US20080247900A1 - Component for Machine Structure, Method of Producing the Same and Material for Induction Hardening - Google Patents
Component for Machine Structure, Method of Producing the Same and Material for Induction Hardening Download PDFInfo
- Publication number
- US20080247900A1 US20080247900A1 US11/587,731 US58773106A US2008247900A1 US 20080247900 A1 US20080247900 A1 US 20080247900A1 US 58773106 A US58773106 A US 58773106A US 2008247900 A1 US2008247900 A1 US 2008247900A1
- Authority
- US
- United States
- Prior art keywords
- mass
- chemical composition
- component
- machine structure
- induction hardening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/06—Surface hardening
- C21D1/09—Surface hardening by direct application of electrical or wave energy; by particle radiation
- C21D1/10—Surface hardening by direct application of electrical or wave energy; by particle radiation by electric induction
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/60—Ferrous alloys, e.g. steel alloys containing lead, selenium, tellurium, or antimony, or more than 0.04% by weight of sulfur
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P10/00—Technologies related to metal processing
- Y02P10/25—Process efficiency
Definitions
- This invention relates to a component for machine structure provided in at least a part thereof with a hardened layer through an induction hardening.
- a drive shaft for an automobile an input shaft, an output shaft, a crankshaft, inner and outer wheels of a constant velocity joint, a hub, a gear and so on.
- the components for machine structure such as a drive shaft for an automobile, a constant velocity joint and the like
- fatigue strengths as a characteristic of the component for machine structure such as torsional fatigue strength, bending fatigue strength, rolling fatigue strength, slip rolling fatigue strength and the like by working a hot rolled steel bar into a given shape through hot forging, cutting, cold forging and the like and then subjecting to induction hardening and tempering.
- the fatigue strength is saturated at a certain depth even in the increase of the hardening depth.
- Patent Document 1 it is attempted to refine the particle size of prior austenite by dispersing a great amount of fine TiC in the heating of the induction hardening, so that it is required to solid-solute TiC prior to the hardening, and hence it is adopted to conduct the heating above 1100° C. at the hot rolling step. For this end, it is required to raise the heating temperature in the hot rolling, so that there is a problem that the productivity is poor.
- the inventors have made various studies in order to effectively improve the fatigue strengths of steel materials through the induction hardening. Particularly, the inventors have noticed the torsional fatigue strength as a typical example of the fatigue strengths and made detail examinations thereon, and obtained the following discoveries.
- the invention is based on the above knowledge.
- a component for machine structure characterized by comprising a hardened layer through an induction hardening in at least a part thereof, in which the hardened layer has a hardness Hv of not less than 750 and an average grain size of prior austenite grains is not more than 7 ⁇ m over a full thickness of the hardened layer.
- a component for machine structure according to the item 1 which has a chemical composition comprising C: 0.3-1.5 mass %, Si: 0.05-3.0 mass %, Mn: 0.2-2.0 mass %, Al: not more than 0.25 mass %, Ti: 0.005-0.1 mass %, Mo: 0.05-0.6 mass %, B: 0.0003-0.006 mass %, S: not more than 0.1 mass % and P: not more than 0.10 mass %, and the remainder being Fe and inevitable impurities, and satisfying at least one of the following equations (1)-(3):
- a component for machine structure according to item 2 wherein a content of Al in the chemical composition is Al: 0.005-0.25 mass %.
- W not more than 1.0 mass %
- Ca not more than 0.005 mass %
- Mg not more than 0.005 mass %
- Te not more than 0.1 mass %
- Se not more than 0.1 mass %
- Bi not more than 0.5 mass %
- Pb not more than 0.5 mass %
- Zr not more than 0.01 mass %
- REM not more than 0.1 mass %.
- a component for machine structure according to item 1 which has a chemical composition comprising C: 0.3-1.5 mass %, Si: 0.05-3.0 mass %, Mn: 0.2-2.0 mass %, Al: not more than 0.25 mass %, Ti: 0.005-0.1 mass %, Mo: 0.05-0.6 mass %, B: 0.0003-0.006 mass %, S: not more than 0.1 mass % and P: not more than 0.10 mass % and the remainder being Fe and inevitable impurities in which the hardened layer is not subjected to a tempering.
- W not more than 1.0 mass %
- Ca not more than 0.005 mass %
- Mg not more than 0.005 mass %
- Te not more than 0.1 mass %
- Se not more than 0.1 mass %
- Bi not more than 0.5 mass %
- Pb not more than 0.5 mass %
- Zr not more than 0.01 mass %
- REM not more than 0.1 mass %.
- a method of producing a component for machine structure by subjecting at least a part of a starting material having a chemical composition comprising C: 0.3-1.5 mass %, Si: 0.05-3.0 mass %, Mn: 0.2-2.0 mass %, Al: not more than 0.25 mass %, Ti: 0.005-0.1 mass %, Mo: 0.05-0.6 mass %, B: 0.0003-0.006 mass %, S: not more than 0.1 mass % and P: not more than 0.10 mass %, and the remainder being Fe and inevitable impurities, and satisfying at least one of the following equations (1)-(3):
- an induction hardening at least once characterized in that either or both of bainite structure and martensite structure in steel microstructure of the starting material prior to the induction hardening is adjusted to not less than 10 volume %, and a ultimate temperature of the induction hardening is not higher than 1000° C.
- W not more than 1.0 mass %
- Ca not more than 0.005 mass %
- Mg not more than 0.005 mass %
- Te not more than 0.1 mass %
- Se not more than 0.1 mass %
- Bi not more than 0.5 mass %
- Pb not more than 0.5 mass %
- Zr not more than 0.01 mass %
- REM not more than 0.1 mass %.
- a material for induction hardening used for the formation of a component for machine structure having in at least a part of its surface a hardened layer with an average grain size of prior austenite of not more than 7 ⁇ m through an induction hardening characterized by having a chemical composition comprising C: 0.3-1.5 mass %, Si: 0.05-3.0 mass %, Mn: 0.2-2.0 mass %, Al: not more than 0.25 mass %, Ti: 0.005-0.1 mass %, Mo: 0.05-0.6 mass %, B: 0.0003-0.006 mass %, S: not more than 0.1 mass % and P: not more than 0.10 mass %, and the remainder being Fe and inevitable impurities, and satisfying at least one of the following equations (1)-(3):
- a material for induction hardening according to any one of items 15 to 17, wherein the chemical composition further contains one or more selected from W: not more than 1.0 mass %, Ca: not more than 0.005 mass %, Mg: not more than 0.005 mass %, Te: not more than 0.1 mass %, Se: not more than 0.1 mass %, Bi: not more than 0.5 mass %, Pb: not more than 0.5 mass %, Zr: not more than 0.01 mass % and REM: not more than 0.1 mass %.
- W not more than 1.0 mass %
- Ca not more than 0.005 mass %
- Mg not more than 0.005 mass %
- Te not more than 0.1 mass %
- Se not more than 0.1 mass %
- Bi not more than 0.5 mass %
- Pb not more than 0.5 mass %
- Zr not more than 0.01 mass %
- REM not more than 0.1 mass %.
- a material for induction hardening according to any one of items 15 to 18, wherein Mo-based precipitate is dispersed in an amount of not less than 500 per 1 ⁇ m 3 and an average particle size of the Mo-based precipitate is not more than 20 nm.
- FIG. 1 is a graph showing an influence of a heating temperature in an induction hardening on a grain size of prior austenite in a hardened layer with respect to Mo-added steel and Mo-free steel;
- FIG. 2 is a transmission electron microphotograph of a fine precipitate (Mo-based precipitate) effective for super-refining ⁇ grains;
- FIG. 3 is a graph showing a relation between an average grain size of prior austenite and a torsional fatigue strength with respect to Mo-added steel and Mo-free steel;
- FIG. 4 is a graph showing a relation between an average grain size of prior austenite and a torsional fatigue strength with or without tampering
- FIG. 5 is a partial section view of a constant velocity joint
- FIG. 6 is a section view showing a hardened texture layer in an inner wheel of a constant velocity joint.
- the components for machine structure according to the invention are a drive shaft for an automobile, an input shaft, an output shaft, a crankshaft, inner and outer wheels of a constant velocity joint, a hub, a gear and so on and have various forms and structures every the component.
- they have particularly a hardened layer subjected to a hardening in its portion requiring fatigue strengths or a whole thereof, and the hardened layer is important to have a hardness Hv of not less than 750 and an average grain size of prior austenite of not more than 7 ⁇ m over a full thickness of the hardened layer.
- grain size of the prior austenite in the hardened layer is required to be not more than 7 ⁇ m, preferably not more than 6 ⁇ m, more preferably not more than 5 ⁇ m, further preferably not more than 3 ⁇ m. Because, the intergranular strength becomes considerably strong as the grain size is refined.
- the intergranular strength is not increased and becomes a rate-determining step and hence it is not expected to further increase the strength.
- the intergranular strength is considerably increased by refining the grain size, so that it is expected to further increase the strength.
- the average grain size of the prior austenite in the induction hardened portion is measured as follows.
- An outermost surface layer in the hardened layer after the induction hardening has a martensite structure of 100% as an area ratio.
- the region of 100% martensite structure continues to a certain thickness ranging from the surface of the hardened layer, but the surface area of the martensite structure violently decreases after that.
- a region ranging from the surface of the induction hardened portion to a place that the surface area of the martensite structure decreases to 98% is the hardened layer, and an average depth from the surface is a thickness of the hardened layer.
- the average grain size of the prior austenite are measured at positions of 1 ⁇ 5, 1 ⁇ 2 and 4 ⁇ 5 of the whole of the thickness from the surface, and when the average grain size of the prior austenite is 7 ⁇ m in any positions, it is defined that the average grain size of the prior austenite grains is not more than 7 ⁇ m over the full thickness.
- the average grain size of the prior austenite grains is measured by corroding a section of the hardened layer with a corroding solution, which is formed by dissolving 50 g of picric acid in 500 g of water and adding 11 g of sodium dodecylbenzene sulfonate, 1 g of ferrous chloride and 1.5 g of oxalic acid, and observing the corroded section at 5 places every each position by means of an optical microscope of from 400 magnification (area of one place: 0.25 mm ⁇ 0.225 mm) to 1000 magnification (area of one place: 0.10 mm ⁇ 0.09 mm), and then analyzing with an image analysis equipment.
- a corroding solution which is formed by dissolving 50 g of picric acid in 500 g of water and adding 11 g of sodium dodecylbenzene sulfonate, 1 g of ferrous chloride and 1.5 g of oxalic acid, and observing the corroded section at 5 places
- the thickness of the hardened layer is not less than 2 mm. It is more preferably not less than 2.5 mm, further preferably not less than 3 mm.
- the Vickers hardness Hv of the hardened layer is less than 750, the transgranular strength of the hardened layer is weak, so that even if the prior austenite grains are refined, it can not be expected to improve the fatigue strength so as to match with such a refining. That is, even when the austenite grains are refined to increase the intergranular strength as mentioned above, if the transgranular strength is not increased, the transgranular fracture becomes rate-determined step and it can not be expected to increase the static strength and fatigue strengths. In the invention, therefore, the Vickers hardness Hv of the hardened layer (corresponding to the transgranular strength) is required to be not less than 750.
- the upper limit of the Vickers hardness Hv of the hardened layer is not particularly limited, but it is preferable to be not more than 900 because when it exceeds 900, the amount of the elements added becomes large and hence the machinability of the base metal, the cold forgeability and the resistance to quenching crack lower.
- the Vickers hardness is an average of values measured when 98 N (10 kgf) is struck to a position of 1 ⁇ 5 from the surface in the thickness of the hardened layer 5 times.
- the C is an element affecting a greatest influence on the induction hardenability, and contributes to the improvement of the fatigue strengths by increasing the transgranular strength of the hardened layer and more thickening the induction hardened portion.
- the hardened layer should be considerably increased for ensuring the required torsional fatigue strength, and hence the occurrence of quenching crack becomes remarkable and it is difficult to obtain a bainite structure as mentioned later.
- the C amount is preferable to be 0.3-1.5 mass %.
- Si increases the transgranular strength of the hardened layer and contributes to the improvement of the fatigue strengths. Further, it is an element useful for obtaining the bainite structure as mentioned later. From this meaning, it is preferable to be not less than 0.05 mass %. However, when it exceeds 3 mass %, it is difficult to ensure the machinability and cold forgeability because ferrite is solid-solution hardened, so that it is preferable to be not more than 3 mass %.
- Mn is an element for improving the induction hardenability and ensuring the thickness of the hardened layer.
- the Mn amount is preferable to be not less than 0.2 mass %, further preferably not less than 0.3 mass %.
- the residual austenite increases after the hardening, which is easy to bring about the lowering of the hardness of the surface layer portion. Therefore, it is preferable to be not more than 2.0 mass %.
- the Mn amount is too large, the machinability tends to become disadvantageous, so that it is more preferably not more than 1.2 mass %, further preferably not more than 1.0 mass %.
- Al is an element effective for the deoxidation of steel. Also, it is an element for suppressing the growth of austenite grains in the heating for the induction hardening to refine the induction hardened portion. When it exceeds 0.25 mass %, the effect is saturated and the increase of the cost is rather caused. Therefore, the Al amount is preferable to be not more than 0.25 mass %. Moreover, the above effect of Al is not developed when the amount is less than 0.001 mass %, so that the amount is more preferably not less than 0.001 mass %. Further, it is preferable to be not less than 0.005 mass %.
- Ti has an effect that it bonds to N included as an inevitable impurity to form BN with B mentioned later to thereby prevent the fadeaway of the induction hardenability. Therefore, the amount is preferable to be not less than 0.005 mass %. While, when it exceeds 0.1 mass %, a great amount of TiN is formed and tends to lower the fatigue strengths as a starting point of fatigue fracture, so that the Ti amount is preferable to be 0.005-0.1 mass %. Further preferably, it is 0.01-0.07 mass %. Moreover, in order to effectively develop the hardenability of B by surely precipitating solid-soluted N as TiN, it is preferable that the Ti and N amounts are controlled to be Ti (mass %)/N (mass %) ⁇ 3.42.
- Mo has an action that austenite is refined by promoting the formation of bainite structure after the hot working in the heating for the induction hardening to refine the hardened layer. Also, it has an action that the growth of austenite grains in the heating for the induction hardening is suppressed to refine the hardened layer. Particularly, when the heating temperature in the induction hardening is 800-1000° C., preferably 800-950° C., the growth of austenite grains can be suppressed remarkably. Further, it is an element effective for the improvement of the hardenability, so that it is also used for the adjustment of the hardenability. In addition, it has an action of suppressing the formation of a carbide to prevent the lowering of the intergranular strength.
- Mo is a very useful element for obtaining the effects of the invention, but when the amount is not less than 0.05 mass %, it is easy to render the average grain size of prior austenite in the hardened layer into not more than 7 ⁇ m, so that it is preferable to be not less than 0.05 mass %. While, when the Mo amount exceeds 0.6 mass %, the hardness of the steel material in the hot working for shaping into a component form considerably increases to lower the workability. Therefore, the Mo amount is preferably 0.05-0.6 mass %, more preferably 0.1-0.6 mass %, further preferably 0.3-0.4 mass %.
- the B is useful for refining the grain size of the prior austenite in the hardened layer when the microstructure prior to the induction hardening includes the bainite structure or martensite structure as mentioned later. Also, the addition of a slight amount improves the induction hardenability and thickens the hardened layer and hence has an effect of improving the fatigue strengths. Furthermore, it is preferentially segregated in the grain boundary to reduce P concentration segregated in the grain boundary, and hence the intergranular strength is increased to improve the fatigue strengths. However, the effects are poor when the amount is less than 0.0003 mass %. While, when it exceeds 0.006 mass %, the effects are saturated and the increase of the cost is rather caused. Therefore, the B amount is preferably 0.0003-0.006 mass %, more preferably 0.0005-0.004 mass %, further preferably 0.0015-0.003 mass %.
- S is an element forming MnS to improve the machinability of steel.
- the S amount is preferably not more than 0.1 mass %, further preferably not more than 0.06 mass %.
- the P increases the transgranular strength of the hardened layer and contributes to the improvement of the fatigue strengths. However, when the amount exceeds 0.10 mass %, it is segregated in the grain boundary to lower the intergranular strength. Therefore, the P amount is preferable to be not more than 0.10 mass %.
- the remainder other than the above elements may be Fe and inevitable impurities.
- it is particularly preferable to adjust the chemical composition so as to satisfy at least one of the following equations (1)-(3):
- the tempering treatment usually conducted after the induction hardening can be omitted.
- the temper softening is not caused, so that even if either of the equations (1) to (3) is not satisfied, Hv of not less than 750 can be satisfied in the above chemical composition range.
- Hv of not less than 750 can be satisfied in the above chemical composition range.
- the Cr is effective for the improvement of the hardenability and is an element useful for ensuring the hardened depth, and may be added.
- the Cr amount is desirable to be reduced as far as possible, but is allowed up to 2.5 mass %.
- it is not more than 1.5 mass %.
- it is preferable to be not less than 0.03 mass %.
- Cu is effective for the improvement of the hardenability and also is solid-soluted in ferrite, in which the fatigue strengths are improved by such a solid solution strengthening. Furthermore, the formation of the carbide is suppressed to control the lowering of the intergranular strength due to the carbide and improve the fatigue strengths.
- the addition amount is not more than 1.0 mass %. More preferably, it is not more than 0.5 mass %.
- the addition amount of less than 0.03 mass % is small in the effect of improving the hardenability and the effect of suppressing the lowering of the intergranular strength, so that it is desirable to be not less than 0.03 mass %.
- it is 0.1-1.0 mass %.
- Ni not more than 3.5 mass %
- Ni is an element improving the hardenability and is used in case of adjusting the hardenability. Also, it is an element suppressing the formation of the carbide to suppress the lowering of the intergranular strength due to the carbide and improve the fatigue strengths.
- Ni is a very expensive element, so that when it is added over 3.5 mass %, the cost of steel material increases, and hence the addition amount is not more than 3.5 mass %.
- the addition amount of less than 0.05 mass % is small in the effect of improving the hardenability and the effect of suppressing the lowering of the intergranular strength, so that it is desirable to be not less than 0.05 mass %.
- it is 0.1-1.0 mass %.
- Co is an element suppressing the formation of the carbide to suppress the lowering of the intergranular strength due to the carbide and improve the fatigue strengths.
- Co is a very expensive element, so that when it is added over 1.0 mass %, the cost of steel material increases, and hence the addition amount is not more than 1.0 mass %.
- the addition amount of less than 0.01 mass % is small in the effect of suppressing the lowering of the intergranular strength, so that it is desirable to be not less than 0.01 mass %.
- it is 0.02-0.5 mass %.
- Nb not more than 0.1 mass %
- Nb has an effect of improving the hardenability but also bonds to C, N in steel to act as a precipitation strengthening element. Also, it is an element improving the resistance to temper softening. The fatigue strengths are improved by these effects. However, when the amount exceeds 0.1 mass %, these effects are saturated, so that 0.1 mass % is an upper limit. Moreover, the addition amount of less than 0.005 mass % is small in the precipitation strengthening action and the effect of improving the resistance to temper softening, so that it is desirable to be not less than 0.005 mass %. Preferably, it is 0.01-0.05 mass %.
- V not more than 0.5 mass %
- the fatigue strengths are improved by these effects. However, when the amount exceeds 0.5 mass %, the effects are saturated, so that it is not more than 0.5 mass %. Moreover, the addition amount of less than 0.01 mass % is small in the effect of improving the fatigue strengths, so that it is desirable to be not less than 0.01 mass %. Preferably, it is 0.03-0.3 mass %.
- Ta not more than 0.5 mass %
- Ta may be added because there are an effect on the delay in the change of microstructure and an effect of preventing the deterioration of fatigue strengths, particularly rolling fatigue strength.
- the amount when the amount is increased over 0.5 mass %, it does not contribute to the improvement of the strength, so that it is not more than 0.5 mass %.
- it in order to develop the action of improving the fatigue strengths, it is preferable to be not less than 0.02 mass %.
- Hf may be added because there are an effect on the delay in the change of microstructure and an effect of preventing the deterioration of fatigue strengths, particularly rolling fatigue strength.
- the amount when the amount is increased over 0.5 mass %, it does not contribute to the improvement of the strength, so that it is not more than 0.5 mass %.
- it in order to develop the action of improving the fatigue strengths, it is preferable to be not less than 0.02 mass %.
- Sb may be added because there are an effect on the delay in the change of microstructure and an effect of preventing the deterioration of fatigue strengths, particularly rolling fatigue strength.
- the amount is increased over 0.015 mass %, the toughness is deteriorated, so that it is not more than 0.015 mass %, preferably not more than 0.010 mass %.
- it is preferable to be not less than 0.005 mass %.
- W is an element of improving the machinability through embrittlement action. However, when it is added over 1.0 mass %, the effect is saturated and the cost disadvantageously increases, so that it is preferable to be not more than 1.0 mass %. Moreover, W is preferable to be not less than 0.005 mass % for the improvement of the machinability.
- Ca forms a sulfide with MnS, which acts as a chip breaker to improve the machinability, so that it may be added, if necessary.
- the amount is added over 0.005 mass %, the effect is saturated and the cost increases, so that it is not more than 0.005 mass %.
- the effect of improving the machinability is small, so that it is preferable to be not less than 0.0001 mass %.
- Mg is a deoxidation element but also has an effect of improving the machinability as a stress concentration source, so that it may be added, if necessary. However, when the addition is excessive, the effect is saturated and the cost increases, so that it is not more than 0.005 mass %. Moreover, when it is less than 0.0001 mass %, the effect of improving the machinability is small, so that it is preferable to be not less than 0.0001 mass %.
- Ta not more than 0.1 mass %
- Se and Te form MnSe and MnTe through bonding with Mn, respectively, which act as a chip breaker to improve the machinability.
- the amount exceeds 0.1 mass %, the effect is saturated and the cost increases, so that each amount is not more than 0.1 mass %.
- Se amount is not less than 0.003 mass % and Te amount is not less than 0.003 mass %, respectively.
- Bi improves the machinability through the fusion, lubrication and embrittlement actions in the cutting, and may be added for this purpose. However, when it is added over 0.5 mass %, the effect is saturated but also the cost increases, so that it is not more than 0.5 mass %. Moreover, when it is less than 0.01 mass %, the effect of improving the machinability is small, so that it is preferable to be not less than 0.01 mass %.
- Pb improves the machinability through the fusion, lubrication and embrittlement actions in the cutting, and may be added for this purpose. However, when it is added over 0.5 mass %, the effect is saturated but also the cost increases, so that it is not more than 0.5 mass %. Moreover, when it is less than 0.01 mass %, the effect of improving the machinability is small, so that it is preferable to be not less than 0.01 mass %.
- Zr forms a sulfide with MnS, which acts as a chip breaker to improve the machinability.
- MnS acts as a chip breaker to improve the machinability.
- the effect is saturated but also the cost increases, so that it is not more than 0.01 mass %.
- the effect of improving the machinability is small, so that it is preferable to be not less than 0.003 mass %.
- REM forms a sulfide with MnS, which acts as a chip breaker to improve the machinability.
- MnS acts as a chip breaker to improve the machinability.
- REM is preferable to be not less than 0.0001 mass %.
- the chemical composition is limited to the above range and further the steel texture prior to the induction hardening is made to the following texture, whereby there can be obtained the aforementioned average particle size of the prior austenite of not more than 7 ⁇ m.
- the microstructure of the base metal i.e. microstructure prior to the hardening (corresponding to the microstructure other than that of the hardened layer after the induction hardening) has a bainite structure and/or a martensite structure and a total of either or both of the bainite structure and the martensite structure is not less than 10 volume %.
- the bainite structure or the martensite structure is a microstructure finely dispersing the carbide therein as compared with a ferrite-pearlite microstructure, so that an area of an ferrite/carbide interface as a nuclear formation site of austenite in the heating and hardening increases to refine the resulting austenite, which effectively contributes to the refining of the grain size in the hardened layer after the hardening. Further, such a refining of the grain size in the hardened layer after the hardening increases the intergranular strength and improves the fatigue strengths.
- the total of either or both of the bainite structure and the martensite structure is not less than 20 volume %.
- an upper limit of a microstructure fraction in the total of either or both of the bainite structure and the martensite structure is about 90 volume %. Because, when the microstructure fraction exceeds 90 volume %, the effect of refining the prior austenite grains in the hardened layer through the hardening is saturated but also the machinability is rapidly deteriorated.
- the martensite structure has an effect approximately equal to that of the bainite structure.
- the bainite structure is advantageous as compared with the martensite structure because the amount of alloying elements added is less from an industrial viewpoint, and the machinability is good, and it is possible to produce at a low cooling rate.
- the martensite structure is preferable for refining the grain size of the prior austenite in martensite of the hardened layer after the induction hardening.
- the component for machine structure according to the invention can be produced by subjecting a steel material having the aforementioned chemical composition to a hot working such as bar steel rolling, hot forging or the like to shape into a component and then subjecting at least a part of the component to an induction hardening under a condition of heating temperature: 800-1000° C.
- a hot working such as bar steel rolling, hot forging or the like
- at least a part of the component to an induction hardening under a condition of heating temperature: 800-1000° C.
- the term “at least a part” means a portion requiring fatigue strengths.
- the total working ratio at 800-1000° C. is not less than 80% and the subsequent temperature region of 700-500° C. is cooled at a rate of not less than 0.2° C./s.
- the microstructure prior to the hardening can be made to uniform and fine bainite and/or martensite structure (microstructure fraction: not less than 10 volume %). That is, since bainite and martensite are a microstructure finely dispersing the carbide therein as compared with a ferrite-pearlite microstructure, the area of ferrite/carbide interface as a nucleus formation site of austenite increases in the heating for the induction hardening, which is advantageous for refining the resulting austenite.
- the microstructure fraction in the total of either or both of bainite and martensite is not less than 10 volume %.
- the cooling rate in the temperature region of 700-500° C. is less than 0.2° C./s
- the microstructure fraction in the total of either or both of bainite and martensite can not be made to not less than 10 volume %. More preferably, the cooling rate is not less than 0.5° C./s.
- the bainite and/or martensite structure prior to the induction hardening can be more refined by subjecting to a working of not less than 20% at a temperature region of lower than 800° C.
- a working of not less than 20% at a temperature region of lower than 800° C Prior to the induction hardening (hereinafter referred to as a second working step), whereby the further refining of the prior austenite grains after the induction hardening can be attained, so that it is preferable to conduct the second working step.
- the working at the temperature region of lower than 800° C.
- the working below 800° C. is preferable to be not less than 30%.
- the working method for example, cold forging, cold ironing, forming of rolling, shot peening and the like.
- the working below 800° C. is refined the bainite or martensite structure prior to the induction hardening, and hence the average grain size of the prior austenite in the hardened layer obtained after the induction hardening becomes finer to more improve the fatigue strengths.
- the prior austenite grains having an average grain size of not more than 7 ⁇ m are first obtained by combining the adjustment of the microstructure prior to the hardening by the above working and cooling with the following induction hardening conditions.
- the heating temperature is lower than 800° C.
- the formation of austenite microstructure is insufficient and the hardened layer can not be obtained.
- the heating temperature exceeds 1000° C. or when the temperature rising rate at 600-800° C. is less than 300° C./s, the growth of the austenite grains is promoted and at the same time the scattering of the grains becomes large to lower the fatigue strengths. That is, as to the grain size of the prior austenite in the finally obtained hardened layer, it is important how to prevent the grain growth at the austenite zone in the heating for the hardening.
- the microstructure prior to the hardening is a microstructure having fine bainite or martensite as mentioned above, there are many nucleus formation sites for inverse transformation to austenite, so that when the cooling is started while the produced austenite grains do not grow, the average particle size of the prior austenite in the hardened microstructure can be refined.
- the growth of the austenite grains proceeds as the temperature becomes higher or as the keeping time in the austenite zone becomes longer, in order to prevent the grain growth and finally obtain the prior austenite grains having an average grain size of not more than 7 ⁇ m, the ultimate temperature in the heating is not higher than 1000° C. and the temperature rising rate at 600-800° C. is not less than 300° C./s.
- the ultimate temperature in the heating is preferable to be 800-950° C.
- the temperature rising rate at 600-800° C. is preferably not less than 700° C./s, more preferably not less than 1000° C./s.
- the residence time above 800° C. in the induction heating becomes long, the austenite grains grow and the grain size of the prior austenite tends to finally exceed over 7 ⁇ m, so that the residence time above 800° C. is preferable to be not more than 5 seconds. More preferably, the heating time is not more than 3 seconds.
- FIG. 1 shows results examined on a relation between a heating temperature in an induction hardening and a grain size of prior austenite in a hardened layer with respect to Mo-added steel and Mo-free steel.
- 150 kg of a steel material having a chemical composition shown in the following a-steel, b-steel, c-steel, d-steel and e-steel is melted in a vacuum melting furnace, hot-forged into 150 mm square to form a dummy billet, which is subjected to a hot working of 80% at 850° C. and cooled at 0.7° C./s within a temperature range of 700-500° C. to form a bar steel rolled material. Further, a part of the bar steels is subjected to a cold working of 20% after the cooling as a second working step.
- a test specimen for torsional fatigue is sampled from the resulting bar steel, subjected to an induction hardening at a frequency of 10-200 kHz and a heating temperature of 870-1050° C. and further subjected to a tempering in a heating furnace under conditions of 170° C. ⁇ 30 minutes to obtain a test material.
- the induction hardening conditions are adjusted so that the temperature rising rate is not less than 300° C./s and the residence time above 800° C. is not more than 1 second.
- test material is subjected to a torsional fatigue test to measure a stress broken at torsion number of 10 5 on the torsional stepped test specimen of 18 mm ⁇ .
- average grain size of prior austenite in the hardened layer through the induction hardening is measured by the previously mentioned method.
- Vickers hardness is measured at a position of 1 ⁇ 5 of the full thickness from the surface of the hardened layer. As the Vickers hardness is adopted an average value measured when 98 N (10 kgf) is struck 5 times.
- the grain size of prior austenite in the hardened layer can be made small by lowering the heating temperature in the induction hardening.
- the refining of the grain size in the hardened layer is remarkably attained by rendering the ultimate temperature in the heating to not higher than 1000° C., preferably not higher than 950° C.
- the grain size of the prior austenite can be more refined by adding the second working step (cold working).
- the inventors have guessed that in the steels containing Mo, the reason why the average grain size of prior austenite in the hardened layer through the induction hardening can be more refined to improve the fatigue strengths is due to the fact that the fine Mo-based precipitates are highly dispersed to make the above pinning effect large.
- a-steel is melted, rolled, subjected to forgings of 80% at 850° C. and 25% at 750° C. and then cooled in air (cooling rate in air: 0.8° C./s). Then, a sample for the observation with a transmission electron microscope is taken out from the starting material prior to the induction hardening to observe a state of fine precipitates. The sample for the observation with the transmission electron microscope is proved by taking out a flat plate sample from the central portion of the starting material and subjecting to an electrolytic polishing with a perchloric acid-methanol based electrolyte for thinning.
- the thickness of the observation zone is adjusted to a range of 50-100 nm.
- the thickness of the sample is estimated from an electron energy loss spectrum.
- FIG. 2 is shown an example of the actually obtained transmission electron microphotograph. Considering that the thickness of the sample in the view field is about 0.1 ⁇ m, it is revealed that fine precipitates having a diameter of about 5-10 nm are dispersed in a high density of about 3000 particles per 1 ⁇ m 3 .
- a nucleus of austenite is formed from a grain boundary of bainite or martensite, a packet boundary, a carbide and the like, which grows into grains.
- the above fine precipitates control the movement of the grain boundary face so as to push a finger (precipitates) into a balloon (grain boundary face) when the austenite grain boundary face arrives at the precipitates and passes therethrough.
- Such a control of moving the boundary face is called as a pinning.
- the pinning force is large as the precipitates becomes small when the amount of the precipitates is constant, or is strong as the amount of the precipitates becomes large when the size of the precipitates is constant.
- the inventors conducted a model calculation by varying a precipitation volume ratio of Mo in order to estimate the influence of the precipitate dispersed state on the average grain size of prior austenite in the induction heating treatment. That is, assuming that the solid solution of Mo into the other precipitation phase is slight, if a precipitation volume ratio: f and average grain size: d of the Mo-based fine precipitates are determined, there is estimated the number of Mo-based fine precipitates per 1 ⁇ m 3 (precipitation density) in the case of uniform dispersion precipitation. If the average grain size of the prior austenite is governed by the pinning of the fine precipitation, such a size is inversely proportional to the precipitation density.
- the residue after the precipitates are extracted from the base metal is identified by an X-ray diffractometry, it is guessed to be mainly hcp-type (Mo, Ti) 2 (C, N). Further, it has been revealed from results of EDX analysis attached with the transmission electron microscope that the atomic ratio of Mo to Ti is about 8:2 and Mo is a main component.
- the precipitates include a composition deviated from a stoichiometric composition of complete (Mo, Ti) 2 (C, N). In any case, it is considered to be a composite carbonitride including Mo and Ti.
- the (Mo, Ti) 2 (C, N) precipitate is known to be relatively hard different from the precipitate of Cu or the like and considered to be high in the ability preventing the pass through the grain boundary face. Also, considering that Mo is fairly larger than Ti in the composition ratio and Mo is a hardly dispersing element, it is not thought that (Mo, Ti) 2 (C, N) becomes rapidly large even it is kept within a temperature range of about 600-700° C. as a (Mo, Ti) 2 (C, N) precipitation temperature for a short time.
- the newly precipitation of (Mo, Ti) 2 (C, N) can be expected by isothermally keeping the above temperature range within a range of providing a microstructure fraction of bainite and martensite as mentioned later for a short tim while suppressing the coarsening of the previously precipitated (Mo, Ti) 2 (C, N) at minimum.
- FIG. 3 is shown a relation between a grain size of prior austenite and a torsional fatigue strength in the hardened layer.
- the grain size becomes small even in a region that the grain size of the prior austenite is not more than 7 ⁇ m and also the fatigue properties are improved.
- the Mo-free steel as the grain size becomes not more than 7 ⁇ m, even if the grain size is made further smaller than the above value, the fatigue strengths are not improved.
- the inventors have discovered that an increment of the fatigue strengths by the refining of the grain size of the prior austenite can be made large by increasing the hardness of the above hardened layer and get an idea that the transgranular strength can be raised by omitting the tempering treatment after the induction hardening instead of the feature that the transgranular strength is raised by increasing any content of C, Si and P, and hence the fatigue strengths are raised by the omission of the tempering treatment.
- the torsional fatigue strength is examined on the above a-steel and b-steel provided that the tempering treatment is omitted in the step of preparing the specimen for the torsional fatigue test.
- the Vickers hardness Hv in the a-steel and b-steel omitting the tempering is 740 and 780, respectively.
- FIG. 4 is shown a relation between a grain size of prior austenite and torsional fatigue property in the hardened layer for the comparison between tempering and no tempering. From FIG. 4 , it is seen that the fatigue strengths can be improved even by omitting the tempering.
- the invention can positively adopt the method of conducting no tempering.
- the tempering treatment after the induction hardening is a usual step.
- Such cracking is usually an intergranular fracture, which results from the lacking of the intergranular strength.
- the intergranular strength is high through the refining of the prior austenite grains, the cracking is hardly caused even in the omission of the tempering treatment.
- the omission of the tempering treatment is effective in the deterrence of softening due to the tempering and the reduction of the cost based on the tempering.
- Nos. 7 and 25 are comparative examples wherein all contents of C, Si and P are low, and it is seen that the fatigue strengths in the invention examples are further improved as compared with these comparative examples.
- the content of Mo, B or Ti is insufficient as shown in Nos. 26, 27 and 28, the grain size of the prior austenite becomes coarse and the torsional fatigue strength lowers.
- the microstructure of the base metal is particularly rendered into ferrite-pearlite, so that the grain size of the prior austenite is coarsened and the fatigue strengths lower.
- the tempering treatment after the induction hardening is not conducted as shown in Nos.
- the fatigue strengths are further improved as compared with steels of Nos. 1 and 7.
- the total working ratio at 800-1000° C. in the hot working is small, so that the grain size of the prior austenite becomes large and the fatigue strengths are low.
- a constant velocity joint 12 interposed for transmitting a motive energy from a drive shaft 10 to a wheel hub 11 as shown in FIG. 5 .
- the constant velocity joint 12 is a combination of an outer wheel 13 sand an inner wheel 14 . That is, the inner wheel 14 is swingably fixed to an inside of a mouth portion 13 a of the outer wheel 13 through balls 15 fitted into a ball track groove formed in the inner face of the mouth portion 13 a , while the drive shaft 10 is connected to the inner wheel 14 .
- a stem portion 13 b of the outer wheel 13 is, for example, spline-bonded to the hub 11 , whereby the motive energy is transmitted from the drive shaft 10 to the hub 11 of the wheel.
- a starting material of steel having a chemical composition shown in Table 3 is melted in a converter and continuously cast to form a cast bloom.
- the cast bloom has a size of 300 ⁇ 400 mm.
- the cast bloom is rolled into a billet of 150 mm square through a break down step and then rolled into a bar steel of 55 mm ⁇ .
- the bar steel is cut into a given length and hot-forged to form an inner wheel of a constant velocity joint (outer diameter: 45 mm and inner diameter: 20 mm), and thereafter a groove for spline bond is formed on a fitting face thereof by machining or roll forming. Also, a rolling face for balls is formed by machining or cold forging.
- the cooling after the hot forging is carried out under conditions shown in Table 4. At this moment, the total working ratio in the hot forging and cold forging is obtained by adjusting an area reducing ratio of a section perpendicular to an axial direction of the rolling face.
- the rolling face 14 a for balls lying to the outer wheel of the constant velocity joint is rendered into a hardened texture layer 16 by subjecting to an induction hardening at 1050° C. and to a subsequent induction hardening under conditions shown in Table 4 in an induction hardening apparatus with a frequency of 15 Hz, which is tempered under conditions of 180° C. ⁇ 2 h in a heating furnace. Moreover, the tempering is omitted in a part of the constant velocity joints.
- the drive shaft is fitted onto the fitting face of the inner wheel of the thus obtained constant velocity joint, which is mounted to the mouth portion of the outer wheel of the constant velocity joint through balls (steel balls), while the hub is fitted into the stem portion of the outer wheel of the constant velocity joint, whereby there is obtained a constant velocity joint unit (see FIG. 5 ).
- the specifications of the ball, outer wheel, drive shaft and hub are shown as follows.
- the durable test for rolling fatigue strength in the rolling face for balls is carried out in a motive energy transmission system of the constant velocity joint in which a rotational motion of the drive shaft is transmitted to the inner wheel of the constant velocity joint and then through the inner wheel to the hub.
- the test for the rolling fatigue strength is carried out by the motive energy transmission under conditions that a torque is 900 N ⁇ m and an operating angle (an angle defined between axial line of inner wheel and axial line of drive shaft) is 20° and a revolution number is 300 rpm, and a time causing the peeling in the rolling face of the inner wheel of the constant velocity joint is evaluated as the rolling fatigue strength.
- the dimensions and forms of the drive shaft, outer wheel of constant velocity joint and the like are set so that the inner wheel of the constant velocity joint becomes weakest in the durable test.
- the average grain size of prior austenite and hardness in the hardened layer with respect to the inner wheel of the constant velocity joints prepared under the same conditions are measured by the same methods as mentioned above.
- Nos. 7 and 25 are comparative examples wherein all contents of C, Si and P are low, and the rolling fatigue life is improved in the invention examples as compared with these comparative examples.
- the content of Mo, B or Ti is lacking as in Nos. 26, 27 and 28, the grain size of the prior austenite is coarsened and the rolling fatigue life lowers.
- the microstructure of the base material is particularly ferrite-pearlite, so that the grain size of the prior austenite is coarsened and the rolling fatigue life lowers.
- the tempering treatment is omitted after the induction hardening as in Nos. 29 and 30, the rolling fatigue life is further improved as compared with No. 1 steel and No. 7 steel, respectively.
- the total working ration of 800-1000° C. in the hot working is small, so that the grain size of the prior austenite becomes large and the rolling fatigue life is low.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Heat Treatment Of Steel (AREA)
- Heat Treatment Of Articles (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JPPCT/JP2004/010200 | 2004-07-16 | ||
JP2004010200 | 2004-07-16 | ||
PCT/JP2005/012397 WO2006008960A1 (ja) | 2004-07-16 | 2005-07-05 | 機械構造用部品およびその製造方法と高周波焼入れ用素材 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20080247900A1 true US20080247900A1 (en) | 2008-10-09 |
Family
ID=35785080
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/587,731 Abandoned US20080247900A1 (en) | 2004-07-16 | 2005-07-05 | Component for Machine Structure, Method of Producing the Same and Material for Induction Hardening |
Country Status (5)
Country | Link |
---|---|
US (1) | US20080247900A1 (de) |
EP (1) | EP1770181B1 (de) |
JP (1) | JP4645593B2 (de) |
CN (1) | CN100529137C (de) |
WO (1) | WO2006008960A1 (de) |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100296764A1 (en) * | 2007-10-04 | 2010-11-25 | Ingemar Strandell | Rolling Element or Ring Formed From a Bearing Steel |
US20110091348A1 (en) * | 2008-06-19 | 2011-04-21 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | Steel for heat treatment |
US20120018028A1 (en) * | 2009-02-06 | 2012-01-26 | Jfe Steel Corporation | High strength steel pipe for low-temperature usage having excellent buckling resistance and toughness of welded heat affected zone and method for producing the same |
US20120321503A1 (en) * | 2009-11-30 | 2012-12-20 | Minoru Honjo | Method for manufacturing ingot steel for bearings and bearing steel |
US9062360B2 (en) | 2009-06-05 | 2015-06-23 | Kobe Steel, Ltd. | Steel for machine structural use |
US20160032417A1 (en) * | 2014-07-29 | 2016-02-04 | Korea Institute Of Machinery And Materials | Work hardenable yield ratio-controlled steel and method of manufacturing the same |
US20180187280A1 (en) * | 2015-06-29 | 2018-07-05 | Ntn Corporation | Mechanical component |
US10151010B2 (en) | 2013-05-30 | 2018-12-11 | Nippon Steel & Sumitomo Metal Corporation | Soft nitrided induction hardened steel part |
US10260123B2 (en) * | 2014-07-03 | 2019-04-16 | Nippon Steel & Sumitomo Metal Corporation | Rolled steel bar for machine structural use and method of producing the same |
US10266908B2 (en) * | 2014-07-03 | 2019-04-23 | Nippon Steel & Sumitomo Metal Corporation | Rolled steel bar for machine structural use and method of producing the same |
US20190161838A1 (en) * | 2017-11-28 | 2019-05-30 | GM Global Technology Operations LLC | High-strength bainitic steel |
CN111542638A (zh) * | 2017-12-26 | 2020-08-14 | Posco公司 | 耐冲击性优异的热轧钢板、钢管、部件及其制造方法 |
US11326238B2 (en) | 2016-02-03 | 2022-05-10 | Jfe Steel Corporation | Steel material for high heat input welding |
EP4026928A4 (de) * | 2019-09-04 | 2023-04-12 | Posco | Stahlblech mit ausgezeichneter festigkeit und tieftemperaturzähigkeit sowie verfahren zu seiner herstellung |
Families Citing this family (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2007154305A (ja) * | 2005-07-05 | 2007-06-21 | Jfe Steel Kk | 強度、延性及び靱性に優れた機械構造用鋼およびその製造方法 |
JP5886537B2 (ja) * | 2011-04-18 | 2016-03-16 | 日本パーカライジング株式会社 | 高耐久性エンジンバルブ |
US20140083574A1 (en) * | 2011-06-30 | 2014-03-27 | Hyundai Hysco Co.,Ltd. | Heat-hardened steel with excellent crashworthiness and method for manufacturing heat-hardenable parts using same |
CN104294172A (zh) * | 2014-09-30 | 2015-01-21 | 合肥恒泰钢结构有限公司 | 一种高碳热轧硅钢合金 |
CN104593558A (zh) * | 2015-01-10 | 2015-05-06 | 安徽东星汽车部件有限公司 | 一种高频淬火剂及其制备方法 |
CN105483523A (zh) * | 2015-12-28 | 2016-04-13 | 合肥中澜新材料科技有限公司 | 一种抗变形汽车合金踏板 |
CN106048173A (zh) * | 2016-07-20 | 2016-10-26 | 柳州科尔特锻造机械有限公司 | 一种合金钢的热处理方法 |
CN106282725A (zh) * | 2016-08-15 | 2017-01-04 | 合肥万向钱潮汽车零部件有限公司 | 一种汽车轮毂材料配方 |
EP3354764B1 (de) * | 2017-01-26 | 2020-03-11 | SSAB Technology AB | Abschreckgehärteter stahl |
WO2018138270A1 (en) * | 2017-01-26 | 2018-08-02 | Ssab Technology Ab | Quench hardened steel |
US20200190618A1 (en) * | 2017-04-07 | 2020-06-18 | Jfe Steel Corporation | Steel member, hot-rolled steel sheet for steel member, and production method therefor |
CN107326305A (zh) * | 2017-05-27 | 2017-11-07 | 江苏金基特钢有限公司 | 一种耐腐蚀钢板及其制造方法 |
CN107523761A (zh) * | 2017-08-30 | 2017-12-29 | 宁波正凯机械有限公司 | 采用精锻塑性成型工艺制作球笼式万向节的方法 |
JP7185574B2 (ja) * | 2019-03-25 | 2022-12-07 | 株式会社神戸製鋼所 | 鋼材 |
CN112981237B (zh) * | 2021-01-28 | 2022-10-11 | 江阴兴澄特种钢铁有限公司 | 一种球笼式万向节保持架用钢及其生产方法 |
Family Cites Families (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3208960B2 (ja) * | 1993-10-20 | 2001-09-17 | 株式会社神戸製鋼所 | 高面疲労強度機械構造用部品及びその製法 |
JP3374667B2 (ja) * | 1995-10-17 | 2003-02-10 | Ntn株式会社 | 高強度等速ジョイント用外輪およびその製造法 |
JPH10195589A (ja) * | 1996-12-26 | 1998-07-28 | Nippon Steel Corp | 高捩り疲労強度高周波焼入れ鋼材 |
JP3562192B2 (ja) * | 1997-01-31 | 2004-09-08 | Jfeスチール株式会社 | 高周波焼入用部品およびその製造方法 |
JPH1129836A (ja) * | 1997-05-13 | 1999-02-02 | Kawasaki Steel Corp | 高周波焼入れ用機械構造用鋼 |
JP3593255B2 (ja) * | 1998-04-17 | 2004-11-24 | 山陽特殊製鋼株式会社 | 高強度シャフトの製造方法 |
JP2002069577A (ja) * | 2000-08-30 | 2002-03-08 | Nippon Steel Corp | 鍛造性と製品靭性に優れた冷・温間鍛造用鋼とその製造方法 |
JP3774697B2 (ja) * | 2002-12-04 | 2006-05-17 | 新日本製鐵株式会社 | 高強度高周波焼き入れ用鋼材及びその製造方法 |
JP4487482B2 (ja) * | 2003-01-17 | 2010-06-23 | Jfeスチール株式会社 | 疲労強度に優れた高強度鋼材およびその製造方法 |
TWI238197B (en) * | 2003-09-29 | 2005-08-21 | Jfe Steel Corp | Component for machine and structural purposes, material therefor, and manufacturing method therefor |
KR100845633B1 (ko) * | 2004-04-28 | 2008-07-10 | 제이에프이 스틸 가부시키가이샤 | 기계구조용 부품 및 그 제조방법 |
-
2005
- 2005-07-05 US US11/587,731 patent/US20080247900A1/en not_active Abandoned
- 2005-07-05 EP EP05758220.7A patent/EP1770181B1/de not_active Expired - Fee Related
- 2005-07-05 JP JP2006519625A patent/JP4645593B2/ja not_active Expired - Fee Related
- 2005-07-05 WO PCT/JP2005/012397 patent/WO2006008960A1/ja active Application Filing
- 2005-07-05 CN CNB2005800137361A patent/CN100529137C/zh not_active Expired - Fee Related
Cited By (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8562767B2 (en) * | 2007-10-04 | 2013-10-22 | Aktiebolaget Skf | Method of heat treating a steel bearing component |
US20100296764A1 (en) * | 2007-10-04 | 2010-11-25 | Ingemar Strandell | Rolling Element or Ring Formed From a Bearing Steel |
US20110091348A1 (en) * | 2008-06-19 | 2011-04-21 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | Steel for heat treatment |
US9023159B2 (en) * | 2008-06-19 | 2015-05-05 | Kobe Steel, Ltd. | Steel for heat treatment |
US20120018028A1 (en) * | 2009-02-06 | 2012-01-26 | Jfe Steel Corporation | High strength steel pipe for low-temperature usage having excellent buckling resistance and toughness of welded heat affected zone and method for producing the same |
US8765269B2 (en) * | 2009-02-06 | 2014-07-01 | Jfe Steel Corporation | High strength steel pipe for low-temperature usage having excellent buckling resistance and toughness of welded heat affected zone and method for producing the same |
US9062360B2 (en) | 2009-06-05 | 2015-06-23 | Kobe Steel, Ltd. | Steel for machine structural use |
US20120321503A1 (en) * | 2009-11-30 | 2012-12-20 | Minoru Honjo | Method for manufacturing ingot steel for bearings and bearing steel |
US10151010B2 (en) | 2013-05-30 | 2018-12-11 | Nippon Steel & Sumitomo Metal Corporation | Soft nitrided induction hardened steel part |
US10266908B2 (en) * | 2014-07-03 | 2019-04-23 | Nippon Steel & Sumitomo Metal Corporation | Rolled steel bar for machine structural use and method of producing the same |
US10260123B2 (en) * | 2014-07-03 | 2019-04-16 | Nippon Steel & Sumitomo Metal Corporation | Rolled steel bar for machine structural use and method of producing the same |
US20160032417A1 (en) * | 2014-07-29 | 2016-02-04 | Korea Institute Of Machinery And Materials | Work hardenable yield ratio-controlled steel and method of manufacturing the same |
US10557183B2 (en) * | 2014-07-29 | 2020-02-11 | Korea Institute Of Machinery And Materials | Work hardenable yield ratio-controlled steel and method of manufacturing the same |
US20180187280A1 (en) * | 2015-06-29 | 2018-07-05 | Ntn Corporation | Mechanical component |
US11326238B2 (en) | 2016-02-03 | 2022-05-10 | Jfe Steel Corporation | Steel material for high heat input welding |
US20190161838A1 (en) * | 2017-11-28 | 2019-05-30 | GM Global Technology Operations LLC | High-strength bainitic steel |
CN111542638A (zh) * | 2017-12-26 | 2020-08-14 | Posco公司 | 耐冲击性优异的热轧钢板、钢管、部件及其制造方法 |
EP4026928A4 (de) * | 2019-09-04 | 2023-04-12 | Posco | Stahlblech mit ausgezeichneter festigkeit und tieftemperaturzähigkeit sowie verfahren zu seiner herstellung |
Also Published As
Publication number | Publication date |
---|---|
EP1770181B1 (de) | 2013-11-06 |
EP1770181A1 (de) | 2007-04-04 |
CN1950530A (zh) | 2007-04-18 |
CN100529137C (zh) | 2009-08-19 |
JPWO2006008960A1 (ja) | 2008-05-01 |
JP4645593B2 (ja) | 2011-03-09 |
WO2006008960A1 (ja) | 2006-01-26 |
EP1770181A4 (de) | 2010-11-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1770181B1 (de) | Komponente für eine maschinenstruktur, verfahren zu deren herstellung und material für hochfrequenzhärtung | |
EP1743950B1 (de) | Nahtloses stahlrohr und herstellungsverfahren dafür | |
KR100726252B1 (ko) | 강제의 기계구조용 부품, 그 소재, 및 그 제조방법 | |
US9297051B2 (en) | Case hardening steel, method for producing same, and mechanical structural part using case hardening steel | |
US20170335426A1 (en) | Rolled steel bar or rolled wire rod for cold-forged component | |
CN114729435A (zh) | 低温冲击韧性优异的高硬度耐磨钢及其制造方法 | |
JPH11335777A (ja) | 冷間加工性と低浸炭歪み特性に優れた肌焼鋼とその製造方法 | |
CN113661019B (zh) | 通过离心铸造法制造的轧制用复合辊及其制造方法 | |
JP5262740B2 (ja) | 浸炭時の粗大粒防止特性と疲労特性に優れた肌焼鋼とその製造方法 | |
JP6766362B2 (ja) | 浸炭時の粗大粒防止特性と疲労特性と被削性に優れた肌焼鋼およびその製造方法 | |
JP3738004B2 (ja) | 冷間加工性と浸炭時の粗大粒防止特性に優れた肌焼用鋼材とその製造方法 | |
KR100883716B1 (ko) | 기계구조용 부품 및 그 제조방법과 고주파 담금질용 소재 | |
JP3738003B2 (ja) | 冷間加工性と浸炭時の粗大粒防止特性に優れた肌焼用鋼材およびその製造方法 | |
JP3196579B2 (ja) | 強度と靭性に優れた快削非調質鋼 | |
JPH11293390A (ja) | 高強度快削非調質鋼材 | |
JP2007231337A (ja) | 熱延鋼板および鋼部品 | |
JP4608979B2 (ja) | 疲労特性に優れた鋼材および高周波焼入れ用鋼素材 | |
JP3978111B2 (ja) | 捻り疲労特性に優れた浸炭用鋼 | |
JP5050515B2 (ja) | クランクシャフト用v含有非調質鋼 | |
JP3081927B2 (ja) | 駆動軸継手用浸炭焼入部品及びその製造方法 | |
JP6390685B2 (ja) | 非調質鋼およびその製造方法 | |
US20070000582A1 (en) | Steel product for induction hardening, induction-hardened member using the same, and methods for production them | |
JP2008223083A (ja) | クランクシャフト及びその製造方法 | |
JP4280923B2 (ja) | 浸炭部品又は浸炭窒化部品用の鋼材 | |
JP2008056956A (ja) | 表層細粒鋼部品とその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: JFE STEEL CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HAYASHI, TORU;OHMORI, YASUHIRO;KUROSAWA, NOBUTAKA;AND OTHERS;REEL/FRAME:018494/0673 Effective date: 20060927 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |