US20050208372A1 - Separator for a battery having a zinc electrode - Google Patents
Separator for a battery having a zinc electrode Download PDFInfo
- Publication number
- US20050208372A1 US20050208372A1 US10/803,710 US80371004A US2005208372A1 US 20050208372 A1 US20050208372 A1 US 20050208372A1 US 80371004 A US80371004 A US 80371004A US 2005208372 A1 US2005208372 A1 US 2005208372A1
- Authority
- US
- United States
- Prior art keywords
- separator
- surfactant
- days
- less
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/24—Electrodes for alkaline accumulators
- H01M4/244—Zinc electrodes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M4/00—Electrodes
- H01M4/02—Electrodes composed of, or comprising, active material
- H01M4/24—Electrodes for alkaline accumulators
- H01M4/32—Nickel oxide or hydroxide electrodes
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/411—Organic material
- H01M50/429—Natural polymers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/409—Separators, membranes or diaphragms characterised by the material
- H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
- H01M50/457—Separators, membranes or diaphragms characterised by the material having a layered structure comprising three or more layers
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/463—Separators, membranes or diaphragms characterised by their shape
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
- H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
- H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
- H01M50/491—Porosity
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/24—Alkaline accumulators
- H01M10/30—Nickel accumulators
-
- H—ELECTRICITY
- H01—ELECTRIC ELEMENTS
- H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- H01M10/00—Secondary cells; Manufacture thereof
- H01M10/36—Accumulators not provided for in groups H01M10/05-H01M10/34
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
- Y02E60/10—Energy storage using batteries
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
- Y02P70/50—Manufacturing or production processes characterised by the final manufactured product
Definitions
- the instant invention relates to a separator for a battery having a zinc electrode.
- Batteries having zinc electrodes are known. See U.S. Pat. Nos. 4,359,510; 4,438,185; and 4,544,616; Tuck, C. D. S., Editor, Modern Battery Technology, Ellis Horwood Limited, Chichester, England (1991); and Linden, D., Editor, Handbook of Batteries, Second Edition, McGraw-Hill, Inc., New York, N.Y. (1995), each of which is incorporated herein by reference.
- One such battery is the nickel-zinc (NiZn) battery (or cell).
- the nickel-zinc (zinc/nickel oxide) battery system includes a zinc electrode, a nickel electrode, an electrolyte, and a separator.
- the zinc/nickel oxide battery system uses zinc as the negative active material and nickel oxide as the positive, and the electrolyte is an alkaline potassium hydroxide solution.
- NiZn cells are well known, they have never reached a significant commercial success; apparently, because of the limited effective cycle life of such batteries.
- Besenhard J., Editor, Handbook of Battery Materials, Wiley-VCH, New York, N.Y. (1999).
- the reason for this limited cycle life is the high solubility of the zinc hydroxide in alkaline electrolyte; the zincate ions formed are deposited again during the subsequent charging in the form of dendrites, i.e. fernlike crystals.
- dendrites i.e. fernlike crystals.
- a short term remedy can be achieved by a decrease in zinc solubility in the electrolyte or by suppression of dendrite formation; cadmium-, lead-, or bismuth oxide, as well as calcium hydroxide or aluminum hydroxide have been added to the zinc electrode or the electrolyte to suppress dendrite formation. See Besenhard, Ibid. However, this remedy does not have long-lasting effectiveness. See Besenhard, Ibid.
- microporous films could be used to overcome the problems associated with the use of zinc electrodes. See Tuck, Ibid., Linden, Ibid., and U.S. Pat. Nos. 4,359,510; 4,438,185; and 4,544,616.
- Celgard® 3406 One commercially available microporous membrane for use in batteries having zinc electrodes is Celgard® 3406 microporous membrane. See: U.S. Pat. Nos. 4,359,510 and 4,438,185.
- Celgard® 3406 is a microporous membrane having a polymer coating on one surface.
- the microporous membrane is commercially available as Celgard® 2400 microporous membrane, a polypropylene microporous membrane having an average pore size of about 0.045 microns.
- the polymer coating consists of cellulose acetate and a surfactant commercially available as VICTAWET® 12 wetting agent.
- VICTAWET® 12 an oxirane polymer with 2-ethylhexyl dihydrogen phosphate, is commercially available from Akzo Chemicals, Inc., Chicago, Ill. While Celgard 3406 performs adequately, it has a limited shelf life (about 9 months from the coating date) and it wets only once (i.e., the surfactant readily washes off).
- Celgard® 3407 coated microporous membrane Another commercially available microporous membrane for use in batteries having zinc electrodes is Celgard® 3407 coated microporous membrane. See: U.S. Pat. No. 6,479,190.
- Celgard® 3407 which is commercially available from Celgard, Inc. of Charlotte, N.C., comprises a microporous membrane having a coating on at least one surface of the membrane.
- Celgard® 3407 microporous membrane having an average pore size of about 0.045 microns, is typically a hydrophobic, polyolefinic polymer.
- the coating consists of cellulose acetate and a surfactant, which has an active ingredient selected from the group consisting of organic ethers.
- the surfactant is commercially available as IGEPAL CO-530 from Rhone-Poulenc of Cranbury, N.J.
- Celgard® 3407 has furnished design improvements to overcome the limited cycle life performance of the nickel-zinc batteries, Celgard® 3407 has an electrical resistance of less than 20 milliohms-inch 2 , and it may take up to 100 seconds to wet in aqueous electrolytes after 12 months of storage.
- the instant invention is a separator for a battery having a zinc electrode.
- the battery separator according to the instant invention includes a microporous membrane, and a coating on at least one surface of the microporous membrane.
- the coating includes a mixture of 25-40 weight % polymer and 60-75 weight % surfactant combination.
- the polymer is cellulose acetate, and the surfactant combination includes a first surfactant and a second surfactant.
- the first surfactant preferably, has an active ingredient selected from the group consisting of organic ethers
- the second surfactant is, preferably, an oxirane polymer with 2-ethylhexyl dihydrogen phosphate.
- the instant invention is directed to a separator for a battery having a zinc electrode.
- Those batteries are typically secondary (i.e., rechargeable) batteries.
- Such batteries may be nickel-zinc or silver-zinc batteries.
- the battery discussed in detail will be a nickel-zinc (zinc/nickel oxide) battery. The invention, however, is not so limited.
- the zinc/nickel oxide battery system typically, includes a zinc electrode, a nickel electrode, an electrolyte, and a separator. Typically, the electrodes sandwich the separator, and the electrolyte communicates with the two electrodes via the separator.
- the zinc electrode is the anode or the negative electrode.
- the anode is the reducing or fuel electrode; thus, the zinc electrode gives up electrons to the external circuit and becomes oxidized during an electrochemical reaction.
- Zinc electrodes may be made from metallic zinc. Typically, zinc electrodes are designed to be 60-70% porous in their all-metallic state.
- the nickel electrode is the cathode or the positive electrode.
- the cathode is the oxidizing electrode; thus, the nickel electrode accepts electrons from the external circuit and becomes reduced during an electrochemical reaction.
- the nickel electrode is, typically, made from nickel oxide.
- the electrolyte is, typically, an ionic conductor, which provides the medium for transfer of electrons, as ions, inside a cell between the anode and the cathode.
- the electrolyte is typically a liquid, such as water or other solvent, with dissolved salts, acids, or alkalis to impart ionic conductivity.
- the electrolyte may be a solid electrolyte, which is an ionic conductor at the operating temperature of the cell.
- An example of electrolyte in zinc/nickel oxide battery system includes, but is not limited to, an aqueous potassium hydroxide (KOH) solution, where the potassium hydroxide concentration ranges from about 20 to 45 percent by weight.
- KOH potassium hydroxide
- the separator according to instant invention comprises a microporous membrane, and a coating on at least one surface of the membrane.
- the microporous membrane is typically a hydrophobic, polyolefinic polymer.
- the hydrophobic, polyolefinic polymers include, for example, polyethylene and polypropylene, the latter is preferred.
- the method of manufacturing the membrane is not critical, and may include, for example, the “dry” stretch (or Celgard) process or the “solvent” stretch (or phase inversion) process.
- Such membranes may have a thicknesses less than 3 mils (about 75 microns), preferably less than 1.5 mils (38 microns), and most preferably a thickness of about 1 mil (25 microns).
- the membrane may have an average pore size of about 0.045 ⁇ 0.002 micron, a porosity of 28-40%, and a Gurley of 20-45 sec/inch 2 .
- Such membranes are commercially available from, for example, Celgard Inc., Charlotte, N.C., U.S.A.; Tonen K.K., Tokyo, Japan; Asahi Chemical Co., Tokyo, Japan; Ube Industries, Tokyo, Japan; and Nitto Denko Corporation, Tokyo, Japan.
- the coating comprises a polymer and a surfactant combination.
- the coating is applied to at least one surface of a microporous membrane.
- the coating is applied to both surfaces of a microporous membrane.
- the coating may have surface density in the range of about 0.30 to 0.43 mg/cm 2 , and preferably, the coating may have a surface density in the range of 0.31 to 0.38 mg/cm 2 .
- the coating is preferably applied in solution and the solvent (e.g., acetone or methylethyl ketone) is driven off in any known manner.
- the polymer may be selected from the group consisting of cellulose acetate.
- the optimum amount of cellulose acetate is an amount which is sufficient to coat both surfaces of a microporous membrane creating the sieve effect (i.e. ability to selectively pass/reject molecules based upon size) when wetted; however, too much cellulose acetate will block the pores of the microporous membrane, and it will increase its electrical resistance.
- the cellulose acetate may have a surface density in the range of about 0.10 to 0.13 mg/cm 2 .
- Cellulose acetate (which has about 2.5 acetyl groups per glucose, e.g.
- CA-398-3) is a commercially available material from, for example, Celanese Acetate LLC of Charlotte, N.C., U.S.A.; or Eastman Chemical Co. of Kingsport, Tenn., U.S.A.
- Celanese cellulose acetate HB-105 is preferred.
- the surfactant combination comprises a first surfactant and a second surfactant.
- the optimum amount of surfactant combination is a sufficient amount thereof to wet in aqueous electrolyte in a short period of time; however, too much surfactant combination will block the pores of the microporous membrane, and it will increase its electrical resistance.
- the surfactant combination may have a surface density in the range of 0.20 to 0.30 mg/cm 2 , and preferably, the surfactant combination may have a surface density of 0.25 mg/cm 2 .
- First surfactant and second surfactant, with respect to each other, may have any weight ratios.
- first surfactant and second surfactant have a weight ratio of 1:3 or 3:1, respectively, and most preferably, first surfactant and second surfactant have a weight ratio of 1:1.
- first surfactant three considerations help define the selection criteria, those considerations are: 1) first surfactant must be inert to the electrolyte (e.g. non-hydrolyzable in the electrolyte); 2) first surfactant should not be soluble or readily soluble in the electrolyte; and 3) first surfactant should be adherent to the membrane.
- second surfactant two considerations help define the selection criteria, those considerations are: 1) second surfactant must be inert to the electrolyte (e.g. non-hydrolyzable in the electrolyte); 2) second surfactant must increase the wetting speed and stability of the membrane without interfering with long term membrane storage life.
- First surfactant may have an active ingredient selected from the group consisting of organic ethers.
- organic ether is nonylphenoxypoly (ethyleneoxy) ethanol.
- One such surfactant is commercially available under the tradename IGEPAL CO-530 from Rhone-Poulenc of Cranbury, N.J., U.S.A.
- the first surfactant may have a surface density in the range of 0.10 to 0.20 mg/cm 2 .
- the first surfactant may have a surface density in the range of 0.10 to 0.15 mg/cm 2 , and most preferably, the first surfactant may have a surface density of 0.125 mg/cm 2 .
- Second surfactant may be an oxirane polymer with 2-ethylhexyl dihydrogen phosphate.
- VICTAWET® 12 wetting agent VICTAWET® 12 is commercially available from Akzo Chemicals, Inc., Chicago, Ill.
- the second surfactant may have a surface density in the range of 0.10 to 0.20 mg/cm 2 .
- the second surfactant may have a surface density in the range of 0.10 to 0.15 mg/cm 2 , and most preferably, the second surfactant may have a surface density of 0.125 mg/cm 2 .
- the freshly coated separator according to instant invention may have any electrical resistance.
- the freshly coated separator according to instant invention has an electrical resistance of less than 10.4 milliohms-inch 2 , and most preferably, an electrical resistance in the range of about 9.9 to 10.4 milliohms-inch 2 .
- the coated separator according to instant invention, stored for a period not less than 22 days and not exceeding 256 days at 70° C. may have any electrical resistance.
- the coated separator according to instant invention stored for a period not less than 22 days and not exceeding 256 days at 70° C., has an electrical resistance of less than 10 milliohms-inch 2 , and most preferably, an electrical resistance in the range of about 7.7 to 10 milliohms-inch 2 Electrical resistance (“ER”) of a microporous film as defined herein and employed in the claims is determined by soaking a sample thereof having a known surface area (e.g., 1.0 sq. inches) in about a 30% by weight, solution of KOH in water for 24 hours.
- ER Electrical resistance
- the resulting sample is then disposed between working platinum electrodes (i.e., anode and a cathode) immersed in an electrolyte of a 30%, by weight, solution of KOH in water and a direct current of known amperage (e.g., 40 milliamperes) is passed through the cell between the electrodes.
- a direct current of known amperage e.g. 40 milliamperes
- the potential drop across the film (E′) is measured with an electrometer.
- the potential drop across the cell without the microporous film disposed therein (E) is also determined using the same current. E is measured in millivolts.
- the coated separator may have a thickness of less than 3 mils (75 microns), and preferably, a thickness of less than or equal to 1.5 mils.
- the freshly coated separator according to instant invention may be capable of wetting in less than 8 seconds. Furthermore, the coated separator according to instant invention, stored for a period not less than 22 days and not exceeding 256 days at 70° C., is capable of wetting in one second, and preferably, it is capable of wetting almost instantaneously.
- the effective average pore size of the coated separator should be less than 0.045 micron, preferably in the range of about 0.030 to 0.040 micron, and most preferably less than 0.035 micron.
- An effective average pore size which is too large will adversely impact cycle life because too many zincate ions will pass through the separator, and if too low, it will adversely impact conductivity within the cell because electrical resistance will be too great.
- the effective average pore size refers to the apparent pore size exhibited by the coated membrane when wet out by the electrolyte. Effective average pore size is measured by solute passage method. See for example: Cheryan, M., Ultrafiltration Handbook , Technomic Publishing Co., Lancaster, Pa., (1986) p. 62-71.
- the pore size of a membrane was estimated to be 0.035 micron (35 nm) by the foregoing method using: myoglobulin-17,600 molecular weight (MW), 3.7 nanometers (nm) size, 0% rejection; lactoglobulin-38,000 MW, 5.2 nm, 10%; albumin-69,000 MW, 6.4 nm, 30%; serum globulin-148,000 MW, 9.2 nm, 75%; haemocyanine (Palinurus)-450,000 MW, 11.7 nm, 90%.
- MW molecular weight
- nm nanometers
- the separator made according to instant invention was compared to the commercially available products, i.e. Celgard® 3407 microporous membrane and Celgard® 3406 microporous membrane at 70° C.
- the comparative analysis included six separator samples.
- Coating solution of sample 2 as shown in Table I included, on a weight of a solvent basis, 1.75% cellulose acetate, 3.5% IGEPAL CO-530, and 0.5% VICTAWET-12.
- Coating solution of sample 6 (3406 control), as shown in Table I, included, on a weight of a solvent basis, 1.75% cellulose acetate, 0% IGEPAL CO-530, and 7% VICTAWET-12.
- Table II shows the electrical resistance (“ER”), measured in milliohms-inch 2 , of the abovementioned samples after 0 days, 22 days, 48 days, 104 days, 122 days, and 256 days of storage at 70° C.
- Table III shows the wettability (“W”), measured in seconds, of the abovementioned samples after 0 days, 22 days, 48 days, 104 days, 122 days, and 256 days of storage at 70° C.
Landscapes
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Electrochemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Manufacturing & Machinery (AREA)
- Cell Separators (AREA)
- Secondary Cells (AREA)
Priority Applications (9)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/803,710 US20050208372A1 (en) | 2004-03-18 | 2004-03-18 | Separator for a battery having a zinc electrode |
TW094105652A TWI279939B (en) | 2004-03-18 | 2005-02-24 | Separator for a battery having a zinc electrode |
CA002498597A CA2498597A1 (en) | 2004-03-18 | 2005-02-25 | Separator for a battery having a zinc electrode |
SG200501567A SG115759A1 (en) | 2004-03-18 | 2005-03-14 | Separator for a battery having a zinc electrode |
KR1020050021676A KR100676558B1 (ko) | 2004-03-18 | 2005-03-16 | 아연 전극을 갖는 전지를 위한 격리판 |
CNB2005100548356A CN1314143C (zh) | 2004-03-18 | 2005-03-17 | 具有锌电极的电池用隔膜 |
EP05005910A EP1577968A2 (en) | 2004-03-18 | 2005-03-18 | Separator for a battery having a zinc electrode |
JP2005078697A JP4446069B2 (ja) | 2004-03-18 | 2005-03-18 | 亜鉛電極を有する電池のためのセパレーター |
US12/834,922 US7981549B2 (en) | 2004-03-18 | 2010-07-13 | Separator for a battery having a zinc electrode |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/803,710 US20050208372A1 (en) | 2004-03-18 | 2004-03-18 | Separator for a battery having a zinc electrode |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/834,922 Continuation US7981549B2 (en) | 2004-03-18 | 2010-07-13 | Separator for a battery having a zinc electrode |
Publications (1)
Publication Number | Publication Date |
---|---|
US20050208372A1 true US20050208372A1 (en) | 2005-09-22 |
Family
ID=34838926
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/803,710 Abandoned US20050208372A1 (en) | 2004-03-18 | 2004-03-18 | Separator for a battery having a zinc electrode |
US12/834,922 Expired - Lifetime US7981549B2 (en) | 2004-03-18 | 2010-07-13 | Separator for a battery having a zinc electrode |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/834,922 Expired - Lifetime US7981549B2 (en) | 2004-03-18 | 2010-07-13 | Separator for a battery having a zinc electrode |
Country Status (8)
Country | Link |
---|---|
US (2) | US20050208372A1 (ja) |
EP (1) | EP1577968A2 (ja) |
JP (1) | JP4446069B2 (ja) |
KR (1) | KR100676558B1 (ja) |
CN (1) | CN1314143C (ja) |
CA (1) | CA2498597A1 (ja) |
SG (1) | SG115759A1 (ja) |
TW (1) | TWI279939B (ja) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2472641A1 (en) | 2010-12-31 | 2012-07-04 | Fuyuan Ma | Nickel-zinc battery and manufacturing method thereof |
US8404396B2 (en) | 2007-05-14 | 2013-03-26 | Brigham Young University | Fuel cell and method for generating electric power |
CN110364660A (zh) * | 2018-04-10 | 2019-10-22 | 中国科学院上海硅酸盐研究所 | 一种水系锌离子电池复合隔膜及制备方法 |
US10651445B2 (en) | 2017-01-23 | 2020-05-12 | ZAF Energy Systems, Incorporated | Electrode with cellulose acetate separator system |
WO2021207083A1 (en) * | 2020-04-06 | 2021-10-14 | Daramic, Llc | Surfactant coated separator |
US11502374B2 (en) * | 2016-04-08 | 2022-11-15 | Daramic, Llc | Separators for enhanced flooded batteries, batteries, and related methods |
Families Citing this family (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP5942113B2 (ja) * | 2011-09-26 | 2016-06-29 | 旭化成株式会社 | 微多孔膜 |
KR101672609B1 (ko) | 2012-01-19 | 2016-11-03 | 나이키 이노베이트 씨.브이. | 에너지 소비 |
JP2013203894A (ja) * | 2012-03-28 | 2013-10-07 | Asahi Kasei E-Materials Corp | ポリオレフィン微多孔膜 |
EP3166171B1 (de) * | 2015-11-05 | 2020-02-26 | VARTA Microbattery GmbH | Elektrochemische zelle |
WO2017142522A1 (en) * | 2016-02-17 | 2017-08-24 | Daramic, Llc | Improved battery separators which reduce water loss in lead acid batteries and improved lead acid batteries including such improved battery separators |
CN106129305B (zh) * | 2016-08-05 | 2018-11-06 | 大连理工大学 | 一种用于镍锌电池的微孔膜及其制备方法 |
WO2018136337A2 (en) * | 2017-01-18 | 2018-07-26 | Aqua Metals Inc. | Pretreatment of diaphragms used in electrochemical processes |
US11404747B1 (en) * | 2022-02-18 | 2022-08-02 | ZAF Energy Systems, Incorporated | Ceria coatings and structures for zinc-based battery separators |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3811957A (en) * | 1969-07-22 | 1974-05-21 | Exxon Research Engineering Co | Battery separators made from polymeric fibers |
US4298666A (en) * | 1980-02-27 | 1981-11-03 | Celanese Corporation | Coated open-celled microporous membranes |
US4359510A (en) * | 1980-07-31 | 1982-11-16 | Celanese Corporation | Hydrophilic polymer coated microporous membranes capable of use as a battery separator |
US4438185A (en) * | 1980-07-31 | 1984-03-20 | Celanese Corporation | Hydrophilic polymer coated microporous membranes capable of use as a battery separator |
US4544616A (en) * | 1984-02-16 | 1985-10-01 | The United States Of America As Represented By The United States Department Of Energy | Secondary battery containing zinc electrode with modified separator and method |
US6479190B1 (en) * | 2000-09-21 | 2002-11-12 | Celgard Inc. | Separator for battery having zinc electrode |
Family Cites Families (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4298668A (en) * | 1980-07-03 | 1981-11-03 | Kimberly-Clark Corporation | Alkaline battery, electrolyte absorber therefor |
US4501793A (en) | 1983-06-17 | 1985-02-26 | Celanese Corporation | Surfactant treated polyolefinic microporous materials capable of multiple re-wetting with aqueous solutions |
-
2004
- 2004-03-18 US US10/803,710 patent/US20050208372A1/en not_active Abandoned
-
2005
- 2005-02-24 TW TW094105652A patent/TWI279939B/zh not_active IP Right Cessation
- 2005-02-25 CA CA002498597A patent/CA2498597A1/en not_active Abandoned
- 2005-03-14 SG SG200501567A patent/SG115759A1/en unknown
- 2005-03-16 KR KR1020050021676A patent/KR100676558B1/ko not_active IP Right Cessation
- 2005-03-17 CN CNB2005100548356A patent/CN1314143C/zh not_active Expired - Fee Related
- 2005-03-18 JP JP2005078697A patent/JP4446069B2/ja not_active Expired - Fee Related
- 2005-03-18 EP EP05005910A patent/EP1577968A2/en not_active Withdrawn
-
2010
- 2010-07-13 US US12/834,922 patent/US7981549B2/en not_active Expired - Lifetime
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3811957A (en) * | 1969-07-22 | 1974-05-21 | Exxon Research Engineering Co | Battery separators made from polymeric fibers |
US4298666A (en) * | 1980-02-27 | 1981-11-03 | Celanese Corporation | Coated open-celled microporous membranes |
US4359510A (en) * | 1980-07-31 | 1982-11-16 | Celanese Corporation | Hydrophilic polymer coated microporous membranes capable of use as a battery separator |
US4438185A (en) * | 1980-07-31 | 1984-03-20 | Celanese Corporation | Hydrophilic polymer coated microporous membranes capable of use as a battery separator |
US4544616A (en) * | 1984-02-16 | 1985-10-01 | The United States Of America As Represented By The United States Department Of Energy | Secondary battery containing zinc electrode with modified separator and method |
US6479190B1 (en) * | 2000-09-21 | 2002-11-12 | Celgard Inc. | Separator for battery having zinc electrode |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8404396B2 (en) | 2007-05-14 | 2013-03-26 | Brigham Young University | Fuel cell and method for generating electric power |
EP2472641A1 (en) | 2010-12-31 | 2012-07-04 | Fuyuan Ma | Nickel-zinc battery and manufacturing method thereof |
US11502374B2 (en) * | 2016-04-08 | 2022-11-15 | Daramic, Llc | Separators for enhanced flooded batteries, batteries, and related methods |
US10651445B2 (en) | 2017-01-23 | 2020-05-12 | ZAF Energy Systems, Incorporated | Electrode with cellulose acetate separator system |
CN110364660A (zh) * | 2018-04-10 | 2019-10-22 | 中国科学院上海硅酸盐研究所 | 一种水系锌离子电池复合隔膜及制备方法 |
WO2021207083A1 (en) * | 2020-04-06 | 2021-10-14 | Daramic, Llc | Surfactant coated separator |
Also Published As
Publication number | Publication date |
---|---|
US7981549B2 (en) | 2011-07-19 |
CN1670988A (zh) | 2005-09-21 |
EP1577968A2 (en) | 2005-09-21 |
TW200603465A (en) | 2006-01-16 |
CA2498597A1 (en) | 2005-09-18 |
KR100676558B1 (ko) | 2007-01-30 |
US20100279167A1 (en) | 2010-11-04 |
SG115759A1 (en) | 2005-10-28 |
CN1314143C (zh) | 2007-05-02 |
JP2005268225A (ja) | 2005-09-29 |
TWI279939B (en) | 2007-04-21 |
KR20060043678A (ko) | 2006-05-15 |
JP4446069B2 (ja) | 2010-04-07 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7981549B2 (en) | Separator for a battery having a zinc electrode | |
JP4618831B2 (ja) | 親水性ポリオレフィン | |
US7642012B2 (en) | Polymer separator for a lithium battery | |
EP2372813A1 (en) | Batteries Including Improved Fine Fiber Separators | |
WO2008154022A1 (en) | Batteries with permanently wet-able fine fiber separators | |
US6479190B1 (en) | Separator for battery having zinc electrode | |
WO2017098732A1 (ja) | 電解質膜及びその製造方法、並びに電解質膜を備えた燃料電池用の膜-電極接合体 | |
CN112803117A (zh) | 一种亲水性隔膜及含有该亲水性隔膜的电池 | |
JPH08273653A (ja) | アルカリ電池用セパレーター及びアルカリ電池 | |
JP2981238B2 (ja) | 電池用セパレーター | |
JP2764378B2 (ja) | ニッケル−水素吸蔵合金蓄電池 | |
KR100264774B1 (ko) | 알카리 아연 축전지 | |
CN117438741A (zh) | 一种基于无机氧化物的疏水性锌离子电池隔膜及其在锌电池中的应用 | |
JPH0773863A (ja) | アルカリ電池用セパレータ | |
JPH02216757A (ja) | アルカリ亜鉛蓄電池 | |
JPS62249367A (ja) | 水素電池 | |
JP3114082B2 (ja) | アルカリ電池用セパレータおよびこれを用いたアルカリ蓄電池 | |
JP2021192361A (ja) | 二次電池用負極および二次電池 | |
JPH1154102A (ja) | 一次電池用セパレーター | |
JPH02155159A (ja) | アルカリ亜鉛蓄電池 | |
JPS58165243A (ja) | ニツケル亜鉛電池 | |
JP2000082454A (ja) | 二次電池用セパレータ | |
JPH09283108A (ja) | アルカリ蓄電池 | |
JP2001135296A (ja) | 電池用セパレータおよびこれを用いたニッケル・水素蓄電池 | |
JPS62122056A (ja) | ボタン形空気電池 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CELGARD INC., NORTH CAROLINA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:WATSON, JILL V.;WENSLEY, C. GLEN;REEL/FRAME:015558/0188;SIGNING DATES FROM 20040609 TO 20040617 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION |