US20050234136A1 - Colloidal compositions and methods of preparing same - Google Patents

Colloidal compositions and methods of preparing same Download PDF

Info

Publication number
US20050234136A1
US20050234136A1 US10/827,214 US82721404A US2005234136A1 US 20050234136 A1 US20050234136 A1 US 20050234136A1 US 82721404 A US82721404 A US 82721404A US 2005234136 A1 US2005234136 A1 US 2005234136A1
Authority
US
United States
Prior art keywords
metal
silicate
solution
colloidal
silica
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/827,214
Other languages
English (en)
Inventor
Brian Holland
Francois Batllo
Carmen Ortiz
Dennis Mac Donald
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ecolab USA Inc
Original Assignee
Nalco Co LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nalco Co LLC filed Critical Nalco Co LLC
Priority to US10/827,214 priority Critical patent/US20050234136A1/en
Assigned to NALCO COMPANY reassignment NALCO COMPANY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BATLLO, FRANCOIS, HOLLAND, BRIAN T., MAC DONALD, DENNIS L., ORTIZ, CARMEN Y.
Priority to SG200902613-9A priority patent/SG152248A1/en
Priority to CN2005800118801A priority patent/CN1942237B/zh
Priority to EP05735668.5A priority patent/EP1744825B1/en
Priority to BRPI0509859-9A priority patent/BRPI0509859B1/pt
Priority to CN2010102460035A priority patent/CN101912755B/zh
Priority to PCT/US2005/012371 priority patent/WO2005104683A2/en
Priority to CA2560748A priority patent/CA2560748C/en
Priority to JP2007509513A priority patent/JP5103168B2/ja
Priority to KR1020067021598A priority patent/KR20070027535A/ko
Priority to TW094112213A priority patent/TWI377980B/zh
Publication of US20050234136A1 publication Critical patent/US20050234136A1/en
Assigned to BANK OF AMERICA, N.A., AS COLLATERAL AGENT reassignment BANK OF AMERICA, N.A., AS COLLATERAL AGENT SECURITY AGREEMENT Assignors: CALGON LLC, NALCO COMPANY, NALCO CROSSBOW WATER LLC, NALCO ONE SOURCE LLC
Assigned to NALCO COMPANY reassignment NALCO COMPANY RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: BANK OF AMERICA, N.A.
Assigned to NALCO COMPANY reassignment NALCO COMPANY RELEASE BY SECURED PARTY (SEE DOCUMENT FOR DETAILS). Assignors: BANK OF AMERICA, N.A.
Assigned to ECOLAB USA INC. reassignment ECOLAB USA INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: CALGON CORPORATION, CALGON LLC, NALCO COMPANY LLC, ONDEO NALCO ENERGY SERVICES, L.P.
Assigned to NALCO COMPANY LLC reassignment NALCO COMPANY LLC CHANGE OF NAME (SEE DOCUMENT FOR DETAILS). Assignors: NALCO COMPANY
Assigned to ECOLAB USA INC. reassignment ECOLAB USA INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: NALCO COMPANY
Priority to US15/877,168 priority patent/US10730756B2/en
Abandoned legal-status Critical Current

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01BNON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00Silicon; Compounds thereof
    • C01B33/113Silicon oxides; Hydrates thereof
    • C01B33/12Silica; Hydrates thereof, e.g. lepidoic silicic acid
    • C01B33/14Colloidal silica, e.g. dispersions, gels, sols
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01BNON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00Silicon; Compounds thereof
    • C01B33/20Silicates
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61KPREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K8/00Cosmetics or similar toiletry preparations
    • A61K8/02Cosmetics or similar toiletry preparations characterised by special physical form
    • A61K8/04Dispersions; Emulsions
    • A61K8/042Gels
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61KPREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K8/00Cosmetics or similar toiletry preparations
    • A61K8/18Cosmetics or similar toiletry preparations characterised by the composition
    • A61K8/19Cosmetics or similar toiletry preparations characterised by the composition containing inorganic ingredients
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61KPREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K8/00Cosmetics or similar toiletry preparations
    • A61K8/18Cosmetics or similar toiletry preparations characterised by the composition
    • A61K8/19Cosmetics or similar toiletry preparations characterised by the composition containing inorganic ingredients
    • A61K8/25Silicon; Compounds thereof
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61KPREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K8/00Cosmetics or similar toiletry preparations
    • A61K8/18Cosmetics or similar toiletry preparations characterised by the composition
    • A61K8/30Cosmetics or similar toiletry preparations characterised by the composition containing organic compounds
    • A61K8/40Cosmetics or similar toiletry preparations characterised by the composition containing organic compounds containing nitrogen
    • A61K8/41Amines
    • A61K8/416Quaternary ammonium compounds
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61QSPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
    • A61Q19/00Preparations for care of the skin
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01JCHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J13/00Colloid chemistry, e.g. the production of colloidal materials or their solutions, not otherwise provided for; Making microcapsules or microballoons
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01JCHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J13/00Colloid chemistry, e.g. the production of colloidal materials or their solutions, not otherwise provided for; Making microcapsules or microballoons
    • B01J13/0004Preparation of sols
    • B01J13/0008Sols of inorganic materials in water
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B82NANOTECHNOLOGY
    • B82YSPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
    • B82Y30/00Nanotechnology for materials or surface science, e.g. nanocomposites
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01BNON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00Silicon; Compounds thereof
    • C01B33/113Silicon oxides; Hydrates thereof
    • C01B33/12Silica; Hydrates thereof, e.g. lepidoic silicic acid
    • C01B33/14Colloidal silica, e.g. dispersions, gels, sols
    • C01B33/141Preparation of hydrosols or aqueous dispersions
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01BNON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B33/00Silicon; Compounds thereof
    • C01B33/20Silicates
    • C01B33/26Aluminium-containing silicates, i.e. silico-aluminates
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01BNON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B37/00Compounds having molecular sieve properties but not having base-exchange properties
    • C01B37/02Crystalline silica-polymorphs, e.g. silicalites dealuminated aluminosilicate zeolites
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01BNON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
    • C01B39/00Compounds having molecular sieve and base-exchange properties, e.g. crystalline zeolites; Their preparation; After-treatment, e.g. ion-exchange or dealumination
    • C01B39/02Crystalline aluminosilicate zeolites; Isomorphous compounds thereof; Direct preparation thereof; Preparation thereof starting from a reaction mixture containing a crystalline zeolite of another type, or from preformed reactants; After-treatment thereof
    • AHUMAN NECESSITIES
    • A61MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61KPREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
    • A61K2800/00Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
    • A61K2800/10General cosmetic use
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00Particle morphology
    • C01P2004/60Particles characterised by their size
    • C01P2004/62Submicrometer sized, i.e. from 0.1-1 micrometer
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00Particle morphology
    • C01P2004/60Particles characterised by their size
    • C01P2004/64Nanometer sized, i.e. from 1-100 nanometer
    • CCHEMISTRY; METALLURGY
    • C01INORGANIC CHEMISTRY
    • C01PINDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00Physical properties of inorganic compounds
    • C01P2006/12Surface area

Definitions

  • the present invention generally relates to colloidal compositions and methods of producing same.
  • the present invention relates to colloidal compositions that include a silicate with a metal dispersed within the silicate and at varying metal loadings that can range from as high as about 35 wt % based on silica.
  • the colloidal compositions can further include a stabilizer, such as a quaternary compound, that can facilitate the dispersion and loading of the metal within the silicate.
  • the present invention provides a novel and unique alternative to conventional surface-treated silica colloids.
  • the colloidal compositions of the present invention can be made in any suitable way.
  • the colloidal compositions are, in general, synthesized according to two procedures as further detailed below pursuant to various embodiments of the present invention.
  • a method of producing a silica colloid includes providing an alkaline solution having a stabilizing component, adding a silicic acid solution to the alkaline solution, and forming a colloid of silica particles wherein the stabilizing component is dispersed throughout each particle. Further, a cationic metal component can be added to the stabilizer-containing alkaline solution in an embodiment. Addition of the silicic acid solution to the alkaline solution thus forms a colloid of silica particles having both the stabilizing component and the metal component dispersed within one or more of the silicate particles, such as in a homogenous manner.
  • the stabilizer is a quaternary compound, preferably a quaternary amine, such as a quaternary ammonium hydroxide and the like.
  • the stabilizer performs several functions in the synthesis of the colloidal silica.
  • the stabilizer provides the OH ⁇ component to the alkaline solution, which catalyzes the reaction between the silicic acid and metal component to form the colloid.
  • the stabilizer also enables more of the metal component to bond or chemically combine with the silica component during formation of the colloid.
  • the resultant silica colloid demonstrates the capability to carry increased amounts of metal.
  • the colloid can have a metal content from about 0.0001 wt % to about 35 wt % based on silica.
  • the colloidal particles are amorphous and spherical in shape.
  • the colloidal composition can be further processed to produce a crystalline structure as described in greater detail below.
  • the diameter of the colloidal particles is in the range of about 2 nm to about 1000 nm according to an embodiment.
  • a method of preparing a metal-containing silica colloid wherein a silicic acid solution is reacted with a cationic metal component to form a metal silicate solution.
  • the metal silicate solution is subsequently added to an alkaline solution to form a colloid of metal silicate particles.
  • Reacting the silicic acid solution with the metal component forms a metal-silicate monomer that is subsequently polymerized as the metal silicate solution is added to the alkaline solution.
  • the polymerization forms a homogeneous metal-silicate lattice microstructure or framework throughout the entire solid phase of the colloid.
  • the polymerization of the metal-silicate and the utilization of a polyvalent cationic metal component in formation of the colloid yields a metal silicate colloids having metal content in the range of about 0.0001% to as high as 2% by weight silica according to an embodiment.
  • the lattice metal-silicate structure throughout the entire solid phase also improves the stability of the colloid.
  • the metal silicate colloid of the present invention remains soluble throughout the entire pH range, i.e., pH 1-14.
  • the solid phase of the metal silicate colloid of the present invention is substantially amorphous having a generally spherical particle shape and size in the range of from about 2 nm to about 1000 nm according to an embodiment.
  • the location of a metal component within the metal-containing silica colloid can be effectively controlled.
  • the metal silicate solution and the silicic acid solution can be selectively added to the alkaline solution to form a colloid of silica particles containing metal that is dispersed within one or more of the particles.
  • the sequence and duration in which the metal silicate solution and the silicic acid solution are added effectively controls the location of the metal within the solid phase of the colloid.
  • the metal silicate solution can be added to the alkaline solution before the silicic acid solution to form a colloid of silica particles having metal dispersed within an interior core layer of each particle.
  • the silicic acid solution can be added to the alkaline solution before the metal silicate solution to form a colloid of silica particles having a silica core and metal dispersed within an outer or exterior layer of each particle.
  • the metal silicate solution and the silicic acid solution can be added to the alkaline solution in an alternating manner to form a colloid of silica particles having a number of layers, wherein the layers alternate between metal containing layers and layers containing only silica in a repeat or successive manner.
  • the present invention provides a colloidal composition.
  • the colloidal composition includes a silicate doped with a metal, and a stabilizer dispersed within the silicate.
  • the silicate doped with metal includes about 35 wt % or less of metal based on silica.
  • the stabilizer includes a quaternary compound.
  • the quaternary compound is a quaternary amine.
  • an amount of the stabilizer correlates to an amount of the metal.
  • the present invention provides a colloidal silicate composition doped with a metal.
  • the colloidal silicate composition includes one or more silicate particles wherein the metal is dispersed within one or more of the silicate particles.
  • the metal is dispersed in a controlled manner.
  • one or more of the silicate particles includes a layered structure.
  • the metal is controllably dispersed within one or more particle layers of the layered structure.
  • the metal includes an alkali metal, an alkaline earth metal, a 1 st row transition metal, a 2 nd row transition metal, a lanthanide, and combinations thereof.
  • the metal is about 2 wt % or less based on silica.
  • the present invention provides a method of forming a colloidal composition.
  • the method includes preparing a heel solution including a stabilizer; preparing a silicic acid solution; and mixing and further processing the heel solution and the silicic acid solution to form the colloidal composition.
  • a metal is added to the heel solution.
  • the colloidal composition includes the stabilizer and a silicate doped with the metal such that the stabilizer and the metal are dispersed within one or more particles of the silicate.
  • the metal includes about 35 wt % or less based on silica.
  • the colloidal composition is further processed to form a crystalline structure.
  • the colloidal composition is further processed by heating.
  • a metal is added to the heel solution prior to crystallization.
  • the colloidal composition includes a zeolite.
  • the stabilizer includes a quaternary amine.
  • the present invention provides a method of forming a colloidal silicate composition.
  • the method includes preparing a silicic acid solution, a metal silicate solution and an alkaline solution; mixing and further processing the silicic acid solution and the metal silicate solution with the alkaline solution; and forming one or more silicate particles doped with a metal wherein the metal is dispersed within one or more of the silicate particles.
  • the metal is dispersed in a controlled manner.
  • the silica doped with metal includes about 2 wt % or less of the metal based on silica.
  • the metal includes an alkali metal, an alkaline earth metal, a 1 st row transition metal, a 2 nd row transition metal, a lanthanide, and combinations thereof.
  • a method of controlling a location of a metal within a metal-containing silica colloid includes preparing a silicic acid solution, a metal silicate solution and an alkaline solution; and selectively adding the metal silicate solution and the silicic acid solution to the alkaline solution to form a colloid of silica particles containing the metal.
  • the method further comprises adding the metal silicate solution before the silicic acid solution and forming the colloid of silica particles having the metal dispersed within an interior layer of one or more of the silica particles.
  • the method further comprises adding the silicic acid solution before the metal silicate solution and forming the colloid of silica particles having the metal dispersed within an outer layer of one or more of the silica particles.
  • the method further comprises adding the metal silicate solution and the silicic acid solution in an alternating manner and forming the colloid of silica particles having a metal-containing layer and a non-metal containing layer.
  • the silica particles includes a layered structure that has the non-metal containing layer disposed on the metal containing layer in a repeat manner.
  • the present invention generally relates to colloidal compositions and methods of preparing same.
  • the term “colloid” and other like terms including “colloidal”, “sol”, and the like refer to a two-phase system having a dispersed phase and a continuous phase.
  • the colloids of the present invention have a solid phase dispersed or suspended in a continuous or substantially continuous liquid phase, typically an aqueous solution.
  • the term “colloid” encompasses both phases whereas “colloidal particles” or “particles” refers to the dispersed or solid phase.
  • the present invention relates to colloidal compositions that include a silicate and that can be made in a readily and cost effective manner as described below in greater detail.
  • the present invention provides two types of synthesis procedures.
  • the present invention utilizes a heel solution that includes a stabilizer, such as a quaternary compound.
  • the stabilizer can enhance the colloidal synthesis in a number of ways, such as by stabilizing and better enabling a metal to be dispersed within the silicate of the colloidal composition. It is believed that the stabilizer can also enhance the ability of the silicate to have higher metal loading, such as about 35 wt % or less based on silica.
  • silicic acid and a metal silicate solution are selectively added to an alkaline solution thereby producing a colloid that includes a silicate with a metal dispersed therein in a controlled manner.
  • a method of preparing a colloidal composition provides adding a silicic acid solution to a reaction vessel that includes a heel solution having an aqueous solution containing a metal component and a stabilizing component to form a colloid of silica particles.
  • the stabilizer is an amine or quaternary compound.
  • amines suitable for use as the stabilizer include dipropylamine, trimethylamine, triethylmine, tri-n-propylamine, diethanolamine, monoethanolamine, triethanolamine, diisobutylamine, isopropylamine, diisopropylamine, dimethylamine, ethylenediaminetetraacetic acid, pyridine, the like and combinations thereof.
  • the stabilizing component is a quaternary amine that forms an alkaline solution when dispersed in water, such as quaternary ammonium hydroxides.
  • the quaternary amine includes a tetraalkyl ammonium ion wherein each alkyl group has a carbon chain length of 1 to 10, the alkyl groups being the same or different.
  • Nonlimiting examples of quaternary amines suitable for use as the stabilizer include tetramethylammonium hydroxide (TMAOH), tetrapropylammonium hydroxide (TPAOH), tetraethylammonium hydroxide (TEAOH), tetrabutylammonium hydroxide (TBAOH), tetrahexylammonium hydroxide, tetraoctylammonium hydroxide, tributylmethylammonium hydroxide, triethylmethylammonium hydroxide, trimethylphenylammonium hydroxide, methyltripropylammonium hydroxide, dodecyltrimethylammonium hydroxide, hexadecyltrimethylammonium hydroxide, dimethyldodecylethylammonium hydroxide, diethyldimethylammonium hydroxide, the like and combinations thereof.
  • TMAOH tetramethylammonium
  • the metal can include any suitable material and be derived from any suitable material including metal salts that are soluble or substantially soluble in an aqueous solution.
  • the metal includes an alkali metal, an alkaline earth metal, a 1 st row transition metal, a 2 nd row transition metal, a lanthanide, and combinations thereof.
  • Preferred metal components include aluminum, cerium, titanium, tin, zirconium, zinc, copper, nickel, molybdenum, iron, rhenium, vanadium, boron, the like and any combination thereof.
  • the silicic acid solution can be prepared by passing a sodium silicate solution through a bed of H + -cation exchange resin.
  • the resulting deionized silicic acid solution tends to be quite reactive and is typically kept cooled to retard polymerization.
  • the disassociated OH ⁇ from the stabilizer catalyzes a polymerization reaction between the cationic metal component and a silicate component from the silicic acid to form the colloid of silica particles.
  • the reaction thereby yields a solid phase composed of the metal component, the stabilizer and silica wherein the metal and stabilizer are dispersed within the silica particles.
  • Utilization of the stabilizer component obviates the need to provide a heel containing alkaline catalysts, such as NaOH, KOH, NH 4 OH, the like, and combinations thereof. It should be appreciated that any suitable type of silicic acid solution can be utilized.
  • the stabilizer serves as a stabilizing agent for the metal component.
  • the quaternary amine cation interacts with the metal oxide anion in the heel (MO 4 X ⁇ wherein M is the metal cation) ultimately stabilizing the metal.
  • the quaternary amine maintains the metal oxide anion in a four-fold coordination state or tetrahedral orientation so that silicon-to-metal ratios of four can be obtained. Stabilizing the metal component in this manner produces a greater number of silicon-metal linkages allowing the solid phase of the colloid to carry an increased amount of metal compared to surface treated colloids, for example.
  • the resultant silica colloid is capable of supporting from about 0.0001 wt % to about 35 wt % metal based on silica.
  • the metal-stabilized silica solid phase also demonstrates increased stability and remains stable in a pH range of about 1 to about 14.
  • stable means that the solid phase of the colloid is present, dispersed through the medium and stable throughout this entire pH range with effectively no precipitate.
  • the solid phase in an embodiment is amorphous and has a number of particles that are generally spherical in shape.
  • the colloidal particles have a diameter in the range of about 2 nanometers (nm) to about 1000 nm pursuant to an embodiment.
  • silicic acid is utilized to incorporate or disperse a metal component into the framework of colloidal silica (i.e., doping).
  • the method includes preparing a heel.
  • the heel includes an aqueous solution that at least includes a quaternary amine as defined herein or an alkaline agent. Suitable alkaline agents include, for example, NaOH, KOH, NH 4 OH, the like and combination thereof.
  • the silicic acid solution (can be prepared as previously discussed or other suitable manner) is reacted with a cationic metal component to form a metal silicate solution, represented chemically below: H 4 SiO 4 +M x+ ⁇ [x(H 3 SiO 4 ⁇ )-M x+ ]+xH +
  • the metal silicate solution is subsequently added to the heel to form the colloid.
  • the OH ⁇ present in the heel catalyzes the copolymerization of the cationic metal component and silicate (SiO 4 ⁇ ) from the silicic acid.
  • This produces a colloid with the metal dispersed within the silicate i.e., incorporated into the particle framework as discussed above, such as having a homogenous distribution of the metal component throughout the entire solid phase of the colloid.
  • the dispersion and loading of the metal is obtained as the copolymerization forms a metal-silicate lattice throughout the microstructure of the solid phase.
  • Nonlimiting examples of suitable metals that can be used as the cationic metal component include aluminum, cerium, titanium, tin, zirconium, zinc, copper, nickel, molybdenum, iron, rhenium, vanadium, boron, 1 st and 2 nd row transition metals, lanthanides, alkali metals, alkaline earth metals, the like and any combination thereof.
  • the metal component can be derived from any suitable metal source including, for example, any suitable metal salt that is soluble or substantially soluble in an aqueous solution.
  • metal silicate colloids of the present invention can have a metal content from about 0.0001% to about 2% by weight based on silica.
  • the metal silicate colloids of the present invention are amorphous and generally spherical in shape, wherein the particles have an effective diameter or particle size from about 2 nm to about 1000 nm in an embodiment.
  • the metal silicate colloids are stable at a pH range from about 1 to about 14, exhibiting effectively no precipitation in this range.
  • the size of the colloidal particles can be adjusted by varying the addition time of the metal silicate solution to the heel.
  • the metal silicate solution and the silicic acid solution are selectively added to the heel to control the position of the metal within the solid phase of the colloid as desired.
  • Both silicic acid solution and metal silicate solution can be added to the heel to initiate particle formation or to grow or otherwise increase the size of a pure silica particle initially added to the heel.
  • the metal silicate solution is added to the heel before the silicic acid solution in an embodiment.
  • This addition sequence yields a metal containing silica colloid wherein the metal is dispersed in a core or interior layer of the colloidal particle.
  • the subsequent addition of the silicic acid can be used to cover the interior metal-containing portion of the particle with a layer containing on silica without the metal.
  • the silicic acid solution can be added to the heel prior to the addition of the metal silicate solution in an embodiment.
  • This addition sequence yields colloidal particles having a core or interior composed of silica.
  • the metal silicate solution can then be added to coat the silica particle to produce a particle containing metal on an exterior surface or outer layer of the particle wherein the metal is dispersed within this particle layer.
  • Addition of only the metal silicate solution to the heel can yield a colloid having a dispersion or distribution of metal within one or more of the colloidal particle as previously discussed.
  • Adding the metal silicate solution and the silicic acid solution in an alternating manner or a sequence such as metal silicate-silicic acid-metal silicate-silicic acid can yield a colloidal particle having a number of layers wherein metal containing layers are separated by layers containing silica and without a metal in an embodiment. It will be appreciated that the duration of silicic acid and/or metal silicate addition can be varied as desired to vary the width or thickness of each particle layer in the colloid.
  • the multiple layered colloid particles of the present invention are generally spherical in shape and have an effective particle size of about 2 nm to about 1000 nm according to an embodiment.
  • colloidal compositions and methods of making same can be modified in any suitable manner.
  • the colloidal compositions as described above can be further processed to form a crystalline structure, such as a crystalline silicate, a crystalline metallosilicate including a zeolite, the like and combinations thereof.
  • continued hydrothermal treatment at suitable temperatures and over a suitable period of time can produce a more crystalline silicate including metallosilicates, such as zeolites, from the colloidal compositions described-above wherein the colloidal composition includes silicate and a stabilizer with or without a metal dispersed within the silicate, specific examples of which are provided below in greater detail.
  • a stabilizer including tetramethylammonium hydroxide (TMAOH), tetrapropylammonium hydroxide (TPAOH), tetraethylammonium hydroxide (TEAOH) and/or the like e.g., a stabilizer including tetramethylammonium hydroxide (TMAOH), tetrapropylammonium hydroxide (TPAOH), tetraethylammonium hydroxide (TEAOH) and/or the like
  • TMAOH tetramethylammonium hydroxide
  • TPAOH tetrapropylammonium hydroxide
  • TEAOH tetraethylammonium hydroxide
  • Doped colloidal silica is useful in multitudinous industrial applications including, for example, dental applications, protein separation, molecular sieves, nanoporous membranes, wave guides, photonic crystals, refractory applications, clarification of wine and juice, chemical mechanical planarization of semiconductor and disk drive components, catalyst supports, retention and drainage aids in papermaking, fillers, surface coatings, ceramic materials, investment casting binders, flattening agents, proppants, cosmetic formulations, particularly sunscreens, and polishing abrasives in the glass, optical and electronics and semiconductor industries.
  • the form of silica used in a particular application depends in large part on the silica particle's size and porosity characteristics. Doped colloidal silica having the desired characteristics is readily prepared according to the method of this invention.
  • this invention is a material for use in an industrial application comprising the colloidal composition described herein.
  • the industrial application is selected from the group consisting of catalyst supports, retention and drainage aids in papermaking, fillers, flattening agents, proppants and polishing abrasives.
  • a 5 wt % tetramethylammonium hydroxide (20-25 wt %) solution was added to a 12-gallon reactor along with 10.23 wt % of deionized (DI) water.
  • DI deionized
  • a 0.70 wt % aluminum chlorohydrate (50 wt %) solution was added to 19.82 wt % DI water.
  • the aluminum chlorohydrate solution was then added to the reactor at room temperature at a rate of 200 mL/min.
  • the reactor was heated to 100° C.
  • 64.25 wt % silicic acid was added to the reactor at a ramp rate of 100-220 mL/min over 3.25 hours.
  • Table 1 lists the physical characteristics of the colloidal aluminosilicate made in the 12-gallon reactor after it was concentrated by ultra-filtration: TABLE 1 Concentrated Colloidal Aluminosilicate (12 gallon reactor) Results Solids wt % (specific 25.30 gravity) Al 2 O 3 .SiO 2 wt % (ash) 24.72 Solids wt % (removing 29.75 water) “includes organic moiety” PH 11.02 Specific Gravity 1.1671 Conductance (mhos) 7100 Particle Size (nm), 5.00 Titration wt % Al 2 O 3 (BOS), ICP 3.93
  • a 0.37 M AlCl 3 .6H 2 O solution was prepared with a pH of 2.2 and was used as prepared as further described below.
  • a second solution of 0.50 M AlCl 3 .6H 2 O was prepared. This solution was passed through an ion exchange column containing an anion exchange resin (Dowex 550A (OH ⁇ )). 100 g of AlCl 3 .6H 2 O solution was passed through 100 mL of resin. The pH of the aluminum containing solution was ca. 3.4 after being passed through the column. Aluminum chlorohydrate can also be used.
  • the silicic acid solution/monomeric aluminum solution (2.93 g of 0.37 M AlCl 3 .6H 2 O solution) was added to a caustic heel containing 0.30 g of NaOH (50 wt %) in 14.40 g of DI water over a 5.0 hours ramp. A total of 68.57 g of silicic acid solution/aluminum solution was added.
  • the silicic acid solution/polyvalent aluminum solution (3.02 g of 0.50 M AlCl 3 .6H 2 O anion-exchanged solution) was added to a caustic heel containing 0.30 g of NaOH (50 wt %) in 14.20 g of DI water over a 5.0 hour ramp. A total of 68.57 g of silicic acid solution/aluminum solution was added.
  • the silicic acid solution/polyvalent aluminum solution (3.02 g of 0.50 M AlCl 3 .6H 2 O anion-exchanged solution) was added to a caustic heel containing 0.30 g of NaOH (50 wt %) in 14.20 g of Example 2 over a 5.0 hour ramp. A total of 68.57 g of silicic acid solution/aluminum solution was added.
  • the silicic acid solution/aluminum solution (3.02 g of 0.50 M AlCl 3 .6H 2 O anion-exchanged solution) was added to a caustic heel containing 0.30 g of NaOH (50 wt %) in 14.20 g of Example 3 over a 5.0 hour ramp. A total of 68.57 g of silicic acid solution/aluminum solution was added.
  • the silicic acid solution/aluminum solution (0.67 g of a 0.87 M solution of aluminum chlorohydrate) was added to a caustic heel containing 0.11 g NaOH (50 wt %) in 3.82 g of 20 nm silica sol in 8.18 g of DI water over a 4.75 hours ramp.
  • the reaction was heated at 93° C.
  • a total of 87.89 g of silicic acid solution/aluminum solution was added.
  • the final product was cation-exchanged to remove excess sodium, large particle filtered (LPC) and pH adjusted to 6.4.
  • LPC large particle filtered
  • a solution of 0.50 M Ce 2 (CO 3 ) 3 was prepared by adding 46 g Ce 2 (CO 3 ) 3 into 100 ml DI water then adding 1N HCl until dissolved. The solution was then topped up to 200 ml with DI water.
  • a silicic acid solution was prepared where 200 g of (sodium silicate) was added to 1000 g of DI water. The solution was passed through a column containing a cation exchange resin (Dowex 650C (H + )). About 40 mL of resin for 100 g of diluted sodium silicate solution was used.
  • a cation exchange resin Dowex 650C (H + )
  • the silicic acid solution/cerium solution (6.2 ml of 0.5 M Ce 2 (CO 3 ) 3 solution) was added to a caustic heel containing 5 g of KOH (45 wt %) in 200 g of DI water over a 5.0 hours ramp. A total of 1200 g of silicic acid solution/cerium solution was added to produce the cerium doped silica colloids
  • a titanium containing solution was prepared.
  • a solution of 0.50 M TiCl 4 was prepared by slowly adding 100 ml DI water into a beaker containing 9.4 g TiCl 4 and 10 ml isopropyl alcohol.
  • the silicic acid was prepared in the same fashion as described in Example 6. To the silicic acid was added an amount of the titanium containing solution to produce the desired concentration (ppm) of titanium based on silica (BOS) as illustrated below in Table 2.
  • the silicic acid solution/titanium solution (12.6 ml of 0.5 M TiCl4 solution) was added to a caustic heel containing 5 g of KOH (45 wt %) in 200 g of DI water over a 5.0 hours ramp. A total of 1200 g of silicic acid solution/cerium solution was added to produce the titanium doped silica colloid.
  • the zinc containing solution used in this procedure was a commercially-available product, namely 1N Zn(NO 3 ) 2 .
  • the silicic acid was prepared in the same fashion as described in Example 6. To the silicic acid was added an amount of zinc containing solution to provide the desired concentration (ppm) of zinc based on silica (BOS) as illustrated below in Table 2.
  • the silicic acid solution/zinc solution (6 ml of 1 M Zn(NO 3 ) 2 solution) was added to a caustic heel containing 5 g of KOH (45 wt %) in 200 g of DI water over a 5.0 hours ramp. A total of 1200 g of acid sol/cerium solution was added to produce the zinc doped silica colloid.
  • Colloidal Silicalite-1 was synthesized with a narrow particle size distribution from a mole composition of: 1TPAOH:1.9SiO 2 :109H 2 O
  • the source of silica was silicic acid.
  • the reactor vessel was charged with a 20-25 wt % solution of TPAOH, which was heated to 90° C. To this, the silicic acid was added over 3 hours. A clear solution resulted, which was heated for 18 hours.
  • Colloidal ZSM-5 was synthesized with a narrow particle size distribution from a mole composition of: 65TPAOH:125 SiO 2 :1Al 2 O 3 :7000H 2 O
  • the source of silica was silicic acid.
  • the reactor vessel was charged with a 20-25 wt % solution of TPAOH, which was heated to 90° C. To this the aluminum/silicic acid solution was added over 2 hours. A clear solution resulted, which was heated for 24 hours.
  • Metallosilicate Colloids :
  • Table 2 shows the various prepared metal doped samples with the different heels, pH of the different metal containing solutions, amounts of metal added to the acid sol based on silica (BOS) and a variety of characterization techniques to determine particle size and the extent, if any, agglomeration.
  • BOS silica
  • Table 2 provides a summary of the synthesis procedures according to Examples 1-10 as detailed above: TABLE 2 Theoretical and Particle calculated diameter pH final (ICP) Particle (nm) solution amounts of diameter and (surface [Final wt % Sample Metal source metal QELS and area) m 2 /g metal doped (Heel) and pH BOS a (ppm) (TEM) (nm) Titration Observations SiO 2 ] Example 1 AlCl 3 .6H 2 O 2.2 3,500 (3,281) 47.8 (29.6) 12.9 (233) Prec.
  • ICP Theoretical and Particle calculated diameter pH final (ICP) Particle (nm) solution amounts of diameter and (surface [Final wt % Sample Metal source metal QELS and area) m 2 /g metal doped (Heel) and pH BOS a (ppm) (TEM) (nm) Titration Observations SiO 2 ]
  • Example 5 Al 2 (OH) 5 Cl.2H 2 O 3,192 (2,446) 49.3 (53.9) 29.4 (102) No prec. 6.87 3.8 [32.7]
  • Example 6 Ce 2 (CO 3 ) 3 11650 50.8 No prec. 5.55
  • Example 7 TiCl4 3985 45.7 No prec. 5.42
  • Example 8 Zn(NO 3 ) 2 5438 No prec. 5.38
  • Example 9 — — 241 No prec. 11.5 Silicalite by XRD
  • Example 10 Al 2 (OH) 5 Cl.2H 2 O 26000 292 No prec. 11.5 3.8 ZSM-5 byXRD *Aluminum source is anion exchanged to remove chloride and increase pH.
  • a BOS means based on silica.
  • the metal doped colloids described above and made pursuant to various embodiments exhibit good stability in the pH range 3-9.
  • a stability test was conducted on the filtered and cation deionized aluminosilicate colloid of Example 5. The pH was adjusted to 4.1, 6.5 and 8.5 and effective particle diameters were measured (QELS) before and after heat treatment for two weeks at 60° C.
  • colloidal compositions of the present invention can be utilized in a number of different and suitable types of applications in any suitable forms and amounts thereof.
  • the colloidal composition can be used as a chemical mechanical polishing agent including use for electronic components; a catalyst material and supports thereof including use in the petrochemical industry, such as cracking to increase fractions of gasoline; as a detergent or agent thereof to remove calcium ions and/or the like from solution; and any other types of suitable applications.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Inorganic Chemistry (AREA)
  • Public Health (AREA)
  • Veterinary Medicine (AREA)
  • Animal Behavior & Ethology (AREA)
  • General Health & Medical Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Birds (AREA)
  • Epidemiology (AREA)
  • Dispersion Chemistry (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Geology (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Materials Engineering (AREA)
  • Nanotechnology (AREA)
  • Dermatology (AREA)
  • Physics & Mathematics (AREA)
  • Composite Materials (AREA)
  • Condensed Matter Physics & Semiconductors (AREA)
  • General Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Colloid Chemistry (AREA)
  • Silicon Compounds (AREA)
US10/827,214 2004-04-19 2004-04-19 Colloidal compositions and methods of preparing same Abandoned US20050234136A1 (en)

Priority Applications (12)

Application Number Priority Date Filing Date Title
US10/827,214 US20050234136A1 (en) 2004-04-19 2004-04-19 Colloidal compositions and methods of preparing same
KR1020067021598A KR20070027535A (ko) 2004-04-19 2005-04-13 콜로이드성 조성물 및 그의 제조방법
CN2005800118801A CN1942237B (zh) 2004-04-19 2005-04-13 胶体组合物及其制备方法
JP2007509513A JP5103168B2 (ja) 2004-04-19 2005-04-13 コロイド状組成物およびその調製方法
EP05735668.5A EP1744825B1 (en) 2004-04-19 2005-04-13 Colloidal compositions and methods of preparing same
BRPI0509859-9A BRPI0509859B1 (pt) 2004-04-19 2005-04-13 Método para controlar uma localização de um metal dentro de um colóide de sílica contendo metal
CN2010102460035A CN101912755B (zh) 2004-04-19 2005-04-13 胶体组合物及其制备方法
PCT/US2005/012371 WO2005104683A2 (en) 2004-04-19 2005-04-13 Colloidal compositions and methods of preparing same
CA2560748A CA2560748C (en) 2004-04-19 2005-04-13 Colloidal compositions and methods of preparing same
SG200902613-9A SG152248A1 (en) 2004-04-19 2005-04-13 Colloidal compositions and methods of preparing same
TW094112213A TWI377980B (en) 2004-04-19 2005-04-18 Colloidal compositions and methods of preparing same
US15/877,168 US10730756B2 (en) 2004-04-19 2018-01-22 Colloidal compositions and methods of preparing same

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US10/827,214 US20050234136A1 (en) 2004-04-19 2004-04-19 Colloidal compositions and methods of preparing same

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/877,168 Continuation US10730756B2 (en) 2004-04-19 2018-01-22 Colloidal compositions and methods of preparing same

Publications (1)

Publication Number Publication Date
US20050234136A1 true US20050234136A1 (en) 2005-10-20

Family

ID=35097100

Family Applications (2)

Application Number Title Priority Date Filing Date
US10/827,214 Abandoned US20050234136A1 (en) 2004-04-19 2004-04-19 Colloidal compositions and methods of preparing same
US15/877,168 Active 2025-02-03 US10730756B2 (en) 2004-04-19 2018-01-22 Colloidal compositions and methods of preparing same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/877,168 Active 2025-02-03 US10730756B2 (en) 2004-04-19 2018-01-22 Colloidal compositions and methods of preparing same

Country Status (10)

Country Link
US (2) US20050234136A1 (ru)
EP (1) EP1744825B1 (ru)
JP (1) JP5103168B2 (ru)
KR (1) KR20070027535A (ru)
CN (2) CN101912755B (ru)
BR (1) BRPI0509859B1 (ru)
CA (1) CA2560748C (ru)
SG (1) SG152248A1 (ru)
TW (1) TWI377980B (ru)
WO (1) WO2005104683A2 (ru)

Cited By (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070034116A1 (en) * 2005-08-10 2007-02-15 Mac Donald Dennis L Silica sols with controlled minimum particle size and preparation thereof
US20070231249A1 (en) * 2006-04-04 2007-10-04 Francois Batllo Production and use of polysilicate particulate materials
US20070282122A1 (en) * 2006-05-30 2007-12-06 Holland Brian T Organically modifid silica and use thereof
WO2007137508A1 (fr) * 2006-05-26 2007-12-06 Anji Microelectronics (Shanghai) Co., Ltd Suspension de polissage pour planarisation fine de surfaces et procédé d'utilisation associé
US20080085412A1 (en) * 2006-10-04 2008-04-10 Ortiz C Yolanda Silica-coated metal oxide sols having variable metal oxide to silica ratio
US20080108497A1 (en) * 2006-11-08 2008-05-08 Holland Brian T Metal-rich siliceous compositions and methods of producing same
US20080190861A1 (en) * 2007-02-14 2008-08-14 Branning Merle L Composition and method for agglomerating solids in solid-liquid separation processes
US20090018219A1 (en) * 2005-08-10 2009-01-15 Macdonald Dennis L Method of producing silica sols with controllable broad size distribution and minimum particle size
EP2085142A1 (en) * 2006-11-10 2009-08-05 Yuka Collaboration Corporation Method for producing coating agent exhibiting photocatalytic activity and coating agent obtained by the same
US20100146117A1 (en) * 2008-12-01 2010-06-10 Sebastiaan Hoeksel Access control for M2M devices in a mobile communication network
WO2010117949A2 (en) 2009-04-06 2010-10-14 Nalco Company Novel approach in controlling dsp scale in the bayer process
WO2013028958A1 (en) 2011-08-25 2013-02-28 Basf Corporation Molecular sieve precursors and synthesis of molecular sieves
WO2014081607A1 (en) * 2012-11-25 2014-05-30 Chevron U.S.A. Inc. Method for preparing cha-type molecular sieves using colloidal aluminosilicate
US8764974B2 (en) 2010-04-16 2014-07-01 Nalco Company Processing aids to improve the bitumen recovery and froth quality in oil sands extraction processes
WO2014150884A1 (en) * 2013-03-15 2014-09-25 Ecolab Usa Inc. Methods of polishing sapphire surfaces
US9283648B2 (en) 2012-08-24 2016-03-15 Ecolab Usa Inc. Methods of polishing sapphire surfaces
US9302228B2 (en) 2014-02-28 2016-04-05 Pall Corporation Charged porous polymeric membrane with high void volume
US9309126B2 (en) 2014-02-28 2016-04-12 Pall Corporation Rapidly dissolvable nanoparticles
US9446355B2 (en) 2014-02-28 2016-09-20 Pall Corporation Porous polymeric membrane with high void volume
US9561473B2 (en) 2014-02-28 2017-02-07 Pall Corporation Charged hollow fiber membrane having hexagonal voids
US9610548B2 (en) 2014-02-28 2017-04-04 Pall Corporation Composite porous polymeric membrane with high void volume
US9737860B2 (en) 2014-02-28 2017-08-22 Pall Corporation Hollow fiber membrane having hexagonal voids
US9764292B2 (en) 2014-02-28 2017-09-19 Pall Corporation Porous polymeric membrane with high void volume
US9776142B2 (en) 2014-02-28 2017-10-03 Pall Corporation Porous polymeric membrane with high void volume
WO2018111390A1 (en) 2016-12-13 2018-06-21 Chevron U.S.A. Inc. Synthesis of molecular sieve ssz-41
US10005982B2 (en) 2015-07-18 2018-06-26 Ecolab Usa Inc. Chemical additives to improve oil separation in stillage process operations
US10087081B2 (en) 2013-03-08 2018-10-02 Ecolab Usa Inc. Process for producing high solids colloidal silica
EP3368478A4 (en) * 2015-10-26 2019-06-05 Ecolab USA Inc. VERY HOMOGENEOUS ZEOLITE PRELUDE
US10377014B2 (en) 2017-02-28 2019-08-13 Ecolab Usa Inc. Increased wetting of colloidal silica as a polishing slurry
US10654724B2 (en) 2016-12-02 2020-05-19 Ecolab Usa Inc. Polyaluminum salts and their uses in preparation of high-purity colloidal aluminum-silica composite particles and zeolites
US11384023B2 (en) 2017-09-26 2022-07-12 Delta Faucet Company Aqueous gelcasting formulation for ceramic products

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101225282B (zh) * 2007-01-19 2013-05-01 安集微电子(上海)有限公司 一种低介电材料抛光液
GB0922503D0 (en) * 2009-12-23 2010-02-10 Pilkington Group Ltd Fire resistant glazings
CN102344761A (zh) * 2011-08-03 2012-02-08 南通海迅天恒纳米科技有限公司 一种铈掺杂二氧化硅溶胶的制备方法
CN105778775B (zh) * 2014-12-23 2021-03-02 安集微电子(上海)有限公司 一种中性胶体二氧化硅的制备方法
CN104745146A (zh) * 2015-03-23 2015-07-01 江苏天恒纳米科技股份有限公司 含铈掺杂二氧化硅纳米复合磨粒溶胶、抛光液及其制备方法
CN106867449A (zh) * 2016-12-30 2017-06-20 上海映智研磨材料有限公司 一种氧化硅复合磨粒及其制备方法和用途
CN111315687B (zh) * 2017-07-24 2023-09-15 普瑞伯纳公司 包含金属的制剂
CN108862215B (zh) * 2018-07-26 2020-05-08 河钢股份有限公司承德分公司 一种生产氮化钒用粘结剂及其制备方法

Citations (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1552341A (en) * 1921-09-13 1925-09-01 L D Caulk Company Dental cement and process of making same
US2736668A (en) * 1952-05-09 1956-02-28 Du Pont Process of methoxylating the surface of a siliceous material, and the resulting product
US2913419A (en) * 1956-04-18 1959-11-17 Du Pont Chemical process and composition
US2974108A (en) * 1957-01-14 1961-03-07 Du Pont Aluminosilicate aquasols and their preparation
US4287086A (en) * 1975-05-02 1981-09-01 Nl Industries, Inc. Viscous organic systems containing an organophilic clay gellant without an organic dispersant therefor
US4410501A (en) * 1979-12-21 1983-10-18 Snamprogetti S.P.A. Preparation of porous crystalline synthetic material comprised of silicon and titanium oxides
US4468023A (en) * 1981-10-13 1984-08-28 Solloway Daniel S Aquatic neck exercise assembly
US4623142A (en) * 1984-01-31 1986-11-18 Mackechnie Bruce Hand held, multi-directional device for aquatic exercising
US4666692A (en) * 1978-06-22 1987-05-19 Snamprogetti, S.P.A. Silica-based synthetic material containing titanium in the crystal lattice and process for its preparation
US4670617A (en) * 1985-12-30 1987-06-02 Amoco Corporation Propylation of toluene with a high surface area, zinc-modified, crystalline silica molecular sieve
US5024826A (en) * 1990-03-05 1991-06-18 E. I. Du Pont De Nemours And Company Silica particulate composition
US5031904A (en) * 1988-06-20 1991-07-16 Solloway Daniel S Aquatic boot
US5221497A (en) * 1988-03-16 1993-06-22 Nissan Chemical Industries, Ltd. Elongated-shaped silica sol and method for preparing the same
US5558851A (en) * 1992-12-16 1996-09-24 Chevron U.S.A. Inc. Preparation of aluminosilicate zeolites
US5597512A (en) * 1993-10-15 1997-01-28 Nissan Chemical Industries, Ltd. Method for preparing elongated-shaped silica sol
US6191323B1 (en) * 2000-04-25 2001-02-20 Uop Llc Process for the reduction of ketones and aldehydes to alcohols using a tin substituted zeolite beta
US6306364B1 (en) * 1998-12-18 2001-10-23 Uop Llc Stannosilicate molecular sieves
US6358882B1 (en) * 1998-12-08 2002-03-19 The Standard Oil Company Fluid bed vinyl acetate catalyst
US6442795B1 (en) * 2001-01-16 2002-09-03 Girefa Enterprise Co., Ltd. Damper for a pivot door
US6669924B1 (en) * 1999-11-23 2003-12-30 Universite Laval Mesoporous zeolitic material with microporous crystalline mesopore walls
US6672993B2 (en) * 2001-01-12 2004-01-06 Aqualogix, Inc. Aquatic exercise device
US20050014000A1 (en) * 2003-07-18 2005-01-20 Eastman Kodak Company Cationic shelled particle
US20070034116A1 (en) * 2005-08-10 2007-02-15 Mac Donald Dennis L Silica sols with controlled minimum particle size and preparation thereof
US20070104643A1 (en) * 2005-08-05 2007-05-10 Holland Brian T Mesoporous nanocrystaline zeolite composition and preparation from amorphous colloidal metalosilicates
US20090018219A1 (en) * 2005-08-10 2009-01-15 Macdonald Dennis L Method of producing silica sols with controllable broad size distribution and minimum particle size

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4243828A (en) * 1963-02-27 1981-01-06 Mobil Oil Corporation Alkylation of aromatics using a high silica zeolite
US3442795A (en) * 1963-02-27 1969-05-06 Mobil Oil Corp Method for preparing highly siliceous zeolite-type materials and materials resulting therefrom
DE3370150D1 (en) 1982-11-10 1987-04-16 Montedipe Spa Process for the conversion of linear butenes to propylene
JP2803134B2 (ja) * 1988-03-16 1998-09-24 日産化学工業株式会社 細長い形状のシリカゾル及びその製造法
NO300125B1 (no) 1988-03-16 1997-04-14 Nissan Chemical Ind Ltd Stabil væskeformig silikasol, samt fremgangsmåte ved fremstilling derav
EP0512986A4 (en) * 1990-01-31 1993-04-07 Industrial Progress, Inc. Functional complex microgels with rapid formation kinetics
DE4211050C2 (de) 1992-04-02 1995-10-19 Siemens Ag Verfahren zur Herstellung eines Bipolartransistors in einem Substrat
US6274112B1 (en) * 1999-12-08 2001-08-14 E. I. Du Pont De Nemours And Company Continuous production of silica-based microgels
JP2003183019A (ja) * 2001-12-18 2003-07-03 Catalysts & Chem Ind Co Ltd ゼオライトの濾過分離方法
CN1224590C (zh) * 2002-05-22 2005-10-26 吉林大学 一种复合磁性粒子的制备方法

Patent Citations (27)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1552341A (en) * 1921-09-13 1925-09-01 L D Caulk Company Dental cement and process of making same
US2736668A (en) * 1952-05-09 1956-02-28 Du Pont Process of methoxylating the surface of a siliceous material, and the resulting product
US2913419A (en) * 1956-04-18 1959-11-17 Du Pont Chemical process and composition
US2974108A (en) * 1957-01-14 1961-03-07 Du Pont Aluminosilicate aquasols and their preparation
US4287086A (en) * 1975-05-02 1981-09-01 Nl Industries, Inc. Viscous organic systems containing an organophilic clay gellant without an organic dispersant therefor
US4666692A (en) * 1978-06-22 1987-05-19 Snamprogetti, S.P.A. Silica-based synthetic material containing titanium in the crystal lattice and process for its preparation
US4410501A (en) * 1979-12-21 1983-10-18 Snamprogetti S.P.A. Preparation of porous crystalline synthetic material comprised of silicon and titanium oxides
US4468023A (en) * 1981-10-13 1984-08-28 Solloway Daniel S Aquatic neck exercise assembly
US4623142A (en) * 1984-01-31 1986-11-18 Mackechnie Bruce Hand held, multi-directional device for aquatic exercising
US4670617A (en) * 1985-12-30 1987-06-02 Amoco Corporation Propylation of toluene with a high surface area, zinc-modified, crystalline silica molecular sieve
US5221497A (en) * 1988-03-16 1993-06-22 Nissan Chemical Industries, Ltd. Elongated-shaped silica sol and method for preparing the same
US5031904A (en) * 1988-06-20 1991-07-16 Solloway Daniel S Aquatic boot
US5024826A (en) * 1990-03-05 1991-06-18 E. I. Du Pont De Nemours And Company Silica particulate composition
US5558851A (en) * 1992-12-16 1996-09-24 Chevron U.S.A. Inc. Preparation of aluminosilicate zeolites
US5597512A (en) * 1993-10-15 1997-01-28 Nissan Chemical Industries, Ltd. Method for preparing elongated-shaped silica sol
US6358882B1 (en) * 1998-12-08 2002-03-19 The Standard Oil Company Fluid bed vinyl acetate catalyst
US6306364B1 (en) * 1998-12-18 2001-10-23 Uop Llc Stannosilicate molecular sieves
US6669924B1 (en) * 1999-11-23 2003-12-30 Universite Laval Mesoporous zeolitic material with microporous crystalline mesopore walls
US6191323B1 (en) * 2000-04-25 2001-02-20 Uop Llc Process for the reduction of ketones and aldehydes to alcohols using a tin substituted zeolite beta
US6672993B2 (en) * 2001-01-12 2004-01-06 Aqualogix, Inc. Aquatic exercise device
US20040053749A1 (en) * 2001-01-12 2004-03-18 Stout Tadlington A. Aquatic exercise device
US6442795B1 (en) * 2001-01-16 2002-09-03 Girefa Enterprise Co., Ltd. Damper for a pivot door
US20050014000A1 (en) * 2003-07-18 2005-01-20 Eastman Kodak Company Cationic shelled particle
US20070104643A1 (en) * 2005-08-05 2007-05-10 Holland Brian T Mesoporous nanocrystaline zeolite composition and preparation from amorphous colloidal metalosilicates
US20100104500A1 (en) * 2005-08-05 2010-04-29 Holland Brian T Method of manufacturing mesoporous zeolite agglomerates
US20070034116A1 (en) * 2005-08-10 2007-02-15 Mac Donald Dennis L Silica sols with controlled minimum particle size and preparation thereof
US20090018219A1 (en) * 2005-08-10 2009-01-15 Macdonald Dennis L Method of producing silica sols with controllable broad size distribution and minimum particle size

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
Holland et al, "Dual Templating of Macroporous Silicates with Zeolitic Microporous Frameworks," J. Am. Chem. Soc. 1999, 121, 4308-4309. *
The Merriam-Webster Unabridged Dictionary., Online @ http://www.merriam-webster.com/dictionary/lattice (copyright 2014), Headword: lattice, layer; p. 1 of 1. *

Cited By (58)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090018219A1 (en) * 2005-08-10 2009-01-15 Macdonald Dennis L Method of producing silica sols with controllable broad size distribution and minimum particle size
US20070034116A1 (en) * 2005-08-10 2007-02-15 Mac Donald Dennis L Silica sols with controlled minimum particle size and preparation thereof
US8052788B2 (en) 2005-08-10 2011-11-08 Nalco Company Method of producing silica sols with controllable broad size distribution and minimum particle size
US20070231249A1 (en) * 2006-04-04 2007-10-04 Francois Batllo Production and use of polysilicate particulate materials
US10227238B2 (en) * 2006-04-04 2019-03-12 Ecolab Usa Inc. Production and use of polysilicate particulate materials
WO2007137508A1 (fr) * 2006-05-26 2007-12-06 Anji Microelectronics (Shanghai) Co., Ltd Suspension de polissage pour planarisation fine de surfaces et procédé d'utilisation associé
US20070282122A1 (en) * 2006-05-30 2007-12-06 Holland Brian T Organically modifid silica and use thereof
WO2007143416A3 (en) * 2006-05-30 2008-02-28 Nalco Co Organically modified silica and use thereof
US8372999B2 (en) 2006-05-30 2013-02-12 Nalco Company Organically modified silica and use thereof
CN101454245B (zh) * 2006-05-30 2013-01-02 纳尔科公司 有机改性的二氧化硅及其用途
EP2021282A2 (en) * 2006-05-30 2009-02-11 Nalco Company Organically modified silica and use thereof
US8106229B2 (en) 2006-05-30 2012-01-31 Nalco Company Organically modifid silica and use thereof
EP2021282A4 (en) * 2006-05-30 2012-01-18 Nalco Co ORGANICALLY MODIFIED SILICA AND THEIR APPLICATION
WO2008060768A3 (en) * 2006-10-04 2008-08-07 Nalco Co Silica-coated metal oxide sols having variable metal oxide to silica ration
JP2010505731A (ja) * 2006-10-04 2010-02-25 ナルコ カンパニー 可変シリカ対金属酸化物比を有するシリカ被覆金属酸化物ゾル
US20080085412A1 (en) * 2006-10-04 2008-04-10 Ortiz C Yolanda Silica-coated metal oxide sols having variable metal oxide to silica ratio
EP2074061A2 (en) * 2006-10-04 2009-07-01 Nalco Company Silica-coated metal oxide sols having variable metal oxide to silica ration
EP2074061A4 (en) * 2006-10-04 2012-10-10 Nalco Co SILICA-COATED METAL OXIDEOLE WITH CHANGING METALXOXIDE / SILICA RATIO
US20100074974A1 (en) * 2006-11-08 2010-03-25 Holland Brian T Metal-rich siliceous compositions and methods of producing same
US20080108497A1 (en) * 2006-11-08 2008-05-08 Holland Brian T Metal-rich siliceous compositions and methods of producing same
US8003707B2 (en) * 2006-11-08 2011-08-23 Nalco Company Metal-rich siliceous compositions and methods of producing same
EP2079546A2 (en) * 2006-11-08 2009-07-22 Nalco Company Metal-rich siliceous compositions and methods of producing same
EP2079546A4 (en) * 2006-11-08 2012-08-29 Nalco Co METALLIC SILICATE COMPOSITIONS AND MANUFACTURING METHOD THEREFOR
US20100056365A1 (en) * 2006-11-10 2010-03-04 Yuku Collaboration Corporation Method for producing coating agent exhibiting photocatalytic activity and coating agent obtained thereby
EP2085142A4 (en) * 2006-11-10 2011-08-24 Yuka Collaboration Corp METHOD FOR MANUFACTURING A COATING AGENT HAVING PHOTOCATALYTIC ACTIVITY AND COATING AGENT OBTAINED BY THIS PROCESS
EP2085142A1 (en) * 2006-11-10 2009-08-05 Yuka Collaboration Corporation Method for producing coating agent exhibiting photocatalytic activity and coating agent obtained by the same
US20080190861A1 (en) * 2007-02-14 2008-08-14 Branning Merle L Composition and method for agglomerating solids in solid-liquid separation processes
US20100146117A1 (en) * 2008-12-01 2010-06-10 Sebastiaan Hoeksel Access control for M2M devices in a mobile communication network
WO2010117949A2 (en) 2009-04-06 2010-10-14 Nalco Company Novel approach in controlling dsp scale in the bayer process
US8764974B2 (en) 2010-04-16 2014-07-01 Nalco Company Processing aids to improve the bitumen recovery and froth quality in oil sands extraction processes
WO2013028958A1 (en) 2011-08-25 2013-02-28 Basf Corporation Molecular sieve precursors and synthesis of molecular sieves
US9174849B2 (en) 2011-08-25 2015-11-03 Basf Corporation Molecular sieve precursors and synthesis of molecular sieves
US9283648B2 (en) 2012-08-24 2016-03-15 Ecolab Usa Inc. Methods of polishing sapphire surfaces
US9446493B2 (en) 2012-08-24 2016-09-20 Ecolab Usa Inc. Kit for polishing sapphire surfaces
WO2014081607A1 (en) * 2012-11-25 2014-05-30 Chevron U.S.A. Inc. Method for preparing cha-type molecular sieves using colloidal aluminosilicate
US10087081B2 (en) 2013-03-08 2018-10-02 Ecolab Usa Inc. Process for producing high solids colloidal silica
WO2014150884A1 (en) * 2013-03-15 2014-09-25 Ecolab Usa Inc. Methods of polishing sapphire surfaces
US9896604B2 (en) 2013-03-15 2018-02-20 Ecolab Usa Inc. Methods of polishing sapphire surfaces
EP2969391A4 (en) * 2013-03-15 2017-02-01 Ecolab USA Inc. Methods of polishing sapphire surfaces
US9776142B2 (en) 2014-02-28 2017-10-03 Pall Corporation Porous polymeric membrane with high void volume
US9302228B2 (en) 2014-02-28 2016-04-05 Pall Corporation Charged porous polymeric membrane with high void volume
US9737860B2 (en) 2014-02-28 2017-08-22 Pall Corporation Hollow fiber membrane having hexagonal voids
US9764292B2 (en) 2014-02-28 2017-09-19 Pall Corporation Porous polymeric membrane with high void volume
US9561473B2 (en) 2014-02-28 2017-02-07 Pall Corporation Charged hollow fiber membrane having hexagonal voids
US9446355B2 (en) 2014-02-28 2016-09-20 Pall Corporation Porous polymeric membrane with high void volume
US9610548B2 (en) 2014-02-28 2017-04-04 Pall Corporation Composite porous polymeric membrane with high void volume
US9309126B2 (en) 2014-02-28 2016-04-12 Pall Corporation Rapidly dissolvable nanoparticles
US10005982B2 (en) 2015-07-18 2018-06-26 Ecolab Usa Inc. Chemical additives to improve oil separation in stillage process operations
US10513669B2 (en) 2015-07-18 2019-12-24 Ecolab Usa Inc. Chemical additives to improve oil separation in stillage process operations
EP3368478A4 (en) * 2015-10-26 2019-06-05 Ecolab USA Inc. VERY HOMOGENEOUS ZEOLITE PRELUDE
US10399859B2 (en) 2015-10-26 2019-09-03 Ecolab Usa Inc. Highly homogenous zeolite precursors
US10773967B2 (en) 2015-10-26 2020-09-15 Ecolab Usa Inc. Highly homogenous zeolite precursors
US10934173B2 (en) 2015-10-26 2021-03-02 Ecolab Usa Inc. Highly homogenous zeolite precursors
US10654724B2 (en) 2016-12-02 2020-05-19 Ecolab Usa Inc. Polyaluminum salts and their uses in preparation of high-purity colloidal aluminum-silica composite particles and zeolites
WO2018111390A1 (en) 2016-12-13 2018-06-21 Chevron U.S.A. Inc. Synthesis of molecular sieve ssz-41
US10377014B2 (en) 2017-02-28 2019-08-13 Ecolab Usa Inc. Increased wetting of colloidal silica as a polishing slurry
US11384023B2 (en) 2017-09-26 2022-07-12 Delta Faucet Company Aqueous gelcasting formulation for ceramic products
US11851376B2 (en) 2017-09-26 2023-12-26 Delta Faucet Company Aqueous gelcasting method for ceramic products

Also Published As

Publication number Publication date
TW200539935A (en) 2005-12-16
CA2560748C (en) 2013-06-18
JP5103168B2 (ja) 2012-12-19
TWI377980B (en) 2012-12-01
KR20070027535A (ko) 2007-03-09
US10730756B2 (en) 2020-08-04
EP1744825A2 (en) 2007-01-24
WO2005104683A2 (en) 2005-11-10
CN1942237B (zh) 2011-07-06
BRPI0509859A (pt) 2007-10-09
CN101912755A (zh) 2010-12-15
CA2560748A1 (en) 2005-11-10
CN101912755B (zh) 2012-07-04
WO2005104683A3 (en) 2006-11-30
BRPI0509859B1 (pt) 2019-04-24
CN1942237A (zh) 2007-04-04
EP1744825B1 (en) 2019-02-27
JP2007532470A (ja) 2007-11-15
US20180141822A1 (en) 2018-05-24
SG152248A1 (en) 2009-05-29
EP1744825A4 (en) 2011-09-07

Similar Documents

Publication Publication Date Title
US10730756B2 (en) Colloidal compositions and methods of preparing same
US8658127B2 (en) Method of manufacturing mesoporous zeolite agglomerates
JP4919948B2 (ja) ヘテロ構造非zsm−48シーディングによるzsm−48結晶の合成
US8003707B2 (en) Metal-rich siliceous compositions and methods of producing same
JP5334385B2 (ja) ポリシリケート粒子状材料の製造および使用
US20020090337A1 (en) Synthesis of zeolites
JP3587315B2 (ja) メソポーラスシリカおよびその製造方法
WO2007021402A2 (en) Silica sols with controlled minimum particle size and preparation thereof
CN1092142C (zh) 沸石及其制备方法
JP3577681B2 (ja) メソポーラスメタロシリケートの製造方法
KR102656777B1 (ko) 층상 규산염의 제조 방법, 및 실리카 나노 시트의 제조 등에 있어서의 그 응용
JP3828571B2 (ja) ミクロ粒子
EP0753482A1 (en) Zeolites and processes for their manufacture
MXPA06009055A (en) Synthesis of zsm-48 crystals with heterostructural, non zsm-48, seeding

Legal Events

Date Code Title Description
AS Assignment

Owner name: NALCO COMPANY, ILLINOIS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HOLLAND, BRIAN T.;BATLLO, FRANCOIS;ORTIZ, CARMEN Y.;AND OTHERS;REEL/FRAME:015674/0956

Effective date: 20040802

AS Assignment

Owner name: BANK OF AMERICA, N.A., AS COLLATERAL AGENT, NEW YO

Free format text: SECURITY AGREEMENT;ASSIGNORS:NALCO COMPANY;CALGON LLC;NALCO ONE SOURCE LLC;AND OTHERS;REEL/FRAME:022703/0001

Effective date: 20090513

Owner name: BANK OF AMERICA, N.A., AS COLLATERAL AGENT,NEW YOR

Free format text: SECURITY AGREEMENT;ASSIGNORS:NALCO COMPANY;CALGON LLC;NALCO ONE SOURCE LLC;AND OTHERS;REEL/FRAME:022703/0001

Effective date: 20090513

AS Assignment

Owner name: NALCO COMPANY, ILLINOIS

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:035771/0668

Effective date: 20111201

AS Assignment

Owner name: NALCO COMPANY, ILLINOIS

Free format text: RELEASE BY SECURED PARTY;ASSIGNOR:BANK OF AMERICA, N.A.;REEL/FRAME:041808/0713

Effective date: 20111201

AS Assignment

Owner name: ECOLAB USA INC., MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:NALCO COMPANY LLC;CALGON CORPORATION;CALGON LLC;AND OTHERS;REEL/FRAME:041836/0437

Effective date: 20170227

Owner name: NALCO COMPANY LLC, DELAWARE

Free format text: CHANGE OF NAME;ASSIGNOR:NALCO COMPANY;REEL/FRAME:041835/0903

Effective date: 20151229

AS Assignment

Owner name: ECOLAB USA INC., MINNESOTA

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:NALCO COMPANY;REEL/FRAME:042147/0420

Effective date: 20170227

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION