US20040234438A1 - Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification - Google Patents
Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification Download PDFInfo
- Publication number
- US20040234438A1 US20040234438A1 US10/488,826 US48882604A US2004234438A1 US 20040234438 A1 US20040234438 A1 US 20040234438A1 US 48882604 A US48882604 A US 48882604A US 2004234438 A1 US2004234438 A1 US 2004234438A1
- Authority
- US
- United States
- Prior art keywords
- ceric oxide
- hours
- oxide
- cerium
- ceric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- CETPSERCERDGAM-UHFFFAOYSA-N ceric oxide Chemical compound O=[Ce]=O CETPSERCERDGAM-UHFFFAOYSA-N 0.000 title claims abstract description 90
- 229910000422 cerium(IV) oxide Inorganic materials 0.000 title claims abstract description 90
- 229940044927 ceric oxide Drugs 0.000 title claims abstract description 89
- 239000003054 catalyst Substances 0.000 title claims abstract description 25
- 238000004519 manufacturing process Methods 0.000 title description 4
- 238000005352 clarification Methods 0.000 title 1
- 238000001354 calcination Methods 0.000 claims abstract description 42
- 239000003426 co-catalyst Substances 0.000 claims abstract description 22
- 238000000034 method Methods 0.000 claims abstract description 19
- 229910052684 Cerium Inorganic materials 0.000 claims description 33
- GWXLDORMOJMVQZ-UHFFFAOYSA-N cerium Chemical compound [Ce] GWXLDORMOJMVQZ-UHFFFAOYSA-N 0.000 claims description 27
- 239000011148 porous material Substances 0.000 claims description 22
- 239000002244 precipitate Substances 0.000 claims description 19
- 238000010438 heat treatment Methods 0.000 claims description 17
- 229910000420 cerium oxide Inorganic materials 0.000 claims description 13
- BMMGVYCKOGBVEV-UHFFFAOYSA-N oxo(oxoceriooxy)cerium Chemical compound [Ce]=O.O=[Ce]=O BMMGVYCKOGBVEV-UHFFFAOYSA-N 0.000 claims description 13
- 238000001816 cooling Methods 0.000 claims description 8
- -1 cerium ions Chemical class 0.000 claims description 7
- 239000002904 solvent Substances 0.000 claims description 2
- 239000007789 gas Substances 0.000 abstract description 26
- 239000000463 material Substances 0.000 abstract description 17
- 229910052760 oxygen Inorganic materials 0.000 abstract description 14
- 239000001301 oxygen Substances 0.000 abstract description 14
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 abstract description 13
- 230000001747 exhibiting effect Effects 0.000 abstract description 2
- 239000000843 powder Substances 0.000 description 37
- 239000000243 solution Substances 0.000 description 32
- 238000005259 measurement Methods 0.000 description 11
- 239000012065 filter cake Substances 0.000 description 10
- 239000004570 mortar (masonry) Substances 0.000 description 10
- 229910002651 NO3 Inorganic materials 0.000 description 9
- NHNBFGGVMKEFGY-UHFFFAOYSA-N Nitrate Chemical compound [O-][N+]([O-])=O NHNBFGGVMKEFGY-UHFFFAOYSA-N 0.000 description 9
- 238000010298 pulverizing process Methods 0.000 description 9
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 8
- 230000000052 comparative effect Effects 0.000 description 7
- 239000002243 precursor Substances 0.000 description 7
- NLXLAEXVIDQMFP-UHFFFAOYSA-N Ammonium chloride Substances [NH4+].[Cl-] NLXLAEXVIDQMFP-UHFFFAOYSA-N 0.000 description 6
- VHUUQVKOLVNVRT-UHFFFAOYSA-N Ammonium hydroxide Chemical compound [NH4+].[OH-] VHUUQVKOLVNVRT-UHFFFAOYSA-N 0.000 description 6
- 239000002253 acid Substances 0.000 description 6
- QGZKDVFQNNGYKY-UHFFFAOYSA-N ammonia Natural products N QGZKDVFQNNGYKY-UHFFFAOYSA-N 0.000 description 6
- 235000011114 ammonium hydroxide Nutrition 0.000 description 6
- 238000006243 chemical reaction Methods 0.000 description 6
- 238000000926 separation method Methods 0.000 description 5
- 239000002002 slurry Substances 0.000 description 5
- 238000004438 BET method Methods 0.000 description 4
- UGFAIRIUMAVXCW-UHFFFAOYSA-N Carbon monoxide Chemical compound [O+]#[C-] UGFAIRIUMAVXCW-UHFFFAOYSA-N 0.000 description 3
- KWYUFKZDYYNOTN-UHFFFAOYSA-M Potassium hydroxide Chemical compound [OH-].[K+] KWYUFKZDYYNOTN-UHFFFAOYSA-M 0.000 description 3
- HEMHJVSKTPXQMS-UHFFFAOYSA-M Sodium hydroxide Chemical compound [OH-].[Na+] HEMHJVSKTPXQMS-UHFFFAOYSA-M 0.000 description 3
- 239000007864 aqueous solution Substances 0.000 description 3
- 229910002091 carbon monoxide Inorganic materials 0.000 description 3
- 239000012159 carrier gas Substances 0.000 description 3
- KKFPIBHAPSRIPB-UHFFFAOYSA-N cerium(3+);oxygen(2-);hydrate Chemical compound O.[O-2].[O-2].[O-2].[Ce+3].[Ce+3] KKFPIBHAPSRIPB-UHFFFAOYSA-N 0.000 description 3
- 239000013078 crystal Substances 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 239000007788 liquid Substances 0.000 description 3
- 239000000203 mixture Substances 0.000 description 3
- MWUXSHHQAYIFBG-UHFFFAOYSA-N nitrogen oxide Inorganic materials O=[N] MWUXSHHQAYIFBG-UHFFFAOYSA-N 0.000 description 3
- 239000002245 particle Substances 0.000 description 3
- 238000011160 research Methods 0.000 description 3
- 238000003756 stirring Methods 0.000 description 3
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 2
- MHAJPDPJQMAIIY-UHFFFAOYSA-N Hydrogen peroxide Chemical compound OO MHAJPDPJQMAIIY-UHFFFAOYSA-N 0.000 description 2
- AFCARXCZXQIEQB-UHFFFAOYSA-N N-[3-oxo-3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propyl]-2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidine-5-carboxamide Chemical compound O=C(CCNC(=O)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)N1CC2=C(CC1)NN=N2 AFCARXCZXQIEQB-UHFFFAOYSA-N 0.000 description 2
- KDLHZDBZIXYQEI-UHFFFAOYSA-N Palladium Chemical compound [Pd] KDLHZDBZIXYQEI-UHFFFAOYSA-N 0.000 description 2
- 230000003197 catalytic effect Effects 0.000 description 2
- 238000001035 drying Methods 0.000 description 2
- 239000001307 helium Substances 0.000 description 2
- 229910052734 helium Inorganic materials 0.000 description 2
- SWQJXJOGLNCZEY-UHFFFAOYSA-N helium atom Chemical compound [He] SWQJXJOGLNCZEY-UHFFFAOYSA-N 0.000 description 2
- 229910052751 metal Inorganic materials 0.000 description 2
- 239000002184 metal Substances 0.000 description 2
- 239000012452 mother liquor Substances 0.000 description 2
- 230000001473 noxious effect Effects 0.000 description 2
- 230000001590 oxidative effect Effects 0.000 description 2
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical compound [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 description 2
- 230000001376 precipitating effect Effects 0.000 description 2
- 239000000047 product Substances 0.000 description 2
- 239000012429 reaction media Substances 0.000 description 2
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 1
- 150000000703 Cerium Chemical class 0.000 description 1
- 238000010521 absorption reaction Methods 0.000 description 1
- 230000003213 activating effect Effects 0.000 description 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 description 1
- 229910052786 argon Inorganic materials 0.000 description 1
- 238000007664 blowing Methods 0.000 description 1
- 239000000919 ceramic Substances 0.000 description 1
- HSJPMRKMPBAUAU-UHFFFAOYSA-N cerium(3+);trinitrate Chemical compound [Ce+3].[O-][N+]([O-])=O.[O-][N+]([O-])=O.[O-][N+]([O-])=O HSJPMRKMPBAUAU-UHFFFAOYSA-N 0.000 description 1
- DPUCLPLBKVSJIB-UHFFFAOYSA-N cerium;tetrahydrate Chemical compound O.O.O.O.[Ce] DPUCLPLBKVSJIB-UHFFFAOYSA-N 0.000 description 1
- 239000002131 composite material Substances 0.000 description 1
- 238000007796 conventional method Methods 0.000 description 1
- 229910052878 cordierite Inorganic materials 0.000 description 1
- 239000008367 deionised water Substances 0.000 description 1
- 229910021641 deionized water Inorganic materials 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 238000003795 desorption Methods 0.000 description 1
- JSKIRARMQDRGJZ-UHFFFAOYSA-N dimagnesium dioxido-bis[(1-oxido-3-oxo-2,4,6,8,9-pentaoxa-1,3-disila-5,7-dialuminabicyclo[3.3.1]nonan-7-yl)oxy]silane Chemical compound [Mg++].[Mg++].[O-][Si]([O-])(O[Al]1O[Al]2O[Si](=O)O[Si]([O-])(O1)O2)O[Al]1O[Al]2O[Si](=O)O[Si]([O-])(O1)O2 JSKIRARMQDRGJZ-UHFFFAOYSA-N 0.000 description 1
- 229910001873 dinitrogen Inorganic materials 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 238000002474 experimental method Methods 0.000 description 1
- 238000001914 filtration Methods 0.000 description 1
- 239000000446 fuel Substances 0.000 description 1
- 229930195733 hydrocarbon Natural products 0.000 description 1
- 150000002430 hydrocarbons Chemical class 0.000 description 1
- 239000001257 hydrogen Substances 0.000 description 1
- 229910052739 hydrogen Inorganic materials 0.000 description 1
- 150000002431 hydrogen Chemical class 0.000 description 1
- 239000000413 hydrolysate Substances 0.000 description 1
- QSHDDOUJBYECFT-UHFFFAOYSA-N mercury Chemical compound [Hg] QSHDDOUJBYECFT-UHFFFAOYSA-N 0.000 description 1
- 229910052753 mercury Inorganic materials 0.000 description 1
- 239000013081 microcrystal Substances 0.000 description 1
- 238000006386 neutralization reaction Methods 0.000 description 1
- 150000002926 oxygen Chemical class 0.000 description 1
- 229910052763 palladium Inorganic materials 0.000 description 1
- 229910052697 platinum Inorganic materials 0.000 description 1
- 238000001556 precipitation Methods 0.000 description 1
- 238000003825 pressing Methods 0.000 description 1
- 238000010992 reflux Methods 0.000 description 1
- 229910052703 rhodium Inorganic materials 0.000 description 1
- 239000010948 rhodium Substances 0.000 description 1
- MHOVAHRLVXNVSD-UHFFFAOYSA-N rhodium atom Chemical compound [Rh] MHOVAHRLVXNVSD-UHFFFAOYSA-N 0.000 description 1
- 238000010079 rubber tapping Methods 0.000 description 1
- 238000005245 sintering Methods 0.000 description 1
- 239000007784 solid electrolyte Substances 0.000 description 1
- 238000010561 standard procedure Methods 0.000 description 1
- 238000003860 storage Methods 0.000 description 1
- 230000008542 thermal sensitivity Effects 0.000 description 1
- 238000005406 washing Methods 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F17/00—Compounds of rare earth metals
- C01F17/20—Compounds containing only rare earth metals as the metal element
- C01F17/206—Compounds containing only rare earth metals as the metal element oxide or hydroxide being the only anion
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
- B01J20/06—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising oxides or hydroxides of metals not provided for in group B01J20/04
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
- B01D53/34—Chemical or biological purification of waste gases
- B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
- B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D53/00—Separation of gases or vapours; Recovering vapours of volatile solvents from gases; Chemical or biological purification of waste gases, e.g. engine exhaust gases, smoke, fumes, flue gases, aerosols
- B01D53/34—Chemical or biological purification of waste gases
- B01D53/92—Chemical or biological purification of waste gases of engine exhaust gases
- B01D53/94—Chemical or biological purification of waste gases of engine exhaust gases by catalytic processes
- B01D53/9445—Simultaneously removing carbon monoxide, hydrocarbons or nitrogen oxides making use of three-way catalysts [TWC] or four-way-catalysts [FWC]
- B01D53/945—Simultaneously removing carbon monoxide, hydrocarbons or nitrogen oxides making use of three-way catalysts [TWC] or four-way-catalysts [FWC] characterised by a specific catalyst
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/02—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material
- B01J20/0203—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof comprising inorganic material comprising compounds of metals not provided for in B01J20/04
- B01J20/0207—Compounds of Sc, Y or Lanthanides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J20/00—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof
- B01J20/28—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties
- B01J20/28054—Solid sorbent compositions or filter aid compositions; Sorbents for chromatography; Processes for preparing, regenerating or reactivating thereof characterised by their form or physical properties characterised by their surface properties or porosity
- B01J20/28057—Surface area, e.g. B.E.T specific surface area
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/10—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of rare earths
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
- B01J35/31—Density
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/61—Surface area
- B01J35/612—Surface area less than 10 m2/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/61—Surface area
- B01J35/613—10-100 m2/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/61—Surface area
- B01J35/615—100-500 m2/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/63—Pore volume
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/60—Catalysts, in general, characterised by their form or physical properties characterised by their surface properties or porosity
- B01J35/63—Pore volume
- B01J35/633—Pore volume less than 0.5 ml/g
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/03—Precipitation; Co-precipitation
- B01J37/031—Precipitation
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F17/00—Compounds of rare earth metals
- C01F17/20—Compounds containing only rare earth metals as the metal element
- C01F17/206—Compounds containing only rare earth metals as the metal element oxide or hydroxide being the only anion
- C01F17/224—Oxides or hydroxides of lanthanides
- C01F17/235—Cerium oxides or hydroxides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01D—SEPARATION
- B01D2255/00—Catalysts
- B01D2255/20—Metals or compounds thereof
- B01D2255/206—Rare earth metals
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/12—Surface area
- C01P2006/13—Surface area thermal stability thereof at high temperatures
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/14—Pore volume
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/90—Other properties not specified above
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02A—TECHNOLOGIES FOR ADAPTATION TO CLIMATE CHANGE
- Y02A50/00—TECHNOLOGIES FOR ADAPTATION TO CLIMATE CHANGE in human health protection, e.g. against extreme weather
- Y02A50/20—Air quality improvement or preservation, e.g. vehicle emission control or emission reduction by using catalytic converters
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T10/00—Road transport of goods or passengers
- Y02T10/10—Internal combustion engine [ICE] based vehicles
- Y02T10/12—Improving ICE efficiencies
Definitions
- the present invention relates to ceric oxide that has excellent heat resistance useful for catalysts, functional ceramics, solid electrolyte for fuel cells, and the like, and particularly suitable for use as a co-catalyst material in catalysts for purifying vehicle exhaust gas.
- the present invention also relates to a method for preparing such ceric oxide, and a catalyst for purifying exhaust gas utilizing such ceric oxide.
- Catalysts for purifying vehicle exhaust gas are composed of a catalytic metal such as platinum, palladium, or rhodium, and a co-catalyst for enhancing the catalytic action of such metal, both supported on a catalyst support made of, for example, alumina or cordierite.
- a co-catalyst material are used cerium oxide-containing materials, which have the properties of absorbing oxygen under the oxidizing atmosphere and desorbing oxygen under the reducing atmosphere, originated in ceric oxide, i.e., oxygen absorbing and desorbing capability.
- the cerium oxide-containing materials purify noxious components in exhaust gases such as hydrocarbons, carbon monoxide, and nitrogen oxides at excellent efficiency. As such, large quantities of the cerium oxide-containing materials are used as a co-catalyst.
- efficiency of exhaust gas treatment with a catalyst is proportional to the contact area between the active phase of the catalyst and the exhaust gas, and to the oxygen absorbing and desorbing capability of the co-catalyst material, such as ceric oxide.
- the co-catalyst material is required to have a sufficiently large specific surface area and a sufficiently high oxygen absorbing and desorbing capability, as well as high activity at lower temperatures.
- JP-7-61863-B proposes a method for obtaining a ceric oxide having good heat resistance, including precipitating ceric hydroxide in a reaction medium at pH 6 to about pH 10, treating the resulting precipitate in an autoclave at 100 to 350° C., and calcining at 300 to 1000° C., to thereby obtain ceric oxide.
- the heat resistance of the resulting ceric oxide represented by the specific surface area after calcination at 900° C. is 15 m 2 /g, which is not sufficient.
- JP-2001-89143-A, JP-2000-281343-A, JP-2789313-B, and JP-2000-128537-A propose cerium-containing oxides having improved oxygen storage capacity (OSC).
- OSC oxygen storage capacity
- all of these oxides are composite oxides containing ceric oxide having one or more other elements solid-solutioned therein, and are not high-purity ceric oxides.
- JP-3-24478-B, JP-3-24411-B, and JP-2537662-B propose methods for preparing ceric oxide including refluxing an aqueous solution of ceric nitrate, separating the resulting hydrolysate by filtering, washing, drying, and calcining, to thereby prepare ceric oxide.
- the ceric oxide thus obtained has low heat resistance represented by a specific surface area after calcination at 900° C. for 5 hours of as low as not higher than 10 m 2 /g.
- ceric oxide that has excellent heat resistance and oxygen absorbing and desorbing capability useful as a co-catalyst material suitable for a catalyst for purifying exhaust gas, that is capable of maintaining a large specific surface area even in use in a high temperature environment, and that is suitable for use in a high temperature environment, yet capable of exhibiting high oxygen absorbing and desorbing capability also in a lower temperature range, a method for preparing such ceric oxide, and a catalyst for purifying exhaust gas utilizing such ceric oxide.
- the present inventors have made an intensive research for achieving the above objects.
- the inventors made a detailed research on the possible effect of crystallinity of cerium oxide hydrate, which is a precursor of ceric oxide, on the drop in the specific surface area observed in conventional ceric oxide upon heating to a high temperature, irrespective of its large specific surface area before heating.
- crystallinity of a cerium oxide precursor prepared by a conventional method known to produce a highly heat resistant ceric oxide i.e. by drying a cerium sol, an aqueous solution of a cerium salt, or a mixture of these, is extremely sensitive to thermal energy, possibly due to its microcrystal.
- a ceric oxide which is an oxide consisting essentially of ceric oxide and has a specific surface area of not smaller than 30.0 m 2 /g after calcination at 900° C. for 5 hours.
- a catalyst for purifying exhaust gas comprising a co-catalyst, wherein said co-catalyst comprises the above ceric oxide.
- FIG. 1 is a graph showing TPR curves drawn in Examples 1 and 9 and Comparative Examples 1 and 2.
- the ceric oxide according to the present invention is an oxide consisting essentially of ceric oxide, and has a specific surface area of not smaller than 30.0 m 2 /g, preferably not smaller than 40.0 m 2 /g, more preferably not smaller than 50.0 m 2 /g, after calcination at 900° C. for 5 hours.
- the maximum specific surface area after calcination at 900° C. for 5 hours is not particularly limited, and may usually be about 100 m 2 /g.
- the ceric oxide of the present invention generally has a large specific surface area of not smaller than 180 m 2 /g after calcination at 250° C. for 5 hours, not smaller than 160 m 2 /g after calcination at 300° C. for 5 hours, not smaller than 40.0 m 2 /g after calcination at 800° C. for 5 hours, not smaller than 30.0 m 2 /g after calcination at 900° C. for 5 hours, and not smaller than 20.0 m 2 /g after calcination at 1000° C. for 5 hours.
- No ceric oxide is hitherto known having such a large specific surface area after calcination at such high temperatures.
- the ceric oxide of the present invention may be used as a co-catalyst material capable of withstanding expected use at a higher temperature of about 900° C.
- the specific surface area referred to in the present specification is measured according to the BET method utilizing absorption of nitrogen gas, which is the most standard method for measuring the specific surface area of powders.
- the ceric oxide of the present invention may preferably has an S1/S2 ratio, that is, a ratio of the area (S 1 ) defined by the baseline and the TPR curve in the temperature range of 200 to 600° C., to the area (S 2 ) defined by the baseline and the TPR curve in the temperature range of 600 to 1000° C., of usually not lower than 0.120, more preferably not lower than 0.150, most preferably not lower than 0.190, measured after calcination at 1000° C. for 5 hours.
- S1/S2 ratio of not lower than 0.120 means that the ceric oxide exhibits excellent reducibility in a low temperature range of not higher than 600° C., after calcination at as high as 1000° C.
- the “baseline” means a line segment drawn from the point on the TPR curve corresponding to 200° C. in parallel to the axis representing temperature, up to 1000° C.
- the TPR is performed using a temperature programmed desorption analyzer (trade name: TP-5000) manufactured by OKURA RIKEN CO., LTD., with a carrier gas containing 90% argon and 10% hydrogen, at a gas flow rate of 30 ml/min, at a heating rate of a sample during measurement of 13.3° C./min, and using 0.5 g of a sample.
- TP-5000 temperature programmed desorption analyzer
- the ceric oxide of the present invention preferably has, after calcination at 900° C. for 5 hours, OSC of not smaller than 0.60 mlO 2 /g/s evaluated at 400° C.
- the maximum OSC is not particularly limited, and is usually 2.0 mlO 2 /g/s. No ceric oxide is hitherto known having such high OSC.
- the OSC and the active temperature of a co-catalyst material, such as ceric oxide are important. Usually, catalysts for purifying vehicle exhaust gas do not function until they are heated to a particular temperature, and prematurely discharge exhaust gas without purifying the noxious components therein.
- the ceric oxide of the present invention may preferably have the excellent OSC as mentioned above, and is thus quite useful for catalysts for purifying vehicle exhaust gas.
- the OSC is determined by holding 30 mg of a sample in the atmosphere at 900° C. for 5 hours, allowing to cool to an ordinary temperature, heating up to 400° C., subjecting to alternate flows of two different carrier gases (one contains 95% helium and 5% carbon monoxide, and the other contains 97.5% helium and 2.5% oxygen) at the flow rate of 200 ml/min at the interval of 1 second, measuring the amounts of carbon monoxide and oxygen in the carrier gases passed through the sample by means of a mass spectrograph, and making a calculation in accordance with the following formula:
- ⁇ CO stands for an amount of CO reduced in a unit time
- rCO stands for a flow rate of CO gas
- WT stands for weight of the sample.
- the ceric oxide of the present invention preferably has a tap density of usually not higher than 1.3 g/ml, more preferably not higher than 1.2 g/ml, after calcination at 300° C. for 10 hours.
- the minimum tap density is not particularly limited, and is usually about 0.80 g/ml.
- the tap density may be measured by taking 10 g of ceric oxide calcined at 300° C. for 10 hours in a 20 ml cylinder, and tapping the cylinder with drop height of 2 cm for 200 strokes.
- the ceric oxide of the present invention preferably has a total pore volume of usually not smaller than 0.50 ml/g, more preferably not smaller than 0.60 ml/g, after calcination at 300° C. for 10 hours.
- the maximum total pore volume is not particularly limited, and is usually 1.5 ml/g.
- the total pore volume may be measured by ordinary mercury porosimeter.
- ceric oxide of the present invention may preferably be prepared by the production method according to the present invention to be discussed below, with good reproducibility and in an economical manner.
- step (a) first a cerium solution not less than 90 mol % of which cerium ions are tetravalent is provided in step (a).
- the cerium solution not less than 90 mol % of which cerium ions are tetravalent may preferably be a ceric nitrate solution.
- a ceric nitrate solution initially contains 250 g per liter of cerium in terms of cerium oxide, and has an initial acid concentration of usually 0.1 to 1N. The initial acid concentration relates to the acid concentration in the subsequent reaction. If the acid concentration is too low, the crystallinity of the precipitate to be discussed later may not be improved sufficiently, resulting in low heat resistance of the objective ceric oxide. If the acid concentration is too high, excess base is required in the neutralization reaction for precipitating cerium, thus being industrially disadvantageous.
- the acid concentration of the cerium solution is adjusted to usually 5 to 150 g/L, preferably 10 to 120 g/L, more preferably 15 to 100 g/L, in terms of cerium oxide, usually with water, preferably with deionized water.
- step (a) next the cerium solution prepared in step (a) is held at 60 to 220° C. under heating to cause reaction of the cerium solution in step (b).
- Any reaction vessel may be used in step (b) without critical limitation, and either a sealed vessel or an open vessel may be used.
- an autoclave reactor may preferably be used.
- the temperature for holding under heating is 60 to 220° C., preferably 80 to 180° C., more preferably 90 to 160° C., and the duration of holding under heating is usually 10 minutes to 48 hours, preferably 30 minutes to 36 hours, more preferably 1 hour to 24 hours. If the cerium solution is not sufficiently held under heating, the crystallinity of the precipitate to be discussed later may not be improved, resulting in insufficient heat resistance of the objective ceric oxide. Even if the cerium solution is held under heating for a longer time, the heat resistance may be affected little, and thus being industrially disadvantageous.
- step (b) the heated cerium solution is usually cooled in step (c).
- the cerium solution may usually be cooled under stirring.
- Means for cooling are not critical, and may be cooling in an atmosphere or forced cooling with cooling tube.
- the cooling temperature is usually not higher than 60° C., preferably not higher than room temperature.
- a precipitant is added to the cooled cerium solution to prepare a precipitate in step (d).
- the precipitant used in step (d) may be a base such as sodium hydroxide, potassium hydroxide, an aqueous ammonia solution, ammonia gas, or mixtures thereof, with an aqueous ammonia solution being preferred.
- the precipitant may be added by preparing an aqueous solution of the precipitant at a suitable concentration and adding the solution to the precursor solution prepared in step (c) under stirring, or when ammonia gas is used, by blowing the gas into the reaction vessel under stirring.
- the amount of the precipitant may easily be decided by tracing the pH change of the solution. Usually, a sufficient amount is such that the pH of the solution is not lower than 7, and a preferred amount is such that the pH is 7 to 8.
- a product with grown crystals may be precipitated.
- This product is a preferable precursor for obtaining the ceric oxide of the present invention, and may be separated, for example, by Nutsche method, centrifuging, or filter pressing.
- the precipitate may optionally be washed with water, as required. Further, the precipitate may optionally be dried to a suitable extent for improving the efficiency in the following step (e).
- the precipitate obtained in step (d) may be subjected to, before step (e), step (d- 1 ) of dispersing the precipitate in a solvent such as water, and heat-treating the resulting solution at usually 60 to 220° C., preferably 80 to 180° C., more preferably 90 to 160° C., to obtain a reprecipitate.
- the duration of the heat treatment is usually 10 minutes to 48 hours, preferably 30 minutes to 36 hours, more preferably 1 to 24 hours.
- the precipitate thus obtained is calcined in step (e) to obtain the objective ceric oxide.
- the calcination temperature may suitably be selected from the range of usually 250 to 900° C.
- the selection of the temperature may be made as desired, depending on the required or guaranteed values of the specific surface area and bulk density.
- the calcination temperature may preferably be 250 to 800° C., more preferably 250 to 700° C., most preferably 280 to 450° C.
- the duration of calcination may suitably be determined depending on the temperature, and may preferably be 1 to 10 hours.
- the ceric oxide obtained may usually be pulverized.
- the pulverization may sufficiently be performed in an ordinary pulverizer, such as a hammer mill, to obtain a powder of a desired particle size.
- the ceric oxide obtained by the present method may be given a desired particle size through the above mentioned pulverization.
- a preferred average particle size of the ceric oxide is 1 to 50 ⁇ m.
- the catalyst for purifying exhaust gas according to the present invention may be of any type, as long as it has a co-catalyst containing the ceric oxide of the present invention.
- the catalyst may be produced, for example, by a commonly known method and with commonly known other materials.
- the ceric oxide of the present invention has a large specific surface area, and in particular, is capable of maintaining a specific surface area of at least 30.0 m 2 /g even after calcination at 900° C. for 5 hours.
- the present ceric oxide finds particular application in a co-catalyst in catalysts for purifying exhaust gas, in place of conventional ceric oxide, and is useful in the field of more effective catalysts for purifying exhaust gas.
- the method of the present invention allows production of the above ceric oxide with good reproducibility and in an economical manner.
- a ceric nitrate solution not less than 90 mol % cerium ions of which were tetravalent was taken so that 20 g of cerium in terms of cerium oxide was contained, and the total volume was adjusted to 1 liter with pure water.
- concentration in terms of cerium oxide was 20 g/L.
- the solution was placed in an autoclave reactor, heated to 100° C., held at this temperature for 24 hours, and allowed to cool in an atmosphere to room temperature.
- Powder (A) was calcined at 1000° C. for 5 hours, and then the TPR measurement was made. The results are shown in FIG. 1. Further, from the TPR curve taken after calcination at 1000° C. for 5 hours, the ratio of the area (S 1 ) defined by the baseline and the TPR curve in the temperature range of 200 to 600° C. to the area (S 2 ) defined by the baseline and the TPR curve in the temperature range of 600 to 1000° C., i.e., the S1/S2 ratio, was determined. The results are shown in Table 1.
- Ceric oxide powder was prepared in the same way as in Example 1, except that the temperature and duration for holding the prepared ceric nitrate solution under heating were changed as shown in Table 1.
- a filter cake was obtained in the same way as in Example 1.
- the filter cake obtained was treated in an autoclave reactor, dispersed in water to reslurry, heated to 100° C., held at this temperature for 1 hour, and cooled to room temperature.
- the slurry was then subjected to solid-liquid separation with a Nutsche filter, to obtain a filter cake.
- the filter cake was calcined at 300° C. for 10 hours in a box-type electric furnace under air atmosphere, and ground in a mortar, to thereby obtain ceric oxide powder.
- the resulting powder was subjected to the same measurements as in Example 1. The results are shown in Table 1.
- Ceric oxide powder was prepared in the same way as in Example 3, except that the concentration of the ceric nitrate solution, the temperature and duration for holding the ceric nitrate solution under heating were changed as shown in Table 1.
- the ceric oxide powder obtained was subjected to the same measurements as in Example 1. The results are shown in Table 1.
- the ceric oxide powder obtained by calcination at 300° C. for 10 hours, followed by pulverization in a mortar was further calcined at 500° C. for 5 hours, or at 700° C. for 5 hours, and then the tap density and total pore volume were measured, respectively. The results of these are also shown in Table 1.
- the ceric oxide powder obtained by calcination at 300° C. for 10 hours, followed by pulverization in a mortar was further calcined at 1000° C. for 5 hours, and then the TPR measurement was made as in Example 1. The results are shown in FIG. 1.
- a ceric nitrate solution not less than 90 mol % cerium ions of which were tetravalent was taken so that 20 g of cerium in terms of cerium oxide was contained, and the total volume was adjusted to 1 liter with pure water.
- the concentration in terms of cerium oxide was 20 g/L.
- the resulting solution was immediately neutralized with an aqueous ammonia solution to pH 8 without the heat treatment in an autoclave reactor, to thereby obtain cerium oxide hydrate in the form of a slurry.
- the slurry was then subjected to solid-liquid separation with a Nutsche filter, followed by separation of the mother liquor, to obtain a filter cake.
- the filter cake was calcined at 300° C.
- Example 1 the ceric oxide powder obtained by calcining at 300° C. for 10 hours, followed by pulverization in a mortar, was further calcined at 1000° C. for 5 hours, and then the TPR measurement was made. The results are shown in FIG. 1.
- a filter cake was obtained in the same way as in Comparative Example 2.
- the obtained filter cake was subjected to the heat treatment and calcination in the same way as in Example 3, to obtain ceric oxide powder.
- the powder was subjected to the same measurements as in Example 1. The results are shown in Table 2.
- REO concentration is the concentration of cerium in the ceric nitrate solution in terms of cerium oxide.
- BET(1) is the specific surface area of the ceric oxide powder obtained by calcining at 300° C. for 10 hours, followed by pulverization in a mortar;
- BET(2) is the specific surface area of the powder in BET(1) further calcined at 800° C. for 2 hours;
- BET(3) is the specific surface area of the powder in BET(1) further calcined at 900° C. for 5 hours;
- BET(4) is the specific surface area of the powder in BET(1) further calcined at 1000° C. for 5 hours, all measured by the BET method.
- the specific surface area is shown in m 2 /g.
- Tap density (1) is the tap density of the ceric oxide powder obtained by calcining at 300° C. for 10 hours, followed by pulverization in a mortar;
- Tap density (2) is the tap density of the powder in Tap density (1) further calcined at 500° C. for 5 hours;
- Tap density (3) is the tap density of the powder in Tap density (1) further calcined at 700° C. for 5 hours.
- the tap density is shown in g/ml.
- Total pore volume (1) is the total pore volume of the ceric oxide powder obtained by calcining at 300° C. for 10 hours, followed by pulverization in a mortar;
- Total pore volume (2) is the total pore volume of the powder in Total pore volume (1) further calcined at 500° C.
- Total pore volume (3) is the total pore volume of the powder in Total pore volume (1) further calcined at 700° C. for 5 hours.
- the total pore volume is shown in ml/g. TABLE 1 Example 1 2 3 4 5 6 7 8 9 10 11 REO Concentration (g/L) 20 20 20 15 25 40 60 20 20 10 30 Temperature (° C.) 100 130 100 100 100 100 100 100 120 120 120 Duration (h) 24 1 24 24 24 24 24 24 6 6 6 6 6 BET (1) 175.4 155.1 197.4 236.6 213.4 166.0 172.0 241.4 217.1 215.3 220.0 BET (2) 73.3 75.5 85.6 80.0 80.1 68.3 72.5 78.6 88.6 81.6 84.4 BET (3) 33.6 36.6 47.7 44.6 42.3 31.1 30.8 40.7 48.0 53.2 50.3 BET (4) 21.6 22.4 23.7 22.2 21.6 21.1 22.3 21.0 24.2 23.7 23.0 Tap density (1) 1.1 1.1 1.1 1.1 1.2 1.2 1.1 1.1 1.1 1.1
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Materials Engineering (AREA)
- Analytical Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Combustion & Propulsion (AREA)
- Biomedical Technology (AREA)
- Environmental & Geological Engineering (AREA)
- General Chemical & Material Sciences (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Life Sciences & Earth Sciences (AREA)
- Geology (AREA)
- Catalysts (AREA)
- Exhaust Gas Treatment By Means Of Catalyst (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/673,352 US7361322B2 (en) | 2001-09-07 | 2007-02-09 | Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2001272054 | 2001-09-07 | ||
JP2001-272054 | 2001-09-07 | ||
PCT/JP2002/009025 WO2003022740A1 (fr) | 2001-09-07 | 2002-09-05 | Oxyde cerique et procede de production de celui-ci, ainsi que catalyseur destine a l'epuration des gaz d'echappement |
Related Child Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/673,352 Continuation US7361322B2 (en) | 2001-09-07 | 2007-02-09 | Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification |
Publications (1)
Publication Number | Publication Date |
---|---|
US20040234438A1 true US20040234438A1 (en) | 2004-11-25 |
Family
ID=19097479
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/488,826 Pending US20040234438A1 (en) | 2001-09-07 | 2002-09-05 | Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification |
US11/673,352 Expired - Lifetime US7361322B2 (en) | 2001-09-07 | 2007-02-09 | Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/673,352 Expired - Lifetime US7361322B2 (en) | 2001-09-07 | 2007-02-09 | Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification |
Country Status (8)
Country | Link |
---|---|
US (2) | US20040234438A1 (ja) |
EP (1) | EP1435338B1 (ja) |
JP (1) | JP4382482B2 (ja) |
KR (1) | KR100890773B1 (ja) |
CN (1) | CN1290770C (ja) |
CA (1) | CA2459496C (ja) |
DE (1) | DE60239212C5 (ja) |
WO (1) | WO2003022740A1 (ja) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060032150A1 (en) * | 2004-08-16 | 2006-02-16 | So Jae H | Method for producing improved cerium oxide abrasive particles and compositions including such particles |
US20060156635A1 (en) * | 2004-12-16 | 2006-07-20 | K.C. Tech Co., Ltd. | Abrasive particles, polishing slurry, and producing method thereof |
US20070075291A1 (en) * | 2005-06-03 | 2007-04-05 | Paik Un G | CMP Slurry, Preparation Method Thereof and Method of Polishing Substrate Using the Same |
US20150306577A1 (en) * | 2011-01-14 | 2015-10-29 | Santoku Corporation | Catalyst and process for producing same |
US20170313594A1 (en) * | 2014-11-12 | 2017-11-02 | Rhodia Operations | Cerium oxide particles and method for production thereof |
CN114368774A (zh) * | 2021-12-20 | 2022-04-19 | 兰州大学 | 一种多孔氧化铈的制备方法及处理氮氧化物的方法 |
Families Citing this family (24)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH11181403A (ja) * | 1997-12-18 | 1999-07-06 | Hitachi Chem Co Ltd | 酸化セリウム研磨剤及び基板の研磨法 |
JP4602165B2 (ja) * | 2004-06-02 | 2010-12-22 | 財団法人電力中央研究所 | 揮発性有機化合物の分解除去法と分解除去用触媒 |
JP4982692B2 (ja) * | 2006-03-17 | 2012-07-25 | Dowaエレクトロニクス株式会社 | 触媒用酸化セリウム粉体およびdpf |
FR2917646B1 (fr) | 2007-06-20 | 2011-06-03 | Anan Kasei Co Ltd | Oxyde mixte a haute surface specifique de cerium et d'autre terre rare, procede de preparation et utilisation en catalyse |
EP2518018B1 (en) | 2009-12-25 | 2020-11-25 | Solvay Special Chem Japan, Ltd. | Complex oxide, method for producing same, and exhaust gas purifying catalyst |
CN103833569B (zh) * | 2012-11-23 | 2016-12-21 | 丰益高分子材料(连云港)有限公司 | 脂肪族羧酸酰胺的制备方法 |
WO2014202149A1 (en) | 2013-06-21 | 2014-12-24 | Rhodia Operations | Composite oxide based on cerium oxide, silicon oxide and titanium oxide |
JP2015120844A (ja) * | 2013-12-24 | 2015-07-02 | 旭硝子株式会社 | 研磨剤の製造方法、研磨方法および半導体集積回路装置の製造方法 |
EP3237365B1 (en) | 2014-12-22 | 2018-11-28 | Rhodia Operations | Cycloalkane oxidation catalysts and method to produce alcohols and ketones |
EP3070074A1 (en) | 2015-03-20 | 2016-09-21 | Rhodia Operations | Dehydration of alcohols |
CA3024282A1 (en) * | 2016-05-18 | 2017-11-23 | Rhodia Operations | Cerium oxide particles and method for production thereof |
CN106040241B (zh) * | 2016-06-03 | 2019-04-26 | 浙江科技学院 | 一种废弃物沼渣制备非均相Fenton催化剂的方法和应用 |
WO2018040058A1 (en) * | 2016-09-02 | 2018-03-08 | Rhodia Operations | Dehydration of diols |
WO2019042911A1 (en) | 2017-08-29 | 2019-03-07 | Rhodia Operations | USE OF A MIXED OXIDE TO ABSORB NOX |
WO2019042910A1 (en) | 2017-08-29 | 2019-03-07 | Rhodia Operations | MIXED OXIDE WITH ENHANCED REDOX PROPERTIES |
FR3077567A1 (fr) | 2018-02-02 | 2019-08-09 | Rhodia Operations | Procede de preparation d'un oxyde a base de cerium et/ou de zirconium |
FR3077566A1 (fr) | 2018-02-02 | 2019-08-09 | Rhodia Operations | Procede de preparation d'un oxyde a base de cerium et/ou de zirconium |
US11897779B2 (en) | 2018-08-24 | 2024-02-13 | East China Normal University | Microporous aluminotitanosilicate crystalline zeolite, method of preparation and applications thereof |
EP3902771A1 (en) | 2018-12-28 | 2021-11-03 | Rhodia Operations | Cerium oxide particles and method for production thereof |
CN111089763A (zh) * | 2019-11-28 | 2020-05-01 | 中国汽车技术研究中心有限公司 | 一种用于obd验证试验的临界汽车尾气催化剂制备方法 |
KR102659037B1 (ko) | 2020-11-24 | 2024-04-22 | 라이너스 레어 얼스 리미티드 | 도핑된 산화세륨을 생성하기 위한 물질, 방법 및 기술 |
KR20240014060A (ko) | 2021-05-28 | 2024-01-31 | 로디아 오퍼레이션스 | 특정 다공성 프로파일을 갖는 산화알루미늄과 산화세륨의 조성물 |
WO2023006686A1 (en) | 2021-07-30 | 2023-02-02 | Rhodia Operations | Composition of aluminium oxide and cerium oxide |
WO2023242394A1 (en) | 2022-06-17 | 2023-12-21 | Rhodia Operations | Suspension of cerium oxide particles |
Citations (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4661330A (en) * | 1984-02-20 | 1987-04-28 | Rhone-Poulenc Specialties Chimiques | Process for the preparation of cerium oxide particulates |
US4663137A (en) * | 1984-02-20 | 1987-05-05 | Rhone-Poulenc Specialties Chimiques | Process for producing cerium oxide particulates |
US4965057A (en) * | 1987-06-26 | 1990-10-23 | Rhone-Poulenc Chimie | Process for producing morphologically improved ceric oxide particulates |
US5002747A (en) * | 1987-06-29 | 1991-03-26 | Rhone-Poulenc Chimie | Process for obtaining ceric oxide |
US5011671A (en) * | 1987-06-29 | 1991-04-30 | Rhone-Poulenc Chimie | Ceric oxide with new morphological characteristics and method for obtaining same |
US5174984A (en) * | 1987-06-29 | 1992-12-29 | Rhone-Poulenc Chimie | Ceric oxide with new morphological characteristics and method for obtaining same |
US5279789A (en) * | 1988-12-23 | 1994-01-18 | Rhone-Poulenc Chimie | Ceric oxide particulates having improved morphology |
US20020016060A1 (en) * | 1996-02-07 | 2002-02-07 | Jun Matsuzawa | Cerium oxide abrasive for polishing insulating films formed on substrate and methods for using the same |
US20030215378A1 (en) * | 2002-05-15 | 2003-11-20 | Xiao-Dong Zhou | Method for preparation of nanometer cerium-based oxide particles |
US20050031517A1 (en) * | 2001-05-07 | 2005-02-10 | Siu-Wai Chan | Apparatus and method for preparing cerium oxide nanoparticles |
US20050113249A1 (en) * | 2003-11-24 | 2005-05-26 | Robin Ziebarth | Catalyst for a diesel particulate filter |
US20060039846A1 (en) * | 1999-11-17 | 2006-02-23 | Cheng-Hung Hung | Ceria composition and process for preparing same |
Family Cites Families (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2640954B1 (ja) * | 1988-12-23 | 1991-03-29 | Rhone Poulenc Chimie | |
FR2640953B1 (ja) * | 1988-12-23 | 1991-02-08 | Rhone Poulenc Chimie | |
JP2641108B2 (ja) * | 1990-06-21 | 1997-08-13 | 大日精化工業株式会社 | 酸化セリウム微粉体の製造方法 |
JP2794645B2 (ja) * | 1991-10-15 | 1998-09-10 | 三徳金属工業株式会社 | 酸素吸収・放出能を有する酸化セリウム及びその製造法 |
JPH11330015A (ja) * | 1996-03-29 | 1999-11-30 | Hitachi Chem Co Ltd | 酸化セリウム研磨剤及び基板の製造法 |
JP4053623B2 (ja) * | 1996-12-27 | 2008-02-27 | 阿南化成株式会社 | ジルコニウム−セリウム系複合酸化物及びその製造方法 |
DE19714707A1 (de) * | 1997-04-09 | 1998-10-15 | Degussa | Sauerstoff speicherndes Material mit hoher Temperaturstabilität sowie Verfahren zu seiner Herstellung |
US6200143B1 (en) * | 1998-01-09 | 2001-03-13 | Tessera, Inc. | Low insertion force connector for microelectronic elements |
-
2002
- 2002-09-05 CA CA2459496A patent/CA2459496C/en not_active Expired - Lifetime
- 2002-09-05 JP JP2003526823A patent/JP4382482B2/ja not_active Expired - Lifetime
- 2002-09-05 WO PCT/JP2002/009025 patent/WO2003022740A1/ja active Application Filing
- 2002-09-05 DE DE60239212.8T patent/DE60239212C5/de not_active Expired - Lifetime
- 2002-09-05 EP EP02767896A patent/EP1435338B1/en not_active Expired - Lifetime
- 2002-09-05 US US10/488,826 patent/US20040234438A1/en active Pending
- 2002-09-05 CN CNB028221060A patent/CN1290770C/zh not_active Expired - Lifetime
- 2002-09-05 KR KR1020047003356A patent/KR100890773B1/ko active IP Right Grant
-
2007
- 2007-02-09 US US11/673,352 patent/US7361322B2/en not_active Expired - Lifetime
Patent Citations (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5080877A (en) * | 1984-02-20 | 1992-01-14 | Rhone-Poulenc Specialties Chimiques | Novel cerium oxide particulates |
US4663137A (en) * | 1984-02-20 | 1987-05-05 | Rhone-Poulenc Specialties Chimiques | Process for producing cerium oxide particulates |
US4661330A (en) * | 1984-02-20 | 1987-04-28 | Rhone-Poulenc Specialties Chimiques | Process for the preparation of cerium oxide particulates |
US5017352A (en) * | 1984-02-20 | 1991-05-21 | Rhone-Pulenc Specialites Chimique | Novel cerium oxide particulates |
US4965057A (en) * | 1987-06-26 | 1990-10-23 | Rhone-Poulenc Chimie | Process for producing morphologically improved ceric oxide particulates |
US5466428A (en) * | 1987-06-26 | 1995-11-14 | Rhone-Poulenc Chimie | Morphologically improved ceric oxide particulates |
US5174984A (en) * | 1987-06-29 | 1992-12-29 | Rhone-Poulenc Chimie | Ceric oxide with new morphological characteristics and method for obtaining same |
US5023070A (en) * | 1987-06-29 | 1991-06-11 | Rhone-Poulenc Chimie | Process for obtaining a ceric oxide |
US5011671A (en) * | 1987-06-29 | 1991-04-30 | Rhone-Poulenc Chimie | Ceric oxide with new morphological characteristics and method for obtaining same |
US5002747A (en) * | 1987-06-29 | 1991-03-26 | Rhone-Poulenc Chimie | Process for obtaining ceric oxide |
US5279789A (en) * | 1988-12-23 | 1994-01-18 | Rhone-Poulenc Chimie | Ceric oxide particulates having improved morphology |
US5891412A (en) * | 1988-12-23 | 1999-04-06 | Rhone-Poulenc Chimie | Ceric oxide particulates having improved morphology |
US20020016060A1 (en) * | 1996-02-07 | 2002-02-07 | Jun Matsuzawa | Cerium oxide abrasive for polishing insulating films formed on substrate and methods for using the same |
US20060039846A1 (en) * | 1999-11-17 | 2006-02-23 | Cheng-Hung Hung | Ceria composition and process for preparing same |
US20050031517A1 (en) * | 2001-05-07 | 2005-02-10 | Siu-Wai Chan | Apparatus and method for preparing cerium oxide nanoparticles |
US20030215378A1 (en) * | 2002-05-15 | 2003-11-20 | Xiao-Dong Zhou | Method for preparation of nanometer cerium-based oxide particles |
US20050113249A1 (en) * | 2003-11-24 | 2005-05-26 | Robin Ziebarth | Catalyst for a diesel particulate filter |
Cited By (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060032150A1 (en) * | 2004-08-16 | 2006-02-16 | So Jae H | Method for producing improved cerium oxide abrasive particles and compositions including such particles |
US20060156635A1 (en) * | 2004-12-16 | 2006-07-20 | K.C. Tech Co., Ltd. | Abrasive particles, polishing slurry, and producing method thereof |
US20070075291A1 (en) * | 2005-06-03 | 2007-04-05 | Paik Un G | CMP Slurry, Preparation Method Thereof and Method of Polishing Substrate Using the Same |
US8062547B2 (en) | 2005-06-03 | 2011-11-22 | K.C. Tech Co., Ltd. | CMP slurry, preparation method thereof and method of polishing substrate using the same |
US20150306577A1 (en) * | 2011-01-14 | 2015-10-29 | Santoku Corporation | Catalyst and process for producing same |
US9962685B2 (en) * | 2011-01-14 | 2018-05-08 | Santoku Corporation | Catalyst and process for producing same |
US20170313594A1 (en) * | 2014-11-12 | 2017-11-02 | Rhodia Operations | Cerium oxide particles and method for production thereof |
US10160658B2 (en) * | 2014-11-12 | 2018-12-25 | Rhodia Operations | Cerium oxide particles and method for production thereof |
US11034589B2 (en) | 2014-11-12 | 2021-06-15 | Rhodia Operations | Cerium oxide particles and method for production thereof |
CN114368774A (zh) * | 2021-12-20 | 2022-04-19 | 兰州大学 | 一种多孔氧化铈的制备方法及处理氮氧化物的方法 |
Also Published As
Publication number | Publication date |
---|---|
EP1435338B1 (en) | 2011-02-16 |
EP1435338A1 (en) | 2004-07-07 |
CN1582258A (zh) | 2005-02-16 |
DE60239212C5 (de) | 2021-09-23 |
CN1290770C (zh) | 2006-12-20 |
DE60239212D1 (de) | 2011-03-31 |
US7361322B2 (en) | 2008-04-22 |
EP1435338A4 (en) | 2006-01-25 |
JP4382482B2 (ja) | 2009-12-16 |
CA2459496C (en) | 2011-11-22 |
JPWO2003022740A1 (ja) | 2004-12-24 |
KR20040039332A (ko) | 2004-05-10 |
US20070128097A1 (en) | 2007-06-07 |
WO2003022740A1 (fr) | 2003-03-20 |
KR100890773B1 (ko) | 2009-03-31 |
CA2459496A1 (en) | 2003-03-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7361322B2 (en) | Ceric oxide and method for production thereof, and catalyst for exhaust gas clarification | |
US6171572B1 (en) | Method for preparing a zirconium-cerium composite oxide | |
EP1287876B1 (en) | Composite oxide, process for producing the same, and exhaust gas reducing co-catalyst | |
RU2509725C2 (ru) | Композиция на основе оксида церия и оксида циркония с особой пористостью, способ получения и применение в катализе | |
US9931614B2 (en) | Ceria-zirconia-based composite oxide and method for producing same, and catalyst for exhaust gas purification including ceria-zirconia-based composite oxide | |
EP2505262B1 (en) | Complex oxide, method for producing same and exhaust gas purifying catalyst | |
US9757711B2 (en) | Complex oxide, method for producing same, and exhaust gas purifying catalyst | |
JPH11322339A (ja) | セリウム−ジルコニウム系複合酸化物及びその製造方法ならびに排ガス浄化用触媒材料 | |
EP2505263B1 (en) | Complex oxide, method for producing same and exhaust gas purifying catalyst | |
EP2794488B1 (en) | Composite oxide, method for producing the same, and catalyst for exhaust gas purification | |
CN110841623A (zh) | 一种高温结构稳定的铈锆复合氧化物及其制备方法 | |
JP2000319019A (ja) | ジルコニウム−セリウム系複合酸化物及びその製造方法 | |
WO2013092557A1 (en) | Composite oxide, method for producing the same, and catalyst for exhaust gas purification | |
US20080242536A1 (en) | Metal Oxide with High Thermal Stability and Preparing Method Thereof | |
EP1928788B1 (en) | Method for preparing metal oxide containing precious metals | |
JPH0796186A (ja) | 排気ガス浄化用触媒およびその製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: ANAN KASEI CO., LTD., JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DAI, LIANXIN;PACAUD, BERNARD;AOZASA, SHIGERU;AND OTHERS;REEL/FRAME:015531/0347 Effective date: 20040319 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: FINAL REJECTION MAILED |