US20170321143A1 - High temperature lubricant for the food industry - Google Patents
High temperature lubricant for the food industry Download PDFInfo
- Publication number
- US20170321143A1 US20170321143A1 US15/532,304 US201515532304A US2017321143A1 US 20170321143 A1 US20170321143 A1 US 20170321143A1 US 201515532304 A US201515532304 A US 201515532304A US 2017321143 A1 US2017321143 A1 US 2017321143A1
- Authority
- US
- United States
- Prior art keywords
- oil
- temperature
- grease
- group
- food
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M169/00—Lubricating compositions characterised by containing as components a mixture of at least two types of ingredient selected from base-materials, thickeners or additives, covered by the preceding groups, each of these compounds being essential
- C10M169/04—Mixtures of base-materials and additives
- C10M169/044—Mixtures of base-materials and additives the additives being a mixture of non-macromolecular and macromolecular compounds
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M169/00—Lubricating compositions characterised by containing as components a mixture of at least two types of ingredient selected from base-materials, thickeners or additives, covered by the preceding groups, each of these compounds being essential
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M111/00—Lubrication compositions characterised by the base-material being a mixture of two or more compounds covered by more than one of the main groups C10M101/00 - C10M109/00, each of these compounds being essential
- C10M111/04—Lubrication compositions characterised by the base-material being a mixture of two or more compounds covered by more than one of the main groups C10M101/00 - C10M109/00, each of these compounds being essential at least one of them being a macromolecular organic compound
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M105/00—Lubricating compositions characterised by the base-material being a non-macromolecular organic compound
- C10M105/02—Well-defined hydrocarbons
- C10M105/06—Well-defined hydrocarbons aromatic
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M105/00—Lubricating compositions characterised by the base-material being a non-macromolecular organic compound
- C10M105/08—Lubricating compositions characterised by the base-material being a non-macromolecular organic compound containing oxygen
- C10M105/32—Esters
- C10M105/36—Esters of polycarboxylic acids
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M107/00—Lubricating compositions characterised by the base-material being a macromolecular compound
- C10M107/02—Hydrocarbon polymers; Hydrocarbon polymers modified by oxidation
- C10M107/08—Hydrocarbon polymers; Hydrocarbon polymers modified by oxidation containing butene
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M109/00—Lubricating compositions characterised by the base-material being a compound of unknown or incompletely defined constitution
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M113/00—Lubricating compositions characterised by the thickening agent being an inorganic material
- C10M113/06—Metals; Alloys
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M113/00—Lubricating compositions characterised by the thickening agent being an inorganic material
- C10M113/08—Metal compounds
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M115/00—Lubricating compositions characterised by the thickener being a non-macromolecular organic compound other than a carboxylic acid or salt thereof
- C10M115/08—Lubricating compositions characterised by the thickener being a non-macromolecular organic compound other than a carboxylic acid or salt thereof containing nitrogen
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M121/00—Lubricating compositions characterised by the thickener being a compound of unknown or incompletely defined constitution
- C10M121/04—Reaction products
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M129/00—Lubricating compositions characterised by the additive being an organic non-macromolecular compound containing oxygen
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M133/00—Lubricating compositions characterised by the additive being an organic non-macromolecular compound containing nitrogen
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M141/00—Lubricating compositions characterised by the additive being a mixture of two or more compounds covered by more than one of the main groups C10M125/00 - C10M139/00, each of these compounds being essential
- C10M141/06—Lubricating compositions characterised by the additive being a mixture of two or more compounds covered by more than one of the main groups C10M125/00 - C10M139/00, each of these compounds being essential at least one of them being an organic nitrogen-containing compound
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M169/00—Lubricating compositions characterised by containing as components a mixture of at least two types of ingredient selected from base-materials, thickeners or additives, covered by the preceding groups, each of these compounds being essential
- C10M169/04—Mixtures of base-materials and additives
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
- C10M2201/04—Elements
- C10M2201/05—Metals; Alloys
- C10M2201/056—Metals; Alloys used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
- C10M2201/06—Metal compounds
- C10M2201/062—Oxides; Hydroxides; Carbonates or bicarbonates
- C10M2201/0626—Oxides; Hydroxides; Carbonates or bicarbonates used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
- C10M2201/10—Compounds containing silicon
- C10M2201/102—Silicates
- C10M2201/1026—Silicates used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
- C10M2201/10—Compounds containing silicon
- C10M2201/102—Silicates
- C10M2201/103—Clays; Mica; Zeolites
- C10M2201/1036—Clays; Mica; Zeolites used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2201/00—Inorganic compounds or elements as ingredients in lubricant compositions
- C10M2201/10—Compounds containing silicon
- C10M2201/105—Silica
- C10M2201/1056—Silica used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2203/00—Organic non-macromolecular hydrocarbon compounds and hydrocarbon fractions as ingredients in lubricant compositions
- C10M2203/06—Well-defined aromatic compounds
- C10M2203/065—Well-defined aromatic compounds used as base material
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2205/00—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions
- C10M2205/02—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions containing acyclic monomers
- C10M2205/026—Butene
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2205/00—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions
- C10M2205/02—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions containing acyclic monomers
- C10M2205/026—Butene
- C10M2205/0265—Butene used as base material
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
- C10M2207/02—Hydroxy compounds
- C10M2207/023—Hydroxy compounds having hydroxy groups bound to carbon atoms of six-membered aromatic rings
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
- C10M2207/10—Carboxylix acids; Neutral salts thereof
- C10M2207/12—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms
- C10M2207/125—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids
- C10M2207/127—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids polycarboxylic
- C10M2207/1276—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids polycarboxylic used as thickening agent
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
- C10M2207/10—Carboxylix acids; Neutral salts thereof
- C10M2207/12—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms
- C10M2207/125—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids
- C10M2207/128—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids containing hydroxy groups; Ethers thereof
- C10M2207/1285—Carboxylix acids; Neutral salts thereof having carboxyl groups bound to acyclic or cycloaliphatic carbon atoms having hydrocarbon chains of eight up to twenty-nine carbon atoms, i.e. fatty acids containing hydroxy groups; Ethers thereof used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
- C10M2207/28—Esters
- C10M2207/285—Esters of aromatic polycarboxylic acids
- C10M2207/2855—Esters of aromatic polycarboxylic acids used as base material
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2207/00—Organic non-macromolecular hydrocarbon compounds containing hydrogen, carbon and oxygen as ingredients in lubricant compositions
- C10M2207/28—Esters
- C10M2207/30—Complex esters, i.e. compounds containing at leasst three esterified carboxyl groups and derived from the combination of at least three different types of the following five types of compounds: monohydroxyl compounds, polyhydroxy xompounds, monocarboxylic acids, polycarboxylic acids or hydroxy carboxylic acids
- C10M2207/301—Complex esters, i.e. compounds containing at leasst three esterified carboxyl groups and derived from the combination of at least three different types of the following five types of compounds: monohydroxyl compounds, polyhydroxy xompounds, monocarboxylic acids, polycarboxylic acids or hydroxy carboxylic acids used as base material
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2213/00—Organic macromolecular compounds containing halogen as ingredients in lubricant compositions
- C10M2213/06—Perfluoro polymers
- C10M2213/062—Polytetrafluoroethylene [PTFE]
- C10M2213/0626—Polytetrafluoroethylene [PTFE] used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2215/00—Organic non-macromolecular compounds containing nitrogen as ingredients in lubricant compositions
- C10M2215/10—Amides of carbonic or haloformic acids
- C10M2215/102—Ureas; Semicarbazides; Allophanates
- C10M2215/1026—Ureas; Semicarbazides; Allophanates used as thickening material
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2215/00—Organic non-macromolecular compounds containing nitrogen as ingredients in lubricant compositions
- C10M2215/26—Amines
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2219/00—Organic non-macromolecular compounds containing sulfur, selenium or tellurium as ingredients in lubricant compositions
- C10M2219/04—Organic non-macromolecular compounds containing sulfur, selenium or tellurium as ingredients in lubricant compositions containing sulfur-to-oxygen bonds, i.e. sulfones, sulfoxides
- C10M2219/044—Sulfonic acids, Derivatives thereof, e.g. neutral salts
- C10M2219/0445—Sulfonic acids, Derivatives thereof, e.g. neutral salts used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2227/00—Organic non-macromolecular compounds containing atoms of elements not provided for in groups C10M2203/00, C10M2207/00, C10M2211/00, C10M2215/00, C10M2219/00 or C10M2223/00 as ingredients in lubricant compositions
- C10M2227/006—Organic non-macromolecular compounds containing atoms of elements not provided for in groups C10M2203/00, C10M2207/00, C10M2211/00, C10M2215/00, C10M2219/00 or C10M2223/00 as ingredients in lubricant compositions used as thickening agents
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
- C10M2227/00—Organic non-macromolecular compounds containing atoms of elements not provided for in groups C10M2203/00, C10M2207/00, C10M2211/00, C10M2215/00, C10M2219/00 or C10M2223/00 as ingredients in lubricant compositions
- C10M2227/09—Complexes with metals
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2010/00—Metal present as such or in compounds
- C10N2010/02—Groups 1 or 11
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2010/00—Metal present as such or in compounds
- C10N2010/04—Groups 2 or 12
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2010/00—Metal present as such or in compounds
- C10N2010/06—Groups 3 or 13
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/02—Pour-point; Viscosity index
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/04—Detergent property or dispersant property
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/06—Oiliness; Film-strength; Anti-wear; Resistance to extreme pressure
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/08—Resistance to extreme temperature
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/12—Inhibition of corrosion, e.g. anti-rust agents or anti-corrosives
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/62—Food grade properties
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
- C10N2030/76—Reduction of noise, shudder, or vibrations
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2040/00—Specified use or application for which the lubricating composition is intended
- C10N2040/08—Hydraulic fluids, e.g. brake-fluids
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2040/00—Specified use or application for which the lubricating composition is intended
- C10N2040/38—Conveyors or chain belts
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2050/00—Form in which the lubricant is applied to the material being lubricated
- C10N2050/04—Aerosols
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2050/00—Form in which the lubricant is applied to the material being lubricated
- C10N2050/10—Semi-solids; greasy
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
- C10N2060/00—Chemical after-treatment of the constituents of the lubricating composition
- C10N2060/02—Reduction, e.g. hydrogenation
-
- C10N2230/62—
-
- C10N2240/52—
-
- C10N2250/04—
-
- C10N2250/10—
Definitions
- the invention relates to a high-temperature lubricant, more particularly a high-temperature oil based on an aromatic ester, such as a trimellitic ester and mixtures of different trimellitic esters, heteroaromatics, estolides, and a fully hydrogenated or hydrogenated polyisobutylene or a mixture thereof.
- the high-temperature lubricant may, furthermore, be a high-temperature grease, if a thickener is added to the components stated above.
- the invention further relates to the use of these high-temperature lubricants for lubricating equipment used in the processing of foods.
- the lubricants are required to fulfill a great many other functions: they must cool, reduce friction, wear, and force transmission, protect against corrosion, and at the same exhibit a sealing effect.
- Base oils used for high-temperature applications are often synthetic esters, since these esters possess very good oxidative, hydrolytic, and thermal stability.
- the lubricants are required to exhibit qualities including high stability, low coefficients of friction, and high wear resistances.
- the lubricant In order to be able to ensure uniform lubrication even at high temperatures, there must be a liquid lubricating film maintained between metal parts throughout the processing operation. At the maximum processing temperature, therefore, the lubricant must undergo little evaporation, form little residue, and form cracking residues to as small an extent as possible.
- the base oils for lubricating equipment for the processing of foods are subject to particular requirements in relation to their environmental compatibility and toxicity. Fundamentally, a food-grade lubricant ought to have H1 suitability if the lubricant can come into contact, directly or indirectly, with foods, beverages, and comestibles.
- the preferred areas of application in the food industry include chains in baking ovens, and other high-temperature applications, and also ancillary transport means, more particularly trolleys and their bearings.
- H1 The grading “H1” is to be met by lubricants which are in “incidental food contact”, meaning that they are in occasional, technically unavoidable contact with foods. Intended or lasting contact, however, must be ruled out even in the case where “H1” lubricants are used.
- An “H2” classification can be achieved by lubricants which are not toxic and not carcinogenic. With the use of “H2” lubricants, nevertheless, any contact with the food must be ruled out.
- a disadvantage of the known food-grade lubricants which are used in the high-temperature sector is that they often lack satisfactory technical performance.
- the food-grade lubricants used to date do possess good oxidation resistance and an acceptable pour point, their residue behavior after full evaporation does not conform to the exacting requirements required in high-temperature applications.
- the cracking residues which develop form deposits which, after a certain time, have to be removed again.
- the operation of the plant must be stopped and the residue must be detached or the components must be replaced.
- the object of the present invention is to provide a high-temperature oil and a high-temperature grease that meet the standards of an NSF/H1 lubricant and, furthermore, have satisfactory tribological properties.
- the lubricant is to exhibit good lubricating activity at high temperature over a long time period.
- the cracking residues formed are not to exhibit “varnishing”, but are instead to be redissoluble by means of fresh oil.
- the high-temperature lubricant is to have good stability to hydrolysis, be resistant to corrosion and to wear, and to possess good oxidation resistance and low-temperature behavior adapted to the requirements.
- the food-grade high-temperature grease of the invention comprises the following components:
- additives individually or in combination, selected from the group consisting of anticorrosion additives, antioxidants, antiwear additives, UV stabilizers, inorganic or organic solid lubricants, and
- the high-temperature oil of the invention and the high-temperature grease of the invention are not only suitable for H1 classification but also display outstanding functionality.
- the high-temperature oil or high-temperature grease of the invention exhibits high thermal stability in combination with long lifetime and good lubricating properties.
- the high-temperature oil of the invention and the high-temperature grease of the invention comprise, as an ester compound, a trimellitic ester of a mixture of different trimellitic esters, the alcohol group of the ester being a linear or branched alkyl group having 8 to 16 carbon atoms.
- a trimellitic ester of a mixture of different trimellitic esters the alcohol group of the ester being a linear or branched alkyl group having 8 to 16 carbon atoms.
- the properties of the lubricant for example the viscosity, the viscosity/temperature behavior, the oxidation resistance, and residue characteristics.
- the aromatic ester comprises a sterically hindered alcohol as alcohol component, preferably an alcohol having 8 to 16 carbon atoms, more particularly 10 to 13 carbon atoms, more particularly trimellitic acid tri(iso-C 10 ) esters (1) and trimellitic acid tri(iso-C 13 ) esters (2).
- the mixing ratio of (1) to (2) is 99:1 to 1:99; with particular preference, the mixing ratio (1):(2) is 87.12.
- the high-temperature oil or grease of the invention may comprise a second oil which comprises an aromatic.
- An aromatic for the purposes of the invention is a monocyclic, bicyclic or tricylic ring system having four to fifteen carbon atoms, the monocyclic ring system being aromatic, or at least one of the rings in a bicyclic or tricyclic ring system being aromatic. Preference is given to using a bicyclic ring system, having preferably 10 carbon atoms.
- the aromatic is preferably substituted by one or more aliphatic substituents.
- the aromatic is substituted by one to four aliphatic substituents and more particularly by two or three aliphatic substituents.
- An alkyl group in accordance with the invention is a saturated aliphatic hydrocarbon group having 1 to 30, preferably 3 to 20, more preferably 4 to 17, and more particularly 6 to 15 carbon atoms.
- An alkyl group may be linear or branched and is optionally substituted by one or more of the substituents stated above.
- mixtures of differently substituted naphthalenes i.e. mixtures of naphthalenes which have a different degree of substitution and different aliphatic substituents, are particularly suitable.
- the properties, such as the viscosity, for example, of the high-temperature lubricant are particularly suitable.
- Aliphatically substituted naphthalenes are notable for outstanding dissolution properties and high thermooxidative stability.
- the viscosity, measured at 40° C., of the aliphatically substituted naphthalene is preferably 30 to 600 mm 2 /s, more preferably 30 to 300 mm 2 /s.
- estolides can also be used as component a).
- Preferred viscosities measured at 40° C. are between 30 and 500 mm 2 /sec. Particularly preferred are viscosities from 30 to 140 mm 2 /sec.
- estolides are meant ester compounds which are prepared with acidic or enzymatic catalysts from fatty acids, preferably oleic acid, or dicarboxylic acids.
- the acid function attacks the double bond of an adjacent fatty acid molecule, to form an ester compound of higher molecular mass.
- the terminal acid group is then conventionally esterified with an alcohol, preferably 2-ethylhexanol, and the remaining double bonds are subsequently hydrogenated or esterified with carboxylic acid-acetic acid for example.
- Other alcohols such as isoamyl alcohol or Guerbet alcohols, for example, are likewise conceivable for the esterification of the terminal acid group.
- estolides may also be synthesized via a condensation of hydroxycarboxylic acids, examples being derivatives of oleic acid or of stearic acid.
- the chain lengths of the hydroxycarboxylic acids or unsaturated acids used may range from C 6 to C 54 .
- the acids may contain further functional groups, e.g., amines, ethers, sulfur-containing groups. Also conceivable, furthermore, is esterification with alpha-olefins or ⁇ -farnesene.
- the high-temperature oil or grease of the invention further comprises a polyisobutylene.
- a polyisobutylene Through appropriate selection of the polyisobutylene, especially with regard to degree of hydrogenation and molecular weight, it is possible to influence the properties of the oil and grease of the invention in a desired way—for example, its kinematic viscosity.
- the polyisobutylene may be used in hydrogenated or fully hydrogenated form, and a mixture of hydrogenated and fully hydrogenated polyisobutylene may also be used. Preference is given to using fully hydrogenated polyisobutylenes.
- the polyisobutylene is present in an amount of 6 to 45 wt % in the composition, with preferably 10 to 45 wt % and more particularly 15 to 45 wt % being used.
- the polyisobutylene has a number-average molecular weight of 115 to 10 000 g/mol, preferably of 160 to 5000 g/mol.
- the high-temperature oil or grease of the invention further comprises from 0.1 to 5 wt % of additives, which are used individually or in combination and are selected from the group consisting of anticorrosion additives, antioxidants, antiwear additives, UV stabilizers, inorganic or organic solid lubricants.
- the high-temperature grease of the invention further comprises a thickener.
- the thickener in the high-temperature grease of the invention in the lubricant composition is either a reaction product of a diisocyanate, preferably 2,4-diisocyanatotoluene, 2,6-diisocyanatotoluene, 4,4′-diisocyanatodiphenylmethane, 2,4′-diisocyanatophenylmethane, 4,4′-diisocyanato-biphenyl, 4,4′-diisocyanato-3,3′-dimethylphenyl, 4,4′-diisocynato-3,3′-dimethylphenylmethane, which may be used individually or in combination, with an amine of the general formula R′ 2 —N—R, or with a diamine of the general formula R′ 2 —N—R—NR′ 2 , where R is an aryl, al
- Al complex soaps simple metal soaps of the elements of the first and second main groups of the Periodic Table, metal complex soaps of the elements of the first and second main groups of the Periodic Table, bentonites, sulfonates, silicates, Aerosil, polyimides or PTFE, or a mixture of the aforesaid thickeners.
- antioxidants may reduce or even prevent oxidation of the oil or grease of the invention, especially in the course of its use. In the event of oxidation, unwanted free radicals may form and, consequently, decomposition reactions may occur to an increased extent in the high-temperature lubricant.
- the addition of antioxidants stabilizes the high-temperature oil or grease.
- Antioxidants particularly suitable in accordance with the invention are the following food-grade compounds: Diaromatic amines, phenolic resins, thiophenolic resins, phosphites, butylated hydroxytoluene, butylated hydroxyanisole, phenyl-alpha-naphthylamine, phenyl-beta-naphthylamine, octylated/butylated diphenylamine, di-alpha-tocopherol, di-tert-butylphenyl, benzenepropanoic acid and mixtures of these components.
- IRGANOX® 1010 (benzenepropanoic acid, 3,5-bis(1,1-dimethylethyl)-4-hydroxy-2,2-bis[[3-[3,5-bis(1,1-dimethylethyl)-4-hydroxyphenyl]-1-oxopropoxy]methyl]-1,3-propanediyl ester;
- IRGANOX® L06 alkylated phenyl-alpha-naphthylamine or N-phenyl-ar-(1,1,3,3-tetramethylbutyl)-1-naphthalenamine;
- IRGANOX® L01 dioctylated diphenylamine);
- IRGANOX® L57 mixture of alkylated diphenylamines);
- IRGANOX® L150 (mixture of aminic and phenolic antioxidants with high molecular weight);
- IRGANOX® L64 mixture of mono- and dialkyl-butyl/octyl-diphenylamine);
- IRGANOX® 1035 (mixture consisting of thiodiethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate);
- IRGANOX® L101 mixture consisting of tetrakis[methylene-3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionato]methane
- IRGANOX® L109 benzenepropanoic acid, 3,5-bis(1,1-dimethyl)-4-hydroxy-1,6-hexanediyl ester
- IRGANOX® L115 (benzenepropanoic acid, 3,5-bis(1,1-dimethylethyl)-4-hydroxythiodi-2,1-ethanediyl ester);
- IRGANOX® E201 liquid DL-alpha-tocopherol, 2H-1-benzopyran-6-ol, 3,4-dihydro-2,5,7,8-tetramethyl-2-(4,8,12-trimethyltridecyl);
- IRGAFOS® 168 (mixture containing tris(2,4-di-tert-butylphenyl) phosphate);
- ADDITIN® RC7130 N-phenyl-1-naphthylamine
- Na-LUBE® A0142 liquid, diphenylamine-based antioxidant
- VANLUBE® 961 (mixture of octylated and butylated diphenylamine or benzenamine, N-phenyl, reaction product of 2,4-tri
- the high-temperature oil or grease may, furthermore, comprise anticorrosion additives, metal deactivators or ion complexing agents.
- anticorrosion additives metal deactivators or ion complexing agents.
- These include triazoles, imidazolines, N-methylglycine (sarcosine), benzotriazole derivatives, N,N-bis(2-ethylhexyl)-ar-methyl-1H-benzotriazole-1-methanamine; n-methyl-N(1-oxo-9-octadecenyl)glycine, a mixture of phosphoric acid and mono- and diisooctyl esters reacted with (C 11-14 )-alkylamines, mixture of phosphoric acid and mono- and diisooctyl esters reacted with tert-alkylamine and primary (C 12-14 )-amines, dodecanoic acid, triphenyl phosphorothionate, and amine phosphate
- IRGAMET® 39 IRGACOR® DSS G, Amine O; SARKOSY® O (Ciba), COBRATEC® 122, CUVAN® 303, VANLUBE® 9123, CI-426, CI-426EP, CI429, and CI-498.
- antiwear additives are amines, amine phosphates, phosphates, thiophosphates, phosphorothionates, and mixtures of these components.
- the commercially available antiwear additives include IRGALUBE® TPPT, IRGALUBE® 232, IRGALUBE® 349, IRGALUBE® 211 and ADDITIN® RC3760 Liq 3960, FIRC-SHUN®FG 1505 and FG 1506, NA-LUBE® KR-015FG, LUBEBOND®, FLUORO® FG, SYNALOX® 40-D, ACHESON® FGA 1820 and ACHESON® FGA 1810.
- the oil or grease may further comprise solid lubricants with food suitability such as PTFE, BN, Na pyrophosphate, Zn oxide, Mg oxide, Zn pyrophosphate, Na thiosulfate, Mg carbonate, Ca carbonate, Ca stearate, Zn sulfide, or a mixture thereof.
- solid lubricants with food suitability such as PTFE, BN, Na pyrophosphate, Zn oxide, Mg oxide, Zn pyrophosphate, Na thiosulfate, Mg carbonate, Ca carbonate, Ca stearate, Zn sulfide, or a mixture thereof.
- the high-temperature oil or grease of the invention may comprise an oil preferably selected from the group consisting of mineral oil, aliphatic carboxylic and dicarboxylic esters, fatty acid triglycerides, and/or poly-alpha-olefins.
- the high-temperature oil or grease of the invention comprises an estolide, the main constituents of the estolide preferably being obtained by chemical or enzymatic processes on the basis of natural oils from the group of sunflower oil, rapeseed oil, castor oil, linseed oil, corn oil, safflower oil, soybean oil, linseed oil, groundnut oil, “Lesqueralle” oil, palm oil, olive oil, or mixtures of the aforesaid oils.
- the high-temperature oil or grease of the invention on the basis of its physical and chemical properties can be used outstandingly to lubricate equipment for the processing of foods.
- it may be employed even at high service temperatures up to 260° C., preferably at temperatures of 150 to 250° C., with chains in baking ovens being an example.
- the invention further relates to a method for producing the high-temperature oil or grease described above, wherein the base oils and the additives are mixed with one another.
- trimellitic esters Two trimellitic esters are charged to a stirred vessel. At 100° C., with stirring, the polyisobutylene and optionally a further oil are added. The mixture is subsequently stirred for 1 hour in order to give a homogeneous mixture. The antiwear agents and the antioxidant are added to the vessel with stirring at 60° C. After about 1 hour, the completed oil can be dispensed into the intended containers.
- Table 1 shows the compositions of the high-temperature oils and the redissolubility of the oil residue after complete evaporation of the oil, as a function of the amount of polyisobutylene added.
- examples to 10 below show the outstanding properties of the food-grade high-temperature oil of the invention in relation to dissolubility when different components a) are used as oil.
- Table 5 provides an exemplary description below of the food-grade high-temperature greases of the invention.
- the samples were conditioned at 250° C. for 72 hours. The residue was redissolved using the respective base oil of the grease specimen. In all examples the redissolubility was good.
- the thickeners used in examples 11 to 16 are complex Li (Ex. 11 and 12), complex Al (Ex. 13), bentonite (Ex. 14), simple Ca (Ex. 15), simple Li (Ex. 16), and urea (Ex. 17).
- the redissolubility of the oil residue after full evaporation at two different temperatures (220° C./120 h) and (250° C./72 h) was investigated as a function of the mixing ratio of the two trimellitic esters (1) and (2).
- the concentration of the fully hydrogenated PIB was kept constant at 25 wt %. It was found, surprisingly, that for both temperatures the redissolubility is dependent on the mixing ratio of the two trimellitic esters.
- the dissolubility of the residues is dependent not only on the degree of hydrogenation of the polyisobutylene but also on the mixing ratio of the two esters. Both esters must be used in combination in order to ensure the H1 capacity of the high-temperature oil.
- the mixing ratios are freely selectable, with the preferred ranges beginning from a 1:1 mixture.
- the particularly preferred ratio is 87.12 (iso-C 10 /iso-C 13 ).
- the above-described food-grade high-temperature oils and high-temperature greases can also be used for lubricating equipment subject to limitations similar to those relating to the requirements imposed on the lubricants. Included here are the cosmetic and pharmaceutical industries and also the animal feed industry.
- the high-temperature lubricants of the invention can be used for the lubrication of equipment in food processing, as hydraulic oils for the food industry, for transport chains and control chains in the food industry, and also for devices for the processing of cereal, flour, and animal feed, and also for baking ovens.
Landscapes
- Chemical & Material Sciences (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Inorganic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Emergency Medicine (AREA)
- Metallurgy (AREA)
- Lubricants (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102014018719.5A DE102014018719A1 (de) | 2014-12-17 | 2014-12-17 | Hochtemperaturschmierstoff für die Lebensmittelindustrie |
DE102014018719.5 | 2014-12-17 | ||
PCT/EP2015/002323 WO2016096075A2 (de) | 2014-12-17 | 2015-11-19 | Hochtemperaturschmierstoff für die lebensmittelindustrie |
Publications (1)
Publication Number | Publication Date |
---|---|
US20170321143A1 true US20170321143A1 (en) | 2017-11-09 |
Family
ID=54771065
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US15/532,304 Abandoned US20170321143A1 (en) | 2014-12-17 | 2015-11-19 | High temperature lubricant for the food industry |
Country Status (12)
Country | Link |
---|---|
US (1) | US20170321143A1 (zh) |
EP (3) | EP3375851A1 (zh) |
JP (1) | JP6400211B2 (zh) |
KR (1) | KR101931511B1 (zh) |
CN (1) | CN107001968B (zh) |
BR (1) | BR112017012562B1 (zh) |
DE (1) | DE102014018719A1 (zh) |
DK (1) | DK3375850T3 (zh) |
ES (1) | ES2901414T3 (zh) |
MX (1) | MX2017007681A (zh) |
PL (1) | PL3375850T3 (zh) |
WO (1) | WO2016096075A2 (zh) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11525101B2 (en) | 2016-12-12 | 2022-12-13 | Total Marketing Services | Lubricant composition for industrial gearing coming into contact with food |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102016011022A1 (de) * | 2015-09-17 | 2017-03-23 | Klüber Lubrication München Se & Co. Kg | Biologisch abbaubare Schmierstoffzusammensetzungen mit hoher Elastomerverträglichkeit zur Verwendung im Marinebereich, speziell im Bereich der Stevenrohrschmierung |
JP7187104B2 (ja) * | 2017-05-22 | 2022-12-12 | コスモ石油ルブリカンツ株式会社 | 食品機械用グリース組成物 |
WO2019204141A1 (en) * | 2018-04-18 | 2019-10-24 | The Lubrizol Corporation | Lubricant with high pyrophosphate level |
CN108753426B (zh) * | 2018-07-10 | 2021-05-28 | 河南倍佳润滑科技股份有限公司 | 一种特高温食品级合成链条油组合物 |
JP7255854B2 (ja) * | 2019-03-29 | 2023-04-11 | 住鉱潤滑剤株式会社 | 食品機械用潤滑剤組成物 |
DE102020112993A1 (de) * | 2020-05-13 | 2021-11-18 | Klüber Lubrication München Se & Co. Kg | Lithiumkomplexhybridfett |
JP7401717B2 (ja) | 2021-10-25 | 2023-12-19 | ミネベアミツミ株式会社 | グリース組成物、ピボットアッシー軸受および該軸受を備えた軸受装置 |
WO2023094321A1 (de) * | 2021-11-24 | 2023-06-01 | Klueber Lubrication Muenchen Se & Co. Kg | Hochtemperaturschmierfett |
WO2023179897A1 (de) * | 2022-03-25 | 2023-09-28 | Klueber Lubrication Muenchen Se & Co. Kg | Verwendung einer schmierstoffzusammensetzung zum schmieren von arbeitsgeräten |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4601840A (en) * | 1985-06-21 | 1986-07-22 | National Distillers And Chemical Corp. | Mist lubrication process |
US20020142920A1 (en) * | 2000-11-06 | 2002-10-03 | Nsk Ltd. | Lubricating grease compositon and rolling apparatus |
US6465400B1 (en) * | 1998-12-25 | 2002-10-15 | Idemitsu Kosan Co., Ltd. | Lubricating oil composition for high-temperature use |
US20030027731A1 (en) * | 2001-06-28 | 2003-02-06 | Takayuki Kawamura | Heat-resistant, high-speed, high-load rolling bearing and grease composition |
Family Cites Families (26)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE636108A (zh) * | 1961-08-18 | 1900-01-01 | ||
US4075112A (en) * | 1975-01-28 | 1978-02-21 | Labofina S.A. | Grease composition |
GB8408017D0 (en) * | 1984-03-28 | 1984-05-10 | Bp Chem Int Ltd | Oil-based lubricant compositions |
US4604491A (en) * | 1984-11-26 | 1986-08-05 | Koppers Company, Inc. | Synthetic oils |
AU5874786A (en) * | 1985-06-21 | 1986-12-24 | National Distillers And Chemical Corporation | Process of mist lubrication using synthetic esters |
EP0645444A3 (en) * | 1993-09-27 | 1995-05-24 | Texaco Development Corp | Lubricant with overbased detergents made from linear alkyl aromatics. |
JPH1053786A (ja) * | 1996-06-03 | 1998-02-24 | Nkk Corp | 合成潤滑油組成物 |
CZ6799A3 (cs) * | 1996-07-12 | 1999-08-11 | Castrol Limited | Mazivo obsahující ester a jeho použití |
DE19730318C2 (de) * | 1997-07-15 | 2002-04-04 | Klueber Lubrication | Schmierfettzusammensetzung, Verfahren zur Herstellung derselben sowie deren Verwendung |
US6316649B1 (en) * | 1998-11-13 | 2001-11-13 | The United States Of America As Represented By The Secretary Of Agriculture | Biodegradable oleic estolide ester having saturated fatty acid end group useful as lubricant base stock |
JP2003201492A (ja) * | 2000-11-06 | 2003-07-18 | Nsk Ltd | グリース組成物及び転動装置 |
WO2006086752A1 (en) * | 2005-02-10 | 2006-08-17 | Inolex Investment Corporation | High temperature lubricant compositions and methods of making the same |
BRPI0610628A8 (pt) * | 2005-04-26 | 2016-03-08 | Renewable Lubricants Inc | lubrificante, processo para aprimorar a lubrificação de equipamento |
US20070078066A1 (en) * | 2005-10-03 | 2007-04-05 | Milner Jeffrey L | Lubricant formulations containing extreme pressure agents |
DE102006043747A1 (de) * | 2006-09-13 | 2008-03-27 | Addinol Lube Oil Gmbh | Hochtemperaturschmierstoff für Ketten |
US8258088B2 (en) * | 2007-06-20 | 2012-09-04 | KLüBER LUBRICATION MüNCHEN KG | Lubricating grease composition |
CN102089415A (zh) * | 2008-07-14 | 2011-06-08 | 科聚亚公司 | 用于稳定润滑剂组合物的液态添加剂 |
JP5534386B2 (ja) * | 2009-02-13 | 2014-06-25 | 協同油脂株式会社 | 消音用グリース組成物 |
DE102011102540B4 (de) * | 2011-05-26 | 2013-12-12 | KLüBER LUBRICATION MüNCHEN KG | Hochtemperaturöl |
MY191912A (en) * | 2011-06-17 | 2022-07-18 | Biosynthetic Technologies Llc | Estolide compositions exhibiting high oxidative stability |
JP2014517123A (ja) * | 2011-06-17 | 2014-07-17 | バイオシンセティック テクノロジーズ,リミティド ライアビリティ カンパニー | エストリド基油を含むグリース組成物 |
DE102012015648A1 (de) * | 2012-04-16 | 2013-10-17 | KLüBER LUBRICATION MüNCHEN KG | Hochtemperaturfett |
RU2014114597A (ru) * | 2011-09-15 | 2015-10-20 | Клюбер Лубрикацион Мюнхен Се Унд Ко. Кг | Высокотемпературный смазочный материал |
US8980361B2 (en) * | 2012-12-21 | 2015-03-17 | Biosynthetic Technologies, Llc | Cooking oils and food products comprising estolides |
WO2014142157A1 (ja) * | 2013-03-14 | 2014-09-18 | 出光興産株式会社 | 高温用潤滑油組成物 |
CN103343032B (zh) * | 2013-07-25 | 2015-09-09 | 中国石油化工股份有限公司 | 一种润滑脂及其制备方法 |
-
2014
- 2014-12-17 DE DE102014018719.5A patent/DE102014018719A1/de not_active Withdrawn
-
2015
- 2015-11-19 BR BR112017012562-5A patent/BR112017012562B1/pt active IP Right Grant
- 2015-11-19 PL PL18000086T patent/PL3375850T3/pl unknown
- 2015-11-19 JP JP2017533030A patent/JP6400211B2/ja active Active
- 2015-11-19 MX MX2017007681A patent/MX2017007681A/es unknown
- 2015-11-19 EP EP18000087.9A patent/EP3375851A1/de not_active Withdrawn
- 2015-11-19 KR KR1020177016304A patent/KR101931511B1/ko active IP Right Grant
- 2015-11-19 CN CN201580068966.1A patent/CN107001968B/zh active Active
- 2015-11-19 ES ES18000086T patent/ES2901414T3/es active Active
- 2015-11-19 DK DK18000086.1T patent/DK3375850T3/da active
- 2015-11-19 US US15/532,304 patent/US20170321143A1/en not_active Abandoned
- 2015-11-19 EP EP18000086.1A patent/EP3375850B1/de active Active
- 2015-11-19 WO PCT/EP2015/002323 patent/WO2016096075A2/de active Application Filing
- 2015-11-19 EP EP15804064.2A patent/EP3234080A2/de not_active Withdrawn
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4601840A (en) * | 1985-06-21 | 1986-07-22 | National Distillers And Chemical Corp. | Mist lubrication process |
US6465400B1 (en) * | 1998-12-25 | 2002-10-15 | Idemitsu Kosan Co., Ltd. | Lubricating oil composition for high-temperature use |
US20020142920A1 (en) * | 2000-11-06 | 2002-10-03 | Nsk Ltd. | Lubricating grease compositon and rolling apparatus |
US20030027731A1 (en) * | 2001-06-28 | 2003-02-06 | Takayuki Kawamura | Heat-resistant, high-speed, high-load rolling bearing and grease composition |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11525101B2 (en) | 2016-12-12 | 2022-12-13 | Total Marketing Services | Lubricant composition for industrial gearing coming into contact with food |
Also Published As
Publication number | Publication date |
---|---|
MX2017007681A (es) | 2018-01-23 |
KR20170083612A (ko) | 2017-07-18 |
KR101931511B1 (ko) | 2019-03-13 |
EP3234080A2 (de) | 2017-10-25 |
BR112017012562B1 (pt) | 2022-04-05 |
JP2017538840A (ja) | 2017-12-28 |
DE102014018719A1 (de) | 2016-06-23 |
DK3375850T3 (da) | 2022-01-17 |
EP3375850B1 (de) | 2021-10-27 |
CN107001968B (zh) | 2020-07-17 |
PL3375850T3 (pl) | 2022-01-31 |
WO2016096075A2 (de) | 2016-06-23 |
JP6400211B2 (ja) | 2018-10-03 |
BR112017012562A2 (pt) | 2018-01-02 |
CN107001968A (zh) | 2017-08-01 |
EP3375850A1 (de) | 2018-09-19 |
WO2016096075A3 (de) | 2016-09-01 |
EP3375851A1 (de) | 2018-09-19 |
ES2901414T3 (es) | 2022-03-22 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20170321143A1 (en) | High temperature lubricant for the food industry | |
CN101133143B (zh) | 改进工业流体的氧化稳定性的方法 | |
US8895490B2 (en) | Food grade compressor lubricant | |
US20170327760A1 (en) | High temperature lubricant | |
AU2004245977B2 (en) | Improved food-grade-lubricant | |
US11117854B2 (en) | Ester compounds, method for the preparation thereof and use thereof | |
KR102155674B1 (ko) | 윤활유 | |
ZA200509605B (en) | Improved food-grade-lubricant | |
JPWO2015045816A1 (ja) | トラクションドライブ変速機用潤滑油組成物 | |
CN109666529B (zh) | 一种以合成油为主的食品级真空泵油组合物 | |
US11781086B2 (en) | Lubricating oils and greases | |
JP2015140415A (ja) | グリース組成物 | |
CN108165352A (zh) | 一种含有生物基、无硫、无磷有机锡化合物的润滑脂组合物 | |
US11248188B2 (en) | Lubricant composition | |
CN106467805A (zh) | 一种用于抗磨液压油添加剂 | |
CN106467793A (zh) | 一种用于抗磨液压油复合剂 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: KLUBER LUBRICATION MUNCHEN SE & CO. KG, GERMANY Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:EGERSDORFER, KARL;KILTHAU, THOMAS;SCHMIDT-AMELUNXEN, MARTIN;SIGNING DATES FROM 20170523 TO 20170531;REEL/FRAME:043212/0462 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |
|
STCV | Information on status: appeal procedure |
Free format text: NOTICE OF APPEAL FILED |
|
STCV | Information on status: appeal procedure |
Free format text: APPEAL BRIEF (OR SUPPLEMENTAL BRIEF) ENTERED AND FORWARDED TO EXAMINER |
|
STCV | Information on status: appeal procedure |
Free format text: EXAMINER'S ANSWER TO APPEAL BRIEF MAILED |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |