TW201323205A - 光學膜、包括其的背光單元和包括其的光學顯示設備 - Google Patents
光學膜、包括其的背光單元和包括其的光學顯示設備 Download PDFInfo
- Publication number
- TW201323205A TW201323205A TW101146781A TW101146781A TW201323205A TW 201323205 A TW201323205 A TW 201323205A TW 101146781 A TW101146781 A TW 101146781A TW 101146781 A TW101146781 A TW 101146781A TW 201323205 A TW201323205 A TW 201323205A
- Authority
- TW
- Taiwan
- Prior art keywords
- optical film
- rubber
- meth
- acrylate
- optical
- Prior art date
Abstract
本公開提供了光學膜、包括其的背光單元和包括其的光學顯示設備。所述光學膜具有在亮度、抗刮性、抗靜電性能和低黃變方面的優異的性能,並在背光單元組裝時能夠使缺陷率最小化。
Description
本發明涉及光學膜、包括其的背光單元和包括其的光學顯示設備。更具體的,本發明涉及光學膜、包括其的背光單元和包括其的光學顯示設備,所述光學膜具有優異的亮度、抗刮性、抗靜電性能和低黃變(yellowing),並能夠在組裝背光單元時使缺陷率最小化。
在光學膜的結構中,棱鏡片用於改善液晶顯示器(LCD)的亮度。由於LCD自身不能發光,其藉由光源(CCFL或LED)的方式獲得光。獲得的光藉由導光板分布到整個區域,其藉由擴散片轉變成具有更均勻亮度的表面光源。在這個過程中,由最初光源發出的光的效率穩定降低。如果使用棱鏡片,藉由將側光改變為前光並收集反射光可提高亮度。
用作光收集片的棱鏡片為具有薄膜撓性的光學膜,其形成表面結構,以便在一側以線性排列布置棱鏡圖案,從而改善亮度。
除了藉由形成物理結構以改善亮度,也可考慮基於光學材料改善亮度。為此目的,折射率可為一個主要因素。當折射率增加時,
改善了棱鏡膜的性能,從而實現了高亮度。
為改善亮度,棱鏡片具有期望的光學性能,例如棱鏡膜和用於棱鏡的光固化材料的折射率,是很重要的。然而,在棱鏡片中遇到的主要問題是,在背光單元操作等的過程中,在形成棱鏡片後的運輸中,由意外事件造成的外部撞擊引起的膜和塗布劑的收縮和形狀的變形。可應用於現有棱鏡片的各種光固化單體和組合物不能解决這些問題。因此,為解决這些問題,已經使用具有低折射率和或多或少的彈性的氨基甲酸酯丙烯酸酯(urethane acrylate)開發了基於具有自恢復性能的光固化組合物的棱鏡片。然而,由於與自恢復相關的限制,這樣的棱鏡片不適於提高亮度。
本發明的一個方面提供了光學膜,包括基膜和在所述基膜的至少一側形成的光學功能層,其中,所述基膜和所述光學功能層的至少一種可包括橡膠。
所述橡膠可為選自由丁腈橡膠(nitrile butadiene rubber,NBR)、苯乙烯丁二烯橡膠(styrene butadiene rubber,SBR)、矽酮橡膠、氨基甲酸酯橡膠、(甲基)丙烯酸橡膠、氯丁二烯橡膠(chloroprene rubber,CR)、三元乙丙(ethylene propylene diene monomer,EPDM)橡膠和氟化橡膠組成的族群中的至少一種。
所述橡膠可具有1,000 g/mol至1,000,000 g/mol範圍內的重均分子量。
所述橡膠在所述光學膜中的含量可為1 wt%至50 wt%。
所述光學功能層可包括含所述橡膠和可UV固化不飽和化合物(UV-curable unsaturated compound)的組合物的固化產物。
所述可UV固化不飽和化合物可包括(甲基)丙烯酸酯低聚物和(甲基)丙烯酸酯單體中的至少一種。
所述可UV固化不飽和化合物可包括含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或單體。
所述含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或其單體在所述組合物中的含量可為5 wt%至90 wt%。
基於100重量份的所述橡膠,所述可UV固化不飽和化合物在所述組合物中的含量可為10重量份至900重量份。
所述組合物可進一步包括抗靜電劑、矽酮添加劑和引發劑。
所述抗靜電劑可包含藉由結合具有離子性(ionically)鍵結到離子導電金屬的環氧乙基或環氧丙基的離子導電聚合物與常規反應性矽酮樹脂而獲得的樹脂。
所述矽酮添加劑可包括聚醚矽氧烷共聚物和有機改性聚矽氧烷化合物中的至少一種。
所述組合物可包括1 wt%至50 wt%的所述橡膠,25 wt%至90 wt%的所述可UV固化不飽和化合物,0.1 wt%至10 wt%的所述抗靜電劑,0.01 wt%至10 wt%的所述矽酮添加劑和0.5 wt%至7wt%的所述引發劑。
所述光學功能層可包括選自棱鏡、雙凸透鏡、微透鏡和壓紋形狀(embossed shape)中的至少一種光學圖案。
所述光學膜可包括棱鏡片。
本發明的另一個方面提供包括所述光學膜的背光單元。
本發明的再一個方面提供包括所述光學膜的光學顯示設備。
本發明中,“光學膜”可包括基膜和形成在基膜上的光學功能層。
如此處所用,術語“光學功能層”可指作用為收集、漫射、透射、折射或反射光的層。
在本發明的一個方面,光學膜可包括橡膠。橡膠可包括在基膜和光學功能層的至少一個中。優選地,橡膠可包括於光學功能層中。
橡膠可包括於光學膜中,並能夠改善自恢復和抗刮性,使黃變最小化,及加强光學膜的抗靜電性能的改善效果。
橡膠可具有1,000 g/mol至1,000,000 g/mol的重均分子量。在這個範圍內,橡膠可與其它包括於光學膜中的組分相容,並可以容易地獲得。優選地,橡膠可具有10,000 g/mol至1,000,000 g/mol的重均分子量。
橡膠可作為液體橡膠聚合物包括在用於光學膜的組合物中,並與將被包括在所述光學膜的以下可UV固化不飽和化合物進行交聯反應。對於交聯反應,液體橡膠聚合物可在聚合物的末端包括氨基、羥基、羧酸基、異氰酸基、鹵素基團、丙烯酸基等。
橡膠可為選自丁腈橡膠(NBR)、苯乙烯丁二烯橡膠(SBR)、矽酮橡膠、氨基甲酸酯橡膠、(甲基)丙烯酸橡膠、氯丁二烯橡膠(CR)、三元乙丙橡膠(EPDM)橡膠和氟化橡膠中的至少一種。
在光學膜中,橡膠含量可為1 wt%至50 wt%、優選為10 wt%至40 wt%,更優選為30 wt%至40 wt%。在該範圍內,可獲得優異的光學膜的自恢復和抗刮性。
在光學功能層中,橡膠含量可為1 wt%至50 wt%、優選10 wt%至40 wt%,更優選30 wt%至40 wt%。在該範圍內,可獲得優異的光學膜的自恢復和抗刮性。
光學功能層可具有收集、漫射、透射、折射或反射由基膜獲得的光的功能,藉此光學膜可用作棱鏡片、擴散片、導光板等。
光學功能層可具有光學圖案,以具有收集、漫射、透射、折射或反射光的功能。光學圖案可包括棱鏡、雙凸透鏡、微透鏡、壓紋形狀等的至少一種,不限於此。光學圖案的高度可在30 μm至50 μm的範圍內。
光學功能層可包括含所述液體橡膠聚合物和所述可UV固化不飽和化合物的組合物的固化產物。
可UV固化不飽和化合物可藉由與用於形成橡膠的液體聚合物進行交聯反應形成光學膜的基質。
可UV固化不飽和化合物可包括(甲基)丙烯酸酯低聚物和(甲基)丙烯酸酯單體中的至少一種。
本領域中使用的任何(甲基)丙烯酸酯低聚物可無限制地用作
(甲基)丙烯酸酯低聚物。例如,可使用具有1,000 g/mol至100,000 g/mol範圍內的重均分子量的(甲基)丙烯酸酯低聚物。具體地,(甲基)丙烯酸酯低聚物可為選自氨基甲酸酯(甲基)丙烯酸酯、環氧(甲基)丙烯酸酯(epoxy(meth)acrylate)、聚酯(甲基)丙烯酸酯(polyester (meth)acrylate)、氟代(甲基)丙烯酸酯(fluorine(meth)acrylate)、(甲基)丙烯酸芴酯(fluorene(meth)acrylate)、矽酮(甲基)丙烯酸酯(silicone (meth)acrylate)、(甲基)丙烯酸磷酸酯(phosphate(meth)acrylate)、馬來醯亞胺改性(甲基)丙烯酸酯(maleimide modified(meth)acrylate)和丙烯酸酯(甲基)丙烯酸酯(acrylate(meth)acrylate)中的至少一種。
氨基甲酸酯(甲基)丙烯酸酯可包括由多醇、異氰酸酯化合物和(甲基)丙烯酸酯合成並在其分子結構中具有氨基甲酸酯鍵的低聚物。多醇的實例可包括聚酯多醇、聚醚多醇、聚碳酸酯多醇、聚己內酯多醇、開環四氫呋喃環氧丙烷共聚物、聚丁二烯二醇、聚二甲基矽氧烷二醇、乙二醇、丙二醇、1,4-丁二醇、1,5-戊二醇、1,6-乙二醇、新戊二醇、1,4-環己二甲醇、雙酚A、氫化雙酚A或混合物。異氰酸酯化合物的實例可包括2,4-甲苯二異氰酸酯、1,3-二甲苯二異氰酸酯、1,4-二甲苯二異氰酸酯、1,5-萘二異氰酸酯、二異氰酸1,6-己酯(1,6-hexane diisocyanate)、二異氰酸異佛爾酮酯(isophorone diisocyanate)和它們的混合物。(甲基)丙烯酸酯的實例可包括含C1至C50烷基和羥基的(甲基)丙烯酸酯。
環氧(甲基)丙烯酸酯可選自(甲基)丙烯酸酯低聚物,其分子間結構包括2-溴氫醌(2-bromohydroquinone),間苯二酚,鄰苯二酚,例
如雙酚A、雙酚F、雙酚AD和雙酚S的雙酚,4,4'-二羥基聯苯、雙(4-羥苯基)醚等的骨架;和(甲基)丙烯酸酯低聚物,其分子間結構包括烷基、芳基、羥甲基、烯丙基、脂環、例如四溴雙酚A的鹵素、硝基等。
馬來醯亞胺改性(甲基)丙烯酸酯可指由具有至少兩個馬來醯亞胺基團的化合物和(甲基)丙烯酸酯製備的低聚物。所述化合物可為選自由1-甲基-2,4-雙馬來醯亞胺苯、N,N'-間-亞苯基雙馬來醯亞胺(N,N'-m-phenylenebismaleimide)、N,N'-對-亞苯基馬來醯亞胺、N,N'-間-甲代亞苯基雙馬來醯亞胺(N,N'-m-toluylenebismaleimide)、N,N'-4,4-亞聯苯基雙馬來醯亞胺、N,N'-4,4-(3,3'-二甲基亞聯苯基)雙馬來醯亞胺、N,N'-4,4-(3,3'-二甲基二苯基甲烷)雙馬來醯亞胺、N,N'-4,4-(3,3'-二乙基二苯基甲烷)雙馬來醯亞胺、N,N'-4,4-二苯基甲烷雙馬來醯亞胺、N,N'-4,4-二苯基丙烷雙馬來醯亞胺、N,N'-4,4-二苯醚雙馬來醯亞胺、2,2-雙(4-(4-馬來醯亞胺苯氧基)苯基)丙烷、2,2-雙(3-叔丁基-4-(4-馬來醯亞胺苯氧基)苯基)丙烷、1,1-雙(4-(4-馬來醯亞胺苯氧基)苯基)癸烷、4,4’-亞環己基雙(1-(4-馬來醯亞胺苯氧基)-2-環己基苯、2,2-雙(4-(4-馬來醯亞胺苯氧基)苯基)六氟丙烷和它們的混合物組成的族群中的至少一種。所述(甲基)丙烯酸酯可為具有C1至C50烷基的(甲基)丙烯酸酯。
在一個實施方式中,(甲基)丙烯酸酯低聚物可包括選自(甲基)丙烯酸芴酯、雙酚A環氧(甲基)丙烯酸酯、雙酚F環氧(甲基)丙烯酸酯和酚醛樹脂環氧(甲基)丙烯酸酯中的至少一種。
在本發明中,可無任何限制地使用本領域中通常使用的任何
(甲基)丙烯酸酯單體。具體地,(甲基)丙烯酸酯單體可為選自(甲基)丙烯酸苯甲酯(benzyl(meth)acrylate)、(甲基)丙烯酸苯氧基苯甲酯、2-苯基苯氧乙基(甲基)丙烯酸酯、1,6-己二醇單(甲基)丙烯酸酯、2-羥乙基(甲基)丙烯酸酯、2-羥丙基(甲基)丙烯酸酯、2-羥丁基(甲基)丙烯酸酯、2-羥-3-苯氧丙基(甲基)丙烯酸酯、1,4-丁二醇單(甲基)丙烯酸酯或1,4-丁二醇二(甲基)丙烯酸酯、2-羥乙基(甲基)丙烯醯磷酸酯(2-hydroxyethyl(meth)acryloyl phosphate)、4-羥環己基(甲基)丙烯酸酯、新戊二醇單(甲基)丙烯酸酯、三羥甲基乙烷二(甲基)丙烯酸酯、三羥甲基丙烷二(甲基)丙烯酸酯、季戊四醇三(甲基)丙烯酸酯、二季戊四醇五(甲基)丙烯酸酯、二季戊四醇六(甲基)丙烯酸酯、二(甲基)丙烯酸甘油酯(glycerin di(meth)acrylate)、(甲基)丙烯酸四氫糠酯(tetrahydrofurfuryl(meth)acrylate)、(甲基)丙烯酸異癸酯、2-(2-乙氧基乙氧基)乙基(甲基)丙烯酸酯、(甲基)丙烯酸硬脂酯、(甲基)丙烯酸月桂酯、2-苯氧乙基(甲基)丙烯酸酯、(甲基)丙烯酸異冰片酯、(甲基)丙烯酸十三烷基酯、乙氧加成型壬基苯酚(甲基)丙烯酸酯(ethoxy addition type nonylphenol(meth)acrylate)、乙二醇二(甲基)丙烯酸酯、二乙二醇二(甲基)丙烯酸酯、三乙二醇二(甲基)丙烯酸酯、四乙二醇二(甲基)丙烯酸酯、聚乙二醇二(甲基)丙烯酸酯、1,3-丁二醇二(甲基)丙烯酸酯、三丙二醇二(甲基)丙烯酸酯、乙氧加成型雙酚A二(甲基)丙烯酸酯、環己烷二甲醇二(甲基)丙烯酸酯、苯氧基四甘醇(甲基)丙烯酸酯(phenoxy-tetra-glycol(meth)acrylate)、2-(甲基)丙烯醯氧乙基磷酸酯(2-(meth)acryloyloxyethyl phosphate)、二甲醇三環癸烷二(甲基)丙烯酸
酯、三羥甲基丙烷苯甲酸丙烯酸酯、(甲基)丙烯酸芴酯、雙酚F(甲基)丙烯酸酯、雙酚A環氧(甲基)丙烯酸酯、酚醛樹脂環氧(甲基)丙烯酸酯、苯基苯氧乙基(甲基)丙烯酸酯、乙氧基化硫代聯苯基二(甲基)丙烯酸酯(ethoxylated thiodiphenyl di(meth)acrylate)和苯基硫代乙基(甲基)丙烯酸酯中的至少一種。
此外,可UV固化不飽和化合物可包括含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或單體。含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯可改善光學膜的彈性和自恢復,從而改善光學膜的抗刮性。(甲基)丙烯酸酯低聚物或其單體優選可包括具有10 mol%至50 mol%的環氧乙基,更優選為10 mol%至40 mol%,還更優選為10 mol%至30 mol%。
如此處所用,術語“環氧乙基”可指-CH2-CH2-O-或-O-CH2-CH2-。
含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或單體在光學膜中的含量可為5 wt%至90 wt%。在這個範圍內,可增强所述光學膜的彈性,從而改善光學膜的自恢復性能和抗刮性。含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或單體在光學膜中的含量可優選為5 wt%至80 wt%,更優選為10 wt%至70 wt%,還更優選為10 wt%至50 wt%。
基於100重量份的橡膠,可UV固化不飽和化合物的固化產物的含量可為10重量份至900重量份。在這個範圍內,對基膜可濕性良好,因此可防止黏合的退化。此外,由於聚合物主鏈的撓性可能不
會減小,所以製造光學膜,尤其是棱鏡膜後,不大可能出現破裂。可UV固化不飽和化合物的固化產物的含量可優選為50重量份至300重量份,更優選為100重量份至250重量份,還更優選為135重量份至213重量份。
可UV固化不飽和化合物的固化產物在光學膜中的含量可為25 wt%至90 wt%。在這個範圍內,基質可具有穩定的交聯網絡。可UV固化不飽和化合物的固化產物在光學膜中的含量可優選為50 wt%至80 wt%,更優選為54 wt%至64 wt%。
將光學膜在50℃和0.34 W/m2下放置200小時後測量黃變指數(△YI),所述光學膜可具有6.0或更小,優選為5.1至5.9的黃變指數。
光學膜可由包括液體橡膠和可UV固化不飽和化合物的組合物製造。
液體橡膠可指用於形成橡膠的液體聚合物。其詳細說明如上所述。
液體橡膠在組合物中的含量可為1 wt%至50 wt%,更優選為10 wt%至40 wt%,更優選為30 wt%至40 wt%。在這個範圍內,可獲得光學膜的自恢復性能和優異的抗刮性。
上面給出了可UV固化不飽和化合物的詳細說明。
可UV固化不飽和化合物在所述組合物中的含量可為25 wt%至90 wt%。在這個範圍內,光學膜的基質可具有穩定交聯的網絡。可UV固化不飽和化合物的含量可優選為50 wt%至80 wt%,更優選為54
wt%至64 wt%。
除了液體橡膠和可UV固化不飽和化合物,所述組合物可進一步包括引發劑、抗靜電劑或矽酮添加劑中的至少一種。
組合物固化後,抗靜電劑可防止在製造的光學膜的生產和組裝中靜電荷的聚集。雖然可無限制地使用任何抗靜電劑,可藉由結合反應性矽酮樹脂與具有離子性鍵結到離子導電金屬的環氧乙基或環氧丙基的離子導電聚合物製備抗靜電劑。
抗靜電劑可為樹脂,其中,離子導電聚合物鍵結到反應性矽酮鏈上,如化學式1表示:
其中,R為-(CH2)m-或-O-;m為1至10的整數;R'為-CH3、-CH=CH2或-C(CH3)=CH2;並且M為鹼金屬。
優選地,M為鋰。
這樣,可藉由結合具有與離子導電金屬離子性鍵結的環氧乙基或環氧丙基的離子導電聚合物與常規反應性矽酮樹脂製備所述抗靜電劑,或可商購抗靜電劑。例如,抗靜電劑可為選自由HR-E、ELECON-600DA和ELECON-700DA(全部購自NANO COMETECH有限公司)、離子液體系列(Ionic Liquid Series),例如IL-A21-9、IL-A2和IL-A5(全部購自KOEI有限公司)等組成的族群中的至少一種。
抗靜電劑在組合物中的含量可為0.1 wt%至10 wt%,優選為0.1 wt%至5 wt%。在這個範圍內,可顯示抗靜電效果,並且離子組分在高溫/高濕的環境下不從光學膜中大量滲出,從而防止界面間黏合以及光學膜的機械和光學性能的退化。
矽酮添加劑在使組合物由模具脫模時可改善模具脫模性能。常規的聚醚矽氧烷共聚物、有機改性聚矽氧烷化合物或它們的混合物可用作矽酮添加劑。可商購的矽酮添加劑的實例包括BYK UV-3500、BYK UV-3530(購自BYK有限公司)或TEGO Glide-100、TEGO Glide-ZG400、TEGO Glide-450(全部可購自TEGO有限公司)等。
矽酮添加劑在組合物中的含量可為0.01 wt%至10 wt%、優選為0.01 wt%至5 wt%。在這個範圍內,在高溫/高濕環境下表面間黏合和光學膜的機械和光學性能無劣化的情况下,可增加模具脫模性能。
引發劑可用於藉由UV來固化組合物。引發劑可包括選自由光聚合引發劑和自由基引發劑組成的族群中的至少一種。引發劑的實例可包括丙酮引發劑、甲酮引發劑、氧化膦引發劑和磷酸酯引發劑,不限於此。
引發劑在組合物中的含量可為0.5 wt%至7 wt%,優選為1 wt%至6 wt%。在這個範圍內,在沒有光學膜的機械强度和棱鏡層的光學性能劣化,例如黃變,的情况下,可獲得高的光反應性。
在25℃和10至100 rpm下,組合物可具有300 cps至3,000 cps範圍內的黏度。這個範圍的黏度可適於生產光學膜。
可藉由常規的方法使用用於光學膜的組合物生產光學膜。
用於光學膜的組合物可用於製備光學膜的光學功能層或基膜。
在一個實施方式中,生產光學膜的方法可包括:在其上雕刻有棱鏡層的模具雕刻輥上塗布用於光學膜的組合物;當與基膜的一側接觸時,固化塗布在雕刻輥上的組合物;使已固化並附著在基膜上的組合物的塗層從模具雕刻輥上脫模,以獲得光學膜。
可藉由本領域中已知的任何塗布方法在其上雕刻有棱鏡層的模具雕刻輥上塗布用於光學膜的組合物。
可將透明材料,尤其是玻璃、透明合成樹脂等用作基膜。通常,可使用聚對苯二甲酸乙二醇酯樹脂。
在另一個實施方式中,生產光學膜的方法可包括:(a)在離型膜上塗布用於光學膜的組合物以形成第一塗層,(b)在模具雕刻輥上塗布用於光學功能層的樹脂組合物以形成第二塗層,(c)使第二塗層與第一塗層的一側接觸,(d)用UV光照射第一或第二塗層以固化第一及第二塗層,和(e)使固化的第一和第二塗層從模具雕刻輥上脫模。
用於所述光學功能層的樹脂組合物可包括可UV固化不飽和化合物和引發劑。只要其用於生產能夠收集、散射、透射、折射或反射光的現有膜,任何樹脂組合物都可用於形成光學功能層。
可藉由照射波長為190 nm至450 nm且强度為100 mJ/cm2至900 mJ/cm2的UV來進行用於光學膜的組合物的固化,不限於此。
本發明的再一個方面,背光單元可包括光學膜。例如,光學膜可包括棱鏡膜。
本發明的再一個方面,光學顯示設備可包括根據本發明的光學膜或背光單元。例如,所述光學顯示設備可包括液晶顯示器,不限於此。
接下來,將參照以下實施例詳細說明本發明的構造和功能。提供這些實施例僅用於說明的目的,而不應以任何方式解釋為限制本發明。
這裏將省略對本領域技術人員顯而易見的細節的說明。
實施例和對比例中使用的組分的細節如下:
(A)液體橡膠:
(A1)氨基甲酸酯液體橡膠(PU340,MIWON Commercial有限公司)
(A2)氨基甲酸酯液體橡膠(HSC2067,HS Chemtron有限公司)
(A3)氨基甲酸酯液體橡膠(HSC3007,HS Chemtron有限公司)
(A4)NBR液體橡膠(N280,Kenima有限公司)
(A5)矽酮液體橡膠(UV Electro 235-2,Momentive有限公司)
(A6)矽酮液體橡膠(UV LSR 2060,Momentive有限公司)
(B)可UV固化不飽和化合物:(B1)丙烯酸苯氧基苄酯、(B2)含10 mol%的環氧乙基的丙烯酸酯、(B3)含30 mol%的環氧乙基的丙烯酸酯、(B4)丙烯酸芴酯、(B5)雙酚F丙烯酸酯、(B6)酚醛樹脂環氧丙烯
酸酯、(B7)苯基苯氧基乙基丙烯酸酯、(B8)雙酚A環氧丙烯酸酯、(B9)乙氧基化硫代聯苯基二丙烯酸酯。
(C)抗靜電劑:矽酮改性的離子導電丙烯酸酯(HR-E,NANO Chemtech有限公司)
(D)矽酮添加劑:含聚醚改性丙烯酸官能團的聚二甲基矽氧烷(UV-3530,BYK有限公司)
(E)引發劑:(E1)1-羥基-環己基-苯基-甲酮(Irgacure 184,Ciba Specialty Chemicals)和(E2)2,4,6-三甲基苯甲醯基二苯基氧化膦(Chemcure TPO)
(F)高硬度氨基甲酸酯丙烯酸酯:Miramer PU370(MIWON commercial有限公司)
藉由以表1中所列的量(單位:重量份)混合組分製備用於光學膜的組合物。藉由在其上刻有棱鏡層的軟模具或金屬模具上塗布所述組合物,UV照射基膜接觸在雕刻模具上的塗層的一側以光固化所述組合物,然後使附著到基膜的固化塗層從雕刻模具脫模,以製備具有在基膜的一側上形成的棱鏡層的棱鏡膜。使棱鏡層形成至30 μm的高度,且使UV由裝備D型燈泡的無電極UV輻射器(600 W/英寸)以500 mJ/cm2强度和190 nm的波長照射。
除了示於表1中的組分的量,以與實施例1中相同的方式生產組合物和光學膜。
檢驗所製備的光學膜或組合物的物理性能。結果概括於表2。
1)折射率:用折射計(型號:1T,ATAGO ABBE,日本)測量所述組合物的折射率。將589.3 nm的D型鈉燈用做光源。
2)亮度(Cd/m2):將棱鏡膜固定到17英寸液晶顯示板的背光單元上。然後,用分光光度計(型號:BM-7,TOPCON公司,日本)在
液晶顯示板上的25個點和9個點上測量亮度,並且平均測量的值。
3)抗刮性(g):在透明PET基膜上塗布和固化組合物後,翻轉固化的棱鏡層,以便接觸放置約500 g的砝碼的遮光側。將該砝碼以10 cm的距離往復10次,並當開始刮擦棱鏡層時,測量質量。
4)黃變指數(△YI):將光學膜在50℃和0.34 W/m2的耐氣候色牢度儀(Weather-O-meter)中放置200小時,然後用色差計測量顏色變化。
5)黏合力(殘留陣列的數目):在透明PET基膜上塗布和固化光固化樹脂組合物後,將固化的棱鏡層切成每個具有10×10 mm2的面積的100個陣列單元。將膠帶附著在所述單元上,並當垂直釋放棱鏡層時,測量從膠帶釋放單元的數目。
6)表面電阻(Ω/cm2):在透明PET基膜上塗布和固化光固化樹脂組合物後,用DSM-8103(Toadenshi Kogyo有限公司,日本)施加恆定電壓以測量表面電阻。
7)模具脫模性能:將實施例中提到的光固化樹脂組合物引入聚酯基膜和具有雕刻其上的棱鏡形狀的金屬模具之間。層壓後,使基膜從金屬模具脫模時的模具脫模性能評估為0至10分。10分定義為優異的模具脫模性能。
8)黏性:在25℃和10至100 rpm下用Brookfield黏度計(DV-II+PRO黏度計,Brookfield有限公司)測量組合物的黏度。
如表2所顯示,可知本發明的光學膜具有優異的抗刮性和改善的亮度、折射率以及對基膜的黏合强度。此外,還可看出用於本發明的光學膜的組合物具有適於加工的黏度和優異的模具脫模性能,並由於包括抗靜電劑等而具有優異的抗靜電效果。
雖然本文已經說明一些實施方式,但是本發明不限於這些實施方式,而是可以各種方式實現。此外,本領域技術人員應理解在不背離本發明的精神和範圍的情况下可做出各種改變。因此,提供這些實施方式僅用於說明的目的,而不應以任何方式解釋為限制本發明。
Claims (17)
- 一種光學膜,包含基膜和在所述基膜的至少一側形成的光學功能層,其中,所述基膜和所述光學功能層的至少一個包含橡膠。
- 如申請專利範圍第1項所述的光學膜,其中,所述橡膠包含選自由丁腈橡膠、苯乙烯丁二烯橡膠、矽酮橡膠、氨基甲酸酯橡膠、(甲基)丙烯酸橡膠、氯丁二烯橡膠,三元乙丙二烯橡膠和氟化橡膠組成的族群中的至少一種。
- 如申請專利範圍第1項所述的光學膜,其中,所述橡膠具有1,000 g/mol至1,000,000 g/mol的重均分子量。
- 如申請專利範圍第1項所述的光學膜,其中,所述橡膠在所述光學膜中的含量為1 wt%至50 wt%。
- 如申請專利範圍第1項所述的光學膜,其中,所述光學功能層包含含所述橡膠和可UV固化不飽和化合物的組合物的固化產物。
- 如申請專利範圍第5項所述的光學膜,其中,所述可UV固化不飽和化合物包含(甲基)丙烯酸酯低聚物和(甲基)丙烯酸酯單體的至少一種。
- 如申請專利範圍第5項所述的光學膜,其中,所述可UV固化不飽和化合物包含含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或單體。
- 如申請專利範圍第7項所述的光學膜,其中,所述含10 mol%或更多的環氧乙基的(甲基)丙烯酸酯低聚物或單體在所述組合物中的含量為5 wt%至90 wt%。
- 如申請專利範圍第5項所述的光學膜,其中,基於100重量份的所述橡膠,所述可UV固化不飽和化合物在所述組合物中的含量為10重量份至900重量份。
- 如申請專利範圍第5項所述的光學膜,其中,所述組合物更包含抗靜電劑、矽酮添加劑和引發劑中的至少一種。
- 如申請專利範圍第10項所述的光學膜,其中,所述抗靜電劑包含藉由結合離子導電聚合物與常規反應性矽酮樹脂獲得的樹脂,所述離子導電聚合物具有與離子導電金屬離子性鍵結的環氧乙基或環氧丙基。
- 如申請專利範圍第10項所述的光學膜,其中,所述矽酮添加劑包含聚醚矽氧烷共聚物和有機改性聚矽氧烷化合物中的至少一種。
- 如申請專利範圍第10項所述的光學膜,其中,所述組合物包含1 wt%至50 wt%的所述橡膠,25 wt%至90 wt%的所述可UV固化不飽和化合物,0.1 wt%至10 wt%的所述抗靜電劑,0.01 wt%至10 wt%的所述矽酮添加劑和0.5 wt%至7 wt%的所述引發劑。
- 如申請專利範圍第1項所述的光學膜,其中,所述光學功能層包含選自棱鏡、雙凸透鏡、微透鏡和壓紋形狀的至少一種光學圖案。
- 如申請專利範圍第1項所述的光學膜,其中,所述光學膜包含棱鏡片。
- 一種背光單元,包含如申請專利範圍第1項至第15項中任一項所述的光學膜。
- 一種光學顯示設備,包含如申請專利範圍第1項至第15項中任一項所述的光學膜。