to 20.0 cm 3 /10 min, even more preferably 2.0 cm 3 /10 min to 10.0 cm 3 /10 min, and particularly preferably 2.0 cm 3 /10 min to 7.0 cm 3 /10 min.
  • melt volume rate is a value measured at a temperature of 230° C. or 260° C. at a load of 2.16 kg (21.18 N) in accordance with JIS K7210.
  • the glass transition point (Tg) of the cyclic olefin resin can be appropriately selected according to the purpose without particular limitation; however, the glass transition point is preferably 60° C. or higher, and more preferably 75° C. or higher.
  • Tg of a cyclic olefin resin having a high Tg is preferably 100° C. or higher, and more preferably 125° C. or higher.
  • the content of a cyclic olefin resin having a Tg of 100° C. or higher in the surface resin layer is preferably 50% by mass or more, more preferably 75% by mass or more, and even more preferably 90% by mass or more, from the viewpoint that the resulting frangible film has excellent frangibility and rigidity.
  • the content of a cyclic olefin resin having a Tg of 100° C. or higher in the surface resin layer and the inorganic substance-containing layer is preferably 30% by mass or more, and more preferably 40% by mass or more, from the viewpoint that the resulting frangible film has excellent frangibility and rigidity.
  • the glass transition point (Tg) of the cyclic olefin resin can be appropriately selected according to the purpose without particular limitation; however, from the viewpoint that production according to a co-extrusion lamination method with other resin layers is enabled, and from the viewpoint of the ease of industrial availability of raw materials, the glass transition point is preferably 200° C. or lower.
  • the glass transition point can be measured using a differential scanning calorimeter (DSC) (for example, manufactured by Hitachi High-Tech Science Corporation, DSC-7020).
  • DSC differential scanning calorimeter
  • norbornene-based copolymers having a high glass transition point may have low tensile strength and may be easily cut or torn off
  • a high-Tg product and a low-Tg product having a glass transition point of lower than 100° C. may be used in combination to adjust the balance of physical properties, in consideration of the balance between the film-forming properties, suitability for take-up or winding at the time of slitting, and lamination strength.
  • the strength can be improved by blending a COC having a Tg of lower than 100° C.
  • an olefin resin such as a propylene resin or an ethylene resin, which has high compatibility with COC and does not have a cyclic structure, may also be blended.
  • the thickness ratio of the base material layer is 40% or more, preferably 50% or more, and more preferably 60% or more, with respect to the total thickness of the frangible film.
  • the average thickness of the base material layer can be appropriately selected according to the purpose without particular limitation; however, the average thickness is preferably 5 ⁇ m to 40 ⁇ m, and more preferably 10 ⁇ m to 36 ⁇ m.
  • the thickness ratio of the surface resin layer (A) can be appropriately selected according to the purpose without particular limitation; however, with respect to the total thickness of the frangible film, when the base material is a combined form, the thickness ratio is preferably 10% to 90%, and more preferably 15% to 80%; and when the base material is a surface resin layer alone, the thickness ratio is preferably 40% to 95%, and more preferably 50% to 90%.
  • the average thickness of the surface resin layer (A) can be appropriately selected according to the purpose without particular limitation; however, when the base material layer is a combined form, the average thickness is preferably 2 ⁇ m to 38 ⁇ m, and more preferably 2.5 ⁇ m to 35 ⁇ m; and when the base material layer is a surface resin layer alone, the average thickness is preferably 5 ⁇ m to 40 ⁇ m, and more preferably 8 ⁇ m to 36 ⁇ m.
  • the inorganic substance-containing layer (B) contains a cyclic olefin resin as a main resin component, further contains an inorganic substance, and includes other components as necessary.
  • the resin component may contain an olefin resin that does not have a cyclic structure, as necessary; however, it is preferable that the resin component is composed of a cyclic olefin resin.
  • the items described for the base material layer and the surface resin layer (A) can be appropriately selected.
  • the inorganic substance can be appropriately selected according to the purpose without particular limitation, and examples thereof include calcium carbonate, talc, silica, alumina, clay, antimony oxide, aluminum hydroxide, magnesium hydroxide, hydrotalcite, calcium silicate, magnesium oxide, potassium titanate, barium titanate, titanium oxide, calcium oxide, magnesium oxide, manganese dioxide, boron nitride, and aluminum nitride.
  • the inorganic substances may be used singly, or two or more kinds thereof may be used in combination.
  • one or more selected from the group consisting of calcium carbonate, silica, alumina, aluminum hydroxide, barium titanate, talc, boron nitride, and aluminum nitride are preferred, and one or more selected from the group consisting of calcium carbonate, alumina, aluminum hydroxide, and talc are more preferred.
  • the shape such as particle size, fiber length, and fiber diameter of the inorganic filler is not particularly limited, and may be appropriately adjusted according to the intended use applications.
  • the surface treatment state of the inorganic filler is also not particularly limited, and surface modification with, for example, a saturated fatty acid or the like may be carried out in accordance with the intended use applications.
  • the inorganic filler may be used in the form of being blended in advance into the thermoplastic resin, or may be used in the form of a master batch.
  • the content of the inorganic substance can be appropriately selected according to the purpose without particular limitation; however, the content is preferably 0.1% by mass or more and 10% by mass or less, and more preferably 1% by mass or more and 5% by mass or less, with respect to the total amount of the frangible film.
  • the frangible film When the content is 0.1% by mass or more and 10% by mass or less, the frangible film has excellent frangibility and is also satisfactory in terms of barrier properties and film-forming properties.
  • the thickness ratio of the inorganic substance-containing layer (B) can be appropriately selected according to the purpose without particular limitation; however, when the base material layer is a combined form, the thickness ratio is preferably 10% to 90%, and more preferably 15% to 50%, with respect to the total thickness of the frangible film; and when the base material layer is an inorganic substance-containing layer alone, the thickness ratio is preferably 40% to 95%, and more preferably 50% to 90%.
  • the average thickness of the inorganic substance-containing layer (B) can be appropriately selected according to the purpose without particular limitation; however, when the base material layer is a combined form, the average thickness is preferably 2 ⁇ m to 38 ⁇ m, and more preferably 2.5 ⁇ m to 35 ⁇ m; and when the base material layer is an inorganic substance-containing layer alone, the average thickness is preferably 5 ⁇ m to 40 ⁇ m, and more preferably 8 ⁇ m to 36 ⁇ m.
  • the heat seal layer (C) contains a known thermoplastic resin that imparts heat sealing properties as a main resin component, and further contains other resins and components as necessary.
  • thermoplastic resin a known thermoplastic resin can be appropriately selected according to the purpose without particular limitation, and examples thereof include an ⁇ -olefin resin, a styrene resin, an ester resin, an acrylic resin, and the cyclic olefin resin. Among these, from the viewpoint that satisfactory heat sealing properties can be imparted, an ⁇ -olefin resin is preferred.
  • ⁇ -olefin resin examples include homopolymers of ⁇ -olefin monomers (a polyethylene homopolymer, a polypropylene homopolymer, and the like); and copolymers containing ⁇ -olefin monomers as main components (a propylene-ethylene block copolymer, a propylene-ethylene random copolymer, an ethylene-butene-1 copolymer, a propylene-butene-1 copolymer, and the like). These may be used singly, or two or more kinds thereof may be used in combination.
  • the thickness ratio of the heat seal layer (C) can be appropriately selected according to the purpose without particular limitation; however, the thickness ratio is preferably 20% to 60%, and more preferably 30% to 60%, with respect to the total thickness of the frangible film.
  • the average thickness of the heat seal layer (C) can be appropriately selected according to the purpose without particular limitation; however, the average thickness is preferably 4 ⁇ m to 28 ⁇ m, and more preferably 6 ⁇ m to 25 ⁇ m.
  • the heat seal layer is disposed on the base material layer directly or with an optional layer such as an anchor coat layer interposed therebetween.
  • the heat seal layer (C) can be provided by extruding the resin and the like together with the base material layer by a co-extrusion method. Furthermore, the heat seal layer (C) can be provided by applying a heat sealing agent obtained by dispersing or dissolving the resin and the like in a solvent.
  • a commercially available hot melt sealing agent can be used.
  • the heat sealing agent can be applied entirely or partially on a desired side of the outermost surface of the laminate.
  • the heat sealing agent is not particularly limited, and may be in any form, such as a type in which a thermoplastic resin having heat sealing properties is dissolved in an organic solvent, a type in which the thermoplastic resin is dissolved in water or an aqueous organic solvent, or an emulsion type in which the thermoplastic resin is dispersed in water or an aqueous organic solvent.
  • thermoplastic resins such as a shellac, a rosin, a rosin-modified maleic acid resin, a rosin-modified phenol resin, nitrocellulose, cellulose acetate, cellulose acetyl propionate, cellulose acetyl butyrate, chlorinated rubber, cyclized rubber, vinyl chloride, vinylidene chloride, a polyamide resin, a vinyl chloride-vinyl acetate copolymer, a polyester resin, a ketone resin, a butyral resin, a chlorinated polypropylene resin, a chlorinated polyethylene resin, a chlorinated ethylene vinyl acetate resin, an ethylene vinyl acetate resin, an acrylic resin, a urethane resin, an ethylene-vinyl alcohol resin, a styrene-maleic acid resin, casein, and an alkyd resin. These may be used singly, or two or more kinds thereof may be used in combination.
  • the organic solvent can be appropriately selected according to the purpose without particular limitation, and examples thereof include various organic solvents, including aromatic hydrocarbon-based solvents such as toluene, xylene, SOLVESSO #100, and SOLVESSO #150; aliphatic hydrocarbon-based solvents such as hexane, heptane, octane, and decane; and ester-based solvents such as methyl acetate, ethyl acetate, isopropyl acetate, butyl acetate, amyl acetate, ethyl formate, and butyl propionate.
  • aromatic hydrocarbon-based solvents such as toluene, xylene, SOLVESSO #100, and SOLVESSO #150
  • aliphatic hydrocarbon-based solvents such as hexane, heptane, octane, and decane
  • ester-based solvents such as methyl acetate, ethyl
  • aqueous organic solvent examples include alcohol-based solvents such as methanol, ethanol, propanol, and butanol; ketone-based solvents such as acetone, methyl ethyl ketone, and cyclohaxanone; and glycol ethers such as ethylene glycol (mono-, di-)methyl ether, ethylene glycol (mono-, di-)ethyl ether, ethylene glycol monopropyl ether, ethylene glycol monoisopropyl ether, monobutyl ether, diethylene glycol (mono-, di-)methyl ether, diethylene glycol (mono-, di-)ethyl ether, diethylene glycol monoisopropyl ether, diethylene glycol monobutyl ether, triethylene glycol (mono-, di-)methyl ether, propylene glycol (mono-, di-)methyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl
  • the heat sealing agent may further include other components.
  • the other components include lubricating agents such as a wax and a filler, an antifoaming agent, a plasticizer, a leveling agent, an emulsifier, a dispersion stabilizer, a surfactant, a tackifier, an antiseptic agent, an antibacterial agent, an antirust agent, an antioxidant, a crosslinking agent, a curing agent, a curing catalyst, a light stabilizer, an ultraviolet absorber, a photocatalytic compound, a dye, an inorganic pigment, an organic pigment, an extender pigment, and an antistatic agent.
  • lubricating agents such as a wax and a filler, an antifoaming agent, a plasticizer, a leveling agent, an emulsifier, a dispersion stabilizer, a surfactant, a tackifier, an antiseptic agent, an antibacterial agent, an antirust agent, an antioxidant, a crosslinking agent, a
  • the wax can be appropriately selected according to the purpose without particular limitation, and examples thereof include fatty acid amide wax, carbana wax, polyolefin waxes such as polyethylene wax and polypropylene wax; paraffin wax, Fischer-Tropsch wax, beeswax, microcrystalline wax, oxidized polyethylene wax, amide wax; coconut oil fatty acids, and soybean oil fatty acids. These may be used singly, or two or more kinds thereof may be used in combination.
  • the blocking resistance can be improved. From the viewpoint of improving the blocking resistance without deteriorating the heat sealing properties, it is preferable to use a polyethylene wax.
  • the blending amount of the wax can be appropriately selected according to the purpose without particular limitation; however, the blending amount is preferably 0.1% by mass to 20% by mass with respect to the total amount of the thermoplastic resin, and from the viewpoint of the balance between heat sealing properties and blocking resistance, the blending amount is more preferably 3% by mass or more and 15% by mass or less.
  • the filler can be appropriately selected according to the purpose without particular limitation, and examples thereof include silica, calcium carbonate, calcium phosphate, talc, urethane beads, acrylic beads, and melamine beads. These may be used singly, or two or more kinds thereof may be used in combination. It is preferable to use either or both of silica and acrylic beads.
  • the blocking resistance can be improved. Furthermore, for example, when the laminate of the present invention is stored at a high temperature, it is possible to suppress the heat seal layer from flowing out and having a smaller film thickness.
  • the shape of the filler can be appropriately selected according to the purpose without particular limitation; however, from the viewpoint of being less susceptible to deformation due to heat and obtaining a stable anti-blocking effect regardless of the mode of dispersion in the coating film, the shape is preferably a spherical shape.
  • the average particle size of the filler is appropriately adjusted depending on the filler used; however, the average particle size is, for example, 0.5 ⁇ m to 10 ⁇ m.
  • the anti-foaming agent can be appropriately selected according to the purpose without particular limitation, and examples thereof include fatty acid salts, higher alcohol sulfates, liquid fatty oil sulfuric acid esters, sulfates of aliphatic amines and aliphatic amides, aliphatic alcohol phosphoric acid esters, sulfonates of dibasic fatty acid esters, fatty acid amide sulfonates, alkyl allyl sulfonates, naphthalene sulfonates of formalin condensation, polyoxyethylene alkyl ethers, polyoxyethylene alkyl phenol ethers, polyoxyethylene alkyl esters, sorbitan alkyl esters, polyoxyethylene sorbitan alkyl esters, acrylic polymers, silicon-mixed acrylic polymers, vinyl-based polymers, and polysiloxane compounds.
  • the method for applying the heat sealing agent can be appropriately selected according to the purpose without particular limitation, and examples thereof include a gravure coating method, a reverse coating method, a kiss coating method, an air knife coating method, a Mayer bar coating method, a roll coating method, and a dip coating method.
  • the heat seal layer may be provided over the entire surface of the laminate, or may be provided only on the portion that will be heat-sealed when a package is produced.
  • the drying temperature is 50° C. to 180° C., and the drying time is about 0.5 seconds to 1 minute.
  • the drying method is not particularly limited; however, an example thereof may be hot air drying. If necessary, a corona discharge treatment or the like may be carried out as a post-treatment.
  • the amount of the heat sealing agent applied can be appropriately selected according to the purpose without particular limitation, and for example, the amount is 1.0 g/m 2 to 15.0 g/m 2 , preferably 2.0 g/m 2 to 10.0 g/m 2 , and more preferably 2.0 g/m 2 to 8.0 g/m 2 .
  • an anchor coat layer may be provided under the heat seal layer.
  • a resin similar to that of the above-mentioned heat seal layer can be used for the anchor coat layer.
  • the anchor coat layer can be formed by, for example, applying a coating liquid containing a resin on one surface of the base material layer.
  • the average thickness of the anchor coat layer can be appropriately selected according to the purpose without particular limitation; however, the average thickness is preferably 1 ⁇ m to 10 ⁇ m, and more preferably 1 ⁇ m to 5 ⁇ m.
  • components such as an antifogging agent, an antistatic agent, a heat stabilizer, a nucleating agent, an antioxidant, a lubricating agent, an anti-blocking agent, a mold release agent, an ultraviolet absorber, a colorant, and an extrusion modifier can be added as necessary, to the extent that does not impair the purpose of the present invention.
  • the frangible film of the present invention may have another layer ( ⁇ ) such as a water vapor and/or oxygen barrier layer (hereinafter, may be referred to as a “barrier layer”), a print layer, an OP varnish layer (also referred to as an “overprint varnish layer”, an “overcoat layer”, or a “topcoat layer”).
  • ⁇ a water vapor and/or oxygen barrier layer
  • OP varnish layer also referred to as an “overprint varnish layer”, an “overcoat layer”, or a “topcoat layer”.
  • the frangible film has the other layer ( ⁇ )
  • the other layer ( ⁇ ) is a water vapor and/or oxygen barrier layer, from the viewpoint that, for example, in a case where the object to be accommodated is a pharmaceutical product, the required high storage stability can be ensured.
  • the other layer ( ⁇ ) may be a print layer on which printing of a packaging film can be provided.
  • the frangible film may further have another layer ( ⁇ ) on the surface side of the base material layer, and may be a frangible film in which ( ⁇ )/base material layer/heat seal layer are laminated in this order, or a frangible film in which ( ⁇ )/(A)/(B)/(C) are laminated in this order.
  • the other layer ( ⁇ ) may be a single layer, or may be a plurality of layers.
  • a plurality of the other layers ( ⁇ ) may have compositions identical with each other, or may have compositions different from each other.
  • the other layer ( ⁇ ) may be extruded together with the base material layer and the heat seal layer and form a co-extruded frangible film in which ( ⁇ )/base material layer/heat seal layer are laminated in this order, or ( ⁇ )/(A)/(B)/(C) are laminated in this order, or the other layer ( ⁇ ) may be adhered to a frangible film in which base material layer/heat seal layer are laminated in this order, or (A)/(B)/(C) are laminated in this order, to form a laminate film in which ( ⁇ )/(A)/(B)/(C) are laminated in this order.
  • the other layer ( ⁇ ) may be provided by applying a coating agent or an ink composition.
  • the method of adhering when laminating the other layer ( ⁇ ) can be appropriately selected according to the purpose without particular limitation, and examples thereof include dry lamination, wet lamination, non-solvent lamination, and extrusion lamination.
  • the other layer ( ⁇ ) can be appropriately selected according to the purpose without particular limitation, and examples for co-extrusion include olefin resins such as a propylene resin, while examples for a laminate film include unstretched polyester (CPET), unstretched nylon (CNY), unstretched polypropylene (CPP), unstretched polyethylene (CPE), unstretched polystyrene (CPS), expanded polystyrene (EPS), biaxially stretched polyester (OPET), biaxially stretched polypropylene (OPP), an ethylene-vinyl alcohol copolymer (EVOH), co-extruded biaxially stretched polypropylene, a biaxially stretched ethylene-vinyl alcohol copolymer (EVOH), co-extruded biaxially stretched polypropylene coated with polyvinylidene chloride (PVDC), and biaxially stretched nylon.
  • CPET unstretched polyester
  • CNY unstretched nylon
  • CPE unstretched polyethylene
  • the other layer ( ⁇ ) may be provided between the base material layer and the heat seal layer, or may be provided on both surfaces of the base material layer.
  • the frangible film can be configured to have base material layer/( ⁇ )/heat seal layer or ( ⁇ )/base material layer/( ⁇ )/heat seal layer.
  • the following configuration may be mentioned as a configuration in which a barrier layer, a print layer, and an OP varnish layer are provided as the other layers ( ⁇ ).
  • the average thickness of the other layer ( ⁇ ) in the case of a plurality of layers, the total average thickness
  • the average thickness of the other layer ( ⁇ ) in the case of a plurality of layers, the total average thickness
  • a method for forming the barrier layer a method of laminating a film having barrier properties, a method of producing a coating film layer by applying a barrier coating agent, and the like may be mentioned.
  • a method of producing a coating film layer by applying a barrier coating agent is preferred from the viewpoint of convenience.
  • barrier coating agent examples include coating agents containing polymers such as polyvinyl alcohol (PVOH), ethylene vinyl alcohol (EVOH), polysaccharide, polymers based on acrylic acid or methacrylic acid, starch or starch derivatives, cellulose nanofibers (CNF), nanocrystalline cellulose (NCC), chitosan, other cellulose derivatives, hemicellulose, and polyvinylidene chloride (PVDC); and coating agents using at least any one of the above-described coating agents and an inorganic compound in combination.
  • PVH polyvinyl alcohol
  • EVOH ethylene vinyl alcohol
  • PVDC cellulose nanofibers
  • PVDC nanocrystalline cellulose
  • the inorganic substance examples include plate-shaped inorganic compounds such as silica, alumina, aluminum flakes, glass flakes, hydrous silicates (phyllosilicate minerals and the like), kaolinite-serpentine family clay minerals (halloysite, kaolinite, endelite, dickite, nacrite, antigorite, chrysotile, and the like), pyrophyllite-talc family (pyrophyllite, talc, kerolite, and the like), smectite family clay minerals (montmorillonite, beidellite, nontronite, saponite, hectorite, sauconite, stevensite, and the like), vermiculite family clay minerals (vermiculite and the like), mica or mica family clay minerals (mica such as muscovite and phlogopite, margarite, tetrasilylic mica, tainiolite, and the like), chlorite family (cookeit
  • the barrier coating agent is not particularly limited, and any known barrier coating agent can be used in accordance with the purpose.
  • Examples of the known barrier coating agent include “Sunbar” series manufactured by SUNCHEMICAL Co., Ltd., and the polyester-based barrier coating agents described in JP 5617831 B2.
  • the barrier layer may be an inorganic vapor deposition layer that can be provided for the purpose of imparting gas barrier properties.
  • the inorganic vapor deposition layer can be formed using inorganic substances, inorganic oxides, various metals, metal oxides, metal hydroxides, metal salts, and the like.
  • aluminum, alumina, silica, zinc oxide, magnesium oxide, calcium oxide, manganese oxide, iron oxide, cobalt oxide, nickel oxide, and the like may be used singly, or two or more kinds thereof can be used in combination, as in the case of binary vapor deposition of silica and alumina.
  • Two or more inorganic vapor deposition layers may be provided. When two or more inorganic vapor deposition layers are provided, each may have the same composition, or they may have different compositions. From the viewpoint of the gas barrier properties, it is preferable to use aluminum.
  • the inorganic vapor deposition layer can be provided on each of the above-mentioned layers or on a separate base material, by a conventionally known method.
  • a method for forming an inorganic vapor deposition layer include Physical Vapor Deposition methods (PVD methods) such as a vacuum vapor deposition method, a sputtering method, and an ion plating method; and Chemical Vapor Deposition methods (CVD methods) such as a plasma chemical vapor deposition method, a thermochemical vapor deposition method, and a photochemical vapor deposition method.
  • PVD methods Physical Vapor Deposition methods
  • CVD methods Chemical Vapor Deposition methods
  • the film thickness of the inorganic vapor deposition layer is preferably 1 nm to 200 nm.
  • the film thickness is more preferably 1 nm to 100 nm, even more preferably 15 nm to 60 nm, and still more preferably 10 nm to 40 nm.
  • the film thickness is preferably 1 nm to 100 nm, more preferably 10 nm to 50 nm, and even more preferably 20 nm to 30 nm.
  • the print layer is a layer on which a desired pattern is formed using ink or the like in order to impart aesthetic appeal, various pieces of information related to the object to be accommodated, and functionality to the frangible film of the present invention, which is an object to be subjected to printing.
  • the print layer contains a binder resin and a colorant and is formed by printing ink.
  • the print layer may be a single layer, or there may be a plurality of print layers.
  • the single layer may be a character print layer on which characters or any objects are printed, or may be a solid print layer.
  • the print layer may be a solid print layer, or a print layer obtained by overprinting a character print layer on a print layer with objects and the like printed thereon, and the respective inks used for the print layers may be the same, may have the same composition with only the colorant being different, or may have different compositions.
  • the ink is preferably a liquid printing ink used as a gravure printing ink or a flexographic printing ink.
  • the liquid printing inks are roughly classified into organic solvent type liquid printing inks that use organic solvents as a main solvent, and aqueous liquid printing inks that use water as a main solvent; however, either may be used in the present invention.
  • organic solvent type liquid printing inks that use organic solvents as a main solvent
  • aqueous liquid printing inks that use water as a main solvent
  • organic solvent type liquid printing inks which constitute the mainstream, will be described.
  • a binder resin used for the liquid printing inks examples include cellulosic resins, such as cellulose-based resins such as nitrocellulose, cellulose acetate propionate (CAP), and cellulose acetate butyronate (CAB), a polyamide-based resin, a urethane-based resin, an acrylic resin, a vinyl chloride-vinyl acetate copolymer resin, a chlorinated polypropylene resin, an ethylene-vinyl acetate copolymer resin, a vinyl acetate resin, vinyl chloride-based resins such as a polyvinyl chloride resin, a polyester resin, an alkyd resin, a rosin-based resin, a rosin-modified maleic acid resin, a ketone resin, a cyclized rubber, a chlorinated rubber, butyral, and petroleum resins.
  • cellulosic resins such as cellulose-based resins such as nitrocellulose, cellulose acetate propionate (CAP),
  • a curing agent may be used in combination with the binder resin.
  • the curing agent any curing agent generally used in organic solvent-based gravure printing inks may be used; however, the most commonly used curing agents are isocyanate-based curing agents.
  • the amount of an isocyanate compound added is preferably 0.3% by mass to 10.0% by mass, and more preferably 1.0% by mass to 7.0% by mass, with respect to the liquid printing ink solid content.
  • the binder resin is preferably 0.15% by mass to 50% by mass, and more preferably 1% by mass to 40% by mass, with respect to the liquid printing ink.
  • the solvent used in the liquid printing ink is not particularly limited; however, examples thereof include water, aromatic hydrocarbon-based organic solvents such as toluene, xylene, SOLVESSO #100, and SOLVESSO #150; aliphatic hydrocarbon-based organic solvents such as hexane, methylcyclohexane, heptane, octane, and decane; and various ester-based organic solvents such as methyl acetate, ethyl acetate, isopropyl acetate, normal propyl acetate, butyl acetate, amyl acetate, ethyl formate, and butyl propionate.
  • aromatic hydrocarbon-based organic solvents such as toluene, xylene, SOLVESSO #100, and SOLVESSO #150
  • aliphatic hydrocarbon-based organic solvents such as hexane, methylcyclohexane, heptane, octan
  • examples of a water-miscible organic solvent include various organic solvents of alcohol-based solvents such as methanol, ethanol, propanol, butanol, and isopropyl alcohol; ketone-based solvents such as acetone, methyl ethyl ketone, and cyclohaxanone; and glycol ether-based solvents such as ethylene glycol (mono-, di-)methyl ether, ethylene glycol (mono-, di-)ethyl ether, ethylene glycol monopropyl ether, ethylene glycol monoisopropyl ether, monobutyl ether, diethylene glycol (mono-, di-)methyl ether, diethylene glycol (mono-, di-)ethyl ether, diethylene glycol monoisopropyl ether, diethylene glycol monobutyl ether, triethylene glycol (mono-, di-)methyl ether, propylene glycol (mono-, di-)methyl ether, propy
  • the liquid printing ink contains a colorant, and can be used as a liquid printing ink containing a colorant used for design printing and the like for the purpose of imparting aesthetic beauty and the like.
  • the colorant include inorganic pigments, organic pigments, and dyes used in general inks, paints, recording agents, and the like, and pigments are preferred.
  • organic pigments examples include soluble azo-based, insoluble azo-based, azo-based, phthalocyanine-based, halogenated phthalocyanine-based, anthraquinone-based, anthanthrone-based, dianthraquinonyl-based, anthrapyrimidine-based, perylene-based, perinone-based, quinacridone-based, thioindigo-based, dioxazine-based, isoindolinone-based, quinophthalone-based, azomethine azo-based, flavanthrone-based, diketopyrrolopyrrole-based, isoindoline-based, indanthrone-based, and carbon black-based pigments.
  • Further examples include carmine 6B, lake red C, permanent red 2B, disazo yellow, pyrazolone orange, carmine FB, chromophthalic yellow, chromophthalic red, phthalocyanine blue, phthalocyanine green, dioxazine violet, quinacridone magenta, quinacridone red, indanthrone blue, pyrimidine yellow, thioindigo bordeaux, thioindigo magenta, perylene red, perinone orange, isoindolinone yellow, aniline black, diketopyrrolopyrrole red, and daylight fluorescent pigment. Furthermore, both non-acid-treated pigments and acid-treated pigments can be used.
  • the inorganic pigments include white inorganic pigments such as titanium oxide, zinc oxide, zinc sulfide, barium sulfate, calcium carbonate, chromium oxide, silica, lithopone, antimony white, and gypsum.
  • white inorganic pigments such as titanium oxide, zinc oxide, zinc sulfide, barium sulfate, calcium carbonate, chromium oxide, silica, lithopone, antimony white, and gypsum.
  • titanium oxide exhibits white color and is preferred from the viewpoints of coloring power, concealing power, chemical resistance, and weather resistance, and from the viewpoint of printing performance, it is preferable that the titanium oxide is treated with silica and/or alumina.
  • examples of the inorganic pigments other than white pigments include aluminum particles, mica, bronze powder, chromium vermilion, lead yellow, cadmium yellow, cadmium red, ultramarine, Prussian blue, red iron oxide, yellow iron oxide, black iron oxide, and zircon.
  • Aluminum is in a powdered form or a paste form; however, from the viewpoints of handleability and safety, it is preferable to use aluminum in a paste form, and whether leafing or non-leafing aluminum should be used is appropriately selected in view of high brightness feeling and concentration.
  • the content of the pigment is preferably an amount sufficient for ensuring the concentration and coloring power of the liquid printing ink, that is, 1% by mass to 60% by mass with respect to the total mass of the liquid printing ink, and the content is preferably 10% by mass to 90% by mass in the solid content weight ratio in the liquid printing ink. Furthermore, these pigments can be used singly or in combination of two or more kinds thereof.
  • the organic solvent type liquid printing ink can further contain a wax, a chelate-based crosslinking agent, an extender pigment, a leveling agent, an antifoaming agent, a plasticizer, an infrared absorber, an ultraviolet absorber, an aromatic agent, a flame retardant, and the like as necessary.
  • liquid printing ink it is preferable to use a liquid printing ink that uses plant-derived raw materials, in consideration of the need to establish a recycling-based society that should continue to develop (sustainability).
  • plant-derived raw materials examples include cellulosic resins such as cellulose acetate propionate resin and nitrocellulose; polyamide resins that use dimer acids or polymerized fatty acids derived from natural oils such as soybean oil-derived, palm oil-derived, and rice bran oil-derived natural oils; biomass polyurethanes synthesized from plant-derived raw materials, such as succinic acid, succinic anhydride, adipic acid, azelaic acid, sebacic acid, dimer acid, glutaric acid, malic acid, and the like as polycarboxylic acids, and ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, neopentyl glycol, pentylene glycol, 1,10-dodecanediol, dimer diol, isosorbide, and the like as polyols, and 1,5-pentamethylene diisocyanate and dimer diisocyanate
  • the liquid printing ink used in the present invention it is also preferable to use a UV cut ink having an ultraviolet radiation shielding effect.
  • the UV cut ink is not particularly limited as long as it is an ink containing zinc oxide and the like and having a high ultraviolet radiation shielding effect, and any commercially available UV cut ink can be used.
  • the OP varnish layer is a coating for protecting the lid material surface from scratches or heat.
  • a polyvinyl butyral resin for example, a polyvinyl butyral resin; a blend of an epoxy resin and an amino resin; cellulose resins such as a nitrocellulose resin, cellulose acetate, cellulose propionate, and cellulose butyrate; polyester resins having a benzene ring of phthalic acid, naphthalenedicarboxylic acid, ethylene oxide (hereinafter, may be referred to as “EO”) adduct of bisphenol A, or the like, and/or an alicyclic skeleton such as cyclopentanediol and dimethyloltricyclodecane; and urethane resins in which an aromatic isocyanate such as diphenylmethane diisocyanate, toluene diisocyanate, xylene diisocyanate, or naphthalene diisocyanate, an alicyclic isocyanate such as isophorone diisocyanate or norbornene diis
  • a polyisocyanate that uses the above-mentioned isocyanates may be used.
  • a radical copolymer of a compound having a benzene ring and an unsaturated double bond, such as styrene or phenoxy diethylene glycol acrylate; a compound having an alicyclic structure and an unsaturated double bond, such as isobornyl acrylate or dicyclopentanyl acrylate; a (meth)acrylate; and the like can also be preferably used.
  • the OP varnish layer has heat resistance, and it is preferable that among the OP vanish, the OP varnish layer contains a resin having a polymer skeleton such as a cellulose skeleton, a benzene ring skeleton, an isocyanuric ring skeleton, or an alicyclic skeleton, and having a polymer glass transition temperature (hereinafter, may be referred to as “Tg”) of 100° C. or higher.
  • Tg polymer glass transition temperature
  • a resin having a low Tg may be mixed into the OP varnish and used.
  • the OP varnish layer may further contain a colorant and be colored.
  • the colorant is not particularly limited, and examples thereof include inorganic pigments, organic pigments, and dyes used in general inks and the like, which are used in the above-mentioned print layer.
  • the OP varnish layer further contains inorganic microparticles as an aggregate, since the inorganic microparticles have excellent heat resistance.
  • inorganic microparticles examples include boron nitride, aluminum nitride, alumina, magnesia, titania, zirconia, zinc oxide, silicon oxide, and silica (quartz, fumed silica, precipitated silica, silicic anhydride, fused silica, crystalline silica, ultrafine amorphous silica, and the like).
  • boron nitride, aluminum nitride, alumina, titania, magnesia, zinc oxide, silicon oxide, and the like are preferable because they have excellent thermal conductivity.
  • the inorganic microparticles may be used singly, or two or more kinds thereof may be used in combination.
  • the primary particle size of the inorganic microparticles is preferably 5 nm to 200 nm, and more preferably 10 nm to 100 nm. When the primary particle size is 5 nm or more, the inorganic microparticles in the dispersion are satisfactorily dispersed, and when the primary particle size is 200 nm or less, the strength of the cured product is improved.
  • the OP varnish layer may further contain at least any one of a wax, a silicon additive, and organic beads.
  • Examples of the wax include amide wax, polypropylene wax, polyethylene wax, paraffin wax, carnauba wax, and rice wax.
  • Examples of the silicon additive include an ethylene oxide (EO) adduct of dimethylsiloxane, and a silicon modification product.
  • Examples of the organic beads include organic beads formed from acryl, nylon, urethane, or epoxy.
  • the solvent used for the coating agent that forms the OP varnish layer is not particularly limited, and solvents similar to the solvents used in the above-described printing ink can be used.
  • the method for producing the frangible film of the present invention is not particularly limited; however, a co-extrusion method in which each resin or resin mixture used in each layer is heated and melted in each separate extruder, surface resin layer (A)/inorganic substance-containing layer (B)/heat seal layer (C), or surface resin layer (A) alone or inorganic substance-containing layer (B) alone/heat seal layer (C) are laminated in a molten state by a method such as a co-extrusion multilayer die method or a feed block method, and then the laminate is molded into a film form by an inflation method, a T-die chill roll method, or the like, may be mentioned.
  • a co-extrusion method in which each resin or resin mixture used in each layer is heated and melted in each separate extruder, surface resin layer (A)/inorganic substance-containing layer (B)/heat seal layer (C), or surface resin layer (A) alone or inorganic substance-containing layer (B) alone/heat seal
  • a co-extrusion method is preferred because it is possible to adjust the thickness ratio of each layer relatively freely, and a multilayer film having excellent hygienic properties and excellent cost performance is obtained.
  • a resin having a large difference between the melting point and Tg is laminated, the film appearance may be deteriorated during co-extrusion processing, or it may be difficult to form a uniform layer configuration.
  • a T-die chill roll method by which melt extrusion can be carried out at a relatively high temperature is preferred.
  • a heat seal layer When a heat seal layer is formed using the above-described heat sealing agent, a heat seal layer may be provided by obtaining a laminate other than the heat seal layer, a surface resin layer (A) alone, or an inorganic substance-containing layer (B) alone, and then applying the heat sealing agent thereon by the above-described method.
  • the surface other than the heat seal layer (C) is subjected to a surface treatment in order to improve the adhesiveness to printing inks or adhesives.
  • a surface treatment include surface oxidation treatment such as a corona treatment, a plasma treatment, a chromic acid treatment, a flame treatment, a hot air treatment, and an ozone-ultraviolet radiation treatment; and surface unevenness treatments such as sand blasting.
  • a corona treatment is preferred.
  • the exposed surface on the heat seal layer (C) side may be subjected to a surface treatment.
  • any known container can be appropriately selected according to the purpose without particular limitation, and in the case of an embodiment of PTP, a container obtained by molding a resin is preferred, while in the case of a container for beverages, a paper pack, a plastic cup, and the like that can be heat-sealed to a lid material for a straw opening is preferred.
  • any known olefin resin that can be heat-sealed can be appropriately selected according to the purpose without particular limitation.
  • the package of the present invention has a lid material and a container with a recessed part, the lid material can be thermally adhered (heat-sealed) to the opening part of the container, and an object to be accommodated can be accommodated in the recessed part and sealed by heat-sealing of the lid material and the container.
  • an object to be accommodated can be accommodated in the package and sealed.
  • any known method can be appropriately selected according to the purpose without particular limitation, and examples thereof include a co-extrusion method and lamination processing.
  • any known method can be appropriately selected according to the purpose without particular limitation, and for example, a method of molding a container having a recessed part capable of accommodating an object to be accommodated, from a sheet-shaped film using a mold having a specific shape (for example, a shape conforming to the object to be accommodated), may be mentioned.
  • the shape and number of the recessed parts, and the seal width or area between the lid material and the container in the package vary widely depending on the shape or form of the object to be accommodated and cannot be univocally specified; however, those items can be appropriately selected according to the intended application form without particular limitation.
  • any known method can be appropriately selected according to the purpose without particular limitation, and for example, a method in which the object to be accommodated is accommodated in the recessed part of the container, subsequently the lid material is placed over the container, air is removed or purged with an inert gas or the like, and a contact portion between the lid material and the container is heat-sealed, may be mentioned.
  • the heat-sealing can be appropriately carried out using a known heat-sealing packaging machine according to the purpose without particular limitation.
  • the molding heating temperature and molding time in the heat-sealing can be appropriately selected according to the purpose without particular limitation, and for example, the molding heating temperature and molding time may be 80° C. to 180° C. and 0.1 seconds to 5.0 seconds.
  • a frangible film 10 according to the present embodiment is, for example, a frangible film composed of a surface resin layer (A) 1, an inorganic substance-containing layer (B) 2, and a heat seal layer (C) 3 as shown in FIG. 1 , in which the layers are laminated in the order of (A)/(B)/(C).
  • the frangible film 10 may be a frangible film further having another layer ( ⁇ ) 4 on the surface resin layer (A) 1 side, in which the layers are laminated in the order of ( ⁇ )/(A)/(B)/(C).
  • the other layer ( ⁇ ) 4 may be a single layer, or may be a plurality of layers.
  • FIG. 3 is a schematic cross-sectional view illustrating an example of the package according to the present embodiment.
  • a package 100 is a package having a lid material 20 and a container 30 with a recessed part, in which contents 40 (for example, tablets) can be individually accommodated in a plurality of independent recessed parts, and each of the contents can be taken out by thrusting out.
  • contents 40 for example, tablets
  • the lid material 20 is the frangible film 10
  • the heat seal layer (C) 3 of the frangible film 10 is heat-sealed with the container 30.
  • cyclic olefin resin (a) 50 parts by mass of a ring-opening polymer of a norbornene-based monomer
  • MVR 4 cm 3 /10 min (260° C., 2.16 kg), density: 1.02 g/cm 3 , glass transition temperature: 158° C.
  • cyclic olefin resin (b) 50 parts by mass of a ring-opening polymer of a norbornene-based monomer
  • cyclic olefin resin (b) MVR: 12 cm 3 /10 min (230° C., 2.16 kg), density: 1.02 g/cm 3 , glass transition temperature: 78° C.
  • cyclic olefin resin (a) and 30 parts by mass of the cyclic olefin resin (b), which were the same as those of the layer A, were used as resins for the inorganic substance-containing layer (layer B), and 20 parts by mass of a masterbatch containing 40% by mass of talc was used as an inorganic substance.
  • propylene resin (a) 100 parts by mass of polypropylene (hereinafter, referred to as “propylene resin (a)”, MFR: 6 g/10 min (230° C., 21.18 N), density: 0.89 g/cm 3 ) was used as a resin for the heat seal layer (layer C).
  • An extrusion was performed by a co-extrusion method through a T-die at an extrusion temperature of 250° C. such that the layers were laminated in the order of (A)/(B)/(C) and the thickness ratio of each layer was 20%/30%/50%, the layers were cooled with a water-cooled metal cooling roll at 50° C., subsequently subjected to a corona discharge treatment such that the wet tension of the surface resin layer (A) was 40 mN/m, subsequently wound on a roll, and aged for 24 hours in an aging chamber at 40° C., to obtain a frangible film 1 of Example 1, which was a co-extruded laminated film having a total thickness of 30 ⁇ m.
  • the content of the inorganic substance with respect to the total amount of the frangible film was 2.4% by mass.
  • the container (bottom material) a container having independent recessed parts for tablet accommodation, which was obtained by vacuum and pressure forming of the molded resin sheet, was used.
  • the produced frangible film 1 and the package 1 were evaluated as follows.
  • the frangible film 1 was fixed between two sheets of stainless steel having a hole (diameter: 55 mm) at the center, a jig having a circular and flat plate-shaped tip part with a diameter of 13 mm was thrust into the film stretched over the hole, and the thrust strength (compression strength) applied when the frangible film 1 broke was measured.
  • the container (bottom material) of the produced package 1 was pressed with a finger to take out the tablets, which were the contents, and the push-through properties were evaluated according to the following criteria.
  • Polylene resin (b) is a polypropylene with MFR: 2.5 g/10 min (230° C., 21.18 N) and density: 0.90 g/cm 3 .

Landscapes

  • Chemical & Material Sciences (AREA)
  • Composite Materials (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • Pharmacology & Pharmacy (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Animal Behavior & Ethology (AREA)
  • General Health & Medical Sciences (AREA)
  • Public Health (AREA)
  • Veterinary Medicine (AREA)
  • Wrappers (AREA)
  • Laminated Bodies (AREA)
  • Medical Preparation Storing Or Oral Administration Devices (AREA)
US18/997,320 2022-08-05 2023-07-21 Frangible film and packaging material Pending US20260035153A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2022125223 2022-08-05
JP2022-125223 2022-08-05
PCT/JP2023/026865 WO2024029377A1 (ja) 2022-08-05 2023-07-21 易破断フィルム、及び包装体

Publications (1)

Publication Number Publication Date
US20260035153A1 true US20260035153A1 (en) 2026-02-05

Family

ID=89848917

Family Applications (1)

Application Number Title Priority Date Filing Date
US18/997,320 Pending US20260035153A1 (en) 2022-08-05 2023-07-21 Frangible film and packaging material

Country Status (5)

Country Link
US (1) US20260035153A1 (https=)
EP (1) EP4566816A1 (https=)
JP (1) JP7544302B2 (https=)
CN (1) CN119384357A (https=)
WO (1) WO2024029377A1 (https=)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2025169957A1 (https=) * 2024-02-05 2025-08-14

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH11105217A (ja) * 1997-10-06 1999-04-20 Tohcello Co Ltd プレススルーパックカバー用積層フィルム
JP3744686B2 (ja) * 1998-05-07 2006-02-15 住友ベークライト株式会社 薬品包装体
JP3942737B2 (ja) 1998-07-01 2007-07-11 三井化学株式会社 環状オレフィン系樹脂積層体
JP2000017088A (ja) 1998-07-01 2000-01-18 Mitsui Chemicals Inc 易打ち抜き開封性包装材料
JP4614710B2 (ja) 2004-08-11 2011-01-19 三菱樹脂株式会社 板状フィラーを含む樹脂組成物及びフィルム
JP5991504B2 (ja) * 2011-01-28 2016-09-14 Dic株式会社 易貫通性蓋材
JP5617831B2 (ja) 2011-12-21 2014-11-05 Dic株式会社 ガスバリアコーティング剤及びそれを用いたフィルム
JP7106158B2 (ja) 2020-10-08 2022-07-26 株式会社寺岡精工 販売データ処理装置及びプログラム

Also Published As

Publication number Publication date
JP7544302B2 (ja) 2024-09-03
WO2024029377A1 (ja) 2024-02-08
EP4566816A1 (en) 2025-06-11
JPWO2024029377A1 (https=) 2024-02-08
CN119384357A (zh) 2025-01-28

Similar Documents

Publication Publication Date Title
HK1205984A1 (en) Sealable, peelable film
WO2015093405A1 (ja) 容器用印刷フィルム及びその製造方法
US20260035153A1 (en) Frangible film and packaging material
JP6375805B2 (ja) 積層フィルム及び包装材
JP7643647B1 (ja) 防曇性多層フィルム、これを用いる積層体、及び包装材
JP7435918B1 (ja) 積層体、及び包装材
EP3073471B1 (en) Stretch label and manufacturing method therefor
JP5404017B2 (ja) 食品用包装体
JP4815744B2 (ja) 透明蒸着フィルムおよびその製造法
JP2026028591A (ja) 積層フィルム、及び包装体
JP7288591B2 (ja) 積層体、包装材料及び包装体
US20240351316A1 (en) Thermoformable sheet and thermoformed package
JP7849668B1 (ja) 防曇性多層フィルム、これを用いる積層体、及び包装材
JP7545609B1 (ja) 積層体、包装袋、蓋材、および積層体の製造方法
JP7602737B2 (ja) 積層体、チューブ容器本体およびチューブ容器
JP7844989B2 (ja) 積層体および積層体の製造方法
JP2024043721A (ja) 積層体、包装体、及びヒートシール組成物
JP4679120B2 (ja) 遮光性包装材及びこれを用いた包装体
WO2025249481A1 (ja) 印刷物、印刷媒体、及び包装体
JP2000117912A (ja) バリア性フィルムおよびそれを使用した積層材
JP2004359346A (ja) ガゼット型袋
JP2005145486A (ja) 餅包装体
JP2024073024A (ja) 超音波シール用シーラントフィルム、ラミネートフィルム及び包装材
WO2018003803A1 (ja) インモールドラベル及びインモールド成形体
TW202610838A (zh) 防霧性多層膜、使用其之積層體、及包裝材

Legal Events

Date Code Title Description
STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION