SU1682335A1 - Фритта - Google Patents
Фритта Download PDFInfo
- Publication number
- SU1682335A1 SU1682335A1 SU894740625A SU4740625A SU1682335A1 SU 1682335 A1 SU1682335 A1 SU 1682335A1 SU 894740625 A SU894740625 A SU 894740625A SU 4740625 A SU4740625 A SU 4740625A SU 1682335 A1 SU1682335 A1 SU 1682335A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- frit
- glass
- glasses
- reduce
- mgo
- Prior art date
Abstract
Изобретение относитс к составам бессвинцовых легкоплавких стекол, позвол ющих использовать их при изготовлении эмалей по стеклу. Цель изобретени - снижение токсичности и удешевление. Фритта содержит следующие компоненты, мас.%: 8263 24,5-30,0; ZnO 30.0-33,7; SiOz 18.2-21,5; 0,55-2,95; MgO 0,90-1,80; NaaO 7,7-9,7; CaO 1,5-2,9; TI02 3,0-4,9; LlaO 1,4-3.0. Температура варки стекол 1000-1100°С. Сваренное стекло гранулируют на воду. Из фритты мокрым помолом изготавливают эмаль, которую методом пульверизации нанос т на стекл нные плитки с последующим обжигом при 580°С. Фритта характеризуетс отсутствием высокотоксичных и дефицитных компонентов, высокой водоустойчивостью и адгезией к стекл нной подложке. 2 табл.
Description
Изобретение относитс к составам бессвинцовых легкоплавких стекол, которые могут быть использованы в качестве эмалей по стеклу.
Цель изобретени -снижение токсичности и удешевление.
Составы фритт приведены в табл. 1.
В состав шихты дл варки фритты вход т традиционные недефицитные сырьевые материалы: кварцевый песок, борна кислота, отходы цинкового производства , углекислый литий, глинозем, доломит , сода, диоксид титана. Варку стекол производ т в тигельной и горшко- вой печах при 1000-1100°С с выдержкой 1 ч. Сваренные стекла гранулируют на воду. Из этой фритты мокрым помолом изготавливают эмаль при мельничном составе , мас.%: фритта 65,0; глина 2,0; вода 33,0, Эмаль методом пульверизации нанос т на стекл нные плитки и обжигают при 580°С в общем цикле обжига 110 мин.
Из характеристики полученных фритт и прототипа, приведенных в табл.2, следует, что фритта предлагаемого состава характеризуетс пониженной температурой варки. согласованностью КЛТР со стекл нной подложкой (стекло непрерывного проката, КЛТР-96х10 7 1/град), высокой водостойкостью и адгезией.
Предлагаема фритта имеет преимущество перед известной в том, что не содержит токсичного фосфорного ангидрида и дефицитного оксида кадми .
Изобретение позвол ет снизить себестоимость шихты дл производства фритты
О 00
hO
GO
OJ
сл
за счет использовани недефицитных сырь- что, с целью снижени токсичности и уде
евых материалов и утилизации отходов цветной металлургии.
Claims (1)
- Формула изобретени Фритта, включающа SI02, ВаОз, ZnO, АЬОз, MgO, Na20, отличающа с тем,1,, -у Vшевлени , она дополнительно содержит CaO, TiOa, Li20 при следующем соотношении компонентов, мас.%: SI02 18,2-21,5; В20з 24.5-30,0; ZnO 30,0-33.7; 0,55- 2,95; MgO 0,9-1.8; Na20 7,7-9,7; CaO 1,5-2,9: TI02 3,0-4,9; LI20 1,4-3,0.Таблица 1Таблица 2