US20160030728A1 - Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids - Google Patents

Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids Download PDF

Info

Publication number
US20160030728A1
US20160030728A1 US14/448,432 US201414448432A US2016030728A1 US 20160030728 A1 US20160030728 A1 US 20160030728A1 US 201414448432 A US201414448432 A US 201414448432A US 2016030728 A1 US2016030728 A1 US 2016030728A1
Authority
US
United States
Prior art keywords
tube
tubular
pbe
wall
solvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/448,432
Other languages
English (en)
Inventor
Philip D. Bourgeois
Joseph E. Olsavsky
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tekni Plex Inc
Original Assignee
Tekni Plex Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tekni Plex Inc filed Critical Tekni Plex Inc
Priority to US14/448,432 priority Critical patent/US20160030728A1/en
Assigned to TEKNI-PLEX, INC. reassignment TEKNI-PLEX, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BOURGEOIS, PHILIP D., OLSAVSKY, JOSEPH E.
Assigned to CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, AS COLLATERAL AGENT reassignment CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, AS COLLATERAL AGENT FIRST LIEN PATENT SECURITY AGREEMENT Assignors: TEKNI-PLEX, INC.
Assigned to BANK OF AMERICA, N.A., AS COLLATERAL AGENT reassignment BANK OF AMERICA, N.A., AS COLLATERAL AGENT ABL PATENT SECURITY AGREEMENT Assignors: TEKNI-PLEX, INC.
Assigned to CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, AS COLLATERAL AGENT reassignment CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, AS COLLATERAL AGENT SECOND LIEN PATENT SECURITY AGREEMENT Assignors: TEKNI-PLEX, INC.
Priority to CA2956907A priority patent/CA2956907C/en
Priority to CN201580046314.8A priority patent/CN106795343B/zh
Priority to JP2017505503A priority patent/JP6806667B2/ja
Priority to MX2017001434A priority patent/MX2017001434A/es
Priority to PCT/US2015/039641 priority patent/WO2016018577A1/en
Priority to BR112017002034-3A priority patent/BR112017002034B1/pt
Priority to EP15747620.1A priority patent/EP3191290B1/en
Priority to CR20170063A priority patent/CR20170063A/es
Publication of US20160030728A1 publication Critical patent/US20160030728A1/en
Assigned to TRI-SEAL HOLDINGS, INC., PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., TEKNI-PLEX, INC., NATVAR HOLDINGS, LLC reassignment TRI-SEAL HOLDINGS, INC. RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH
Assigned to TRI-SEAL HOLDINGS, INC., PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., TEKNI-PLEX, INC., NATVAR HOLDINGS, LLC reassignment TRI-SEAL HOLDINGS, INC. RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH
Assigned to TRI-SEAL HOLDINGS, INC., PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., TEKNI-PLEX, INC., NATVAR HOLDINGS, LLC reassignment TRI-SEAL HOLDINGS, INC. RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: BANK OF AMERICA, N.A.
Assigned to BMO HARRIS BANK, N.A. reassignment BMO HARRIS BANK, N.A. SECURITY INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: NATVAR HOLDINGS, LLC, PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., TEKNI-PLEX, INC., TRI-SEAL HOLDINGS, INC.
Assigned to CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH reassignment CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH SECURITY INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: NATVAR HOLDINGS, LLC, PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., TEKNI-PLEX, INC., TRI-SEAL HOLDINGS, INC.
Priority to US15/866,891 priority patent/US10716927B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • G—PHYSICS
    • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
    • G21G—CONVERSION OF CHEMICAL ELEMENTS; RADIOACTIVE SOURCES
    • G21G1/00—Arrangements for converting chemical elements by electromagnetic radiation, corpuscular radiation or particle bombardment, e.g. producing radioactive isotopes
    • G21G1/04—Arrangements for converting chemical elements by electromagnetic radiation, corpuscular radiation or particle bombardment, e.g. producing radioactive isotopes outside nuclear reactors or particle accelerators
    • G21G1/06—Arrangements for converting chemical elements by electromagnetic radiation, corpuscular radiation or particle bombardment, e.g. producing radioactive isotopes outside nuclear reactors or particle accelerators by neutron irradiation
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61M—DEVICES FOR INTRODUCING MEDIA INTO, OR ONTO, THE BODY; DEVICES FOR TRANSDUCING BODY MEDIA OR FOR TAKING MEDIA FROM THE BODY; DEVICES FOR PRODUCING OR ENDING SLEEP OR STUPOR
    • A61M39/00—Tubes, tube connectors, tube couplings, valves, access sites or the like, specially adapted for medical use
    • A61M39/08—Tubes; Storage means specially adapted therefor
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61M—DEVICES FOR INTRODUCING MEDIA INTO, OR ONTO, THE BODY; DEVICES FOR TRANSDUCING BODY MEDIA OR FOR TAKING MEDIA FROM THE BODY; DEVICES FOR PRODUCING OR ENDING SLEEP OR STUPOR
    • A61M5/00—Devices for bringing media into the body in a subcutaneous, intra-vascular or intramuscular way; Accessories therefor, e.g. filling or cleaning devices, arm-rests
    • A61M5/14—Infusion devices, e.g. infusing by gravity; Blood infusion; Accessories therefor
    • A61M5/158—Needles for infusions; Accessories therefor, e.g. for inserting infusion needles, or for holding them on the body
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
    • B29C65/48—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor using adhesives, i.e. using supplementary joining material; solvent bonding
    • B29C65/4805—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor using adhesives, i.e. using supplementary joining material; solvent bonding characterised by the type of adhesives
    • B29C65/481—Non-reactive adhesives, e.g. physically hardening adhesives
    • B29C65/482—Drying adhesives, e.g. solvent based adhesives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
    • B29C65/48—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor using adhesives, i.e. using supplementary joining material; solvent bonding
    • B29C65/4895—Solvent bonding, i.e. the surfaces of the parts to be joined being treated with solvents, swelling or softening agents, without adhesives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/01—General aspects dealing with the joint area or with the area to be joined
    • B29C66/05—Particular design of joint configurations
    • B29C66/10—Particular design of joint configurations particular design of the joint cross-sections
    • B29C66/12—Joint cross-sections combining only two joint-segments; Tongue and groove joints; Tenon and mortise joints; Stepped joint cross-sections
    • B29C66/122—Joint cross-sections combining only two joint-segments, i.e. one of the parts to be joined comprising only two joint-segments in the joint cross-section
    • B29C66/1222—Joint cross-sections combining only two joint-segments, i.e. one of the parts to be joined comprising only two joint-segments in the joint cross-section comprising at least a lapped joint-segment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/01—General aspects dealing with the joint area or with the area to be joined
    • B29C66/05—Particular design of joint configurations
    • B29C66/10—Particular design of joint configurations particular design of the joint cross-sections
    • B29C66/12—Joint cross-sections combining only two joint-segments; Tongue and groove joints; Tenon and mortise joints; Stepped joint cross-sections
    • B29C66/122—Joint cross-sections combining only two joint-segments, i.e. one of the parts to be joined comprising only two joint-segments in the joint cross-section
    • B29C66/1224—Joint cross-sections combining only two joint-segments, i.e. one of the parts to be joined comprising only two joint-segments in the joint cross-section comprising at least a butt joint-segment
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/50—General aspects of joining tubular articles; General aspects of joining long products, i.e. bars or profiled elements; General aspects of joining single elements to tubular articles, hollow articles or bars; General aspects of joining several hollow-preforms to form hollow or tubular articles
    • B29C66/51—Joining tubular articles, profiled elements or bars; Joining single elements to tubular articles, hollow articles or bars; Joining several hollow-preforms to form hollow or tubular articles
    • B29C66/53—Joining single elements to tubular articles, hollow articles or bars
    • B29C66/534—Joining single elements to open ends of tubular or hollow articles or to the ends of bars
    • B29C66/5344—Joining single elements to open ends of tubular or hollow articles or to the ends of bars said single elements being substantially annular, i.e. of finite length, e.g. joining flanges to tube ends
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
    • B29C66/71—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the composition of the plastics material of the parts to be joined
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
    • B29C66/71—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the composition of the plastics material of the parts to be joined
    • B29C66/712—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the composition of the plastics material of the parts to be joined the composition of one of the parts to be joined being different from the composition of the other part
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
    • B29C66/72—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the structure of the material of the parts to be joined
    • B29C66/723—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the structure of the material of the parts to be joined being multi-layered
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
    • C08J5/12—Bonding of a preformed macromolecular material to the same or other solid material such as metal, glass, leather, e.g. using adhesives
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61M—DEVICES FOR INTRODUCING MEDIA INTO, OR ONTO, THE BODY; DEVICES FOR TRANSDUCING BODY MEDIA OR FOR TAKING MEDIA FROM THE BODY; DEVICES FOR PRODUCING OR ENDING SLEEP OR STUPOR
    • A61M2207/00—Methods of manufacture, assembly or production
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2219/00—Chemical, physical or physico-chemical processes in general; Their relevant apparatus
    • B01J2219/00049—Controlling or regulating processes
    • B01J2219/00051—Controlling the temperature
    • B01J2219/00121—Controlling the temperature by direct heating or cooling
    • B01J2219/00123—Controlling the temperature by direct heating or cooling adding a temperature modifying medium to the reactants
    • B01J2219/00126—Cryogenic coolants
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
    • B29C65/56—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor using mechanical means or mechanical connections, e.g. form-fits
    • B29C65/565—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor using mechanical means or mechanical connections, e.g. form-fits involving interference fits, e.g. force-fits or press-fits
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C65/00—Joining or sealing of preformed parts, e.g. welding of plastics materials; Apparatus therefor
    • B29C65/82—Testing the joint
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
    • B29C66/00—General aspects of processes or apparatus for joining preformed parts
    • B29C66/70—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material
    • B29C66/73—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset
    • B29C66/737—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the state of the material of the parts to be joined
    • B29C66/7377—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the state of the material of the parts to be joined amorphous, semi-crystalline or crystalline
    • B29C66/73773—General aspects of processes or apparatus for joining preformed parts characterised by the composition, physical properties or the structure of the material of the parts to be joined; Joining with non-plastics material characterised by the intensive physical properties of the material of the parts to be joined, by the optical properties of the material of the parts to be joined, by the extensive physical properties of the parts to be joined, by the state of the material of the parts to be joined or by the material of the parts to be joined being a thermoplastic or a thermoset characterised by the state of the material of the parts to be joined amorphous, semi-crystalline or crystalline the to-be-joined area of at least one of the parts to be joined being semi-crystalline
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2023/00—Use of polyalkenes or derivatives thereof as moulding material
    • B29K2023/10—Polymers of propylene
    • B29K2023/12—PP, i.e. polypropylene
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29K—INDEXING SCHEME ASSOCIATED WITH SUBCLASSES B29B, B29C OR B29D, RELATING TO MOULDING MATERIALS OR TO MATERIALS FOR MOULDS, REINFORCEMENTS, FILLERS OR PREFORMED PARTS, e.g. INSERTS
    • B29K2105/00—Condition, form or state of moulded material or of the material to be shaped
    • B29K2105/0085—Copolymers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
    • B29L—INDEXING SCHEME ASSOCIATED WITH SUBCLASS B29C, RELATING TO PARTICULAR ARTICLES
    • B29L2023/00—Tubular articles
    • B29L2023/005—Hoses, i.e. flexible
    • B29L2023/007—Medical tubes other than catheters
    • G—PHYSICS
    • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
    • G21G—CONVERSION OF CHEMICAL ELEMENTS; RADIOACTIVE SOURCES
    • G21G4/00—Radioactive sources
    • G21G4/02—Neutron sources
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05H—PLASMA TECHNIQUE; PRODUCTION OF ACCELERATED ELECTRICALLY-CHARGED PARTICLES OR OF NEUTRONS; PRODUCTION OR ACCELERATION OF NEUTRAL MOLECULAR OR ATOMIC BEAMS
    • H05H2277/00—Applications of particle accelerators
    • H05H2277/10—Medical devices
    • H05H2277/11—Radiotherapy
    • H05H2277/116—Isotope production
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05H—PLASMA TECHNIQUE; PRODUCTION OF ACCELERATED ELECTRICALLY-CHARGED PARTICLES OR OF NEUTRONS; PRODUCTION OR ACCELERATION OF NEUTRAL MOLECULAR OR ATOMIC BEAMS
    • H05H2277/00—Applications of particle accelerators
    • H05H2277/13—Nuclear physics, e.g. spallation sources, accelerator driven systems, search or generation of exotic elements
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05H—PLASMA TECHNIQUE; PRODUCTION OF ACCELERATED ELECTRICALLY-CHARGED PARTICLES OR OF NEUTRONS; PRODUCTION OR ACCELERATION OF NEUTRAL MOLECULAR OR ATOMIC BEAMS
    • H05H3/00—Production or acceleration of neutral particle beams, e.g. molecular or atomic beams
    • H05H3/06—Generating neutron beams

Definitions

  • the present invention relates to the composition, structure, assembly and method of making an extruded polymeric tube and bonding the tube in a co-axial arrangement with a pre-fabricated polymeric body (e.g., fitting) for delivery of fluids.
  • a pre-fabricated polymeric body e.g., fitting
  • Plasticized polyvinyl chloride (PVC) tubing has been utilized in the medical field for many decades. Over this time period, there have been various post tube manufacturing operations utilized to apply fitments at the end of the tube so as to incorporate the tube into various medical assemblies, e.g., connected to an insulin pump or the like, or to a delivery member (e.g. needle set) for the delivery of fluids to a patient(human or other animal) for health maintenance or during operational procedures.
  • these various fitments include a region where the tube is inserted into the fitment and it is then secured (e.g., by adhesives or other chemical and non-chemical bonding means) in liquid-tight engagement to the fitment.
  • Fitments may be made from various materials, including acrylonitrile-butadiene-styrene (ABS) copolymers, polycarbonate (PC), acrylic resins and other thermoplastic materials so chosen for their mechanical properties, thermal stability and for the ability to be precisely molded within very tight dimensional tolerances.
  • ABS acrylonitrile-butadiene-styrene
  • PC polycarbonate
  • acrylic resins acrylic resins and other thermoplastic materials so chosen for their mechanical properties, thermal stability and for the ability to be precisely molded within very tight dimensional tolerances.
  • a bonding material such as a UV curable adhesive material
  • an applicator to the external outer surface of the tube
  • the tube is then physically engaged into the fitment.
  • UV (ultraviolet) light activates the adhesive to cure into a final solid form and the tube is adhesively bonded to the fitment.
  • the nature of the bonding which occurs is such that it takes a certain amount of force to physically remove the tube portion from the fitment, e.g., to prevent unintended dislodgement during use of the assembly. This force is typically much larger after the application and curing of the adhesive to the surfaces versus simply a physical insertion of the tube into the fitment, in the absence of the adhesive.
  • Plasticized PVC tubing has been demonstrated to be most useful for all of these operations with a variety of fitments made from the different materials types referenced above. However, for at least environmental, regulatory and/or legislative reasons, there is a need to avoid the use of plasticized PVC as the material with which to make medical tubing. The potential for migration of the plasticizer into the medicinal fluid has been cited as a concern for some fluid types.
  • elastomeric materials also have chemical functionality (esters, amide, etc.) that may have interactions with various medicinal fluids.
  • chemical functionality esters, amide, etc.
  • Medicinal fluids may comprise balanced/stable colloids and suspensions of the active pharmacological agents that are buffered with surfactants and other dispersion/suspending agents. These agents may preferentially adsorb to chemical functionalities of the tube material/luer and thus affect the medicinal efficacy of the fluid.
  • ABS, PC, and acrylics are amorphous materials that are subject to crazing/cracking.
  • ABS, PC, Acrylic, etc luers in common usage today may have molded in stress which makes them especially susceptible to cracking in the presence of solvents, either prior to or during use.
  • the nature of the medicinal fluids may cause stress cracking of such amorphous materials or changes in dimensions of the luers that cause leakage or failure.
  • the present invention contemplates the manufacture of an extruded tube, preferably a multilayer coextruded tube of at least two non-PVC containing polymeric materials (lacking chemical functionality) that are coextruded, whereby the tubing materials are bonded securely to each other and such that the outer tubing layer of the two materials can be readily and securely solvent bonded on an exposed outside surface to the inside surface of the central channel of a tubular component, such as a luer or other fitment.
  • the tubing is particularly well adapted for bonding to a fitment comprised of inert polypropylene based materials for use in medical fluid delivery and treatment applications.
  • the present invention avoids the problems of the prior art plasticized PVC tubing, and also avoids the problems of using UV curable adhesives. These curable adhesives are expensive, and require the additional step of exposure to UV light, which adds considerably to the cost of assembling the tubing and fitment.
  • the invention further avoids the potential for fluid contamination. It has been observed that the fluid being injected through a tubing and fitment will often wet out the area of engagement between the tubing and fitment, thereby encountering the adhesive polymer material.
  • the UV curable polymers may have extractable uncured monomer or other components that are not intended and would be detrimental to the patient if they become part of the injected fluids delivered to the patient.
  • the present invention further eliminates the need for the use of ester, urethane, or amide containing elastomers or other chemical functionality, such as carbonyls or acid groups, that may contact and interact with fluids being delivered through the tubing or fitment.
  • the invention further avoids the use of fitment materials that are prone to stress cracking in the presence of medicinal fluids.
  • the solvent is selected from one or more of cyclohexanone, cyclohexane, hexane, xylene, tetrahydrofuran (THF), ethyl acetate (EA) and methyl ethyl ketone (MEK).
  • the solvent is selected from one or more of cyclohexane, cyclohexanone, xylene, tetrahydrofuran, and hexane.
  • the PBE is a copolymer or blend of propylene and an alpha-olefin.
  • the PBE is a propylene/alpha-olefin copolymer with semi-crystalline isotactic propylene segments.
  • the PBE is a blend of a first polymer component (FPC) which is a predominately crystalline stereoregular polypropylene, and a second polymer component (SPC) which is a crystallizable copolymer of C2,C4-C20 alpha-olefin and propylene.
  • FPC first polymer component
  • SPC second polymer component
  • the alpha-olefin is ethylene.
  • PE polyethylene
  • the PE of the inner wall is a low density polyethylene (LDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE) or blends thereof.
  • LDPE low density polyethylene
  • LLDPE linear low density polyethylene
  • HDPE high density polyethylene
  • the step of extruding comprises coextruding an outer tubular layer of the PBE material with at least one innermost tubular layer of a thermoplastic ethylene-based olefinic material.
  • the coextruded outer layer of the mating tube is the PBE with an ethylene content of at least 9% by weight and the innermost layer of the mating tube is polyethylene.
  • the tubular body comprises a prefabricated body of PBE material.
  • the PBE material of the tubular body is a homopolymer polypropylene or a copolymer of predominately propylene units and ethylene.
  • a bonded tubular assembly comprising:
  • the extruded tube is a coextruded tube having an outer tubular layer of the PBE material with at least one innermost tubular layer of a thermoplastic ethylene-based olefinic material.
  • the coextruded outer layer of the mating tube is the PBE material with an ethylene content of at least 9% by weight and the innermost layer of the mating tube is polyethylene.
  • the tube has an inner wall forming the central tubular passage comprising a coextruded a layer of a polyethylene (PE).
  • PE polyethylene
  • the PE is a low density polyethylene (LDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE) or blends thereof.
  • LDPE low density polyethylene
  • LLDPE linear low density polyethylene
  • HDPE high density polyethylene
  • a method is provided of delivering an aqueous based or non-aqueous based medicinal fluid or combination thereof to a patient comprising inserting a fluid delivery member into the body, the member being fluidly connected to the bonded tubular assembly, and delivering the medical fluid through the tube to the delivery member.
  • the medicinal fluid comprises one or more of:
  • nonaqueous solvents selected from the group consisting of: vegetable oils, ethyl oleate, propylene glycol, and polyethylene glycols with molecular weights of 300 and 400.
  • the medicinal fluid comprises one or more of:
  • the fluid preparations are selected form the group consisting of ethyl alcohol; benzyl alcohol; phenylethyl alcohol; propylene glycol; butylene glycol; trichloro-t-butyl; polyoxyethylene glycol; ethyl ether; phenoxyethanol; ethyl acetate ethyl oleate; benzyl benzoate; N-methylacetamide; N,N-dimethylacetamide; dimethyl sulfoxide (DMSO), and N-methyl 2-pyrrolidone, (NMP).
  • DMSO dimethyl sulfoxide
  • NMP N-methyl 2-pyrrolidone
  • FIG. 1 is a schematic perspective view of a portion of a multilayer co-extruded tube according to one embodiment of the invention, the tube having a terminal end portion of a selected axial length AL.
  • FIG. 2 is a side cross-sectional view of the tube of FIG. 1 with its terminal end portion coaxially inserted and solvent bonded within a central fluid flow channel end of a prefabricated tubular body (luer).
  • FIG. 3 is a schematic flow chart of one method according to the invention.
  • FIG. 4 is a schematic perspective view of a portion of a monolayer tube according to another embodiment of the invention.
  • FIG. 5 is a graph of measured bond strength values for various embodiments of the invention utilizing different solvents for bonding the extruded tube and luer fitting, all showing a substantial improvement over an interference fit without solvent bonding.
  • FIG. 6 is a graph similar to FIG. 5 showing significant improvements in bonding strength for co-extruded tubing samples filled with different fluids.
  • a polymeric tube 10 is fabricated by co-extruding a first outer layer 12 comprised of an extrudable thermoplastic propylene-based elastomer (PBE) material into bonding engagement with the outer surface 14 a of a first inner layer 14 comprised of an extrudable thermoplastic ethylene-based olefinic material.
  • PBE polypropylene-based elastomer
  • One or more additional intermediate or inner layers 19 of extrudable polymeric materials can, as optionally desired, be co-extruded together with the materials of layers 12 , 14 into successive bonding engagement with the layers 12 , 14 to form a three or more layered tube 10 .
  • a monolayer tube of the extrudable thermoplastic PBE (same material as outer layer 12 ) may be used as shown in FIG. 4 and described below.
  • the propylene-based outer layer 12 is typically selected to comprise a PBE that renders the material flexible for use as tubing for delivery of a medicinal fluid depending on the intended applications and also compatible with a propylene-based fitting (e.g., luer) to enable solvent bonding thereto.
  • a propylene-based fitting e.g., luer
  • the present invention relates to a polymeric tube for the delivery of medicinal fluids comprising a propylene based elastomer (PBE) that exhibits substantially equivalent mechanical performance to plasticized PVCs known in the industry.
  • PBE propylene based elastomer
  • the PBE polymers' composition of the present invention is propylene/alpha-olefin copolymers with semi-crystalline isotactic propylene segments.
  • the PBE for use in the present invention have a comonomer range of between 9 to 16%, preferably between 9 to 11%.
  • the comonomers are alpha-olefins.
  • the PBE polymers may have a narrow molecular weight distribution of 2-3. The molecular weight distribution is induced Mw/Mn (also referred to as polydispersity index or MWD).
  • the suitable PBE for use in the present invention is ExxonMobil Vistamaxx series (eg, 3020FL or 3980FL grades).
  • One method of producing such a PBE is disclosed in U.S. Pat. No. 6,927,258, which is incorporated by reference herein.
  • such a PBE is produced by blending a “first polymer component” (“FPC”) which is a predominately crystalline stereoregular polypropylene with a “second polymer component” (“SPC”) which is a crystallizable copolymer of C2, C4-C20 alpha-olefin (preferable ethylene) and propylene.
  • FPC first polymer component
  • SPC second polymer component
  • the FPC melts higher than 110 C (degrees Centigrade) and has a heat of fusion of at least 75 J/g (Joules/gram), as determined by DSC (Differential Scanning calorimetry) analysis.
  • the crystalline polypropylene can be either a homopolymer or a copolymer with other alpha olefins.
  • the SPC, and optionally the SPC2 if used, have stereoregular propylene sequences long enough to crystallize.
  • the SPC has a melting point of less than 105 C and has a heat of fusion of less than 75 J/g.
  • the SPC2 has a melting point of less than 115 C and has a heat of fusion of less than 75 J/g.
  • One embodiment is blending isotactic polypropylene (FPC) with ethylene propylene copolymers (SPC) having about 4 wt % to about 35 wt % ethylene so as to ensure high compatibility with the FPC.
  • the ratio of the FPC to the SPC of the blend composition may vary in the range 2:98 to 70:30 by weight.
  • the PBEs of the present invention have a glass transition temperature (Tg) range of about ⁇ 15 to ⁇ 35 C.
  • the PBE of the present invention have a melt flow range (MFR) as measured at 230 C of between 0.5 to 50 grams/10 minutes as per ASTM D1238.
  • MFR melt flow range
  • the PBE of the present invention have a preferred Shore A hardness range of about 60 to 90 and have a flexural modulus range of about 500 to 20,000 psi (pounds per square inch) and more preferably of about 1,000 to 16,500 psi.
  • the outer layer may comprise a blend of polypropylene and other olefinic polymers (e.g., polyethylene or polyethylene-octene block copolymers); the blend should be extrudable and compatible with both the inner layer and the fitment to which it will be solvent bonded.
  • polypropylene and other olefinic polymers e.g., polyethylene or polyethylene-octene block copolymers
  • the thickness of outer layer 12 typically ranges between about 0.0005 inches and about 0.050 inches.
  • the thickness of the outer layer will vary depending on cost of materials, desired physical properties, extrusion equipment, intended use of the tubing and fitment, and other design concerns.
  • the ethylene-based olefinic material of which the first inner layer 14 is comprised is preferably a predominately extrudable thermoplastic ethylene-based olefinic material.
  • the inner layer may be comprised of a polyethylene (“PE”), typically a low density polyethylene (“LDPE”), linear low density polyethylene (“LLDPE”), high density polyethylene (“HDPE”) or blends thereof.
  • PE polyethylene
  • LDPE low density polyethylene
  • LLDPE linear low density polyethylene
  • HDPE high density polyethylene
  • the inner layer is extrudable, compatible with adjacent tube layers, and where as it comprises the innermost layer that forms the fluid delivery channel, substantially inert and approved for use with the fluid.
  • the thickness of the inner layer 14 typically ranges between about 0.0005 inches and about 0.025 inches but again will vary with overall tube dimensions and lengths, cost of materials, extrusion equipment, intended use (application), and other design concerns.
  • Both the first and second layer materials are thermoplastic materials that are extrudable, processable as a melt at elevated temperature, do not have significant creep, are of generally low modulus and are flexible materials that can be stretched repeatedly at room temperature with an ability to return to their approximate original length if not stretched beyond their elastic yield strain.
  • the inner layer 14 is non-polar and otherwise lacking chemical functionality (functional groups) that would interact with a medicinal fluid of the intended application.
  • medicinal fluid it is meant any aqueous based fluid, non-aqueous based fluid, or combination thereof acceptable for injection into a patient (human or other animal) which includes the active pharmacological substance or biological substance, the choice of which is for an intended beneficial medical treatment of the patient.
  • the active pharmacological or biological substance to be injected may include but is not limited to insulin, anti-inflammatories, anti-septics, cancer therapies, arthritis therapies, other treatment therapies, protein and enzyme based pharmaceuticals, nutrients, and other medicants.
  • the active pharmacological or biological substance may be delivered via any of various aqueous, nonaqueous, or mixed solvents and other carrier fluids.
  • nonaqueous solvents the following are examples: vegetable oils, ethyl oleate, propylene glycol, and polyethylene glycols with molecular weights of 300 and 400.
  • Synthetic and semisynthetic preparations are also available as solvent or mixed solvent based fluid preparations for injection to the patient; examples include the alcohols (e.g., ethyl, benzyl, phenylethyl, propylene glycol, butylene glycol, trichloro-t-butyl, etc.), ethers and esters (e.g., polyoxytheylene glycol, ethyl ether, phenoxyethanol, ethyl acetate ethyl oleate, benzl benzoate, etc.), amides (e.g., N-methylacetamide and N,N-dimethylacetamide), sulfoxides (e.g,. dimethyl sulfoxide, (DMSO)), pyrrolidones (e.g., N-methyl 2-pyrrolidone, (NMP)) and the like.
  • alcohols e.g., ethyl, benzyl, phenyle
  • the active pharmacological substance or biological substance is typically prepared as a stabilized mixture, suspension or emulsion in combination with the aqueous, nonaqueous or solvent based carrier fluid.
  • Chemical interaction of the medicinal fluid with the chemical functionalities of the tube and fitment during conveyance to the patient, through adsorption or absorption of components of the medicinal fluid, is to be avoided as it may negatively affect the stability of the medicinal fluid and affect the proper administration of the active pharmacological substance or biological substance, thus negatively affecting the efficacy of the intended medical treatment of the patient.
  • the fitments must also not have any negative interaction with the medicinal fluid, either through direct solvation of the fitment by components of the medicinal fluid or through environmental stress cracking (ESC) of the fitment by the medicinal fluid.
  • Solvation of the fitment by the medicinal fluid leads to loss of mechanical integrity of the fitment itself, decreases the bond strength between the tube and fitment during use and is also a means by which the dissolved fitment material may potentially be injected to the patient during fluid conveyance.
  • Environmental stress cracking of the fitment leads to the mechanical failure of the fitment due to continuously acting external and/or internal stresses in the fitment due to the presence of surface active substances (known as stress cracking agents) that may exist in the form of surfactants, buffering agents or other suspending agents utilized to produce stable medicinal solutions and suspensions in which the fitment will come into contact with while in use.
  • the ESC of the fitment may also contribute to a decrease of the bond strength between the tube and fitment.
  • ESC results from the interaction of the polymer used to make the fitment with certain chemicals, it is usually not a chemical reaction between the polymer and the active environment and is well in known in the art.
  • ESC occurs more readily in amorphous polymers such as ABS (acrylonitrile-butadiene-styrene terpolymers), PC (polycarbonate), PMMA (polymethyl methacrylate), PEMA (polyethyl methacrylate), PS (polystyrene), rigid PVC, SAN (styrene-acrylonitrile copolymer), all of which are commonly utilized as materials for fitments, as well as in some semi-crystalline thermoplastics like polyethylene.
  • injection molding is typically the process of choice and manufacturing necessity and there exists the potential for internally induced stresses in the final fitment due to the very high polymer melt injection pressures utilized in the injection molding process.
  • Amorphous polymers exhibit a higher tendency for this type of failure because their loose structure facilitates fluid permeation into the polymer.
  • the stress acting agents which may exist in the medicinal fluid may promote crazing, cracking or plasticization of the fitment.
  • crack formation due to ESC is often preceded by craze formation.
  • Crazes are expanded regions held together by highly drawn fibrils which bridge the micro-cracks and prevent their propagation and coalescence.
  • Semi-crystalline polymers such as PE show brittle fracture under stress if exposed to stress cracking agents.
  • the crystallites are connected by the tie molecules through the amorphous phase.
  • the tie molecules play a decisive role in the mechanical properties of the polymer, through the transmission of load. Stress cracking agents act to lower the cohesive forces which maintain the tie molecules in the crystallites, thus facilitating their “pull-out” and disentanglement from the lamellae.
  • polypropylene is a material which is desirable for use as the fitment material as it has no known solvent at room temperature which may be utilized in a medicinal fluid
  • polypropylene is a material in which ESC does not readily occur.
  • the tubular body or fitment 20 to be solvent bonded to the tube 10 is typically formed into the configuration of a luer, plastic tube connector or other fitment that is used in medical applications such as for connecting tubes for delivery of medicinal fluids from a fluid source to a patient or receptacle in a sterile manner where the fluid is sealed within a closed system, the tubing and connector maintaining the fluid contained within the sealed system.
  • the tubular body 20 is most preferably comprised of a prefabricated PBE material, utilizing either a homopolymer polypropylene or a copolymer of predominately propylene units and a compatible co-monomer, such as ethylene.
  • the polymeric material of which tubular body 20 is comprised can also have optional components such as fillers, colorants, antioxidants, nucleating agents, lubricants and other process aids.
  • the tube 10 has a terminal end portion 11 having an outer surface 18 and a selected axial length AL for purposes of insertion into passage 22 and solvent bonding to the inner wall surface 22 a of the central fluid passage 22 of tubular body 20 (typically in the form of a luer).
  • the end portion 11 of the tube (after being coated with a solvent for bonding to the fitment 20 ) is inserted into passage 22 of body 20 such that axis A 1 of the tube 10 is generally coaxially aligned with the axis A 2 of the tubular body 20 .
  • the cross-sectional diameter D2 of the passage 22 is preferably complementary to the cross-sectional diameter D1 of the end portion 11 of the tube 10 .
  • the diameter D2 can be slightly smaller than D1 (e.g., 0.001 to about 0.015 inches smaller) in order to ensure a snug fit of the end portion 11 within passage 22 .
  • the outer surface 18 engages against the inner surface 22 a of passage 22 and the solvent that has been applied to surface 18 of tube end 11 prior to insertion is spread over both surfaces 18 and 22 a along substantially the entire selected axial length AL.
  • the tubular body 20 typically has separate co-axially aligned (A 1 -A 2 ) hollow central passage portions 22 , 24 respectively that have different cross-sectional inner diameters D2 and D3, where D3 is typically smaller than D2 thus forming a stop surface 25 against which the larger diameter D1 terminal end surface 17 of the terminal end portion 11 of tube 10 (about the same or slightly larger than D2) is stopped and abuts against on forcible manual insertion of end portion 11 axially into and through passage
  • the solvent for treating outer surface 18 of the tube 10 is typically selected from one or more hydrocarbons, such as cyclohexanone, cyclohexane, hexane, xylene, tetrahydrofuran (THF), ethyl acetate (EA) and methyl ethyl ketone (MEK).
  • Solvent treatment typically comprises applying the solvent to surface 18 of the end portion 11 of tube 10 prior to inserting the end portion 11 into the axial passage 22 of the tubular body 20 .
  • FIG. 3 is a flow chart illustrating one method embodiment of the invention.
  • a tube such as multilayer tube 10 shown in FIGS. 1-2 , is co-extruded as the mating tube to be solvent bonded with the tubular body 20 .
  • the outer surface of the mating tube at one end portion is treated with solvent, e.g., by applying a coating of the solvent.
  • the treated end portion of the mating tube is inserted into a central tubular passage of the tubular body, to form a mated juncture along the coaxial mating portions of the outer surface of the tube and central passage of the tubular body.
  • the mated juncture is allowed to dry so that the solvent evaporates such that a solvent bond is formed between the mating portion of the outer surface of the tube and the central tubular passage of the tubular body.
  • a monolayer tube of the thermoplastic PBE material is provided.
  • the single layer tubular wall forms both the outer surface 18 for solvent bonding with the central passage of the tubular body, and the inner tubular surface 21 of the single layer forms the fluid delivery passage that is intended, as previously described, to be non-polar and otherwise lacking in chemical functionality that would interact with a medicinal fluid of the intended application.
  • Tubing Test Samples Tubing specimens were fabricated by co-extrusion in multilayer form, with materials as specified below, and using an extrusion tooling such as the “Tri Die” extrusion apparatus manufactured by the Genca Division of General Cable Company, Clearwater, Fla.:
  • the outer layer of the PBE had a thickness of 0.026 inches
  • the inner layer of ethylene-based material had a thickness of 0.005 inches
  • the extrusion or co-extrusion process is carried out by melting the polymeric material(s), routing the melted material(s) under pressure through a suitable die head to form a tubular shaped extrudate or co-extrudate that is then cooled through conventional water baths or water vacuum tanks to form an end product.
  • Tubing specimens so fabricated were then bonded to commercially available luers as specified below and then pull tested for bond strength.
  • the test samples were prepared and test equipment and parameters utilized were as follows.
  • a multi-layer (2 material, 2 layer) tube 10 having an outer surface layer formed from the VistamaxxTM 3980 FL (striped bars) or VistamaxxTM 3020 FL (unstriped bars) that is solvent bonded to the least effective bonding solvent (ethyl acetate) still provides a significant improvement in bonding strength to a polypropylene luer, relative to a non-solvent bonded assembly that relies solely on a mechanical interference fit.
  • the bonding strength of the least effective solvent was at least about 3.5 lbs as compared with a bonding strength of about 2.3-2.6 lbs based on a mechanical interference fit alone (without solvent).
  • a number of solvents produced bond strengths greater than 4 lbs., ranging from 6.3 to 13.5 lbs.
  • FIG. 6 demonstrates the chemical compatibility of two non-aqueous fluid systems, DMSO and NMP, respectively, with the aforementioned Vistamaxx 3980 FL tubing samples according to one embodiment of the invention.
  • DMSO dimethyl sulfoxide
  • NMP N-methyl 2-pyrrolidone
  • DMSO and NMP are common fluid carriers or solvents recognized by the US Food and Drug Administrtion for use in medicinal fluids and are typically utilized, amongst other uses, for solubilizing lipophilic pharmacological substances that are not readily soluble in water.
  • DMSO and NMP are also recognized to be very aggressive to many polymers either as strong solvents or stress crack agents.
  • the data presents the pull test results for samples made from Vistamaxx 3980FL as the outer layer, when coextruded with an inner layer of polyethylene, and solvent bonded to the polypropylene luer utilizing xylene or cyclohexane.
  • the luer was heat crimped to seal the luer at the end opposite to which the tube was inserted.
  • the tube and luer assemblies were filled with either DMSO or NMP, and left at room temperature conditions (72 F/50% R.H.) in a sealed glass jar.
  • the DMSO and NMP were drained from the tube and luer assemblies and the samples were pull tested.
  • FIG. 6 there was little or no degradation of bond strength between the tube and luer over the stated time periods. There was no noted swelling of the tube and no swelling or cracking of the luer.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heart & Thoracic Surgery (AREA)
  • General Engineering & Computer Science (AREA)
  • Physics & Mathematics (AREA)
  • General Chemical & Material Sciences (AREA)
  • High Energy & Nuclear Physics (AREA)
  • Veterinary Medicine (AREA)
  • Anesthesiology (AREA)
  • Biomedical Technology (AREA)
  • Hematology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Animal Behavior & Ethology (AREA)
  • General Health & Medical Sciences (AREA)
  • Public Health (AREA)
  • Pulmonology (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Medicinal Chemistry (AREA)
  • Materials Engineering (AREA)
  • Manufacturing & Machinery (AREA)
  • Materials For Medical Uses (AREA)
  • Extrusion Moulding Of Plastics Or The Like (AREA)
  • Rigid Pipes And Flexible Pipes (AREA)
  • Lining Or Joining Of Plastics Or The Like (AREA)
  • Infusion, Injection, And Reservoir Apparatuses (AREA)
  • Medicinal Preparation (AREA)
  • Laminated Bodies (AREA)
  • Vascular Medicine (AREA)
US14/448,432 2014-07-31 2014-07-31 Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids Abandoned US20160030728A1 (en)

Priority Applications (10)

Application Number Priority Date Filing Date Title
US14/448,432 US20160030728A1 (en) 2014-07-31 2014-07-31 Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids
CR20170063A CR20170063A (es) 2014-07-31 2015-07-09 Tubería extrusionable y montaje unido por solvente para suministro de fluidos medicinales
EP15747620.1A EP3191290B1 (en) 2014-07-31 2015-07-09 Solvent bonded fitting for delivery of medicinal fluids
BR112017002034-3A BR112017002034B1 (pt) 2014-07-31 2015-07-09 Montagem tubular ligada e processo de ligação coaxial de um tubo polimérico a um corpo tubular préfabricado
PCT/US2015/039641 WO2016018577A1 (en) 2014-07-31 2015-07-09 Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids
CA2956907A CA2956907C (en) 2014-07-31 2015-07-09 Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids
CN201580046314.8A CN106795343B (zh) 2014-07-31 2015-07-09 用于输送药用流体的挤出成型管和溶剂粘合接头
JP2017505503A JP6806667B2 (ja) 2014-07-31 2015-07-09 医薬流体の送達のための押出可能な管類および溶剤結合したフィッティング
MX2017001434A MX2017001434A (es) 2014-07-31 2015-07-09 Tuberia extrusionable y montaje unido por solvente para suministro de fluidos medicinales.
US15/866,891 US10716927B2 (en) 2014-07-31 2018-01-10 Extrudable tubing for delivery of medicinal fluids

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US14/448,432 US20160030728A1 (en) 2014-07-31 2014-07-31 Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/866,891 Continuation US10716927B2 (en) 2014-07-31 2018-01-10 Extrudable tubing for delivery of medicinal fluids

Publications (1)

Publication Number Publication Date
US20160030728A1 true US20160030728A1 (en) 2016-02-04

Family

ID=53783923

Family Applications (2)

Application Number Title Priority Date Filing Date
US14/448,432 Abandoned US20160030728A1 (en) 2014-07-31 2014-07-31 Extrudable tubing and solvent bonded fitting for delivery of medicinal fluids
US15/866,891 Active 2035-01-13 US10716927B2 (en) 2014-07-31 2018-01-10 Extrudable tubing for delivery of medicinal fluids

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/866,891 Active 2035-01-13 US10716927B2 (en) 2014-07-31 2018-01-10 Extrudable tubing for delivery of medicinal fluids

Country Status (9)

Country Link
US (2) US20160030728A1 (zh)
EP (1) EP3191290B1 (zh)
JP (1) JP6806667B2 (zh)
CN (1) CN106795343B (zh)
BR (1) BR112017002034B1 (zh)
CA (1) CA2956907C (zh)
CR (1) CR20170063A (zh)
MX (1) MX2017001434A (zh)
WO (1) WO2016018577A1 (zh)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018057867A1 (en) * 2016-09-26 2018-03-29 Becton, Dickinson And Company Enhancing bond strength of medical devices
US11666729B2 (en) 2017-11-03 2023-06-06 Hollister Incorporated Methods of bonding components to polymeric substrates
EP4041340A4 (en) * 2019-10-18 2023-12-13 Bard Access Systems, Inc. QUICK INSERTION CENTRAL CATHETER AND RELATED METHODS

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110079245A (zh) * 2019-05-17 2019-08-02 深圳市凯思特医疗科技股份有限公司 一种粘结剂及其制备方法和用途
KR20220024885A (ko) 2019-07-01 2022-03-03 생-고뱅 퍼포먼스 플라스틱스 코포레이션 프로파일 연결부
DE102019219245A1 (de) * 2019-12-10 2021-06-10 B. Braun Melsungen Aktiengesellschaft Konnektor, System mit Konnektor und Schlauchleitung sowie Verfahren zum Verbinden eines Konnektors mit einer Schlauchleitung
US20210207754A1 (en) * 2019-12-27 2021-07-08 Saint-Gobain Performance Plastics Corporation Profile disconnection
CN115916510A (zh) 2020-06-19 2023-04-04 美国圣戈班性能塑料公司 复合制品和形成复合制品的方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050123703A1 (en) * 2001-01-08 2005-06-09 Ling Michael T. Port tube and closure composition, structure and assembly for a flowable material container
US20070015871A1 (en) * 2005-07-12 2007-01-18 Jsr Corporation Thermoplastic elastomer composition
US20070119511A1 (en) * 2002-01-25 2007-05-31 Donohue Robert J Co-extruded tubing

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100581789B1 (ko) * 1998-07-01 2006-05-23 엑손모빌 케미칼 패턴츠 인코포레이티드 프로필렌의 결정성 중합체 및 결정화가능한 중합체를포함하는 탄성 블렌드 조성물
JP4435934B2 (ja) * 1999-04-23 2010-03-24 川澄化学工業株式会社 多層チューブ及び多層チューブからなる医療用具
ES2257315T3 (es) 2000-04-21 2006-08-01 Kuraray Co., Ltd. Tubo multicapa y dispositivo medico que comprende el tubo multicapa.
JP2003205033A (ja) * 2002-01-10 2003-07-22 Nitta Ind Corp 医療溶液の搬送・保存用基材
JP4561964B2 (ja) * 2003-04-11 2010-10-13 Ｊｓｒ株式会社 医療用部材および医療用器具
CN101287790B (zh) * 2005-04-14 2011-07-27 埃克森美孚化学专利公司 透明的聚烯烃组合物
UA87772C2 (ru) 2005-06-29 2009-08-10 Сеинт-Гобен Ебрейсивз, Инк. Абразивный продукт, способ изготовления абразивного продукта, сшитая формальдегидная смола для абразивного продукта, способ сшивания формальдегидной смолы, отверждаемая композиция и способ абразивной обработки рабочей поверхности
US20070155905A1 (en) 2006-01-03 2007-07-05 Marta Drewniak Polyolefin material with enhanced surface durability
DE102006023301A1 (de) * 2006-05-18 2008-02-28 Raumedic Ag Medizinisches Arbeitsmittel, medizinische Baugruppe mit einem derartigen Arbeitsmittel sowie Verwendung eines derartigen medizinischen Arbeitsmittels
JP5097266B2 (ja) * 2007-04-11 2012-12-12 チョンウェ コーポレーション 医療用チューブ
CN101796131B (zh) * 2007-09-07 2012-11-28 可乐丽股份有限公司 管及使用其的医疗用具
KR101161969B1 (ko) * 2007-09-28 2012-07-04 가부시키가이샤 프라임 폴리머 주사기용 폴리프로필렌 수지 및 이것을 원료로 하여 얻어지는 주사기 및 프리필드 주사기 제제
DE102008042718A1 (de) * 2008-10-09 2010-04-15 Invendo Medical Gmbh Medizintechnischer, elastischer Polymerschlauch und Verfahren zu seiner Herstellung
US8735491B2 (en) * 2008-12-16 2014-05-27 Polyone Corporation Solvent bondable thermoplastic elastomers
EP2915540A1 (en) * 2009-12-31 2015-09-09 Stealth Peptides International, Inc. Methods for performing a coronary artery bypass graft procedure
JP5632226B2 (ja) * 2010-07-30 2014-11-26 株式会社細川洋行 医療用多層チューブ、および医療用輸液バッグ
JP2013539812A (ja) 2010-10-14 2013-10-28 リライアンス、インダストリーズ、リミテッド 高溶融強度プロピレン系重合体の調製プロセス
WO2012078649A1 (en) * 2010-12-06 2012-06-14 Follica, Inc. Methods for treating baldness and promoting hair growth
JP5962457B2 (ja) * 2012-11-22 2016-08-03 株式会社ジェイ・エム・エス 医療用押出成形二層チューブおよび輸液バッグ製品

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050123703A1 (en) * 2001-01-08 2005-06-09 Ling Michael T. Port tube and closure composition, structure and assembly for a flowable material container
US20070119511A1 (en) * 2002-01-25 2007-05-31 Donohue Robert J Co-extruded tubing
US20070015871A1 (en) * 2005-07-12 2007-01-18 Jsr Corporation Thermoplastic elastomer composition

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018057867A1 (en) * 2016-09-26 2018-03-29 Becton, Dickinson And Company Enhancing bond strength of medical devices
US11649341B2 (en) 2016-09-26 2023-05-16 Becton, Dickinson And Company Enhancing bond strength of medical devices
US11666729B2 (en) 2017-11-03 2023-06-06 Hollister Incorporated Methods of bonding components to polymeric substrates
EP4041340A4 (en) * 2019-10-18 2023-12-13 Bard Access Systems, Inc. QUICK INSERTION CENTRAL CATHETER AND RELATED METHODS

Also Published As

Publication number Publication date
EP3191290A1 (en) 2017-07-19
BR112017002034B1 (pt) 2021-09-08
US10716927B2 (en) 2020-07-21
US20180126145A1 (en) 2018-05-10
CA2956907C (en) 2022-07-05
CN106795343A (zh) 2017-05-31
WO2016018577A1 (en) 2016-02-04
CR20170063A (es) 2017-06-15
JP6806667B2 (ja) 2021-01-06
BR112017002034A2 (pt) 2017-12-12
EP3191290B1 (en) 2020-05-27
MX2017001434A (es) 2017-05-09
CA2956907A1 (en) 2016-02-04
JP2017524577A (ja) 2017-08-31
CN106795343B (zh) 2020-08-04

Similar Documents

Publication Publication Date Title
US10716927B2 (en) Extrudable tubing for delivery of medicinal fluids
JP6134434B2 (ja) 押出成形可能な多層管材
EP2358806B1 (en) Solvent bondable thermoplastic elastomers
CN103025298B (zh) 医疗用多层管及医疗用输液袋
KR20090005320A (ko) 의료용 튜브
US20230019725A1 (en) Syringe including different materials
JP2017524577A5 (zh)
EP2673026B1 (en) Coupling devices and kits thereof
KR101897132B1 (ko) 넌피브이시계 의료용 수액세트의 제조 방법
KR100812353B1 (ko) 혈액백용 넌-피브이씨 실링부재 및 이를 이용한 혈액백
US11738187B2 (en) Continuous tubing with alternating compositions for medical devices
TW201217009A (en) Non-stick medical tubing
US11826990B2 (en) Multi-layer articles and methods for producing the same
KR102375659B1 (ko) 튜브 접속
WO2023244771A1 (en) Medical tube and method of formation

Legal Events

Date Code Title Description
AS Assignment

Owner name: TEKNI-PLEX, INC., PENNSYLVANIA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BOURGEOIS, PHILIP D.;OLSAVSKY, JOSEPH E.;REEL/FRAME:033523/0945

Effective date: 20140813

AS Assignment

Owner name: CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, AS COLLAT

Free format text: SECOND LIEN PATENT SECURITY AGREEMENT;ASSIGNOR:TEKNI-PLEX, INC.;REEL/FRAME:035814/0362

Effective date: 20150601

Owner name: BANK OF AMERICA, N.A., AS COLLATERAL AGENT, NEW YO

Free format text: ABL PATENT SECURITY AGREEMENT;ASSIGNOR:TEKNI-PLEX, INC.;REEL/FRAME:035814/0314

Effective date: 20150601

Owner name: CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, AS COLLAT

Free format text: FIRST LIEN PATENT SECURITY AGREEMENT;ASSIGNOR:TEKNI-PLEX, INC.;REEL/FRAME:035813/0164

Effective date: 20150601

AS Assignment

Owner name: TEKNI-PLEX, INC., PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:044225/0079

Effective date: 20171017

Owner name: PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., PENNSY

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:044225/0079

Effective date: 20171017

Owner name: NATVAR HOLDINGS, LLC, PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:044225/0079

Effective date: 20171017

Owner name: TRI-SEAL HOLDINGS, INC., PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:044225/0079

Effective date: 20171017

Owner name: TRI-SEAL HOLDINGS, INC., PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0866

Effective date: 20171017

Owner name: PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., PENNSY

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0866

Effective date: 20171017

Owner name: TEKNI-PLEX, INC., PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0866

Effective date: 20171017

Owner name: TEKNI-PLEX, INC., PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0928

Effective date: 20171017

Owner name: NATVAR HOLDINGS, LLC, PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0928

Effective date: 20171017

Owner name: TRI-SEAL HOLDINGS, INC., PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0928

Effective date: 20171017

Owner name: NATVAR HOLDINGS, LLC, PENNSYLVANIA

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0866

Effective date: 20171017

Owner name: PLASTIC SPECIALTIES AND TECHNOLOGIES, INC., PENNSY

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH;REEL/FRAME:044342/0928

Effective date: 20171017

AS Assignment

Owner name: CREDIT SUISSE AG, CAYMAN ISLANDS BRANCH, NEW YORK

Free format text: SECURITY INTEREST;ASSIGNORS:TEKNI-PLEX, INC.;NATVAR HOLDINGS, LLC;PLASTIC SPECIALTIES AND TECHNOLOGIES, INC.;AND OTHERS;REEL/FRAME:044763/0001

Effective date: 20171017

Owner name: BMO HARRIS BANK, N.A., ILLINOIS

Free format text: SECURITY INTEREST;ASSIGNORS:TEKNI-PLEX, INC.;NATVAR HOLDINGS, LLC;PLASTIC SPECIALTIES AND TECHNOLOGIES, INC.;AND OTHERS;REEL/FRAME:044763/0339

Effective date: 20171017

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION