US20200291551A1 - Lyocell filament denim - Google Patents
Lyocell filament denim Download PDFInfo
- Publication number
- US20200291551A1 US20200291551A1 US16/649,201 US201816649201A US2020291551A1 US 20200291551 A1 US20200291551 A1 US 20200291551A1 US 201816649201 A US201816649201 A US 201816649201A US 2020291551 A1 US2020291551 A1 US 2020291551A1
- Authority
- US
- United States
- Prior art keywords
- denim
- lyocell
- yarn
- sample
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 229920000433 Lyocell Polymers 0.000 title claims abstract description 112
- 239000004744 fabric Substances 0.000 claims abstract description 68
- 239000002932 luster Substances 0.000 claims abstract description 28
- 238000012360 testing method Methods 0.000 claims description 47
- 239000000835 fiber Substances 0.000 claims description 34
- 238000004061 bleaching Methods 0.000 claims description 22
- 206010020112 Hirsutism Diseases 0.000 claims description 14
- 238000005299 abrasion Methods 0.000 claims description 9
- FJQXCDYVZAHXNS-UHFFFAOYSA-N methadone hydrochloride Chemical compound Cl.C=1C=CC=CC=1C(CC(C)N(C)C)(C(=O)CC)C1=CC=CC=C1 FJQXCDYVZAHXNS-UHFFFAOYSA-N 0.000 claims description 8
- 230000015572 biosynthetic process Effects 0.000 claims description 7
- 229920000742 Cotton Polymers 0.000 abstract description 48
- 239000000463 material Substances 0.000 abstract description 31
- 239000000523 sample Substances 0.000 description 106
- 230000000052 comparative effect Effects 0.000 description 53
- 229920002678 cellulose Polymers 0.000 description 24
- 239000001913 cellulose Substances 0.000 description 24
- 229920002334 Spandex Polymers 0.000 description 22
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 19
- 238000000034 method Methods 0.000 description 16
- 238000010438 heat treatment Methods 0.000 description 12
- 238000005406 washing Methods 0.000 description 12
- 229920000297 Rayon Polymers 0.000 description 11
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 10
- 230000035807 sensation Effects 0.000 description 9
- 229920000728 polyester Polymers 0.000 description 8
- 229920000642 polymer Polymers 0.000 description 8
- 239000000243 solution Substances 0.000 description 8
- 239000003795 chemical substances by application Substances 0.000 description 7
- QGJOPFRUJISHPQ-UHFFFAOYSA-N Carbon disulfide Chemical compound S=C=S QGJOPFRUJISHPQ-UHFFFAOYSA-N 0.000 description 6
- 150000001412 amines Chemical class 0.000 description 6
- 239000007844 bleaching agent Substances 0.000 description 6
- 239000012925 reference material Substances 0.000 description 6
- 235000011121 sodium hydroxide Nutrition 0.000 description 6
- ZAMOUSCENKQFHK-UHFFFAOYSA-N Chlorine atom Chemical compound [Cl] ZAMOUSCENKQFHK-UHFFFAOYSA-N 0.000 description 5
- 102000004190 Enzymes Human genes 0.000 description 5
- 108090000790 Enzymes Proteins 0.000 description 5
- 239000000460 chlorine Substances 0.000 description 5
- 229910052801 chlorine Inorganic materials 0.000 description 5
- 238000011156 evaluation Methods 0.000 description 4
- 239000002904 solvent Substances 0.000 description 4
- 239000004759 spandex Substances 0.000 description 4
- 239000004753 textile Substances 0.000 description 4
- 238000009941 weaving Methods 0.000 description 4
- 229920001131 Pulp (paper) Polymers 0.000 description 3
- 238000004458 analytical method Methods 0.000 description 3
- 238000001125 extrusion Methods 0.000 description 3
- 238000009991 scouring Methods 0.000 description 3
- 238000001228 spectrum Methods 0.000 description 3
- 229920001059 synthetic polymer Polymers 0.000 description 3
- 238000004804 winding Methods 0.000 description 3
- 229920006309 Invista Polymers 0.000 description 2
- 235000008708 Morus alba Nutrition 0.000 description 2
- 240000000249 Morus alba Species 0.000 description 2
- 239000004677 Nylon Substances 0.000 description 2
- CDBYLPFSWZWCQE-UHFFFAOYSA-L Sodium Carbonate Chemical compound [Na+].[Na+].[O-]C([O-])=O CDBYLPFSWZWCQE-UHFFFAOYSA-L 0.000 description 2
- PMZURENOXWZQFD-UHFFFAOYSA-L Sodium Sulfate Chemical compound [Na+].[Na+].[O-]S([O-])(=O)=O PMZURENOXWZQFD-UHFFFAOYSA-L 0.000 description 2
- 239000002253 acid Substances 0.000 description 2
- 206010061592 cardiac fibrillation Diseases 0.000 description 2
- 238000006243 chemical reaction Methods 0.000 description 2
- 238000010276 construction Methods 0.000 description 2
- 230000002596 correlated effect Effects 0.000 description 2
- 230000000875 corresponding effect Effects 0.000 description 2
- 230000005611 electricity Effects 0.000 description 2
- ZOOODBUHSVUZEM-UHFFFAOYSA-N ethoxymethanedithioic acid Chemical compound CCOC(S)=S ZOOODBUHSVUZEM-UHFFFAOYSA-N 0.000 description 2
- 230000002600 fibrillogenic effect Effects 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-M hydroxide Chemical compound [OH-] XLYOFNOQVPJJNP-UHFFFAOYSA-M 0.000 description 2
- 230000003993 interaction Effects 0.000 description 2
- 239000007788 liquid Substances 0.000 description 2
- 239000000203 mixture Substances 0.000 description 2
- 229920001778 nylon Polymers 0.000 description 2
- 230000000704 physical effect Effects 0.000 description 2
- 239000000047 product Substances 0.000 description 2
- 239000002002 slurry Substances 0.000 description 2
- 230000003068 static effect Effects 0.000 description 2
- 239000002759 woven fabric Substances 0.000 description 2
- 239000012991 xanthate Substances 0.000 description 2
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- 229920001747 Cellulose diacetate Polymers 0.000 description 1
- 229920002284 Cellulose triacetate Polymers 0.000 description 1
- VEXZGXHMUGYJMC-UHFFFAOYSA-M Chloride anion Chemical compound [Cl-] VEXZGXHMUGYJMC-UHFFFAOYSA-M 0.000 description 1
- RWSOTUBLDIXVET-UHFFFAOYSA-N Dihydrogen sulfide Chemical compound S RWSOTUBLDIXVET-UHFFFAOYSA-N 0.000 description 1
- MHAJPDPJQMAIIY-UHFFFAOYSA-N Hydrogen peroxide Chemical compound OO MHAJPDPJQMAIIY-UHFFFAOYSA-N 0.000 description 1
- 239000004743 Polypropylene Substances 0.000 description 1
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 1
- NNLVGZFZQQXQNW-ADJNRHBOSA-N [(2r,3r,4s,5r,6s)-4,5-diacetyloxy-3-[(2s,3r,4s,5r,6r)-3,4,5-triacetyloxy-6-(acetyloxymethyl)oxan-2-yl]oxy-6-[(2r,3r,4s,5r,6s)-4,5,6-triacetyloxy-2-(acetyloxymethyl)oxan-3-yl]oxyoxan-2-yl]methyl acetate Chemical compound O([C@@H]1O[C@@H]([C@H]([C@H](OC(C)=O)[C@H]1OC(C)=O)O[C@H]1[C@@H]([C@@H](OC(C)=O)[C@H](OC(C)=O)[C@@H](COC(C)=O)O1)OC(C)=O)COC(=O)C)[C@@H]1[C@@H](COC(C)=O)O[C@@H](OC(C)=O)[C@H](OC(C)=O)[C@H]1OC(C)=O NNLVGZFZQQXQNW-ADJNRHBOSA-N 0.000 description 1
- 238000010521 absorption reaction Methods 0.000 description 1
- 238000004026 adhesive bonding Methods 0.000 description 1
- VQLYBLABXAHUDN-UHFFFAOYSA-N bis(4-fluorophenyl)-methyl-(1,2,4-triazol-1-ylmethyl)silane;methyl n-(1h-benzimidazol-2-yl)carbamate Chemical compound C1=CC=C2NC(NC(=O)OC)=NC2=C1.C=1C=C(F)C=CC=1[Si](C=1C=CC(F)=CC=1)(C)CN1C=NC=N1 VQLYBLABXAHUDN-UHFFFAOYSA-N 0.000 description 1
- 239000006227 byproduct Substances 0.000 description 1
- 229910052799 carbon Inorganic materials 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 238000000576 coating method Methods 0.000 description 1
- 230000001143 conditioned effect Effects 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 238000006298 dechlorination reaction Methods 0.000 description 1
- 230000007812 deficiency Effects 0.000 description 1
- 238000013461 design Methods 0.000 description 1
- 230000001627 detrimental effect Effects 0.000 description 1
- 238000010790 dilution Methods 0.000 description 1
- 239000012895 dilution Substances 0.000 description 1
- 238000004090 dissolution Methods 0.000 description 1
- 238000005108 dry cleaning Methods 0.000 description 1
- 238000000578 dry spinning Methods 0.000 description 1
- 238000001035 drying Methods 0.000 description 1
- 238000004043 dyeing Methods 0.000 description 1
- 230000000694 effects Effects 0.000 description 1
- 238000004453 electron probe microanalysis Methods 0.000 description 1
- 230000007613 environmental effect Effects 0.000 description 1
- 238000005562 fading Methods 0.000 description 1
- 238000004898 kneading Methods 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 238000005259 measurement Methods 0.000 description 1
- 238000002074 melt spinning Methods 0.000 description 1
- KJPHTXTWFHVJIG-UHFFFAOYSA-N n-ethyl-2-[(6-methoxypyridin-3-yl)-(2-methylphenyl)sulfonylamino]-n-(pyridin-3-ylmethyl)acetamide Chemical compound C=1C=C(OC)N=CC=1N(S(=O)(=O)C=1C(=CC=CC=1)C)CC(=O)N(CC)CC1=CC=CN=C1 KJPHTXTWFHVJIG-UHFFFAOYSA-N 0.000 description 1
- 239000004745 nonwoven fabric Substances 0.000 description 1
- 238000011022 operating instruction Methods 0.000 description 1
- 230000035699 permeability Effects 0.000 description 1
- -1 polypropylene Polymers 0.000 description 1
- 229920001155 polypropylene Polymers 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 238000003825 pressing Methods 0.000 description 1
- 238000012545 processing Methods 0.000 description 1
- 239000002994 raw material Substances 0.000 description 1
- 239000000376 reactant Substances 0.000 description 1
- 238000011084 recovery Methods 0.000 description 1
- 239000013074 reference sample Substances 0.000 description 1
- 229910052938 sodium sulfate Inorganic materials 0.000 description 1
- 235000011152 sodium sulphate Nutrition 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 229910001220 stainless steel Inorganic materials 0.000 description 1
- 239000010935 stainless steel Substances 0.000 description 1
- 239000000126 substance Substances 0.000 description 1
- 239000001117 sulphuric acid Substances 0.000 description 1
- 235000011149 sulphuric acid Nutrition 0.000 description 1
- 229920002994 synthetic fiber Polymers 0.000 description 1
- 239000004758 synthetic textile Substances 0.000 description 1
- 239000010409 thin film Substances 0.000 description 1
- 210000002268 wool Anatomy 0.000 description 1
- NWONKYPBYAMBJT-UHFFFAOYSA-L zinc sulfate Chemical compound [Zn+2].[O-]S([O-])(=O)=O NWONKYPBYAMBJT-UHFFFAOYSA-L 0.000 description 1
- 239000011686 zinc sulphate Substances 0.000 description 1
- 235000009529 zinc sulphate Nutrition 0.000 description 1
Images
Classifications
-
- D03D15/0027—
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
- D03D15/20—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads
- D03D15/208—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads cellulose-based
- D03D15/225—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads cellulose-based artificial, e.g. viscose
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F2/00—Monocomponent artificial filaments or the like of cellulose or cellulose derivatives; Manufacture thereof
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D1/00—Woven fabrics designed to make specified articles
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D1/00—Woven fabrics designed to make specified articles
- D03D1/0017—Woven household fabrics
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D13/00—Woven fabrics characterised by the special disposition of the warp or weft threads, e.g. with curved weft threads, with discontinuous warp threads, with diagonal warp or weft
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
- D03D15/20—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads
- D03D15/208—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads cellulose-based
- D03D15/217—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads cellulose-based natural from plants, e.g. cotton
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
- D03D15/20—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads
- D03D15/283—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the material of the fibres or filaments constituting the yarns or threads synthetic polymer-based, e.g. polyamide or polyester fibres
-
- D—TEXTILES; PAPER
- D03—WEAVING
- D03D—WOVEN FABRICS; METHODS OF WEAVING; LOOMS
- D03D15/00—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used
- D03D15/40—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the structure of the yarns or threads
- D03D15/47—Woven fabrics characterised by the material, structure or properties of the fibres, filaments, yarns, threads or other warp or weft elements used characterised by the structure of the yarns or threads multicomponent, e.g. blended yarns or threads
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06L—DRY-CLEANING, WASHING OR BLEACHING FIBRES, FILAMENTS, THREADS, YARNS, FABRICS, FEATHERS OR MADE-UP FIBROUS GOODS; BLEACHING LEATHER OR FURS
- D06L4/00—Bleaching fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods; Bleaching leather or furs
-
- D—TEXTILES; PAPER
- D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
- D06L—DRY-CLEANING, WASHING OR BLEACHING FIBRES, FILAMENTS, THREADS, YARNS, FABRICS, FEATHERS OR MADE-UP FIBROUS GOODS; BLEACHING LEATHER OR FURS
- D06L4/00—Bleaching fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods; Bleaching leather or furs
- D06L4/20—Bleaching fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods; Bleaching leather or furs using agents which contain halogen
- D06L4/22—Bleaching fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods; Bleaching leather or furs using agents which contain halogen using inorganic agents
- D06L4/24—Bleaching fibres, filaments, threads, yarns, fabrics, feathers or made-up fibrous goods; Bleaching leather or furs using agents which contain halogen using inorganic agents using chlorites or chlorine dioxide
-
- D—TEXTILES; PAPER
- D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
- D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
- D10B2201/00—Cellulose-based fibres, e.g. vegetable fibres
- D10B2201/20—Cellulose-derived artificial fibres
- D10B2201/22—Cellulose-derived artificial fibres made from cellulose solutions
Definitions
- the invention relates to a Denim fabric.
- Denim is a fabric which is usually woven from cotton as a warp-faced textile having a twill pattern.
- a very common denim fabric is indigo-dyed denim, in which only the warp is dyed. The weft stays white. The core of the warp, however, remains undyed, which results in fading characteristics which are typical for denim. Due to the warp-faced weaving, denim is colored—typically indigo—on the outside and white—uncolored—on the inside.
- cotton is a fiber which is highly resistant and therefore able to undergo even aggressive finishing, its mechanical properties and its haptic qualities are not ideal and give denim only a small range of capabilities.
- Man-made continuous filament yarns are widely used in the textile industry to produce fabrics with a distinct character compared to fabrics produced from yarns made using staple fiber.
- a continuous filament yarn is one in which all of the fibers are continuous throughout any length of the yarn.
- a continuous filament yarn will commonly consist of 20 to 200 or more individual fibers which are all parallel to each other and the axis of the yarn when produced.
- the yarn is produced by extruding a solution or melt of a polymer or a polymer derivative and then winding the yarn produced onto a bobbin or reel or by forming a cake by centrifugal winding.
- Synthetic polymer continuous filament yarns are common.
- nylon, polyester and polypropylene continuous filament yarns are used in a wide variety of fabrics. They are produced by melt spinning a molten polymer through a spinneret with a number of holes corresponding to the number of fibers required in the yarn produced. After the molten polymer has started to solidify, the yarn may be drawn to orient the polymer molecules and improve the properties of the yarn.
- Continuous filament yarns can also be spun from cellulose derivatives such as cellulose diacetate and cellulose triacetate by dry spinning.
- the polymer is dissolved in a suitable solvent and then extruded through a spinneret.
- the solvent evaporates quickly after extrusion causing the polymer to precipitate in the form of a yarn.
- the newly produced yarn may be drawn to orient the polymer molecules.
- Continuous filament yarns can further be produced from cellulose using the viscose process.
- Cellulose is converted to cellulose xanthate by reaction with sodium hydroxide and carbon disulphide and then dissolved in a sodium hydroxide solution.
- the cellulose solution commonly called viscose, is extruded through a spinneret into an acid bath.
- the sodium hydroxide is neutralized causing the cellulose to precipitate.
- the cellulose xanthate is converted back to cellulose by reaction with the acid.
- the newly formed fiber is drawn to orient the cellulose molecules, washed to remove reactants from the fiber and then dried and wound onto a bobbin.
- the wet yarn was collected into a cake using a centrifugal winder—a Topham Box. The cake of yarn was then dried in an oven before winding onto a bobbin.
- Continuous filament cellulose yarns are also produced using the cupro process.
- Cellulose is dissolved in a solution of cuprammonium hydroxide.
- the resulting solution is extruded into a water bath where the cuprammonium hydroxide is diluted and the cellulose precipitates.
- the resulting yarn is washed, dried and wound onto a bobbin.
- Cellulosic continuous filament yarn produced by either the viscose or the cupro process can be made into fabrics by weaving. Fabrics produced are used for a variety of applications including linings for women's apparel and menswear.
- Fabrics made from continuous filament cellulose yarns are good at moisture handling to enhance the comfort of the wearer. They do not generate static electricity as readily as fabrics made using continuous filament synthetic yarns.
- Fabrics made from currently available continuous filament cellulose yarns generally have poor physical properties.
- the dry strength and the tear strength are poor compared to fabrics made from synthetic polymers such as polyester.
- the wet strength is much lower than the dry strength due to interactions between the cellulose and water.
- the abrasion resistance is low.
- the interactions with water also soften the cellulose causing the fabrics made from the yarn to be unstable when wetted. This is particularly problematic when washing these materials in a household washing machine.
- a denim fabric that is made from weft yarns and warp yarns, wherein at least one of the weft yarns and the warp yarns contains or consists of lyocell filaments.
- Such a lyocell filament denim withstands aggressive finishing agents. Further, the denim comprising or consisting of lyocell filament yarn is softer and smoother even than denim with a silk component. Thus, the inventive lyocell filament denim gives rise to a new class of fabrics with an entirely new set of properties. This is all the more surprising as it would have been expected from the properties of cotton yarn that—if at all—denim containing or consisting of lyocell staple fiber would be a replacement for cotton denim.
- Lyocell is the generic name given to a type of cellulosic man-made fiber produced by a direct dissolution process. The lyocell process is described e.g. in U.S. Pat. No. 4,246,221 and WO 93/19230.
- a slurry of wood pulp is formed with a solution of amine oxide in water. Water is then evaporated from the slurry in a thin film evaporator vessel. When the water level is reduced below a certain level, the cellulose forms a solution in the amine oxide. The resulting viscous liquid solidifies to a glassy solid below about 70° C. If maintained above this temperature, it can be pumped through a spinneret to form filaments which are then immediately immersed in water where the dilution of the amine oxide causes the cellulose to precipitate.
- the spinneret used for extrusion of the amine oxide cellulose solution has a number of holes corresponding to the number of filaments required in the continuous filament yarn.
- the newly formed yarn is washed clean of amine oxide with a counter current flow of water. This washing may be done on self advancing reels on which water is introduced to wash the fiber. A finish may be applied to aid further processing and the yarn is dried. The washed and dried yarn is wound onto a bobbin.
- cellulose in the form of wood pulp is the only raw material used.
- the wood pulp used comes from sustainable managed forests.
- the filaments produced are 100% cellulose and are the only output from the process.
- the amine oxide solvent is recovered from the washing water and reused to produce further filament. This recovery can be as high as 99.7%.
- the environmental impact of the lyocell process is very low. There are virtually no releases of gaseous or liquid emissions from the process and the filament produced is solvent free.
- the viscose process uses carbon disulphide, sodium hydroxide, sulphuric acid and zinc sulphate. Hydrogen sulphide and carbon disulphide can be released from the process unless a great deal of care is taken. Sodium sulphate is produced as a by-product of the process.
- the invention can be further improved by the following additional features, which can be combined independent of one another and which each exhibit a different technical effect.
- the continuous filament lyocell yarns used to produce the products of the invention may be the as produced yarn in an untwisted state or may be twisted by rewinding. It may be a doubled yarn. It may be combined with another continuous filament yarn or staple fiber yarn by twisting the yarns together or by intermingling using for example an air jet.
- the lyocell denim according to the invention contains preferably at least 10% lyocell filaments in at least one of the weft and the warp yarn.
- the minimum overall content of lyocell filaments in the lyocell denim is above 10%.
- a content of more than 10% can improve the handfeel of the fabric significantly given the soft structure of a yarn containing or consisting of Lyocell filaments. Consequently, the total content of lyocell of at least 10% already gives a haptical impact independent of whether the Lyocell filament is used in warp or weft.
- a blend of at least 10% lyocell filaments with other synthetic or cellulose filaments e.g.
- Viscose or Cupro filaments or with Viscose or Cupro staple fibers, or wool and cotton improves the strength of the yarn.
- a blend of at least 10% lyocell filaments and synthetics improves the breathability and moisture management of the fabric significantly.
- the denim is bleached.
- the lyocell filaments are capable of being treated by aggressive finishing agents such as chlorine bleach.
- aggressive finishing agents such as chlorine bleach.
- such an aggressive finishing agent in particular chlorine bleach, softens the yarn containing or consisting of lyocell filaments, and thus actually improves softness and smoothness of the lyocell denim.
- the lyocell denim according to the invention has a superior softness.
- An indirect measure for softness is the TS7 value as determined by a TSA tissue softness analyzer.
- the denim according to the invention has a TS7 value of no more than 8 in the fixed state, i.e. before garment wash.
- a TS7 value of no more than 6 can be obtained with the inventive denim after garment wash, and even after bleaching.
- the TSA also yields another parameter, the TS750 value, which is correlated to smoothness.
- the denim according to the invention in the fixed state has a TS750 value of no more than 120.
- a TS750 value of no more than 120 may also be maintained after garment wash and/or after bleaching.
- the denim according to the invention has higher smoothness and/or softness than a cotton denim and an even partly superior softness and/or smoothness to denim with silk yarn.
- the denim also has high mechanical resilience.
- the denim may score at least 15,000 cycles to hole formation in a Martindale abrasion test in the fixed state, i.e. before garment wash.
- the denim may score 8,000 cycles to hole formation after garment wash and/or after bleaching. This indicates that the denim according to the invention can be used for textiles that are subject to strong wear.
- the outer face of the denim i.e. the warp face of the denim, may, in another embodiment, have a pilling grade of no worse than 5 in the fixed state, i.e. before garment wash, and/or no worse than 5 after garment wash and no worse than 5 after bleaching.
- Yarn strength of the denim in the at least one, warp and/or weft, direction in which the lyocell filament yarn is used is preferably at least 20 cN/tex, more preferably at least 25 cN/tex, in the fixed state cond. 20/65 and/or at least 10 cN/tex, preferably at least 20 cN/tex in the wet state.
- the yarn strength in the at least one, warp and/or weft, direction in which the lyocell filament yarn is used was preferably at least 4.5 cN/tex, more preferably at least 5 cN/tex cond. 20/65, and preferably at least 3, preferably at least 7 cN/tex wet.
- yarn strength in the at least one, warp and/or weft, direction in which the lyocell filament yarn is used is at least 2 cN/tex, preferably at least 3 cN/tex. cond. 20/65, and preferably at least 2 cN/tex, more preferably at least 5 cN/tex wet.
- Yarn elongation of the weft and/or warp yarn which contains or consists of lyocell filaments may be at least 4% after fixation and/or at least 2% after garment wash and/or at least 1% after bleaching.
- the hairiness of the denim according to the invention may have a grade of no worse than 4 after garment wash and of no worse than 3 after bleaching on the warp face, i.e. the outer face of the denim.
- the fiber splice of the denim according to the invention may have a grade of no worse than 4 before and/or after fixation and/or of no worse than 4.5 after garment wash and/or of no worse than 4.5 after bleaching.
- denim according to the invention qualify the denim according to the invention as a fabric suitable for an extremely wide range of denim applications.
- the specific hand as determined by a Handle-O-Meter in the direction of the warp and/or weft yarns that contain or consist of lyocell filaments is at least 4 mN m 2 g ⁇ 1 after garment wash and/or at least 3 mN m 2 g ⁇ 1 after bleaching. These values indicate a high smoothness and flexibility of the inventive denim.
- the luster of the warp and/or weft yarn containing, preferably consisting of, lyocell filaments may be at least 20% reflection. This allows creating a denim having high gloss.
- the invention also relates to a garment, in particular a garment of women's apparel, and/or menswear, such as jackets, coats, blouses, dresses and pants, in which a lyocell denim as described above is used.
- the invention relates to the use of a yarn containing or consisting of lyocell filaments in a denim fabric.
- Moisture regain of the fabric as measured according to ASTMD 1909 is an indicator for the comfort level.
- Mulberry silk has 11% of moisture regain and offers one of the best comfort levels of all fabrics with respect to moisture regain.
- the lyocell filament yarn and/or denim according to the invention preferably has a moisture regain of at least 13% which results in a similar or even better comfort than mulberry silk.
- the lyocell filament denim of the invention may be of any style, weave or finish that is suitable for production with a continuous filament yarn and results in a denim comparable to cotton.
- the lyocell filament denim may be constructed as plain weave, twill, satin, sateen, hopsack, cord and fancy weaves. Fabrics may be woven using any loom suitable for weaving continuous filament yarns including shuttle looms, rapier looms, projectile looms or ribbon looms.
- the lyocell denim fabrics produced using continuous filament lyocell yarns can have aesthetics and appearance similar to a fabric produced from continuous filament viscose yarn, but have significantly better physical properties.
- the higher strength and modulus of the yarn result in improved fabric breaking strength, tear strength, abrasion resistance and stability.
- the wet fabric properties are also superior.
- FIG. 1 shows schematically a garment 1 which at least partly is made from a lyocell denim 2 .
- the garment 1 is only schematically shown to be pants but not limited thereto.
- the garment 1 may be also a dress, a suit, a costume, a jacket, a shirt or a blouse or parts of and/or on these garments.
- the lyocell denim 2 comprises weft yarns 4 and warp yarns 6 , which may be twisted. At least one of the weft yarns 4 and the warp yarns 6 contains or consists of lyocell filaments.
- FIG. 2 An example of a warp and/or weft yarns 6 , 4 with at least one lyocell filament 8 is shown in FIG. 2 .
- FIG. 3 shows a twisted warp and/or weft 3-ply yarn 4 , 6 with at least one lyocell filament.
- At least one of the filaments 8 is a lyocell filament.
- the twisted filament may have any number of filaments and any twist direction.
- at least 50% of the yarn 4 , 6 consist of lyocell filaments 8 .
- samples were prepared and compared to comparative examples made from denim consisting of or containing cotton.
- bottom is the benchmark, against which any denim using yarn from man-made fibers or filaments has to compete in the market.
- the samples of the inventive lyocell filament denim are compared to comparative examples using the following tests:
- luster of the fabrics was determined at an angle of 75° according to TAPPI T480.
- the tests were carried out by 3 persons in a dark room in which a color assessment cabinet “Multilight Datacolor” of Variolux with daylight lamps D65 was provided.
- the lamps were mounted on an upper side of the cabinet.
- test sample was held oblique by the test person and the hairiness was graded between best (grade 5 , no hairiness) and worst (grade 1 , long protruding fibers up to 2 mm).
- the number of pillings was assessed using reference samples (knits K 3 or K 2 , or wovens W 3 or W 2 ) of EMPA Standard SN 198525 analogous to DIN EN ISO 12 945-2.
- the reference samples are graded with 1 to 5 and are compared to the test samples.
- Grade 5 corresponds to a denim having no pillings. The more pillings there are on the surface of the test samples the worse the grade gets. The worst grade is 1.
- Fiber splice is created if fibrillic fibers are moved to the surface by scouring.
- the fibrillic fibers are brushlike ends with stick out if the scoured sample is analyzed under a microscope.
- a microscope SM with an X10 eyepiece of UHL Technische Mikroskope was used for measuring fiber splice.
- grade 5 was given for a smooth surface which showed no fibrilles. If there was a dense fur of long, curved fiber ends that were partly detached from the surface, grade 1 was given.
- Samples were prepared as follows. Hereby, weight was determined according to DIN EN 12127. Yarn count in the weft and warp was performed in accordance with DIN 53820-3.
- Sample 1 was a denim 1857-A, in which the warp consisted of bright, untwisted yarn having dtex 500f300 that was made of lyocell filaments.
- the weft yarn consisted of cotton yarn having a core of Lycra T400. This resulted in a fabric having 70% lyocell yarns, 20% cotton, 8% elastomultiester and 2% elastane.
- the denim had a weight of 343 g m ⁇ 2 .
- Sample 2 was a denim 978-150-814 containing 33% lyocell filaments and 67% cotton.
- the weight was 143 g m ⁇ 2 .
- the warp was made of cotton ring yarn Z.
- the weft was made from yarn dtex 150f90.
- Sample 3 was a denim 1857-8, in which the warp consisted of bright untwisted yarn of 100% lyocell filaments, the yarn having a linear mass density of dtex 500f300.
- the weft was a 100% polyester yarn with an ELAS core of Lycra T400. This resulted in a denim having 356 gm ⁇ 2 and 70% lyocell, 28% polyester and 2% elastane.
- Sample 6 was a denim 1857-CNF containing 70% lyocell, 28% cotton and 2% elastane. Warp consisted of a lyocell filament yarn having 556 dtex. Weft was made from dull cotton ring yarn with an elastane core.
- Sample 5 was a denim 978-100-814 of 45% lyocell and 55% cotton. Warp consisted of cotton ring yarn Z and weft consisted of lyocell yarn dtex 100f 60. The material weight was 128 g m ⁇ 2 .
- Comparative Sample 4 was a denim 840-814 made from 59% cotton and 41% silk, where the warp yarn was made of cotton and the weft yarn was made from silk. This resulted in a denim that had high softness and smoothness, and a luster.
- the weight was 171 g m ⁇ 2 .
- Comparative Sample 7 was denim 435-4047 consisting of 98% cotton and 2% elastene. Warp was made from cotton ring yarn and weft from cotton ring yarn with a dull elastane core.
- Samples 1 to 3 and 6 were benchmarked against comparative sample 7 with respect to washability, resistance against finishing agents, smoothness, softness and luster.
- Samples 2 and 5 were benchmarked against comparative sample 4 , to compare a lyocell warp denim against a cotton warp denim as both featured the same weft material.
- the samples and comparative samples underwent the following finishing steps. After each finishing step, the samples and comparative examples were tested.
- Samples 1 , 2 , 3 , 5 , 6 and comparative samples 4 and 7 were garment-washed as follows.
- Fibrillation was carried out with a liquor ratio of 1:60 with 2.5 kg fabric and 150 l liquor at 22 rpm for 20 minutes at 60° C. with maximum heating rate in 2 g/l Persoftal L, 2 g/l soda and 0.3 g/l Lavasperse KDS conc.
- the liquor was cooled down to 40° C. and rinsed cold with 300 l, then rinsed warm with 150 l for 5 minutes at 50° C., where heating started right at the beginning of the rinsing, and then again rinsed cold with 300 l.
- enzyme washing was carried out at a liquor ratio of 1:60 again with 2.5 kg fabric and 150 l liquor at 22 rpm.
- the liquor contained 2 g/l Persoftal L, 3 g/l Peristal E and 0.3 g/l Lavasperse KDS conc.
- the pH value was controlled to be between pH 4.5-5. After heating to 55° C. at the maximum heating rate, the pH value was checked. At pH 5.5, 2 g/l Perizym 2000 were added before adding the enzyme and then the material was processed at 55° C. for 55 minutes. Then the material was heated to 85° C. and treated at 85° C. for 15 minutes.
- the liquor was then drained and the material rinsed as follows: First, cold rinsing with 300 l, then warm rinsing with 150 l, where the heating started with the filling of the second rinsing step. Warm rinsing continued for 5 minutes at 50° C. Finally, cold rinsing took place with 300 l.
- Reviving took place at a liquor ratio of 1:60 as above using 2% Tubingal RGH, 1% Tubingal RWM, 3 g/l Peristal E at 15 minutes and 40° C. after heating at the maximum rate.
- the liquor was then drained and the material was tumble-dryed for 50 minutes at 80° C. and then allowed to cool down for 20 minutes.
- samples 1 , 2 , 3 , 5 , 6 and comparative samples 4 and 7 were bleached as follows:
- Pre-scouring took place at a liquor ratio of 1:60 with 2.5 kg of fabrics and 150 l of liquor.
- 2 g/l Persoftal L, 0.5 g/l NaOH 100% (1 g/l NaOH 50%) and 0.2 g/l Lava Sperse KDS conc. were used. Pre-scouring was carried out for 20 minutes at 60° C. (maximum heating rate).
- Bleaching took place at a liquor ratio of 1:60 and 15 rpm, cold, for 30 minutes, again with 2.5 kg fabrics and 150 l liquor containing 2 g/l Soda and 0.4 g/l Lavasperse KDS conc. The pH value was checked and maintained at pH 10.
- As bleaching agent 3 g/l active chlorine (20 ml/l bleaching lye solution 150 g/l) was used.
- the liquor was then drained and the material was cold-rinsed with 300 l and warm rinsed with 150 l as above.
- Dechlorination was performed with 2 ml/l hydrogen peroxide 50% for 30 minutes at 40° C.
- cold rinsing with 300 l warm rinsing with 150 l for 5 minutes at 50° C. (heating started with the rinsing), and cold rinsing with 300 l was performed.
- enzyme washing was carried out at a liquor ratio of 1:60 again with 2.5 kg fabric and 150 l liquor at 22 rpm.
- the liquor contained 2 g/l Persoftal L, 3 g/l Peristal E and 0.3 g/l Lavasperse KDS conc.
- the pH value was maintained between pH 4.5-5. After heating to 55° C. at the maximum heating rate, the pH value was checked. before adding the enzyme and then the material was processed at 55° C. for 55 minutes. Then the material was heated to 85° C. and treated at 85° C. for 15 minutes.
- the liquor was then drained and the material rinsed as follows: First, cold rinsing with 300 l, then warm rinsing with 150 l, where the heating started with the filling of the second rinsing step. Warm rinsing continued for 5 minutes at 50° C. Finally, cold rinsing took place with 300 l.
- Reviving took place at a liquor ratio of 1:60 as above using 2% Tubingal RGH, 1% Tubingal RWM, 3 g/l Peristal E at 15 minutes and 40° C. after heating at the maximum rate.
- lyocell filament denim as does cotton—withstands even aggressive finishing agents such as chlorine bleach that destroys silk.
- the lyocell filament denim is at least comparable to if not better by one grade than cotton denim before and after garment wash and after bleaching. Further, the lyocell filaments are not subject to the fibrillation that occurs with cotton after washing.
- yarn strength of the inventive lyocell filament denim is still very good.
- the yarn strength of the lyocell filament denim is paired with luster, softness and smoothness that are all superior to cotton denim and can only be achieved with a denim containing silk. However, the latter cannot be bleached.
- the TSA test was carried out to verify that the haptic qualities of the lyocell filament denim of samples 1 to 5 are at least equal if not superior to the haptic qualities of the silk denim of comparative sample 4 .
- the two predominant haptic qualities that are improved by using silk in denim are softness and smoothness. To assess these characteristics objectively, the TSA test was carried out.
- the TSA test was performed using a TSA Tissue Softness Analyzer device of emtec electronics GmbH, Leipzig, Germany, and the software ESM which is shipped with the TSA.
- the TSA measures a sound spectrum which results from pressing and rotating a star-like body against a sample fabric with a defined force. For testing, the fabric is clamped around its perimeter and unsupported otherwise, in particular opposite the rotating body.
- the software and its evaluation algorithm was not used. Instead, the sound pressure as measured by the TSA at 7 kHz (TS7) was taken as an objective indirect measure of softness and the sound pressure at 750 Hz (TS750) in the sound spectrum measured by the TSA was taken as an objective indirect measure of smoothness.
- the sound pressure is automatically given by the TSA as dB V2 rms, where V is the rotational velocity of the rotating body. Using these values directly avoided any problems that may have arisen due to the EMS algorithm having been developed for tissue, and not for woven fabrics. A total of four probes was subjected to the TSA test for each sample.
- the Handle-O-Meter tests were carried out using a Handle-O-Meter testing device of Thwing-Albert Instrument Company, West Berlin, N.J., USA. Sample size was 10 cm ⁇ 10 cm. The 1 ⁇ 4 inch slot was used with a 1,000 g beam and a stainless steel surface. The tests were conducted on samples cond. 65/20.
- the Handle-O-Meter yields two force measurements which are assigned to two orthogonal directions, a machine direction MD which in the chosen set-up corresponded to the warp direction and a cross direction CD which in the chosen setup corresponded to the weft direction. These forces are correlated to the stiffness and smoothness of the tested surface. The force is normalized with the bulk weight of the test sample, resulting in a specific hand in mN m 2 g ⁇ 1 .
- the silk denim of comparative sample 4 is less smooth then samples 2 and 5 , in which lyocell endless filaments are used in the weft instead of silk. Further, the lyocell filament denim is softer than the silk denim of comparative sample 4 before finishing. After finishing, softness of samples 2 and 5 corresponds to the softness of comparative sample 4 .
- the lyocell filament denim according to the invention combines indeed superior softness and smoothness with the capability of being bleached.
- the lyocell filament denim has high tenacity. This combination results in a new class of denim fabrics.
- a handfeel panel was used.
- the panel was put together consisting of ten independent textile experts.
- the panel's task was to evaluate objectively the touch of the lyocell filament denim according to the invention in comparison to the comparative examples.
- the handfeel panel operated as follows:
- All samples to be tested by the handfeel panel were provided in a format 17 cm ⁇ 17 cm and were glued to carbon using a double-sided gluing tape approximately 2 cm from the border on the upper edge.
- the fabric sample was glued onto the cardboard with the right, warp-faced side facing to the front. It was oriented such that the weft direction was horizontal and the warp direction was vertical.
- a semantic grid was defined by providing contrasting pairs of descriptive adjectives for describing the handfeel.
- the term of the contrasting pairs which corresponded to the desired quality is considered “best”.
- Grades ranged from 1 (worst) to 10 (best).
- Reference sample fabrics of the same construction type with as close construction parameters as possible and, at the same time, significant differences in handfeel were pre-defined for each word pair. For example, a fabric being considered as having a reference coarseness and a fabric being considered as having a reference smoothness were given to the handfeel panel.
- the grades for the respective reference fabrics were fixed at 2 and 8 respectively.
- the reference fabric for the worse quality of a word pair had by definition a grade 2 and the reference fabric for the better quality of a word pair a grade 8 .
- Assigning the grades 2 and 8 , respectively, allowed to expand the scale during the test if materials with a better or worse quality than the two reference materials were met.
- the reference material for coarseness was defined to have a grade 2
- the reference material for smoothness was defined to have a grade 8 in the coarseness-smoothness scale. All other materials which were then tested had to be graded by the handfeel panel relative to the reference material.
- comparative sample 7 was used.
- comparative sample 4 was used for all word pairs.
- the sample card had to be taken up with one hand and the fabric was allowed to fold down. Then, the handfeel panel members were asked to grip into the pending fabric in such a way that the right (warp-faced) side of the denim touched the palm;
- Consistence describes whether the fabric gives a feel of having a more open or more dens weaving.
- the sample card was put on table before the individual handfeel panel members.
- the fabric was taken up with both hands and kneading and stretching the fabric.
- Wearing sensation is determined by again lifting the sampe card with one hand and allow the fabric to fold down.
- the sample card is then shaken to evaluate the falling pattern of the fabric. Then, the fabric is gripped by the free hand for further assessment.
- Luster of individual yarns usable in a lyocell denim according to the invention was measured using a glossmeter.
- the results in % reflection of incident light are given in Table 7.
- For measuring the luster of yarns they were wound on wrap-over cardboard and luster was measured according to EN 14086-01/2003 at 45°.
- the luster of fabrics was determined according to TAPPI T480 at 75°. The viewing angle was directed along the yarn direction for measuring yarn luster.
- Samples 1 , 3 , 7 , 8 were yarns made from 100% bright lyocell filaments having the linear mass densities indicated in Table 7.
- Samples 2 , 4 , 5 , 6 are comparative samples.
- Sample 3 had a far superior luster to all other samples and the comparative examples.
- the luster of samples 1 and 6 was comparable to the denim of comparative sample 7 , containing silk.
- Luster of the yarn usable for denim was at least 20% reflection.
- inventive lyocell filament denim also combines a superior luster with resistance against aggressive finishing agents.
Landscapes
- Engineering & Computer Science (AREA)
- Textile Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Botany (AREA)
- Inorganic Chemistry (AREA)
- Woven Fabrics (AREA)
- Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP17195295.5A EP3467171A1 (fr) | 2017-10-06 | 2017-10-06 | Denim à filaments lyocellulaires |
EP17195295.5 | 2017-10-06 | ||
PCT/EP2018/075492 WO2019068476A1 (fr) | 2017-10-06 | 2018-09-20 | Denim à filaments lyocellulaires |
Publications (1)
Publication Number | Publication Date |
---|---|
US20200291551A1 true US20200291551A1 (en) | 2020-09-17 |
Family
ID=60037511
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US16/649,201 Pending US20200291551A1 (en) | 2017-10-06 | 2018-09-20 | Lyocell filament denim |
Country Status (12)
Country | Link |
---|---|
US (1) | US20200291551A1 (fr) |
EP (1) | EP3467171A1 (fr) |
JP (1) | JP6989079B2 (fr) |
KR (1) | KR102379050B1 (fr) |
CN (1) | CN111183249A (fr) |
AU (1) | AU2018345581B2 (fr) |
BR (1) | BR112020004280A2 (fr) |
MX (1) | MX2020003597A (fr) |
PE (1) | PE20201036A1 (fr) |
RU (1) | RU2753288C1 (fr) |
TW (1) | TWI756474B (fr) |
WO (1) | WO2019068476A1 (fr) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20210047757A1 (en) * | 2019-08-13 | 2021-02-18 | Allbirds, Inc. | Composite yarns |
US20220049384A1 (en) * | 2018-09-13 | 2022-02-17 | Lenzing Aktiengesellschaft | Fabric made of interwoven twines |
US11866858B2 (en) | 2019-04-15 | 2024-01-09 | Teijin Frontier Co., Ltd. | Textile and garment |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20220325479A1 (en) * | 2019-06-17 | 2022-10-13 | Kimberly-Clark Worldwide, Inc. | Soft and strong tissue product including regenerated cellulose fibers |
CN112981665B (zh) * | 2021-02-04 | 2023-02-03 | 鲁泰纺织股份有限公司 | 亚麻弹力面料的制备方法 |
EP4155438A1 (fr) * | 2021-09-28 | 2023-03-29 | Lenzing Aktiengesellschaft | Fibre lyocell comprenant un agent matant et utilisation pour la production d'un tissu textile |
Citations (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5120463A (en) * | 1989-10-19 | 1992-06-09 | Genencor International, Inc. | Degradation resistant detergent compositions based on cellulase enzymes |
WO2015101543A1 (fr) * | 2014-01-03 | 2015-07-09 | Lenzing Aktiengesellschaft | Fibre cellulosique |
Family Cites Families (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4246221A (en) | 1979-03-02 | 1981-01-20 | Akzona Incorporated | Process for shaped cellulose article prepared from a solution containing cellulose dissolved in a tertiary amine N-oxide solvent |
ATA53792A (de) | 1992-03-17 | 1995-02-15 | Chemiefaser Lenzing Ag | Verfahren zur herstellung cellulosischer formkörper, vorrichtung zur durchführung des verfahrens sowie verwendung einer spinnvorrichtung |
RU2043437C1 (ru) * | 1992-08-25 | 1995-09-10 | Ивановский научно-исследовательский экспериментально-конструкторский машиностроительный институт | Способ подготовки основы ткани "деним" и устройство для его осуществления |
GB9313128D0 (en) * | 1993-06-24 | 1993-08-11 | Courtaulds Fibres Ltd | Fabric treatment |
JPH1018145A (ja) * | 1996-07-02 | 1998-01-20 | Asahi Chem Ind Co Ltd | セルロースマルチフィラメント交織裏地、及びその製造方法 |
JPH1072740A (ja) * | 1996-07-02 | 1998-03-17 | Asahi Chem Ind Co Ltd | セルロースマルチフィラメント糸を用いた裏地 |
JPH1072771A (ja) * | 1996-07-05 | 1998-03-17 | Asahi Chem Ind Co Ltd | ポリエステル/セルロース混用布帛 |
JPH10251983A (ja) * | 1997-03-06 | 1998-09-22 | Ipposha Oil Ind Co Ltd | ジーンズ用繊維材料 |
JPH11335935A (ja) * | 1998-05-26 | 1999-12-07 | Kaihara Kk | デニム用混紡糸およびデニム用織編物 |
PT102650B (pt) * | 2001-07-30 | 2004-10-29 | Valfios Armazens De Fios Texte | Linha de costura, que contem o eixo de filamentos continuos de lyocell, recobertos por fibras de algodao |
GB0211916D0 (en) * | 2002-05-23 | 2002-07-03 | Tencel Ltd | Process for making a garment having recoverable stretch properties |
JP2008156760A (ja) * | 2006-12-20 | 2008-07-10 | Yoshikawa Orimono Kk | デニム |
WO2012027374A2 (fr) * | 2010-08-23 | 2012-03-01 | Dyadic International (Usa) Inc. | Glucides-hydrolases fongiques inédites |
AT513219B1 (de) * | 2012-07-23 | 2015-08-15 | Chemiefaser Lenzing Ag | Schwerentflammbares textiles Flächengebilde für Schutzbekleidung |
CN105648634A (zh) * | 2016-03-25 | 2016-06-08 | 宜兴乐威牛仔布有限公司 | 棉天丝混纺染色牛仔布 |
-
2017
- 2017-10-06 EP EP17195295.5A patent/EP3467171A1/fr not_active Withdrawn
-
2018
- 2018-09-20 AU AU2018345581A patent/AU2018345581B2/en active Active
- 2018-09-20 BR BR112020004280-3A patent/BR112020004280A2/pt active Search and Examination
- 2018-09-20 MX MX2020003597A patent/MX2020003597A/es unknown
- 2018-09-20 JP JP2020519759A patent/JP6989079B2/ja active Active
- 2018-09-20 WO PCT/EP2018/075492 patent/WO2019068476A1/fr unknown
- 2018-09-20 PE PE2020000366A patent/PE20201036A1/es unknown
- 2018-09-20 US US16/649,201 patent/US20200291551A1/en active Pending
- 2018-09-20 KR KR1020207012065A patent/KR102379050B1/ko active IP Right Grant
- 2018-09-20 RU RU2020109392A patent/RU2753288C1/ru active
- 2018-09-20 CN CN201880064912.1A patent/CN111183249A/zh active Pending
- 2018-09-28 TW TW107134534A patent/TWI756474B/zh active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5120463A (en) * | 1989-10-19 | 1992-06-09 | Genencor International, Inc. | Degradation resistant detergent compositions based on cellulase enzymes |
WO2015101543A1 (fr) * | 2014-01-03 | 2015-07-09 | Lenzing Aktiengesellschaft | Fibre cellulosique |
US20160326671A1 (en) * | 2014-01-03 | 2016-11-10 | Lenzing Aktiengesellschaft | Cellulose fiber |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20220049384A1 (en) * | 2018-09-13 | 2022-02-17 | Lenzing Aktiengesellschaft | Fabric made of interwoven twines |
US11713523B2 (en) * | 2018-09-13 | 2023-08-01 | Lenzing Aktiengesellschaft | Fabric made of interwoven twines |
US11866858B2 (en) | 2019-04-15 | 2024-01-09 | Teijin Frontier Co., Ltd. | Textile and garment |
US20210047757A1 (en) * | 2019-08-13 | 2021-02-18 | Allbirds, Inc. | Composite yarns |
Also Published As
Publication number | Publication date |
---|---|
JP2020536185A (ja) | 2020-12-10 |
TWI756474B (zh) | 2022-03-01 |
JP6989079B2 (ja) | 2022-01-05 |
EP3467171A1 (fr) | 2019-04-10 |
RU2753288C1 (ru) | 2021-08-12 |
BR112020004280A2 (pt) | 2020-09-29 |
CN111183249A (zh) | 2020-05-19 |
EP3692196A1 (fr) | 2020-08-12 |
WO2019068476A1 (fr) | 2019-04-11 |
AU2018345581B2 (en) | 2021-04-29 |
KR102379050B1 (ko) | 2022-03-24 |
TW201923185A (zh) | 2019-06-16 |
PE20201036A1 (es) | 2020-10-09 |
MX2020003597A (es) | 2020-10-01 |
KR20200057764A (ko) | 2020-05-26 |
AU2018345581A1 (en) | 2020-03-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
AU2018345581B2 (en) | Lyocell filament denim | |
KR102614523B1 (ko) | 라이오셀 필라멘트를 함유하거나 이로 이루어진 실크-라이크 직조 의복 | |
AU2018344310A1 (en) | Lyocell filament lining fabric | |
AU2018345580B2 (en) | Knitted continuous filament lyocell fabrics | |
EP3692196B1 (fr) | Denim à filaments lyocellulaires | |
BR112020004547B1 (pt) | Tecidos de liocel de filamento contínuo de malha, artigo têxtil, e uso de um fio contendo entre 10% e 100% de filamentos de liocel |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: LENZING AKTIENGESELLSCHAFT, AUSTRIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:CARLS, SUSANNE;NEUNTEUFEL, MARTIN;EICHINGER, DIETER;AND OTHERS;SIGNING DATES FROM 20200520 TO 20200624;REEL/FRAME:053302/0079 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |