US20130022776A1 - Leather-like sheet - Google Patents

Leather-like sheet Download PDF

Info

Publication number
US20130022776A1
US20130022776A1 US13/638,759 US201113638759A US2013022776A1 US 20130022776 A1 US20130022776 A1 US 20130022776A1 US 201113638759 A US201113638759 A US 201113638759A US 2013022776 A1 US2013022776 A1 US 2013022776A1
Authority
US
United States
Prior art keywords
sheet
leather
fiber
fiber bundle
treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/638,759
Other languages
English (en)
Inventor
Kimio Nakayama
Masato Warita
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuraray Co Ltd
Original Assignee
Kuraray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuraray Co Ltd filed Critical Kuraray Co Ltd
Assigned to KURARAY CO., LTD. reassignment KURARAY CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: NAKAYAMA, KIMIO, WARITA, MASATO
Publication of US20130022776A1 publication Critical patent/US20130022776A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
    • D06M15/37—Macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M15/564—Polyureas, polyurethanes or other polymers having ureide or urethane links; Precondensation products forming them
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/08—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating
    • D04H3/10—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating with bonds between yarns or filaments made mechanically
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/08—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating
    • D04H3/16—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length characterised by the method of strengthening or consolidating with bonds between thermoplastic filaments produced in association with filament formation, e.g. immediately following extrusion
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D06N3/0002—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate
    • D06N3/0004—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate using ultra-fine two-component fibres, e.g. island/sea, or ultra-fine one component fibres (< 1 denier)
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N3/00—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof
    • D06N3/0002—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate
    • D06N3/0011—Artificial leather, oilcloth or other material obtained by covering fibrous webs with macromolecular material, e.g. resins, rubber or derivatives thereof characterised by the substrate using non-woven fabrics
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N2211/00—Specially adapted uses
    • D06N2211/12—Decorative or sun protection articles
    • D06N2211/28—Artificial leather
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/23907—Pile or nap type surface or component
    • Y10T428/2395—Nap type surface
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24355—Continuous and nonuniform or irregular surface on layer or component [e.g., roofing, etc.]
    • Y10T428/24438—Artificial wood or leather grain surface
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/24—Structurally defined web or sheet [e.g., overall dimension, etc.]
    • Y10T428/24942—Structurally defined web or sheet [e.g., overall dimension, etc.] including components having same physical characteristic in differing degree
    • Y10T428/2495—Thickness [relative or absolute]

Definitions

  • the present invention relates to a leather-like sheet containing a fiber-bundle entangled body of an ultrafine filament bundle, or a so-called ultrafine filament bundle entangled body. Specifically, the present invention relates to a leather-like sheet having a texture well-balanced in stiffness and flexibility.
  • leather-like sheets represented by artificial leather are superior to natural leather in, for example, lightness and handleability. Therefore, leather-like sheets have been widely used as surface materials for garments, general materials, sports items, and the like. Conventional artificial leather is produced, for example, as follows.
  • a sea-island (matrix-domain) type multi-component fiber composed of two polymers that have mutually different solvent solubilities is formed and then stapled (processed into short fibers).
  • the staple is formed into a web using a card, cross wrapper, random weaver, or the like.
  • fibers of the formed web are entangled with each other by needle punching to give a non-woven fabric.
  • the obtained non-woven fabric is impregnated with a polymer elastic body such as polyurethane.
  • the sea component polymer is removed by dissolution from the sea-island (matrix-domain) type multi-component fiber of the non-woven fabric, and only the ultrafine fiber composed of the island component polymer is retained. In this manner, artificial leather containing a non-woven fabric composed of ultrafine staple fibers and a polymer elastic body is obtained.
  • Artificial leather that contains the non-woven fabric composed of ultrafine staple fibers has the following problems. Namely, there is a problem in that since the fiber length of the ultrafine fibers is short, fiber detachment or fiber loss easily occurs. Accordingly, the napped surface of artificial napped leather in which such artificial leather is used as a substrate has poor abrasion resistance. Also, the grain resin layer of artificial grain leather in which such artificial leather is used as a substrate has poor adhesion. Also, there are problems in that during the production of such artificial leather, fibers on the surface of artificial leather become fluffy due to friction received in the production line, thus impairing stiffness or a surface texture, or fibers unevenly stretch when being wound up, thus resulting in inconsistent quality. Note that, the term “stiffness” refers to the texture having stiffness.
  • the following method is known. Specifically, for example, the extent of entanglement of a non-woven fabric is increased to raise the fiber density, and the proportion of the polymer elastic body is increased to intensify a restraint between fibers.
  • the extent of entanglement of a non-woven fabric is increased to raise the fiber density
  • the proportion of the polymer elastic body is increased to intensify a restraint between fibers.
  • the appearance and texture of the obtained artificial leather are likely to be poor.
  • artificial leather containing a non-woven fabric composed of ultrafine fibers of a filament (continuous fiber) is known.
  • a non-woven fabric composed of ultrafine filaments has better strength and shape stability than a non-woven fabric composed of ultrafine staples.
  • a series of large-scale items of equipment such as a raw-fiber feeder, fiber opener, and carding machine is not needed, the production process thereof can be simplified.
  • a non-woven fabric composed of ultrafine filaments having a low fineness is likely to be bulky and have a texture similar to a fabric having poor stiffness. This is because filaments have less crimpability than staples.
  • Patent Document 1 proposes, as a method for ameliorating the bulkiness of a non-woven fabric composed of ultrafine filaments, a method in which ultrafine filaments are partially cut to partially remove distortion for densification.
  • this method is problematic in that the advantage of increased mechanical properties brought about by the long fiber length cannot be sufficiently demonstrated.
  • Patent Document 2 proposes a method for suppressing a change of the shape of a composite sheet by reinforcing a non-woven fabric with a knit/woven fabric.
  • reinforcing a non-woven fabric with a knit/woven fabric is problematic in that creases are easily created.
  • Patent Document 3 discloses an ultrafine filament entangled sheet containing a fiber entangled body of a fiber bundle of ultrafine filaments.
  • natural leather has a structure with a density gradient in the thickness direction.
  • Artificial leather having a density gradient in the fiber or polymer elastic body in the thickness direction so as to mimic the gradient structure of natural leather is also known (see, for example, Patent Documents 4, 5, and 6).
  • An object of the present invention is to provide a leather-like sheet having a texture well-balanced in stiffness and flexibility similar to natural leather.
  • One aspect of the present invention is a leather-like sheet containing a fiber bundle entangled body which is an entangled body of fiber bundles of ultrafine filaments, a fiber occupancy (A 1 ) of a superficial layer that is a zone covering 2 ⁇ 3 of the thickness from a front surface of the fiber bundle entangled body being 36 to 56 vol %, a fiber occupancy (A 2 ) of a bottom layer thereof that is a zone covering 1 ⁇ 3 of the thickness from a back surface being smaller than the fiber occupancy (A 1 ), and a ratio (A 1 /A 2 ) of the fiber occupancy (A 1 ) to the fiber occupancy (A 2 ) being 1.08 to 1.8.
  • a leather-like sheet having a texture well-balanced in stiffness and flexibility similar to natural leather is obtained.
  • FIG. 1 is an explanatory schematic cross-sectional view showing a leather-like sheet 10 of one embodiment.
  • FIG. 2 is a schematic cross-sectional view of a fiber bundle of ultrafine filaments f forming a fiber bundle entangled body 1 .
  • the leather-like sheet 10 of this embodiment contains the fiber bundle entangled body 1 of ultrafine filaments as shown in FIG. 1 .
  • FIG. 2 shows a schematic cross-sectional view of a fiber bundle of ultrafine filaments f forming the fiber bundle entangled body 1 .
  • the fiber occupancy (A 1 ) in a superficial layer 1 a that serves as a zone covering 2 ⁇ 3 of the thickness from the front surface thereof is 36 to 56 vol %.
  • the fiber occupancy (A 2 ) of a bottom layer 1 b that serves as a zone covering 1 ⁇ 3 of the thickness from the back surface is less than the fiber occupancy (A 1 ) of the superficial layer 1 a .
  • the ratio (A 1 /A 2 ) of the fiber occupancy (A 1 ) to the fiber occupancy (A 2 ) is 1.08 to 1.8. Note that in the case where the leather-like sheet is surface-treated, the fiber occupancy is calculated from the zone that does not include the surface-treated portion.
  • the fiber occupancy is a volume fraction of the fiber component relative to the space occupied by the superficial layer 1 a or bottom layer 1 b . Specifically, for example, it can be calculated, based on the apparent specific gravity of a fiber and the specific gravity of the polymer constituting the fiber that are obtained in accordance with JIS K 7112, using the following formula:
  • Fiber occupancy (%) (Apparent specific gravity of fiber/Specific gravity of polymer constituting fiber) ⁇ 100
  • the fiber occupancy can also be estimated by observing a random cross-section that is in parallel with the thickness direction of an osmium oxide-stained leather-like sheet under a scanning electron microscope (100 to 200 magnification) at 100 to 200 magnification and performing image processing through binarization.
  • the fiber bundle entangled body 1 With the superficial layer 1 a having an increased fiber density, the fiber bundle entangled body 1 has a configuration in which the fiber occupancy (A 1 ) of the superficial layer 1 a is significantly higher than the fiber occupancy (A 2 ) of the bottom layer 1 b .
  • This configuration makes it possible to impart considerable stiffness to the superficial layer 1 a of the fiber bundle entangled body 1 and impart excellent lightweight properties and flexibility to the bottom layer 1 b .
  • the bottom layer 1 b is sparser than the superficial layer 1 a , and therefore, for example, the bottom layer 1 b easily deforms in accordance with the deformation of the superficial layer 1 a when the fiber bundle entangled body 1 is bent.
  • the fiber bundle entangled body 1 when the fiber bundle entangled body 1 is bent, a bent state similar to natural leather, i.e., the fiber bundle entangled body 1 is not likely to undergo loss of stiffness, can be reached. Moreover, the front surface thereof is dense, so the fiber bundle entangled body 1 has excellent surface abrasion resistance. Moreover, in the case where a grain layer is formed, the fiber bundle entangled body 1 demonstrates strong adhesion to the grain layer, and in the case where the fiber bundle entangled body 1 is napped, a dense fluffy texture is obtained. These properties are not obtainable from a method in which fiber bundle entangled bodies having different densities are merely adhesion-bonded to each other.
  • the fiber occupancy (A 1 ) in the superficial layer 1 a that serves as a zone covering 2 ⁇ 3 of the thickness from the front surface of the fiber bundle entangled body 1 is 36 to 56 vol %, preferably 40 to 56 vol %, and more preferably 40 to 50 vol %.
  • stiffness is insufficient. In this case, for example, the leather-like sheet easily undergoes loss of stiffness when bent.
  • the fiber occupancy (A) of the outermost layer 1 c that is a zone covering 1 ⁇ 3 of the thickness from the front surface is preferably 36 to 60 vol % and more preferably 45 to 60 vol %.
  • the fiber occupancy (A 3 ) of the outermost layer 1 c is 36 vol % or greater, stiffness is more similar to that of natural leather, and when it is 60 vol % or less, crude creases as found on cardboard are not likely to be created, and creases more similar to those of natural leather are obtained.
  • the fiber occupancy (A 2 ) of the bottom layer 1 b is smaller than the fiber occupancy (A 1 ) of the superficial layer 1 a , and the ratio (A 1 /A 2 ) of the fiber occupancy (A 1 ) to the fiber occupancy (A 2 ) is in the range of 1.08 to 1.8, and preferably in the range of 1.1 to 1.5.
  • the fiber occupancy ratio (A 1 /A 2 ) is in such a range, a leather-like sheet well-balanced in stiffness and flexibility is obtained.
  • the fiber occupancy ratio (A 1 /A 2 ) is less than 1.08, flexibility is excessively small or large, and stiffness and flexibility as found in natural leather cannot be provided.
  • the ratio exceeds 1.8, the difference between the fiber density of the superficial layer 1 a and the fiber density of the bottom layer 1 b is excessive, and the superficial layer 1 a is excessively unstretchable and the bottom layer 1 b is excessively stretchable. Therefore, the sheet easily undergoes loss of stiffness when bent, and the textural balance perceived when the sheet is held or touched is also deteriorated.
  • the ratio (A 3 /A 1 ) of the fiber occupancy (A 3 ) of the outermost layer 1 c to the fiber occupancy (A 1 ) of the superficial layer 1 a is preferably in the range of 0.95 to 1.2, and is more preferably in the range of 1.0 to 1.1.
  • the fiber occupancy ratio (A 3 /A 1 ) is 0.95 or greater, excellent stiffness and creases are obtained, and when 1.2 or less, crude creases as found on cardboard are not likely to be generated.
  • the average fineness of the ultrafine filaments f constituting the fiber bundle of the fiber bundle entangled body 1 is in the range of 0.001 to 0.5 dtex, particularly 0.01 to 0.4 dtex, and especially 0.02 to 0.3 dtex.
  • the average fineness of the ultrafine filaments f is excessively small, fibers do not mutually loosen and are tied together, and as a result, it is likely that the rigidity of the fiber bundle entangled body 1 is increased, and the flexibility is impaired.
  • the average fineness of the ultrafine filaments f is excessively large, surface denseness and voluminousness as found in natural leather are not likely to be obtained.
  • the average fineness of the ultrafine filaments f makes it possible to further control the balance between stiffness and flexibility of the fiber bundle entangled body 1 .
  • the fiber occupancy (A) is 40 to 56%
  • the fiber occupancy (A) is 40 to 50%
  • the fiber occupancy (A) is 36 to 50%.
  • the resin that forms the ultrafine filaments is not particularly limited as long as it is a thermoplastic resin capable of forming the ultrafine filaments.
  • aromatic polyesters such as polyethylene terephthalate (PET), isophthalic acid-modified polyethylene terephthalate, dimethylisophthalic acid-modified polyethylene terephthalate, sulfoisophtharic acid-modified polyethylene terephthalate, polytrimethylene terphthalate, polybutylene terephthalate, and polyhexamethylene terephthalate; aliphatic polyesters such as polylactic acid, polyethylene succinate, polybutylene succinate, polybutylene succinate adipate, and polyhydroxybutyrate-polyhydroxy valerate copolymers; polyamides such as polyamide 6, polyamide 66, polyamide 10, polyamide 11, polyamide 12, and polyamide 6-12; polyolefins such as polyethylene, polypropylene (PP), polybutene, polymethylpentene, and chlorinated polyo
  • PET modified PET such as isophthalic acid-modified PET, polylactic acid, polyamide 6, polyamide 12, polyamide 6-12, polypropylene, and the like are preferable.
  • PET and modified resins such as isophthalic acid-modified PET demonstrate favorable shrinkage characteristics when subjected to a heat-moisture shrinking treatment, which will be described below, and thus are particularly preferable.
  • the extent of modification in modified PET is in the range of, for example, 0.1 to 30 mol %, particularly 0.5 to 15 mol %, and especially 1 to 10 mol %.
  • the modulus of elasticity of a fiber varies, and therefore it is also preferable to control the balance between stiffness and flexibility of the fiber bundle entangled body 1 by more suitably adjusting the fiber occupancy (A) according to the resin.
  • the fiber occupancy (A) is preferably in the range of 36 to 50%.
  • the fiber occupancy (A) is preferably in the range of 40 to 56%.
  • the fiber bundle entangled body 1 is composed of a fiber bundle that is continuously spun and that has a substantially uniform fineness, and has little variation in fineness.
  • the superficial layer and the bottom layer has excellent uniformity, and therefore the fiber bundle entangled body 1 demonstrates tension, firmness, and stiffness when bent and demonstrates large peeling strength, thus being preferable.
  • the fiber bundle entangled body that is continuously produced and has a substantially uniform fineness means that it is not created by bonding different non-woven fabrics to each other.
  • a leather-like sheet is formed from a fiber bundle entangled body obtained by entangling a web composed of different fiber components that are different in, for example, resin composition of a fiber, ultrafine fiber fineness, fiber bundle fineness, and fiber cross-sectional structure
  • the peeling strength is likely to be insufficient.
  • a method for locally densifying, by thermal pressing or the like, only the zone covering a thickness of about 0.1 mm, which ranges about 1 ⁇ 3 or less of the thickness of the entire layers, from the superficial layer is also known.
  • the leather-like sheet may contain, if necessary, a polymer elastic body to impart shape stability by putting a restraint on the fiber bundle entangled body, to impart rigidity by putting a restraint on the ultrafine filaments constituting the fiber bundle, or to improve or adjust the texture.
  • the proportion thereof relative to the mass of the fiber bundle entangled body is preferably 15 mass % or less, more preferably 0.1 to 15 mass %, even more preferably 0.2 to 10 mass %, and especially preferably 0.5 to 5 mass %.
  • the proportion of the polymer elastic body is excessive, a rubber-like feel is considerable, and the texture is likely to be impaired.
  • the inside of the fiber bundle may be impregnated with the polymer elastic body, or the polymer elastic body is adhered to the outside of the fiber bundle.
  • the polymer elastic body puts a restraint on the ultrafine filaments f that constitute the fiber bundle, and thus the rigidity is adjusted.
  • the proportion of the polymer elastic body with which the inside of the fiber bundle of the ultrafine filaments is impregnated is 5 mass % or less relative to the total mass of the entire polymer elastic body, which is the sum of the polymer elastic body present outside the fiber bundle of the fiber bundle entangled body and the polymer elastic body with which the inside of the fiber bundle is impregnated, the ultrafine filaments are excessively tied together, and thus excellent flexibility is obtained. Also, when the proportion of the polymer elastic body present inside the fiber bundle of the ultrafine filaments exceeds 5 mass %, excellent stiffness is obtained. Accordingly, adjusting the proportion of the polymer elastic body with which the inside of the fiber bundle is impregnated makes it possible to adjust the balance between flexibility and stiffness.
  • Rubbers, elastomers, and the like are used without particular limitations as the polymer elastic body. Specific examples thereof include diene-based rubbers such as butadiene rubber, isoprene rubber, chloroprene rubber, and styrene-butadiene rubber; nitrile-based rubbers such as nitrile rubber and hydrogenated nitrile rubber; acryl-based rubbers such as acrylic rubber; urethane-based rubbers such as polyether urethane rubber and polyester urethane rubber; silicone-based rubbers; olefin-based rubbers such as ethylene-propylene rubber; fluorine-based rubbers; polystyrene-based elastomers such as styrene-butadiene block copolymers, styrene-isoprene block copolymers, styrene-butadiene-styrene block copolymers, styrene-isoprene-styren
  • polyurethane-based, polyester-based, and polyamide-based, and like elastomers are preferable.
  • the leather-like sheet of this embodiment has a peeling strength of 3.0 kg/1.0 cm or greater on the superficial layer side and a ratio of the peeling strength on the superficial layer side to the peeling strength on the bottom layer side (the peeling strength on the superficial layer side/the peeling strength on the bottom layer side) of 1.08 to 2.0 and particularly 1.15 to 1.8 because an excellent leather-like sheet is obtained due to the balance between flexibility and stiffness. Note that it can be said that the greater the peeling strength in each layer, the higher the extent of entangling of the fibers.
  • the leather-like sheet of this embodiment has a logarithmic value of a tensile storage elastic modulus at 20° C. of 6.0 to 7.8 Pa and particularly 6.5 to 7.5 Pa.
  • the tensile storage elastic modulus represents properties correlating to the sheet hardness during minor deformation of the leather-like sheet and the extent of entangling or restraint of fibers.
  • the logarithmic value of the tensile storage elastic modulus is excessively small, entangling of fibers is poor, and thus shape retainability is likely to be insufficient.
  • the logarithmic value of the tensile storage elastic modulus is excessively large, fibers are strongly restrained in an excessive manner, and it is thus likely that flexibility is impaired and sewing processability is impaired.
  • the tensile storage elastic modulus at 20° C. can be adjusted by adjusting the extent of entangling of fibers or using the polymer elastic body.
  • the vertical cross-section of the fiber bundle is in the range of 50 bundles/width of 1 mm to 1000 bundles/width of 1 mm and particularly 200 bundles/mm 2 to 4000 bundle s/mm 2 , and especially 100 bundles/width of 1 mm to 1000 bundles/width of 1 mm and 400 bundles/mm 2 to 4000 bundles/mm 2 because shape retainability becomes favorable and little fiber loss occurs on the superficial layer side.
  • a desired finishing treatment may be performed on the surface of the superficial layer, e.g., a grain resin layer may be further formed or a napping treatment may be performed as described below.
  • a method for producing the leather-like sheet of this embodiment includes the steps of, for example, (1) producing a spunbond sheet composed of a sea-island (matrix-domain) type multi-component fiber obtained by melt-spinning a water-soluble thermoplastic resin and a water-insoluble thermoplastic resin, (2) forming an entangled sheet by entangling multiple pieces of the spunbond sheet stacked one on top of the other, (3) creating a shrunk web by subjecting the entangled sheet to heat-moisture shrinking or hot water shrinking, and (4) forming a fiber entangled body of a fiber bundle of ultrafine filaments by dissolving the water-soluble thermoplastic resin of the sea-island (matrix-domain) type multi-component fiber in hot water.
  • the method includes steps of (5) impregnating the fiber bundle entangled body with an aqueous liquid of a polymer elastic body and drying and solidifying the impregnated product, and (6) performing a surface treatment.
  • steps of (5) impregnating the fiber bundle entangled body with an aqueous liquid of a polymer elastic body and drying and solidifying the impregnated product and (6) performing a surface treatment.
  • a spunbond sheet composed of a sea-island (matrix-domain) type multi-component fiber is produced by melt-spinning a water-soluble thermoplastic resin and a water-insoluble thermoplastic resin.
  • the sea-island (matrix-domain) type multi-component fiber is obtained by separately melt-spinning a water-soluble thermoplastic resin and a water-insoluble thermoplastic resin that is poorly compatible with the water-soluble thermoplastic resin and then integrating the resins. From the industrial point of view, the fineness of the sea-island (matrix-domain) type multi-component fiber is preferably in the range of 0.5 to 3 dtex.
  • thermoplastic resin a thermoplastic resin that is removable by dissolution in water, an aqueous alkaline solution, an aqueous acidic solution, or the like and on which melt-spinning can be performed is preferably used.
  • water-soluble thermoplastic resins include polyvinyl alcohol-based resins (PVA-based resins); modified polyesters containing polyethylene glycol and/or alkali metal sulfonate as a copolymer component; polyethylene oxide; and the like.
  • PVA-based resins are preferably used for the following reasons.
  • the formed ultrafine filament is greatly crimped. Accordingly, a fiber bundle entangled body having a large fiber density is obtained.
  • thermoplastic resin examples include the aforementioned polyethylene terephthalate (PET), modified PET, isophthalic acid-modified PET, polylactic acid, polyamide 6, polyamide 12, polyamide 6-12, polypropylene, or like various thermoplastic resins that can form ultrafine filaments are usable.
  • the water-insoluble thermoplastic resin may contain various additives.
  • additives include catalysts, anti-coloring agents, heat-resisting agents, flame retardants, lubricants, stain-proofing agents, fluorescent whitening agents, delustering agents, coloring agents, gloss improving agents, anti-static agents, fragrances, deodorizers, bactericidal agents, miticidal agents, inorganic fine particles, and the like.
  • spunbonding after the water-soluble thermoplastic resin and the water-insoluble thermoplastic resin are integrated by being melt-spun, performing stretching and stacking yields a spunbond sheet composed of a sea-island (matrix-domain) type multi-component fiber of a filament.
  • the “filament” is a fiber produced without a cutting process unlike in staple production.
  • the water-soluble thermoplastic resin and the water-insoluble thermoplastic resin are each melt-kneaded with separate extruders, and strands of molten resins are simultaneously discharged from different spinnerets, thus forming a sea-island (matrix-domain) type multi-component fiber. It is preferable that the mass ratio of the water-soluble thermoplastic resin to the water-insoluble thermoplastic resin is in the range of 5/95 to 50/50 and particularly 10/90 to 40/60 because a high-density fiber entangled body is obtained, and ultrafine filament formability is excellent.
  • the number of islands in the sea-island (matrix-domain) type multi-component fiber is 4 to 4000 islands/fiber and particularly 10 to 1000 islands/fiber because an ultrafine fiber bundle having a small single fiber fineness and a high fiber density is obtained.
  • the sea-island (matrix-domain) type multi-component fiber is cooled with a cooling device and then stretched by a high-speed airflow at a rate corresponding to the withdrawal rate of 1000 to 6000 m/min using a suction device such as an air jet nozzle so as to attain the intended fineness. Then, the stretched sea-island (matrix-domain) type multi-component fiber is deposited on a moving collection surface, thus forming a spunbond sheet. At this time, the spunbond sheet may be partially pressure-bonded if necessary. It is preferable that the weight per unit area of the spunbond sheet is in the range of 20 to 500 g/m 2 because a homogeneous fiber bundle entangled body is obtained and excellent productivity is achieved.
  • An entangled sheet is formed by performing an entangling treatment on multiple pieces of the spunbond sheet stacked one on top of the other using a known non-woven fabric production method such as needle punching or a high-pressure water flow treatment.
  • a silicone-based oil or a mineral oil-based oil such as a needle break preventing oil, an antistatic oil, or an entangling enhancing oil is applied to the spunbond sheet.
  • an oil may be applied after two or more pieces of the spunbond sheet are stacked one on top of the other by a cross wrapper.
  • the amounts or types of oils applied to the front surface side and the back surface side may be changed so as to adjust the coefficient of friction of the fiber on the front surface side that is located on the superficial layer side and the coefficient of friction of the fiber on the back surface side that is located on the bottom layer side.
  • an entangling treatment for three-dimensionally entangling the spunbond sheet is performed by needle punching.
  • Needle punching is preferably performed under needle conditions such that the extent of entangling on the superficial layer side is large and the extent of entangling on the bottom layer side is small. Adjusting the needle conditions on the superficial layer side and on the bottom layer side in this way enables the fiber occupancy (A 1 ) of the superficial layer and the fiber occupancy (A 3 ) of the outermost layer of the obtained leather-like sheet to be higher than the fiber occupancy (A 2 ) of the bottom layer.
  • needle punching from the front surface side is performed with a needle having a large number of barbs
  • needle punching from the back surface side is performed with a needle having a small number of barbs.
  • the larger the number of barbs the more preferable, as long as the needles do not break, and specifically, needles having, for example, 1 to 9 barbs are selected for the respective needles.
  • the number of times needle punching is performed from the front surface side is made greater than the number of times needle punching is performed from the back surface side.
  • the number of times needle punching is performed is adjusted according to the needle shape, the type and amount of oil used, and the like, specifically, 500 to 5000 punches/cm 2 are preferable.
  • needle punching from the front surface side it is also preferable to perform needle punching from the front surface side to reach a large needle depth and perform needle punching from the back surface side to reach a small needle depth.
  • Such a method makes it easy to adjust the fiber occupancy (A 1 ) of the superficial layer that serves as a zone covering 2 ⁇ 3 of the thickness from the front surface of the fiber bundle entangled body constituting the leather-like sheet so as to be 36 to 56 vol % and the ratio (A 1 /A 2 ) of the fiber occupancy (A 1 ) to the fiber occupancy (A 2 ) so as to be 1.08 to 1.8.
  • the entangled sheet obtained in the above-described manner is a sheet that has undergone an entangling treatment so as to have a mass ratio of 1.2 or greater and particularly 1.5 or greater relative to the weight per unit area of the spunbond sheet before the entangling treatment.
  • the upper limit is not particularly set, and it is preferable that the mass ratio is 4 or less in order to avoid an increase of production costs caused by a lowered treatment rate.
  • the weight per unit area of the entangled sheet is suitably selected according to the intended thickness of the fiber bundle entangled body and like features, and specifically, it is preferable that the weight per unit area is in the range of 100 to 1500 g/m 2 because excellent handleability is obtained.
  • the resistance to interlayer separation of the entangled sheet is preferably 7 kg/2.5 cm or greater and particularly 9 kg/2.5 cm or greater because a fiber bundle entangled body that has a favorable shape retainability, undergoes little fiber loss, and has a high fiber density can be obtained.
  • the resistance to interlayer separation serves as a measure of the extent of three-dimensional entangling.
  • the upper limit of the resistance to interlayer separation of the entangled sheet is not particularly set, and 30 kg/2.5 cm or less is preferable for an efficient entangling treatment.
  • the shrinking treatment step is a step of producing a shrunk web in which the extent of entangling of a filament-containing entangled sheet is further raised to increase the fiber density of the fiber bundle entangled body.
  • steam heating conditions it is preferable to perform a heating treatment at an atmosphere temperature in the range of 60 to 130° C., at a relative humidity of 75% or greater, particularly a relative humidity of 90% or greater, for 60 to 600 seconds.
  • These heating conditions are preferable because it is possible to shrink the entangled sheet with a large degree of shrinkage. Note that when the relative humidity is excessively low, moisture that has come into contact with the fiber dries promptly, and shrinking is likely to be insufficient.
  • the temperature is preferably in the range of 50 to 130° C. and particularly 60 to 95° C. because shrinking can be attained with a large degree of shrinkage. Note that when the temperature is excessively low, shrinking is likely to be insufficient, and when the temperature is excessively high, shrinking is likely to be non-uniform.
  • the degree of area shrinkage is 35% or greater and particularly 40% or greater. Allowing the entangled sheet to shrink with such a high degree of shrinkage yields the shrunk web having a high fiber density and a further increased extent of fiber entangling.
  • the upper limit of the degree of area shrinkage is not particularly set, and it is about 80% for an efficient treatment. Note that it is also possible to adjust the degrees of shrinkage on the front surface side and on the back surface side by performing the treatment on the front surface side and the back surface side under different temperature, humidity, and like conditions.
  • the area refers to the average area of the area of the front surface and the area of the back surface of the sheet.
  • the fiber density may be increased by further subjecting the shrunk web obtained by the heat-moisture shrinking treatment to a heating roller or a heating press at a temperature equal to or higher than the heat deflection temperature of at least one component of the sea-island (matrix-domain) type multi-component fiber. It is also possible to adjust the fiber densities on the front surface side and on the back surface side by subjecting the front surface side and the back surface side to a heating roller or a heating press under different conditions.
  • the weight per unit area of the shrunk web is 1.2 times or greater and particularly 1.5 times or greater and 4 times or less and particularly 3 times or less than the weight per unit area of the entangled sheet before the shrinking treatment.
  • the ultrafine fiber forming treatment is a treatment for removing by dissolution or removing by decomposition the water-soluble thermoplastic resin by subjecting the shrunk web to a hot water heating treatment with water, an aqueous alkaline solution, an aqueous acidic solution, or the like.
  • the hot water heating treatment it is preferable that immersion in hot water at 65 to 90° C. for 5 to 300 seconds is performed as a first stage, and then a treatment in hot water at 85 to 100° C. for 100 to 600 seconds is performed as a second stage.
  • a nipping treatment with a roll, a high-pressure water flow treatment, ultrasonication, a shower treatment, a stirring treatment, a rubbing treatment, or a like treatment may be performed if necessary.
  • the formed ultrafine filament is greatly crimped. Since this crimping increases the fiber density, the fiber bundle entangled body having high fiber density is obtained.
  • the shrunk web or the entangled sheet before the shrinking treatment may be impregnated, if necessary, with a polymer elastic body to increase the shape stability of the fiber bundle entangled body or to adjust the mechanical properties, texture, or the like of the fiber bundle entangled body.
  • aqueous liquid of an aqueous polyurethane-based resin examples include an aqueous solution in which a resin component forming an aqueous polyurethane-based resin is dissolved in an aqueous medium and an aqueous dispersion in which a resin component forming an aqueous polyurethane-based resin is dispersed in an aqueous medium.
  • the aqueous dispersion includes a suspended dispersion and an emulsified dispersion. In particular, it is more preferable to use the aqueous dispersion because it has excellent water resistance.
  • polyurethane-based resin examples include various polyurethane-based resins obtained by reacting a polymeric polyol having an average molecular weight of 200 to 6000, an organic polyisocyanate, and a chain extender in a specific molar ratio.
  • polymeric polyol examples include polyether-based polyols such as polyethylene glycol, polypropylene glycol, polytetramethylene glycol, and poly(methyltetramethylene glycol), as well as copolymers thereof; polyester-based polyols such as polybutylene adipate diol, polybutylene sebacate diol, polyhexamethylene adipate diol, poly(3-methyl-1,5-pentylene adipate)diol, poly(3-methyl-1,5-pentylene sebacate)diol, and polycaprolactone diol, as well as copolymers thereof; polycarbonate-based polyols such as polyhexamethylene carbonate diol, poly(3-methyl-1,5-pentylene carbonate)diol, polypentamethylene carbonate diol, and polytetramethylene carbonate diol, as well as copolymers thereof; polyester carbonate polyols;
  • short-chain alcohols such as trifunctional alcohols or tetrafunctional alcohols or ethylene glycol may be used in combination. These may be used alone or may be used in a combination of two or more.
  • amorphous polycarbonate-based polyols, alicyclic polycarbonate-based polyols, linear polycarbonate-based polyol copolymers, polyether-based polyols, and the like are preferable because an excellent leather-like sheet is obtained due to the balance between flexibility and stiffness.
  • organic polyisocyanate examples include non-yellowing diisocyanates such as hexamethylene diisocyanate, isophorone diisocyanate, norbornane diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, and like aliphatic or alicyclic diisocyanates; aromatic diisocyanates such as 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 4,4′-diphenylmethane diisocyanate, and xylylene diisocyanate polyurethane; and the like.
  • non-yellowing diisocyanates such as hexamethylene diisocyanate, isophorone diisocyanate, norbornane diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, and like aliphatic or alicyclic diisocyanates
  • aromatic diisocyanates such as 2,4-tolylene
  • a polyfunctional isocyanate such as a trifunctional isocyanate or a tetrafunctional isocyanate may be used in combination. These may be used alone or may be used in a combination of two or more.
  • 4,4′-dicyclohexylmethane diisocyanate, isophorone diisocyanate, 2,4-tolylene diisocyanate, 2,6-tolylene diisocyanate, 4,4′-diphenylmethane diisocyanate, and xylylene diisocyanate have excellent mechanical properties and are thus preferable.
  • chain extender examples include diamines such as hydrazine, ethylenediamine, propylenediamine, hexamethylenediamine, nonamethylenediamine, xylylenediamine, isophoronediamine, piperazine and derivatives thereof, adipic acid dihydrazide, and isophthalic acid dihydrazide; triamines such as diethylenetriamine; tetramines such as triethylenetetramine; diols such as ethylene glycol, propylene glycol, 1,4-butanediol, 1,6-hexanediol, 1,4-bis( ⁇ -hydroxyethoxy)benzene, and 1,4-cyclohexanediol; triols such as trimethylolpropane; pentaols such as pentaerythritol; amino alcohols such as aminoethyl alcohol and aminopropyl alcohol; and the like.
  • diamines such as hydrazine,
  • a monoamine such as ethylamine, propylamine, or butylamine
  • a carboxyl group-containing monoamine compound such as 4-aminobutanoic acid or 6-aminohexanoic acid
  • a monool such as methanol, ethanol, propanol, or butanol may be used in combination with the chain extender during the chain extending reaction.
  • carboxyl group-containing diol such as 2,2-bis(hydroxymethyl)propionic acid, 2,2-bis(hydroxymethyl)butanoic acid, or 2,2-bis(hydroxymethyl)valeric acid in combination in order to introduce a carboxyl group or a like ionic group into the backbone of the polyurethane-based elastic body makes it possible to adjust producibility and various properties.
  • a crosslinked structure may be formed by adding a crosslinking agent that contains within the molecule two or more functional groups that can react with a functional group contained in the monomeric unit that forms polyurethane or by adding a self-crosslinkable compound such as a polyisocyanate-based compound or a polyfunctional blocked isocyanate-based compound.
  • the dispersion average particle diameter of the aqueous dispersion of the polyurethane-based resin is 0.01 to 1 ⁇ m and particularly 0.03 to 0.5 ⁇ m.
  • Examples of the method to impregnate the shrunk web or the entangled sheet before the shrinking treatment with the polymer elastic body include a method in which a knife coater, a bar coater, or a roll coater is used, a method in which dipping is performed, and a like method.
  • drying the shrunk web or the entangled sheet impregnated with an aqueous liquid or an aqueous dispersion of the polymer elastic body by heating makes it possible to solidify the polymer elastic body.
  • a drying method include a method in which a heat treatment is performed in a drier at 50 to 200° C., a method in which a heat treatment is performed in a drier after infrared heating, a method in which a heat treatment is performed in a drier after a steam treatment, a method in which a heat treatment is performed in a drier after ultrasonic heating, a method in which these procedures are used in combination, and the like.
  • a method may be employed in which a heat-sensitive gelating agent is added and a heat treatment is performed to achieve solidification by gelation prior to removal of water or the like.
  • step (5) for impregnation with the polymer elastic body performing the ultrafine fiber forming treatment on the sea-island (matrix-domain) type multi-component fiber removes the water-soluble thermoplastic resin and creates voids inside the ultrafine fiber bundle.
  • ultrafine filaments form the fiber bundle
  • impregnation with an aqueous liquid of the polymeric elastic body easily occurs due to capillarity. Accordingly, when the polymer elastic body is applied after performing the ultrafine fiber forming treatment, so far as the inside of the ultrafine fiber bundle is impregnated with the polymer elastic body, and thus the ultrafine filaments in the ultrafine fiber bundle cluster together. In this case, the shape retainability of the fiber bundle entangled body is further enhanced.
  • the inside of the ultrafine fiber bundle is barely impregnated with the polymer elastic body, and the polymer elastic body is mainly present on the outer portion of the ultrafine fibers, and the looseness of the ultrafine fiber bundle is increased, and thus the leather-like sheet is likely to have a more flexible texture.
  • the fiber bundle entangled body obtained in the above-described manner is usually subjected to post-processing such as a nap-raising treatment, a grain treatment, a softening treatment, a two-segment treatment, a molding treatment, and a coloring treatment according to applications.
  • post-processing such as a nap-raising treatment, a grain treatment, a softening treatment, a two-segment treatment, a molding treatment, and a coloring treatment according to applications.
  • the fiber bundle entangled body of this embodiment has favorable shape retainability and falls out fibers little even without an application of the polymer elastic body. Therefore, even without a treatment to enhance shape stability by applying the polymer elastic body to the fiber bundle entangled body as performed in conventional artificial leather production, post-processing can be performed.
  • a grain resin layer composed of a polymer elastic body is formed on the front surface of the fiber bundle entangled body as a surface layer.
  • a method for forming a surface layer composed of a polymer elastic body a method in which a surface layer is formed by directly applying a dispersion or a solution of a polymer elastic body to the front surface of the fiber bundle entangled body, a method in which a grain resin layer formed by applying a polymer elastic body to a release paper having a design pattern is bonded to the front surface of the fiber bundle entangled body, or a like method is used.
  • the polymer elastic body used for formation of the surface layer a polymer elastic body that has been conventionally used for production of a grain leather-like sheet is used without particular limitations.
  • the thickness of the grain resin layer is not particularly limited, and specifically, it is preferable that the thickness is in the range of, for example, 2 to 300 ⁇ m, particularly 3 to 100 ⁇ m or less, especially, 3 to 80 ⁇ m, and notably 3 to 50 ⁇ m.
  • a napped leather-like sheet is produced by surface-finishing the fiber bundle entangled body
  • a method that is conventionally used for production of a napped leather-like sheet in which the front surface of the fiber bundle entangled body is made fluffy by a buffing treatment using sandpaper, card clothing, or the like is used.
  • the grain leather-like sheet and the napped leather-like sheet may be colored during the step of forming the ultrafine fiber.
  • a machine kneading treatment in a dry state; a relaxing treatment in a wet state using a coloring machine, a washing machine, or the like; a softening agent treatment; a functionality imparting treatment with a fireproofing agent, a bactericidal agent, a deodorizer, a water/oil repelling agent, or the like; a tactile feel modifier imparting treatment with a silicone-based resin, a silk protein-containing treatment agent, a grippability imparting resin, or the like; or a finishing treatment with a coloring agent, a coating resin for an enamel tone, or the like may be performed.
  • the superficial layer of the fiber bundle entangled body of this embodiment has a very high fiber density
  • a relaxing treatment in a wet state and a softening agent treatment in which a treatment is performed in water at a temperature in the range of about 60 to 140° C. are particularly preferable treatments to significantly improve the texture so as to be similar to natural leather.
  • the ultrafine fiber entangled body to which the polymer elastic body has not been applied is dyed and then the polymer elastic body is applied after dyeing.
  • the polymer elastic body does not become colored, and thus color spots and surface non-uniformity resulting from the difference between the dye absorption properties of the fiber and the polymer elastic body can be avoided, thus improving quality stability.
  • various fastness properties such as fastness against wet rubbing are improved. Therefore, it is preferable that the ultrafine fiber that constitutes the leather-like sheet of this embodiment is dyed, and the polymer elastic body is not substantially dyed or is not dyed at all.
  • the apparent density of the leather-like sheet obtained in the above-described manner is not particularly limited, and it is preferably in the range of 0.5 to 0.85 g/cm 3 because the leather-like sheet attains a superior balance in stiffness and flexibility as well as superior mechanical properties and shape retainability.
  • the thickness of the leather-like sheet is not particularly limited, and it is preferably in the range of about 0.3 to 4 mm because a texture well-balanced in stiffness and flexibility is obtained.
  • a leather-like sheet was sliced so as to be divided into 3 segments or 2 segments in the thickness direction. Specifically, when divided into 3 segments, the sheet was sliced such that each layer had the same thickness, and when divided into 2 segments, the sheet was sliced at a portion corresponding to 2 ⁇ 3 of the thickness from the front surface. Then, the apparent specific gravity of each divided layer was obtained in accordance with JIS K 7112.
  • the fiber occupancy was calculated according to the following formula based on the apparent specific gravity of the fiber of each layer, i.e., superficial layer, outermost layer, and bottom layer, and the specific gravity of the polymer that constitutes the fiber:
  • Fiber occupancy (%) (Apparent specific gravity of fiber/Specific gravity of polymer constituting fiber) ⁇ 100
  • test piece having a length in the sheet length direction of 23 cm and a width of 2.5 cm was cut out.
  • an incision was made with a razor in a substantially central part, relative to the superficial layer side or the bottom layer side in the thickness direction, of an edge face in the longitudinal direction of the test piece.
  • the test piece was separated by being pulled from the edge to the middle such that the divided length of the edge of the superficial layer portion and the edge of the bottom layer portion after separation was about 10 cm.
  • SS curve stress-strain curve
  • the viscoelasticities of the sheet in the longitudinal direction and the horizontal direction, which is perpendicular thereto, were measured under conditions of a frequency of 11 Hz, a tensile mode, and a heating rate of 3° C./min using a viscoelasticity measuring apparatus (FT Rheospectra “DVE-V4” manufactured by Rheology Co., Ltd.) to obtain the storage elastic modulus at 20° C.
  • FT Rheospectra “DVE-V4” manufactured by Rheology Co., Ltd.
  • the cross-sections at random 10 points that are in parallel with the thickness direction of a leather-like sheet dyed with a premetallized dye were observed under an optical microscope (100 to 200 magnification) and the average of the points was calculated after image processing through binarization to measure the volume ratio of the fiber and the polymer elastic body. Then, the mass ratio was calculated from the obtained volume ratio and the specific gravities of the resins constituting the fiber and the polymer elastic body to determine the state of adhesion and the mass proportion of the polymer elastic body.
  • test piece cut out to 20 cm ⁇ 20 cm was regarded as an evaluation sample.
  • Five people in the field of artificial leather touched the test piece and evaluated the texture thereof according to the following criteria, and the evaluation submitted by the largest number of people was regarded as the result of texture evaluation.
  • A Ideal natural leather-like texture demonstrating softness while having relatively very good stiffness when compared with B, which represents an ordinary texture
  • B Ordinary texture of artificial leather widely used as an upper material of a sports shoe
  • C Texture too hard or too soft without any stiffness, making it difficult to use in sports shoe applications
  • test piece cut out to 20 cm ⁇ 20 cm was regarded as an evaluation sample.
  • the shape of a crease created when the test sample was valley-folded such that the upper end meets the lower end in the longitudinal direction was visually inspected. Then, evaluations were made according to the following criteria.
  • a fine and uniform crease was created in the valley-folded surface similar to that found on cowhide.
  • B An ordinary crease often observed in the upper material of a sports shoe or a partially fine crease was created in the valley-folded surface.
  • C A crude crease similar to that created when cardboard is folded was created.
  • Modified PVA water-soluble thermoplastic polyvinyl alcohol-based resin: sea component
  • isophthalic acid-modified polyethylene terephthalate having a degree of modification of 6 mol % (island component) were discharged from a spinneret for melt spinning of a multi-component fiber set at 260° C. (the number of islands: 25 islands/fiber) such that the mass ratio of sea component/island component was 25/75.
  • the ejector pressure was adjusted so as to have a spinning rate of 4000 m/min, and a sea-island (matrix-domain) type multi-component fiber having an average fineness of 2.5 dtex was deposited on a net, thus giving a spunbond sheet having a weight per unit area of 30 g/m 2 .
  • the obtained spunbond sheet was folded into 12 layers by cross wrapping, and a web having a total weight per unit area of 360 g/m 2 was prepared. Then, a needle break preventing oil was sprayed onto the web.
  • the obtained entangled sheet was immersed in hot water at 70° C. for 90 seconds to perform a heat-moisture shrinking treatment, thus giving a shrunk web.
  • the web was immersed in hot water at 95° C. for 10 minutes to remove by dissolution the modified PVA from the sea-island (matrix-domain) type multi-component fiber and was further subjected to drying, thus giving a leather-like sheet A.
  • the average fiber fineness of ultrafine filaments was 0.1 dtex, the weight per unit area was 640 g/m 2 , the thickness was 1.07 mm, and the apparent density was 0.60 g/cm 3 .
  • the front surface of the leather-like sheet A obtained in Example 1-1 was subjected to a buffing treatment with #240 paper, and moreover the sheet was dyed in gray with a disperse dye of 2% owf. Moreover, a finishing buffing treatment was performed to raise the front surface (a napping treatment), thus giving a napped leather-like sheet B. Note that falling out or loosening of fiber during dying or falling out fiber during buffing barely occurred.
  • the leather-like sheet B had a weight per unit area of 580 g/m 2 , a thickness of 1.00 mm, and an apparent density of 0.58 g/cm 3 . Flexibility, stiffness, surface fluffiness, and the state of dense creases were favorable. Results are shown in Table 1.
  • the front surface of the leather-like sheet A obtained in Example 1-1 was subjected to a buffing treatment with #240 paper.
  • a grain resin layer having a thickness of 30 ⁇ m was formed by coating a release paper with aqueous polyurethane for a surface layer and drying it.
  • the surface of the grain resin layer was coated with aqueous polyurethane for an adhesive layer and dried, thus forming an adhesive layer having a thickness of 70 ⁇ m.
  • the adhesive layer and the buffing-treated surface were dry-laminated, thus performing a dry coating treatment.
  • the release paper was peeled off, thus giving a grain leather-like sheet C.
  • the leather-like sheet C had a weight per unit area of 710 g/m 2 , a thickness of 1.15 mm, and an apparent density of 0.62 g/cm 3 . Flexibility, a crease appearance, and roundish voluminousness were favorable.
  • a leather-like sheet D was obtained in the same manner as in Example 1-1 except that the needle punching treatment conditions of Example 1-1 were changed to the following conditions. Specifically, a needle punching treatment was performed from the front surface side of the web at 600 punches/cm 2 and from the back surface side at 500 punches/cm 2 . Moreover, using No. 42 count needles, a needle punching treatment was performed from the front surface side at 600 punches/cm 2 and from the back surface side at 400 punches/cm 2 . In this manner, an entangled sheet was obtained. Note that the degree of area shrinkage of the web due to the needle punching treatment was 28%. The weight per unit area of the needle-punched entangled sheet was 470 g/m 2 , and the resistance to interlayer separation of the needle-punched entangled sheet was 12.0 kg/2.5 cm.
  • the leather-like sheet D had a weight per unit area of 660 g/m 2 , a thickness of 1.07 mm, and an apparent density of 0.62 g/cm 3 . Then, the obtained leather-like sheet was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • the leather-like sheet A obtained in Example 1-1 was immersed in a 2% aqueous liquid of a polyurethane-based aqueous resin (an aqueous resin of a polymer elastic body) and then dried, thus giving a leather-like sheet E.
  • a polyurethane-based aqueous resin an aqueous resin of a polymer elastic body
  • the cross-section in the thickness direction of the leather-like sheet E was observed under a scanning electron microscope (200 magnification)
  • the polymer elastic body was mainly present inside the fiber bundle, and the mass ratio of the non-woven fabric to the polymer elastic body was 99:1.
  • the leather-like sheet E had a weight per unit area of 645 g/m 2 , a thickness of 1.07 mm, and an apparent density of 0.60 g/cm 3 .
  • the polymer elastic body mainly present inside the fiber bundle contributed to further providing stiffness. Then, the obtained leather-like sheet E was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • a buffing treatment and a dry coating treatment were performed on the first surface of the leather-like sheet E in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet F.
  • the leather-like sheet F had a weight per unit area of 720 g/m 2 , a thickness of 1.15 mm, and an apparent density of 0.63 g/cm 3 . Then, the obtained leather-like sheet F was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • the leather-like sheet F had favorable stiffness, was in the state of having fine creases, and thus was favorable.
  • Example 1-1 The procedure up to the production of a shrunk web was carried out in the same manner as in Example 1-1. Then, the shrunk web as obtained in Example 1-1 was immersed in a 5% aqueous liquid of a polyurethane-based aqueous resin and dried, and the superficial layer side was subjected to a pressing treatment at 150° C. The degree of area shrinkage of the shrunk web relative to the entangled sheet in the above-described processing was 44%. The pressed shrunk web had a weight per unit area of 840 g/m 2 , a thickness of 1.4 mm, and an apparent density of 0.70 g/cm 3 .
  • the obtained leather-like sheet G was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet G obtained in Example 4-1 in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet H.
  • the leather-like sheet H had a weight per unit area of 720 g/m 2 , a thickness of 1.15 mm, and an apparent density of 0.63 g/cm 3 . Then, the obtained leather-like sheet H was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • the leather-like sheet H had excellent stiffness, flexibility, and uniformity between the sheet and the coated surface, was in the state of having fine creases, and thus was favorable.
  • a leather-like sheet I was obtained in the same manner as in Example 1 except that a leather-like sheet obtained by changing the needle punching treatment conditions of Example 1-1 to the following conditions was immersed in a 5% aqueous liquid of a polyurethane-based aqueous resin and then dried, and the superficial layer side was subjected to a pressing treatment at 170° C. Specifically, a needle punching treatment was performed from the front surface side of the web at 600 punches/cm 2 and from the back surface side at 300 punches/cm 2 . Moreover, using No. 42 count needles, a needle punching treatment was performed from the front surface side at 600 punches/cm 2 and no needle punching treatment was performed from the back surface side.
  • the leather-like sheet I had a weight per unit area of 620 g/m 2 , a thickness of 0.93 mm, and an apparent density of 0.67 g/cm 3 . Then, the obtained leather-like sheet was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • a leather-like sheet J was obtained in the same manner as in Example 1-1 except that the ejector pressure was adjusted such that the spinning rate was 4400 m/min instead of the spinning rate of 4000 m/min in order to achieve a degree of area shrinkage of 38% before and after the heat-moisture shrinking treatment in which an needle-punched entangled sheet was immersed in hot water at 70° C. for 90 seconds as in Example 1-1.
  • the leather-like sheet J had a weight per unit area of 525 g/m 2 , a thickness of 1.04 mm, and an apparent density of 0.50 g/cm 3 . Then, the obtained leather-like sheet J was evaluated in accordance with the evaluation methods described above. Results are shown in Table 1.
  • a leather-like sheet K was obtained in the same manner as in Example 1 except that the needle punching treatment conditions of Example 1-1 were changed to the following conditions. Specifically, using No. 40 count needles (the number of barbs: 9), a needle punching treatment was performed from the front surface side and the back side of the web both under the condition of 500 punches/cm 2 , and then using No. 42 count needles (the number of barbs: 6), a needle punching treatment was performed from the front surface side and the back surface side of the web both under the condition of 500 punches/cm 2 . Note that the degree of area shrinkage of the entangled sheet due to the needle punching treatment was 28%. The weight per unit area of the needle punched entangled sheet was 470 g/m 2 , and the resistance to interlayer separation was 12.0 kg/2.5 cm.
  • the leather-like sheet K had a weight per unit area of 670 g/m 2 , a thickness of 1.07 mm, and an apparent density of 0.63 g/cm 3 . Then, the obtained leather-like sheet K was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet K in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet L.
  • the leather-like sheet L had a weight per unit area of 735 g/m 2 , a thickness of 1.15 mm, and an apparent density of 0.64 g/cm 3 . Then, the obtained leather-like sheet L was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • the leather-like sheet L had inferior flexibility and denseness of creases.
  • a leather-like sheet M was obtained in the same manner as in Example 1-1 except that the ejector pressure was adjusted such that the spinning rate was 4800 m/min instead of the spinning rate of 4000 m/min in order to achieve a degree of area shrinkage of 20% before and after the heat-moisture shrinking treatment in which an entangled sheet after needle punching was immersed in hot water at 70° C. for 90 seconds as in Example 1-1.
  • the leather-like sheet M had a weight per unit area of 410 g/m 2 , a thickness of 1.02 mm, and an apparent density of 0.40 g/cm 3 . Then, the obtained leather-like sheet M was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet M in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet N.
  • the leather-like sheet N had a weight per unit area of 460 g/m 2 , a thickness of 1.10 mm, and an apparent density of 0.42 g/cm 3 . Then, the obtained leather-like sheet N was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • the leather-like sheet N lacked uniformity between the fiber bundle entangled body and the grain surface, exhibited large creases, and had poor stiffness.
  • a leather-like sheet O was obtained in the same manner as in Example 1-1 except that the conditions of the needle punching treatment of the web obtained of Example 1-1 were changed to the following conditions, and the front surface side was subjected to a pressing treatment at 150° C. after the modified PVA was removed by dissolution from the sea-island (matrix-domain) type multi-component fiber and the fiber was dried.
  • the needle punching treatment conditions using No. 40 count needles (the number of barbs: 9), a needle punching treatment was performed from the front surface side and the back surface side of the web both under the condition of 1000 punches/cm 2 , and then using No.
  • the leather-like sheet O had a weight per unit area of 620 g/m 2 , a thickness of 1.08 mm, and an apparent density of 0.57 g/cm 3 . Then, the obtained leather-like sheet O was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet O in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet P.
  • the leather-like sheet P had a weight per unit area of 685 g/m 2 , a thickness of 1.20 mm, and an apparent density of 0.57 g/cm 3 . Then, the obtained leather-like sheet O was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • the leather-like sheet P lacked stiffness and had paper-like creases.
  • a polyethylene terephthalate filament was discharged from a spinneret for melt spinning set as 260° C. Then, the ejector pressure was adjusted so as to have a spinning rate of 4500 m/min, and filaments having an average fineness of 0.2 dtex were deposited on a net, thus giving a spunbond sheet having a weight per unit area of 30 g/m 2 . Note that the filaments obtained in this manner do not form a fiber bundle.
  • the obtained spunbond sheet was folded into 12 layers, and a web having a total weight per unit area of 360 g/m 2 was prepared by cross wrapping. Then, a needle break preventing oil was sprayed on to the web.
  • Example 1-1 a needle punching treatment was performed in the same manner as in Example 1-1.
  • the degree of area shrinkage of the web due to the needle punching treatment was ⁇ 23%.
  • the weight per unit area of the needle-punched entangled sheet was 280 g/m 2 , and the resistance to interlayer separation of the needle-punched entangled sheet was 2 kg/2.5 cm.
  • the entangled sheet was immersed in hot water at 70° C. for 90 seconds to cause area shrinkage and was further subjected to drying, thus giving a leather-like sheet Q.
  • the degree of area shrinkage before and after immersion in hot water was 20%.
  • the leather-like sheet Q was immersed in a 20% aqueous liquid of a polyurethane-based aqueous resin and then dried.
  • the leather-like sheet Q had a weight per unit area of 350 g/m 2 , a thickness of 1.00 mm, and an apparent density of 0.35 g/cm 3 .
  • the mass ratio of the non-woven fabric to the polymer elastic body of the leather-like sheet Q was 85:15. Then, the obtained leather-like sheet Q was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet Q in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet R.
  • the leather-like sheet R had a weight per unit area of 420 g/m 2 , a thickness of 1.10 mm, and an apparent density of 0.38 g/cm 3 . Then, the obtained leather-like sheet R was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2. The leather-like sheet R had poor stiffness, exhibited large creases, and lacked a classy texture.
  • a leather-like sheet S was obtained in the same manner as in Example 1-1 except that the front surface side of a leather-like sheet as obtained in Comparative Example 1-1 was subjected to a pressing treatment at 150° C.
  • the leather-like sheet S had a weight per unit area of 670 g/m 2 , a thickness of 1.00 mm, and an apparent density of 0.67 g/cm 3 . Then, the obtained leather-like sheet S was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2. Note that regarding the fiber occupancy, the density over 1 ⁇ 3 of the thickness from the front surface was high, the leather-like sheet S had a hard, paper-like texture.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet S in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet T.
  • the leather-like sheet T had a weight per unit area of 735 g/m 2 , a thickness of 1.08 mm, and an apparent density of 0.68 g/cm 3 . Then, the obtained leather-like sheet T was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • the leather-like sheet T had paper-like creases.
  • Modified PVA (sea component) and isophthalic acid-modified polyethylene terephthalate having a degree of modification of 6 mol % (island component) were discharged from a spinneret for melt spinning of a multi-component fiber set at 260° C. (the number of islands: 25 islands/fiber) such that the sea component/island component was 30/70 (mass ratio).
  • the ejector pressure was adjusted so as to have a spinning rate of 4500 m/min, and filaments having an average fineness of 2.0 dtex were collected on a net, thus giving a spunbond sheet (a filament web) having a weight per unit area of 30 g/m 2 .
  • the obtained spunbond sheet was folded into 6 layers, and a stacked web having a total weight per unit area of 180 g/m 2 was prepared by cross wrapping. Then, a needle break preventing oil was sprayed onto the web. Then, using a single-barb needle on which the distance from the needle tip to the barb was 5 mm, the stacked web was needle-punched alternately from both surfaces at 3600 punches/cm 2 to the needle depth of 10 mm, and thus the stacked web was entangled. The degree of area shrinkage due to this needle punching treatment was 53%, and the needle-punched filament entangled sheet had a weight per unit area of 340 g/m 2 and a resistance to interlayer separation of 9.2 kg/2.5 cm.
  • This filament entangled sheet was immersed in hot water at 70° C. for 90 seconds to cause area shrinkage by the relaxation of stress on the island component. Thereafter, one-side hot-pressing was performed at a surface temperature of 150° C. under a pressure of 50 kg/cm 2 , and then the sheet was immersed in hot water at 95° C. for 10 minutes to remove by dissolution the modified PVA, thus giving a leather-like sheet U.
  • the degree of area shrinkage measured after drying was 30%, the weight per unit area was 360 g/m 2 , the apparent density was 0.50 g/cm 3 , and the average single fiber fineness of the ultrafine filaments was 0.1 dtex. Then, the obtained leather-like sheet U was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • a buffing treatment and a dry coating treatment were performed on the front surface of the leather-like sheet U in the same manner as in Example 1-3. Then, the release paper was peeled off, thus giving a grain leather-like sheet V.
  • the leather-like sheet V had a weight per unit area of 430 g/m 2 , a thickness of 0.82 mm, and an apparent density of 0.54 g/cm 3 . Then, the obtained leather-like sheet V was evaluated in accordance with the evaluation methods described above. Results are shown in Table 2.
  • the leather-like sheet V had poor stiffness, exhibited large creases, and lacked a classy texture.
  • One aspect of the present invention described above is a leather-like sheet containing a fiber bundle entangled body which is an entangled body of a fiber bundle of ultrafine filaments, the fiber occupancy (A 1 ) of the superficial layer that is a zone covering 2 ⁇ 3 of the thickness from the front surface of the fiber bundle entangled body being 36 to 56 vol %, the fiber occupancy (A 2 ) of the bottom layer thereof that is a zone covering 1 ⁇ 3 of the thickness from the back surface being smaller than the fiber occupancy (A 1 ), and the ratio (A 1 /A 2 ) of the fiber occupancy (A 1 ) to the fiber occupancy (A 2 ) being 1.08 to 1.8.
  • this leather-like sheet it is possible to impart a high level of stiffness to the fiber bundle entangled body due to the dense fibers of the superficial layer, and flexibility and lightweight properties to the bottom layer that has a smaller fiber density than the superficial layer.
  • a leather-like sheet having a texture well-balanced in stiffness and flexibility is obtained. Since the bottom layer is less dense than the superficial layer and easily stretches, the bottom layer easily deforms in accordance with the superficial layer when the leather-like sheet is bent. As a result, the leather-like sheet can have a property similar to that of natural leather, i.e., is not likely to undergo loss of stiffness when bent. Also, the front surface gives a dense and smooth tactile feel and also has excellent surface abrasion resistance.
  • the leather-like sheet exhibits strong adhesion, and since the fiber density of the superficial layer is high, the leather-like sheet exhibits dense creases similar to those in natural leather.
  • the fiber occupancy (A 3 ) of the outermost layer that is a zone covering 1 ⁇ 3 of the thickness from the front surface is 36 to 60 vol %
  • a structure in which the difference between the fiber occupancy (A 3 ) of 1 ⁇ 3 from the front surface and the fiber occupancy (A 1 ) of 2 ⁇ 3 from the front surface is small and the fiber occupancy of the front surface is gradually transitioned from being high to being low is attained, thus giving an appearance and a texture more similar to those of natural leather.
  • the fiber entangled body of the ultrafine filament bundle is formed of a fiber bundle of continuously formed ultrafine filaments having a uniform fineness.
  • the superficial layer and the bottom layer have excellent uniformity, and therefore the sheet demonstrates tension, firmness, and stiffness when bent.
  • the fiber entangled body of the ultrafine filament bundle has a peeling strength of 3.0 kg/1.0 cm or greater on the superficial layer side, and the peeling strength on the superficial layer side is 1.08 to 2.0 times greater than the peeling strength on the bottom layer side because an even better balance between stiffness and flexibility is obtained.
  • the logarithmic value of the tensile storage elastic modulus at 20° C. is in the range of 6.0 to 7.8 Pa because the leather-like sheet has excellent shape retainability.
  • the content of the polymer elastic body relative to the total mass of the fiber bundle entangled body is 15 mass % or less, and the proportion of the polymer elastic body with which the inside of the fiber bundle of the ultrafine filaments is impregnated is 5 mass % or less relative to the total mass of the polymer elastic body with which the fiber bundle entangled body is impregnated, because the leather-like sheet has excellent shape stability and rigidity while maintaining the balance between stiffness and flexibility.
  • the above-described leather-like sheet is preferably used as a grain leather-like sheet provided with a grain resin layer on its front surface as well as a napped leather-like sheet in which the ultrafine filaments present on the surface of the superficial layer are napped.
  • a leather-like sheet having flexibility and stiffness as found in natural leather is obtained.
  • the leather-like sheet also has excellent surface properties such as fastness and resistance to surface abrasion as well as mechanical properties such as peeling strength.
  • the leather-like sheet can be preferably used as a material of leather-like products such as shoes, balls, furniture, vehicle seats, garments, gloves, baseball gloves, bags, belts, and sacks.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Mechanical Engineering (AREA)
  • Synthetic Leather, Interior Materials Or Flexible Sheet Materials (AREA)
  • Nonwoven Fabrics (AREA)
US13/638,759 2010-03-31 2011-03-23 Leather-like sheet Abandoned US20130022776A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2010-083508 2010-03-31
JP2010083508 2010-03-31
PCT/JP2011/001705 WO2011121940A1 (ja) 2010-03-31 2011-03-23 皮革様シート

Publications (1)

Publication Number Publication Date
US20130022776A1 true US20130022776A1 (en) 2013-01-24

Family

ID=44711707

Family Applications (1)

Application Number Title Priority Date Filing Date
US13/638,759 Abandoned US20130022776A1 (en) 2010-03-31 2011-03-23 Leather-like sheet

Country Status (6)

Country Link
US (1) US20130022776A1 (ja)
EP (1) EP2557223A1 (ja)
JP (1) JP5593379B2 (ja)
KR (1) KR20130052544A (ja)
CN (1) CN102812176A (ja)
WO (1) WO2011121940A1 (ja)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160251797A1 (en) * 2013-11-01 2016-09-01 Kuraray Co., Ltd. Nubuck-leather-like sheet and manufacturing process therefor
US20220002825A1 (en) * 2018-11-05 2022-01-06 Atko Planning Inc. Recycled leather, and apparatus for dry-manufacturing recycled leather

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5959394B2 (ja) * 2012-09-28 2016-08-02 株式会社クラレ 銀付調人工皮革
WO2014132630A1 (ja) * 2013-02-27 2014-09-04 株式会社クラレ 人工皮革基材、銀付調人工皮革、人工皮革基材の製造方法、及び人工皮革基材用改質剤
WO2017043322A1 (ja) * 2015-09-07 2017-03-16 セーレン株式会社 ヌバック調人工皮革、及びヌバック調人工皮革の製造方法
WO2018235512A1 (ja) * 2017-06-19 2018-12-27 東レ株式会社 繊維強化プラスチック
JP6894576B2 (ja) * 2018-02-19 2021-06-30 株式会社クラレ 立毛調人工皮革
WO2022044945A1 (ja) 2020-08-28 2022-03-03 東レ株式会社 人工皮革
CN115214217A (zh) * 2022-05-31 2022-10-21 聚友泰(晋江)新材料科技有限公司 环保皮革面料及其制备工艺
CN117148809B (zh) * 2023-10-31 2023-12-29 南通中奥车用新材料有限公司 用于人造革生产设备的工艺优化方法及系统

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3940532A (en) * 1972-01-28 1976-02-24 The Fiberwoven Corporation Needled textile fabric with a thin polymeric coating thereon
US20090291250A1 (en) * 2006-07-27 2009-11-26 Tradik Co., Ltd. Artificial Leather, Base to be Used in the Leather, and Processes for Production of Both

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS56154558A (en) * 1980-04-25 1981-11-30 Kanai Hiroyuki Substrate for synthetic leather
JPS6420368A (en) 1987-07-09 1989-01-24 Toray Industries Composite sheet like article
JPH06280145A (ja) 1993-03-23 1994-10-04 Kanebo Ltd 皮革様シート状物
JP3728480B2 (ja) * 1997-02-17 2005-12-21 株式会社クラレ 皮革様シートの製造方法
JP3752058B2 (ja) 1997-06-16 2006-03-08 株式会社クラレ 立毛シートの製造方法
JP3176592B2 (ja) 1999-03-25 2001-06-18 帝人株式会社 長繊維不織布およびそれを含む人工皮革
JP4169581B2 (ja) * 2002-11-18 2008-10-22 旭化成せんい株式会社 難燃性人工皮革
JP4602001B2 (ja) * 2004-06-17 2010-12-22 株式会社クラレ 極細長繊維絡合シートの製造方法
KR101190402B1 (ko) 2004-06-17 2012-10-12 가부시키가이샤 구라레 극세 장섬유 엉킴 시트의 제조 방법
JP4086892B2 (ja) * 2005-02-08 2008-05-14 トラディック株式会社 人工皮革及びそれに用いる基体、並びにそれらの製造方法
JP2007046183A (ja) 2005-08-09 2007-02-22 Toray Ind Inc 皮革様シート状物、その製造方法ならびにそれを用いてなる内装材および衣料資材。
JP2007247079A (ja) * 2006-03-14 2007-09-27 Toyobo Co Ltd 積層不織布及びそれを用いた合成皮革

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3940532A (en) * 1972-01-28 1976-02-24 The Fiberwoven Corporation Needled textile fabric with a thin polymeric coating thereon
US20090291250A1 (en) * 2006-07-27 2009-11-26 Tradik Co., Ltd. Artificial Leather, Base to be Used in the Leather, and Processes for Production of Both

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20160251797A1 (en) * 2013-11-01 2016-09-01 Kuraray Co., Ltd. Nubuck-leather-like sheet and manufacturing process therefor
US10689800B2 (en) * 2013-11-01 2020-06-23 Kuraray Co., Ltd. Nubuck-leather-like sheet and manufacturing process therefor
US20220002825A1 (en) * 2018-11-05 2022-01-06 Atko Planning Inc. Recycled leather, and apparatus for dry-manufacturing recycled leather

Also Published As

Publication number Publication date
EP2557223A1 (en) 2013-02-13
JP5593379B2 (ja) 2014-09-24
WO2011121940A1 (ja) 2011-10-06
JPWO2011121940A1 (ja) 2013-07-04
KR20130052544A (ko) 2013-05-22
CN102812176A (zh) 2012-12-05

Similar Documents

Publication Publication Date Title
US20130022776A1 (en) Leather-like sheet
US11268237B2 (en) Elastic artificial leather and production method therefor
TWI386530B (zh) 人造皮革用基材、其製法及使用其之人造皮革
JP5159764B2 (ja) 銀付調皮革様シートおよびその製造方法
TWI701371B (zh) 皮革狀布
US20070231547A1 (en) Grain-Finished Artificial Leathers
TWI447281B (zh) 人造皮革用基材及其製法
KR101644209B1 (ko) 인공 피혁, 필라멘트 낙합 웹 및 그들의 제조 방법
JP6838602B2 (ja) シート状物およびその製造方法
JP5746074B2 (ja) 伸縮性人工皮革の製造方法
CN106661826B (zh) 片状物及其制造方法
JP2018003181A (ja) 銀付人工皮革およびその製造方法
JP5860737B2 (ja) 伸縮性人工皮革
JP2013067917A (ja) 皮革様シート
JP2012017541A (ja) 銀付調人工皮革
JP2007162170A (ja) 銀付調皮革様シート
JP2020051003A (ja) 銀付人工皮革およびその製造方法
JP5903303B2 (ja) 伸縮性人工皮革
JP5903302B2 (ja) 伸縮性人工皮革
JP7405310B1 (ja) 人工皮革およびその製造方法、ならびに、乗物用内装材、座席
WO2024029215A1 (ja) 人工皮革およびその製造方法、ならびに、乗物用内装材、座席
JP2022119295A (ja) 銀付調人工皮革及びその製造方法
JP2022034525A (ja) 人工皮革基材、立毛人工皮革及び人工皮革基材の製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: KURARAY CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NAKAYAMA, KIMIO;WARITA, MASATO;REEL/FRAME:029096/0295

Effective date: 20120830

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION