US20060047052A1 - Oriented nanofibers embedded in polymer matrix - Google Patents
Oriented nanofibers embedded in polymer matrix Download PDFInfo
- Publication number
- US20060047052A1 US20060047052A1 US10/149,216 US14921602A US2006047052A1 US 20060047052 A1 US20060047052 A1 US 20060047052A1 US 14921602 A US14921602 A US 14921602A US 2006047052 A1 US2006047052 A1 US 2006047052A1
- Authority
- US
- United States
- Prior art keywords
- composite
- nanofibers
- polymer
- group
- matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
- D01F6/02—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
- D01F6/04—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyolefins
- D01F6/06—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyolefins from polypropylene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/04—Reinforcing macromolecular compounds with loose or coherent fibrous material
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/36—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die
- B29C48/365—Means for plasticising or homogenising the moulding material or forcing it through the nozzle or die using pumps, e.g. piston pumps
- B29C48/37—Gear pumps
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
- B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
- B29C48/00—Extrusion moulding, i.e. expressing the moulding material through a die or nozzle which imparts the desired form; Apparatus therefor
- B29C48/25—Component parts, details or accessories; Auxiliary operations
- B29C48/92—Measuring, controlling or regulating
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B33—ADDITIVE MANUFACTURING TECHNOLOGY
- B33Y—ADDITIVE MANUFACTURING, i.e. MANUFACTURING OF THREE-DIMENSIONAL [3-D] OBJECTS BY ADDITIVE DEPOSITION, ADDITIVE AGGLOMERATION OR ADDITIVE LAYERING, e.g. BY 3-D PRINTING, STEREOLITHOGRAPHY OR SELECTIVE LASER SINTERING
- B33Y70/00—Materials specially adapted for additive manufacturing
- B33Y70/10—Composites of different types of material, e.g. mixtures of ceramics and polymers or mixtures of metals and biomaterials
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82B—NANOSTRUCTURES FORMED BY MANIPULATION OF INDIVIDUAL ATOMS, MOLECULES, OR LIMITED COLLECTIONS OF ATOMS OR MOLECULES AS DISCRETE UNITS; MANUFACTURE OR TREATMENT THEREOF
- B82B3/00—Manufacture or treatment of nanostructures by manipulation of individual atoms or molecules, or limited collections of atoms or molecules as discrete units
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/02—Elements
- C08K3/04—Carbon
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
- C08K7/02—Fibres or whiskers
- C08K7/04—Fibres or whiskers inorganic
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
- C08K7/02—Fibres or whiskers
- C08K7/04—Fibres or whiskers inorganic
- C08K7/06—Elements
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K7/00—Use of ingredients characterised by shape
- C08K7/22—Expanded, porous or hollow particles
- C08K7/24—Expanded, porous or hollow particles inorganic
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F1/00—General methods for the manufacture of artificial filaments or the like
- D01F1/02—Addition of substances to the spinning solution or to the melt
- D01F1/10—Other agents for modifying properties
-
- D—TEXTILES; PAPER
- D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
- D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
- D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
- D01F6/02—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
- D01F6/04—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyolefins
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y20/00—Nanooptics, e.g. quantum optics or photonic crystals
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K2201/00—Specific properties of additives
- C08K2201/011—Nanostructured additives
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/249921—Web or sheet containing structurally defined element or component
- Y10T428/249924—Noninterengaged fiber-containing paper-free web or sheet which is not of specified porosity
- Y10T428/249933—Fiber embedded in or on the surface of a natural or synthetic rubber matrix
- Y10T428/249934—Fibers are aligned substantially parallel
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/249921—Web or sheet containing structurally defined element or component
- Y10T428/249924—Noninterengaged fiber-containing paper-free web or sheet which is not of specified porosity
- Y10T428/24994—Fiber embedded in or on the surface of a polymeric matrix
- Y10T428/249948—Fiber is precoated
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/249921—Web or sheet containing structurally defined element or component
- Y10T428/249953—Composite having voids in a component [e.g., porous, cellular, etc.]
- Y10T428/249986—Void-containing component contains also a solid fiber or solid particle
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
- Y10T428/2913—Rod, strand, filament or fiber
- Y10T428/2929—Bicomponent, conjugate, composite or collateral fibers or filaments [i.e., coextruded sheath-core or side-by-side type]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/31855—Of addition polymer from unsaturated monomers
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
- Y10T442/30—Woven fabric [i.e., woven strand or strip material]
Definitions
- the present invention relates to the development of a nanofiber reinforced polymer composite system with control over the orientation of the nanofibers dispersed in the system.
- the spinnerets used in the production of most manufactured fibers have from one to several hundred holes. As the filaments emerge from the holes in the spinneret, the liquid polymer is converted first to a rubbery state and then solidified. This process of extrusion and solidification of endless filaments is called spinning, not to be confused with the textile operation of the same name, where short pieces of staple fiber are twisted into yarn. There are four methods of spinning filaments of manufactured fibers: wet, dry, melt, and gel spinning.
- wet spinning is the oldest process. It is used for fiber-forming substances that have been dissolved in a solvent. The spinnerets are submerged in a chemical bath and as the filaments emerge they precipitate from solution and solidify. Because the solution is extruded directly into the precipitating liquid, this process for making fibers is called wet spinning. Acrylic, rayon, aramid, modacrylic and spandex are produced by this process.
- Dry spinning is also used for fiber-forming substances in solution.
- solidification is achieved by evaporating the solvent in a stream of air or inert gas.
- the filaments do not come in contact with a precipitating liquid, eliminating the need for drying and easing solvent recovery.
- This process is used for the production of acetate, triacetate, acrylic, modacrylic, PBI, spandex, and vinyon.
- melt spinning the fiber-forming substance is melted for extrusion through the spinneret and then directly solidified by cooling.
- Nylon, olefin, polyester, saran and sulfur are produced in this manner.
- Melt spun fibers can be extruded from the spinneret in different cross-sectional shapes (round, trilobal, pentagonal, octagonal, and others).
- Gel spinning is a special process used to obtain high strength or other special fiber properties.
- the polymer is not in a true liquid state during extrusion. Not completely separated, as they would be in a true solution, the polymer chains are bound together at various points in liquid crystal form. This produces strong inter-chain forces in the resulting filaments that can significantly increase the tensile strength of the fibers.
- the liquid crystals are aligned along the fiber axis by the shear forces during extrusion.
- the filaments emerge with an unusually high degree of orientation relative to each other, further enhancing strength.
- the process can also be described as dry-wet spinning, since the filaments first pass through air and then are cooled further in a liquid bath.
- the filaments While extruded fibers are solidifying, or after they have hardened, the filaments may be drawn or elongated to impart strength. Drawing pulls the molecular chains together and orients them along the fiber axis, creating a considerably stronger yarn.
- NCF nanofiber continuous fiber
- These micron-size fibers provide for easy handling of nanofibers, provide for control of their distribution, including high degrees of alignment, for subsequent manipulation, and for ease of processing and manufacturing into a range of parts for mechanical, electrical and thermal applications.
- NCFs are continuous fibers with dispersed nanofibers which can be produced in continuous fiber lengths (1000s of km for example) to be filament wound, woven, laid up, processed in rows or bundles, used for thread or yarn to produce a range of products requiring the enhancement from the nanofiber additions.
- the polymer matrix is a system that can easily be processed into various shapes or with other polymer systems or non-polymeric additions.
- the NCFs are a system that can deliver aligned nanotubes for strengthening (including improved impact strength), or electrical or thermal anisotropic features (properties varying in different directions).
- the NCF system can also be applied to nanofibers embedded in matrix and then formed into a tape or film to provide control of distribution and alignment and to enable a variety of subsequent processing steps.
- the present invention relates to the development of a nanofiber reinforced polymer composite system with control over the orientation of the nanofibers dispersed in the system.
- the system is a nanofiber continuous fiber system where nanofibers are embedded in polymer matrices in micron size fibers.
- Nanofibers are carbon fibrils with diameters in the 100 nm and less range, multi-walled nanotubes (MWNTs) and single wall nanotubes (SWNTs), including ropes and their various derivatives with a range of functionalizations, which can be, but are not always, exclusively carbon.
- MWNTs multi-walled nanotubes
- SWNTs single wall nanotubes
- induced orientation of the nanofibers can be processed into a range of micron size diameter fibers that enable nanofibers to be used to enhance mechanical, thermal and electrical properties.
- NCFs can include a nanotube system, where NCFs are made up of nanotubes without a polymer binder.
- the nanotube continuous fibers would originate from a nanotube/polymer precursor system where the polymer has been removed leaving micron size fibers of only nanotubes.
- the NCFs can be prepared with isotropic dispersions of nanofibers or with highly aligned nanofibers that can easily be handled and processed with conventional composite manufacturing technologies to deliver high performance structures. This method of producing nanofibers in a continuous polymer system could have highly dispersed nanofibers or a range of dispersion conditions to suit special property needs.
- Polymer systems are expected to be those, which can undergo high shearing and elongational flow conditions including, but not limited to block copolymers, various thermoplastics, liquid crystal polymers, thermosets, gel processed polymers and elastomers. Rheological studies identified the key steps to dispersing both VGCFs and SWNTs in polymers.
- a number of suitable polymer/nanofiber systems exist, including but not limited to: Acetal, ABS, ASA, PE, PEEK, PET, PP, and Epon epoxy. For some applications epoxies and resins may be desired.
- materials can be prepared with specifically enhanced structural, electrical, and thermal properties.
- the NCFs provide a delivery system or package for handling nanofibers, and specifically SWNTs.
- the NCFs are a structure in and of themselves, a material useful for further processing into other forms, and a method of aligning nanofibers.
- the NCFs can be effectively used to process a range of composite forms including weaves, mats, plies, filament wound tubing and vessels and for a range of applications including wires and electrostatic discharge materials.
- the invention extends to further processing of the nanofiber composites.
- single wall nanotubes SWNTs
- FICs fully integrated nanotube composites
- Full integration of nanotubes requires their development beyond conventional composites so that the level of the non nanotube material is designed to integrate well with the amount of nanotubes so that the nanotubes are part of the matrix rather than a differing component.
- This development of multifunctional materials from nanotubes produces fully integrated nanotube composites (FINCs), a nanotube hybrid material system designed to surpass the limits of rule of mixtures engineering and composite design, implementing designs to fully mimic nanotubes on larger scales.
- This new approach involves integration, dispersion and alignment, functionalization, and polymerization to achieve total integration. Some cases achieve conduction through well designed networks but the goal is conduction through chemistry.
- the material systems described in this invention have application as highly conducting plastic wires and interconnects for multifunctional device and electronic applications. The basis for these materials will be nylon, PMMA, and conducting epoxy. Producing FINCs with gas permeable polymers provides new gas sensor capabilities. Key applications will be the lightweight multifunctional interconnects for electronics and wiring.
- the invention further outlines applications for the full integration of nanotubes.
- the lengths of SWNTs are such that toughening can easily be achieved and our calculations indicate that processing beyond rule of mixtures approaches is necessary to gain the full potential of the SWNTs.
- the invention and methods produce toughened-fully integrated nanotube composites (T-FINCs), a nanotube hybrid material system designed to surpass the limits of rule of mixtures engineering and composite design, to implement designs to fully mimic nanotubes on larger scales for enhanced mechanical properties.
- the basis for these materials will be two standard polymers: polypropylene (PP) and nylon. Shielding systems in the forms of panels and woven shields are typical applications for the new materials.
- Nanotube shielding has a wide range of applications, as intermediate bumpers and rear wall panels, extending to hypervelocity impact applications and shielding for space applications.
- Material systems in sheet form are produced that see ten orders of magnitude drop in electrical resistivity when using VGCFs and fourteen orders of magnitude drop in electrical resistivity when using SWNTs.
- the 10 wt. % SWNT material has been used to produce the first of our wire systems and has an electrical resistivity in the 600 ohm-square range. These systems have highly dispersed nanofibers otherwise the percolation would be even lower (when a segregated network is used).
- Enhancements have also been seen in improved stiffness (as high as 350% for VGCF systems), increased strength (50% increase for the 10 wt. % SWNT material) and with 100% elongation to failure for the SWNT system with the highest loading of nanotubes of 10 wt. %.
- Specific fibers are made from ABS with 10 wt. % VGCFs, PE with 5 wt. % SWNTs, Pe and PP with 1-3 wt. % HiPco, or other SWNTs. Alignment of VGCFs and SWNTs is observed. The ability to make composite fibers extends to making T-FINCs in fiber form.
- FIG. 1 shows (a) volume resistivity versus carbon nanofiber content VGCF (in wt. %) in the PP matrix at room temperature, (b) surface resistivity versus carbon nanofiber content (in wt. %) in the PP matrix at room temperature, and(c) I wt. % SWNTs volume resistivity.
- FIG. 2 is a TEM micrograph of a 20% carbon nanofiber reinforced PP composite from which isotropic dispersion of the individual fibers can be observed.
- FIG. 3 are SEM micrographs of a 10% carbon nanofiber reinforced PP composite in which wetting of the fibers by the PP matrix can be observed.
- FIG. 4 is a comparison of two micron size fiber composite diameters.
- FIG. 5 shows viscosity versus shear rate for various concentrations of VGCFs in a polypropylene matrix demonstrating the reduction in viscosity with increasing shear rate.
- FIG. 6 shows the change in viscosity with increasing shear rate for 3, 5 and 10 wt. % VGCF-polyethylene systems.
- FIG. 7 shows electrical resistivity as a function of SWNT composition.
- FIG. 8 shows surface resistivity of ABS with VGCF and SWNTs.
- FIG. 9 shows a micrograph of a 10 wt. % SWNT/ABS polymer fractured at room temperature.
- FIG. 10 shows torque data for the PP12 and PE10 systems.
- FIG. 11 shows the significant, 100° C. higher, increase in the degradation temperature for PP with just 2 wt. % SWNTs.
- FIG. 12 shows the increase observed in the modulus of polymers when SWNTs are added.
- FIG. 13 shows property enhancement due to high extruder speed and take up speed.
- FIG. 14 shows strength of fibers processed at different speeds.
- FIG. 15 shows a plot indicating the change in diameter of a fiber system at slow extruder speeds and subsequent slow take up speeds.
- FIG. 16 shows extrusion data collected while producing fibers from a Haake extruder.
- FIGS. 17, 18 , and 19 are rheological results for filled and unfilled ABS, polypropylene, and polyethylene, at temperatures and flow rates found to be favorable for fiber spinning with the RH-7.
- FIG. 20 shows an industrial polymer fiber spinning process.
- FIG. 21 shows a micrograph of PP1000 showing well aligned SWNTs.
- FIG. 22 shows tensile tests on polypropylene samples.
- FIG. 23 shows single fiber strength
- FIG. 24 shows products and processes that can be achieved using NCFs.
- FIG. 25 shows ABS with dispersed and aligned VGCFs (10 wt. %).
- FIG. 26 shows PE with dispersed and aligned VGCFs (a) 5 wt. % and (b) 2 wt. %.
- FIG. 27 shows desired nanofiber alignment by inducing directionality by shearing and or elongational flow into fibers.
- FIG. 28 shows nanofiber dispersion issues where the initial preparation of the nanofibers influences the degree of alignment and dispersion obtained fibers.
- FIG. 29 shows tensile test results following correction for the cross-plying
- FIG. 30 shows a micrograph of the polymer with as-received not dispersed SWNT.
- FIG. 31 shows longitudinal cross section of the wire feedstock.
- FIG. 32 shows inter trace fusion
- FIG. 33 shows inter trace fusion in cross ply.
- FIG. 34 shows the two conditions of FIG. 33 .
- FIG. 35 on the right shows attachment of polymer chains to the oxidized edge of a cut SWNT via amide linkages.
- FIG. 35 on the left shows attached organic molecules.
- FIG. 37 shows nanotubes crosslinking polymer chains.
- FIG. 38 shows nanotube block copolymers.
- FIG. 39 shows possible configurations for alternating polymer blocks.
- FIG. 40 shows functionalized SWNTs in graft copolymerization.
- FIG. 41 shows graft copolymerization on only one side.
- FIG. 42 shows a randomly crosslinked chain.
- FIG. 43 shows substrate attached nanotubes.
- FIG. 44 shows nanotubes shear oriented and chemically bonded to the polymer matrix.
- FIG. 45 shows a typical composite design system.
- FIG. 46 shows a comparison of a stress-strain curve for (a) a typical epoxycomposite compared to that for (b) a nanotube composite where significantstrength of the nanotube is discarded.
- SWNTs are expected to have a high degree of elongation to failure.
- FIG. 47 shows parameters used to calculate the properties of SWNT composites by Rule of Mixture Calculations based on an ABS polymer as the matrix.
- NCFs are a continuous fiber system, typically in the 1 to 150 micron diameter size range, made up of polymers and nanofibers, where the composition of the nanofibers range from above zero to 100 wt. %. Processing of nanofibers into polymer matrices in a continuous fiber form will provide control over the nanofiber orientation and offer advanced properties compared to conventional materials. The structural, electrical and thermal properties can be significantly enhanced. NCFs made up of 100% nanofibers are to be processed by mixing with a polymer matrix or binder that is subsequently removed to leave a nanofiber system. This process of making 100% micron size NCFs is especially directed toward development with SWNTs and their various functionalized derivatives.
- Nanofibers are not easily handled or manipulated into various engineered forms for a range of scales.
- Nanotubes can be obtained in low and high purity dried paper forms, called “Bucky Paper,” or may be purchased in various solutions that do not easily lend themselves to processing large scale products. Nanotubes are also available in the as-processed, unpurified condition which carry with them numerous unwanted impurities that affect composite properties.
- a form of nanotubes is presented which can easily be handled in much the same way as thread, yarn, fabrics, etc. are handled. The processing to achieve this end involves dispersing nanofibers in polymeric matrices that are formed into continuous fibers.
- the method of forming the fibers involves high shear processing, where polymers are a liquid, molten or melted and extruded through small orifices to produce high shear and small fiber systems. Elongational flow is subsequently used to further reduce the size of the fibers and to ensure aligned nanofibers (aligned parallel to the length of the continuous fiber system).
- NCFs using vapor-grown carbon fibers have already been processed using ABS with 10 wt. % nanofibers and PE matrices with 2, 5 and 10 wt. % nanofibers.
- NCFs have also been processed using ABS with 5 and 10% wt. % SWNTs and using UHMW (ultra high molecular weight) PE with 2% wt. % SWNTs. Additional systems produced included PP 1000 and 12 wt. % SWNTs with nanotube concentrations up to 6 wt. %.
- Spools of NCFs can be manufactured to use in the as-received form, or may be designed to further activate, functionalize, surface treat, pyrolize, modify, cross link, etc. the fiber system.
- the nanofibers may be further linked to the polymer, to each other, or optimized for non-wetted or unbound conditions according to the needs of the specific application.
- the ability to provide for aligned nanofibers in a range of polymeric materials and to further chemically treat the fiber systems opens a range of opportunities for new product development and materials enhancement. This includes the processing of FINC and T-FINC fibers.
- composites can be processed with isotropic dispersions of nanofibers when a network is formed.
- the material may be designed for Electrostatic Discharge (ESD) applications, primarily used to prevent the buildup of static electrical charges.
- Static electricity is not current or flow electricity; rather it is electricity that is at rest.
- the static dissipative range is known to be between an insulator (surface resistivities higher than 10 13 ohms/square) and a conductor (surface resistivities lower than 10 5 ohms/square). That is, values of surface resistivity between 10 5 and 10 12 ohms/square will provide static electrical dissipation.
- the values are low enough to provide dissipation, but not too low where sparking can occur.
- the volume and surface resistivities of the isotropic nanofiber reinforced composites were measured. The results of the isotropic composites are plotted in FIG. 1 for (a) volume and (b) surface resistivity, respectively.
- a percolation threshold occurs as it is expected for plastic reinforced with conductive materials.
- the nanofiber reinforced polypropylene composite starts to percolate at around 9%, and by 18%, a network of fibers has been formed with no fuirther decrease in resistivity. This system with this level of percolation has the opportunity of providing strengthening over other filled polymers for ESD, where the filler networks only lead to ESD properties.
- the conducting polymers can be processed into NCFs, where the nanofibers are well-aligned and can easily be aligned in bulk form by easy handling of micron size fibers.
- the material which has highly anisotropic electrical properties, has the further potential of being used as an Electromagnetic Interference/Radio Frequency Interference (EMI/RFI) material, since the electrical conductivity can be processed to a higher electrical conductivity.
- EMI/RFI Electromagnetic Interference/Radio Frequency Interference
- the nanofiber network that is formed is highly aligned parallel to the length of the fibers.
- An EMI/RFI material has electrical resistivities in the conductor range ( ⁇ 10 5 ohms/square) and can even be used for wires and electrical interconnects particularly when SWNTs are used. The interconnected network for conduction is maintained but the high degree of alignment further enhances the electrical properties and strength.
- the processing method used in the present invention to incorporate the nanofibers in the plastic matrix was a Banbury-type mixing where high shear stresses and high power were incorporated into the system.
- the Banbury-type mixing was selected to provide a uniform distribution of the nanofibers by exposing the agglomerates to hydrodynamic stresses forcing the agglomerates to break apart without, in most cases, damaging the nanofibers.
- high shear can be used to shorten the fibers, particularly those with a high number of defects.
- Composites with carbon nanofiber concentration ranging from 0-60 wt. % were prepared demonstrating the high degree of fiber concentrations that can be achieved.
- Nanofiber/tube dispersion is a key aspect in the sample preparation, since the physical properties of the finished composite are strongly governed by the dispersion of the fibers in the matrix.
- FIG. 2 shows a transmission electron microscopy micrograph of vapor grown carbon fibers in a polypropylene matrix. These nanofibers with an average diameter of 100 nm are highly dispersed and there are no indications of porosity in the composite system.
- FIG. 3 shows the scanning electron micrograph of a fracture surface of a composite sample tested in tension showing regions of wetting as indicated by the deformation of the polymer around the nanofibers.
- the NCFs were obtained by subsequently processing the composite material in a high shear condition using a capillary rheometer.
- the viscosity of the polymer/nanofiber system is significantly reduced to promote easy processing and high degrees of alignment.
- FIG. 5 shows the reduction in viscosity that can be accomplished as shear rate is increased for a VGCF-polypropylene system.
- the degree of alignment is processed into the micron size fiber system according to the level of shear used (see FIG. 4 for micron size fiber composite).
- FIG. 6 shows a similar reduction in viscosity obtained with increasing shear taken from the capillary rheometer where high degrees of alignment of the nanofibers are achieved.
- the degree of wetting and bonding can be processed into the initial NCF or may subsequently be altered following NCF assembly into various parts.
- the identified mixing approaches are successful for producing highly dispersed SWNTs in polymers where porosity and mixing viscosity is not an issue (typically high shear conditions).
- the process outlined in this invention identifies below key factors for achieving alignment, to producing continuous fibers, and for producing small diameter fibers.
- a composition of 5 wt. % SWNTs in ABS was processed using the torque rheometer.
- the composite was hot pressed into a sheet for subsequent processing.
- the sheets showed good flexibility and could be cut into pieces without cracking.
- the VGCF/polymer composite systems would many times crack when sectioned from the sheet form.
- PP and PE were processed with dispersed as-received and purified SWNTs.
- Polymer powder mixed with SWNTs in solution route proved to be an optimal approach for dispersing nanotubes in a polymer.
- PE powder was used but polymer pellets were used for the PP.
- the solvent was dimethyl formamide (DMF) since it has a low solubility in PE and PP, adequately disperses SWNTs and it boils off at a temperature below the softening temperature of the polymers.
- the coverages were uniform and this method provided a step where unwanted impurities in the as-received SWNT material (whether as-received or purified) could be removed. Unwanted contaminants had to be removed even after purification of the nanotubes.
- These powders formed agglomerates upon drying and the chunks were easy to handle and removed concern of having airborne particles.
- the agglomerates loaded very easily into a torque rheometer for mixing and compounding. Mixed composite was easy to process without any significant increase in torque (this means at low viscosity). Although the viscosity increases with the added SWNTs, the torque requirements for mixing the material are over an order of magnitude lower than the instrument limitations. When mixing the PP (melt flow index of 12) and PE (melt flow index of 10) materials, the torque conditions were the lowest observed.
- SWNTs in the PP and PE were highly dispersed, to have a lesser degree of entanglement, and to have some indication of wetting.
- the composite was porosity free.
- Compositions of 0, 5 wt. % as-received SWNTs (Tubes@rice) in PE (melt flow index of 10), 0, 2 wt. % SWNTs from HiPco in PP1000 and PE ultra-high molecular weight, and 1.7 wt. % SWNTs from NTT in PP12 and 3 wt. % SWNTs in PE10 were used.
- the 10 wt. % SWNTs from Tube@grice in ABS were processed to learn more about the mixing process and the electrical properties of these systems.
- FIG. 7 shows electrical resistivity as a function of SWNT composition. It is expected that the matrix does not play a significant role in the current processing methods.
- FIG. 8 illustrates the surface resistivity of ABS with VGCFs and SWNTs. Note that only 1% SWNTs are needed to achieve conduction from a well dispersed composite system.
- FIG. 9 a micrograph of a 10 wt.
- SWNT/ABS polymer which was fractured at room temperature shows good dispersion, absence of porosity, and the reduced entanglement of the nanotubes.
- the degree of entanglement is reduced since the high shear processing during mixing aids in dispersing the nanotubes from each other.
- SWNTs are wetted by the polymer, as indicated by places where nanotubes appear to be pulled out of the polymer. Some nanotubes are not coated by the polymer, indicating that the fiber/matrix shear strength and normal stress are still relatively low.
- PP with the following formula was used in this project: [—CH 2 CH(CH 3 )—]n (1) that was (1) isotactic, Melt flow index 1000, melting point of 160° C., and density of 0.900 and (2) isotactic, Melt flow index 12, melting point of 165° C. and density of 0.900.
- PE with the following formula was used in this project: (—CH 2 CH 2 —)n (2) that was (1) ultra-high molecular weight, melting temperature of 130° C. and density of 0.940 and (2) Melt flow index 10, Marlex from the Phillips Co., density of 0.94.
- PP1000 was not an optimum polymer to use for melt spinning but it was used to explore the limits of process rheology.
- the ultra high molecular weight PE was also not optimal for melt spinning but could be mixed with the SWNTs by a gel-spinning approach and thus show the extension of the process of this invention to gel-spinning applications.
- Polymers were typically prepared by drying in a hot box at 90-100° C. The slurries of SWNTs, and polymer were dried in a furnace at temperatures below the melting temperature of the polymers to remove the solvent. The resulting materials were polymers overcoated with an even distribution of nanotubes. This step provided the initial dispersion condition and one that would lead to easier dispersion of the nanotubes during the mixing of the melt.
- FIG. 10 gives torque data for the PP12 and PE10 systems which show very low values of torque indicating that mixing has ho problems with excessive viscosity as reported by others. Note that the torque is relatively low and very steady state once the initial mixing was conducted. In some cases, mixing speeds were ramped up from 60-65 rpm to 90 rpm to enhance mixing.
- the mixing parameters including temperature, time, and mixing rate were selected based on a process optimization study and on a database for Banbury mixing of thermoplastic polymers. The mixing and the extrusion could be accomplished in a multiple zone compounding extruder where the mixing residence could be held for sufficient time followed by extrusion of a well dispersed SWNT system. This provides a cost effective approach to making continuous fibers.
- FIG. 11 shows the significant, 100° C. higher, increase in the degradation temperature for PP with just 2 wt. % SWNTs.
- compositions of 1-10 wt. % in ABS were in part, amorphous carbon and catalysts since they were used to ensure numerous runs.
- Compositions shown on plots identify the composition of added nanotube material whether they were purified or not.
- FIG. 12 shows the type of increase observed in the modulus of polymers when SWNTs are added. Although this change for PE appears small (25%), the potential for creating a tough fiber exists over that seen for dispersed VGCFs due to remaining elongational properties of this polymer system.
- FIG. 13 shows the enhancement in properties that would be obtained of high extruder speed and take up speed are used.
- FIG. 13 details the strength of various fibers when processed at different extruder and take up speeds. High extruder speed coupled to high take up speed leads to stronger fibers. It is also known that use of a fast extruder speed with a take up speed that is high can lead to very small diameter fibers.
- FIG. 14 shows the fiber sizes for these processing conditions, more particularly a plot indicating the change in diameter of a fiber system when processed at high extruder speeds and subsequent high take up speeds.
- FIG. 15 provides a plot indicating the change in diameter of a fiber system when processed at slow extruder speeds and subsequent slow take up speeds. Larger diameter fibers result. Thus a range of fiber sizes can be processed according to customer needs.
- Fibers were analyzed using optical microscopy and SEM and were observed in some cases to have aligned nanotubes.
- the samples with compositions greater than 1 wt. % purified SWNTs were considered either ESD or EMI conducting.
- the samples with compositions greater than 2 wt. % purified SWNTs were EMI.
- the 10 wt. % sample was highly conducting and could be used as a plastic wire. A thick plastic wire was placed in an electrical circuit to light up LED's when powered by a DC power supply. This demonstrated a significant application for these new fibers that are being produced according to the invention.
- Both an extruder and a capillary rheometer were used to make fibers in this period of the program.
- a Stratasys Fused Deposition Modeling system could also be used to make continuous fibers. Shown below in FIG. 16 is the extrusion data collected while producing fibers from a single bore Haake extruder. Fibers were processed with the extruder. Using the extruder, one must consider die size, screw rate, and extruder temperature as well as the take up speed when the fibers are drawn out of the extruder. Processing must be at a condition where additional drawing out of the fiber can occur.
- a Rosand RH7 capillary extrusion rheometer was used to investigate the rheological behavior of nanotube-filled and unfilled polymers. It was also used, in conjunction with a spinning wheel take up system (not pictured), to extrude and extend filled and unfilled polymer fibers.
- the now uniform, temperature controlled melt is forced at a consistent flow rate through a capillary in a spinneret die.
- the hole is 100-500 ⁇ m diameter, and the polymer is squeezed out as a stream of fluid.
- the shear in the spinneret partially aligns the polymer molecules, but much of that alignment is lost when as the extrudate swells on exit from the die.
- the extrudate is quenched and drawn off from the bottom, stretching it thinner and longer. There are many types of quenching methods, but the essential characteristic of all of them is the controlled cooling of the filament as it is drawn.
- the stretching provides a degree of alignment that depends on the haul-off speed:
- the fiber After spinning, the fiber is cold-drawn—a vital step in orienting the polymer molecules. The higher the orientation from spinning, the lower the draw ratio in post drawing will be. An undrawn fiber will be extended by a factor of up to four in length as the molecules that make it up are further aligned.
- any fiber drawing process process control is of utmost importance.
- the melt must be consistent, the flow rate through the spinneret must be uniform, and the temperature must be well controlled.
- stresses in the melt which cause fracture or rupture must be avoided, as must a drawing tension which exceeds the strength of the filament.
- the best orientation of molecules in spinning comes when the extensional flow rates are high enough to provide alignment, and the relaxation time of the polymer is long enough so that any aligned molecules do not have a chance to recoil.
- alignment is associated with high spin speeds, high molecular weights, and good quenching efficiency.
- low speed spinning and subsequent cold drawing often produces more alignment than just high speed spinning.
- Low speed spinning and high speed spinning, with additional annealing, hot drawing does even better.
- the RH7 was used as the extruder for a low-speed fiber-spinning process.
- the essential needs of melt spinning were met, albeit with less process control over some areas of the process.
- the RH7 step motor provides excellent control over flow rates even while delivering well-controlled force to the melt.
- the dies found most suitable for fiber drawing were of 0.5 mm diameter; the best fibers were drawn through a 8-mm ⁇ 0.5-mm die, held in a “flat exit” die holder to allow the extrudate easy passage out of the barrel without danger of it getting stuck to the walls of a conventional die holder.
- the flat entry of the die is unlike that of a melt-spinning spinneret.
- the RH7 temperature control is accurate to 0.1° C.
- Fibers with diameters of 35-50 ⁇ m fibers were produced and were reduced to ⁇ 25 ⁇ m by stretching. Uniform thickness fibers with well dispersed SWNTs were produced. A number of the fibers had less than homogeneous dispersion due to the use of unpurified SWNTs in many of the cases. Use of the capillary rheometer led to uniform fibers but use of the extruder tended to produce fibers less uniform and in some cases with small enriched thickness sections. It is known in the art that a process assembly using an extruder calls for extruded melt to go into a fluid metering pump so that a constant pressure is maintained on the die or spinneret.
- FIG. 21 shows a micrograph of PP1000 showing well aligned SWNTs. Alignment was achieved in several fiber systems. The fibers produced using NTT nanotubes also showed alignment but on a limited basis because the SWNTs were only 25% of the starting material.
- the test rate used was 0.5 inches per minute, and the strain was calculated over the gage length (0.3 inches) because extensive deformation was not observed.
- the tensile strength was not improved.
- the average tensile strengths of both materials were 28 MPa.
- the strain to failure of the PP sample with SWNTs was improved by 115%.
- the pure polypropylene sample failed in steps as shown by the stress/strain curve.
- FIG. 23 shows the strength of a single fiber. The graph goes up to the highest load the bundle could withstand. Following this load, individual fibers began to fail. The addition of SWNT increased the tensile strength by 743% and the elongation to failure by 2964%.
- One important note to consider is that as these fibers get further developed they will surpass the bulk properties of PP even by aligning the polymer system itself. Aligned SWNTs along with aligned polymer may well produce enhanced strength rivaling that expected from single nanotubes themselves however, the elongation features of this system may be reduced to that of a well aligned polymer system.
- FIG. 24 shows various products and processing that can be achieved using NCFs. These commercial avenues for NCFs impact the highest percentage of the composite manufacturing industry. Beyond this, they impact the textile and fabric industry as well.
- ESD materials are needed for packaging purposes and also for garments, dissipative chairs, work benches, carpets and floor mats for the personnel working in the electronic manufacture site.
- ESD is a part of everyday life, but in the electronics industry, the cost of damage and rework due to static electricity is estimated to be of billions of dollars annually. Of all the failures in the electronic industry, approximately 40% are ESD related.
- the NCFs can be woven into crossplies for preforms, vacuum bagging and hand lay-ups. Aligned nanofibers are expected to deliver the most optimum mechanical properties for high performance composites. Assembled cross-ply systems still offer superior performance to isotropic composites since a higher degree of alignment can be more easily controlled for these systems.
- the present invention provides a revolutionary approach of processing nanofibers in an isotropic or anisotropic form as a continuous fiber composite providing control over the dispersion and alignment of the nanosize fibers in various polymer matrices. It illuminates a clear path to making aligned nanofibers available to the composite manufacturing community and other industries. It further provides for the opportunity to easily manipulate the nanofibers through additional processing like annealing, reactions, pyrolisys, further modification and functionalization. Polymers can be chosen to enhance or inhibit nanofiber alignment, or selected to be crosslinked or strongly bond to the nanofibers. The polymers themselves may be enhanced and altered by the nanofibers acting as nucleation sites and effecting crystallization and final polymer molecular morphologies. It solves the inherent problem of manipulating nanosize structures while taking advantage of commercial filament and fiber technology.
- the present invention provides an enhanced approach to achieve surface resistivities in the desired ESD range for the prevention of static electricity buildup. It provides a novel composition that can be prepared by conventional plastic processing technologies eliminating or ameliorating many of the problems associated with prior art fibers incorporation in plastic matrices and with processing of conductive plastics filled with metal fibers, flakes and powders or chemically modified polymers.
- the present invention shows purified and unpurified SWNTs, and vapor grown carbon nanofiber reinforced thermoplastic composites made into Nanofiber Continuous Fibers. These composites were prepared by mixing the purified and unpurified SWNTs, or vapor grown carbon nanofibers with the thermoplastic matrix in a Haake miniaturized internal mixer (MIM). The mixing process consisted of distributive mixing where the SWNTs or nanofibers were spread over different positions within the chamber and dispersive mixing where the application of high shear conditions and energy were required to overcome the nanofiber agglomerates. Different compositions by weight percent were prepared ranging from 0 to 60% of SWNTs or nanofibers (up to 10 wt. % SWNTs has been used).
- MIM Haake miniaturized internal mixer
- FIGS. 25-26 show NCFs with aligned nanofibers or SWNTs. Surface conditions of the NCFs can be varied as can degree of alignment and deagglomeration. FIGS. 27 and 28 depict these various conditions.
- nanofibers are black materials, the possibility of having transparent composite materials for specific applications becomes an issue.
- the composite can be thinned to be translucent so some visibility can be obtained (not that this applies to sheet forms).
- the alignment that occurs with nanotube continuous fiber processing can be achieved by Fused Deposition Modeling (FDM) processing.
- FDM Fused Deposition Modeling
- a spool of nanofiber reinforced polymer is formed into wire feedstock for the FDM process, a rapid prototyping (RP) process, also sometimes identified as a free form fabrication technique, is processed into final parts using computer generation of slices of a three dimensional (3D) image for layer by layer manufacturing.
- the alignment is due to shear processing by extrusion and some extensional flow while spooling (to achieve the desired diameter) and enhanced in the hot extrusion aspect of the FDM process.
- the nanofiber composite wire ⁇ 2 mm in diameter
- FDM feedstock can be made by producing wire by extrusion or by grouping NCFs with further processing to make wire.
- FDM FDM-based on-materials
- materials having reinforcing nanotubes which add to, in some cases, electrical and thermal properties
- parts with intricate internal shapes can be manufactured which in the case of other traditional technologies is either not possible, or it will be too costly since, in order to compensate the price, a few thousand parts have to be made.
- these parts include medical tools, electronic, replacement parts, etc.
- An example of space applications of FDM parts made with the material is the use of FDM on the Space Station where the superior feedstock (nanotube filled polymers) is used to make replacement parts, rather than storing supplies of parts in the limited space on the Space Station.
- Vapor grown carbon fibers mixed with various polymers are proving to be a good approach to producing polymeric composites using nanotubes.
- VGCFs can be mixed through shear processing without nanofiber breakage and high degrees of dispersion can be achieved originating from a tangled mass.
- functionalized nanotubes can be more fully integrated into polymeric systems.
- the processing “Bandury” mixing was used to produce feedstock continuous filament for Fused Deposition Modeling (FDM), enabling composite part manufacturing for a range of applications and well past material property evaluation.
- Nanofiber composites significantly enhance rapid prototyping techniques like FDM, SLS, etc. because of their potential for enhancing polymeric properties as a multifunctional material (structural/electrical, structural/thermal, structural/impact).
- FDM is a manufacturing process that takes a feedstock (continuous filament or billet) and hot extrudes it to make continuous traces of polymer material.
- the traces map out a layer and subsequent layers can be deposited on top to build up 3-dimensional shapes. Any number of sample forms can be produced as long as a 3-D computer image can be generated. That file is then cut into slices to match the process parameters for the FDM.
- the FDM unit then builds the part ( ⁇ bottom up technology”) layer by layer starting from a removable support.
- FDM parts are generally used for models, molds and for some part applications where material usage is optimized (waste is minimized) and tooling and part finishing is reduced.
- feedstock materials include wax-filled plastic adhesives, nylon copolymers, investment casting waxes and acrylonitrile-butadiene-styrene (ABS).
- ABS is the more optimal for part applications because of its superior strength to the other materials available.
- Composite feedstocks filled with various reinforcements, including chopped carbon fibers, are now being developed with the purpose of enhancing mechanical strength of FDM parts.
- filled polymers are of interest because they have the potential of improving interlayer strength, many times the weak link in FDM parts, and to enhance stiffness which is often seen in filled polymers.
- the availability of high strength polymers for FDM extends its use in part manufacturing and extends its application range.
- three feedstocks were produced using (1) purified VGCFs, (2) pelletized VGCFs, and (3) as-received SWNTs.
- Pelletized in this case, is a processing method to improve handling where a latex sizing is placed on the nanofibers from the commercial producer.
- the as-received SWNTs provided illustrative processing of SWNTs with ABS using high shear and FDM processing. A number of different parts were produced including three different tensile tests part sizes. Parts were also made connecting plain ABS to the VGCF composite to show that the new materials can work in conjunction with the currently available ABS.
- FDM In the FDM process the wire is fed between two friction bearing rollers that account for velocity control. This process is conducted in a temperature control chamber that terminates in a circular die. The temperature is maintained just above the solidification point. When the material exits the die it solidifies as it is directed into place with the X—Y controlled extruding nozzle.
- FDM consists of the deposition of continuous layers next to and on top of each other to build the specified model under CAD control. The successive layers are bonded by thermal fusion. The heat capacity of the material is important to the amount of shrinkage and the degree that the material fuses to itself.
- FDM work was conducted involving filled feedstocks for producing ceramic filled polymers for prepreg applications.
- the filled polymers are used to trace out a mold that is subsequently sintered to form a ceramic part.
- the polymer is burned out, leaving behind a porous ceramic pre-form which can be infiltrated with metals of other matrix materials.
- VGCFs known as Pyrograph III with an average diameter of 100 nm were obtained from Applied Science, Inc. in as-received and pelletized forms.
- the as-received VGCFs were purified and functionalized before the compounding stage according to previously developed procedures.
- the ABS GMID #31875 was obtained from Magnum. ABS was chosen because of its high strength and use in FDM. Typical properties for ABS are listed in Table I along with those for the VGCFs.
- Composite preparation was conducted using a HAAKE torque rheometer using a 30 g mixing bowl. ABS was compounded with the various nanofibers at high shear rates to achieve a homogeneous dispersion. Dispersion, in this case, means homogeneous spread of the fibers and individually isolated fiber forms (either individual VGCFs or individual ropes). Starting sample compositions of 10 wt. % were prepared. Samples were hot compression molded and pelletized (chopped up into small pellets) to use as a feed material for the wire extrusion. Composite batches were then extruded at a rate of 5 rpm and spooled on to a reel-type container while maintaining a constant cross-section for the length of the wire extruded.
- extruded samples of plain ABS, with VGCFs and with SWNTs had a diameter of 1.7 ⁇ 0.1 mm which was optimum for the FDM processes.
- Extrusion to form the wire for all composites was conducted by starting the extrusion with plain ABS pellets, followed by the composite material, and finished off with plain ABS again to sufficiently fill the extruder barrel. This approach caused the composite of the wire feedstock to vary over the length of the wire so that the maximum composition achieved was 10 wt. % at the middle of the extrusion run.
- the insert shows the schematic of the FDM process showing the extruder tip drawing out polymeric traces being built into layers. The arrows indicate the ability of the extruder to traverse the surface.
- FDM traces were, in all cases, cross-plied with either 90°/180° or 45°/45° orientations.
- Mechanical tests were conducted using a MTS hydraulic tester. The tests were carried out at a strain rate of 2.54 cm/min at room temperature. Care was taken in the placement and orientation of the samples to better understand alignment of the sample effects and those that might be associated with the orientation of the FDM growth process (top and bottom orientations).
- the nanofiber/ABS composites have showed improvements in tensile properties over the unfilled ABS processed at the same conditions.
- Composites tested were from the pelletized VGCFs. These samples were processed with 90°/180° cross-ply conditions. The data for the ABS is relatively consistent, as would be expected from a FDM process.
- the tensile test results for the VGCF/ABS data showed significant scatter related to concentration changes and the lower amount of swelling that occurs in the filled ABS. Scatter in the data is also thought to be related to the variation in the feedstock diameter which would also occur in the traces as the samples are processed. Feedstock wire (filament) was hand-spooled on the spools to be used in FDM and this would lead to variations in the tensile test properties.
- FIG. 29 shows tensile test results following correction for the cross-plying where only half of the sample is effectively tested due to 90°/180° cross-plies. Note again the consistency in the ABS data and the variation in the VGCF/ABS results. This difference is a 65% increase over the unfilled ABS, a significant increase even though there was limited wetting. Table 2 shows the results for the SWNT/ABS material.
- FIG. 30 shows a micrograph of the polymer composite microstructure where the as-received SWNTs are not well dispersed. Non-nanotube material (amorphous carbon and metal catalyst) hinder the shear mixing of the nanotubes. The improvement in strength is important yet not critical since the mixing was not homogeneous.
- FIG. 31 shows the longitudinal cross-section of the wire feedstock.
- the arrow indicates the axial direction of the wire.
- the extrusion high shear condition and the extensional flow during wire spooling caused alignment of the nanofibers. Shown are a high degree of aligned VGCFs which are well dispersed and not bunched up with each other. Since the fibers appear very clean and the polymer is not highly deformed around the fibers, wetting is described as poor with a low level of resistant occurring with fiber pull-out. The fibers have similar lengths to the starting conditions and are undamaged from the high shear that occurs in the mixing and extrusion processes.
- XRD was used to further evaluate the VGCF alignment and Table 3 shows the results for several samples of the feedstock evaluated. The existence of the preferential fiber orientation definitively contributed to strength enhancement since isotropic samples showed no strength variations in a previous study.
- the ABS samples consistently showed good inter-trace fusion as seen in FIG. 32 although it was not ideal.
- the VGCF/ABS samples showed a variation in fusion conditions which tended to match the tensile results and the scatter observed. Shown in FIG. 32 are samples with six layers,(which were cross-plied 90°/180°. Note that interlayer strength is still low for the VGCF/ABS, in part because the FDM is not optimized in its process parameters for the lower swelling of the feedstock material (associated with different thermal properties of the filled material). Limited porosity is also observed in some cases in the VGCF/ABS traces which is attributed to the extrusion process and not to the initial Banbury mixing.
- FIG. 32 and FIG. 33 which shows the directions of traces in a 90°/180° cross-ply samples is can be shown that the traces during FDM processing also resulted in conditions of aligned VGCFs.
- FIG. 34 shows the two conditions depicted in FIG. 33 .
- Micrograph (a) shows a trace produced with the axial direction of the trace shown as the area indicates.
- Figure (b) shows a condition where the trace is effectively pointed out of the page so that the axial direction of the trace is coming out of the page. Note again the alignment conditions, the dispersion and the absence of clustering of the VGCFs.
- the conferred effect of the nanofibers on the fracture behavior of ABS is similar to the fracture behavior of tightly cross-linked resins where the molecular network is unable to deform sufficiently.
- the nanofibers decreased the resistance to yield acting as constraints for chain mobility.
- the decrease in chain mobility increased the stiffness of the material which was first observed by the differences in swelling on the extrusion process.
- the toughness of the composite is therefore lower than that of the pure ABS but the strength and rigidity are improved.
- the material of the present invention has the potential to provide multifunctional properties. This is to say that, while the material is structural, it may also be a thermal management system and or an electrostatic discharge material (or electromagnetic interference material).
- This new material initially described as NCFs, would be a new multifunctional material system that could be manufactured into a range of parts for mechanical, electrical, thermal, or combined applications. Examples of NCFs are mechanical/electrical, mechanical/thermal, electrical/mechanical, impact/strength, and impact/electrical or thermal. NCF can be made with a ceramic matrix, and there are FDM-like systems (a robocaster) for making parts with a ceramic matrix.
- the FDM can further be used to make nanofiber continuous fibers.
- the FDM can be used to extrude out fiber where high shear and elongational flow are implemented. In the die the shearing action takes place and subsequent elongational flow can be achieved as the material leaves the die.
- Conitinuous fibers with 10 wt. % VGCFs and 10 wt. % as-received SWNTs have been processed from a FDM.
- SWNT single wall nanotube
- SNP single wall nanotube
- tip attachment and/or side wall functionalization
- coincident polymerization and high shear alignment.
- This path will provide for hybrid materials that will be designed to expand out the properties of the single nanotubes by translating their properties to each other. This is to say, material that might be considered the matrix must be nanotube like as well.
- nanotube to polymer connections are designed to foster enhanced mechanical properties.
- the first step in this path is through mimicking a polymer (polymer processing) followed by designing an architecture for mimicking nanotubes.
- the second concept leading to the goal of mimicking nanotubes involves identifying the properties of nanotubes in other systems where those properties can be fostered for materials enhancement.
- the starting system is a nanosize graphitic material similar to SWNTs in that it must be separated from itself before subsequent processing.
- small flakes of graphite can be separated on the individual flake basis where no defects occur in the flake (much like for nanotubes).
- the flakes would be bonded through available bonds on the outside of the flakes in a similar way that we would functionalize the tips or the outside wall of the nanotubes.
- nanometer size carbon sheets rather than tubes are identified which mimic nanotubes in a number of ways. A number of bonding conditions for the nanotube-like materials translate back to nanotube advanced materials developments.
- the present disclosure describes the methods to produce a highly conductive polymeric wire and interconnect system with good stability of the conduction properties and permeable plastics to alter conduction by gas interaction.
- Methods of the present invention provide highly conducting polymers resembling metallic-like conduction properties such as that for polyacetylene (PA) but more stable or with higher environmental stability.
- Processing from a polymer basis of nylon, poly(methyl methacrylate) (PMMA), and conducting epoxy develops a polymer architecture for mimicking nanotubes.
- Conducting epoxy is a polymer that can be processed with insulating, semiconducting or conducting properties. Processing further will enhance its stability, its conducting properties and provide a high temperature polymer system. These materials can be used for wire and other interconnects. Extending their properties for multifunctional use also enhance the thermal and structural properties of these material. Gas permeable polymers are considered to alter the electrical conduction by gas exposure.
- the derivatization or functionalization of SWNTs opens the way to new approaches in making advanced hybrid materials that are a cross between polymers and composites.
- the traditional composite mixing with carbon fibers is limited in the amount of interaction and bonding of the nanotubes with the polymer matrix.
- Sidewall and tip functionalization provide attachment of different organic groups to modify and control the bonding and interactions with the polymer.
- the purified nanotube materials as currently available, consist of tangled bundles of SWNTs ropes. Mixing such material with polymers gives physical linking with the random polymer coils and the random nanotube tangles becoming intermingled during mixing. This limits the dispersability of the nanotubes, and the homogeneity of the resulting composites.
- SWNTs can be derivatized on the open edges, which become decorated with oxygen groups (hydroxyl, ketone, carboxylic acids) by sonication treatment in acid.
- the carboxylic acid group can react with amines to form amide bonds, which allows the attachment of compatibilizing groups to increase the interactions with the polymer matrix.
- Aliphatic and aromatic chains of different lengths can be attached and these organic chains can also have polar groups such as ester, ether, amides, or terminal amino groups, which can be used to create hydrogen bonding interactions with suitable polymer matrices.
- Organic chemistry can be used to modify the functional groups in the attached molecules, allowing for complete control of the interactions with the polymer. The left side of FIG.
- FIG. 35 shows the attachment of polymer chains to the oxidized edge of a cut SWNT via amide linkages.
- the left part shows the attachment of an organic molecule that can act as compatibilizer for a polymer matrix.
- the center of the figure shows how the attachment of a reactive molecule (in this case a double bond) can be used as the starting point of a polymer chain.
- the polymer chain will be directly attached to the SWNT tip, as shown in the right part of the figure.
- the attached organic molecules can also serve as a starting point for polymerization, and an example is shown in FIG. 35 where attaching a molecule with a double bond can be used for the radical polymerization of polyethylene.
- the polymer chains formed will be directly attached to the open nanotube tip. During polymerization, two growing polymer chains may join, creating random length polymer links between SWNTs. It is also likely that more than one polymer chain will start from an open nanotube tip. This is expected to result in the nanotube acting as a crosslinking agent between polymer chains, as exemplified in FIG. 37 , a representation of crosslinking that may result from random polymerization starting at SWNT tips.
- Nanotube block co-polymers envisions activating the nanotube tips by adding a functional group (x), that will react with functional groups (y) at the ends of polymer block of a monomer A.
- the resulting polymer would be a “nanotube block copolymer”, where the nanotube is an integral part of the composite, and chemically bonded to the polymer matrix.
- the polymer blocks can be selected to have different properties, chemical backbones, reactivity, lengths and length distributions. Varying the nature and length of the polymer chains between the nanotubes will allow us to selectively vary properties of the composite. It is also possible to have a different polymer block (B) to have further modifications and control of the properties of the nanotube block copolymer. Different alternations of the blocks (polymer A, polymer B, nanotube) are possible, as shown in FIG. 39 , two different possible configurations for nanotube block co-polymers, with alternating polymer blocks.
- Crosslinking can also occur in these cases, and the amount of crosslinking can be controlled by limiting the amount of reagent that will create the functional group x on the open nanotube tips. In this way the average amount of “activated” sites is controlled. Closed SWNT tips can also be modified by applying the knowledge of fullerene chemistry which would allow more options for the attachment of functional groups that will link the polymer to the nanotube. Another possibility is to use functionalized SWNTs in a graft copolymerization as shown in FIG. 40 , nanotube graft copolymer with the nanotubes acting as crosslinking agents.
- the polymer with a chain containing reactive groups can be mixed with “activated” nanotubes, which can be made to bond to the sides of the chain.
- This approach can also result in crosslinks, with the nanotubes bridging between polymer chains.
- the tips can be attached to a solid support, the exposed tip “deactivated” and the other tip derivatized to react with the polymer chain as shown in FIG. 41 , nanotube graft copolymer where only one side of the nanotube can attach to the polymer chain.
- a second approach is to use sidewall derivatization of single-walled nanotubes.
- the sidewalls of the nanotubes can be fluorinated, and control of the amount of fluorination is possible (up to a stoichiometry of C2F).
- the fluorine groups can be substituted by organic groups, as previously shown for alkyl chains. Several different terminal organic groups could be attached to the sidewall, and further modified by organic chemistry techniques.
- modification of the sidewall can be used to control the interactions of the polymers and the nanotubes, making the SWNTs compatible with several polymer matrices with or without polar groups.
- the fluorinated and alkylated SWNTs would also be dispersed as individual tubes to form stable suspensions in polar solvents (e.g. alcohols), allowing for easier manipulation, dispersability, as well as doing chemistry on the sidewalls.
- Having reactive groups on the walls allows for polymerization to start from the nanotubes, in a way similar to the one sketched in the right side of FIG. 35 .
- the nanotube acts as a multifunctional starter for polymerization, and the resulting polymer nanotube composite will most likely be heavily crosslinked, possibly resulting in a thermoset nature of the final product.
- the expected structure is sketched in FIG. 42 , side-wall attached polymer-nanotube composite, with random polymerization creating crosslinking.
- FIG. 43 illustrates “Hairy-tube composites”.
- Left side SWNTs over a substrate, only the exposed surface is covered with polymer.
- Right side Tips of SWNTs attached to a solid support, with the possibility of controlling the length and crosslinking of the polymer chains.
- Another possibility is to use the chemistry of the tips to attach the nanotubes to solid supports, creating “hairy-tube composites”.
- the amounts of polymerization initiation groups in the tube walls can be varied, the probability of crosslinking can be controlled by spacing the attachment points of the nanotubes, and by controlling the degree of polymerization.
- a concept sketch of this approach is shown in the right panel of FIG. 43 . Control of the length of polymer chains attached to the nanotubes allows control over the properties of the final composite. Several different polymer chains can be attached this way, without concern over the adequacy of the solvent for suspending or dissolving the nanotubes.
- the attachment of the SWNT tips to a solid support can also be an approach to create nanotube block co-polymers, like those shown in FIGS. 39 and 40 .
- Polymerization can be started from the exposed tip, or a polymer block can be attached to it.
- This approach can also be used to polymerize alternating monomers, in a way analogous to the Merrifield solid phase syntheses of peptides in biochemistry. After detaching the nanotube from the solid support it is possible to attach another polymer to the unreacted tip, or to use it to graft the nanotube-block copolymer to side groups in a different polymer.
- the aligned SWNTs advanced polymers that can be made in this way are shown in one example in FIG. 45 , nanotubes shear oriented and then chemically bonded to the polymer matrix.
- Combining polymerization with high shear alignment methods we can produce a system analogous to Kevlar or ultra high density polyethylene where the nanoscale features are highly aligned and therefore lead to enhanced properties.
- the idea of mimicking SWNTs starts to take over.
- Providing bonding to continue the enhancements that can be achieved by the nanotubes is the important selection point for this research.
- the conducting polymers will have a significant conducting range as to how they are processed, coupling to gas permeable plastics so that gas detection can occur is possible. Interactions with gases will alter the conduction providing a sensing capability to the wire of sheet configurations.
- SWNT purification, separation, functionalization, and combining SWNTs with gas permeable polymers, and tailoring conduction and percolation these systems may well be used to alter electrical conduction of the conducting polymers when in contact with various gases.
- FIG. 46 shows how one would typically design a composite system compared to that expected for SWNTs in an epoxy matrix. Note that for the nanocomposite, of is not the ultimate strength of the nanotube but ⁇ f ( ⁇ ) since the matrix fails at a much lower strain than the reinforcement.
- FIG. 47 shows by means of the Kelly-Tyson equation the expected composite strength of a SWNT composite with off axis alignment. Note the further reduction in composite strength due to low shear strength and normal stresses. For these various reasons, extensions in processing with SWNTs to produce advanced materials must be accomplished by looking beyond what has been the typical approach of the past. Although the use of rule of mixture calculations and the Kelly-Tyson equations may not be ideal or used appropriately for nanotube composites, one gains a sense that there are significant shortcomings by more conventional composite manufacturing approaches. Composite strength vs. the orientation of the SWNTs when considered to be fully aligned.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Health & Medical Sciences (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Manufacturing & Machinery (AREA)
- Materials Engineering (AREA)
- Nanotechnology (AREA)
- Textile Engineering (AREA)
- General Chemical & Material Sciences (AREA)
- Composite Materials (AREA)
- Mechanical Engineering (AREA)
- Crystallography & Structural Chemistry (AREA)
- Ceramic Engineering (AREA)
- Civil Engineering (AREA)
- Structural Engineering (AREA)
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Reinforced Plastic Materials (AREA)
- Artificial Filaments (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/149,216 US20060047052A1 (en) | 1999-12-07 | 2000-12-07 | Oriented nanofibers embedded in polymer matrix |
US12/025,626 US7897248B2 (en) | 1999-12-07 | 2008-02-04 | Oriented nanofibers embedded in a polymer matrix |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US16927399P | 1999-12-07 | 1999-12-07 | |
US10/149,216 US20060047052A1 (en) | 1999-12-07 | 2000-12-07 | Oriented nanofibers embedded in polymer matrix |
PCT/US2000/033291 WO2001092381A1 (fr) | 1999-12-07 | 2000-12-07 | Nanofibres orientees noyees dans une matrice de polymere |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/025,626 Continuation US7897248B2 (en) | 1999-12-07 | 2008-02-04 | Oriented nanofibers embedded in a polymer matrix |
Publications (1)
Publication Number | Publication Date |
---|---|
US20060047052A1 true US20060047052A1 (en) | 2006-03-02 |
Family
ID=22614952
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/149,216 Abandoned US20060047052A1 (en) | 1999-12-07 | 2000-12-07 | Oriented nanofibers embedded in polymer matrix |
US12/025,626 Expired - Fee Related US7897248B2 (en) | 1999-12-07 | 2008-02-04 | Oriented nanofibers embedded in a polymer matrix |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/025,626 Expired - Fee Related US7897248B2 (en) | 1999-12-07 | 2008-02-04 | Oriented nanofibers embedded in a polymer matrix |
Country Status (10)
Country | Link |
---|---|
US (2) | US20060047052A1 (fr) |
EP (1) | EP1244730B1 (fr) |
JP (1) | JP5770962B2 (fr) |
KR (1) | KR100810977B1 (fr) |
CN (1) | CN1433443B (fr) |
AT (1) | ATE355323T1 (fr) |
AU (1) | AU2577101A (fr) |
CA (1) | CA2394955C (fr) |
DE (1) | DE60033692T2 (fr) |
WO (1) | WO2001092381A1 (fr) |
Cited By (59)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20050074390A1 (en) * | 2001-01-29 | 2005-04-07 | William Marsh Rice University | Process for making polymers comprising derivatized carbon nanotubes and compositions thereof |
US20060166003A1 (en) * | 2003-06-16 | 2006-07-27 | William Marsh Rice University | Fabrication of carbon nanotube reinforced epoxy polymer composites using functionalized carbon nanotubes |
US20070104947A1 (en) * | 2001-08-16 | 2007-05-10 | Shambaugh Robert L | Nanotube/matrix composites and methods of production and use |
US20070110977A1 (en) * | 2005-08-29 | 2007-05-17 | Al-Haik Marwan S | Methods for processing multifunctional, radiation tolerant nanotube-polymer structure composites |
US20070117488A1 (en) * | 2003-06-30 | 2007-05-24 | Kuniyoshi Yokoh | Electron-emitting woven fabric and display device using same |
US20070290410A1 (en) * | 2005-07-29 | 2007-12-20 | Koo Joseph H | Fire retardant polymer nanocomposites for laser sintering |
US20080093577A1 (en) * | 2006-06-21 | 2008-04-24 | Khraishi Tariq A | Metal-carbon nanotube composites for enhanced thermal conductivity for demanding or critical applications |
US20080160290A1 (en) * | 2006-08-30 | 2008-07-03 | Korea Electrotechnology Research Institute | Aligned nanoparticle channel and method of fabricating aligned nanoparticle channel by applying shear force to immiscible binary polymer-blended nanoparticle composite |
WO2009001324A2 (fr) * | 2007-06-27 | 2008-12-31 | Arkema France | Utilisation de nanotubes, notamment de nanotubes de carbone pour améliorer les propriétés mécaniques à température élevée d'une matrice polymère |
US20100188833A1 (en) * | 2009-01-28 | 2010-07-29 | Florida State University Research Foundation | Electromagnetic interference shielding structure including carbon nanotube or nanofiber films and methods |
WO2011005279A1 (fr) * | 2009-07-08 | 2011-01-13 | Toyo Boseki Kabushiki Kaisha | Procédé de fabrication de fibre polyéthylène de forte résistance et fibre polyéthylène de forte résistance |
US20110024694A1 (en) * | 2009-02-17 | 2011-02-03 | Lockheed Martin Corporation | Composites comprising carbon nanotubes on fiber |
US20110098406A1 (en) * | 2008-07-08 | 2011-04-28 | Toyo Boseki Kabushiki Kaisha | Method for Producing High Strength Polyethylene Fiber and High Strength Polyethylene Fiber |
US20110117316A1 (en) * | 2005-09-06 | 2011-05-19 | Lemaire Charles A | Method and apparatus for growing fullerene nanotube forests, and forming nanotube films, threads and composite structures therefrom |
US20110123735A1 (en) * | 2009-11-23 | 2011-05-26 | Applied Nanostructured Solutions, Llc | Cnt-infused fibers in thermoset matrices |
US20110124483A1 (en) * | 2009-11-23 | 2011-05-26 | Applied Nanostructured Solutions, Llc | Ceramic composite materials containing carbon nanotube-infused fiber materials and methods for production thereof |
US20110135491A1 (en) * | 2009-11-23 | 2011-06-09 | Applied Nanostructured Solutions, Llc | Cnt-tailored composite land-based structures |
US20110143087A1 (en) * | 2009-12-14 | 2011-06-16 | Applied Nanostructured Solutions, Llc | Flame-resistant composite materials and articles containing carbon nanotube-infused fiber materials |
US20110186775A1 (en) * | 2010-02-02 | 2011-08-04 | Applied Nanostructured Solutions, Llc. | Carbon nanotube-infused fiber materials containing parallel-aligned carbon nanotubes, methods for production thereof, and composite materials derived therefrom |
WO2014074397A1 (fr) | 2012-11-07 | 2014-05-15 | Bayer Materialscience Llc | Procédé d'incorporation d'un polymère conducteur ionique dans un article en polymère pour obtenir un comportement anti-statique |
US8795561B2 (en) | 2010-09-29 | 2014-08-05 | Milliken & Company | Process of forming a nanofiber non-woven containing particles |
US8889572B2 (en) | 2010-09-29 | 2014-11-18 | Milliken & Company | Gradient nanofiber non-woven |
US9017854B2 (en) | 2010-08-30 | 2015-04-28 | Applied Nanostructured Solutions, Llc | Structural energy storage assemblies and methods for production thereof |
WO2013123023A3 (fr) * | 2012-02-14 | 2015-07-09 | Toray Industries, Inc. | Composition de composite de polymère renforcé par des fibres, ayant des nanofibres alignées |
WO2015102580A1 (fr) * | 2013-12-30 | 2015-07-09 | Halliburton Energy Services, Inc. | Bouillies liquides de matières solides de dimension micrométrique et nanométrique en vue d'une utilisation dans des opérations souterraines |
WO2015184151A1 (fr) * | 2014-05-28 | 2015-12-03 | University Of South Alabama | Appareil et procédé pour l'alignement directionnel de nanofibres dans un milieu poreux |
US20160144566A1 (en) * | 2013-03-22 | 2016-05-26 | Markforged, Inc. | Three dimensional printing of composite reinforced structures |
US9976011B2 (en) | 2010-07-14 | 2018-05-22 | The Curators Of The University Of Missouri | Polymer composites and fabrications thereof |
US20180222601A1 (en) * | 2013-11-15 | 2018-08-09 | Honeywell International Inc. | Fire-and electromagnetic interference (emi)-resistant aircraft components and methods for manufacturing the same |
US10046511B1 (en) | 2017-12-26 | 2018-08-14 | Arevo, Inc. | Alleviating torsional forces on fiber-reinforced thermoplastic filament |
US20180363168A1 (en) * | 2017-06-20 | 2018-12-20 | Zhejiang Jinhao Specialty Fiber Co., Ltd. | Method of preparing wear and cut resistant uhmwpe fibers |
US20190193328A1 (en) * | 2017-12-26 | 2019-06-27 | Arevo, Inc. | Depositing Arced Portions of Fiber-Reinforced Thermoplastic Filament |
US10370510B2 (en) * | 2013-10-08 | 2019-08-06 | Stratasys, Inc. | Consumable filaments having reversible reinforcement for extrusion-based additive manufacturing |
US10603841B2 (en) | 2013-03-22 | 2020-03-31 | Markforged, Inc. | Multilayer fiber reinforcement design for 3D printing |
US10611082B2 (en) | 2013-03-22 | 2020-04-07 | Markforged, Inc. | Apparatus for fiber reinforced additive manufacturing |
US20200148841A1 (en) * | 2016-07-22 | 2020-05-14 | Rutgers, The State University Of New Jersey | In Situ Bonding of Carbon Fibers and Nanotubes to Polymer Matrices |
US10682844B2 (en) | 2013-03-22 | 2020-06-16 | Markforged, Inc. | Embedding 3D printed fiber reinforcement in molded articles |
US10696039B2 (en) | 2013-03-22 | 2020-06-30 | Markforged, Inc. | Multilayer fiber reinforcement design for 3D printing |
US10717228B2 (en) | 2013-03-22 | 2020-07-21 | Markforged, Inc. | Three dimensional printing |
US10821662B2 (en) | 2013-03-22 | 2020-11-03 | Markforged, Inc. | Methods for fiber reinforced additive manufacturing |
US10850429B2 (en) | 2014-11-03 | 2020-12-01 | Arkema France | Process for densification of poly(arylene ether ketone) powders |
US10953609B1 (en) | 2013-03-22 | 2021-03-23 | Markforged, Inc. | Scanning print bed and part height in 3D printing |
US10953610B2 (en) | 2013-03-22 | 2021-03-23 | Markforged, Inc. | Three dimensional printer with composite filament fabrication |
US20210187788A1 (en) * | 2018-05-31 | 2021-06-24 | Lintec Corporation | Method of producing carbon-resin composite material, and composite structure for producing carbon-resin composite material |
US11065861B2 (en) | 2013-03-22 | 2021-07-20 | Markforged, Inc. | Methods for composite filament threading in three dimensional printing |
US11098175B2 (en) | 2012-10-19 | 2021-08-24 | Rutgers, The State University Of New Jersey | In situ exfoliation method to fabricate a graphene-reinforced polymer matrix composite |
US11174366B2 (en) | 2013-04-18 | 2021-11-16 | Rutgers, The State University Of New Jersey | In situ exfoliation method to fabricate a graphene-reinforced polymer matrix composite |
US11225558B2 (en) | 2014-07-30 | 2022-01-18 | Rutgers, The State University Of New Jersey | Graphene-reinforced polymer matrix composites |
US11237542B2 (en) | 2013-03-22 | 2022-02-01 | Markforged, Inc. | Composite filament 3D printing using complementary reinforcement formations |
US11479653B2 (en) | 2018-01-16 | 2022-10-25 | Rutgers, The State University Of New Jersey | Use of graphene-polymer composites to improve barrier resistance of polymers to liquid and gas permeants |
US11479652B2 (en) | 2012-10-19 | 2022-10-25 | Rutgers, The State University Of New Jersey | Covalent conjugates of graphene nanoparticles and polymer chains and composite materials formed therefrom |
US11504892B2 (en) | 2013-03-22 | 2022-11-22 | Markforged, Inc. | Impregnation system for composite filament fabrication in three dimensional printing |
US20230212793A1 (en) * | 2018-04-20 | 2023-07-06 | Mermet | Composite Yarn, Manufacturing Process and Textile Surface Comprising Such a Yarn |
US11702518B2 (en) | 2016-07-22 | 2023-07-18 | Rutgers, The State University Of New Jersey | In situ bonding of carbon fibers and nanotubes to polymer matrices |
US11759990B2 (en) | 2013-03-22 | 2023-09-19 | Markforged, Inc. | Three dimensional printing |
US11760640B2 (en) | 2018-10-15 | 2023-09-19 | Rutgers, The State University Of New Jersey | Nano-graphitic sponges and methods for fabricating the same |
US11787104B2 (en) | 2013-03-22 | 2023-10-17 | Markforged, Inc. | Methods for fiber reinforced additive manufacturing |
US11807757B2 (en) | 2019-05-07 | 2023-11-07 | Rutgers, The State University Of New Jersey | Economical multi-scale reinforced composites |
US11981069B2 (en) | 2021-09-16 | 2024-05-14 | Markforged, Inc. | Three dimensional printing of composite reinforced structures |
Families Citing this family (136)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
ATE494261T1 (de) | 1999-10-27 | 2011-01-15 | Univ Rice William M | Makroskopische geordnete anordnung von kohlenstoffnanoröhren |
WO2002016257A2 (fr) * | 2000-08-24 | 2002-02-28 | William Marsh Rice University | Nanotubes de carbone a paroi simple, enrobes de polymere |
US6682677B2 (en) * | 2000-11-03 | 2004-01-27 | Honeywell International Inc. | Spinning, processing, and applications of carbon nanotube filaments, ribbons, and yarns |
GB2411169B (en) * | 2001-01-29 | 2005-10-26 | Univ Rice William M | Process for derivatizing carbon nanotubes with diazonium species and compositions thereof |
AU2002254367B2 (en) | 2001-03-26 | 2007-12-06 | Eikos, Inc. | Coatings containing carbon nanotubes |
JP2004529840A (ja) | 2001-03-26 | 2004-09-30 | エイコス・インコーポレーテッド | 構造体と修復用組成物におけるカーボンナノチューブ |
WO2002100931A1 (fr) | 2001-06-08 | 2002-12-19 | Eikos, Inc. | Dielectriques nanocomposites |
US7288238B2 (en) | 2001-07-06 | 2007-10-30 | William Marsh Rice University | Single-wall carbon nanotube alewives, process for making, and compositions thereof |
US7125502B2 (en) | 2001-07-06 | 2006-10-24 | William Marsh Rice University | Fibers of aligned single-wall carbon nanotubes and process for making the same |
US6878361B2 (en) | 2001-07-10 | 2005-04-12 | Battelle Memorial Institute | Production of stable aqueous dispersions of carbon nanotubes |
US6896864B2 (en) | 2001-07-10 | 2005-05-24 | Battelle Memorial Institute | Spatial localization of dispersed single walled carbon nanotubes into useful structures |
AU2002332422C1 (en) | 2001-07-27 | 2008-03-13 | Eikos, Inc. | Conformal coatings comprising carbon nanotubes |
EP1436196A4 (fr) * | 2001-09-18 | 2008-08-27 | Eikos Inc | Revetements dissipateurs d'electrostatique destines a etre utilises sur des engins spatiaux |
US7048963B2 (en) | 2001-11-30 | 2006-05-23 | Cambridge Polymers Group, Inc. | Layered aligned polymer structures and methods of making same |
US6921462B2 (en) | 2001-12-17 | 2005-07-26 | Intel Corporation | Method and apparatus for producing aligned carbon nanotube thermal interface structure |
US6965513B2 (en) | 2001-12-20 | 2005-11-15 | Intel Corporation | Carbon nanotube thermal interface structures |
US7423084B2 (en) | 2002-02-15 | 2008-09-09 | Dsm Ip Assets B.V. | Method of producing high strength elongated products containing nanotubes |
EP1336672A1 (fr) * | 2002-02-15 | 2003-08-20 | Dsm N.V. | Procédé de fabrication de produits allongés à haute ténacité contenant des nanotubes de carbone |
EP1478692A2 (fr) * | 2002-02-20 | 2004-11-24 | Electrovac Fabrikation Elektrotechnischer Spezialartikel GmbH | Composites polymeres ignifugeants et procede de fabrication |
US6764628B2 (en) * | 2002-03-04 | 2004-07-20 | Honeywell International Inc. | Composite material comprising oriented carbon nanotubes in a carbon matrix and process for preparing same |
EP1349179A1 (fr) * | 2002-03-18 | 2003-10-01 | ATOFINA Research | Polyoléfines conductrices possédants des bonnes propriétés mécaniques |
US6856016B2 (en) | 2002-07-02 | 2005-02-15 | Intel Corp | Method and apparatus using nanotubes for cooling and grounding die |
AU2003266625A1 (en) * | 2002-09-30 | 2004-04-23 | Bridgestone Corporation | Orientated carbon nanotube composite, process for producing orientated carbon nanotube composite, and, produced using orientated carbon nanotube composite, pneumatic tire, wheel for vehicle, tire wheel assembly and disk brake |
DE60334843D1 (de) * | 2002-11-27 | 2010-12-16 | Univ Rice William M | Verbundwerkstoffe aus funktionalisierten nanoröhren und polymer und wechselwirkungen mit strahlung |
US7316061B2 (en) | 2003-02-03 | 2008-01-08 | Intel Corporation | Packaging of integrated circuits with carbon nano-tube arrays to enhance heat dissipation through a thermal interface |
US7285591B2 (en) | 2003-03-20 | 2007-10-23 | The Trustees Of The University Of Pennsylvania | Polymer-nanotube composites, fibers, and processes |
US8187703B2 (en) * | 2003-06-16 | 2012-05-29 | William Marsh Rice University | Fiber-reinforced polymer composites containing functionalized carbon nanotubes |
DE10327530A1 (de) | 2003-06-17 | 2005-01-20 | Electrovac Gesmbh | Vorrichtung mit wenigstens einer von einem zu kühlenden Funktionselement gebildeten Wärmequelle, mit wenigstens einer Wärmesenke und mit wenigstens einer Zwischenlage aus einer thermischen leitenden Masse zwischen der Wärmequelle und der Wärmesenke sowie thermische leitende Masse, insbesondere zur Verwendung bei einer solchen Vorrichtung |
US8513147B2 (en) * | 2003-06-19 | 2013-08-20 | Eastman Chemical Company | Nonwovens produced from multicomponent fibers |
US7892993B2 (en) | 2003-06-19 | 2011-02-22 | Eastman Chemical Company | Water-dispersible and multicomponent fibers from sulfopolyesters |
US20040260034A1 (en) | 2003-06-19 | 2004-12-23 | Haile William Alston | Water-dispersible fibers and fibrous articles |
US7168484B2 (en) | 2003-06-30 | 2007-01-30 | Intel Corporation | Thermal interface apparatus, systems, and methods |
DE10333961A1 (de) | 2003-07-25 | 2005-02-10 | Robert Bosch Gmbh | Verfahren zur Herstellung einer Precursor-Keramik |
US7652084B2 (en) * | 2003-09-05 | 2010-01-26 | The Reseach Foundation of State University of New York | Nanocomposite fibers and film containing polyolefin and surface-modified carbon nanotubes |
US7163967B2 (en) | 2003-12-01 | 2007-01-16 | Cryovac, Inc. | Method of increasing the gas transmission rate of a film |
US7456052B2 (en) | 2003-12-30 | 2008-11-25 | Intel Corporation | Thermal intermediate apparatus, systems, and methods |
US7180174B2 (en) | 2003-12-30 | 2007-02-20 | Intel Corporation | Nanotube modified solder thermal intermediate structure, systems, and methods |
US7335327B2 (en) | 2003-12-31 | 2008-02-26 | Cryovac, Inc. | Method of shrinking a film |
US8632699B2 (en) | 2004-04-07 | 2014-01-21 | Eikos, Inc. | Fugitive viscosity and stability modifiers for carbon nanotube compositions |
CN1981073B (zh) | 2004-07-27 | 2011-07-13 | 帝斯曼知识产权资产管理有限公司 | 用于制备碳纳米管/超高摩尔质量聚乙烯复合纤维的方法 |
US20060024483A1 (en) * | 2004-07-29 | 2006-02-02 | Koch William J | Transparent composite panel |
US8455583B2 (en) * | 2004-08-02 | 2013-06-04 | University Of Houston | Carbon nanotube reinforced polymer nanocomposites |
TW200633171A (en) | 2004-11-04 | 2006-09-16 | Koninkl Philips Electronics Nv | Nanotube-based fluid interface material and approach |
WO2007015710A2 (fr) * | 2004-11-09 | 2007-02-08 | Board Of Regents, The University Of Texas System | Fabrication et applications de rubans, feuilles et fils retors ou non de nanofibres |
EP2202202B1 (fr) * | 2005-05-03 | 2018-02-21 | Nanocomp Technologies, Inc. | Matériaux en composites de nanotubes en carbone |
EP1910220A1 (fr) * | 2005-07-22 | 2008-04-16 | The Provost, Fellows And Scholars Of The College Of The Holy And Undivided Trinity Of Queen Elizabeth Near Dublin | Polymères nanocomposites |
US7993620B2 (en) | 2005-07-28 | 2011-08-09 | Nanocomp Technologies, Inc. | Systems and methods for formation and harvesting of nanofibrous materials |
US7678841B2 (en) | 2005-08-19 | 2010-03-16 | Cryovac, Inc. | Increasing the gas transmission rate of a film comprising fullerenes |
DE102006037185A1 (de) | 2005-09-27 | 2007-03-29 | Electrovac Ag | Verfahren zur Behandlung von Nanofasermaterial sowie Zusammensetzung aus Nanofasermaterial |
JP2007109732A (ja) * | 2005-10-11 | 2007-04-26 | Mitsubishi Electric Corp | 素子基板の製造方法及び基板保持装置 |
US20110160346A1 (en) * | 2006-03-31 | 2011-06-30 | Applied Nanotech Holdings, Inc. | Dispersion of carbon nanotubes by microfluidic process |
JP4427034B2 (ja) * | 2006-04-28 | 2010-03-03 | 日信工業株式会社 | 炭素繊維複合材料 |
JP4231916B2 (ja) * | 2006-04-28 | 2009-03-04 | 日信工業株式会社 | 炭素繊維複合樹脂材料の製造方法 |
WO2008012196A1 (fr) * | 2006-07-22 | 2008-01-31 | Sineurop Nanotech Gmbh | Composite |
US7910041B1 (en) | 2006-11-27 | 2011-03-22 | Stratasys, Inc. | Build materials containing nanofibers for use with extrusion-based layered depositions systems |
WO2008106143A2 (fr) * | 2007-02-27 | 2008-09-04 | Nanocomp Technologies, Inc. | Matériaux pour protection thermique et procédés de fabrication de ceux-ci |
US9061913B2 (en) * | 2007-06-15 | 2015-06-23 | Nanocomp Technologies, Inc. | Injector apparatus and methods for production of nanostructures |
DE102007029008A1 (de) * | 2007-06-23 | 2008-12-24 | Bayer Materialscience Ag | Verfahren zur Herstellung eines leitfähigen Polymerverbundwerkstoffs |
US9236669B2 (en) * | 2007-08-07 | 2016-01-12 | Nanocomp Technologies, Inc. | Electrically and thermally non-metallic conductive nanostructure-based adapters |
KR100937625B1 (ko) * | 2007-08-10 | 2010-01-20 | 주식회사 제닉 | 가용성 웹 공극필름 및 이의 제조방법 |
WO2009023776A1 (fr) * | 2007-08-14 | 2009-02-19 | Nanocomp Technologies, Inc. | Générateurs thermoélectriques à base de matériau nanostructuré |
DE102007040927A1 (de) | 2007-08-30 | 2009-03-05 | Bayer Materialscience Ag | Verfahren zur Herstellung schlagzähmodifizierter gefüllter Polycarbonat-Zusammensetzungen |
EP2197508B1 (fr) * | 2007-09-06 | 2014-12-10 | Boston Scientific Limited | Dispositifs médicaux contenant des particules de silicate et de carbone |
DE102007049439A1 (de) * | 2007-09-27 | 2009-04-02 | Electrovac Ag | Kunststoff-Composite-Material sowie Verfahren zu dessen Herstellung |
US8344060B2 (en) * | 2008-04-08 | 2013-01-01 | Case Western Reserve University | Dynamic mechanical polymer nanocomposites |
WO2010036405A1 (fr) | 2008-05-07 | 2010-04-01 | Nanocomp Technologies, Inc. | Feuilles composites à nanostructures et procédés d'utilisation |
CA2723619A1 (fr) * | 2008-05-07 | 2009-11-12 | Nanocomp Technologies, Inc. | Dispositifs de chauffage a nanofil et procede d'utilisation |
EP2301993A4 (fr) * | 2008-07-10 | 2012-07-25 | Nissin Kogyo Kk | Nanofibres de carbone, leur procédé de production, et matériau composite à base de fibres de carbone |
JP5409094B2 (ja) | 2008-07-17 | 2014-02-05 | 富士フイルム株式会社 | 曲面状成形体及びその製造方法並びに車両灯具用前面カバー及びその製造方法 |
US20110204296A1 (en) * | 2008-08-20 | 2011-08-25 | Bayer Materialscience Ag | Method for producing composite materials having reduced resistance and comprising carbon nanotubes |
US20100083790A1 (en) * | 2008-10-06 | 2010-04-08 | Graney Jon P | Flywheel device |
FR2940659B1 (fr) * | 2008-12-26 | 2011-03-25 | Arkema France | Fibre composite a base de pekk, son procede de fabrication et ses utilisations |
US8512519B2 (en) * | 2009-04-24 | 2013-08-20 | Eastman Chemical Company | Sulfopolyesters for paper strength and process |
US8354593B2 (en) * | 2009-07-10 | 2013-01-15 | Nanocomp Technologies, Inc. | Hybrid conductors and method of making same |
US8225704B2 (en) * | 2010-01-16 | 2012-07-24 | Nanoridge Materials, Inc. | Armor with transformed nanotube material |
US8051682B1 (en) | 2010-06-01 | 2011-11-08 | The Boeing Company | Apparatus and method for making glass preform with nanofiber reinforcement |
DE102010039318A1 (de) | 2010-08-13 | 2012-02-16 | Sgl Carbon Se | Stabilisierung nanopartikulärer Füllstoffe in Harzformulierungen |
BR112013006120A2 (pt) | 2010-09-14 | 2016-05-31 | Power Tree Corp | volante composto |
US9273417B2 (en) | 2010-10-21 | 2016-03-01 | Eastman Chemical Company | Wet-Laid process to produce a bound nonwoven article |
KR101164637B1 (ko) * | 2010-11-26 | 2012-07-11 | 충남대학교산학협력단 | 정특성 서미스터용 복합재 및 그 제조방법 |
KR101164636B1 (ko) * | 2010-11-26 | 2012-07-11 | 충남대학교산학협력단 | 정특성 서미스터용 복합재 및 그 제조방법 |
US8722171B2 (en) | 2011-01-04 | 2014-05-13 | Nanocomp Technologies, Inc. | Nanotube-based insulators |
US8167190B1 (en) | 2011-05-06 | 2012-05-01 | Lockheed Martin Corporation | Electrically conductive polymer compositions containing metal particles and a graphene and methods for production and use thereof |
US9957379B2 (en) * | 2012-01-03 | 2018-05-01 | Lockheed Martin Corporation | Structural composite materials with high strain capability |
US8882963B2 (en) | 2012-01-31 | 2014-11-11 | Eastman Chemical Company | Processes to produce short cut microfibers |
US20130210965A1 (en) * | 2012-02-14 | 2013-08-15 | Weyerhaeuser Nr Company | Composite Polymer |
WO2013133941A1 (fr) * | 2012-03-06 | 2013-09-12 | Applied Nanotech Holdings, Inc. | Nanocomposites renforcés par des nanotubes de carbone |
WO2013155519A1 (fr) | 2012-04-13 | 2013-10-17 | Case Western Reserve University | Production de microfibres et de nanofibres par coextrusion de microcouches continue |
US9114589B2 (en) * | 2012-06-14 | 2015-08-25 | The Boeing Company | Bicomponent fibers containing nano-filaments for use in optically transparent composites |
BR112015001272A2 (pt) | 2012-07-23 | 2017-07-04 | Hewlett Packard Indigo Bv | composição de tinta eletrostática, substrato e método para imprimir eletrofotograficamente uma composição de tinta |
EP2892859A2 (fr) | 2012-09-04 | 2015-07-15 | OCV Intellectual Capital, LLC | Dispersion de fibres de renforcement améliorées par du carbone dans des milieux aqueux ou non aqueux |
US8936878B2 (en) | 2012-11-20 | 2015-01-20 | Dreamweaver International, Inc. | Methods of making single-layer lithium ion battery separators having nanofiber and microfiber components |
US9303357B2 (en) | 2013-04-19 | 2016-04-05 | Eastman Chemical Company | Paper and nonwoven articles comprising synthetic microfiber binders |
ES2943257T3 (es) | 2013-06-17 | 2023-06-12 | Nanocomp Technologies Inc | Agentes exfoliantes-dispersantes para nanotubos, haces y fibras |
US10029834B2 (en) | 2013-10-15 | 2018-07-24 | Thomas & Betts International Llc | Cable tie employing composite of nylon and carbon nanotubes |
KR102177502B1 (ko) * | 2013-11-20 | 2020-11-11 | 삼성에스디아이 주식회사 | 전자 소자 보호용 통합 실리콘, 이를 이용한 회로 모듈 및 이의 제조 방법 |
US9598802B2 (en) | 2013-12-17 | 2017-03-21 | Eastman Chemical Company | Ultrafiltration process for producing a sulfopolyester concentrate |
US9605126B2 (en) | 2013-12-17 | 2017-03-28 | Eastman Chemical Company | Ultrafiltration process for the recovery of concentrated sulfopolyester dispersion |
CN103788565A (zh) * | 2014-01-14 | 2014-05-14 | 广州优塑塑料科技有限公司 | 一种导电性3d打印塑料线条及其生产方法 |
CA2937085C (fr) | 2014-01-17 | 2023-09-12 | Graphene 3D Lab Inc. | Fabrication de filament fondu a l'aide d'un filament a segments multiples |
US9688538B2 (en) * | 2014-02-05 | 2017-06-27 | University Of Houston System | Graft polymerization initiated on graphitic nanomaterials and their nanocomposite formation |
US9650537B2 (en) | 2014-04-14 | 2017-05-16 | Ut-Battelle, Llc | Reactive polymer fused deposition manufacturing |
US10727537B2 (en) | 2014-09-02 | 2020-07-28 | G6 Materials Corp. | Electrochemical devices comprising nanoscopic carbon materials made by additive manufacturing |
DE102014013243A1 (de) * | 2014-09-12 | 2016-03-17 | Hexion GmbH | Faserverstärktes härtbares Kunststoffgranulat |
US9931778B2 (en) | 2014-09-18 | 2018-04-03 | The Boeing Company | Extruded deposition of fiber reinforced polymers |
US10118375B2 (en) | 2014-09-18 | 2018-11-06 | The Boeing Company | Extruded deposition of polymers having continuous carbon nanotube reinforcements |
US9821339B2 (en) * | 2014-12-19 | 2017-11-21 | Palo Alto Research Center Incorporated | System and method for digital fabrication of graded, hierarchical material structures |
US9486960B2 (en) | 2014-12-19 | 2016-11-08 | Palo Alto Research Center Incorporated | System for digital fabrication of graded, hierarchical material structures |
WO2016126818A1 (fr) | 2015-02-03 | 2016-08-11 | Nanocomp Technologies, Inc. | Structures à nanotubes de carbone et procédés de production de ceux-ci |
US11097492B2 (en) | 2015-03-02 | 2021-08-24 | G6 Materials Corp. | Thermoplastic composites comprising water-soluble PEO graft polymers useful for 3-dimensional additive manufacturing |
CN107428095A (zh) * | 2015-03-10 | 2017-12-01 | 泽菲罗斯有限公司 | 拉挤件及其制造方法 |
US10137617B2 (en) | 2015-04-17 | 2018-11-27 | Ut-Battelle, Llc | Low shear process for producing polymer composite fibers |
CN105001588B (zh) * | 2015-07-14 | 2017-11-07 | 暨南大学 | 一种熔融沉积成型用abs复合材料及其制备方法和应用 |
US11591467B2 (en) | 2015-07-29 | 2023-02-28 | G6 Materials Corp. | Thermoplastic polymer composites and methods for preparing, collecting, and tempering 3D printable materials and articles from same |
US11155673B2 (en) | 2015-11-12 | 2021-10-26 | Zephyros, Inc. | Controlled glass transition polymeric material and method |
JP6754435B2 (ja) | 2016-03-04 | 2020-09-09 | エイチピー・インディゴ・ビー・ブイHP Indigo B.V. | 静電インク組成物 |
CN105904605A (zh) * | 2016-06-17 | 2016-08-31 | 安徽康采恩包装材料有限公司 | 一种混色机 |
US10193030B2 (en) | 2016-08-08 | 2019-01-29 | General Electric Company | Composite materials having red emitting phosphors |
US10581082B2 (en) | 2016-11-15 | 2020-03-03 | Nanocomp Technologies, Inc. | Systems and methods for making structures defined by CNT pulp networks |
US11279836B2 (en) | 2017-01-09 | 2022-03-22 | Nanocomp Technologies, Inc. | Intumescent nanostructured materials and methods of manufacturing same |
JP7154281B2 (ja) | 2017-08-28 | 2022-10-17 | リンテック・オヴ・アメリカ,インコーポレイテッド | 絶縁化ナノファイバー糸 |
US11123900B2 (en) | 2017-09-20 | 2021-09-21 | Bell Helicopter Textron Inc. | Mold tool with anisotropic thermal properties |
CN111566161A (zh) * | 2017-11-16 | 2020-08-21 | 缅因大学系统董事会 | 用于3d打印的改进的长丝 |
KR102063892B1 (ko) * | 2017-12-18 | 2020-01-08 | 세종대학교산학협력단 | 투습 경로를 갖는 필름 및 이의 제조방법 |
FR3077759B1 (fr) * | 2018-02-09 | 2020-03-06 | Institut De Recherche Technologique Jules Verne | Procede de fabrication d'une piece preimpregnee en materiau composite |
US10947419B2 (en) | 2018-07-23 | 2021-03-16 | Palo Alto Research Center Incorporated | Method for joining dissimilar materials |
CN109306070A (zh) * | 2018-08-13 | 2019-02-05 | 浙江工业大学 | 一种具有纳米粒子取向聚合物纤维发泡材料的制备方法 |
CN109291428B (zh) * | 2018-09-29 | 2020-01-14 | 中南大学 | 一种调控复合材料中陶瓷纳米线排列方向的方法 |
US11332197B2 (en) | 2018-10-12 | 2022-05-17 | Zephyros, Inc. | Composite load bearing flooring |
US11589764B1 (en) | 2019-10-30 | 2023-02-28 | Brigham Young University | Methods and devices for aligning miniaturized spectrometers and impedance sensors in wearable devices |
US11471078B1 (en) | 2019-10-30 | 2022-10-18 | Brigham Young University | Miniaturized spectrometers for wearable devices |
US11877845B1 (en) | 2019-10-30 | 2024-01-23 | Brigham Young University | Miniaturized spectrometers on transparent substrates |
US11630316B1 (en) | 2019-10-30 | 2023-04-18 | Brigham Young University | Miniaturized collimators |
CN111070720B (zh) * | 2019-12-31 | 2021-12-17 | 中国人民解放军国防科技大学 | 一种纤维增强复合材料纤维位置控制装置和方法 |
CN112895269A (zh) * | 2021-02-04 | 2021-06-04 | 华南理工大学 | 一种聚合物循环动态力场压力成型方法 |
CN113559320B (zh) * | 2021-07-09 | 2023-03-10 | 浙江理工大学 | 一种多尺度纤维负泊松比三维导电熔喷非织造布心肌补片 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5121329A (en) * | 1989-10-30 | 1992-06-09 | Stratasys, Inc. | Apparatus and method for creating three-dimensional objects |
US5433906A (en) * | 1993-07-09 | 1995-07-18 | General Motors Corporation | Composite of small carbon fibers and thermoplastics and method for making same |
US6265466B1 (en) * | 1999-02-12 | 2001-07-24 | Eikos, Inc. | Electromagnetic shielding composite comprising nanotubes |
US6299812B1 (en) * | 1999-08-16 | 2001-10-09 | The Board Of Regents Of The University Of Oklahoma | Method for forming a fibers/composite material having an anisotropic structure |
US6426134B1 (en) * | 1998-06-30 | 2002-07-30 | E. I. Du Pont De Nemours And Company | Single-wall carbon nanotube-polymer composites |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5591382A (en) * | 1993-03-31 | 1997-01-07 | Hyperion Catalysis International Inc. | High strength conductive polymers |
JPH07102112A (ja) * | 1993-09-10 | 1995-04-18 | Hyperion Catalysis Internatl Inc | 熱可塑性エラストマー組成物および樹脂組成物 |
FR2716887B1 (fr) * | 1994-03-01 | 1996-04-26 | Atochem Elf Sa | Polymères renforcés de microfibrilles de cellulose, latex, poudres, films, joncs correspondants, et leurs applications. |
US6203814B1 (en) * | 1994-12-08 | 2001-03-20 | Hyperion Catalysis International, Inc. | Method of making functionalized nanotubes |
JP3057493B2 (ja) * | 1998-11-25 | 2000-06-26 | 三菱レイヨン株式会社 | 表面改質炭素繊維の製造方法 |
EP1054036A1 (fr) * | 1999-05-18 | 2000-11-22 | Fina Research S.A. | Polymères renforcées |
AU2002236431A1 (en) * | 2000-08-23 | 2002-05-21 | A. Kuper Cynthia | Method for utilizing sol-gel processing in the production of a macroscopic two or three dimensionally ordered array of single wall nanotubes (swnts) |
-
2000
- 2000-12-07 CA CA2394955A patent/CA2394955C/fr not_active Expired - Fee Related
- 2000-12-07 AU AU25771/01A patent/AU2577101A/en not_active Abandoned
- 2000-12-07 DE DE60033692T patent/DE60033692T2/de not_active Expired - Lifetime
- 2000-12-07 EP EP00989235A patent/EP1244730B1/fr not_active Expired - Lifetime
- 2000-12-07 KR KR1020027007255A patent/KR100810977B1/ko not_active IP Right Cessation
- 2000-12-07 WO PCT/US2000/033291 patent/WO2001092381A1/fr active IP Right Grant
- 2000-12-07 US US10/149,216 patent/US20060047052A1/en not_active Abandoned
- 2000-12-07 AT AT00989235T patent/ATE355323T1/de not_active IP Right Cessation
- 2000-12-07 CN CN008188335A patent/CN1433443B/zh not_active Expired - Fee Related
- 2000-12-07 JP JP2002500989A patent/JP5770962B2/ja not_active Expired - Fee Related
-
2008
- 2008-02-04 US US12/025,626 patent/US7897248B2/en not_active Expired - Fee Related
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5121329A (en) * | 1989-10-30 | 1992-06-09 | Stratasys, Inc. | Apparatus and method for creating three-dimensional objects |
US5433906A (en) * | 1993-07-09 | 1995-07-18 | General Motors Corporation | Composite of small carbon fibers and thermoplastics and method for making same |
US6426134B1 (en) * | 1998-06-30 | 2002-07-30 | E. I. Du Pont De Nemours And Company | Single-wall carbon nanotube-polymer composites |
US6265466B1 (en) * | 1999-02-12 | 2001-07-24 | Eikos, Inc. | Electromagnetic shielding composite comprising nanotubes |
US6299812B1 (en) * | 1999-08-16 | 2001-10-09 | The Board Of Regents Of The University Of Oklahoma | Method for forming a fibers/composite material having an anisotropic structure |
Cited By (94)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7304103B2 (en) * | 2001-01-29 | 2007-12-04 | William Marsh Rice University | Process for making polymers comprising derivatized carbon nanotubes and compositions thereof |
US20050074390A1 (en) * | 2001-01-29 | 2005-04-07 | William Marsh Rice University | Process for making polymers comprising derivatized carbon nanotubes and compositions thereof |
US20070104947A1 (en) * | 2001-08-16 | 2007-05-10 | Shambaugh Robert L | Nanotube/matrix composites and methods of production and use |
US20060166003A1 (en) * | 2003-06-16 | 2006-07-27 | William Marsh Rice University | Fabrication of carbon nanotube reinforced epoxy polymer composites using functionalized carbon nanotubes |
US7601421B2 (en) | 2003-06-16 | 2009-10-13 | William Marsh Rice University | Fabrication of carbon nanotube reinforced epoxy polymer composites using functionalized carbon nanotubes |
US7741232B2 (en) * | 2003-06-30 | 2010-06-22 | Ideal Star Inc. | Electron-emitting woven fabric and display device using same |
US20070117488A1 (en) * | 2003-06-30 | 2007-05-24 | Kuniyoshi Yokoh | Electron-emitting woven fabric and display device using same |
US20070290410A1 (en) * | 2005-07-29 | 2007-12-20 | Koo Joseph H | Fire retardant polymer nanocomposites for laser sintering |
US20070110977A1 (en) * | 2005-08-29 | 2007-05-17 | Al-Haik Marwan S | Methods for processing multifunctional, radiation tolerant nanotube-polymer structure composites |
US20110117316A1 (en) * | 2005-09-06 | 2011-05-19 | Lemaire Charles A | Method and apparatus for growing fullerene nanotube forests, and forming nanotube films, threads and composite structures therefrom |
US20080093577A1 (en) * | 2006-06-21 | 2008-04-24 | Khraishi Tariq A | Metal-carbon nanotube composites for enhanced thermal conductivity for demanding or critical applications |
US7998367B2 (en) | 2006-06-21 | 2011-08-16 | Stc.Unm | Metal-carbon nanotube composites for enhanced thermal conductivity for demanding or critical applications |
US20080160290A1 (en) * | 2006-08-30 | 2008-07-03 | Korea Electrotechnology Research Institute | Aligned nanoparticle channel and method of fabricating aligned nanoparticle channel by applying shear force to immiscible binary polymer-blended nanoparticle composite |
WO2009001324A2 (fr) * | 2007-06-27 | 2008-12-31 | Arkema France | Utilisation de nanotubes, notamment de nanotubes de carbone pour améliorer les propriétés mécaniques à température élevée d'une matrice polymère |
WO2009001324A3 (fr) * | 2007-06-27 | 2009-09-03 | Arkema France | Utilisation de nanotubes, notamment de nanotubes de carbone pour améliorer les propriétés mécaniques à température élevée d'une matrice polymère |
US20110098406A1 (en) * | 2008-07-08 | 2011-04-28 | Toyo Boseki Kabushiki Kaisha | Method for Producing High Strength Polyethylene Fiber and High Strength Polyethylene Fiber |
US8520406B2 (en) | 2009-01-28 | 2013-08-27 | Florida State University Research Foundation, Inc. | Electromagnetic interference shielding structure including carbon nanotube or nanofiber films |
US8351220B2 (en) | 2009-01-28 | 2013-01-08 | Florida State University Research Foundation | Electromagnetic interference shielding structure including carbon nanotube or nanofiber films and methods |
US20100188833A1 (en) * | 2009-01-28 | 2010-07-29 | Florida State University Research Foundation | Electromagnetic interference shielding structure including carbon nanotube or nanofiber films and methods |
US9119294B2 (en) | 2009-01-28 | 2015-08-25 | Florida State University Research Foundation | Electromagnetic interference shielding structure including carbon nanotube or nanofiber films |
US20110024694A1 (en) * | 2009-02-17 | 2011-02-03 | Lockheed Martin Corporation | Composites comprising carbon nanotubes on fiber |
US8585934B2 (en) | 2009-02-17 | 2013-11-19 | Applied Nanostructured Solutions, Llc | Composites comprising carbon nanotubes on fiber |
WO2011005279A1 (fr) * | 2009-07-08 | 2011-01-13 | Toyo Boseki Kabushiki Kaisha | Procédé de fabrication de fibre polyéthylène de forte résistance et fibre polyéthylène de forte résistance |
US8168291B2 (en) | 2009-11-23 | 2012-05-01 | Applied Nanostructured Solutions, Llc | Ceramic composite materials containing carbon nanotube-infused fiber materials and methods for production thereof |
US20110133031A1 (en) * | 2009-11-23 | 2011-06-09 | Applied Nanostructured Solutions, Llc | Cnt-tailored composite air-based structures |
US20110132245A1 (en) * | 2009-11-23 | 2011-06-09 | Applied Nanostructured Solutions, Llc | Cnt-tailored composite sea-based structures |
US8662449B2 (en) | 2009-11-23 | 2014-03-04 | Applied Nanostructured Solutions, Llc | CNT-tailored composite air-based structures |
US20110135491A1 (en) * | 2009-11-23 | 2011-06-09 | Applied Nanostructured Solutions, Llc | Cnt-tailored composite land-based structures |
US8601965B2 (en) | 2009-11-23 | 2013-12-10 | Applied Nanostructured Solutions, Llc | CNT-tailored composite sea-based structures |
US20110124483A1 (en) * | 2009-11-23 | 2011-05-26 | Applied Nanostructured Solutions, Llc | Ceramic composite materials containing carbon nanotube-infused fiber materials and methods for production thereof |
US20110123735A1 (en) * | 2009-11-23 | 2011-05-26 | Applied Nanostructured Solutions, Llc | Cnt-infused fibers in thermoset matrices |
US20110143087A1 (en) * | 2009-12-14 | 2011-06-16 | Applied Nanostructured Solutions, Llc | Flame-resistant composite materials and articles containing carbon nanotube-infused fiber materials |
US8545963B2 (en) | 2009-12-14 | 2013-10-01 | Applied Nanostructured Solutions, Llc | Flame-resistant composite materials and articles containing carbon nanotube-infused fiber materials |
US20110186775A1 (en) * | 2010-02-02 | 2011-08-04 | Applied Nanostructured Solutions, Llc. | Carbon nanotube-infused fiber materials containing parallel-aligned carbon nanotubes, methods for production thereof, and composite materials derived therefrom |
WO2011146151A2 (fr) | 2010-02-02 | 2011-11-24 | Applied Nanostructured Solutions, Llc | Matières fibreuses à infusion de nanotubes de carbone contenant des nanotubes de carbone à alignement parallèle, leurs procédés de production, et matériaux composites dérivés |
WO2011146151A3 (fr) * | 2010-02-02 | 2012-01-19 | Applied Nanostructured Solutions, Llc | Matières fibreuses à infusion de nanotubes de carbone contenant des nanotubes de carbone à alignement parallèle, leurs procédés de production, et matériaux composites dérivés |
US8999453B2 (en) | 2010-02-02 | 2015-04-07 | Applied Nanostructured Solutions, Llc | Carbon nanotube-infused fiber materials containing parallel-aligned carbon nanotubes, methods for production thereof, and composite materials derived therefrom |
CN102741465A (zh) * | 2010-02-02 | 2012-10-17 | 应用纳米结构方案公司 | 包含平行排列的碳纳米管的碳纳米管并入的纤维材料、其制造方法及从其衍生的复合材料 |
US9976011B2 (en) | 2010-07-14 | 2018-05-22 | The Curators Of The University Of Missouri | Polymer composites and fabrications thereof |
US9907174B2 (en) | 2010-08-30 | 2018-02-27 | Applied Nanostructured Solutions, Llc | Structural energy storage assemblies and methods for production thereof |
US9017854B2 (en) | 2010-08-30 | 2015-04-28 | Applied Nanostructured Solutions, Llc | Structural energy storage assemblies and methods for production thereof |
US8795561B2 (en) | 2010-09-29 | 2014-08-05 | Milliken & Company | Process of forming a nanofiber non-woven containing particles |
US8889572B2 (en) | 2010-09-29 | 2014-11-18 | Milliken & Company | Gradient nanofiber non-woven |
WO2013123023A3 (fr) * | 2012-02-14 | 2015-07-09 | Toray Industries, Inc. | Composition de composite de polymère renforcé par des fibres, ayant des nanofibres alignées |
US11479652B2 (en) | 2012-10-19 | 2022-10-25 | Rutgers, The State University Of New Jersey | Covalent conjugates of graphene nanoparticles and polymer chains and composite materials formed therefrom |
US11098175B2 (en) | 2012-10-19 | 2021-08-24 | Rutgers, The State University Of New Jersey | In situ exfoliation method to fabricate a graphene-reinforced polymer matrix composite |
US8758860B1 (en) | 2012-11-07 | 2014-06-24 | Bayer Materialscience Llc | Process for incorporating an ion-conducting polymer into a polymeric article to achieve anti-static behavior |
US9388324B2 (en) | 2012-11-07 | 2016-07-12 | Covestro Llc | Process for incorporating an ion-conducting polymer into a polymeric article to achieve anti-static behavior |
WO2014074397A1 (fr) | 2012-11-07 | 2014-05-15 | Bayer Materialscience Llc | Procédé d'incorporation d'un polymère conducteur ionique dans un article en polymère pour obtenir un comportement anti-statique |
US20160144566A1 (en) * | 2013-03-22 | 2016-05-26 | Markforged, Inc. | Three dimensional printing of composite reinforced structures |
US11014305B2 (en) | 2013-03-22 | 2021-05-25 | Markforged, Inc. | Mid-part in-process inspection for 3D printing |
US11787104B2 (en) | 2013-03-22 | 2023-10-17 | Markforged, Inc. | Methods for fiber reinforced additive manufacturing |
US11759990B2 (en) | 2013-03-22 | 2023-09-19 | Markforged, Inc. | Three dimensional printing |
US11577462B2 (en) | 2013-03-22 | 2023-02-14 | Markforged, Inc. | Scanning print bed and part height in 3D printing |
US11504892B2 (en) | 2013-03-22 | 2022-11-22 | Markforged, Inc. | Impregnation system for composite filament fabrication in three dimensional printing |
US11420382B2 (en) | 2013-03-22 | 2022-08-23 | Markforged, Inc. | Apparatus for fiber reinforced additive manufacturing |
US11237542B2 (en) | 2013-03-22 | 2022-02-01 | Markforged, Inc. | Composite filament 3D printing using complementary reinforcement formations |
US11148409B2 (en) * | 2013-03-22 | 2021-10-19 | Markforged, Inc. | Three dimensional printing of composite reinforced structures |
US11065861B2 (en) | 2013-03-22 | 2021-07-20 | Markforged, Inc. | Methods for composite filament threading in three dimensional printing |
US10953610B2 (en) | 2013-03-22 | 2021-03-23 | Markforged, Inc. | Three dimensional printer with composite filament fabrication |
US10603841B2 (en) | 2013-03-22 | 2020-03-31 | Markforged, Inc. | Multilayer fiber reinforcement design for 3D printing |
US10611082B2 (en) | 2013-03-22 | 2020-04-07 | Markforged, Inc. | Apparatus for fiber reinforced additive manufacturing |
US10953609B1 (en) | 2013-03-22 | 2021-03-23 | Markforged, Inc. | Scanning print bed and part height in 3D printing |
US10682844B2 (en) | 2013-03-22 | 2020-06-16 | Markforged, Inc. | Embedding 3D printed fiber reinforcement in molded articles |
US10696039B2 (en) | 2013-03-22 | 2020-06-30 | Markforged, Inc. | Multilayer fiber reinforcement design for 3D printing |
US10717228B2 (en) | 2013-03-22 | 2020-07-21 | Markforged, Inc. | Three dimensional printing |
US10821662B2 (en) | 2013-03-22 | 2020-11-03 | Markforged, Inc. | Methods for fiber reinforced additive manufacturing |
US11174366B2 (en) | 2013-04-18 | 2021-11-16 | Rutgers, The State University Of New Jersey | In situ exfoliation method to fabricate a graphene-reinforced polymer matrix composite |
US10370510B2 (en) * | 2013-10-08 | 2019-08-06 | Stratasys, Inc. | Consumable filaments having reversible reinforcement for extrusion-based additive manufacturing |
US20180222601A1 (en) * | 2013-11-15 | 2018-08-09 | Honeywell International Inc. | Fire-and electromagnetic interference (emi)-resistant aircraft components and methods for manufacturing the same |
GB2534524B (en) * | 2013-12-30 | 2021-05-12 | Halliburton Energy Services Inc | Liquid slurries of micron- and nano-sized solids for use in subterranean operations |
AU2013409497B2 (en) * | 2013-12-30 | 2017-03-16 | Halliburton Energy Services, Inc. | Liquid slurries of micron- and nano-sized solids for use in subterranean operations |
WO2015102580A1 (fr) * | 2013-12-30 | 2015-07-09 | Halliburton Energy Services, Inc. | Bouillies liquides de matières solides de dimension micrométrique et nanométrique en vue d'une utilisation dans des opérations souterraines |
GB2534524A (en) * | 2013-12-30 | 2016-07-27 | Halliburton Energy Services Inc | Liquid slurries of micron- and nano-sized solids for use in subterranean operations |
US20170182718A1 (en) * | 2014-05-28 | 2017-06-29 | University Of South Alabama | Apparatus and method for directional alignment of nanofibers in a porous medium |
US10556390B2 (en) * | 2014-05-28 | 2020-02-11 | University Of South Alabama | Apparatus and method for directional alignment of nanofibers in a porous medium |
WO2015184151A1 (fr) * | 2014-05-28 | 2015-12-03 | University Of South Alabama | Appareil et procédé pour l'alignement directionnel de nanofibres dans un milieu poreux |
US11225558B2 (en) | 2014-07-30 | 2022-01-18 | Rutgers, The State University Of New Jersey | Graphene-reinforced polymer matrix composites |
US10850429B2 (en) | 2014-11-03 | 2020-12-01 | Arkema France | Process for densification of poly(arylene ether ketone) powders |
US11059945B2 (en) * | 2016-07-22 | 2021-07-13 | Rutgers, The State University Of New Jersey | In situ bonding of carbon fibers and nanotubes to polymer matrices |
US11702518B2 (en) | 2016-07-22 | 2023-07-18 | Rutgers, The State University Of New Jersey | In situ bonding of carbon fibers and nanotubes to polymer matrices |
US20200148841A1 (en) * | 2016-07-22 | 2020-05-14 | Rutgers, The State University Of New Jersey | In Situ Bonding of Carbon Fibers and Nanotubes to Polymer Matrices |
US20180363168A1 (en) * | 2017-06-20 | 2018-12-20 | Zhejiang Jinhao Specialty Fiber Co., Ltd. | Method of preparing wear and cut resistant uhmwpe fibers |
US10767279B2 (en) * | 2017-06-20 | 2020-09-08 | Zhejiang Jinhao New Materials Co., Ltd. | Method of preparing wear and cut resistant UHMWPE fibers |
US10046511B1 (en) | 2017-12-26 | 2018-08-14 | Arevo, Inc. | Alleviating torsional forces on fiber-reinforced thermoplastic filament |
US11292190B2 (en) * | 2017-12-26 | 2022-04-05 | Arevo, Inc. | Depositing arced portions of fiber-reinforced thermoplastic filament |
US10239257B1 (en) | 2017-12-26 | 2019-03-26 | Arevo, Inc. | Depositing portions of fiber-reinforced thermoplastic filament while alleviating torsional forces |
US20190193328A1 (en) * | 2017-12-26 | 2019-06-27 | Arevo, Inc. | Depositing Arced Portions of Fiber-Reinforced Thermoplastic Filament |
US11479653B2 (en) | 2018-01-16 | 2022-10-25 | Rutgers, The State University Of New Jersey | Use of graphene-polymer composites to improve barrier resistance of polymers to liquid and gas permeants |
US20230212793A1 (en) * | 2018-04-20 | 2023-07-06 | Mermet | Composite Yarn, Manufacturing Process and Textile Surface Comprising Such a Yarn |
US20210187788A1 (en) * | 2018-05-31 | 2021-06-24 | Lintec Corporation | Method of producing carbon-resin composite material, and composite structure for producing carbon-resin composite material |
US11760640B2 (en) | 2018-10-15 | 2023-09-19 | Rutgers, The State University Of New Jersey | Nano-graphitic sponges and methods for fabricating the same |
US11807757B2 (en) | 2019-05-07 | 2023-11-07 | Rutgers, The State University Of New Jersey | Economical multi-scale reinforced composites |
US11981069B2 (en) | 2021-09-16 | 2024-05-14 | Markforged, Inc. | Three dimensional printing of composite reinforced structures |
Also Published As
Publication number | Publication date |
---|---|
CA2394955C (fr) | 2010-01-26 |
ATE355323T1 (de) | 2006-03-15 |
DE60033692T2 (de) | 2007-11-08 |
CN1433443A (zh) | 2003-07-30 |
US7897248B2 (en) | 2011-03-01 |
AU2577101A (en) | 2001-12-11 |
US20090104386A1 (en) | 2009-04-23 |
KR100810977B1 (ko) | 2008-03-10 |
WO2001092381A1 (fr) | 2001-12-06 |
KR20020076241A (ko) | 2002-10-09 |
EP1244730A1 (fr) | 2002-10-02 |
JP5770962B2 (ja) | 2015-08-26 |
CA2394955A1 (fr) | 2001-12-06 |
CN1433443B (zh) | 2010-05-12 |
JP2003534955A (ja) | 2003-11-25 |
DE60033692D1 (de) | 2007-04-12 |
EP1244730B1 (fr) | 2007-02-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7897248B2 (en) | Oriented nanofibers embedded in a polymer matrix | |
JP2003534955A5 (fr) | ||
Al-Saleh et al. | Review of the mechanical properties of carbon nanofiber/polymer composites | |
Pötschke et al. | Melt mixing of polycarbonate with multiwalled carbon nanotubes: microscopic studies on the state of dispersion | |
Shofner et al. | Single wall nanotube and vapor grown carbon fiber reinforced polymers processed by extrusion freeform fabrication | |
US7662321B2 (en) | Nano-scaled graphene plate-reinforced composite materials and method of producing same | |
Thostenson et al. | Aligned multi-walled carbon nanotube-reinforced composites: processing and mechanical characterization | |
EP1181331B1 (fr) | Polymeres renforces | |
Coleman et al. | High performance nanotube‐reinforced plastics: Understanding the mechanism of strength increase | |
Jimenez et al. | Electrically conductive polymer nanocomposites of polymethylmethacrylate and carbon nanofibers prepared by chaotic mixing | |
EP1474550B1 (fr) | Procede de production de produits allonges a haute resistance contenant des nanotubes | |
CN101835542A (zh) | 碳纤维和碳薄膜及其制造方法 | |
US7423084B2 (en) | Method of producing high strength elongated products containing nanotubes | |
EP1803763B1 (fr) | Nanofibres orientées intégrées dans une matrice polymère | |
Weisenberger et al. | Carbon nanotube polymer composites: recent developments in mechanical properties | |
Lin | Experimental investigation of toughening carbon fibre/epoxy composites with graphene/phenoxy fibres | |
Sharma et al. | Carbon nanotube composites: critical issues | |
Verma | Design, fabrication and characterization of PVA/Nanocarbon composite fibers | |
Furquan et al. | Effect of CNT on the mechanical properties of melt spun PET/CNT nanocomposite fibers | |
Sultana et al. | Nanoscale Reinforcement of Polymer Textile Fibers | |
Dul et al. | Carbon nanotubes-ABS nanocomposites for fused deposition modelling | |
Shinde et al. | A REVIEW ON STUDY OF POLYMERS AND RECENT DEVELOPMENTS IN MATERIALS FOR ADDITIVE MANUFACTURING-3D PRINTING |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: WILLIAM MARSH RICE UNIVERSITY, TEXAS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:BARRERA, ENRIQUE V.;RODRIGUEZ-MACIAS, FERNANDO J.;LOZANO, KAREN;AND OTHERS;REEL/FRAME:013514/0175;SIGNING DATES FROM 20020528 TO 20021107 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |
|
AS | Assignment |
Owner name: NASA, DISTRICT OF COLUMBIA Free format text: CONFIRMATORY LICENSE;ASSIGNOR:RICE UNIVERSITY;REEL/FRAME:022576/0694 Effective date: 20081211 |
|
AS | Assignment |
Owner name: NATIONAL SCIENCE FOUNDATION, VIRGINIA Free format text: CONFIRMATORY LICENSE;ASSIGNOR:RICE UNIVERSITY;REEL/FRAME:028184/0902 Effective date: 20120508 |