US20040244884A1 - Ferritic stainless steel sheet excellent in press formability and secondary formability and its manufacturing method - Google Patents

Ferritic stainless steel sheet excellent in press formability and secondary formability and its manufacturing method Download PDF

Info

Publication number
US20040244884A1
US20040244884A1 US10/860,349 US86034904A US2004244884A1 US 20040244884 A1 US20040244884 A1 US 20040244884A1 US 86034904 A US86034904 A US 86034904A US 2004244884 A1 US2004244884 A1 US 2004244884A1
Authority
US
United States
Prior art keywords
mass
less
steel sheet
annealing
formability
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US10/860,349
Other languages
English (en)
Inventor
Yasutoshi Hideshima
Kouki Tomimura
Naoto Hiramatsu
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Nisshin Co Ltd
Original Assignee
Nisshin Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nisshin Steel Co Ltd filed Critical Nisshin Steel Co Ltd
Assigned to NISSHIN STEEL CO., LTD. reassignment NISSHIN STEEL CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HIDESHIMA, YASUTOSHI, HIRAMATSU, NAOTO, TOMIMURA, KOUKI
Publication of US20040244884A1 publication Critical patent/US20040244884A1/en
Priority to US12/396,966 priority Critical patent/US20090165905A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0405—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0468—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment between cold rolling steps
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0463—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing

Definitions

  • the present invention relates to a ferritic stainless steel sheet, which can be press-formed to a predetermined profile without defects such as poor circularity and torsion and then secondary-formed to a final profile with good hot-extruding, and also relates to a method of manufacturing thereof.
  • Ferritic stainless steels represented by SUS430 or SUS430LX, have been used so far in various fields, e.g. durable consumers' goods, due to good corrosion-resistance and cheapness compared with austenitic stainless steels, which contain Ni as an expensive element.
  • Conditions for press-forming a ferritic stainless steel sheet to a product profile become severe and severe as development of its application.
  • a press-formed steel sheet is often secondarily formed for extrusion of a hole, for instance.
  • there is a strong demand for provision of a new ferritic stainless steel sheet which is fairly excellent in formability compared with conventional ferritic stainless steel sheets and so formed to a product profile without defects even under severe conditions.
  • Shape-freezability and secondary formability of a primary-formed steel sheet which will be formed to a final profile, are also important factors as well as to Lankford value (r) and anti-ridging property.
  • a ferritic stainless steel sheet is generally inferior in formability to an austenitic stainless steel sheet. Especially, it significantly reduces thickness in a primary-formed state, and thickness reduction is anisotropic. Consequently, dimensional accuracy such as circularity becomes worse as severer forming conditions, when the ferritic stainless steel sheet is press-formed to a cylindrical profile. Thickness deviation in the primary-formed state leads to serious degradation of secondary formability such as hole-extruding.
  • the present invention aims at provision of a ferritic stainless steel sheet improved in dimensional accuracy and secondary formability in a press-formed state by controlling particle size and distribution of precipitates, which are dispersed in a steel matrix.
  • the present invention proposes a new ferritic stainless steel sheet, which consists of 0.02 mass % or less of C, 0.8 mass % or less of Si, 1.5 mass % or less of Mn, 0.050 mass % or less of P, 0.01 mass % or less of S, 8.0-35.0 mass % of Cr, 0.05 mass % or less of N, 0.05-0.40 mass % of Ti, 0.10-0.50 mass % of Nb, optionally one or more selected from the group consisting of 0.5 mass % or less of Ni, 3.0 mass % or less of Mo, 2.0 mass % or less of Cu, 0.3 mass % or less of V, 0.3 mass % or less of Zr, 0.3 mass % or less of Al and 0.0100 mass % or less of B, and the balance being Fe except inevitable impurities with a product of (% Ti ⁇ % N) less than 0.005. Its metallurgical structure is defined by distribution of precipitates of 0.15 ⁇ m or more in particle size except TiN
  • the ferritic stainless steel sheet is manufactured as follows:
  • a molten steel with a predetermined composition is cast to a slab.
  • the slab is hot-rolled to a steel sheet at a finish-temperature of 800° C. or lower and annealed at 450-1080° C.
  • the annealed hot-rolled steel sheet is pickled and cold-rolled in accompaniment with at least one intermediate-annealing within a temperature range of from (a recrystallization-finishing temperature—100° C.) to (a recrystallization-finishing temperature).
  • the cold-rolled steel sheet is finally subjected to finish-annealing at a temperature of 1080° C. or lower.
  • the hot-rolled steel sheet may be box-annealed for a predetermined time period of one hour or shorter.
  • the inter-mediate annealing and the finish-annealing may be performed in a continuous annealing furnace for one minute or shorter.
  • FIG. 1 is a view for explaining circularity of a steel sheet, which is cylindrically formed by a multiplaten press.
  • the inventors have researched and examined on manufacturing conditions of ferritic stainless steel sheets for improvement of dimensional accuracy (e.g. circularity, straightness and torsion) from various aspects, and discovered that circularity and secondary formability of a press-formed steel sheet are fairly affected by shape and distribution of TiN and other precipitates in an annealed state.
  • the inventors presume on the basis of the discovery that objective properties are imparted to a ferritic stainless steel sheet by properly controlling shape and distribution of the precipitates.
  • Formation of the precipitates to the shape and distribution suitable for the purpose is realized by adding both of Ti and Nb to a ferritic stainless steel at a value more than a stoichiometric ratio for stabilization of C and N as carbonitrides and subjecting the ferritic stainless steel to optimum thermo-mechanical treatment.
  • C and N in a ferritic stainless steel are mostly precipitated as carbonitrides by addition of Ti and Nb.
  • the precipitated carbonitrides except TiN are substantially reformed to very fine particles in the manufacturing process of from annealing a hot-rolled steel sheet through cold-rolling to finish-annealing.
  • the fine particles allow predominant growth of recrystallized grains with a certain orientation without pinning action, when the manufactured steel sheet is annealed for recrystallization, resulting in formation of an anisotropic grain-mixed structure.
  • the anisotropy causes concentration of strains along a certain direction during primary-forming a steel sheet and so worsens press formability and dimensional accuracy of the steel sheet.
  • the pinning action during recrystallization annealing is expected by distribution of precipitates having a particle size bigger than a certain value.
  • the pinning action suppresses orientative grain growth or growth to coarse grains, so as to improve isotropy and dimensional accuracy of a press-formed steel sheet.
  • the effects of the pinning action on press formability and dimensional accuracy are typically noted by distribution of precipitates of 0.15 ⁇ m or more in particle size except TiN at a rate of 5000-50000/mm 2 , as recognized in the later examples.
  • TiN is disadvantageous for press formability and dimensional accuracy.
  • a steel sheet which has a product of (%Ti X%N) above 0.005
  • Coarse TiN particles which have grown to a cubic shape, are observed at starting points of cracks. The observation result means that strains concentrate at cubic apexes during press-forming and induce micro-cracks. Concentration of strains and formation of micro-cracks around the TiN particles are also unfavorable for hole-extruding in a secondary-forming step.
  • the inventive ferritic stainless steel sheet contains alloying components at predetermined ratios, as follows:
  • C is converted to carbides effective for random growth of recrystallized ferritic grains in a finish-annealing step, but degrades formability of a steel sheet due to its hardening effect. Precipitation of carbides also cause inferior corrosion-resistance.
  • a C content is controlled at a lowest possible level, i.e. 0.02 mass % or less for formability and corrosion-resistance.
  • the C content is preferably reduced to 0.015 mass % or less for improvement of secondary formability.
  • a lower limit of the C content is preferably determined at 0.001 mass %. Definition of the lower limit also assures the effect of carbides on random growth of recrystallized ferritic grains in a finish-annealing step.
  • Si is an alloying component, which is added as a deoxidizing agent during a steel-making process, but has a strong solid-solution hardening effect. Excess Si above 0.8 mass % unfavorably hardens a steel sheet, resulting in poor ductility. An upper limit of a Si content is preferably determined at 0.5 mass % for ductility and secondary formability.
  • Mn does not harden a steel sheet so much due to its solid-solution hardening effect weaker than Si. However, excess Mn above 1.5 mass % causes discharge of manganese fumes during a steel-making process, resulting in poor productivity.
  • P is harmful on hot-workability, so that its upper limit is determined at 0.050 mass %.
  • S is a harmful element, which segregates at grain boundaries and embrittles the grain boundaries. Such defects can be suppressed by controlling a S content to 0.01 mass % or less.
  • a Cr content is controlled to 8.0 mass % or more for assuring corrosion-resistance of a stainless steel.
  • toughness and formability of the stainless steel becomes worse as an increase of the Cr content, so that an upper limit of the Cr content is determined at 35.0 mass %.
  • the Cr content is preferably controlled to 20.0 mass % or less for further improvement of ductility and secondary formability.
  • N is converted to nitrides effective for random growth of recrystallized ferritic grains in a finish-annealing step, but has a hardening effect. Since excess N degrades ductility of a steel sheet, a N content is controlled to a lowest possible level, i.e. 0.05 mass % or less. The N content is preferably controlled to 0.02 mass % or less for further improvement of ductility and secondary formability. However, reduction of the N content to an extremely lower level necessitates a long-term refining operation and raises a steel-manufacturing cost. Therefore, a lower limit of the N content is preferably determined at 0.001 mass %. Definition of the lower limit also assures the effect of nitrides on random growth of recrystallized ferritic grains in a finish-annealing step.
  • Ti is an alloying component, which stabilizes C and N as carbonitrides for formability and corrosion-resistance. Such effect is apparently noted at a Ti content of 0.05 mass % or more. However, excess Ti above 0.40 mass % leads to rising of a steel cost and induces surface defects originated in titanium inclusions.
  • Nb which has the same effect as Ti on stabilization of C and N, is an essential component for precipitation of niobium inclusions of 0.15 ⁇ m or more in particle size except TiN.
  • the niobium inclusions are probably composed of carbides and Fe 2 Nb.
  • a Nb content of 0.10 mass % or more is necessary for precipitation of such niobium inclusions.
  • excess Nb above 0.50 mass % causes exaggerated precipitation and unfavorably raises a recrystallizing temperature of a ferritic stainless steel.
  • Ni is an optional element for toughness of a hot-rolled steel sheet and corrosion-resistance. But excess addition of Ni raises a material cost and hardens a steel sheet, so that an upper limit of a Ni content is determined at 0.5 mass %.
  • Mo is an optional element for corrosion-resistance, but excess Mo above 3.0 mass % is unfavorable for hot-workability.
  • Cu is an optional element, which is often included in a stainless steel from scraps during a steel-making process. Since excess Cu causes poor toughness and degradation of hot-workability, a Cu content is controlled to 2.0 mass % at most.
  • V and Zr are optional elements. V fixes free C as carbide in a steel matrix for formability, while Zr captures free O for formability and toughness. However, excess addition of V or Zr is necessarily avoided for productivity. In this sense, an upper limit each of V and Zr is determined at 0.3 mass %.
  • Al is an optional element, which is added as a deoxidizing agent in a steel-making process.
  • excess Al above 0.3 mass % causes an increase of nonmetallic inclusions, resulting in poor toughness and surface defects.
  • B is an optional element, which stabilizes N and improves corrosion-resistance and formability of a stainless steel.
  • the effects of B is apparently noted at 0.0010 mass % or more, but excess B above 0.0100 mass % is disadvantageous for hot-workability and weldability.
  • Ca, Mg, Co, REM (rare earth metals), etc. other than the above elements may be included from scraps during steel-making. Such elements do not put significant effects on circularity of a deeply-drawn steel sheet or dimensional accuracy of a press-formed steel sheet, unless they are included at extraordinary ratios.
  • TiN grows to coarse particles or forms clusters as an increase of (%Ti ⁇ %N).
  • the coarse TiN particles or cluster promotes accumulation of strains during primary-forming, resulting in formation of micro-cracks at an early stage of a drawing step.
  • Such harmful effects of the coarse TiN particles or cluster are eliminated by control of (%Ti X %N) to a value less than 0.005, as recognized in the later examples.
  • Carbide and nitride precipitates of 0.15 ⁇ m or more in particle size have a pinning action to suppress orientative grain growth and also growth to coarse grains, so as to improve isotropy of a stainless steel sheet, circularity in a cylindrically-drawn state and dimensional accuracy in a press-formed state.
  • Precipitates are carbides and nitrides of Ti and Nb, Laves phase and mixtures thereof.
  • TiN particles which are precipitated in a cubic shape, are excluded from the precipitates effective for press formability and dimensional accuracy, since the cubic TiN particles are likely to concentrate strains at their apexes and act as a starting point of micro-cracks.
  • Distribution of the precipitates of 0.15 ⁇ m or more in particle size except TiN at a rate of 5000-50000/mm 2 assures a pinning action effective for press formability and dimensional accuracy of a press-formed steel piece, as noted in the later examples.
  • a ferritic stainless steel sheet is hot-rolled at a relatively lower finish-temperature in order to induce nuclear site for precipitates, which will be distributed in a finish-annealed steel sheet. Boundaries of ferritic grains and internal strains in a hot-rolled state serve as the nuclear site.
  • a finish-temperature of hot-rolling is determined at 800° C. or lower in order to induce the nuclear sites as many as possible.
  • Precipitates in a hot-rolled steel sheet are moderated to a shape suitable for controlling the precipitates, which will be distributed in a finish-annealed steel sheet, to 0.15 ⁇ m or more in particle size, by annealing the hot-rolled steel sheet at 450-1080° C. If the annealing temperature is lower than 450° C., effective precipitates are scarcely formed. If the hot-rolled steel sheet is heated at a temperature above 1080° C. on the contrary, the precipitated except TiN are unpreferably re-dissolved in a steel matrix.
  • the annealing is completed in one hour for properly controlling distribution number of precipitates without growth to coarse particles.
  • a steel sheet is annealed at a relatively lower temperature in order to inhibit re-dissolution of the precipitates, which have been formed by annealing the hot-rolled steel sheet.
  • a temperature for intermediate-annealing just below a recrystallization-finishing temperature is preferable for relief of stress, which is introduced into the steel sheet by cold-rolling.
  • the steel sheet can be softened without re-dissolution of precipitates regardless somewhat remains of rolling texture, which is not recrystallized yet, as far as the annealing temperature is held within a range of from (a recrystallizing temperature—100° C.) to (a recrystallizing temperature).
  • the intermediate annealing period is completed in one minute in order to avoid re-dissolution of the precipitates, accounting faculty of a conventional continuous annealing furnace.
  • a rolling texture is eliminated by finish-annealing. But, a heating temperature above 1080° C. is not only disadvantageous for mass-productivity but also promotes re-dissolution of the precipitates and growth to coarse grains, resulting in poor toughness.
  • finish-annealing is completed in one minute, accounting faculty of a conventional continuous annealing furnace.
  • the inventors have investigated effects of TiN, which is often precipitated in a ferritic stainless steel matrix, as well as shape effects of precipitates on dimensional accuracy and secondary formability of a press-formed steel piece under the following conditions.
  • Table 1 shows the Nb, Ti and N contents together with a product of (% Ti ⁇ % N) and a recrystallization-finishing temperature. TABLE 1 Nb, Ti and N contents (mass %) together with (% Ti ⁇ % N) and a recrystallization-finishing temperature T rf (° C.) Steel No.
  • Each slab was hot-rolled to thickness of 4 mm at a finish-temperature of 750° C.
  • the hot-rolled steel sheets Nos. 1-7 were annealed at 800° C. for 60 seconds, pickled and then cold-rolled to thickness of 2 mm.
  • the steel sheets were further cold-rolled to final thickness of 0.5 mm, in accompaniment with intermediate-annealing at a temperature of (a recrystallization-finishing temperature ⁇ 50° C.) for 60 seconds.
  • the cold-rolled steel sheets were finish-annealed at 1000° C. for 60 seconds.
  • the hot-rolled steel sheets Nos. 8 and 9 were annealed, pickled and then cold-rolled to thickness of 2 mm.
  • the steel sheets were intermediately annealed and further cold-rolled to final thickness of 0.5 mm.
  • the cold-rolled steel sheets were subjected to finish-annealing.
  • Table 2 shows conditions of annealing the hot-rolled steel sheets, intermediate-annealing and finish-annealing. TABLE 2 Conditions of annealing hot-rolled steel sheets, intermediate-annealing and finish-annealing annealing hot- intermediate- Annealing rolled steel sheets annealing finish-annealing Steel No. No.
  • a test piece sampled from each annealed steel sheet was etched in a nonaqueous electrolyte of 10% acetylacetone-1% tetramethyl ammonium chloride-methyl alcohol under a potentiostatic condition and then observed by a scanning electron microscope to investigate distribution of precipitates.
  • a cross section in parallel to a rolling direction was inspected at arbitrary 50 points, and maximum length of each precipitate was measured and evaluated as particle size.
  • a blank sampled from each annealed steel sheet was press-formed to a cylindrical profile (shown in FIG. 1) by a multiplaten press.
  • Maximum and minimum radii of a cylindrical part C at a position apart 5 mm from a flanged part F were measured by a laser displacement meter.
  • a ratio of (the maximum diameter—the minimum diameter)/(the minimum diameter) was calculated and regarded as circularity to evaluate dimensional accuracy of a press-formed steel sheet.
  • Another test piece was bulged to a height of 10 mm, using a punch of 103 mm in diameter with a curvature radius of shoulder being 10 mm and a die of 105 mm in diameter with a curvature radius of shoulder being 8 mm under the condition a flange of the test piece was fixed with a bead.
  • a blank of 92 mm in diameter was sampled from a bottom of the bulged test piece, and a hole of 10 mm in diameter was formed at a center of the blank with a clearance of 10%. The blank was then subjected to a secondary formability test as follows:
  • the blank was held between a flathead punch of 40 mm in diameter with a curvature radius of shoulder being 3 mm and a die of 42 mm in diameter with a curvature radius of shoulder being 3 mm, in the manner that burrs around the hole faced to the die.
  • the hole was extruded by the punch until occurrence of cracks at its edge, while a flange of the blank was fixed with a bead.
  • a diameter of the hole was measured at the crack initiation.
  • Results are shown in Table 3. It is noted that steel sheets were cracked during press-forming at a product of (% Ti ⁇ % N) above 0.005. Steel sheets with a Nb content less than 0.02 mass % were formed with poor circularity, regardless manufacturing conditions. Observation results on any of cracked steel sheets and formed steel sheets with poor circularity prove that precipitates of 0.15 ⁇ m in particle size except TiN were distributed in a steel matrix only a few.
  • Each slab was hot-rolled to thickness of 4.0 mm, annealed, pickled and cold-rolled to thickness of 2 mm.
  • the cold-rolled steel sheet was intermediately annealed, further cold-rolled to final thickness of 0.5 mm and then finish-annealed.
  • Table 5 shows conditions of a finish-temperature of hot-rolling, annealing hot-rolled steel sheets, intermediate-annealing and finish-annealing.
  • Example 2 Each steel sheet was examined by the same way as Example 1, to investigate shape and distribution of precipitates as well as dimensional accuracy and secondary formability of a press-formed steel sheet.
  • Results shown in Table 6 prove that ferritic stainless steel sheets, wherein precipitates of 0.15 ⁇ m or more in particle size except TiN were distributed in steel matrix at a rate of 5000-50000/mm 2 , were press-formed to a good profile with circularity of 2.5% or less.
  • comparative steel sheets (Example Nos. A2, B2, C2 and D2), which satisfied compositional conditions of the present invention but were manufactured under improper conditions, had poor dimensional accuracy and secondary formability in a press-formed state due to the metallurgical structure that distribution number of the precipitates except TiN were out of 5000-50000/mm 2 .
  • the steel sheet I was too hard due to excess C and cracked during press-forming.
  • the steel sheet K was too strong due to excess Nb and cracked during press-forming.
  • the steel sheet L with a product of (% Ti ⁇ % N) above 0.005 was also cracked during press-forming, wherein the cracks were initiated near coarse TiN particles.
  • the steel sheet J with shortage of Nb was press-formed with poor circularity.
  • ferritic stainless steel sheets which can be press-formed with high dimensional accuracy and excellent secondary formability, are provided by distribution of precipitates of 0.15 ⁇ m or more in particle size except TiN at a rate of 5000-50000/mm 2 in a steel matrix with controlled composition. Shape and distribution of such precipitates suitable for the purpose are realized by properly controlling a finish-temperature of hot-rolling and conditions of heat-treatment for annealing a hot-rolled steel sheet, intermediate-annealing during cold-rolling and finish-annealing a cold-rolled steel sheet.
  • the ferritic stainless steel sheet manufactured in this way are useful as members or parts, which demand for strict dimensional precision, in various fields, e.g.
  • sealing members for organic electro-luminescent devices, precision pressed parts, sinks, utensils, burners of stoves, oil filler tubes of fuel tanks, motor casings, covers, caps of sensors, injector tubes, thermostat valves, bearing seals, flanges and so on, instead of expensive austenitic stainless steel sheets.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
US10/860,349 2003-06-04 2004-06-03 Ferritic stainless steel sheet excellent in press formability and secondary formability and its manufacturing method Abandoned US20040244884A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US12/396,966 US20090165905A1 (en) 2003-06-04 2009-03-03 Ferritic Stainless Steel Sheet Excellent in Press Formability and Secondary Formability and its Manufacturing Method

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2003159275A JP3886933B2 (ja) 2003-06-04 2003-06-04 プレス成形性，二次加工性に優れたフェライト系ステンレス鋼板及びその製造方法
JP2003-159275 2003-06-04

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US12/396,966 Continuation US20090165905A1 (en) 2003-06-04 2009-03-03 Ferritic Stainless Steel Sheet Excellent in Press Formability and Secondary Formability and its Manufacturing Method

Publications (1)

Publication Number Publication Date
US20040244884A1 true US20040244884A1 (en) 2004-12-09

Family

ID=33157175

Family Applications (2)

Application Number Title Priority Date Filing Date
US10/860,349 Abandoned US20040244884A1 (en) 2003-06-04 2004-06-03 Ferritic stainless steel sheet excellent in press formability and secondary formability and its manufacturing method
US12/396,966 Abandoned US20090165905A1 (en) 2003-06-04 2009-03-03 Ferritic Stainless Steel Sheet Excellent in Press Formability and Secondary Formability and its Manufacturing Method

Family Applications After (1)

Application Number Title Priority Date Filing Date
US12/396,966 Abandoned US20090165905A1 (en) 2003-06-04 2009-03-03 Ferritic Stainless Steel Sheet Excellent in Press Formability and Secondary Formability and its Manufacturing Method

Country Status (7)

Country Link
US (2) US20040244884A1 (ru)
EP (1) EP1484424B1 (ru)
JP (1) JP3886933B2 (ru)
KR (1) KR100595383B1 (ru)
CN (1) CN100363523C (ru)
DE (1) DE602004028780D1 (ru)
ES (1) ES2357303T3 (ru)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090092513A1 (en) * 2007-02-26 2009-04-09 Junichi Hamada Ferritic Stainless Steel Sheet Superior in Heat Resistance
US20110033731A1 (en) * 2008-05-12 2011-02-10 Nisshin Steel Co., Ltd. Ferritic stainless steel
US20110061777A1 (en) * 2007-08-20 2011-03-17 Jfe Steel Corporation Ferritic stainless steel sheet having superior punching workability and method for manufacturing the same
US20130183190A1 (en) * 2010-10-14 2013-07-18 Jfe Steel Corporation Ferritic stainless steel excellent in heat resistance property and formability
CN103510013A (zh) * 2013-09-29 2014-01-15 宝钢不锈钢有限公司 一种良好抗皱性的含锡铁素体不锈钢及其制造方法
US9816163B2 (en) 2012-04-02 2017-11-14 Ak Steel Properties, Inc. Cost-effective ferritic stainless steel
CN113227414A (zh) * 2018-12-21 2021-08-06 日铁不锈钢株式会社 耐氢脆性优异的Cr系不锈钢板

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2006233251A (ja) * 2005-02-23 2006-09-07 Nippon Steel & Sumikin Stainless Steel Corp 高純度フェライト系ステンレス鋼の製造方法およびその製品
CN100385032C (zh) * 2006-02-17 2008-04-30 山西太钢不锈钢股份有限公司 中铬含铜铁素体抗菌抗皱不锈钢板带及其制造方法
KR101261192B1 (ko) 2006-05-09 2013-05-09 닛폰 스틸 앤드 스미킨 스테인레스 스틸 코포레이션 내간극 부식성이 우수한 페라이트계 스테인리스 강
ATE541064T1 (de) * 2006-07-26 2012-01-15 Sandvik Intellectual Property Ferritischer stahl mit hohem chromgehalt
JP4998719B2 (ja) * 2007-05-24 2012-08-15 Ｊｆｅスチール株式会社 打ち抜き加工性に優れる温水器用フェライト系ステンレス鋼板およびその製造方法
CN101514431B (zh) * 2008-02-21 2011-11-23 宝山钢铁股份有限公司 一种高强度高延伸率Cr17型冷轧带钢及其制造方法
JP5366498B2 (ja) * 2008-10-17 2013-12-11 日新製鋼株式会社 Ｃｕめっきフェライト系ステンレス鋼板および多重巻き鋼管
CN101812641B (zh) * 2009-02-25 2013-09-04 宝山钢铁股份有限公司 一种铁素体不锈钢
JP4798298B2 (ja) * 2009-07-30 2011-10-19 Ｊｆｅスチール株式会社 導電性と延性に優れた燃料電池セパレータ用ステンレス鋼およびその製造方法
JP5501795B2 (ja) * 2010-02-24 2014-05-28 新日鐵住金ステンレス株式会社 溶接部の耐食性に優れた低クロム含有ステンレス鋼
CN101942609A (zh) * 2010-08-09 2011-01-12 振石集团东方特钢股份有限公司 一种具有低韧脆转变温度的铁素体不锈钢
CN101979166B (zh) * 2010-09-20 2012-10-10 首钢总公司 一种低屈强比微合金管线钢热轧卷板的生产方法
CN102618790B (zh) * 2012-03-26 2014-11-05 宝山钢铁股份有限公司 一种高强度低铬铁素体不锈钢及其制造方法
JP5937861B2 (ja) * 2012-03-27 2016-06-22 新日鐵住金ステンレス株式会社 溶接性に優れた耐熱フェライト系ステンレス鋼板
JP6541992B2 (ja) * 2015-03-12 2019-07-10 日鉄ステンレス株式会社 塗装かつ犠牲防食効果を利用した耐穴あき性に優れた自動車用部材および自動車用給油管
JP6598478B2 (ja) * 2015-03-12 2019-10-30 日鉄ステンレス株式会社 塩害耐食性に優れかつ外観劣化を抑制した自動車用給油管
JP6005234B1 (ja) * 2015-09-29 2016-10-12 日新製鋼株式会社 疲労特性に優れた高強度ステンレス鋼板およびその製造方法
KR101835003B1 (ko) 2016-09-28 2018-04-20 주식회사 포스코 흡음성이 우수한 배기계 열교환기용 페라이트계 스테인리스강 및 이의 제조 방법
JP6768929B2 (ja) * 2017-03-29 2020-10-14 日鉄ステンレス株式会社 高温耐摩耗性に優れたフェライト系ステンレス鋼、フェライト系ステンレス鋼板の製造方法、排気部品、高温摺動部品、およびターボチャージャー部品
CN109136735A (zh) * 2017-06-27 2019-01-04 宝钢不锈钢有限公司 具有良好成形性能的铁素体不锈钢及其制造方法
KR102109898B1 (ko) * 2018-06-26 2020-05-12 주식회사 포스코 진동 감쇄능이 우수한 저Cr 페라이트계 스테인리스강 및 그 제조방법
MX2021004713A (es) * 2018-10-25 2021-06-04 Jfe Steel Corp Chapa de acero inoxidable ferritico laminada en caliente y recocida y metodo para producir la misma.
JP7304715B2 (ja) * 2019-03-04 2023-07-07 日鉄ステンレス株式会社 フェライト系ステンレス鋼板
CN113005269A (zh) * 2021-02-20 2021-06-22 山西太钢不锈钢精密带钢有限公司 一种精密电子产品用沉淀硬化不锈钢精密带钢的生产方法
CN113502376A (zh) * 2021-06-18 2021-10-15 鞍钢联众(广州)不锈钢有限公司 一种改善含钛不锈钢钢坯次表皮夹杂的方法

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7025838B2 (en) * 2001-01-18 2006-04-11 Jfe Steel Corporation Ferritic stainless steel sheet with excellent workability and method for making the same

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5933645B2 (ja) * 1976-10-15 1984-08-17 新日本製鐵株式会社 リジング発生の少ない高加工性フエライト系ステンレス鋼板の製造方法
JP3706428B2 (ja) * 1996-03-15 2005-10-12 新日鐵住金ステンレス株式会社 自動車排気系機器用フェライト系ステンレス鋼
JP3269799B2 (ja) * 1998-02-20 2002-04-02 川崎製鉄株式会社 加工性、耐粒界腐食性および高温強度に優れるエンジン排気部材用フェライト系ステンレス鋼
JP3448498B2 (ja) * 1998-12-25 2003-09-22 新日本製鐵株式会社 リジング特性及び溶接部の加工性に優れたフェライト系ステンレス鋼
JP3601512B2 (ja) * 2000-12-22 2004-12-15 Ｊｆｅスチール株式会社 燃料タンク・燃料パイプ用フェライト系ステンレス鋼板およびその製造方法
US6786981B2 (en) * 2000-12-22 2004-09-07 Jfe Steel Corporation Ferritic stainless steel sheet for fuel tank and fuel pipe
KR100762151B1 (ko) * 2001-10-31 2007-10-01 제이에프이 스틸 가부시키가이샤 딥드로잉성 및 내이차가공취성이 우수한 페라이트계스테인리스강판 및 그 제조방법
JP3932020B2 (ja) * 2001-11-19 2007-06-20 日新製鋼株式会社 深絞り性に優れ面内異方性の小さいフェライト系ステンレス鋼及びその製造方法

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US7025838B2 (en) * 2001-01-18 2006-04-11 Jfe Steel Corporation Ferritic stainless steel sheet with excellent workability and method for making the same

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090092513A1 (en) * 2007-02-26 2009-04-09 Junichi Hamada Ferritic Stainless Steel Sheet Superior in Heat Resistance
US8062584B2 (en) * 2007-02-26 2011-11-22 Nippon Steel & Sumikin Stainless Steel Corporation Ferritic stainless steel sheet superior in heat resistance
US20110061777A1 (en) * 2007-08-20 2011-03-17 Jfe Steel Corporation Ferritic stainless steel sheet having superior punching workability and method for manufacturing the same
US20110033731A1 (en) * 2008-05-12 2011-02-10 Nisshin Steel Co., Ltd. Ferritic stainless steel
US9249475B2 (en) 2008-05-12 2016-02-02 Nisshin Steel Co., Ltd. Ferritic stainless steel
US20130183190A1 (en) * 2010-10-14 2013-07-18 Jfe Steel Corporation Ferritic stainless steel excellent in heat resistance property and formability
US9816163B2 (en) 2012-04-02 2017-11-14 Ak Steel Properties, Inc. Cost-effective ferritic stainless steel
CN103510013A (zh) * 2013-09-29 2014-01-15 宝钢不锈钢有限公司 一种良好抗皱性的含锡铁素体不锈钢及其制造方法
CN113227414A (zh) * 2018-12-21 2021-08-06 日铁不锈钢株式会社 耐氢脆性优异的Cr系不锈钢板
EP3901292A4 (en) * 2018-12-21 2022-11-23 NIPPON STEEL Stainless Steel Corporation CR-BASED STAINLESS STEEL WITH EXCELLENT RESISTANCE TO HYDROGEN EMBRITTLEMENT

Also Published As

Publication number Publication date
US20090165905A1 (en) 2009-07-02
KR100595383B1 (ko) 2006-06-30
DE602004028780D1 (de) 2010-10-07
EP1484424B1 (en) 2010-08-25
CN1572895A (zh) 2005-02-02
CN100363523C (zh) 2008-01-23
EP1484424A1 (en) 2004-12-08
JP3886933B2 (ja) 2007-02-28
ES2357303T3 (es) 2011-04-25
KR20040104939A (ko) 2004-12-13
JP2004360003A (ja) 2004-12-24

Similar Documents

Publication Publication Date Title
US20090165905A1 (en) Ferritic Stainless Steel Sheet Excellent in Press Formability and Secondary Formability and its Manufacturing Method
EP1889935B1 (en) High-strength steel sheet plated with zinc by hot dipping with excellent formability and process for producing the same
KR100977600B1 (ko) 오렌지 필이 작고 성형성이 우수한 페라이트계 스테인레스강판 및 그 제조 방법
CN107250404B (zh) 热轧钢板
JP6485549B2 (ja) 高強度熱延鋼板
JP4721916B2 (ja) 成形時の面内異方性が小さく耐リジング性及び耐肌荒れ性に優れたフェライト系ステンレス鋼薄板及びその製造方法
EP2163658A1 (en) Ferritic stainless steel sheet having excellent corrosion resistance against sulfuric acid, and method for production thereof
JP5126844B2 (ja) 熱間プレス用鋼板およびその製造方法ならびに熱間プレス鋼板部材の製造方法
EP2554705A1 (en) Hot-dip galvanized steel sheet with high tensile strength and superior processability and method for producing same
EP2617852A1 (en) High-strength hot-rolled steel sheet having excellent bending workability and method for producing same
KR100733017B1 (ko) 고강도 냉연강판 및 그 제조방법
WO2013054464A1 (ja) 深絞り性およびコイル内材質均一性に優れた高強度冷延鋼板およびその製造方法
US20240327961A1 (en) High strength cold rolled steel strip sheet for automotive use having good withstandability to retained austentite decomposition
EP2309015B1 (en) Procee for the production of a HIGH-STRENGTH HOT-DIP ZINC-COATED STEEL SHEET HAVING EXCELLENT SURFACE APPEARANCE
US20230052592A1 (en) Low-carbon low-cost ultra-high-strength multiphase steel plate/steel strip and manufacturing method therefor
JP2003213376A (ja) 二次穴拡げ性に優れたフェライト系ステンレス鋼板およびその製造方法
JP2020164956A (ja) フェライト系ステンレス鋼板およびその製造方法
CN111549285B (zh) 一种具有优良耐蚀性的超低碳镀锡板及其制备方法
EP4435120A1 (en) Ferritic stainless steel sheet
JP4740021B2 (ja) 形状凍結性に優れるＣｒ含有薄鋼板およびその製造方法
JP2002003993A (ja) 高強度薄鋼板および高強度亜鉛系めっき鋼板
US20240167137A1 (en) High strength cold rolled steel sheet for automotive use having excellent global formability and bending property
US20240229183A9 (en) Coiling temperature influenced cold rolled strip or steel
CN117966037A (zh) 各方向的材质偏差少的析出硬化型钢板及其制造方法
JP2002003994A (ja) 高強度薄鋼板および高強度亜鉛系めっき鋼板

Legal Events

Date Code Title Description
AS Assignment

Owner name: NISSHIN STEEL CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HIDESHIMA, YASUTOSHI;TOMIMURA, KOUKI;HIRAMATSU, NAOTO;REEL/FRAME:015440/0445

Effective date: 20040519

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION