US20150139851A1 - Ferritic stainless steel - Google Patents

Ferritic stainless steel Download PDF

Info

Publication number
US20150139851A1
US20150139851A1 US14/403,687 US201314403687A US2015139851A1 US 20150139851 A1 US20150139851 A1 US 20150139851A1 US 201314403687 A US201314403687 A US 201314403687A US 2015139851 A1 US2015139851 A1 US 2015139851A1
Authority
US
United States
Prior art keywords
steel
content
less
thermal fatigue
ferritic stainless
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/403,687
Other languages
English (en)
Inventor
Tetsuyuki Nakamura
Hiroki Ota
Hiroyuki Ogata
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
JFE Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JFE Steel Corp filed Critical JFE Steel Corp
Assigned to JFE STEEL CORPORATION reassignment JFE STEEL CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: OGATA, HIROYUKI, OTA, HIROKI, NAKAMURA, TETSUYUKI
Publication of US20150139851A1 publication Critical patent/US20150139851A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/004—Very low carbon steels, i.e. having a carbon content of less than 0,01%
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/52—Ferrous alloys, e.g. steel alloys containing chromium with nickel with cobalt
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N13/00—Exhaust or silencing apparatus characterised by constructional features ; Exhaust or silencing apparatus, or parts thereof, having pertinent characteristics not provided for in, or of interest apart from, groups F01N1/00 - F01N5/00, F01N9/00, F01N11/00
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
    • F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
    • F01N13/00—Exhaust or silencing apparatus characterised by constructional features ; Exhaust or silencing apparatus, or parts thereof, having pertinent characteristics not provided for in, or of interest apart from, groups F01N1/00 - F01N5/00, F01N9/00, F01N11/00
    • F01N13/16—Selection of particular materials
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N3/32—Investigating strength properties of solid materials by application of mechanical stress by applying repeated or pulsating forces
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0014—Type of force applied
    • G01N2203/0016—Tensile or compressive
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0058—Kind of property studied
    • G01N2203/0069—Fatigue, creep, strain-stress relations or elastic constants
    • G01N2203/0073—Fatigue
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/022—Environment of the test
    • G01N2203/0222—Temperature
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/026—Specifications of the specimen
    • G01N2203/0262—Shape of the specimen
    • G01N2203/0268—Dumb-bell specimens

Definitions

  • the present invention relates to ferritic stainless steel having excellent scale adhesion and thermal fatigue properties.
  • an exhaust manifold which is directly connected to an engine, is used under severe conditions where the maximum service temperature reaches as high as 800° C. to 900° C.
  • ferritic stainless steel containing niobium is mainly used as the material.
  • the temperatures experienced by the exhaust manifolds have been increased, particularly in recent years, due to the trends for higher fuel efficiency and clean exhaust gas to cope with environmental issues.
  • Niobium added to ferritic stainless steel improves thermal fatigue properties by being dissolved in the steel so as to increase strength at high temperatures.
  • niobium easily forms carbonitride with carbon and nitrogen present in the steel. Consequently, it is often the case that the amount of solute niobium is decreased and low thermal fatigue properties are caused. Simple increasing in the amount of niobium added to solve this problem results in a deterioration in the workability of steel. Therefore, titanium that has a higher affinity for carbon and nitrogen than that of niobium is added in combination with niobium to induce carbon and nitrogen to form titanium carbonitride, thus preventing the formation of niobium carbonitride.
  • Type 441 ferritic stainless steel (18% Cr-0.5% Nb-0.2% Ti) (EN10088-2:EN1.4509). This steel is widely used for automobile exhaust manifolds.
  • the Nb—Ti complex-added ferritic stainless steels tend to problematically incur the spalling of scales (oxide films) when they experience repeated cycles of high-temperature heating and cooling, namely, cyclic oxidation. Because exhaust manifolds are subjected to severe cyclic oxidation conditions due to the repetition of heating and rapid cooling each time the engine is started and stopped, the spalling of scales exposes the base steel directly to the high-temperature exhaust gas and thus causes oxidation to proceed further, resulting in a reduction of sheet thickness and potentially resulting in pitting or deformation. Further, cracks may occur starting from portions from which scales have spalled. Thus, the Nb—Ti complex-added ferritic stainless steels are also required to have excellent scale adhesion preventing the spalling of scales.
  • Patent Literatures 1 and 2 disclose the addition of molybdenum
  • Patent Literatures 3 to 5 disclose the addition of molybdenum, copper and tungsten.
  • Patent Literature 3 discloses the addition of rare earth metals, calcium, yttrium and zirconium
  • Patent Literature 5 discloses the addition of rare earth metals and calcium.
  • molybdenum and tungsten are expensive and have drawbacks in that the use thereof not only increases the occurrence of surface defects (such as so-called scabs) on steel sheets but also deteriorates workability.
  • the addition of copper disadvantageously causes a significant deterioration in workability at normal temperature and also deteriorates oxidation resistance.
  • rare earth metals, calcium, yttrium and zirconium have drawback in that the addition thereof increases the occurrence of surface defects on steel sheets.
  • the present invention has been made to solve the problems described above. It is therefore an object of the invention to provide ferritic stainless steel achieving excellent scale adhesion and thermal fatigue properties without deteriorations in surface properties.
  • the present inventors have studied the scale adhesion of Nb—Ti complex-added ferritic stainless steels, and have found that the addition of an appropriate amount of nickel improves scale adhesion and thus makes it possible to prevent scale spalling.
  • Patent Literature 1 or 2 discloses that cobalt improves the toughness of welds
  • the present inventors have also found that the addition of an appropriate amount of cobalt provides excellent thermal fatigue properties.
  • a ferritic stainless steel including, by mass %, C: not more than 0.020%, Si: not more than 1.0%, Mn: not more than 1.0%, P: not more than 0.040%, S: not more than 0.030%, Cr: 16.0% to 20.0%, N: not more than 0.020%, Nb: 0.30% to 0.80%, Ti: from 4 ⁇ (C %+N %) % to 0.50% wherein C % and N % indicate the C content and the N content (mass %), respectively, Al: less than 0.20%, Ni: 0.05% to 0.40%, and Co: 0.01% to 0.30%, the balance being Fe and inevitable impurities.
  • ferritic stainless steels exhibiting excellent scale adhesion and thermal fatigue properties may be obtained.
  • the inventive ferritic stainless steels also have excellent surface properties.
  • the ferritic stainless steels of the invention may be suitably used for automobile exhaust system components.
  • FIG. 1 is a view illustrating a thermal fatigue test specimen.
  • FIG. 2 is a diagram illustrating temperature conditions and restraint conditions in a thermal fatigue test.
  • Carbon is an effective element for increasing the strength of steel. This effect may be obtained when the C content is 0.001% or more.
  • the C content is preferably 0.001% or more.
  • scale spalling occurs if more than 0.020% carbon is contained.
  • the 0.0 content is limited to not more than 0.020%.
  • a lower C content is more preferable.
  • the C content is preferably not more than 0.015%, and is more preferably in the range of 0.004% to 0.008%.
  • Silicon is an effective element for increasing oxidation resistance. This effect may be obtained by adding 0.01% or more silicon.
  • the Si content is preferably 0.01% or more.
  • workability is deteriorated if more than 1.0% silicon is added.
  • the Si content is limited to not more than 1.0%.
  • the Si content is preferably in the range of from more than 0.3% to not more than 0.6%.
  • Manganese is an element that increases the strength of steel and also serves as a deoxidizer. These effects may be obtained by adding 0.01% or more manganese. Thus, the Mn content is preferably 0.01% or more. On the other hand, the weight gain by oxidation is significantly increased and oxidation resistance is lowered if more than 1.0% manganese is added. Thus, the Mn content is limited to not more than 1.0%. The Mn content is preferably in the range of 0.2% to 0.6%.
  • Phosphorus is an element which causes a deterioration in toughness, and therefore its content is desirably small.
  • the P content is limited to not more than 0.040%.
  • the P content is preferably not more than 0.035%, and more preferably not more than 0.030%.
  • Sulfur deteriorates formability and corrosion resistance, and therefore its content is desirably small.
  • the S content is limited to not more than 0.030%.
  • the S content is preferably not more than 0.006%, and more preferably not more than 0.003%.
  • Chromium is an element which is necessary for improving oxidation resistance. To obtain good oxidation resistance, the addition of 16.0% or more chromium is required. On the other hand, the addition of more than 20.0% chromium makes the steel hard and results in deteriorations in productivity and workability. Thus, the Cr content is limited to not more than 20.0%. The Cr content is preferably in the range of 17.0% to 19.0%.
  • N content is limited to not more than 0.020%.
  • the N content is preferably not more than 0.015%, and more preferably not more than 0.012%.
  • Niobium is an element that significantly increases high-temperature strength by solid solution strengthening and thereby improves thermal fatigue properties. This effect may be obtained by adding 0.30% or more niobium.
  • the addition of an excessively large amount of niobium exceeding 0.80% not only deteriorates the toughness of steel but also results in the formation of a Laves phase (Fe 2 Nb) at high temperatures and a consequent decrease in high-temperature strength.
  • the Nb content is limited to not more than 0.80%.
  • the Nb content is preferably in the range of 0.40% to 0.60%.
  • Titanium prevents the formation of niobium carbonitride by preferentially combining with carbon and nitrogen to form the carbonitride, and also enhances corrosion resistance, formability and intergranular corrosion resistance at welds.
  • the amount of titanium added needs to be at least 4 ⁇ (C %+N %) %. Below this amount, carbon and nitrogen cannot be fixed completely in the formation of titanium carbonitride but will form niobium carbonitride. Consequently, the amount of solute niobium is deteriorated and thermal fatigue properties are deteriorated. On the other hand, adding an excessively large amount of titanium results in a deterioration in the toughness of steel.
  • the Ti content is limited to not more than 0.50%.
  • the Ti content is preferably from 5 ⁇ (C %+N %) % to 0.30%, and more preferably from 0.10% to 0.25%.
  • Aluminum is an element that is effective for deoxidation. This effect may be obtained by adding 0.01% or more aluminum.
  • the Al content is preferably not less than 0.01%.
  • the Al content is limited to less than 0.20% because otherwise the steel becomes hardened and exhibits poor workability.
  • the Al content is preferably 0.01% to 0.10%, and more preferably 0.02% to 0.06%.
  • Nickel is an important element in order to ensure scale adhesion in the invention. For this purpose, it is advantageous that 0.05% or more nickel be added. As will be described later, the inventive steel exhibits a lowered thermal expansion coefficient due to the addition of an appropriate amount of cobalt. Consequently, the above effect may be obtained by adding a smaller amount of nickel as compared to cobalt-free steel or low-cobalt steel. On the other hand, nickel is expensive and also deteriorates scale adhesion by forming a ⁇ phase at high temperatures when more than 0.40% nickel is added. Thus, the amount in which nickel is added is limited to the range of 0.05% to 0.40%, and is preferably in the range of 0.10% to 0.30%, and more preferably in the range of 0.20% to 0.30%.
  • Cobalt is an important element in the invention. This element is advantageous to enhance thermal fatigue properties. For this purpose, at least 0.01% or more cobalt should ideally be added. Cobalt decreases the thermal expansion coefficient of steel and consequently the amount of expansion during heating is reduced. That is, improved thermal fatigue properties may be achieved by decreasing the amount of strain caused during heating and cooling. As a result of the decrease in the thermal expansion coefficient of steel, the difference in thermal expansion coefficient between the steel and scales becomes small and the scales are unlikely to spalle during cooling. In this manner, cobalt effectively allows for the prevention of scale spalling by the addition of a smaller amount of nickel.
  • the Co content is advantageously limited to not more than 0.30%, and is more preferably in the range of 0.02% to 0.10%, and still more preferably in the range of 0.03% to 0.10%.
  • the present invention resides in the ferritic stainless steels with excellent scale adhesion and thermal fatigue properties that contain the aforementioned essential components with the balance being iron and inevitable impurities. Where appropriate, it is possible to further add one or more selected from calcium, magnesium and boron, and to add one or more selected from molybdenum, copper, vanadium and tungsten in the following amounts.
  • Calcium is a component that is effective for preventing the clogging of nozzles with precipitates of Ti-containing inclusions that are prone to occur during continuous casting. This effect may be obtained by adding 0.0005% or more calcium.
  • the Ca content is to be not more than 0.0030% in order to obtain good surface properties without the occurrence of surface defects.
  • the content of calcium, when added, is limited to the range of 0.0005% to 0.0030%, and is more preferably in the range of 0.0005% to 0.0020%, and is still more preferably in the range of 0.0005% to 0.0015%.
  • Magnesium is an element that increases the equiaxed crystal ratio of slab and is effective for enhancing workability and toughness. Further, this element is effective for suppressing the coarsening of niobium carbonitride and titanium carbonitride. Coarse titanium carbonitride serves as a starting point of brittle crack and thus toughness is lowered. The coarsening of niobium carbonitride decreases the amount of solute niobium in steel, resulting in a deterioration in thermal fatigue properties. The above effects may be obtained by adding 0.0002% or more magnesium. On the other hand, the addition of magnesium in an amount exceeding 0.0020% deteriorates the surface properties of steel. Thus, the content of magnesium, when added, is limited to the range of 0.0002% to 0.0020%, and is preferably in the range of 0.0002% to 0.0015%, and more preferably in the range of 0.0004% to 0.0010%.
  • Boron is an element that is effective for enhancing workability, in particular secondary workability. This effect may be obtained by adding 0.0002% or more boron. On the other hand, the addition of boron in an amount exceeding 0.0020% deteriorates the workability and the toughness of steel, and therefore the amount is to be 0.0020% or less. Thus, the content of boron, when added, is limited to the range of 0.0002% to 0.0020%, and is preferably in the range of 0.0003% to 0.0010%.
  • Molybdenum is an element that increases the strength of steel by solid solution strengthening, thus enhancing thermal fatigue properties. This effect may be obtained by adding 0.02% or more molybdenum. In addition to its expensiveness, the addition of a large amount of molybdenum not only causes the occurrence of surface defects but also results in a deterioration in workability. To obtain good surface properties and good workability, the amount is to be less than 0.10%. Thus, the content of molybdenum, when added, is limited to the range of 0.02% to less than 0.10%, and is preferably in the range of 0.04% to less than 0.10%.
  • Copper strengthens steel by precipitating as ⁇ -Cu, thus enhancing thermal fatigue properties. To obtain this effect, 0.01% or more copper needs to be added. On the other hand, the addition of 0.20% or more copper makes the steel hard and results in a deterioration in workability. To obtain good workability, the amount is to be less than 0.20%. Thus, the content of copper, when added, is limited to the range of 0.01% to less than 0.20%, and is preferably in the range of 0.01% to less than 0.10%.
  • V 0.01% to less than 0.50%
  • Vanadium is an effective element for increasing high-temperature strength. This effect may be obtained by adding 0.01% or more vanadium. On the other hand, the addition of 0.50% or more vanadium results in the precipitation of coarse V(C, N) and causes a deterioration in toughness. Thus, the content of vanadium, when added, is limited to the range of 0.01% to less than 0.50%, and is preferably in the range of 0.02% to less than 0.20%.
  • tungsten increases the strength of steel by solid solution strengthening. This effect may be obtained by adding 0.02% or more tungsten.
  • this element is expensive and the addition of a large amount of tungsten not only causes the occurrence of surface defects but also results in a significant deterioration in workability. To obtain good surface properties and good workability, the amount is to be less than 0.30%. Thus, the content of tungsten, when added, is limited to the range of 0.02% to less than 0.30%.
  • the ferritic stainless steel of the invention may be manufactured by a usual stainless steel production method.
  • a steel having the aforementioned chemical composition is smelted in a melting furnace such as a converter furnace or an electric furnace, then subjected to secondary refining such as ladle refining or vacuum refining, and processed into a steel piece (a slab) by a continuous casting method or an ingot casting-slabbing method; the slab is then hot rolled, and the hot-rolled sheet is annealed and pickled to give a hot-rolled, annealed and pickled sheet; and the steel sheet is further subjected to steps such as cold rolling, finish annealing and pickling, thereby producing a cold-rolled and annealed sheet.
  • a melting furnace such as a converter furnace or an electric furnace
  • secondary refining such as ladle refining or vacuum refining
  • a steel is refined in a furnace such as a converter furnace or an electric furnace, and subjected to secondary refining by an AOD method or a VOD method to produce a molten steel having the aforementioned chemical composition.
  • the steel is processed by a continuous casting method into a slab.
  • the slab is heated to 1000 to 1250° C. and is hot rolled into a hot-rolled sheet having a desired sheet thickness.
  • the hot-rolled sheet is continuously annealed at a temperature of 900° C. to 1100° C. and is thereafter descaled by shot blasting and pickling to give a hot-rolled, annealed and pickled sheet.
  • the hot-rolled, annealed and pickled sheet may be directly used in applications of interest in the invention such as exhaust manifolds.
  • the steel sheet may be further subjected to cold rolling, annealing and pickling to produce a cold-rolled, annealed and pickled sheet.
  • This cold rolling step may involve two or more cold rolling process including process annealing as required.
  • the total rolling reduction by one or more passes through cold rolls is not less than 60%, and preferably not less than 70%.
  • the annealing temperature for the cold-rolled sheet is 900° C. to 1150° C., and preferably 950° C. to 1100° C.
  • the steel sheet may be subjected to light rolling (such as skin-pass rolling) after pickling to control the shape and the quality of the steel sheet. Further, the steel sheet may be annealed in a reducing atmosphere containing hydrogen to give a BA (Bright Annealing)-finished steel without pickling.
  • the hot-rolled and annealed sheet products or the cold-rolled and annealed sheet products manufactured as described above are processed, for example, bent in accordance with the use applications to form shapes such as automobile or motorcycle exhaust pipes or catalytic cylinders, exhaust air ducts in thermal power plants, and fuel cell-related components. Welding of these parts may be performed by any welding methods without limitation, and possible options are various arc welding methods such as TIG, MIG and MAG, resistance welding methods such as spot welding and seam welding, high-frequency resistance welding methods such as electric resistance welding, and high-frequency induction welding methods.
  • the other of the two sheet bars was heated to 1050° C. and was thereafter hot rolled into a hot-rolled sheet with a sheet thickness of 5 mm. Thereafter, the hot-rolled sheet was annealed in the temperature range of 900° C. to 1050° C. and was pickled to produce a hot-rolled and annealed sheet. At this stage, the surface properties of the steel sheet were visually observed. The steel sheet was then cold rolled to a sheet thickness of 2 mm and was subjected to finish annealing in the temperature range of 900° C. to 1050° C., thereby producing a cold-rolled and annealed sheet. This steel sheet was subjected to the following cyclic oxidation test.
  • a sample 20 mm in width and 30 mm in length was cut out from the cold-rolled and annealed sheet, and all the six surfaces were polished with #320 emery paper.
  • the sample was then tested under oxidation test conditions in which the sample was subjected to 400 cycles in which it was held at 1000° C. for 20 minutes and at 100° C. for 1 minute in the air atmosphere.
  • the heating rate and the cooling rate were 5° C./sec and 1.5° C./sec, respectively.
  • the presence or absence of the spalling of scales was visually inspected to evaluate scale adhesion. The obtained results are described in Table 1 and Table 2.
  • the thermal fatigue test specimen was subjected to repeated heating and cooling between 100° C. and 900° C. and was simultaneously caused to undergo repeated applications of strain with a restraint ratio of 0.6 as shown in FIG. 2 , thereby measuring the thermal fatigue lifetime.
  • the measurement was performed by a method in accordance with the standard for high temperature low cycle testing (JSMS-SD-7-03) published from The Society of Materials Science, Japan. First, the load that was detected at 100° C. in each cycle was divided by the sectional area (50.3 mm 2 ) of a uniformly heated parallel portion parallel portion of the test specimen illustrated in FIG. 1 , and the quotient was obtained as the stress in that cycle.
  • the thermal fatigue lifetime was defined as the number of cycles repeated until the stress in a certain cycle decreased to 75% of the initial stress (in the fifth cycle where the test piece came to exhibit stable behavior).
  • the thermal fatigue properties were evaluated based on the number of cycles as the lifetime. The obtained results are described in Table 1 and Table 2.
  • Scale adhesion The surface of the test piece after the cyclic oxidation test was evaluated as 0 (satisfactory) when the area of scale spalling was less than 5%, x (unsatisfactory) when the area of scale spalling was 5% or more, and xx (unsatisfactory) when there was breakway oxidation.
  • Thermal fatigue properties The thermal fatigue properties were evaluated as ⁇ (satisfactory, particularly excellent) when the thermal fatigue lifetime was 600 cycles or more, ⁇ (satisfactory) when the thermal fatigue lifetime was 540 to less than 600 cycles, and x (unsatisfactory) when the thermal fatigue lifetime was less than 540 cycles.
  • Comparative Example No. 18 In contrast, breakway oxidation occurred in Comparative Example No. 18 in which the Cr content was 14.5% and was below the inventive range. Comparative Example No. 19 in which the C content was 0.023% and exceeded the inventive range resulted in scale spalling and failed to pass the scale adhesion test. Due to the less than 0.01% Co content below the inventive range, the comparative steel No. 20 corresponding to Type 441 steel failed to pass the thermal fatigue test and also failed to pass the scale adhesion test in spite of the fact that 0.05% nickel had been added. In Comparative Example No. 21, the Co content was less than 0.01% and was below the inventive range, resulting in a failure to pass the thermal fatigue test. The steels failed to pass the scale adhesion test in Comparative Example Nos.
  • the ferritic stainless steels of the present invention are excellent in scale adhesion and thermal fatigue properties and are suited for exhaust system components in automobiles and other machines, such as exhaust manifolds, various exhaust pipes, converter cases and mufflers. Further, the inventive steels are also suited for exhaust system components in thermal power generation systems, and fuel cell parts.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Organic Chemistry (AREA)
  • Metallurgy (AREA)
  • Materials Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Thermal Sciences (AREA)
  • General Engineering & Computer Science (AREA)
  • Combustion & Propulsion (AREA)
  • Analytical Chemistry (AREA)
  • Biochemistry (AREA)
  • General Health & Medical Sciences (AREA)
  • General Physics & Mathematics (AREA)
  • Immunology (AREA)
  • Pathology (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
US14/403,687 2012-05-28 2013-05-23 Ferritic stainless steel Abandoned US20150139851A1 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
JP2012-120531 2012-05-28
JP2012120531 2012-05-28
JP2012209012 2012-09-24
JP2012-209012 2012-09-24
PCT/JP2013/003282 WO2013179616A1 (fr) 2012-05-28 2013-05-23 Acier inoxydable ferritique

Publications (1)

Publication Number Publication Date
US20150139851A1 true US20150139851A1 (en) 2015-05-21

Family

ID=49672843

Family Applications (1)

Application Number Title Priority Date Filing Date
US14/403,687 Abandoned US20150139851A1 (en) 2012-05-28 2013-05-23 Ferritic stainless steel

Country Status (9)

Country Link
US (1) US20150139851A1 (fr)
EP (1) EP2857538B1 (fr)
JP (1) JP5505570B1 (fr)
KR (1) KR101956709B1 (fr)
CN (1) CN104364404B (fr)
ES (1) ES2673216T3 (fr)
MY (1) MY160980A (fr)
TW (1) TWI503424B (fr)
WO (1) WO2013179616A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150323432A1 (en) * 2014-05-09 2015-11-12 Balhassn S. M. Ali Pin loaded small one-bar specimen (OBS)
US20150377757A1 (en) * 2014-06-30 2015-12-31 Balhassn S. M. Ali Small Two bar specimen (TBS)
WO2018011092A1 (fr) * 2016-07-11 2018-01-18 Universität Siegen Échantillon de matériau, procédé pour définir une géométrie d'échantillon, procédé pour déterminer un comportement du matériau et/ou des valeurs du matériau, courbe contrainte/déformation d'un matériau et produit
US11230756B2 (en) 2016-09-02 2022-01-25 Jfe Steel Corporation Ferritic stainless steel
US20230054762A1 (en) * 2020-01-14 2023-02-23 Hidria D.O.O. Electrical connection

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3517647A4 (fr) * 2016-12-21 2019-12-04 JFE Steel Corporation Acier inoxydable ferritique
FR3107959A1 (fr) * 2020-03-05 2021-09-10 Safran Aircraft Engines Procede d’essai de caracterisation d’une eprouvette en materiau composite et installation correspondante

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020007876A1 (en) * 2000-04-07 2002-01-24 Kawasaki Steel Corporation Ferritic stainless steel

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0735556B2 (ja) 1990-12-26 1995-04-19 川崎製鉄株式会社 高温強度と溶接熱影響部の靱性に優れたフェライト系ステンレス鋼
JP3014822B2 (ja) 1991-09-13 2000-02-28 川崎製鉄株式会社 高靱性高温高強度フェライト系ステンレス鋼
JP3290751B2 (ja) * 1992-05-21 2002-06-10 川崎製鉄株式会社 高加工性高温高強度フェライト系ステンレス鋼
CA2123470C (fr) * 1993-05-19 2001-07-03 Yoshihiro Yazawa Acier ferritique inoxydable possedant une excellente resistance a la corrosion atmospherique et a celle des fissures
JP3563121B2 (ja) * 1994-10-04 2004-09-08 日本冶金工業株式会社 連続鋳造性に優れるフェライト系ステンレス鋼の製造方法
JP3879164B2 (ja) * 1997-03-18 2007-02-07 Ｊｆｅスチール株式会社 冷間圧延性に優れたフェライト系ステンレス熱延鋼帯の製造方法
TW526281B (en) * 1999-04-30 2003-04-01 Kawasaki Steel Co Stainless steel material with excellent antibacterial property and process for producing the same
JP4562280B2 (ja) * 2000-12-25 2010-10-13 日新製鋼株式会社 加工性に優れ面内異方性の小さいフェライト系ステンレス鋼及びその製造方法
JP2003313640A (ja) * 2002-04-25 2003-11-06 Jfe Steel Kk 耐溶融亜鉛メッキ割れ特性に優れた高強度形鋼およびその製造方法
JP4309140B2 (ja) 2003-01-15 2009-08-05 新日鐵住金ステンレス株式会社 自動車排気系機器用フェライト系ステンレス鋼
US7732733B2 (en) * 2005-01-26 2010-06-08 Nippon Welding Rod Co., Ltd. Ferritic stainless steel welding wire and manufacturing method thereof
EP1818421A1 (fr) * 2006-02-08 2007-08-15 UGINE & ALZ FRANCE Acier inoxydable ferritique dit à 19% de chrome stabilisé au niobium
JP2007247013A (ja) * 2006-03-17 2007-09-27 Jfe Steel Kk 耐酸化性、加工性および高温強度に優れるフェライト系ステンレス鋼
JP5002991B2 (ja) * 2006-03-20 2012-08-15 Ｊｆｅスチール株式会社 耐面歪み性及び表面性状に優れたフェライト系ステンレス冷延鋼板の製造方法及び被膜鋼板
JP5297630B2 (ja) 2007-02-26 2013-09-25 新日鐵住金ステンレス株式会社 耐熱性に優れたフェライト系ステンレス鋼板
JP2009035756A (ja) * 2007-07-31 2009-02-19 Nisshin Steel Co Ltd 高温強度に優れた二輪車排ガス経路部材用Ａｌ系めっき鋼板および部材
JP5264199B2 (ja) 2008-01-28 2013-08-14 日新製鋼株式会社 フェライト系ステンレス鋼を用いたｅｇｒクーラー
JP5274047B2 (ja) * 2008-02-23 2013-08-28 日新製鋼株式会社 フェライト系ステンレス鋼材およびその製造方法並びに自動車マフラー
JP4386144B2 (ja) * 2008-03-07 2009-12-16 Ｊｆｅスチール株式会社 耐熱性に優れるフェライト系ステンレス鋼
JP5239642B2 (ja) * 2008-08-29 2013-07-17 Ｊｆｅスチール株式会社 熱疲労特性、高温疲労特性および耐酸化性に優れるフェライト系ステンレス鋼
JP5560578B2 (ja) * 2009-03-31 2014-07-30 Ｊｆｅスチール株式会社 加工性に優れたフェライト系ステンレス冷延鋼板及びその製造方法
EP2460899A4 (fr) * 2009-07-27 2014-07-09 Nisshin Steel Co Ltd Acier inoxydable ferritique pour refroidisseur rge et refroidisseur rge
CN102234740B (zh) * 2010-04-22 2013-07-17 宝山钢铁股份有限公司 一种铁素体不锈钢及其冷轧板的制造方法
JP5152387B2 (ja) * 2010-10-14 2013-02-27 Ｊｆｅスチール株式会社 耐熱性と加工性に優れるフェライト系ステンレス鋼

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020007876A1 (en) * 2000-04-07 2002-01-24 Kawasaki Steel Corporation Ferritic stainless steel

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150323432A1 (en) * 2014-05-09 2015-11-12 Balhassn S. M. Ali Pin loaded small one-bar specimen (OBS)
US20150377757A1 (en) * 2014-06-30 2015-12-31 Balhassn S. M. Ali Small Two bar specimen (TBS)
WO2018011092A1 (fr) * 2016-07-11 2018-01-18 Universität Siegen Échantillon de matériau, procédé pour définir une géométrie d'échantillon, procédé pour déterminer un comportement du matériau et/ou des valeurs du matériau, courbe contrainte/déformation d'un matériau et produit
US11230756B2 (en) 2016-09-02 2022-01-25 Jfe Steel Corporation Ferritic stainless steel
US20230054762A1 (en) * 2020-01-14 2023-02-23 Hidria D.O.O. Electrical connection
US11936147B2 (en) * 2020-01-14 2024-03-19 Hidria D.O.O. Electrical connection

Also Published As

Publication number Publication date
JPWO2013179616A1 (ja) 2016-01-18
TW201410884A (zh) 2014-03-16
CN104364404A (zh) 2015-02-18
EP2857538B1 (fr) 2018-04-18
KR101956709B1 (ko) 2019-03-11
JP5505570B1 (ja) 2014-05-28
CN104364404B (zh) 2020-07-28
EP2857538A1 (fr) 2015-04-08
EP2857538A4 (fr) 2016-03-23
TWI503424B (zh) 2015-10-11
MY160980A (en) 2017-03-31
ES2673216T3 (es) 2018-06-20
WO2013179616A1 (fr) 2013-12-05
KR20150002872A (ko) 2015-01-07

Similar Documents

Publication Publication Date Title
TWI460291B (zh) 肥粒鐵系不銹鋼
EP2902523B1 (fr) Acier inoxydable ferritique
US8153055B2 (en) Ferritic stainless steel with excellent heat resistance
JP5546911B2 (ja) 耐熱性と加工性に優れたフェライト系ステンレス鋼板
JP6075349B2 (ja) フェライト系ステンレス鋼
TWI465587B (zh) 耐氧化性優異之肥粒鐵系不鏽鋼
TWI460292B (zh) 肥粒鐵系不銹鋼
EP2857538B1 (fr) Acier inoxydable ferritique
US10415126B2 (en) Ferritic stainless steel
WO2012036313A1 (fr) Plaque en acier inoxydable thermorésistant de type ferrite présentant une excellente résistance à l'oxydation
WO2012050226A1 (fr) Acier inoxydable ferritique excellent en termes de résistance à la chaleur et d'aptitude au façonnage
WO2015118855A1 (fr) Tôle d'acier inoxydable ferritique laminée à chaud et recuite, procédé pour sa production, et tôle d'acier inoxydable ferritique laminée à froid et recuite
US20180305797A1 (en) Ferritic stainless steel
US10400318B2 (en) Ferritic stainless steel
JP5937861B2 (ja) 溶接性に優れた耐熱フェライト系ステンレス鋼板
JP5958412B2 (ja) 熱疲労特性に優れたフェライト系ステンレス鋼

Legal Events

Date Code Title Description
AS Assignment

Owner name: JFE STEEL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAKAMURA, TETSUYUKI;OTA, HIROKI;OGATA, HIROYUKI;SIGNING DATES FROM 20150113 TO 20150120;REEL/FRAME:035470/0518

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION