US20110131930A1 - Method for blending and loading solid catalyst material into tubular structures - Google Patents

Method for blending and loading solid catalyst material into tubular structures Download PDF

Info

Publication number
US20110131930A1
US20110131930A1 US12/928,212 US92821210A US2011131930A1 US 20110131930 A1 US20110131930 A1 US 20110131930A1 US 92821210 A US92821210 A US 92821210A US 2011131930 A1 US2011131930 A1 US 2011131930A1
Authority
US
United States
Prior art keywords
catalyst
materials
solid
tube
tubes
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/928,212
Other languages
English (en)
Inventor
Fernando Antonio Pessoa Cavalcanti
Michael Stanley DeCourcy
Peter Klugherz
Charles Lonzetta
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to US12/928,212 priority Critical patent/US20110131930A1/en
Publication of US20110131930A1 publication Critical patent/US20110131930A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J8/00—Chemical or physical processes in general, conducted in the presence of fluids and solid particles; Apparatus for such processes
    • B01J8/0015—Feeding of the particles in the reactor; Evacuation of the particles out of the reactor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J8/00—Chemical or physical processes in general, conducted in the presence of fluids and solid particles; Apparatus for such processes
    • B01J8/02—Chemical or physical processes in general, conducted in the presence of fluids and solid particles; Apparatus for such processes with stationary particles, e.g. in fixed beds
    • B01J8/06—Chemical or physical processes in general, conducted in the presence of fluids and solid particles; Apparatus for such processes with stationary particles, e.g. in fixed beds in tube reactors; the solid particles being arranged in tubes
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01G—WEIGHING
    • G01G19/00—Weighing apparatus or methods adapted for special purposes not provided for in the preceding groups
    • G01G19/387—Weighing apparatus or methods adapted for special purposes not provided for in the preceding groups for combinatorial weighing, i.e. selecting a combination of articles whose total weight or number is closest to a desired value
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J2208/00—Processes carried out in the presence of solid particles; Reactors therefor
    • B01J2208/00743—Feeding or discharging of solids
    • B01J2208/00752—Feeding

Definitions

  • the present invention relates to a method for blending and loading solid material into vessels, such as into the tubes of shell and tube reactors, in a manner which maximizes compositional homogeneity and consistency of quantities and configurations of the blended solid materials.
  • the solid materials comprise one or more solid catalyst materials, one or more solid inert materials, or blends thereof.
  • Solid catalyst materials are used in a wide variety of chemical manufacturing processes and are typically loaded, poured, arranged, or otherwise placed in process vessels to form a reactor having one or more reaction zones. In the reaction zones, reactants are contacted with the catalyst materials, under suitable reaction conditions, to produce desired products. Initially, a new reactor is loaded with fresh, new catalyst materials, inert solid materials, and mixtures thereof, in a controlled and pre-determined manner, to organize and form the necessary reaction zones for the desired reactions and products.
  • shell-and-tube heat exchangers are commonly used as process vessels for containing reaction zones to perform certain chemical reaction processes.
  • Such shell and tube reactors when operated on a commercial scale to perform oxidation reactions, typically have a very large number of elongated hollow tubes (e.g., 3,000 to 30,000) which are generally parallel with one another and collectively surrounded by a shell.
  • the inner diameter of each tube is generally between 0.75 and 2.0 inches, with a length of from about 10 to 60 feet, or more.
  • Each of the tubes is in fluid communication with an inlet and an outlet for the passage of reactants and other process fluids through the tubes (i.e., through the “tube side” of the reactor vessel).
  • the shell-and-tube reactor may be vertically-oriented (i.e., with the tubes oriented vertically and the reaction fluids flowing upward, or downward, through the tube), or horizontally-oriented (i.e., with the tubes oriented horizontally and the reaction fluids flowing horizontally through the tube side), depending on the desired reactions, the overall process, and the environment in which the reactor is situated.
  • each of the tubes of such shell and tube reactors typically contains one or more solid catalyst materials which are arranged in the same order, pattern or composition, from tube to tube, thereby collectively forming one or more reaction zones of the reactor.
  • One or more solid catalyst materials are typically mixed with one another, with one or more solid inert materials, or both, to obtain a more homogenous mixture of the desired solid materials, as well as to create mixtures of solids which vary in catalytic activity.
  • mixtures of one or more solid inert materials, without any active catalyst materials may be used to fill at least a portion of the reactor tubes to create inert zones upstream, downstream or intermediate active reaction zones containing one or more catalyst materials.
  • reaction zone and reaction “stage” are generally used to mean regions within a reaction vessel where chemical reactions occur, while “inert zones” are regions in which no chemical reaction is encouraged or catalyzed. More particularly, the term reaction “stage” is used to describe a region in which a specific desired chemical reaction is performed, catalyzed or otherwise promoted.
  • reaction “zone,” on the other hand, is used to describe a region within which the conditions of reaction vary due to physical and operational characteristics such as, but not limited to, catalytic activity, reaction temperature, residence time, etc. There are multiple techniques for varying each of these characteristics which are generally known to persons of ordinary skill and some of which will be discussed in further detail hereinafter.
  • inert zones may be formed for various purposes including, but not limited to, quenching, pre-heating, controlled cooling, manipulating reaction rates, etc.
  • inert zones may be positioned upstream, downstream, or intermediate reaction zones, and inert zones may lie adjacent one another, as desired by practitioners in the field.
  • a particular reaction stage may comprise one or more reaction zones.
  • a reaction process which involves only one chemical reaction mechanism, such as dehydrogenation of ethane to form ethylene, would be said to occur in a single reaction stage wherein ethane feed material is converted directly to ethylene product.
  • This reaction is often performed in the presence of suitable catalyst material, such as chromium-based, or nickel-alumina-based catalysts.
  • the single reaction stage may comprise a single reaction zone, for example, containing a single catalyst material (e.g., same composition, shape, size, dilution, etc.) and being operated under the same reaction conditions (e.g., the same temperature or pressure, or the same degree of catalyst density, etc.) throughout its entire volume.
  • the reaction stage and reaction zone are coexistent and the terms may legitimately be used synonymously.
  • the reaction stage of an ethane dehydrogenation process may comprise more than one reaction zone, in each of which ethane is dehydrogenated, but which differ in other ways.
  • a first reaction zone may be filled with 100% chromium-based catalyst
  • a second reaction zone may contain 100% nickel-alumina-based catalyst, or even a mixture of chromium-based and nickel-alumina-based catalyst.
  • the second reaction zone may contain the same chromium-based catalyst as in the first reaction zone and, instead, differ by being maintained at a different reaction temperature, or fed by an additional reactant feed.
  • a dehydrogenation process for conversion of ethane to ethylene is typically described as having a single reaction stage which may include one or more reaction zones, which may differ in a number of ways but in all of which the same chemical reaction mechanism occurs.
  • a two-stage catalytic reaction process for conversion of propylene to acrylic acid comprises a first reaction stage in which propylene is converted to acrolein and a second reaction stage wherein the acrolein from the first stage is further converted to acrylic acid.
  • each reaction stage contains catalyst material suitable for catalyzing the desired reaction therein, such as a molybdenum-bismuth-iron-based catalyst for conversion of propylene to acrolein in the first reaction stage, and a molybdenum-vanadium-based catalyst for conversion of the acrolein of the first stage to acrylic acid in the second reaction stage.
  • each of the first and second reaction stages may comprise one or more different reaction zones which differ from one another, within each stage, by the type, composition or strength of catalyst material, reaction temperature, etc.
  • a type of short-handed terminology may be used wherein the catalyst composition present in the first reaction stage is referred to as “R1” catalyst and the catalyst composition that is used in the second reaction stage may be referred to, similarly, as “R2” catalyst. Such terminology will be used hereinafter.
  • Each hollow lance has a hard-tipped distal end shaped for impacting and dislodging the solid materials during rotation of the lance as it is inserted further into the tube.
  • a vacuum source is connected to each hollow lance for removal of dislodged solid materials.
  • an important preliminary step is the preparation of reasonably homogenous mixtures of one or more solid catalyst compositions, with or without inert materials, which are suitable in quantity and quality for forming reaction zones in the shell-and-tube reactor vessel.
  • the more homogeneous the solid mixtures are the more consistent the reaction zones formed from these mixtures will be in each tube of the reactor.
  • the more consistent the reaction zones formed in each tube the more uniform the reaction conditions will be throughout each reaction zone of the reactor, thereby ensuring efficient and predictable reaction processes for making products of uniform quality. It is noted that perfect or statistical homogeneity need not be achieved.
  • one or more catalysts are selected having particular properties including, but not limited to, composition, size, color, shape, purity, catalytic activity, surface area, temperature tolerance and mechanical integrity.
  • Solid catalyst materials may be obtained from multiple individual batch manufacturing processes and, therefore, while they have substantially the same properties, one or more of these properties may vary within acceptable ranges from batch to batch.
  • U.S. Pat. No. 4,285,602 describes a gravity flow blending system for granular materials, such as granular thermoplastic resins (e.g., polyethylene pellets).
  • the system shown in U.S. Pat. No. 4,285,602 also includes a dust collector and an outlet port member for removing dust from the system.
  • U.S. Pat. Nos. 4,907,892 and 4,978,227 provide disclosures of apparati and methods for blending solid particulate material, such as plastic pellets, using pressurized gaseous fluid for entraining the material and measuring the amount of material, by height or weight, so as to be able to equalize the fresh feed and withdrawal rates from the main vessel.
  • U.S. Pat. No. 4,569,597 describes an apparatus for efficiently and uniformly blending solids, such as powders or other granular materials. This apparatus has interior baffles and is rotated about an axis.
  • U.S. Pat. No. 4,553,849 provides a method and apparatus for blending solid particulate materials, such as polymer pellets, using a plurality of conduits and optional baffles.
  • combinatorial weighing methods involve selecting a combination of articles whose total weight or number is closest to a desired value, and is often accomplished using computer algorithms along with sensors and feedback loop programming. See, for example, U.S. Pat. Nos. 4,661,917, 4,858,708, 5,050,064, 5,962,816, as well as devices and processes commercially available from Ishida Scales Manufacturing of Kyoto, Japan and Triangle Package Machinery Company of Chicago, Ill.
  • Such combinatorial weighing methods and apparatus often have vibration means to move the solid materials along through the apparatus.
  • the blends produced by combinatorial weighing methods are known for their consistency of composition with respect to each type of component, but not necessarily for homogeneity throughout each blend. For example, where each “blend” of cereal flakes and raisins can reasonably be expected to contain the same percentage of each component, from batch to batch, it is not necessarily assured that the cereal flakes and raisins will be homogeneously mixed with one another in each blended batch.
  • Accurate and consistent measurement of the quantities of the various mixtures of solid materials before beginning loading operations facilitates the consistent and sequential loading of the solid materials into the tubes of a reactor to achieve uniform arrangement of solid materials in the tubes.
  • the mixtures of solid materials are loaded into temporary holding vessels or containers, such as bins or bags. This simplifies and speeds the later step of loading the materials into the tubes of the reactor in a consistent, predetermined and sequential order using apparatus adapted for such purposes.
  • the homogenous mixtures of solid materials are loaded, poured, arranged, or otherwise placed in the tubes to form one or more reaction zones of a process vessel.
  • the reaction zones differ from one another in one or more characteristics including, but not limited to, catalytic activity, reaction temperature, residence time, etc.
  • each mixture of solid materials should be situated similarly in each of the tubes, i.e., the mixtures should be reasonably homogeneous compared to one another and occupy a region of the same volume and position in each tube, relative to other tubes.
  • the mixtures of solid materials be as uniform and homogenous as possible to ensure consistent and predictable catalytic activity and fluid flow throughout each reaction zone.
  • proper configuration of reaction zone(s) requires that the various mixtures of catalyst and/or inert materials are provided to, and deposited in, each of the tubes in the same quantities, consistently, in predetermined and sequential order, having consistent density and packing ratios, relative to the other tubes.
  • each tube, or other compartment containing reaction zones is filled with solid materials in substantially the same amount and arrangement to ensure formation of reaction zones and inert zones, of known volume and shape and, thereby, consistent catalytic activity and fluid flow.
  • Catalyst loader While it is, of course, possible to load solid materials, such as catalyst and inerts, into reactor tubes by hand, such as, for example, by pouring the catalyst through a funnel, it is preferred to utilize a mechanized loading apparatus, commonly referred to in the art as a “catalyst loader.” Catalyst loaders minimize tube-to-tube variability, and often will also provide a substantial increase in loading rate over manual loading methods which shortens the time necessary to load and pack all of the tubes in a reactor. Examples of suitable catalyst loaders include the single-tube loader described in U.S. Pat. No. 5,626,455, which has a single tubular member for solid catalyst delivery, and the multi-tube loader disclosed in U.S. Pat. No.
  • Multi-tube catalyst loaders having vibrating compartments, chutes, trays, etc., such as those described in U.S. Pat. Nos. 4,402,643, 6,132,157 and 6,170,670, are especially useful, not only because of their ability to simultaneously load multiple tubes, but also because the catalyst loading rate can be adjusted easily by changing the vibration frequency of the loader.
  • a well-known measure of catalyst loading rate is the “drop rate,” or “drop time,” of the catalyst.
  • the drop rate is commonly measured in units of seconds/liter of catalyst loaded.
  • the optimal catalyst loading rate is one which best balances the competing goals of: (a) loading as quickly as possible to minimize reactor downtime, and (b) loading slowly enough to ensure uniform distribution of the catalyst within the tubes. If particulate solids are loaded into a tube too quickly, the particles may collide and become lodged within the tube (commonly known as “bridging”) at a location above their intended accumulation point.
  • Non-uniform filling can generally be detected through measurement of actual zone length in a given tube vs. the target zone length (commonly referred to as “outage measurement”); generally an increase of more than about 5-10% increase in zone length vs. the target length is indicative of non-uniform filling.
  • dP pressure drop
  • U.S. Pat. No. 6,694,802 discloses an example of a device used for simultaneously measuring dP through multiple catalyst-containing tubes. Many other devices operating on essentially the same principle are known.
  • the measurement of dP may be performed at any point in the loading process to ensure that tube-to-tube packing density is within acceptable limits. For example, it is common in the loading of SRS-type reactors to check dP after a completing the placement of the first reaction stage within the reactor.
  • variation in dP measurements is considered excessive when a given tube is more than about 20% higher or lower than the average measured pressure drop value.
  • the pressure drop of a given tube should not be more than 15%, for example not more than 10%, higher or lower than the average measured pressure drop value.
  • dP measurement of the tubes it will be recognized by persons of ordinary skill that it is not necessary, in all cases, to measure the pressure drop in every tube. Rather, a random sampling of tubes will often be sufficient for quality control purposes. If a random sampling of tubes is used, not more than 25% of the tubes undergo dP measurement, such as for example, not more than 10%, or not more than 5%, or even not more than 1% of the tubes, undergo dP measurement.
  • a higher-than-expected pressure drop may result from accumulation of catalyst fines, dust, and/or tailings within a given tube, rather than from catalyst bridging.
  • This situation may often be corrected by blowing a volume of pressurized dry gas (such as, for example, 100-120 psig air or nitrogen) into one end of the tube, through the solid materials packed in the tube, and out the opposite end of the tube—thereby ejecting the unwanted particulates that may be restricting flow.
  • the degree of catalyst fines accumulation can often be minimized by utilizing vibratory catalyst loaders comprising dust removal means, such as vacuum hoods, screening trays, and the like (see for example U.S. Pat. No. 6,132,157, U.S. Pat. No.
  • optional dust removal means may also be employed within the combinatorial weighing system to further minimize dust contained in a particular mixture of solid materials.
  • the quickest allowable drop rate that may be used without the occurrence of bridging is dependent on many factors, most notably the size of the catalyst particle relative to the inside diameter of the tube into which it is loaded, the shape of the catalyst particle, and particle-to-particle uniformity. Other factors that may affect the allowable drop rate include the density of individual catalyst particles, the surface finish (or roughness) of the catalyst particles, the friability of the particles, the tendency of the particles to agglomerate or self-adhere, and the tendency of the particles to absorb moisture and swell. It will of course be apparent to persons of ordinary skill that similar concerns apply to all mixtures of solid materials, including solid catalysts, inert materials, and blends thereof, which may be loaded into reactor tubes.
  • the minimum particulate solids drop rate for a specific catalyst loading situation are typically determined empirically, on a case-by-case basis, by simple trial-and-error experimentation, as will be described in greater detail hereinafter in accordance with the present invention.
  • This use of experimentation is especially preferred when catalyst blends—such as those produced by the method of the present invention—are being loaded, because the drop rates for these blends will be most difficult to predict by other means given complex particle-to-particle interactions, such as those which might occur, for example, between a mixture of variable-geometry particles in a diluted catalyst charge.
  • the present invention addresses the above-described issues and requirements by employing combinatorial weighing machines to blend and prepare distinct and separate batches, or charges, of mixed solid materials, each comprising at least one solid catalyst material or solid inert material, in predetermined amounts.
  • the batches of mixed solid materials are collected and later loaded into the tubes of a tubular reactor to form the various desired reaction zones to perform the desired chemical reactions.
  • the present invention provides a method for blending and loading solid material into the tubes of a shell and tube reactor.
  • the method involves identifying a packing schedule which lists the types and amounts of solid materials needed to form different batches of solid materials for arranging in the tubes and forming desired regions in the shell and tube reactor.
  • Each of the batches comprises one or more materials selected from the group consisting of: solid catalyst materials, solid inert materials, and blends thereof.
  • the present method next requires using a combinatorial weighing machine to produce the different batches, and the types and amounts of solid catalyst materials and solid inert materials blended for each batch of solid materials are selected based on the packing schedule.
  • Each of the batches of solid materials is collected in a plurality of containers, and each container contains the same amount and proportion of the one or more solid materials, where the amount is determined based upon the packing schedule.
  • Each of said plurality of containers comprises a total number of containers which is determined by the number and size of the tubes of the shell and tube reactor.
  • the present method includes loading the batches of solid materials from each of the containers into corresponding tubes of the shell and tube reactor, according to a predetermined order dictated by the packing schedule, to form the desired regions within the reactor consistently and homogeneously.
  • the combinatorial weighing machine may comprise adjustable vibrating means for changing the rate at which solid materials are moved through the machine and blended with one another.
  • the combinatorial weighing machine may comprise dust collection means for collecting and removing dust from the solid materials, thereby preventing unwanted accumulation of dust in the tubes of the shell and tube reactor.
  • the containers may be bags and a bagging machine may be used with the combinatorial weighing machine to accomplish the step of collecting each of the batches of solid materials in a plurality of containers.
  • the step of loading the batches of solid materials from each of said containers into corresponding tubes of the shell and tube reactor is accomplished using a solids loading machine having one or more tubular members aligned with corresponding tubes of the shell and tube reactor.
  • the method of the present invention may further be applied to load a reactor for two-stage oxidation of an alkene to form a corresponding unsaturated carboxylic acid.
  • a packing schedule is selected which provides a list of types and amounts of materials required to perform two-stage oxidation of an alkene to form a corresponding unsaturated carboxylic acid, and the desired regions comprise a first reaction stage wherein the alkene is converted to an unsaturated aldehyde and a second reaction stage wherein the unsaturated aldehyde is further converted to the corresponding unsaturated carboxylic acid.
  • the first reaction stage may comprise at least one catalyst comprising a mixed metal oxide and being capable of catalyzing the conversion of an alkene to an unsaturated aldehyde
  • the second reaction stage may comprise at least one catalyst comprising a mixed metal oxide and being capable of catalyzing the conversion of an unsaturated aldehyde to an unsaturated carboxylic acid.
  • Either or both of the first and second reaction stages may comprise one or a plurality of reaction zones.
  • FIG. 1 is a schematic elevational view of a single tube of a shell and tube reactor in which a 2-stage, 3-zone catalyst packing schedule has been created using the method of the present invention
  • FIG. 2A is a schematic elevational view of a single tube of a shell and tube reactor in which a 2-stage, 4-zone catalyst packing schedule has been created using the method of the present invention
  • FIG. 2B is a top plan view of a catalyst clip used to retain the solid materials in the tube of FIGS. 1 and 2A ;
  • FIG. 3 is a schematic representation of the combinatorial weighing machine system with dust collector and bagger options which is used in accordance with the method of the present invention.
  • the method of the present invention is suitable for blending and loading solid materials into vessels, such as into the tubes of shell and tube reactors, in a manner which maximizes compositional homogeneity and consistency of quantities and configurations of the blended solid materials.
  • the solid materials comprise one or more solid catalyst materials, one or more solid inert materials, or blends thereof.
  • the present invention provides a method for blending and loading solid material into the tubes of a shell and tube reactor.
  • the method involves identifying a packing schedule which lists the types and amounts of solid materials needed to form different batches of solid materials for arranging in the tubes and forming desired regions in the shell and tube reactor.
  • Each of the batches comprises one or more materials selected from the group consisting of: solid catalyst materials, solid inert materials, and blends thereof.
  • the desired regions are determined based on what types of products are desired and what starting materials are to be used, which, in turn, dictates what chemical reactions are to be performed by the reaction process. All such selections and decisions concerning which processes, products and starting materials to use, are well known and understood to practitioners in industry as persons of ordinary skill in the art who typically exercise such judgment on a routine basis early in the process design stages.
  • the method according to the present invention uses a combinatorial weighing machine to produce the different batches, and the types and amounts of solid catalyst materials and solid inert materials blended for each batch of solid materials are selected based on the packing schedule.
  • Each of the batches of solid materials is collected in a plurality of containers, and each container contains the same amount and proportion of the one or more solid materials, where the amount is determined based upon the packing schedule.
  • Each of said plurality of containers comprises a total number of containers which is determined by the number and size of the tubes of the shell and tube reactor.
  • the present method calls for loading the batches of solid materials from each of the containers into corresponding tubes of the shell and tube reactor, according to a predetermined order dictated by the packing schedule, to form the desired regions within the reactor consistently and homogeneously.
  • the method of the present invention is not limited to use with a specific reaction process, but rather, may be utilized with any known solid particulate catalysts and/or solid inert materials in numerous reaction systems.
  • catalysts and their associated oxidation production processes to which the method of the present invention is applicable include, but are not limited to:
  • the catalysts suitable for use in connection with the present invention are not especially limited to the above solid particulate catalysts (1) to (10) used for a gas-phase catalytic oxidation reactions, but other solid particulate catalysts used for other reactions such as, without limitation, ammoxidation reactions, hydrogenation reactions, and dehydrogenation reactions are also suitable in accordance with the present invention.
  • a catalyst that comprises a Group VIII noble metal, a Group IA and/or a Group IIA component as essential components, and is useful for the oxidative dehydrogenation (ODH) of alkanes to alkenes (see U.S. Pat. No. 4,788,371), such as, for example, the conversion of propane to propylene (see U.S. Patent Publication No. US 2008/0177117).
  • ODH oxidative dehydrogenation
  • a catalyst that comprises gold and palladium as essential components is useful for the production of vinyl acetate monomer (VAM) by reaction of ethylene, oxygen, and acetic acid in the gas phase (for example, see U.S. Pat. Nos. 5,808,136, 5,859,287 and U.S. Pat. No. 6,013,834).
  • VAM vinyl acetate monomer
  • catalytic reaction systems typically use particulate solid catalysts and inert materials within their tubes. While the use of blended catalyst mixtures can provide the opportunity for improved reactor productivity and yield, it has been quite difficult in practice to achieve mixtures of sufficient homogeneity to realize such benefits with large-scale commercial reaction systems. While perfect homogeneity need not be achieved, as previously understood in the art, substantial homogeneity is required.
  • Reliable blending of solids is, in general, very difficult and known methods of mixing materials tend to fall far short of producing the desired homogeneous mixtures. Homogenous blending of particulate solids is especially difficult, even more so than the blending of powdered solids.
  • blend and “mixture” are used herein interchangeably to mean a quantity of solid materials that contains more than one type of solid materials, such as, two or more catalysts which differ in composition, activity, shape, size, etc., or at least one catalyst and at least one inert material, or two or more inert materials which differ in composition, shape, size, etc.
  • combinatorial weighing machine(s) to produce various blends and mixtures of solid materials simultaneously accomplishes the combination of the desired amounts of each type of solid material, as well as sufficient mixing of the solid materials without subsequent mechanical mixing or stirring of the solids after they are combined.
  • the bulk catalyst loaders known in the art for loading catalyst materials into reactors are not able to reliably blend mixtures of solid catalysts and/or inert solids to achieve sufficient homogenous reaction zones within reactor tubes.
  • Catalyst may be purchased from commercial suppliers prepackaged in containers, such as plastic bags. As previously noted, catalyst which is prepackaged in this way allows for easier handling of catalyst and more efficient loading of catalyst materials into reactor tubes.
  • Typical weight variability of such commercially available prepackaged charges is about +/ ⁇ 5%, or roughly +/ ⁇ 120 grams per nominal 2000-gram charge weight. This is an undesirably high level of weight variability and will result in high tube-to-tube variations in reaction zone length, undesirable non-uniformity of reaction zone activities, and ultimately diminished reactor performance. Additionally, the manual process by which such prepackaged charges are prepared is time consuming, requiring between 1 and 10 minutes per bag.
  • the method of the present invention provides an extremely cost effective means for obtaining bags of catalyst which are suitable and ready for loading into the oxidation reactor. That is, the method allows for purchase of catalyst materials in bulk, which is less costly than pre-bagged catalyst, and, by utilizing the method of the present invention, thousands of bags of catalyst with extremely low weight variability per charge may be rapidly and cost-effectively produced.
  • Examples of combinatorial weighing machines that may be used in accordance with the method of the present invention include machines produced by Ishida Co., Ltd of Kyoto, Japan; Yamoto Scale Co., Ltd of Akashi, Japan; Package Machinery Co. of Stafford Springs, Conn. USA; Triangle Package Machinery of Chicago, Ill. USA; and Hassia-Redatron of Butzback, Germany. It is advantageous to install the combinatorial weighing system in a humidity controlled environment to minimize the potential for moisture absorption by the catalyst particles, as this can lead to incremental weight gain and adversely affect the determination of weights in the system scales.
  • YX-38.52DU (“R1” type) oxidation catalyst, commercially available from Nippon Kayaku of Japan, were used in this example. Each lot of catalyst comprised about 230 kg of catalyst pellets and was contained in its own uniquely-numbered drum. Samples of approximately 80 grams were taken from each drum (lot) and were independently tested in a laboratory-scale reaction system to determine propylene conversion. For comparison purposes, all samples were tested at constant conditions, using the same reaction temperature, pressure, space velocity, time-on-stream, propylene concentration, and propylene:air:steam feed ratio. The results were as follows:
  • the combinatorial weighing system used in this example is shown schematically in FIG. 3 . It is a Selectacom, Model A918H1RN, in-line weigher with optional dust collection ( 100 ), in combination with a model SB62PR vertical form/fill/seal (f/f/s) bagger ( 120 ); both machines are available from Triangle Package Machinery Company of Chicago, Ill. USA and are similar to those configured and adapted for packaging solids foods, such as dry cereals.
  • the left feed train ( 104 , 105 , 106 ) and the right feed train ( 101 , 102 , 103 ) continuously supply material to the top of weigher ( 100 ); weigher ( 100 ) surmounts the bagger ( 120 ) such that catalyst pellets move vertically downward through the weigher and exit as bagged charges ( 150 a, 150 b, 150 c ) of catalyst mixture from the bottom of the bagger.
  • the entire system is configured to use a single, common computer controller module ( 110 ). In this example, the computer controller ( 110 ) is adjusted to enable operation in the “single-product” mode.
  • Optional drum dumping units (not shown) were utilized in this example to transfer drums of catalyst into the two large feed hoppers ( 101 , 104 ) at the base of the combinatorial weighing system (five drums into each hopper).
  • material placed in hopper ( 101 ) will be referred to in this example as “Catalyst R” and material placed in hopper ( 104 ) will be referred to as “Catalyst L”.
  • conveyors ( 102 , 105 ) continuously transferred catalyst pellets from each large feed hopper to two small hoppers ( 103 , 106 ) at the top of the system. Any dust present was continuously removed from the hoppers and conveyors via an optional integrated aspirating system (not shown).
  • the small hoppers ( 103 , 106 ) transferred catalyst pellets into a set of 9 vibrating feeders ( 121 , 122 , 123 , 124 , 125 , 126 , 127 , 128 , 129 ), each adjusted independently via controller ( 110 ) to operate at specific amplitude.
  • the specific amplitude settings were as follows:
  • These vibrating feeders delivered catalyst pellets at rates dependent on their amplitude setting to accumulators ( 107 a, 107 b, 107 c, 107 d, 107 e, 107 f, 107 g, 107 h, 107 i ) with larger amplitude values delivering a greater quantity of catalyst pellets per unit time into the accumulators and smaller amplitude settings delivering a lesser quantity of catalyst pellets per unit time into the accumulators; in this specific case, the left side Feeders ( 121 , 122 , 123 , 124 ) transferred pellets of Catalyst L into four of the accumulators ( 107 a, 107 b, 107 c, 107 d ) and the right side feeders ( 125 , 126 , 127 , 128 , 129 ) transferred pellets of Catalyst R into the remaining five accumulators ( 107 e, 107 f, 107 g, 107 h, 107 i
  • the vibrating feeders were set at range of amplitude settings, rather than a single, identical amplitude setting, weight variations were intentionally incorporated into each accumulator to enhance blending; through experimentation with the system, we have determined that a variation of only about 5 and 10% in the individual amplitude settings, relative to the average setting, is sufficient to provide good results. It should also be noted that the average amplitude of the four left side feeders ( 121 , 122 , 123 , 124 ) should be greater than the average amplitude of the five right side Feeders ( 125 , 126 , 127 , 128 , 129 ) to compensate for the differing number of feeders on each side.
  • each accumulator then simultaneously transferred its contents into one of 9 scales ( 108 a, 108 b, 108 c, 108 d, 108 e, 108 f, 108 g, 108 h, 108 i ) directly below them, resulting in four scales containing Catalyst L ( 108 a, 108 b, 108 c, 108 d ) and five scales containing Catalyst R ( 108 e, 108 f, 108 g, 108 h, 108 i ).
  • the scales dropped the material into 9 of 18 holders ( 109 a, 109 b, 109 c, 109 d, 109 e, 109 f, 109 g, 109 h, 109 i, 109 j, 109 k, 109 l, 109 m, 109 n, 109 o, 109 p, 109 q, 109 r ); these steps were repeated a second time to fill the remaining 9 holders.
  • the computer controller ( 110 ) then selected an optimal subset of the 18 individual weights, which when combined, achieves the closest match to the target weight of 1020.3 grams. These selected holders then opened simultaneously to release into discharge port ( 115 ) enough pellets to create a half-charge of catalyst; the release of pellets from the selected holders into the discharge port signifies the end of a single scale cycle.
  • the vertical f/f/s bagger ( 120 ) continuously drew polyethylene film from a supply roll (not shown), shaped it into a nine inch (22.9 cm) diameter cylinder, vertically sealed the cylinder to form a tube, and then sealed the tube horizontally at the bottom edge to form a bag below discharge port ( 115 ).
  • Controller 110 was programmed to produce bags that were 12 inches (30.5 cm) in length, sufficient to hold the desired charge volume.
  • the formed bag was then filled with the aforementioned single blended charge of catalyst ( 130 ), the top was sealed horizontally, the finished bag of catalyst was cut free (the remaining edge becoming the bottom of the next bag) and the finished bag exited the bagger on a conveyor belt ( 140 ).
  • Each successive finished bag ( 150 a, 150 b, 150 c ) was visually inspected and manually placed into a storage drum (not shown). The system continued operating in this fashion, producing over 1050 bagged catalyst charges at a rate of about 35 bags/minute, until the large feed hoppers ( 101 , 104 ) were emptied.
  • Table 1B compares the measured weights of the samples to the target weight; it is evident from this data that the method of the present invention reproducibly provides catalyst charges with negligible variation in weights.
  • a homogeneous “R2Z1” catalyst mixture (75 wt % catalyst pellets/25 wt % diluent) was prepared for use in the second reaction stage of the example commercial-scale reactor.
  • This R2Z1 catalyst mixture is to be placed in the upstream zone of the second reaction stage ( 21 ) as illustrated in FIG. 1 .
  • Example 2 The same Combinatorial Weighing system described in Example 1 and illustrated in FIG. 3 was again used.
  • the specific catalyst in this example was T-202.52XS3 (R2 type) and the diluent was IB-1000 5 mm diameter inert spheres, both commercially available from Nippon Kayaku.
  • Catalyst the majority component of the catalyst mixture, was placed in the right side large feed hopper ( 101 ) at the base of the combinatorial weighing system and diluent, the minoroity component of the catalyst mixture, was placed in the left side large feed hopper ( 104 ).
  • the scale's computer controller ( 110 ) was adjusted to enable operation in the “two-product” mode and the target percentage of diluent was set to 25%. Additionally, system settings were adjusted to produce a full charge (566.5 grams target weight) per scale cycle and to use 1 scale cycle per bag.
  • conveyors ( 102 , 105 ) continuously transferred catalyst pellets and diluent from the large hoppers to the two smaller hoppers ( 103 , 106 ) at the top of the system.
  • the Left Feed Train ( 104 , 105 , 106 ) and the Right Feed Train ( 101 , 102 , 103 ) operated independently at speeds sufficient to maintain pace with the usage rate of the two streams. Any dust present was continuously removed from the hoppers and conveyors via an optional integrated aspirating system (not shown).
  • the small hoppers ( 103 & 106 ) transferred catalyst pellets into a set of 9 vibrating feeders ( 121 , 122 , 123 , 124 , 125 , 126 , 127 , 128 , 129 ), each adjusted independently via controller ( 110 ) to operate at specific amplitude.
  • the specific amplitude settings were as follows:
  • These vibrating feeders delivered catalyst pellets at rates dependent on their amplitude setting to accumulators ( 107 a, 107 b, 107 c, 107 d, 107 e, 107 f, 107 g, 107 h, 107 i ); in this specific case, the left side Feeders ( 121 , 122 , 123 , 124 ) transferred pellets of diluent into four of the accumulators ( 107 a, 107 b, 107 b, 107 d ) and the right side feeders ( 125 , 126 , 127 , 128 , 129 ) transferred pellets of Catalyst into the remaining five accumulators ( 107 e, 107 f, 107 g, 107 h, 107 i ).
  • the accumulators then simultaneously transferred their contents into 9 scales ( 108 a, 108 b, 108 c, 108 d, 108 e, 108 f, 108 g, 108 h, 108 i ) directly below them, resulting in four scales containing diluent ( 108 a, 108 b, 108 c, 108 d ) and five scales containing catalyst ( 108 e, 108 f, 108 g, 108 h, 108 i ).
  • the scales dropped the material into 9 of 18 holders ( 109 a, 109 b, 109 c, 109 d, 109 e, 109 f, 109 g, 109 h, 109 i, 109 j, 109 k, 109 l, 109 m, 109 n, 109 o, 109 p, 109 q, 109 r ); these steps were repeated a second time to fill the remaining 9 holders.
  • the computer controller ( 110 ) then selected an optimal subset of the 18 individual weights, which when combined, achieves the closest match to the target weight of 566.5 grams total charge weight, while simultaneously providing the closest match to the required weight ratio of 424.875 grams of catalyst and 141.625 grams of diluent; these selected holders then opened simultaneously to release into discharge port ( 115 ) enough particulate solids to create a single blended charge of catalyst. Additional particulate material then moved through the accumulators and scales to refill the emptied holders and the weight optimization and release cycle was repeated. As previously stated, the system was configured in this example to release a full charge (566.5 grams) of catalyst mixture per scale cycle and to use just 1 scale cycle per bag of catalyst mixture.
  • the vertical f/f/s bagger ( 120 ) continuously drew polyethylene film from a supply roll (not shown), shaped it into a nine inch (22.9 cm) diameter cylinder, vertically sealed the cylinder to form a tube, and then sealed the tube horizontally at the bottom edge to form a bag below discharge port ( 115 ).
  • Controller ( 110 ) was programmed to produce bags that were 8.5 inches (21.6 cm) in length, sufficient to hold the desired charge volume.
  • the bagger operated as in the previous example, discharging finished bags containing single, complete charges of R2Z1 catalyst mixture onto the conveyor belt. Each finished bag was visually inspected and manually placed into a storage drum.
  • Table 2 demonstrates that the measured weights of the sample charges as compared to the target charge weight are within the range of +/ ⁇ 0.11%; Table 2 also shows that the blend error for the actual catalyst mixture as compared to the 75% catalyst mixture target is not more than about 0.5%. It is therefore evident from this data that the method of the present invention (a) provides catalyst charges with negligible variation in weights and (b) produces catalyst mixtures with negligible variation in composition.
  • a ten-tube, vibratory catalyst loader of the type described in U.S. Pat. No. 6,132,157 (commercially available from Cat Tech of Deer Park, Tex.), was utilized to load test charges of material (inerts or catalyst mixture) into a set number of the ten possible reactor tubes.
  • the catalyst loader used in this example is one of several identical loaders in a set which are routinely used to load catalyst into commercial scale reactors.
  • the loader comprises a horizontal vibrating tray with ten sequentially numbered, parallel lanes. These lanes are aligned with ten adjacent reactor tubes during the loading operation.
  • the catalyst loader's lanes are sequentially numbered 1 through 10, with lanes 1 and 10 being the outermost lanes located at the edge of the tray, and lanes 5 and 6 being the innermost lanes, located in the center of the tray.
  • These experiments were performed by placing the loader on the top tubesheet of a commercial-scale oxidation reactor with the same design and tube size (25 mm inside diameter) as the reactor to be loaded.
  • the drop rate of material (catalyst, inert and/or mixtures thereof) in each test trial was controlled by adjusting the vibration frequency of the loader to a specific numbered setting using the loader's built-in digital controller. In this way, the exact settings for the particular catalyst loader in use can be determined and recorded.
  • the term “drop time” refers to the elapsed time period that begins with the first particle falling from the catalyst loader's tray into a given reactor tube and ends when the last particle falls from the catalyst loader's tray into that same reactor tube.
  • the “outage” i.e., the topmost elevation of the accumulated material in the tube—is manually measured to verify that the intended quantity of material and packing density has been obtained.
  • a catalyst loader vibration setting of 40 might be an appropriate starting point for testing.
  • a first R2Z1 catalyst charge was transferred through Lane 1 of the loader in a total time of 56 seconds, which is equivalent to a drop rate of 118 seconds/liter.
  • the resulting zone length was determined to be 968 mm; as compared to the target length of 1000 mm, this represented an average zone length variation of ⁇ 3.2%.
  • the controller setting was adjusted to 47, which transferred the catalyst charge more quickly. More particularly, a second R2Z1 catalyst charge was transferred through Lane 3 of the loader, with the controller setting on 47, in a total time of 39 seconds, which is equivalent to a drop rate of 81 seconds/liter.
  • the resulting zone length was determined to be 984 mm; as compared to the target length of 1000 mm, this represented a reduced average zone length variation of ⁇ 1.6%.
  • the controller setting was next adjusted to 48, thereby transferring the catalyst mixture just a little more quickly.
  • a third and a fourth R2Z1 catalyst charge were simultaneously transferred through Lanes 4 and 5, respectively, of the loader in a total time of 36 seconds, which is equivalent to a drop rate of 75 seconds/liter.
  • the resulting average zone length was determined to be 981 mm; as compared to the target length of 1000 mm, this represented an average zone length variation of ⁇ 1.9%. Because there were now two length measurements, it was also possible to assess individual tube zone length variability against the average zone length value. In this case, the individual variability was just 0.16%, which is well within the desired range of not more than 0.5%.
  • a final test drop was performed, this time using four R2Z1 catalyst charges.
  • the catalyst loader controller setting was maintained at the setting of 48.
  • Each of the four test charges were simultaneously transferred through Lanes 6, 7, 9, and 10, respectively, of the catalyst loader in a time of 37 seconds, which is equivalent to a drop rate of 77 seconds/liter.
  • the resulting average zone length was determined to be 975 mm; as compared to the target length of 1000 mm, this represented an average zone length variation of ⁇ 2.5%.
  • the individual tube variability as compared to the average zone length was not more than ⁇ 0.37%, which is well within the desired range (not more than 0.5%).
  • multi-tube vibratory catalyst loaders wherein catalyst is conveyed across a tray and into a series of adjacent tubes, may also experience variation in the drop rate across the lanes of the tray, with the outer lanes of the tray tending to drop the catalyst at a different rate than the lanes nearest the center of the tray.
  • a commercial-scale single reactor shell (SRS-type) oxidation reactor is to be used to produce acrylic acid from propylene.
  • the specific SRS oxidation reactor of this example comprises over 25,000 identical tubes.
  • FIG. 1 represents a single tube from this reactor, with a diameter of 1 inch (25.4 mm) and a length of 26 feet (7925 mm).
  • the example reactor is operated in an “upflow” configuration—that is, in operation, reactants will be introduced from the bottom of each tube and flow vertically upward; products will exit each reactor tube at the top.
  • the first reaction stage (R1) lies between the bottom tubesheet ( 1 ) and the intermediate tubesheet ( 15 ) in each tube; the second reaction stage (R2) lies between the intermediate tubesheet ( 15 ) and the top tubesheet ( 31 ) in each tube.
  • This three catalyst zone packing schedule comprises a single catalyst zone for the first reaction stage (R1) and two catalyst zones of differing activity for the second reaction stage (R2), with an interstage zone comprising solid inert material positioned between the first and second reaction stages (R1, R2).
  • cooling salt enters the lower portion of the reactor shell at a point above bottom tubesheet ( 1 ), flows around the tubes and exits the middle portion of the reactor shell at a point below intermediate tubesheet ( 15 ); in the R2 salt circulation, cooling salt enters the middle portion of the reactor shell at a point above the intermediate tubesheet ( 15 ), flows around the tubes and exits the upper portion of the reactor shell at a point below the top tubesheet ( 31 ).
  • a co-current cooling salt circulation is referred to as a co-current cooling salt circulation.
  • Pre-blended charges of particulate solids material for each zone within the tube shown in FIG. 1 are prepared according to the method of the present invention, and are placed into bags for ease of handling, as described in Examples 1 and 2. Each tube is to be loaded in the following manner, to achieve the packing schedule illustrated in FIG. 1 :
  • a catalyst clip ( 2 ) of the type shown in FIG. 2 b and commercially available from Deggendorfer Werft and Eisenbau GmbH of Germany is first placed at the bottom of each tube to hold the catalyst in-place within each tube.
  • a multi-tube, vibratory catalyst loader of the type described in U.S. Pat. No. 6,132,157 (commercially available from Cat Tech of Deer Park, Tex.), is utilized to simultaneously load charges of material (inerts or catalyst mixture) into each of ten reactor tubes at one time.
  • material inerts or catalyst mixture
  • this example focuses on the operation of a single catalyst loader, it will be evident to one of ordinary skill that the task of loading tubes in a large reactor can be performed more quickly when multiple catalyst loaders are employed at the same time. While the optimal number of loaders that can be operated simultaneously will vary with the size of the reactor and the physical dimensions of the loader itself, it is common for between five and ten catalyst loaders to be operated simultaneously during catalyst installation.
  • the drop rate of solid material (catalyst mixture or inert) in each step is controlled by adjusting the vibration frequency of the loader to the previously-determined target value identified in drop testing.
  • the “outage”—or topmost elevation of the accumulated material in the tube— is measured to verify that intended quantity of material and packing density has been obtained.
  • Measurement of pressure drop (“dP”) on a random sampling of tubes may also be performed to assure tube-to-tube uniformity. If either of these measurements indicates an appreciable error in loading, the non-compliant charge of material may be removed and a fresh charge loaded to correct the error.
  • the aforementioned catalyst loader is used to place a layer of 218 grams of inert material (6.4 mm diameter Denstone 57® catalyst bed supports, available from Norton Chemical Process Products Corp., of Akron, Ohio) on top of clip ( 2 ), to form preheating zone ( 3 ).
  • R1Z1 catalyst mixture comprises 100 wt % YX-38.52 DU catalyst, manufactured by Nippon Kayaku; preparation of R1Z1 charges has been previously described in Example 1.
  • the IS inert material comprises 7.5 mm diameter by 6 mm long stainless steel Raschig rings.
  • the second reaction stage (R2) is loaded. Again using the vibratory catalyst loader, two-catalyst zones ( 21 and 22 ) are sequentially loaded into each tube to form the second reaction stage. A bagged charge of approximately 566 grams of “R2Z1” catalyst mixture is placed into the catalyst loader and transferred to the tube at a drop rate of 77 seconds/liter to form catalyst zone ( 21 ) within the second reaction stage; this catalyst zone occupies the 1000 mm of tube length directly above inert material ( 16 ).
  • R2Z1 catalyst mixture comprises a homogenous blend of 75 wt % T202.52XS3 catalyst, manufactured by Nippon Kayaku, and 25 wt % 1B-1000 (5.2 mm diameter spheres) diluent, also available from Nippon Kayaku; preparation of R2Z1 charges has been previously described in Example 2.
  • R2Z2 catalyst mixture comprises 100 wt % T202.52XS3 catalyst, manufactured by Nippon Kayaku, and was prepared in essentially the same manner as used to prepare charges of R1Z1 catalyst.
  • inert material ( 32 ) is loaded on top of catalyst zone ( 22 ) by hand (although the aforementioned vibratory catalyst loader could be used if desired); this inert material forms the “exit cooling zone” and generally occupies the 270 mm of tube length directly above catalyst zone ( 22 ).
  • inert material ( 32 ) comprises 6.4mm diameter Denstone 57® catalyst bed supports, available from Norton Chemical Process Products Corp., of Akron, Ohio.
  • a final measurement of dP on a random sampling of tubes is performed to assure tube-to-tube uniformity.
  • the quantity of inert material ( 32 ) may be increased or decreased, as appropriate, to provide a final adjustment to the dP of the tube.
  • the repacked reactor was then put into commercial operation producing acrylic acid under the following operating conditions, whereby it was demonstrated that acrylic acid was produced stably, for a long time at excellent yield:
  • a four zone catalyst packing schedule (see FIG. 2 a ) was developed for use in another SRS-type commercial reactor for the production of acrylic acid from propylene.
  • propylene is converted to acrolein in a first reaction stage, followed by the conversion of acrolein to acrylic acid in a second reaction stage.
  • the four zone packing schedule of this example comprised two catalyst zones of differing activity for the first reaction stage, and two catalyst zones of differing activity for the second reaction stage.
  • ACF4 and ACS6 catalysts, available from Nippon Shokubai Chemical Limited (NSCL) of Japan were utilized in this example reactor.
  • the example reactor comprised over 25,000 tubes and was operated in an “downflow” configuration—that is, in operation, reactants will be introduced from the top of each tube and flow vertically downward; products will exit each reactor tube at the bottom.
  • the first reaction stage (R1) lies between the top tubesheet ( 201 ) and the intermediate tubesheet ( 215 ) in each tube; the second reaction stage (R2) lies between the intermediate tubesheet ( 215 ) and the bottom tubesheet ( 231 ) of each tube.
  • cooling salt enters the lower portion of the reactor shell at a point above bottom tubesheet ( 231 ), flows around the tubes and exits the middle portion of the reactor shell at a point below intermediate tubesheet ( 215 ); in the R1 salt circulation, cooling salt enters the middle portion of the reactor shell at a point above the intermediate tubesheet ( 215 ), flows around the tubes and exits the upper portion of the reactor shell at a point below the top tubesheet ( 201 ).
  • a counter-current cooling salt circulation is referred to as a counter-current cooling salt circulation.
  • a catalyst clip ( 232 ) of the type shown in FIG. 2 b and commercially available from Deggendorfer Werft and Eisenbau GmbH of Germany is first placed at the bottom of each tube to hold the catalyst in-place within each tube.
  • a layer of 232 grams of 3 ⁇ 8′′ diameter spherical ceramic balls is then placed on top of clip ( 232 ), forming the cooling zone ( 233 ).
  • 1395 grams of R2Z2 catalyst mixture ( 222 ) is placed on top of cooling zone ( 233 ).
  • On top of the R2Z2 catalyst mixture ( 222 ) is next placed a layer of 616 grams of R2Z1 catalyst mixture ( 221 ).
  • Interstage zone ( 216 ) Next is placed a layer of 635 grams of 1 ⁇ 4′′1 ⁇ 4′′ ⁇ 0.03′′ wall thickness stainless steel Raschig rings, forming the Interstage zone ( 216 ) for this particular packing schedule. Above interstage zone ( 216 ) is placed a layer of 986 grams of R1Z2 catalyst mixture ( 212 ). Finally, a layer of 447 grams of R1Z1 catalyst mixture ( 211 ) is placed on top of the R1Z2 catalyst ( 212 ) to complete the filling of the tube.
  • a multi-tube, vibratory catalyst loader of the type described in U.S. Pat. No. 6,132,157 (commercially available from Cat Tech of Deer Park, Tex.), is utilized to simultaneously load charges of material (catalyst mixture or inerts) into each of ten reactor tubes at one time.
  • material catalog or inerts
  • individual charges of catalyst, raschig rings, and ceramic balls are prepared in advance using the method of the present invention and are placed into individual sealed bags for ease of handling.
  • Table 4 summarizes the activity involved in the use of a combinatorial weighing system in accordance with the inventive method:
  • the total time to produce these more than 156,000 bags was just 115.5 hours, including time spent filling hoppers, programming the system controller, and cleaning the system between charges—resulting in an overall average operating speed for the system of more than 25 bags/minute. Random sampling indicated that all charge weights were within +/ ⁇ 3 grams of the target weight, equivalent to not more than +/ ⁇ 1% by weight variability based on the total desired weight of each bag. This demonstrates that the substantial number of catalyst charges having sufficient homogeneity of amount and composition that is needed for a commercial scale reaction system can be quickly and efficiently produced using the method of the present invention.
  • the inventive method can be used to prepare a “hybrid” catalyst blend comprising 60 wt % ACF7 catalyst (available from NSCL) and 40 wt % YX-129 catalyst (available from Nippon Kayaku), both of which are suitable catalysts for use in the first reaction stage of a propylene oxidation reactor.
  • a “hybrid” catalyst blend would be suitable for loading into the first reaction stage of the reactor to form the single catalyst zone ( 11 ), in accordance with the 3-reaction zone packing schedule illustrated in FIG. 1 and discussed hereinabove.
  • Such a hybrid catalyst blend is not available commercially, but can be produced through the use of a combinatorial weighing system, in accordance with the method of the present invention.
  • This hybrid catalyst blend would be useful in the commercial-scale production of acrylic acid from propylene, in the first reaction zone of the oxidation reactor, because it would maximize desirable features such as catalyst service life and selectivity of one of the commercial catalysts, while minimizing undesirable features such as molybdenum sublimation in the other commercial catalyst. It is envisioned that similar blends ranging from about 40 to 75 wt % ACF7 catalyst might also be beneficially utilized in the first reaction stage of the 3-reaction zone packing schedule illustrated in FIG. 1 .
  • the inventive method can be used to prepare a “hybrid” catalyst blend comprising 50 wt % YX-38 catalyst (available from Nippon Kayaku) and 50 wt % ACF4 catalyst (available from NSCL), both of which are suitable catalysts for use in the first reaction stage of a propylene oxidation reactor.
  • a “hybrid” catalyst blend would be suitable for loading into single catalyst zone ( 11 ) in accordance with the 3-reaction zone packing schedule illustrated in FIG. 1 .
  • Such a hybrid catalyst blend is not available commercially, but can be produced through the use of a combinatorial weighing system, in accordance with the method of the present invention.
  • This hybrid catalyst blend would be useful in the commercial-scale production of acrylic acid from propylene as it maximizes desirable features such as catalyst service life and selectivity of one commercial catalyst, while minimizing undesirable features such as molybdenum sublimation in the other commercial catalyst. It is envisioned that similar blends ranging from about 30 to 70 wt % YX-38 catalyst might also be beneficially utilized in the first reaction stage of the 3-reaction zone packing schedule illustrated in FIG. 1 .

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • General Physics & Mathematics (AREA)
  • Devices And Processes Conducted In The Presence Of Fluids And Solid Particles (AREA)
  • Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
  • Catalysts (AREA)
US12/928,212 2009-12-09 2010-12-07 Method for blending and loading solid catalyst material into tubular structures Abandoned US20110131930A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/928,212 US20110131930A1 (en) 2009-12-09 2010-12-07 Method for blending and loading solid catalyst material into tubular structures

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US28383309P 2009-12-09 2009-12-09
US12/928,212 US20110131930A1 (en) 2009-12-09 2010-12-07 Method for blending and loading solid catalyst material into tubular structures

Publications (1)

Publication Number Publication Date
US20110131930A1 true US20110131930A1 (en) 2011-06-09

Family

ID=43558200

Family Applications (1)

Application Number Title Priority Date Filing Date
US12/928,212 Abandoned US20110131930A1 (en) 2009-12-09 2010-12-07 Method for blending and loading solid catalyst material into tubular structures

Country Status (9)

Country Link
US (1) US20110131930A1 (ko)
EP (1) EP2332641A1 (ko)
JP (1) JP2011121048A (ko)
KR (1) KR20110065374A (ko)
CN (1) CN102101033A (ko)
BR (1) BRPI1005664A2 (ko)
MX (1) MX2010013227A (ko)
SG (1) SG172557A1 (ko)
TW (1) TW201124205A (ko)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110315078A1 (en) * 2010-06-29 2011-12-29 Hon Hai Precision Industry Co., Ltd. Coating system
WO2021048373A1 (de) * 2019-09-13 2021-03-18 Hte Gmbh The High Throughput Experimentation Company Verfahren zur befüllung von reaktoren und zur untersuchung von katalysatoren
US11261033B2 (en) * 2018-06-27 2022-03-01 Yamato Scale Co., Ltd. Combination weighing device

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3112014A1 (en) * 2015-06-30 2017-01-04 Shell Internationale Research Maatschappij B.V. Method of loading a particulate material into a reactor
LU93012B1 (en) * 2016-04-04 2017-11-08 Cppe Carbon Process & Plant Eng S A En Abrege Cppe S A Sulfur dioxide removal from waste gas
AU2017268362B2 (en) * 2016-05-18 2019-07-18 Usa Debusk Llc Device for removing catalyst and other material from refinery and petrochemical reactors and other vessels
CN110841495B (zh) * 2019-11-05 2022-05-31 河钢股份有限公司承德分公司 一种钒钛和普通铁精粉精准混匀系统及方法

Citations (64)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3833649A (en) * 1970-10-23 1974-09-03 Nippon Catalytic Chem Ind Process for producing unsaturated carboxylic acids
US3864280A (en) * 1972-06-19 1975-02-04 Chevron Res Catalyst for a n-butane oxidation to maleic anhydride
US3886092A (en) * 1971-10-19 1975-05-27 Nippon Catalytic Chem Ind Process for producing unsaturated carboxylic acids
US3909457A (en) * 1972-12-12 1975-09-30 Basf Ag Supported catalyst for the oxidation of o-xylene or naphthalene into phthalic anhydride
US3972920A (en) * 1973-06-11 1976-08-03 Mitsubishi Rayon Co., Ltd. Process for producing unsaturated aldehydes, unsaturated fatty acids or conjugated dienes
US3985266A (en) * 1975-08-13 1976-10-12 K-Tron Corporation Apparatus for controlling the feed rate and batch size of a material feeder
US4017521A (en) * 1972-06-19 1977-04-12 Chevron Research Company Process for the manufacture of maleic anhydride using high surface area catalyst
US4051180A (en) * 1976-01-02 1977-09-27 The Standard Oil Company Preparation of acrylic acid and methacrylic acid
US4123453A (en) * 1971-02-04 1978-10-31 The Standard Oil Company Process for the manufacture of acrylonitrile and methacrylonitrile
US4176234A (en) * 1971-02-04 1979-11-27 Standard Oil Company Process for the oxidation of olefins to aldehydes and acids
US4182907A (en) * 1971-02-04 1980-01-08 The Standard Oil Company (Ohio) Process for the oxidation of olefins to aldehydes and acids
US4256783A (en) * 1977-07-13 1981-03-17 Nippon Skokubei Kagaku Kogyo Co., Ltd. Catalytic vapor phase oxidation reactor apparatus
US4285602A (en) * 1979-05-14 1981-08-25 Union Carbide Corporation Method and apparatus for the blending of granular materials
US4323703A (en) * 1971-02-04 1982-04-06 Standard Oil Company Process for the oxidation of olefins to aldehydes and acids
US4402349A (en) * 1978-11-16 1983-09-06 Basf Aktiengesellschaft Process and apparatus for charging tubular reactors with granular solids, more particularly catalysts
US4402643A (en) * 1981-02-18 1983-09-06 Ppg Industries, Inc. Catalyst loader
US4419270A (en) * 1980-06-26 1983-12-06 Nippon Shokubai Kagaku Kogyo Co. Ltd. Oxidation catalyst
US4461327A (en) * 1980-06-02 1984-07-24 Basf Aktiengesellschaft Process and arrangements for charging a tubular reactor with granular solids
US4537874A (en) * 1982-10-22 1985-08-27 Nippon Shokubai Kagaku Kogyo Co Ltd Catalyst for production of unsaturated aldehydes
US4553849A (en) * 1983-08-26 1985-11-19 Phillips Petroleum Company Method for blending solids or the like
US4568029A (en) * 1983-08-01 1986-02-04 Ppg Industries, Inc. Method and apparatus for unloading catalyst from a tubular reactor
US4569597A (en) * 1984-10-10 1986-02-11 United Utensils Company, Inc. Solids blending apparatus
US4661917A (en) * 1982-11-18 1987-04-28 Kabushiki Kaisha Ishida Koki Seisakusho Mixing combinatorial counting and weighing method, and apparatus therefor
US4701101A (en) * 1984-03-13 1987-10-20 Catalyst Technology, Inc. Modular multi-tube catalyst loading funnel
US4707460A (en) * 1985-06-05 1987-11-17 Mitsubishi Rayon Co., Ltd. Method for regenerating phosphorus-molybdenum-alkali containing oxidation catalyst
US4760153A (en) * 1985-03-26 1988-07-26 Nippon Shokubai Kagaku Kogyo Co., Ltd. Process for producing maleic anhydride
US4788371A (en) * 1987-12-30 1988-11-29 Uop Inc. Catalytic oxidative steam dehydrogenation process
US4812437A (en) * 1986-05-09 1989-03-14 Mitsubishi Petrochemical Co., Ltd. Silver-deposited catalyst for production of ethylene oxide
US4858708A (en) * 1987-09-11 1989-08-22 Ishida Scales Mfg. Co. Ltd. Combinatorial weighing apparatus
US4907892A (en) * 1989-02-02 1990-03-13 Fuller Company Method and apparatus for filling, blending and withdrawing solid particulate material from a vessel
US4978227A (en) * 1986-04-03 1990-12-18 Fuller Company Blender for solid particulate material
US5050064A (en) * 1989-12-06 1991-09-17 E. I. Du Pont De Nemours And Company Method for controlling the blending of solids with a computer
US5145824A (en) * 1991-01-22 1992-09-08 Shell Oil Company Ethylene oxide catalyst
US5169820A (en) * 1990-03-16 1992-12-08 Nippon Shokubai Kagaku Kogyo Co., Ltd. Catalyst for producing phthalic anhydride
US5222533A (en) * 1990-10-10 1993-06-29 Basf Corporation Nozzle for use in a catalyst unloader
US5228484A (en) * 1991-06-20 1993-07-20 Catalyst Technology, Inc. Air lance reel for catalyst unloading of tubular reactors
US5395812A (en) * 1992-02-27 1995-03-07 Nippon Shokubai Co., Ltd. Silver catalyst for production of ethylene oxide and method for production of the catalyst
US5446004A (en) * 1993-02-03 1995-08-29 Basf Aktiengesellschaft Multimetal oxide compositions
US5496787A (en) * 1993-01-29 1996-03-05 Mitsubishi Chemical Corporation Process for producing a vanadium-phosphorus oxide catalyst precursor
US5504052A (en) * 1994-12-02 1996-04-02 Scientific Design Company, Inc. Silver catalyst preparation
US5626455A (en) * 1994-01-27 1997-05-06 Basf Corporation Ethylene oxide catalyst loading device
US5808136A (en) * 1995-01-23 1998-09-15 Degussa Aktiengesellschaft Catalyst, method of its production and its use for the production of vinyl acetate monomer
US5859287A (en) * 1997-10-30 1999-01-12 Celanese International Corporation Process for preparing vinyl acetate utilizing a catalyst comprising palladium, gold, and any of certain third metals
US5959143A (en) * 1995-03-03 1999-09-28 Nippon Kayaku Kabushiki Kaisha Catalysts and process for the preparation thereof
US5959124A (en) * 1996-04-01 1999-09-28 Nippon Shokubai Co., Ltd. Method of preparing maleic anhydride by vapor phase oxidation of hydrocarbon
US5962816A (en) * 1996-05-06 1999-10-05 Multipond Wagetechnik Gmbh Combinatorial weighing apparatus
US5994580A (en) * 1996-10-21 1999-11-30 Toagosei Co., Ltd. Process for producing acrylic acid
US6013834A (en) * 1999-03-04 2000-01-11 Celanese International Corporation Production of vinyl acetate in a catalytic reactor equipped with filter and distribution bed
US6132157A (en) * 1996-10-01 2000-10-17 Comardo; Mathis P. Catalytic reactor charging system and method for operation thereof
US6170670B1 (en) * 1997-01-23 2001-01-09 Nippon Shokubai Co., Ltd. Methods of and apparatus for feeding granular material
US6182716B1 (en) * 1999-07-08 2001-02-06 Philip St, Inc. Catalyst unloading device
US6268571B1 (en) * 2000-06-23 2001-07-31 David Benyukhis Counting and combinatorial weighing method and apparatus
US6384274B1 (en) * 1998-09-27 2002-05-07 Rohm And Haas Company Single reactor process for preparing acrylic acid from propylene having improved capacity
US20020136678A1 (en) * 2001-01-25 2002-09-26 Nippon Shokubai Co., Ltd. Fixed-bed shell-and-tube reactor and its usage
US6639106B1 (en) * 1999-07-23 2003-10-28 Rohm And Haas Company Process for preparing and purifying acrylic acid from propylene having improved capacity
US6675844B2 (en) * 2001-05-16 2004-01-13 Bayer Aktiengesellschaft Method of loading moist, sticky bulk material into a fluid pervious container
US6694802B1 (en) * 2000-09-22 2004-02-24 Mathis P. Comardo Delta P testing system for tube and shell type catalytic reactors
US6723171B2 (en) * 2001-01-25 2004-04-20 Nippon Shokubai Co., Ltd. Process for extracting solid material from shell-and-tube reactor
US6981529B2 (en) * 2002-06-28 2006-01-03 Catalyst Services, Inc. Measuring catalyst(s) for filling reactor tubes in reactor vessels
US7038079B2 (en) * 2002-08-08 2006-05-02 Nippon Shokubai Co., Ltd. Method for production of acrylic acid
US20060243342A1 (en) * 2005-04-08 2006-11-02 Degussa Ag Method for filling apparatuses with solids
US20070199741A1 (en) * 2004-07-02 2007-08-30 Kenji Noumi Combined Weighing Apparatus
US20080177117A1 (en) * 2006-10-16 2008-07-24 Abraham Benderly Integrated catalytic process for converting alkanes to alkenes and catalysts useful for same
US20090112367A1 (en) * 2007-03-01 2009-04-30 Decourcy Michael Stanley Apparatus and method for dislodging and extracting solid materials from tubes

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA982142A (en) 1971-02-04 1976-01-20 Robert K. Grasselli Process for the oxidation of olefins to aldehydes and acids
JPS5324403B2 (ko) 1973-06-11 1978-07-20
JPS5339037B2 (ko) 1973-06-15 1978-10-19
IT1049403B (it) 1974-05-03 1981-01-20 Basf Ag Catalizzatore supportato per l ossidazione di o.xilene o di naftalina ad anidride ftalica
GB1579023A (en) 1976-02-10 1980-11-12 Tup Panama Sa Bedlike massage and transportation equipment
JPS6033539B2 (ja) 1981-04-16 1985-08-03 株式会社日本触媒 酸化用触媒およびその調製法
JPS5912758A (ja) 1982-07-14 1984-01-23 Sumitomo Chem Co Ltd メタクリル酸製造用触媒
JPS5976541A (ja) 1982-10-22 1984-05-01 Nippon Shokubai Kagaku Kogyo Co Ltd プロピレン酸化用触媒の製造法
IN170003B (ko) 1985-06-28 1992-01-25 Shell Int Research
JPH07116070B2 (ja) 1987-08-26 1995-12-13 株式会社日本触媒 メチルタ−シャリ−ブチルエ−テルからメタクロレインおよびメタクリル酸の製法
JPH0729056B2 (ja) 1990-03-16 1995-04-05 株式会社日本触媒 無水フタル酸製造用触媒
JPH05115783A (ja) 1991-10-24 1993-05-14 Mitsui Toatsu Chem Inc 無水マレイン酸製造用触媒およびその製造法
JP3313164B2 (ja) 1992-02-27 2002-08-12 株式会社日本触媒 エチレンオキシド製造用銀触媒およびその製造方法
JPH0751573A (ja) 1993-01-29 1995-02-28 Mitsubishi Chem Corp バナジウム−リン酸化物含有触媒前駆体の製造方法
JP3139285B2 (ja) * 1994-06-20 2001-02-26 住友化学工業株式会社 アクロレインおよびアクリル酸の製造方法
JP3502526B2 (ja) 1996-04-01 2004-03-02 株式会社日本触媒 バナジウム−リン系酸化物、その製造方法、該酸化物からなる気相酸化用触媒および炭化水素類の部分気相酸化方法
JP4081824B2 (ja) 1996-05-24 2008-04-30 東亞合成株式会社 アクリル酸の製造方法
JPH1057813A (ja) 1996-08-22 1998-03-03 Mitsubishi Chem Corp 複合金属酸化物触媒の製造方法、及び該触媒を用いるアクリル酸の製造方法
JP3924824B2 (ja) 1996-10-21 2007-06-06 東亞合成株式会社 アクリル酸の製造方法
JP4334797B2 (ja) * 2001-01-25 2009-09-30 株式会社日本触媒 固定床多管式反応器への固体粒状物の充填方法
JP2003146920A (ja) * 2001-11-07 2003-05-21 Mitsubishi Chemicals Corp アクロレインおよびアクリル酸の製造方法
AU2004311900B2 (en) * 2003-12-19 2008-10-02 Celanese International Corporation Layered support material for catalysts
DE102005013845B4 (de) * 2005-03-24 2010-04-29 Süd-Chemie AG Beschickungsvorrichtung für Rohrbündelreaktoren und Verfahren zum Betrieb der Beschickungsvorrichtung

Patent Citations (72)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3833649A (en) * 1970-10-23 1974-09-03 Nippon Catalytic Chem Ind Process for producing unsaturated carboxylic acids
US4176234A (en) * 1971-02-04 1979-11-27 Standard Oil Company Process for the oxidation of olefins to aldehydes and acids
US4323703A (en) * 1971-02-04 1982-04-06 Standard Oil Company Process for the oxidation of olefins to aldehydes and acids
US4182907A (en) * 1971-02-04 1980-01-08 The Standard Oil Company (Ohio) Process for the oxidation of olefins to aldehydes and acids
US4123453A (en) * 1971-02-04 1978-10-31 The Standard Oil Company Process for the manufacture of acrylonitrile and methacrylonitrile
US4156660A (en) * 1971-02-04 1979-05-29 The Standard Oil Company Catalyst useful for the manufacture of acrylonitrile and methacrylonitrile
US3886092A (en) * 1971-10-19 1975-05-27 Nippon Catalytic Chem Ind Process for producing unsaturated carboxylic acids
US3864280A (en) * 1972-06-19 1975-02-04 Chevron Res Catalyst for a n-butane oxidation to maleic anhydride
US4017521A (en) * 1972-06-19 1977-04-12 Chevron Research Company Process for the manufacture of maleic anhydride using high surface area catalyst
US3909457A (en) * 1972-12-12 1975-09-30 Basf Ag Supported catalyst for the oxidation of o-xylene or naphthalene into phthalic anhydride
US3972920A (en) * 1973-06-11 1976-08-03 Mitsubishi Rayon Co., Ltd. Process for producing unsaturated aldehydes, unsaturated fatty acids or conjugated dienes
US3985266A (en) * 1975-08-13 1976-10-12 K-Tron Corporation Apparatus for controlling the feed rate and batch size of a material feeder
US4051180A (en) * 1976-01-02 1977-09-27 The Standard Oil Company Preparation of acrylic acid and methacrylic acid
US4256783A (en) * 1977-07-13 1981-03-17 Nippon Skokubei Kagaku Kogyo Co., Ltd. Catalytic vapor phase oxidation reactor apparatus
US4402349A (en) * 1978-11-16 1983-09-06 Basf Aktiengesellschaft Process and apparatus for charging tubular reactors with granular solids, more particularly catalysts
US4285602A (en) * 1979-05-14 1981-08-25 Union Carbide Corporation Method and apparatus for the blending of granular materials
US4461327A (en) * 1980-06-02 1984-07-24 Basf Aktiengesellschaft Process and arrangements for charging a tubular reactor with granular solids
US4419270A (en) * 1980-06-26 1983-12-06 Nippon Shokubai Kagaku Kogyo Co. Ltd. Oxidation catalyst
US4402643A (en) * 1981-02-18 1983-09-06 Ppg Industries, Inc. Catalyst loader
US4537874A (en) * 1982-10-22 1985-08-27 Nippon Shokubai Kagaku Kogyo Co Ltd Catalyst for production of unsaturated aldehydes
US4661917A (en) * 1982-11-18 1987-04-28 Kabushiki Kaisha Ishida Koki Seisakusho Mixing combinatorial counting and weighing method, and apparatus therefor
US4568029A (en) * 1983-08-01 1986-02-04 Ppg Industries, Inc. Method and apparatus for unloading catalyst from a tubular reactor
US4553849A (en) * 1983-08-26 1985-11-19 Phillips Petroleum Company Method for blending solids or the like
US4701101A (en) * 1984-03-13 1987-10-20 Catalyst Technology, Inc. Modular multi-tube catalyst loading funnel
US4569597A (en) * 1984-10-10 1986-02-11 United Utensils Company, Inc. Solids blending apparatus
US4760153A (en) * 1985-03-26 1988-07-26 Nippon Shokubai Kagaku Kogyo Co., Ltd. Process for producing maleic anhydride
US4707460A (en) * 1985-06-05 1987-11-17 Mitsubishi Rayon Co., Ltd. Method for regenerating phosphorus-molybdenum-alkali containing oxidation catalyst
US4978227A (en) * 1986-04-03 1990-12-18 Fuller Company Blender for solid particulate material
US4812437A (en) * 1986-05-09 1989-03-14 Mitsubishi Petrochemical Co., Ltd. Silver-deposited catalyst for production of ethylene oxide
US4858708A (en) * 1987-09-11 1989-08-22 Ishida Scales Mfg. Co. Ltd. Combinatorial weighing apparatus
US4788371A (en) * 1987-12-30 1988-11-29 Uop Inc. Catalytic oxidative steam dehydrogenation process
US4907892A (en) * 1989-02-02 1990-03-13 Fuller Company Method and apparatus for filling, blending and withdrawing solid particulate material from a vessel
US5050064A (en) * 1989-12-06 1991-09-17 E. I. Du Pont De Nemours And Company Method for controlling the blending of solids with a computer
US5169820A (en) * 1990-03-16 1992-12-08 Nippon Shokubai Kagaku Kogyo Co., Ltd. Catalyst for producing phthalic anhydride
US5222533A (en) * 1990-10-10 1993-06-29 Basf Corporation Nozzle for use in a catalyst unloader
US5145824A (en) * 1991-01-22 1992-09-08 Shell Oil Company Ethylene oxide catalyst
US5228484A (en) * 1991-06-20 1993-07-20 Catalyst Technology, Inc. Air lance reel for catalyst unloading of tubular reactors
US5395812A (en) * 1992-02-27 1995-03-07 Nippon Shokubai Co., Ltd. Silver catalyst for production of ethylene oxide and method for production of the catalyst
US5496787A (en) * 1993-01-29 1996-03-05 Mitsubishi Chemical Corporation Process for producing a vanadium-phosphorus oxide catalyst precursor
US5591870A (en) * 1993-01-29 1997-01-07 Mitsubishi Chemical Corporation Process for producing a vanadium-phosphorus oxide catalyst precursor
US5446004A (en) * 1993-02-03 1995-08-29 Basf Aktiengesellschaft Multimetal oxide compositions
US5493052A (en) * 1993-02-03 1996-02-20 Basf Aktiengesellschaft Multimetal oxide compositions
US5626455A (en) * 1994-01-27 1997-05-06 Basf Corporation Ethylene oxide catalyst loading device
US5504052A (en) * 1994-12-02 1996-04-02 Scientific Design Company, Inc. Silver catalyst preparation
US5646087A (en) * 1994-12-02 1997-07-08 Scientific Design Company, Inc. Promoted silver acatalyst preparation
US5808136A (en) * 1995-01-23 1998-09-15 Degussa Aktiengesellschaft Catalyst, method of its production and its use for the production of vinyl acetate monomer
US5959143A (en) * 1995-03-03 1999-09-28 Nippon Kayaku Kabushiki Kaisha Catalysts and process for the preparation thereof
US5959124A (en) * 1996-04-01 1999-09-28 Nippon Shokubai Co., Ltd. Method of preparing maleic anhydride by vapor phase oxidation of hydrocarbon
US5962816A (en) * 1996-05-06 1999-10-05 Multipond Wagetechnik Gmbh Combinatorial weighing apparatus
US6132157A (en) * 1996-10-01 2000-10-17 Comardo; Mathis P. Catalytic reactor charging system and method for operation thereof
US6060422A (en) * 1996-10-21 2000-05-09 Toagosei Co., Ltd. Process for producing acrylic acid
US5994580A (en) * 1996-10-21 1999-11-30 Toagosei Co., Ltd. Process for producing acrylic acid
US6170670B1 (en) * 1997-01-23 2001-01-09 Nippon Shokubai Co., Ltd. Methods of and apparatus for feeding granular material
US5859287A (en) * 1997-10-30 1999-01-12 Celanese International Corporation Process for preparing vinyl acetate utilizing a catalyst comprising palladium, gold, and any of certain third metals
US6384274B1 (en) * 1998-09-27 2002-05-07 Rohm And Haas Company Single reactor process for preparing acrylic acid from propylene having improved capacity
US6013834A (en) * 1999-03-04 2000-01-11 Celanese International Corporation Production of vinyl acetate in a catalytic reactor equipped with filter and distribution bed
US6182716B1 (en) * 1999-07-08 2001-02-06 Philip St, Inc. Catalyst unloading device
US6639106B1 (en) * 1999-07-23 2003-10-28 Rohm And Haas Company Process for preparing and purifying acrylic acid from propylene having improved capacity
US6268571B1 (en) * 2000-06-23 2001-07-31 David Benyukhis Counting and combinatorial weighing method and apparatus
US6694802B1 (en) * 2000-09-22 2004-02-24 Mathis P. Comardo Delta P testing system for tube and shell type catalytic reactors
US20020136678A1 (en) * 2001-01-25 2002-09-26 Nippon Shokubai Co., Ltd. Fixed-bed shell-and-tube reactor and its usage
US20060245992A1 (en) * 2001-01-25 2006-11-02 Nippon Shokubai Co., Ltd. Fixed-bed shell-and-tube reactor and its usage
US6723171B2 (en) * 2001-01-25 2004-04-20 Nippon Shokubai Co., Ltd. Process for extracting solid material from shell-and-tube reactor
US7850928B2 (en) * 2001-01-25 2010-12-14 Nippon Shokubai Co., Ltd. Fixed-bed shell-and-tube reactor and its usage
US6675844B2 (en) * 2001-05-16 2004-01-13 Bayer Aktiengesellschaft Method of loading moist, sticky bulk material into a fluid pervious container
US7439455B2 (en) * 2002-06-28 2008-10-21 Catalyst Services, Inc. Measuring catalyst(s) for filling reactor tubes in reactor vessels
US6981529B2 (en) * 2002-06-28 2006-01-03 Catalyst Services, Inc. Measuring catalyst(s) for filling reactor tubes in reactor vessels
US7038079B2 (en) * 2002-08-08 2006-05-02 Nippon Shokubai Co., Ltd. Method for production of acrylic acid
US20070199741A1 (en) * 2004-07-02 2007-08-30 Kenji Noumi Combined Weighing Apparatus
US20060243342A1 (en) * 2005-04-08 2006-11-02 Degussa Ag Method for filling apparatuses with solids
US20080177117A1 (en) * 2006-10-16 2008-07-24 Abraham Benderly Integrated catalytic process for converting alkanes to alkenes and catalysts useful for same
US20090112367A1 (en) * 2007-03-01 2009-04-30 Decourcy Michael Stanley Apparatus and method for dislodging and extracting solid materials from tubes

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20110315078A1 (en) * 2010-06-29 2011-12-29 Hon Hai Precision Industry Co., Ltd. Coating system
US11261033B2 (en) * 2018-06-27 2022-03-01 Yamato Scale Co., Ltd. Combination weighing device
WO2021048373A1 (de) * 2019-09-13 2021-03-18 Hte Gmbh The High Throughput Experimentation Company Verfahren zur befüllung von reaktoren und zur untersuchung von katalysatoren
US11738316B2 (en) 2019-09-13 2023-08-29 Hte Gmbh The High Throughput Experimentation Method for filling reactors and for examining catalytic reactors

Also Published As

Publication number Publication date
SG172557A1 (en) 2011-07-28
BRPI1005664A2 (pt) 2013-04-09
KR20110065374A (ko) 2011-06-15
EP2332641A1 (en) 2011-06-15
TW201124205A (en) 2011-07-16
MX2010013227A (es) 2011-06-16
CN102101033A (zh) 2011-06-22
JP2011121048A (ja) 2011-06-23

Similar Documents

Publication Publication Date Title
US20110131930A1 (en) Method for blending and loading solid catalyst material into tubular structures
US6657088B2 (en) Temperature measurements in tubular reactors during treatment of fluid masses
CN101888898B (zh) 用于烯烃的催化聚合的反应器系统和方法以及该反应器系统在烯烃催化聚合中的用途
TWI313189B (en) Charging device for tube bundle reactors and method for operating the same
US8525049B2 (en) Combination weigher having reduced batch time and improved operational speed
US20110017348A1 (en) Method of loading solid particles into a fixed-bed multitubular reactor
JPS6366568B2 (ko)
US20070196253A1 (en) Device for filling tubes, containers and the like with bulk materials
US7776288B2 (en) Charging device for a tubular reactor
JP4768726B2 (ja) 接触管束の接触管を構造的に充填する方法
JP4334797B2 (ja) 固定床多管式反応器への固体粒状物の充填方法
US7731916B2 (en) Method of charging catalyst tubes of a bundle of catalyst tubes in a structured fashion
JP2006142297A (ja) 触媒充填方法および触媒充填機
JPH11333282A (ja) 触媒充填機
JPH039770B2 (ko)
EP1397199A1 (en) Method of loading a particulate solid into a vessel
US20210381879A1 (en) Combinatorial weighing device
US20070058486A1 (en) Rotary processor
US20020136678A1 (en) Fixed-bed shell-and-tube reactor and its usage
CA2123125A1 (en) Conveyor trough apparatus for loading catalyst pellets into vertical, tubular reactors
JP2005325044A (ja) 多管式反応器のパイロットテスト方法
US20200353434A1 (en) Methods and systems for sock-loading fixed bed reactors
JP4194359B2 (ja) 気相接触酸化方法
US5558484A (en) Apparatus for dispensing particulate material
JP7088578B1 (ja) 食料混合装置

Legal Events

Date Code Title Description
STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION